WO2023162636A1 - 熱伝導性シリコーン組成物 - Google Patents
熱伝導性シリコーン組成物 Download PDFInfo
- Publication number
- WO2023162636A1 WO2023162636A1 PCT/JP2023/003586 JP2023003586W WO2023162636A1 WO 2023162636 A1 WO2023162636 A1 WO 2023162636A1 JP 2023003586 W JP2023003586 W JP 2023003586W WO 2023162636 A1 WO2023162636 A1 WO 2023162636A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- thermally conductive
- silicone composition
- conductive silicone
- component
- mass
- Prior art date
Abstract
本発明は、(A)1分子中に少なくとも2個のアルケニル基を有するオルガノポリシロキサン:100質量部、(B)1分子中に少なくとも2個のケイ素原子結合水素原子を有するオルガノハイドロジェンポリシロキサン:(B)成分の(Si-H基の個数)/(A)成分の(アルケニル基の個数)が0.5~3.0となる量、(C)熱伝導性粉末を一種類以上含む充填剤:800~20,000質量部、(D)式(1)の加水分解性オルガノポリシロキサン:20~400質量部、(E)式(2)R2 bSi(OR3)4-bで示されるオルガノシラン:0.01~100質量部、(F)白金又は白金化合物:白金原子が(A)成分の0.1~500ppm、(G)反応制御剤:0.01~1質量部を含む熱伝導性シリコーン組成物である。これにより、高温高湿下でも熱抵抗値が悪化せず、高温下でも高弾性率化せず、ボイドが発生しない高い熱伝導率の熱伝導性シリコーン組成物が提供される。
Description
本発明は、熱伝導性シリコーン組成物(熱伝導性付加硬化型シリコーン組成物)に関する。
プリント配線基板上に実装される電子部品であるCPU等のICパッケージは、使用時の発熱による温度上昇によって性能が低下したり破損したりすることがあるため、従来、ICパッケージと放熱フィン等の間に熱伝導性のよい放熱シートや放熱グリースが用いられている(特許文献1~特許文献6)。
特に放熱グリースはCPUや放熱フィン等の部材表面の凹凸に影響されることなく、それら被着面に追随、密着できるため高い性能を発揮することが出来る。近年では、高い放熱性能が必要となるため、多量の熱伝導性フィラーを充填した放熱グリースが使用される傾向にあるが、多量のフィラーを充填しているために、高温高湿下に曝らされると、放熱グリースの劣化が進行してしまい、被覆面への追従や密着が不十分になり、熱抵抗値が悪化したり、ボイドが発生してしまう問題があった。
本発明は、上記事情を改善したもので、高温高湿下に曝されても熱抵抗値が悪化せず、高温下に曝されても高弾性率化せず、ボイドが発生しない高い熱伝導率をもつ熱伝導性シリコーン組成物を提供することを目的とする。
上記課題を解決するために、本発明では、
(A)1分子中に少なくとも2個のアルケニル基を有するオルガノポリシロキサン:100質量部
(B)1分子中に少なくとも2個のケイ素原子結合水素原子を有するオルガノハイドロジェンポリシロキサン:前記(B)成分のSi-H基の個数と、前記(A)成分のアルケニル基の個数比(Si-H基の個数)/(アルケニル基の個数)が0.5~3.0となる量
(C)熱伝導性粉末を一種類以上含む充填剤:800~20,000質量部
(D)下記一般式(1)で表される加水分解性オルガノポリシロキサン:20~400質量部
(式中のR1は置換基を有していても良い炭素数1~10の1価炭化水素基を表し、それぞれのR1は同一であっても異なっていても良い。また、aは5~100である。)
(E)下記一般式(2)で示されるオルガノシラン:0.01~100質量部
