WO2023181849A1 - ポリカーボネート樹脂組成物及びアンテナ用部材 - Google Patents
ポリカーボネート樹脂組成物及びアンテナ用部材 Download PDFInfo
- Publication number
- WO2023181849A1 WO2023181849A1 PCT/JP2023/008041 JP2023008041W WO2023181849A1 WO 2023181849 A1 WO2023181849 A1 WO 2023181849A1 JP 2023008041 W JP2023008041 W JP 2023008041W WO 2023181849 A1 WO2023181849 A1 WO 2023181849A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polycarbonate resin
- mass
- parts
- polycarbonate
- resin composition
- Prior art date
Abstract
ポリカーボネート樹脂（Ａ）１００質量部に対し、ポリスチレン系樹脂（Ｂ）を３０～１５０質量部、およびエラストマー（Ｃ）を３～６０質量部含み、ポリカーボネート樹脂（Ａ）はビスフェノールＡ型ポリカーボネート（Ａ１）と特定の構成単位を有するポリカーボネート（Ａ２）を含み、両者の含有量の質量比（Ａ２／Ａ１）が５／９５～８０／２０であることを特徴とするポリカーボネート樹脂組成物、その成形品、及びアンテナ用部材。
Description
本発明はポリカーボネート樹脂組成物及びアンテナ用部材に関し、詳しくは、比誘電率及び誘電正接が共に低く、高度の耐衝撃性を有し、耐熱性、剛性及び硬度にも優れたポリカーボネート樹脂組成物、その成形品、及びアンテナ用部材に関する。
移動体通信機器、その基地局装置、サーバー、ルーター等のネットワークインフラ機器、大型コンピュータなどの電子機器では使用する信号の高速化及び大容量化が進行している。また、上記した電子機器の他に、自動車や交通システム関連、あるいは室内の近距離通信分野でも高周波無線信号を扱うシステムの実用化が進んでいる。
そして、ＧＨｚレベルの高周波信号を用いた情報通信分野では高速化の伸びが著しく、国内では２０２０年３月に第５世代移動通信システム（５Ｇ）の商用サービスが開始され、その次の世代となる第６世代移動通信システム（６Ｇ）ではより高い周波数帯域の使用が検討されている。
このような大容量・高速化に対応するため、使用する通信機器やレーダー機器の部品には、低比誘電率及び低誘電正接の材料が求められる。
このような大容量・高速化に対応するため、使用する通信機器やレーダー機器の部品には、低比誘電率及び低誘電正接の材料が求められる。
本出願人は、特許文献１にて、熱可塑性樹脂とアルミナ（Ｂ）とを含む樹脂組成物が、比誘電率と誘電正接も低く、ミリ波透過性に優れたミリ波レーダー用カバーを提供することを提案した。しかし、アルミナは誘電率の絶対値が高い材料であり、特許文献１のポリカーボネート樹脂を含有する実施例２には比誘電率は３．７、誘電正接は０．００９３であることが示されている。
電磁波の透過損失を小さくするためには、材料に発生する誘電損失の大きさが、材料の比誘電率の平方根と誘電正接の積に比例するため、比誘電率と誘電正接が共に小さい材料が求められるが、上記のような比誘電率と誘電正接では大容量・高速化対応の材料としては十分とはいい難い。
電磁波の透過損失を小さくするためには、材料に発生する誘電損失の大きさが、材料の比誘電率の平方根と誘電正接の積に比例するため、比誘電率と誘電正接が共に小さい材料が求められるが、上記のような比誘電率と誘電正接では大容量・高速化対応の材料としては十分とはいい難い。
さらに、本出願人は、特許文献２にて、特定のビスフェノール単位のポリカーボネート樹脂が低誘電正接であることを見出し、これを汎用のポリカーボネート樹脂にブレンドすることにより、比誘電率と誘電正接を共に低減させたポリカーボネート樹脂材料のミリ波レーダー用カバーを提案した。このポリカーボネート樹脂材料は有効な材料であるが、価格が高くなるために用途が限定されるという問題がある。
誘電特性の良い樹脂として、ポリスチレンを配合することが考えられるが、ポリスチレンは汎用のポリカーボネート樹脂とは相溶性が悪く、また耐熱性が悪く、さらに耐衝撃性が悪いという欠点がある。
また、アンテナ用の基材やカバー等は、剛性を十分に保持するため、また、屋外設置において風圧に十分に耐えうるために高い剛性や耐衝撃性に優れることも要求され、さらに、高温下でも機能が損なわれないためにも耐熱性に優れることが求められる。
本発明は、上記状況に鑑みなされたものであり、その目的（課題）は、低コストで、低比誘電率で低誘電正接であり、耐熱性、剛性及び耐衝撃性に優れたポリカーボネート樹脂組成物を提供することにある。
汎用のポリカーボネート樹脂にポリスチレン系樹脂を配合すると、低誘電正接にはなるが耐衝撃性が大きく低下する。そこでエラストマーを添加すると耐衝撃性は向上するが、添加しすぎると強度、剛性、耐熱性が低下するという課題がある。
汎用のポリカーボネート樹脂にポリスチレン系樹脂を配合すると、低誘電正接にはなるが耐衝撃性が大きく低下する。そこでエラストマーを添加すると耐衝撃性は向上するが、添加しすぎると強度、剛性、耐熱性が低下するという課題がある。
本発明者は、上記課題を解決すべく、鋭意検討を重ねた結果、汎用のポリカーボネート樹脂とポリスチレン系樹脂を含有する系において、エラストマー、さらに特定構造のポリカーボネート樹脂を含むことにより、耐衝撃性が劇的に向上し、上記課題が解決できることを見出し、本発明を完成するに至った。
本発明は、以下のポリカーボネート樹脂組成物、成形品及びアンテナ用部材に関する。
本発明は、以下のポリカーボネート樹脂組成物、成形品及びアンテナ用部材に関する。
１．ポリカーボネート樹脂（Ａ）１００質量部に対し、ポリスチレン系樹脂（Ｂ）を３０～１５０質量部、及びエラストマー（Ｃ）を３～６０質量部含み、ポリカーボネート樹脂（Ａ）はビスフェノールＡ型ポリカーボネート（Ａ１）と下記式（１）で表される構成単位を有するポリカーボネート（Ａ２）を含み、両者の含有量の質量比（Ａ２／Ａ１）が５／９５～８０／２０であることを特徴とするポリカーボネート樹脂組成物。
［式（１）中、Ｒ１はメチル基を表し、Ｒ２は水素原子またはメチル基を表し、Ｘは下記のいずれかの式を表し、
Ｒ３およびＲ４は、それぞれ独立に、水素原子またはメチル基を表し、ＺはＣと結合して炭素数６～１２の、置換基を有していてもよい脂環式炭化水素を形成する基を表す。］２．エラストマー（Ｃ）が、ブタジエン／メチル（メタ）アクリレート共重合体、ブタジエン／メチル（メタ）アクリレート／スチレン共重合体、およびスチレン／エチレン／ブチレン／スチレン共重合体から選ばれる１種または２種以上である上記１に記載のポリカーボネート樹脂組成物。