R2 bSi(OR3)4-b (2)
(式中、R2は炭素数14~20の、置換基を有していてもよい飽和又は不飽和の一価炭化水素基、エポキシ基、(メタ)アクリル基の中から選択される1種類以上の基であり、R3は炭素数1~6のアルキル基である。bは1~3の整数である。)
(F)白金又は白金化合物の触媒:白金原子として前記(A)成分の0.1~500ppmとなる量
(G)反応制御剤:0.01~1質量部
を含む熱伝導性シリコーン組成物を提供する。
(A)1分子中に少なくとも2個のアルケニル基を有するオルガノポリシロキサン:100質量部
(B)1分子中に少なくとも2個のケイ素原子結合水素原子を有するオルガノハイドロジェンポリシロキサン:前記(B)成分のSi-H基の個数と、前記(A)成分のアルケニル基の個数比(Si-H基の個数)/(アルケニル基の個数)が0.5~3.0となる量
(C)熱伝導性粉末を一種類以上含む充填剤:800~20,000質量部
(D)下記一般式(1)で表される加水分解性オルガノポリシロキサン:20~400質量部
(E)下記一般式(2)で示されるオルガノシラン:0.01~100質量部
R2 bSi(OR3)4-b (2)
(式中、R2は炭素数14~20の、置換基を有していてもよい飽和又は不飽和の一価炭化水素基、エポキシ基、(メタ)アクリル基の中から選択される1種類以上の基であり、R3は炭素数1~6のアルキル基である。bは1~3の整数である。)
(F)白金又は白金化合物の触媒:白金原子として前記(A)成分の0.1~500ppmとなる量
(G)反応制御剤:0.01~1質量部
を含む熱伝導性シリコーン組成物を提供する。
このような熱伝導性シリコーン組成物であれば、高温高湿下に曝されても熱抵抗値が高くなって悪化せず、高温下に曝されても高弾性率化せず、ボイドが発生しない高い熱伝導率をもつ熱伝導性シリコーン組成物を提供することができる。
また、前記(A)成分の粘度は25℃で10~100,000mm2/sであることが好ましい。
このような熱伝導性シリコーン組成物であれば、保存安定性が良く、伸展性も良好である。
また、前記(C)成分はアルミニウム粉末と酸化亜鉛粉末を含むことが好ましい。
このような熱伝導性シリコーン組成物であれば、安定性が良く、オイル分離が起こらない。
また、前記(E)成分の前記R2は炭素数14~20のアルキル基であることが好ましい。
このような熱伝導性シリコーン組成物であれば、揮発し難くて高温下でボイドが発生せず、取り扱いし易くて低温特性が低下しない。
また、前記(E)成分の前記R2は炭素数16~20のアルキル基であることが好ましい。
このような熱伝導性シリコーン組成物であれば、更に揮発し難くて高温下でボイドが発生せず、取り扱いし易くて低温特性が低下しない。
また、前記(G)成分はアセチレン化合物、窒素化合物、有機りん化合物、オキシム化合物、及び有機クロロ化合物のいずれか一つ以上を含むものであることが好ましい。
このような熱伝導性シリコーン組成物であれば、室温でのヒドロシリル化反応の進行を抑え、シェルフライフ、ポットライフを延長させることができる。
また、前記熱伝導性シリコーン組成物は、25℃における粘度が50~1,000Pa・sの範囲のものであることが好ましい。
このような熱伝導性シリコーン組成物であれば、保存時に熱伝導性充填剤が沈降しないため不均一にならず、伸展性があり作業効率が落ちない。
また、前記熱伝導性シリコーン組成物は、その硬化物が、高速加速寿命試験(130℃、湿度85%、96h)後でも、熱抵抗値が、高速加速寿命試験前と比べて1.5mm2・K/W以上高くならないものであることが好ましい。
このような熱伝導性シリコーン組成物であれば、長期的に熱抵抗性能を持続することができる。
また、前記熱伝導性シリコーン組成物は、前記熱伝導性シリコーン組成物をガラス板2枚に挟み、150℃、60分で硬化させた硬化物が、260℃で5分間加熱する工程を5回繰り返した後にボイドが観測されないものであることが好ましい。
このような熱伝導性シリコーン組成物であれば、高温下でもボイドの発生を抑制することができる。