３．周波数５．８ＧＨｚでの誘電正接が０．００４０以下である上記１または２に記載のポリカーボネート樹脂組成物。
４．ポリスチレン系樹脂（Ｂ）とエラストマー（Ｃ）の含有量の比［（Ｂ）／（Ｃ）］が９以下である上記１～３のいずれかに記載のポリカーボネート樹脂組成物。
５．アクリロニトリル－ブタジエン－スチレン共重合体を含有しないか、含有する場合の含有量が、ポリカーボネート樹脂（Ａ）１００質量部に対し、１０質量部以下である上記１～４のいずれかに記載のポリカーボネート樹脂組成物。
６．上記１～５のいずれかに記載のポリカーボネート樹脂組成物の成形品。
７．アンテナ用部材である上記６に記載の成形品。
３．周波数５．８ＧＨｚでの誘電正接が０．００４０以下である上記１または２に記載のポリカーボネート樹脂組成物。
４．ポリスチレン系樹脂（Ｂ）とエラストマー（Ｃ）の含有量の比［（Ｂ）／（Ｃ）］が９以下である上記１～３のいずれかに記載のポリカーボネート樹脂組成物。
５．アクリロニトリル－ブタジエン－スチレン共重合体を含有しないか、含有する場合の含有量が、ポリカーボネート樹脂（Ａ）１００質量部に対し、１０質量部以下である上記１～４のいずれかに記載のポリカーボネート樹脂組成物。
６．上記１～５のいずれかに記載のポリカーボネート樹脂組成物の成形品。
７．アンテナ用部材である上記６に記載の成形品。
本発明のポリカーボネート樹脂組成物は、低コストでありながら、前記式（１）のポリカーボネート（Ａ２）がポリスチレン系樹脂（Ｂ）との密着性が向上して極めて高い耐衝撃性を有し、さらに、剛性、耐熱性及び硬度に優れ、比誘電率と誘電正接が共に低く、電磁波の透過減衰量が小さいので、５Ｇや６Ｇのような高周波帯域にも対応可能な電子電気機器部品、特にアンテナ基材やアンテナカバー等のアンテナ用部材、中でも周波数１ＧＨｚ以上の電磁波を使用するアンテナ用の部材として好適に使用でき、電磁波の信頼性を十分に確保することができる。
以下、本発明について実施形態及び例示物等を示して詳細に説明する。
なお、本明細書において、「～」とは、特に断りがない場合、その前後に記載される数値を下限値及び上限値として含む意味で使用される。
なお、本明細書において、「～」とは、特に断りがない場合、その前後に記載される数値を下限値及び上限値として含む意味で使用される。
本発明のポリカーボネート樹脂組成物は、ポリカーボネート樹脂（Ａ）１００質量部に対し、ポリスチレン系樹脂（Ｂ）を３０～１５０質量部、及びエラストマー（Ｃ）を３～６０質量部含み、ポリカーボネート樹脂（Ａ）はビスフェノールＡ型ポリカーボネート（Ａ１）と前記式（１）で表される構成単位を有するポリカーボネート（Ａ２）を含み、両者の含有量の質量比（Ａ２／Ａ１）が５／９５～８０／２０であることを特徴とする。
以下、本発明のポリカーボネート樹脂組成物に使用するポリカーボネート樹脂組成物を構成する各成分等につき、詳細に説明する。
［ポリカーボネート樹脂（Ａ）］
本発明で用いるポリカーボネート樹脂（Ａ）は、ビスフェノールＡ型ポリカーボネート（Ａ１）と下記式（１）で表される構成単位を有するポリカーボネート（Ａ２）を含み、両者の含有量の質量比（Ａ２／Ａ１）が５／９５～８０／２０であるポリカーボネート樹脂である。
（式（１）中、Ｒ１はメチル基を表し、Ｒ２は水素原子またはメチル基を表し、Ｘは下記のいずれかの式を表し、
Ｒ３およびＲ４は、それぞれ独立に、水素原子またはメチル基を表し、ＺはＣと結合して炭素数６～１２の、置換基を有していてもよい脂環式炭化水素を形成する基を表す。）
本発明で用いるポリカーボネート樹脂（Ａ）は、ビスフェノールＡ型ポリカーボネート（Ａ１）と下記式（１）で表される構成単位を有するポリカーボネート（Ａ２）を含み、両者の含有量の質量比（Ａ２／Ａ１）が５／９５～８０／２０であるポリカーボネート樹脂である。
ポリカーボネート樹脂（Ａ）は、ビスフェノールＡ型ポリカーボネート（Ａ１）と、上記式（１）で表される構成単位のポリカーボネート（Ａ２）から構成されるポリカーボネート共重合体またはポリカーボネートブレンド物のいずれであってもよく、両者の含有量の質量比（Ａ２／Ａ１）が５／９５～８０／２０であるポリカーボネート樹脂である。
上記質量比は、ポリカーボネート樹脂（Ａ）が、（Ａ１）と（Ａ２）のポリカーボネート共重合体であっても、ポリカーボネート（Ａ１）を主たる構成単位とするポリカーボネート樹脂と、構成単位（Ａ２）を主たる構成単位とするポリカーボネート樹脂をブレンドした混合物（ポリカーボネートブレンド物）によって達成されていてもよい。
ここで、主たる構成単位とは、各ポリカーボネートのカーボネート構成単位１００質量％中、（Ａ１）あるいは（Ａ２）が５０質量％超、好ましくは８０質量％以上、より好ましくは９０質量％以上、さらに好ましくは９５質量％以上、最も好ましくは９７質量％以上の割合であることを意味する。
ここで、主たる構成単位とは、各ポリカーボネートのカーボネート構成単位１００質量％中、（Ａ１）あるいは（Ａ２）が５０質量％超、好ましくは８０質量％以上、より好ましくは９０質量％以上、さらに好ましくは９５質量％以上、最も好ましくは９７質量％以上の割合であることを意味する。
ポリカーボネート（Ａ２）は、式（１）中、ＺがＣと結合して形成される脂環式炭化水素としては、シクロヘキシリデン基、シクロヘプチリデン基、シクロドデシリデン基、アダマンチリデン基、シクロドデシリデン基等のシクロアルキリデン基が挙げられる。ＺがＣと結合して形成される置換基を有する脂環式炭化水素としては、上述した脂環式炭化水素基のメチル置換体、エチル置換体などが挙げられる。これらの中でも、シクロヘキシリデン基、シクロヘキシリデン基のメチル置換体（好ましくは３，３，５－トリメチル置換体）、シクロドデシリデン基が好ましい。
また、式（１）中、Ｘが、
である場合、Ｒ３およびＲ４は、少なくとも一方がメチル基であることが好ましく、両方がメチル基であることがより好ましい。
ポリカーボネート（Ａ２）の好ましい具体例としては、以下のイ）～ニ）が好ましく挙げられる。
イ）２，２－ビス（３－メチル－４－ヒドロキシフェニル）プロパン単位を有するもの、
ロ）１，１－ビス（３－メチル－４－ヒドロキシフェニル）シクロドデカン単位を有するもの、
ハ）２，２－ビス（３，５－ジメチル－４－ヒドロキシフェニル）プロパン単位を有するもの、
ニ）１，１－ビス（３－メチル－４－ヒドロキシフェニル）シクロヘキサン単位を有するもの。
イ）２，２－ビス（３－メチル－４－ヒドロキシフェニル）プロパン単位を有するもの、
ロ）１，１－ビス（３－メチル－４－ヒドロキシフェニル）シクロドデカン単位を有するもの、
ハ）２，２－ビス（３，５－ジメチル－４－ヒドロキシフェニル）プロパン単位を有するもの、
ニ）１，１－ビス（３－メチル－４－ヒドロキシフェニル）シクロヘキサン単位を有するもの。
上記した構成単位のポリカーボネート樹脂は、それぞれ、２，２－ビス（３－メチル－４－ヒドロキシフェニル）プロパン、２，２－ビス（３－メチル－４－ヒドロキシフェニル）シクロドデカン、２，２－ビス（３，５－ジメチル－４－ヒドロキシフェニル）プロパン、１，１－ビス（３－メチル－４－ヒドロキシフェニル）シクロヘキサン、３，３－ジメチルビフェノールを、ジヒドロキシ化合物として使用して製造することができる。
ポリカーボネート樹脂（Ａ）の分子量は任意であり、適宜選択して決定すればよい。
ポリカーボネート樹脂（Ａ）が、（Ａ１）と（Ａ２）のポリカーボネート共重合体の場合、あるいは（Ａ１）と、（Ａ２）のブレンド物である場合のいずれの場合も、ポリカーボネート共重合体並びに各ポリカーボネート樹脂の粘度平均分子量Ｍｖは、粘度平均分子量Ｍｖは、通常１００００以上、好ましくは１４０００以上、より好ましくは１６０００以上であり、また、通常４００００以下、好ましくは３００００以下である。粘度平均分子量を前記範囲の下限値以上とすることにより、樹脂組成物の機械的強度をより向上させることができる。一方、粘度平均分子量を前記範囲の上限値以下とすることにより樹脂組成物の流動性低下を抑制して改善でき、成形加工性を高めて成形加工を容易に行えるようになる。
なお、粘度平均分子量の異なる２種類以上のポリカーボネート樹脂を混合して用いてもよく、この場合には、粘度平均分子量が上記の好適な範囲外であるポリカーボネート樹脂を混合してもよい。
ポリカーボネート樹脂（Ａ）が、（Ａ１）と（Ａ２）のポリカーボネート共重合体の場合、あるいは（Ａ１）と、（Ａ２）のブレンド物である場合のいずれの場合も、ポリカーボネート共重合体並びに各ポリカーボネート樹脂の粘度平均分子量Ｍｖは、粘度平均分子量Ｍｖは、通常１００００以上、好ましくは１４０００以上、より好ましくは１６０００以上であり、また、通常４００００以下、好ましくは３００００以下である。粘度平均分子量を前記範囲の下限値以上とすることにより、樹脂組成物の機械的強度をより向上させることができる。一方、粘度平均分子量を前記範囲の上限値以下とすることにより樹脂組成物の流動性低下を抑制して改善でき、成形加工性を高めて成形加工を容易に行えるようになる。
なお、粘度平均分子量の異なる２種類以上のポリカーボネート樹脂を混合して用いてもよく、この場合には、粘度平均分子量が上記の好適な範囲外であるポリカーボネート樹脂を混合してもよい。
ポリカーボネート樹脂は、高分子量のポリカーボネート樹脂、例えば好ましくは粘度平均分子量Ｍｖが、５００００～９５０００のポリカーボネート樹脂を含有することも好ましい。高分子量ポリカーボネート樹脂の粘度平均分子量は、より好ましくは５５０００以上であり、さらに好ましくは６００００以上、中でも６１０００以上、特には６２０００以上が好ましく、また、より好ましくは９００００以下、さらに好ましくは８５０００以下、中でも８００００以下、とりわけ７５０００以下、特には７００００以下が好ましい。
高分子量ポリカーボネート樹脂を含む場合は、ポリカーボネート樹脂中、５質量％以上含むことが好ましく、１０質量％以上がより好ましく、１５質量％以上であることがさらに好ましい。なお、上限は、好ましくは４０質量％以下であり、より好ましくは３０質量％以下である。
なお、本発明において、ポリカーボネート樹脂の粘度平均分子量Ｍｖは、溶媒としてメチレンクロライドを使用し、ウベローデ粘度計を用いて温度２５℃での極限粘度［η］（単位ｄｌ／ｇ）を求め、Ｓｃｈｎｅｌｌの粘度式、すなわち、
η＝１．２３×１０－４Ｍｖ０．８３ から算出される値を意味する。
また極限粘度［η］とは、各溶液濃度［Ｃ］（ｇ／ｄｌ）での比粘度［ηｓｐ］を測定し、下記式により算出した値である。
η＝１．２３×１０－４Ｍｖ０．８３ から算出される値を意味する。
また極限粘度［η］とは、各溶液濃度［Ｃ］（ｇ／ｄｌ）での比粘度［ηｓｐ］を測定し、下記式により算出した値である。
ポリカーボネート樹脂の末端水酸基濃度は任意であり、適宜選択して決定すればよいが、通常２０００ｐｐｍ以下、好ましくは１５００ｐｐｍ以下、より好ましくは１０００ｐｐｍ以下である。これにより本発明の樹脂組成物の滞留熱安定性及び色調をより向上させることができる。また、その下限は、特に溶融エステル交換法で製造されたポリカーボネート樹脂では、通常１０ｐｐｍ以上、好ましくは３０ｐｐｍ以上、より好ましくは４０ｐｐｍ以上である。これにより、分子量の低下を抑制し、本発明の樹脂組成物の機械的特性をより向上させることができる。
なお、末端水酸基濃度の単位は、ポリカーボネート樹脂の質量に対する、末端水酸基の質量をｐｐｍで表示したものである。その測定方法は、四塩化チタン／酢酸法による比色定量（Ｍａｃｒｏｍｏｌ．Ｃｈｅｍ．８８ ２１５（１９６５）に記載の方法）である。
また、成形品の外観の向上や流動性の向上を図るため、ポリカーボネート樹脂は、ポリカーボネートオリゴマーを含有していてもよい。このポリカーボネートオリゴマーの粘度平均分子量Ｍｖは、通常１５００以上、好ましくは２０００以上であり、また、通常９５００以下、好ましくは９０００以下である。さらに、含有されるポリカーボネートオリゴマーは、ポリカーボネート樹脂（ポリカーボネートオリゴマーを含む）の３０質量％以下とすることが好ましい。
また、成形品の外観の向上や流動性の向上を図るため、ポリカーボネート樹脂は、ポリカーボネートオリゴマーを含有していてもよい。このポリカーボネートオリゴマーの粘度平均分子量Ｍｖは、通常１５００以上、好ましくは２０００以上であり、また、通常９５００以下、好ましくは９０００以下である。さらに、含有されるポリカーボネートオリゴマーは、ポリカーボネート樹脂（ポリカーボネートオリゴマーを含む）の３０質量％以下とすることが好ましい。
ポリカーボネート樹脂は、バージン樹脂だけでなく、使用済みの製品から再生されたポリカーボネート樹脂（いわゆるマテリアルリサイクルされたポリカーボネート樹脂）、あるいは、ポリカーボネート樹脂を化学的に分解して原料にまで戻したものから製造したポリカーボネート樹脂（いわゆるケミカルリサイクルされたポリカーボネート樹脂）であってもよく、バージン樹脂とリサイクル樹脂の両方を含有することも好ましく、リサイクルポリカーボネート樹脂からなることでもよい。リサイクルポリカーボネート樹脂を含む場合、ポリカーボネート樹脂中のリサイクルポリカーボネート樹脂の割合は４０％以上、５０％以上、６０％以上、８０％以上が好ましく、リサイクルポリカーボネート樹脂が１００％であることも好ましい。
［ポリスチレン系樹脂（Ｂ）］
本発明のポリカーボネート樹脂組成物は、ポリスチレン系樹脂（Ｂ）を、ポリカーボネート樹脂（Ａ）１００質量部に対し、３０～１５０質量部を含有する。
本発明のポリカーボネート樹脂組成物は、ポリスチレン系樹脂（Ｂ）を、ポリカーボネート樹脂（Ａ）１００質量部に対し、３０～１５０質量部を含有する。
ポリスチレン系樹脂としては、好ましくはスチレンの単独重合体であり、あるいは他の芳香族ビニルモノマー、例えばα－メチルスチレン、パラメチルスチレン、ビニルトルエン、ビニルキシレン等を例えば、５０質量％未満の範囲で共重合したものであってもよい。