また、前記熱伝導性シリコーン組成物は、その硬化物が、25℃においてAskerCで10以上の硬度のものであることが好ましい。
このような熱伝導性シリコーン組成物であれば、加熱後の硬化物が脆くならず破損しない。
また、前記熱伝導性シリコーン組成物の硬化物が、260℃のチャンバーに5分間入れた後に取り出す工程を3回繰り返す加熱試験を実施しても、前記加熱試験実施前から引張弾性率が20MPa以上上昇しないものであることが好ましい。
このような熱伝導性シリコーン組成物であれば、高温下に曝されても引張弾性率が高くなることを抑制できる。
以上のように、本発明の熱伝導性シリコーン組成物であれば、高温高湿下に曝されても熱抵抗値が悪化せず、高温下に曝されても高弾性率化せず、ボイドが発生しない高い熱伝導率をもつ熱伝導性シリコーン組成物を提供することができる。
上述のように、高温高湿下に曝されても熱抵抗値が上昇して悪化せず、高温下に曝されても高弾性率化せず、ボイドが発生しない高い熱伝導率をもつ熱伝導性シリコーン組成物とその硬化物の開発が求められていた。
本発明者らは、上記課題について鋭意検討を重ねた結果、上記目的を達成するために、(A)1分子中に少なくとも2個のアルケニル基を有するオルガノポリシロキサンと、(B)1分子中に少なくとも2個のケイ素原子結合水素原子を有するオルガノハイドロジェンポリシロキサンを含む付加反応硬化型のシリコーン組成物において、熱伝導性粉末を一種類以上含む充填剤を配合し、かつ一般式(2)で示される長鎖アルキル基を有するオルガノシランを配合することにより、充填剤の充填量を増加でき、その結果十分な熱伝導率が得られると共に、高温高湿下に曝されても熱抵抗値が悪化せず、高温下に曝されてもボイドが発生しない熱伝導性シリコーン組成物が得られることを見出し、本発明を完成させた。
即ち、本発明は、
(A)1分子中に少なくとも2個のアルケニル基を有するオルガノポリシロキサン:100質量部
(B)1分子中に少なくとも2個のケイ素原子結合水素原子を有するオルガノハイドロジェンポリシロキサン:前記(B)成分のSi-H基の個数と、前記(A)成分のアルケニル基の個数比(Si-H基の個数)/(アルケニル基の個数)が0.5~3.0となる量
(C)熱伝導性粉末を一種類以上含む充填剤:800~20,000質量部
(D)下記一般式(1)で表される加水分解性オルガノポリシロキサン:20~400質量部
(式中のR1は置換基を有していても良い炭素数1~10の1価炭化水素基を表し、それぞれのR1は同一であっても異なっていても良い。また、aは5~100である。)
(E)下記一般式(2)で示されるオルガノシラン:0.01~100質量部
R2 bSi(OR3)4-b (2)
(式中、R2は炭素数14~20の、置換基を有していてもよい飽和又は不飽和の一価炭化水素基、エポキシ基、(メタ)アクリル基の中から選択される1種類以上の基であり、R3は炭素数1~6のアルキル基である。bは1~3の整数である。)
(F)白金又は白金化合物の触媒:白金原子として前記(A)成分の0.1~500ppmとなる量
(G)反応制御剤:0.01~1質量部
を含む熱伝導性シリコーン組成物である。
(A)1分子中に少なくとも2個のアルケニル基を有するオルガノポリシロキサン:100質量部
(B)1分子中に少なくとも2個のケイ素原子結合水素原子を有するオルガノハイドロジェンポリシロキサン:前記(B)成分のSi-H基の個数と、前記(A)成分のアルケニル基の個数比(Si-H基の個数)/(アルケニル基の個数)が0.5~3.0となる量
(C)熱伝導性粉末を一種類以上含む充填剤:800~20,000質量部
(D)下記一般式(1)で表される加水分解性オルガノポリシロキサン:20~400質量部
(E)下記一般式(2)で示されるオルガノシラン:0.01~100質量部
R2 bSi(OR3)4-b (2)
(式中、R2は炭素数14~20の、置換基を有していてもよい飽和又は不飽和の一価炭化水素基、エポキシ基、(メタ)アクリル基の中から選択される1種類以上の基であり、R3は炭素数1~6のアルキル基である。bは1~3の整数である。)