また、ポリスチレン系樹脂は、ゴム強化ポリスチレン樹脂であってもよい。ゴム強化ポリスチレン樹脂としては、好ましくはブタジエン系ゴム成分を共重合またはブレンドしたものであり、ブタジエン系ゴム成分の量は、通常１質量％以上５０質量％未満であり、好ましくは３～４０質量％、より好ましくは５～３０質量％、さらに好ましくは５～２０質量％である。ゴム強化ポリスチレン樹脂としては、ハイインパクトポリスチレン（ＨＩＰＳ）が特に好ましい。
ポリスチレン系樹脂（Ｂ）の含有量は、ポリカーボネート樹脂（Ａ）１００質量部に対して、３０～１５０質量部であるが、好ましくは４０質量部以上、より好ましくは５０質量部以上、中でも６０質量部以上、特に７０質量部以上が好ましく、好ましくは１３０質量部以下、より好ましくは１２０質量部以下、中でも１１０質量部以下、特に１００質量部以下が好ましい。
ただし、アクリロニトリル－ブタジエン－スチレン共重合体（ＡＢＳ樹脂）等のアクリロニトリルを含む共重合体は、誘電正接を高める傾向があるため、含有しない方が好ましく、含有する場合でもその量は、ポリカーボネート樹脂（Ａ）１００質量部に対して、１０質量部以下であることが好ましく、より好ましくは７質量部以下、中でも５質量部以下、３質量部以下、２質量部以下、１質量部以下が好ましい。
ただし、アクリロニトリル－ブタジエン－スチレン共重合体（ＡＢＳ樹脂）等のアクリロニトリルを含む共重合体は、誘電正接を高める傾向があるため、含有しない方が好ましく、含有する場合でもその量は、ポリカーボネート樹脂（Ａ）１００質量部に対して、１０質量部以下であることが好ましく、より好ましくは７質量部以下、中でも５質量部以下、３質量部以下、２質量部以下、１質量部以下が好ましい。
［エラストマー（Ｃ）］
エラストマーとしては、エラストマーとしては、ゴム成分にこれと共重合可能な単量体成分をグラフト共重合した共重合体が好ましい。このようなグラフト共重合体の製造方法としては、塊状重合、溶液重合、懸濁重合、乳化重合などのいずれの製造方法であってもよく、共重合の方式は一段グラフトでも多段グラフトであってもよい。
エラストマーとしては、エラストマーとしては、ゴム成分にこれと共重合可能な単量体成分をグラフト共重合した共重合体が好ましい。このようなグラフト共重合体の製造方法としては、塊状重合、溶液重合、懸濁重合、乳化重合などのいずれの製造方法であってもよく、共重合の方式は一段グラフトでも多段グラフトであってもよい。
上記ゴム成分は、ガラス転移温度が通常０℃以下、中でも－２０℃以下のものが好ましく、更には－３０℃以下のものが好ましい。ゴム成分の具体例としては、ポリブタジエンゴム、ポリイソプレンゴムあるいはその水添物、ブタジエン－アクリル複合ゴム、スチレン－ブタジエンゴム、エチレン－プロピレンゴムやエチレン－ブテンゴム、エチレン－オクテンゴムなどのエチレン－αオレフィン系ゴム、エチレン－アクリルゴムなどを挙げることができる。これらは、単独でも２種以上を混合して使用してもよい。これらの中でも、ポリブタジエンゴム、ポリイソプレンゴムその水添物、スチレン－ブタジエンゴムが好ましい。
ゴム成分が、ポリブチルアクリレートやポリ（２－エチルヘキシルアクリレート）、ブチルアクリレート・２－エチルヘキシルアクリレート共重合体などのポリアルキルアクリレートゴム、あるいはオルガノポリシロキサンゴムなどのシリコーン系ゴムのものは、誘電正接が上昇しやすいので好ましくない。
ゴム成分が、ポリブチルアクリレートやポリ（２－エチルヘキシルアクリレート）、ブチルアクリレート・２－エチルヘキシルアクリレート共重合体などのポリアルキルアクリレートゴム、あるいはオルガノポリシロキサンゴムなどのシリコーン系ゴムのものは、誘電正接が上昇しやすいので好ましくない。
ゴム成分とグラフト共重合可能な単量体成分の具体例としては、芳香族ビニル化合物、シアン化ビニル化合物、（メタ）アクリル酸エステル化合物、（メタ）アクリル酸化合物、グリシジル（メタ）アクリレート等のエポキシ基含有（メタ）アクリル酸エステル化合物；マレイミド、Ｎ－メチルマレイミド、Ｎ－フェニルマレイミド等のマレイミド化合物；マレイン酸、フタル酸、イタコン酸等のα，β－不飽和カルボン酸化合物やそれらの無水物（例えば無水マレイン酸等）などが挙げられる。これらの単量体成分は１種を単独で用いても２種以上を併用してもよい。これらの中でも、芳香族ビニル化合物、（メタ）アクリル酸エステル化合物が好ましく、スチレン、（メタ）アクリル酸メチル、（メタ）アクリル酸エチル、（メタ）アクリル酸ブチル、（メタ）アクリル酸シクロヘキシル、（メタ）アクリル酸オクチル等を好ましく挙げることができる。
エラストマーは、コア／シェル型グラフト共重合体タイプのものが好ましい。中でもポリブタジエン含有ゴム、エチレン／ブチレンゴム、ポリブチルアクリレート含有ゴムから選ばれる少なくとも１種のゴム成分をコア層とし、その周囲に（メタ）アクリル酸エステルを共重合して形成されたシェル層からなる、コア／シェル型グラフト共重合体が好ましく、特にブタジエン系ゴムをコアとするコア／シェル型エラストマーが好ましい。上記コア／シェル型グラフト共重合体において、ゴム成分を４０質量％以上含有するものが好ましく、６０質量％以上含有するものがさらに好ましい。また、（メタ）アクリル酸成分は、１０質量％以上含有するものが好ましい。
これらコア／シェル型グラフト共重合体の好ましい具体例としては、ブタジエン／メチル（メタ）アクリレート共重合体（ＭＢ）、ブタジエン／メチル（メタ）アクリレート／スチレン共重合体（ＭＢＳ）、およびスチレン／エチレン／ブチレン／スチレン共重合体（ＳＥＢＳ）等が好ましく挙げられ、ブタジエン／メチル（メタ）アクリレート共重合体（ＭＢ）、ブタジエン／メチル（メタ）アクリレート／スチレン共重合体（ＭＢＳ）、およびスチレン／エチレン／ブチレン／スチレン共重合体（ＳＥＢＳ）がより好ましい。
エラストマー（Ｃ）の含有量は、ポリカーボネート樹脂（Ａ）１００質量部に対し、３～６０質量部である。このような量で含有することにより、ポリカーボネート樹脂組成物の耐衝撃性、剛性及び耐熱性、さらに比誘電率と誘電正接をバランスよく良好なものとすることができる。エラストマー（Ｃ）の含有量は、好ましくは５質量部以上、より好ましくは７．５質量部以上、中でも１０質量部以上、特に１５質量部以上が好ましく、好ましくは５０質量部以下、より好ましくは４０質量部以下、中でも３０質量部以下、特に２５質量部以下が好ましい。
また、ポリカーボネート樹脂組成物のポリスチレン系樹脂（Ｂ）とエラストマー（Ｃ）の含有量比（ポリスチレン系樹脂（Ｂ）の含有量／エラストマー（Ｃ）の含有量）が９以下であると、ノッチ付きシャルピー衝撃強さ値が高くなるため好ましい。
また、ポリカーボネート樹脂組成物のポリスチレン系樹脂（Ｂ）とエラストマー（Ｃ）の含有量比（ポリスチレン系樹脂（Ｂ）の含有量／エラストマー（Ｃ）の含有量）が９以下であると、ノッチ付きシャルピー衝撃強さ値が高くなるため好ましい。
［安定剤］
本発明のポリカーボネート樹脂組成物は、安定剤を含有することが好ましく、安定剤としてはリン系安定剤（熱安定剤）やフェノール系安定剤（酸化防止剤）が好ましい。
本発明のポリカーボネート樹脂組成物は、安定剤を含有することが好ましく、安定剤としてはリン系安定剤（熱安定剤）やフェノール系安定剤（酸化防止剤）が好ましい。
リン系安定剤としては、公知の任意のものを使用できる。具体例を挙げると、リン酸、ホスホン酸、亜燐酸、ホスフィン酸、ポリリン酸などのリンのオキソ酸；酸性ピロリン酸ナトリウム、酸性ピロリン酸カリウム、酸性ピロリン酸カルシウムなどの酸性ピロリン酸金属塩；リン酸カリウム、リン酸ナトリウム、リン酸セシウム、リン酸亜鉛など第１族または第２Ｂ族金属のリン酸塩；有機ホスフェート化合物、有機ホスファイト化合物、有機ホスホナイト化合物などが挙げられるが、有機ホスファイト化合物が特に好ましい。
有機ホスファイト化合物としては、トリフェニルホスファイト、トリス（モノノニルフェニル）ホスファイト、トリス（モノノニル／ジノニル・フェニル）ホスファイト、トリス（２，４－ジ－ｔｅｒｔ－ブチルフェニル）ホスファイト、モノオクチルジフェニルホスファイト、ジオクチルモノフェニルホスファイト、モノデシルジフェニルホスファイト、ジデシルモノフェニルホスファイト、トリデシルホスファイト、トリラウリルホスファイト、トリステアリルホスファイト、２，２－メチレンビス（４，６－ジ－ｔｅｒｔ－ブチルフェニル）オクチルホスファイト等が挙げられる。
このような、有機ホスファイト化合物としては、具体的には、例えば、ＡＤＥＫＡ社製「アデカスタブ１１７８」、「アデカスタブ２１１２」、「アデカスタブＨＰ－１０」、城北化学工業社製「ＪＰ－３５１」、「ＪＰ－３６０」、「ＪＰ－３ＣＰ」、ＢＡＳＦ社製「イルガフォス１６８」等が挙げられる。
なお、リン系安定剤は、１種が含有されていてもよく、２種以上が任意の組み合わせ及び比率で含有されていてもよい。
このような、有機ホスファイト化合物としては、具体的には、例えば、ＡＤＥＫＡ社製「アデカスタブ１１７８」、「アデカスタブ２１１２」、「アデカスタブＨＰ－１０」、城北化学工業社製「ＪＰ－３５１」、「ＪＰ－３６０」、「ＪＰ－３ＣＰ」、ＢＡＳＦ社製「イルガフォス１６８」等が挙げられる。
なお、リン系安定剤は、１種が含有されていてもよく、２種以上が任意の組み合わせ及び比率で含有されていてもよい。
リン系安定剤の含有量は、ポリカーボネート樹脂（Ａ）１００質量部に対し、好ましくは０．０１質量部以上、より好ましくは０．０３質量部以上であり、また、通常１質量部以下、好ましくは０．７質量部以下、より好ましくは０．５質量部以下である。リン系安定剤の含有量が前記範囲の下限値未満の場合は、熱安定効果が不十分となる可能性があり、リン系安定剤の含有量が前記範囲の上限値を超える場合は、効果が頭打ちとなり経済的でなくなる可能性がある。
フェノール系安定剤としては、例えばヒンダードフェノール系酸化防止剤が挙げられる。その具体例としては、ペンタエリスリトールテトラキス［３－（３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシフェニル）プロピオネート］、オクタデシル－３－（３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシフェニル）プロピオネート、チオジエチレンビス［３－（３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシフェニル）プロピオネート］、Ｎ，Ｎ’－ヘキサン－１，６－ジイルビス［３－（３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシフェニル）プロピオナミド］、２，４－ジメチル－６－（１－メチルペンタデシル）フェノール、ジエチル［［３，５－ビス（１，１－ジメチルエチル）－４－ヒドロキシフェニル］メチル］ホスフォエート、３，３’，３”，５，５’，５”－ヘキサ－ｔｅｒｔ－ブチル－ａ，ａ’，ａ”－（メシチレン－２，４，６－トリル）トリ－ｐ－クレゾール、４，６－ビス（オクチルチオメチル）－ｏ－クレゾール、エチレンビス（オキシエチレン）ビス［３－（５－ｔｅｒｔ－ブチル－４－ヒドロキシ－ｍ－トリル）プロピオネート］、ヘキサメチレンビス［３－（３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシフェニル）プロピオネート］、１，３，５－トリス（３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシベンジル）－１，３，５－トリアジン－２，４，６（１Ｈ，３Ｈ，５Ｈ）－トリオン，２，６－ジ－ｔｅｒｔ－ブチル－４－（４，６－ビス（オクチルチオ）－１，３，５－トリアジン－２－イルアミノ）フェノール、２－［１－（２－ヒドロキシ－３，５－ジ－ｔｅｒｔ－ペンチルフェニル）エチル］－４，６－ジ－ｔｅｒｔ－ペンチルフェニルアクリレート等が挙げられる。
中でも、ペンタエリスリトールテトラキス［３－（３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシフェニル）プロピオネート］、オクタデシル－３－（３，５－ジ－ｔｅｒｔ－ブチル－４－ヒドロキシフェニル）プロピオネートが好ましい。このようなフェノール系酸化防止剤としては、具体的には、例えば、ＢＡＳＦ社製「イルガノックス１０１０」、「イルガノックス１０７６」、ＡＤＥＫＡ社製「アデカスタブＡＯ－５０」、「アデカスタブＡＯ－６０」等が挙げられる。
なお、フェノール系安定剤は、１種が含有されていてもよく、２種以上が任意の組み合わせ及び比率で含有されていてもよい。
なお、フェノール系安定剤は、１種が含有されていてもよく、２種以上が任意の組み合わせ及び比率で含有されていてもよい。
フェノール系安定剤の含有量は、ポリカーボネート樹脂（Ａ）１００質量部に対し、好ましくは０．０１質量部以上であり、また、通常１質量部以下、好ましくは０．５質量部以下である。フェノール系安定剤の含有量を前記範囲の下限値以上とすることで、フェノール系安定剤としての効果を十分得ることができる。また、フェノール系安定剤の含有量が前記範囲の上限値以下にすることにより、効果が頭打ちになることなく経済的である。
［離型剤］
本発明のポリカーボネート樹脂組成物は、離型剤を含有することが好ましい。離型剤としては、例えば、脂肪族カルボン酸、脂肪族カルボン酸とアルコールとのエステル、数平均分子量２００～１５０００の脂肪族炭化水素化合物、ポリシロキサン系シリコーンオイルなどが挙げられる。
本発明のポリカーボネート樹脂組成物は、離型剤を含有することが好ましい。離型剤としては、例えば、脂肪族カルボン酸、脂肪族カルボン酸とアルコールとのエステル、数平均分子量２００～１５０００の脂肪族炭化水素化合物、ポリシロキサン系シリコーンオイルなどが挙げられる。