(F)白金又は白金化合物の触媒:白金原子として前記(A)成分の0.1~500ppmとなる量
(G)反応制御剤:0.01~1質量部
を含む熱伝導性シリコーン組成物である。
以下、本発明について詳細に説明するが、本発明はこれらに限定されるものではない。
[熱伝導性シリコーン組成物]
((A)成分)
本発明の熱伝導性シリコーン組成物を構成する(A)成分のオルガノポリシロキサンは、ケイ素原子に直結したアルケニル基を1分子中に少なくとも2個有するもので、直鎖状でも分岐状でもよく、また2種以上の異なる粘度の混合物でもよい。
((A)成分)
本発明の熱伝導性シリコーン組成物を構成する(A)成分のオルガノポリシロキサンは、ケイ素原子に直結したアルケニル基を1分子中に少なくとも2個有するもので、直鎖状でも分岐状でもよく、また2種以上の異なる粘度の混合物でもよい。
アルケニル基としては、ビニル基、アリル基、プロペニル基、イソプロペニル基、1-ブテニル基、1-ヘキセニル基、シクロヘキセニル基、オクテニル基等が挙げられる。これらの基の水素原子の一部又は全部をフッ素、臭素、塩素等のハロゲン原子、シアノ基等で置換したもの、例えばクロロメチル基、クロロプロピル基、ブロモエチル基、3,3,3-トリフロロプロピル基、シアノエチル基等も例示される。合成の容易さ、コストの面から特に好ましくはビニル基である。
ケイ素原子に結合する残余の官能基としては、メチル基、エチル基、プロピル基、イソプロピル基、ブチル基、イソブチル基、tert-ブチル基、ペンチル基、ネオペンチル基、ヘキシル基、シクロヘキシル基、オクチル基、ノニル基、デシル基、ドデシル基等のアルキル基、フェニル基、トリル基、キシリル基、ナフチル基等のアリール基、ベンジル基、フェニルエチル基、2-フェニルプロピル基等のアラルキル基が例示される。これらのうち、合成の容易さ、コストの面からメチル基が特に好ましい。
この場合、少なくとも2個はアルケニル基(特に炭素数2~8のものが好ましく、更に好ましくは2~6である)であることが必要である。アルケニル基の個数の上限は、特に限定されないが、(A)成分のオルガノポリシロキサンの分子の組成に応じて決まるものであり、典型的には9個である。このアルケニル基は、分子鎖末端のケイ素原子に結合していても、分子鎖途中のケイ素原子に結合していても、両者に結合していてもよいが、組成物の硬化速度、硬化物の物性等の点から、本発明で用いるオルガノポリシロキサンは、少なくとも分子鎖末端のケイ素原子に結合したアルケニル基を含んだものであることが好ましい。
上記(A)成分のオルガノポリシロキサンの25℃における粘度は、特に限定されないが、10mm2/s以上であれば組成物の保存安定性が良く、100,000mm2/s以下であれば得られる組成物の伸展性が良好であるため、10~100,000mm2/sの範囲が好ましく、より好ましくは100~80,000mm2/sの範囲である。
本発明において、動粘度は、ウベローデ型オストワルド粘度計により測定した25℃における値である(以下、同じ)。
本発明において、動粘度は、ウベローデ型オストワルド粘度計により測定した25℃における値である(以下、同じ)。
((B)成分)
(B)成分は、下記平均組成式(3)で表され、1分子中に少なくとも2個のケイ素原子結合水素原子を有するオルガノハイドロジェンポリシロキサンである。このオルガノハイドロジェンポリシロキサンが1分子中に有するケイ素原子結合水素原子は、好ましくは3~100個、より好ましくは3~50個、さらにより好ましくは3~20個である。
R4 cHdSiO(4-c-d)/2 (3)
(式中、R4は脂肪族不飽和結合を有さない非置換又は置換の1価炭化水素基であり、また、cは0.7~2.2、dは0.001~0.5で、かつc+dが0.8~2.5を満足する正数である。)