脂肪族カルボン酸としては、例えば、飽和または不飽和の脂肪族一価、二価または三価カルボン酸を挙げることができる。ここで脂肪族カルボン酸とは、脂環式のカルボン酸も包含する。これらの中で好ましい脂肪族カルボン酸は、炭素数６～３６の一価または二価カルボン酸であり、炭素数６～３６の脂肪族飽和一価カルボン酸がさらに好ましい。かかる脂肪族カルボン酸の具体例としては、パルミチン酸、ステアリン酸、カプロン酸、カプリン酸、ラウリン酸、アラキン酸、ベヘン酸、リグノセリン酸、セロチン酸、メリシン酸、テトラリアコンタン酸、モンタン酸、アジピン酸、アゼライン酸などが挙げられる。
脂肪族カルボン酸とアルコールとのエステルにおける脂肪族カルボン酸としては、例えば、前記脂肪族カルボン酸と同じものが使用できる。一方、アルコールとしては、例えば、飽和または不飽和の一価または多価アルコールが挙げられる。これらのアルコールは、フッ素原子、アリール基などの置換基を有していてもよい。これらの中では、炭素数３０以下の一価または多価の飽和アルコールが好ましく、炭素数３０以下の脂肪族飽和一価アルコールまたは脂肪族飽和多価アルコールがさらに好ましい。なお、ここで脂肪族とは、脂環式化合物も包含する用語として使用される。
かかるアルコールの具体例としては、オクタノール、デカノール、ドデカノール、ステアリルアルコール、ベヘニルアルコール、エチレングリコール、ジエチレングリコール、グリセリン、ペンタエリスリトール、２，２－ジヒドロキシペルフルオロプロパノール、ネオペンチレングリコール、ジトリメチロールプロパン、ジペンタエリスリトール等が挙げられる。
なお、上記のエステルは、不純物として脂肪族カルボン酸及び／またはアルコールを含有していてもよい。また、上記のエステルは、純物質であってもよいが、複数の化合物の混合物であってもよい。さらに、結合して一つのエステルを構成する脂肪族カルボン酸及びアルコールは、それぞれ、１種を用いてもよく、２種以上を任意の組み合わせ及び比率で併用してもよい。
脂肪族カルボン酸とアルコールとのエステルの具体例としては、蜜ロウ（ミリシルパルミテートを主成分とする混合物）、ステアリン酸ステアリル、ベヘン酸ベヘニル、ベヘン酸ステアリル、グリセリンモノパルミテート、グリセリンモノステアレート、グリセリンジステアレート、グリセリントリステアレート、ペンタエリスリトールモノパルミテート、ペンタエリスリトールモノステアレート、ペンタエリスリトールジステアレート、ペンタエリスリトールトリステアレート、ペンタエリスリトールテトラステアレート等が挙げられる。
数平均分子量２００～１５０００の脂肪族炭化水素としては、例えば、流動パラフィン、パラフィンワックス、マイクロワックス、ポリエチレンワックス、フィッシャ－トロプシュワックス、炭素数３～１２のα－オレフィンオリゴマー等が挙げられる。なお、ここで脂肪族炭化水素としては、脂環式炭化水素も含まれる。また、これらの炭化水素は部分酸化されていてもよい。
これらの中では、パラフィンワックス、ポリエチレンワックスまたはポリエチレンワックスの部分酸化物が好ましく、パラフィンワックス、ポリエチレンワックスがさらに好ましい。
また、前記の脂肪族炭化水素の数平均分子量は、好ましくは５０００以下である。
なお、脂肪族炭化水素は、単一物質であってもよいが、構成成分や分子量が様々なものの混合物であっても、主成分が上記の範囲内であれば使用できる。
これらの中では、パラフィンワックス、ポリエチレンワックスまたはポリエチレンワックスの部分酸化物が好ましく、パラフィンワックス、ポリエチレンワックスがさらに好ましい。
また、前記の脂肪族炭化水素の数平均分子量は、好ましくは５０００以下である。
なお、脂肪族炭化水素は、単一物質であってもよいが、構成成分や分子量が様々なものの混合物であっても、主成分が上記の範囲内であれば使用できる。
ポリシロキサン系シリコーンオイルとしては、例えば、ジメチルシリコーンオイル、メチルフェニルシリコーンオイル、ジフェニルシリコーンオイル、フッ素化アルキルシリコーン等が挙げられる。
なお、上述した離型剤は、１種が含有されていてもよく、２種以上が任意の組み合わせ及び比率で含有されていてもよい。
離型剤の含有量は、ポリカーボネート樹脂（Ａ）１００質量部に対して、通常０．００１質量部以上、好ましくは０．０１質量部以上であり、また、通常２質量部以下、好ましくは１質量部以下である。離型剤の含有量が前記範囲の下限値未満の場合は、離型性の効果が十分でない場合があり、離型剤の含有量が前記範囲の上限値を超える場合は、耐加水分解性の低下、射出成形時の金型汚染などが生じる可能性がある。
［添加剤等］
ポリカーボネート樹脂組成物は、上記した以外のその他の添加剤、例えば、紫外線吸収剤、充填材、強化材（炭素繊維、ガラス繊維）、顔料、染料、難燃剤、帯電防止剤、可塑剤、相溶化剤などの添加剤、またポリカーボネート樹脂（Ａ）、ポリスチレン系樹脂（Ｂ）以外の他の樹脂を含有することができる。これらの添加剤あるいは他の樹脂は一種または二種以上を配合してもよい。
なお、上記したポリカーボネート樹脂（Ａ）及びポリスチレン系樹脂（Ｂ）以外の他の樹脂を含有する場合の含有量は、ポリカーボネート樹脂（Ａ）１００質量部に対し、４０質量部以下とすることが好ましく、より好ましくは３０質量部以下、さらには２０質量部以下、１０質量部以下、特には５質量部以下とすることが好ましい。
ポリカーボネート樹脂組成物は、上記した以外のその他の添加剤、例えば、紫外線吸収剤、充填材、強化材（炭素繊維、ガラス繊維）、顔料、染料、難燃剤、帯電防止剤、可塑剤、相溶化剤などの添加剤、またポリカーボネート樹脂（Ａ）、ポリスチレン系樹脂（Ｂ）以外の他の樹脂を含有することができる。これらの添加剤あるいは他の樹脂は一種または二種以上を配合してもよい。
なお、上記したポリカーボネート樹脂（Ａ）及びポリスチレン系樹脂（Ｂ）以外の他の樹脂を含有する場合の含有量は、ポリカーボネート樹脂（Ａ）１００質量部に対し、４０質量部以下とすることが好ましく、より好ましくは３０質量部以下、さらには２０質量部以下、１０質量部以下、特には５質量部以下とすることが好ましい。
［ポリカーボネート樹脂組成物の製造方法］
ポリカーボネート樹脂組成物の製造方法に制限はなく、公知のポリカーボネート樹脂組成物の製造方法を広く採用でき、各必須成分、並びに、必要に応じて配合されるその他の成分を、例えばタンブラーやヘンシェルミキサーなどの各種混合機を用い予め混合した後、バンバリーミキサー、ロール、ブラベンダー、単軸混練押出機、二軸混練押出機、ニーダーなどの混合機で溶融混練する方法が挙げられる。なお、溶融混練の温度は特に制限されないが、通常２４０～３２０℃の範囲である。
ポリカーボネート樹脂組成物の製造方法に制限はなく、公知のポリカーボネート樹脂組成物の製造方法を広く採用でき、各必須成分、並びに、必要に応じて配合されるその他の成分を、例えばタンブラーやヘンシェルミキサーなどの各種混合機を用い予め混合した後、バンバリーミキサー、ロール、ブラベンダー、単軸混練押出機、二軸混練押出機、ニーダーなどの混合機で溶融混練する方法が挙げられる。なお、溶融混練の温度は特に制限されないが、通常２４０～３２０℃の範囲である。
上記したポリカーボネート樹脂組成物をペレタイズしたペレットは、各種の成形法で成形し、成形体が製造できる。またペレットを経由せずに、押出機で溶融混練された樹脂を直接、成形して成形体にすることもできる。