(B)成分は、下記平均組成式(3)で表され、1分子中に少なくとも2個のケイ素原子結合水素原子を有するオルガノハイドロジェンポリシロキサンである。このオルガノハイドロジェンポリシロキサンが1分子中に有するケイ素原子結合水素原子は、好ましくは3~100個、より好ましくは3~50個、さらにより好ましくは3~20個である。
R4 cHdSiO(4-c-d)/2 (3)
(式中、R4は脂肪族不飽和結合を有さない非置換又は置換の1価炭化水素基であり、また、cは0.7~2.2、dは0.001~0.5で、かつc+dが0.8~2.5を満足する正数である。)
上記式(3)中、R4は独立に脂肪族不飽和結合を含まない非置換又は置換の1価炭化水素基であり、その炭素原子数は、特に限定されないが、好ましくは通常1~10、より好ましくは1~6である。その具体例としては、メチル基、エチル基、プロピル基、イソプロピル基、ブチル基、イソブチル基、tert-ブチル基、ペンチル基、ネオペンチル基、へキシル基、シクロヘキシル基、オクチル基、ノニル基、デシル基等のアルキル基;フェニル基、トリル基、キシリル基、ナフチル基等のアリール基;ベンジル基、フェニルエチル基、フェニルプロピル基等のアラルキル基;これらの基の水素原子の一部又は全部を、塩素、臭素、フッ素等のハロゲン原子で置換した3,3,3-トリフルオロプロピル基等が挙げられる。中でも好ましくはアルキル基、アリール基、3,3,3-トリフルオロプロピル基であり、より好ましくはメチル基、フェニル基、3,3,3-トリフルオロプロピル基である。
また、cは0.7~2.2の正数であることが好ましく、1.0~2.1の正数であることがより好ましい。dは0.001~0.5の正数であることが好ましく、0.005~0.1の正数であることがより好ましい。c+dは0.8~2.5の範囲であることが好ましく、1.0~2.5の範囲を満たすことがより好ましく、1.5~2.2の範囲を満たすことがさらにより好ましい。
(B)成分のオルガノハイドロジェンポリシロキサンの1分子中のケイ素原子の数(即ち、重合度)は、特に限定されないが、通常10~1,000個が好ましく、組成物の取扱作業性及び得られる硬化物の特性が良好となる点から、より好ましくは20~500個、さらにより好ましくは20~100個である。
(B)成分のオルガノハイドロジェンポリシロキサンの分子構造は、上記要件を満たすものであれば特に限定されず、(B)成分のオルガノハイドロジェンポリシロキサンの粘度も特に限定されないが、通常、1~10,000mPa・sが好ましく、より好ましくは3~2,000mPa・s、さらにより好ましくは10~1,000mPa・sであり、室温(25℃)で液状のものが望ましい。
上記式(3)で表されるオルガノハイドロジェンポリシロキサンとしては、例えば、メチルハイドロジェンシロキサン・ジメチルシロキサン環状共重合体、両末端ジメチルハイドロジェンシロキシ基封鎖メチルハイドロジェンポリシロキサン、両末端ジメチルハイドロジェンシロキシ基封鎖メチルハイドロジェン・ジメチルシロキサン共重合体、両末端ジメチルハイドロジェンシロキシ基封鎖メチルハイドロジェン・ジフェニルシロキサン共重合体、両末端ジメチルハイドロジェンシロキシ基封鎖メチルハイドロジェン・ジメチルシロキサン・ジフェニルシロキサン共重合体、両末端トリメチルシロキシ基封鎖メチルハイドロジェンポリシロキサン、両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルハイドロジェンシロキサン共重合体、両末端トリメチルシロキシ基封鎖メチルハイドロジェンシロキサン・ジフェニルシロキサン共重合体、両末端トリメチルシロキシ基封鎖メチルハイドロジェンシロキサン・ジフェニルシロキサン・ジメチルシロキサン共重合体、(CH3)2HSiO1/2単位と(CH3)2HSiO単位とCH3SiO3/2単位からなる共重合体、(CH3)2HSiO1/2単位と(C6H5)2SiO単位と(CH3)2SiO単位とCH3SiO3/2単位からなる共重合体、(CH3)(C6H5)HSiO1/2単位と(CH3)2SiO単位とCH3SiO3/2単位からなる共重合体、(CH3)2HSiO1/2単位と(CH3)2SiO単位とC6H5SiO3/2単位からなる共重合体、(CH3)(CF3C2H4)HSiO1/2単位と(CH3)(CF3C2H4)SiO単位とCH3SiO3/2単位とからなる共重合体、(CH3)(CF3C2H4)HSiO1/2単位と(CH3)(CF3C2H4)SiO単位と(CH3)2SiO単位とCH3SiO3/2単位とからなる共重合体、(CH3)2HSiO1/2単位と(CH3)(CF3C2H4)SiO単位とCH3SiO3/2単位とからなる共重合体、(CH3)2HSiO1/2単位と(CH3)(CF3C2H4)SiO単位と(CH3)2SiO単位とCH3SiO3/2単位とからなる共重合体、(CH3)2HSiO1/2単位と(CH3)(CF3C2H4)SiO単位と(CH3)2SiO単位と(CF3C2H4)SiO3/2単位とからなる共重合体等が挙げられる。
(B)成分のオルガノハイドロジェンポリシロキサンは、一種単独で用いても二種以上を併用してもよい。また、このオルガノハイドロジェンポリシロキサンは、従来公知の方法で合成される。
(B)成分の配合量は、(A)成分中のアルケニル基の数に対する(B)成分中のSi-H基の数の比、即ち{Si-H基の個数}/{(A)成分のアルケニル基の個数}が0.5より小さいと十分な網状構造をとれず硬化後に必要な硬さが得られないため、ボイドが発生してしまうおそれがあり、3.0より大きいと未反応のSi-H基が水分などにより余剰の架橋反応を起こし硬くなり、組成物の柔軟性が失われることに加え、高速加速寿命試験後の熱抵抗値の悪化が著しいため、0.5~3.0の範囲である必要があり、好ましくは0.6~2.0の範囲である。
((C)成分)
本発明の(C)成分の充填剤は、本発明の組成物に熱伝導性を付与するためのものであり、熱伝導性粉末を一種類以上含む。(C)成分の熱伝導率は10W/m・℃以上であれば、組成物の熱伝導性を十分に確保できるため、10W/m・℃以上の熱伝導率を有する熱伝導性粉末を含むことが好ましい。
本発明の(C)成分の充填剤は、本発明の組成物に熱伝導性を付与するためのものであり、熱伝導性粉末を一種類以上含む。(C)成分の熱伝導率は10W/m・℃以上であれば、組成物の熱伝導性を十分に確保できるため、10W/m・℃以上の熱伝導率を有する熱伝導性粉末を含むことが好ましい。
本発明の(C)成分の充填剤に使用する粉末の種類としてアルミニウム粉末と酸化亜鉛粉末を用いることが好ましい。アルミニウム粉末の平均粒径が0.1μm以上であれば、得られる組成物の粘度が高くなりすぎず、伸展性を確保でき、100μm以下であれば、得られる組成物が不均一とならないため、特に限定されないが、好ましくは0.1~100μmの範囲、より好ましくは1~50μmの範囲である。
また、上記酸化亜鉛粉末の平均粒径は、0.1μm以上であれば、得られる組成物の粘度が高くなりすぎず、伸展性を確保でき、5μm以下であれば、得られる組成物が不均一とならないため、特に限定されないが、好ましくは0.1~5μmの範囲、より好ましくは1~4μmの範囲である。また、アルミニウム粉末、酸化亜鉛粉末の形状は、球状、不定形状いずれでもよい。
上記熱伝導性粉末としてアルミニウム粉末、酸化亜鉛粉末の熱伝導率は、それぞれ約237W/m・K、約20W/m・Kであることから、高い熱伝導率を得ることができるため、これら鉱物を充填剤に用いることが好ましい。本発明の(C)成分の充填剤として、アルミニウム粉末単独で用いてもよいが、酸化亜鉛粉末と混合することで、オイル分離を抑制でき、得られる組成物の安定性を保つことができる。その割合は、特に限定されないが、重量比でアルミニウム粉末:酸化亜鉛粉末が1:1~10:1の範囲が好ましく、2:1~8:1の範囲がより好ましい。アルミニウム粉末の比率が1:1以上であれば、得られる組成物の熱伝導率が低くならず、10:1以下であれば、経時でのオイル分離をより抑制できる。
これら充填剤の配合量は、(A)成分100質量部に対して800~20,000質量部であり、好ましくは850~7,000質量部である。800質量部より少ないと、得られる組成物の熱伝導率が乏しいものとなり、20,000質量部より多いとペースト状にすることが難しい。