成形体を製造する方法は、ポリカーボネート樹脂組成物について一般に採用されている成形法を任意に採用できる。その例を挙げると、射出成形法、超高速射出成形法、射出圧縮成形法、二色成形法、ガスアシスト等の中空成形法、断熱金型を使用した成形法、急速加熱金型を使用した成形法、発泡成形（超臨界流体も含む）、インサート成形、ＩＭＣ（インモールドコーティング成形）成形法、押出成形法、シート成形法、熱成形法、回転成形法、積層成形法、プレス成形法、ブロー成形法などが挙げられ、また、ホットランナー方式を使用した成形法を用いることも出来る。
これらの中でも、射出成形法、超高速射出成形法、射出圧縮成形法などの射出成形法が好ましい。
成形体を製造する方法は、ポリカーボネート樹脂組成物について一般に採用されている成形法を任意に採用できる。その例を挙げると、射出成形法、超高速射出成形法、射出圧縮成形法、二色成形法、ガスアシスト等の中空成形法、断熱金型を使用した成形法、急速加熱金型を使用した成形法、発泡成形（超臨界流体も含む）、インサート成形、ＩＭＣ（インモールドコーティング成形）成形法、押出成形法、シート成形法、熱成形法、回転成形法、積層成形法、プレス成形法、ブロー成形法などが挙げられ、また、ホットランナー方式を使用した成形法を用いることも出来る。
これらの中でも、射出成形法、超高速射出成形法、射出圧縮成形法などの射出成形法が好ましい。
更に、前記成形品の表面には、ハードコート層を設けてもよい。ハードコート層を形成するためのハードコート剤としては、公知の材料を適宜使用することができ、例えば、シリコーン系、アクリル系、シラザン系、ウレタン系などの種々のハードコート剤を使用することができる。接着性や耐候性を向上させるために、ハードコート剤を塗布する前にプライマー層を設ける２コートタイプのハードコート剤であってもよい。ハードコート剤のコーティング方法としては、特に制限はないが、スプレーコート、ディップコート、フローコート、スピンコート、バーコート、カーテンコート、ダイコート、グラビアコート、ロールコート、ブレードコート及びエアーナイフコート等のいずれの塗工方法によって塗布することもできる。
ハードコート層の厚みは、好ましくは１～５０μｍ、より好ましくは５～３０μｍである。
ハードコート層の厚みは、好ましくは１～５０μｍ、より好ましくは５～３０μｍである。
本発明のポリカーボネート樹脂組成物は、誘電正接が小さく、周波数５．８ＧＨｚでの誘電正接が好ましくは０．００４０以下であり、より好ましくは０．００３６以下、さらに好ましくは０．００３４以下、特に好ましくは０．００３２以下である。
また、本発明のポリカーボネート樹脂組成物の比誘電率も小さく、比誘電率は好ましくは２．８以下であり、より好ましくは２．７以下、更に好ましくは２．６以下である。
誘電正接および比誘電率の具体的な測定方法の詳細は、実施例に記載の通りである。
また、本発明のポリカーボネート樹脂組成物の比誘電率も小さく、比誘電率は好ましくは２．８以下であり、より好ましくは２．７以下、更に好ましくは２．６以下である。
誘電正接および比誘電率の具体的な測定方法の詳細は、実施例に記載の通りである。
また、本発明のポリカーボネート樹脂組成物は耐熱性に優れ、その指標となる荷重たわみ温度が、好ましくは８８℃超であり、より好ましくは９０℃以上である。荷重たわみ温度の測定はＩＳＯ７５－２に準拠して行い、その具体的な測定方法の詳細は、実施例に記載する通りである。
また、本発明のポリカーボネート樹脂組成物は耐衝撃性に優れ、シャルピー衝撃強度が、ノッチなしでＮＢ（ノンブレーク）、ノッチ付きで２０ｋＪ／ｍ２以上であることが好ましい。シャルピー衝撃強度の測定はＩＳＯ１７９－１，２に準拠して行い、その具体的な測定方法の詳細は、実施例に記載する通りである。
さらに、本発明のポリカーボネート樹脂組成物は剛性に優れ、曲げ弾性率が２０００ＭＰａ以上、曲げ強度が６７Ｐａ以上であることが好ましい。曲げ弾性率と曲げ強度の測定は、ＩＳＯ１７８に準拠して行い、その具体的な方法の詳細は、実施例に記載する通りである。
また、本発明のポリカーボネート樹脂組成物は耐衝撃性に優れ、シャルピー衝撃強度が、ノッチなしでＮＢ（ノンブレーク）、ノッチ付きで２０ｋＪ／ｍ２以上であることが好ましい。シャルピー衝撃強度の測定はＩＳＯ１７９－１，２に準拠して行い、その具体的な測定方法の詳細は、実施例に記載する通りである。
さらに、本発明のポリカーボネート樹脂組成物は剛性に優れ、曲げ弾性率が２０００ＭＰａ以上、曲げ強度が６７Ｐａ以上であることが好ましい。曲げ弾性率と曲げ強度の測定は、ＩＳＯ１７８に準拠して行い、その具体的な方法の詳細は、実施例に記載する通りである。
本発明のポリカーボネート樹脂組成物は、好ましくは、特に周波数１ＧＨｚ以上の電磁波を使用する電子電気機器部品に用いられる。本発明のポリカーボネート樹脂組成物からな電子電気機器部品は、特に周波数１ＧＨｚ以上の広い範囲の帯域に利用可能である。５Ｇの無線通信規格の「ＮＲ」の５２．６ＧＨｚまでの周波数帯、今後の５Ｇ ｅｖｏｌｕｔｉｏｎで利用が検討されている９０ＧＨｚ程度まで、あるいは６Ｇに向けての９０Ｇ～３００ＧＨｚといったサブテラヘルツ波にも適応可能である。もちろん、既存の低周波帯や、６Ｇローバンド／ミッドバンドの１０～２０ＧＨｚというような帯域にも好適である。
本発明のポリカーボネート樹脂組成物の成形品が利用可能な電子電気機器部品には、電子電気機器の筐体、回路基板、半導体層間絶縁膜、アンテナ部品（基板、アンテナカバー、レーダーカバー）、高周波同軸ケーブルの絶縁材料抵抗器、スイッチ、コンデンサ、フォトセンサ等のベース部品、ＩＣソケットやコネクタ、自動車、自転車、オートバイ、トラック、鉄道車両、ヘリコプター、航空機等の輸送機器、ブルドーザー、油圧ショベル、クレーン等の建設機械、商船、特殊用途船、漁船、艦艇等の船舶、トラクター、収穫機等の農業機械、スマートフォン、タブレット、ウェアラブルデバイス、コンピュータ、テレビジョン受像機、ＶＲゴーグル、カメラ、スピーカー、ドローン、ロボット、センサー、医療機器、分析機器等の部品を挙げることができ、特にアンテナの基板やアンテナカバー、レーダーカバーとして特に好適である。
アンテナカバー、レーダー用カバーは、電磁波を送信もしくは受信するアンテナモジュールを格納または保護するハウジング、アンテナカバー（レドーム）等であり、さらにはレーダーモジュールから送受信される電磁波の経路上に設置される部材などを含む。
アンテナカバー、レーダー用カバーは、電磁波を送信もしくは受信するアンテナモジュールを格納または保護するハウジング、アンテナカバー（レドーム）等であり、さらにはレーダーモジュールから送受信される電磁波の経路上に設置される部材などを含む。
以下、本発明を実施例により、更に具体的に説明する。ただし、本発明は以下の実施例に限定して解釈されるものではない。
以下の実施例及び比較例で使用した原料は以下の表１の通りである。