((D)成分)
本発明の(D)成分は、下記一般式(1)で表される加水分解性オルガノポリシロキサンである。
(式中のR1は置換基を有していても良い炭素数1~10の1価炭化水素基を表し、それぞれのR1は同一であっても異なっていても良い。また、aは5~100である。)
本発明の(D)成分は、下記一般式(1)で表される加水分解性オルガノポリシロキサンである。
これは、ウエッターとして用いられるものであり、上記(A)成分は充填剤との濡れ性が悪く、ウエッターを添加して混合しないと十分な充填量が得られない。そこで検討した結果、上記一般式(1)のオルガノポリシロキサンを添加することで、著しく充填剤の充填量を上げられることを見出したものである。一般式(1)中、R1は、炭素数1~10、好ましくは1~6のアルキル基である。具体的には、メチル基、エチル基、プロピル基、イソプロピル基、ブチル基、sec-ブチル基、tert-ブチル基、ペンチル基、ヘキシル基等が挙げられる。
組成式(1)のaは5~100であり、好ましくは10~60である。aが5より小さいと組成物のオイルブリードがひどく、ボイドが発生するおそれがある。aが100より大きいと、組成物の粘度が高くなり、作業性が悪くなるおそれがある。添加量は組成物の全体量に対し20~400質量部であり、好ましくは40~200質量部である。添加量が全体量に対して20質量部より少ないと、組成物の濡れ性が不十分となるおそれがあり、添加量が全体量に対して400質量部より多いと、組成物のオイルブリードがひどく、ボイドが発生するおそれがある。
((E)成分)
本発明の(E)成分は、下記一般式(2)で示されるオルガノシランである。
R2 bSi(OR3)4-b (2)
(式中、R2は炭素数14~20の、置換基を有していてもよい飽和又は不飽和の一価炭化水素基、エポキシ基、(メタ)アクリル基の中から選択される1種類以上の基であり、R3は炭素数1~6のアルキル基である。bは1~3の整数である。)
本発明の(E)成分は、下記一般式(2)で示されるオルガノシランである。
R2 bSi(OR3)4-b (2)
(式中、R2は炭素数14~20の、置換基を有していてもよい飽和又は不飽和の一価炭化水素基、エポキシ基、(メタ)アクリル基の中から選択される1種類以上の基であり、R3は炭素数1~6のアルキル基である。bは1~3の整数である。)
これは(D)成分と同様に、充填剤の充填量を著しく上げるウエッターとしての効果があることに加え、高温高湿下に曝されても熱抵抗値の悪化を著しく抑制する効果があることを見出したものである。
ここで、上記式(2)において、R2は炭素数14~20の、置換基を有していてもよい飽和又は不飽和の一価炭化水素基、エポキシ基、(メタ)アクリル基の中から選択される1種類以上の基であり、好ましくは、炭素数14~20のアルキル基であり、さらに好ましくは炭素数16~20、より好ましくは16~18のアルキル基である。例えばヘキサデシル基、オクタデシル基等が挙げられる。炭素数が14より少ないと揮発しやすく、高温下でボイドを発生させてしまうおそれがあり、20より多いとオルガノシランが常温で固化するので取り扱いが不便な上、得られた組成物の低温特性が低下する。また、bは1~3の整数であるが、特に1であることが好ましい。上記式(2)中のR3は炭素数1~6のアルキル基であり、特に、メチル基、エチル基が好ましい。
上記一般式(2)で表される上記(E)成分のオルガノシランの具体例としては、下記のものを挙げることができる。
C14H29Si(OCH3)3
C16H33Si(OCH3)3
C18H37Si(OCH3)3
C20H41Si(OCH3)3
C16H33Si(OC2H5)3
C18H37Si(OC2H5)3
C14H29Si(OCH3)3
C16H33Si(OCH3)3
C18H37Si(OCH3)3
C20H41Si(OCH3)3
C16H33Si(OC2H5)3
C18H37Si(OC2H5)3