以下の実施例及び比較例で使用した原料は以下の表１の通りである。
（実施例１～１９、比較例１～７）
［ポリカーボネート樹脂組成物ペレットの製造］
上記表１に記載した各成分を、以下の表２－４に記した割合（質量部）で配合し、タンブラーにて２０分混合した後、二軸押出機（東芝機械株式会社製、ＴＥＭ２６ＳＸ）を用いて、シリンダー温度２６０℃で溶融混練し、ストランドカットによりポリカーボネート樹脂組成物のペレットを得た。
［ポリカーボネート樹脂組成物ペレットの製造］
上記表１に記載した各成分を、以下の表２－４に記した割合（質量部）で配合し、タンブラーにて２０分混合した後、二軸押出機（東芝機械株式会社製、ＴＥＭ２６ＳＸ）を用いて、シリンダー温度２６０℃で溶融混練し、ストランドカットによりポリカーボネート樹脂組成物のペレットを得た。
＜比誘電率、誘電正接＞
上述の方法で得られたペレットを、１００℃で５時間乾燥させた後、射出成形機（ファナック社ＲＯＢＯＳＨＯＴ Ｓ－２０００ｉ １５０Ｂ）を用いて、１００ｍｍ×１５０ｍｍ×厚みが約２ｍｍの成形品を得た。上記方法によって得られた平板状試験片から１００ｍｍ×１ｍｍ×２ｍｍの平板状試験片を切削により得た後、ＫＥＹＳＩＧＨＴ社製、ネットワークアナライザおよび関東電子応用開発社製、空洞共振器を用いて、摂動法により周波数５．８ＧＨｚにおける比誘電率と誘電正接を測定した。
上述の方法で得られたペレットを、１００℃で５時間乾燥させた後、射出成形機（ファナック社ＲＯＢＯＳＨＯＴ Ｓ－２０００ｉ １５０Ｂ）を用いて、１００ｍｍ×１５０ｍｍ×厚みが約２ｍｍの成形品を得た。上記方法によって得られた平板状試験片から１００ｍｍ×１ｍｍ×２ｍｍの平板状試験片を切削により得た後、ＫＥＹＳＩＧＨＴ社製、ネットワークアナライザおよび関東電子応用開発社製、空洞共振器を用いて、摂動法により周波数５．８ＧＨｚにおける比誘電率と誘電正接を測定した。
＜曲げ弾性率、曲げ強度＞
上述の方法で得られたペレットを１００℃で５時間乾燥した後、日精樹脂工業社製のＮＥＸ８０ＩＩＩ型射出成形機を用いて、シリンダー温度２６０℃、金型温度８０℃、成形サイクル５０秒の条件で射出成形を行い、ＩＳＯ多目的試験片（４ｍｍ厚）を成形した。得られた試験片を用い、室温（２３℃）条件下でＩＳＯ－１７８規格に基づき、曲げ試験を行い、曲げ弾性率（単位：ＭＰａ）、曲げ強度（単位：ＭＰａ）を測定した。
上述の方法で得られたペレットを１００℃で５時間乾燥した後、日精樹脂工業社製のＮＥＸ８０ＩＩＩ型射出成形機を用いて、シリンダー温度２６０℃、金型温度８０℃、成形サイクル５０秒の条件で射出成形を行い、ＩＳＯ多目的試験片（４ｍｍ厚）を成形した。得られた試験片を用い、室温（２３℃）条件下でＩＳＯ－１７８規格に基づき、曲げ試験を行い、曲げ弾性率（単位：ＭＰａ）、曲げ強度（単位：ＭＰａ）を測定した。
＜シャルピー衝撃強度＞
上述の方法で得られたペレットを１００℃で５時間乾燥した後、日精樹脂工業社製のＮＥＸ８０ＩＩＩ型射出成形機を用いて、シリンダー温度２６０℃、金型温度８０℃、成形サイクル５０秒の条件で射出成形を行い、ＩＳＯ１７９－１、２に基づく３ｍｍ厚の耐衝撃性試験片を作製した。得られた試験片を用い、２３℃の温度環境下において、ノッチ無し、及びノッチ付きシャルピー衝撃強度（単位：ｋＪ／ｍ２）を測定した。
上述の方法で得られたペレットを１００℃で５時間乾燥した後、日精樹脂工業社製のＮＥＸ８０ＩＩＩ型射出成形機を用いて、シリンダー温度２６０℃、金型温度８０℃、成形サイクル５０秒の条件で射出成形を行い、ＩＳＯ１７９－１、２に基づく３ｍｍ厚の耐衝撃性試験片を作製した。得られた試験片を用い、２３℃の温度環境下において、ノッチ無し、及びノッチ付きシャルピー衝撃強度（単位：ｋＪ／ｍ２）を測定した。
＜荷重たわみ温度＞
上述の方法で得られたペレットを１００℃で５時間乾燥した後、日精樹脂工業社製のＮＥＸ８０ＩＩＩ型射出成形機を用いて、シリンダー温度２６０℃、金型温度８０℃、成形サイクル５０秒の条件で射出成形を行い、ＩＳＯ多目的試験片（４ｍｍ厚）を成形した。得られた試験片を用い、東洋精機社製６Ａ－２型ＨＤＴ測定装置を用いて、ＩＳＯ７５－２に準拠し、高荷重（１．８０ＭＰａ）の条件で荷重たわみ温度（単位：℃）を測定した。
以上の評価結果を以下の表２～４に示す。
上述の方法で得られたペレットを１００℃で５時間乾燥した後、日精樹脂工業社製のＮＥＸ８０ＩＩＩ型射出成形機を用いて、シリンダー温度２６０℃、金型温度８０℃、成形サイクル５０秒の条件で射出成形を行い、ＩＳＯ多目的試験片（４ｍｍ厚）を成形した。得られた試験片を用い、東洋精機社製６Ａ－２型ＨＤＴ測定装置を用いて、ＩＳＯ７５－２に準拠し、高荷重（１．８０ＭＰａ）の条件で荷重たわみ温度（単位：℃）を測定した。
以上の評価結果を以下の表２～４に示す。
上記結果から明らかな通り、本発明のポリカーボネート樹脂組成物は、機械物性（耐衝撃性、剛性、硬度、耐熱性等）に優れ、電気特性（比誘電率、誘電正接）にも優れる。これに対し、比較例の場合は、機械物性と電気特性を両立する結果は得られなかった。
本発明のポリカーボネート樹脂組成物は、比誘電率及び誘電正接が共に低く、高度の耐衝撃性を有し、耐熱性、剛性及び硬度にも優れるので、電磁波を使用する各種の電子電気機器部品に広く好適に利用できる。また、本発明のポリカーボネート樹脂組成物からなる成形体は、比誘電率及び誘電正接が共に低く、透過減衰量が低減され、耐熱性、耐衝撃性及び剛性に優れるので、特に周波数１ＧＨｚ以上の電磁波を使用する各種のアンテナ用部材として、広く好適に利用できる。
Claims (7)
- ポリカーボネート樹脂（Ａ）１００質量部に対し、ポリスチレン系樹脂（Ｂ）を３０～１５０質量部、及びエラストマー（Ｃ）を３～６０質量部含み、ポリカーボネート樹脂（Ａ）はビスフェノールＡ型ポリカーボネート（Ａ１）と下記式（１）で表される構成単位を有するポリカーボネート（Ａ２）を含み、両者の含有量の質量比（Ａ２／Ａ１）が５／９５～８０／２０であることを特徴とするポリカーボネート樹脂組成物。
- エラストマー（Ｃ）が、ブタジエン／メチル（メタ）アクリレート共重合体、ブタジエン／メチル（メタ）アクリレート／スチレン共重合体、およびスチレン／エチレン／ブチレン／スチレン共重合体から選ばれる１種または２種以上である請求項１に記載のポリカーボネート樹脂組成物。
- 周波数５．８ＧＨｚでの誘電正接が０．００４０以下である請求項１または２に記載のポリカーボネート樹脂組成物。
- ポリスチレン系樹脂（Ｂ）とエラストマー（Ｃ）の含有量の比［（Ｂ）／（Ｃ）］が９以下である請求項１～３のいずれかに記載のポリカーボネート樹脂組成物。
- アクリロニトリル－ブタジエン－スチレン共重合体を含有しないか、含有する場合の含有量が、ポリカーボネート樹脂（Ａ）１００質量部に対し、１０質量部以下である請求項１～４のいずれかに記載のポリカーボネート樹脂組成物。
- 請求項１～５のいずれかに記載のポリカーボネート樹脂組成物の成形品。
- アンテナ用部材である請求項６に記載の成形品。