上記(E)成分であるオルガノシランの配合量は、(A)成分100質量部に対し、0.01質量部より少ないと濡れ性が乏しく、長期間の高温高湿下で柔軟性を保つことができず、100質量部より多く配合しても効果が増大することがなく不経済であり、高温下でのボイドが発生することがあるため、0.01~100質量部の範囲であり、好ましくは10~70質量部の範囲である。
((F)成分)
(F)成分の白金及び白金化合物から選ばれる触媒は、(A)成分のアルケニル基と(B)成分のSi-H基との間の付加反応の促進成分である。この(F)成分は、例えば白金の単体、塩化白金酸、白金-オレフィン錯体、白金-アルコール錯体、白金配位化合物などが挙げられる。(F)成分の配合量は、(A)成分100質量部に対し、白金原子として0.1ppmより少ないと触媒としての効果がなく、500ppmより多く配合しても、特に硬化速度の向上は期待できないため0.1~500ppmの範囲であり、より好ましくは、1~200ppmの範囲である。
(F)成分の白金及び白金化合物から選ばれる触媒は、(A)成分のアルケニル基と(B)成分のSi-H基との間の付加反応の促進成分である。この(F)成分は、例えば白金の単体、塩化白金酸、白金-オレフィン錯体、白金-アルコール錯体、白金配位化合物などが挙げられる。(F)成分の配合量は、(A)成分100質量部に対し、白金原子として0.1ppmより少ないと触媒としての効果がなく、500ppmより多く配合しても、特に硬化速度の向上は期待できないため0.1~500ppmの範囲であり、より好ましくは、1~200ppmの範囲である。
((G)成分)
(G)成分の反応制御剤は、室温でのヒドロシリル化反応の進行を抑え、シェルフライフ、ポットライフを延長させるものである。(G)成分の反応制御剤としては公知のものを使用することができ、アセチレン化合物、各種窒素化合物、有機りん化合物、オキシム化合物、有機クロロ化合物等が利用できる。(G)成分の配合量は(A)成分100質量部に対し、0.01質量部より少ないと十分なシェルフライフ、ポットライフが得られず、1質量部より多いと硬化性が低下するため、0.01~1質量部の範囲であり、好ましくは0.1~0.8質量部の範囲である。
(G)成分の反応制御剤は、室温でのヒドロシリル化反応の進行を抑え、シェルフライフ、ポットライフを延長させるものである。(G)成分の反応制御剤としては公知のものを使用することができ、アセチレン化合物、各種窒素化合物、有機りん化合物、オキシム化合物、有機クロロ化合物等が利用できる。(G)成分の配合量は(A)成分100質量部に対し、0.01質量部より少ないと十分なシェルフライフ、ポットライフが得られず、1質量部より多いと硬化性が低下するため、0.01~1質量部の範囲であり、好ましくは0.1~0.8質量部の範囲である。
また、本発明の熱伝導性シリコーン組成物には上記した(A)~(G)成分以外に、必要に応じて、CPUなどのICパッケージとヒートシンク等の放熱体とを化学的に接着、固定するために接着助剤等を添加してもよいし、劣化を防ぐために酸化防止剤等を添加してもよい。
本発明の熱伝導性シリコーン組成物は、上記(A)~(G)成分、その他の任意成分を混合し、一液付加タイプとして長期低温保存できる。
[熱伝導性シリコーン組成物の製造方法]
本発明の熱伝導性シリコーン組成物は、上記成分を混合して作製することができる。各成分の添加順序は特に限定されないが、(A)~(G)成分および必要に応じてその他の成分を混合して調製することができ、例えば、(A)成分、(C)成分、(D)成分を含むパートと、(B)成分を含むパートとを個別に調製した後、それら2パートを混合して使用することもできる。
本発明の熱伝導性シリコーン組成物は、上記成分を混合して作製することができる。各成分の添加順序は特に限定されないが、(A)~(G)成分および必要に応じてその他の成分を混合して調製することができ、例えば、(A)成分、(C)成分、(D)成分を含むパートと、(B)成分を含むパートとを個別に調製した後、それら2パートを混合して使用することもできる。
本発明のシリコーン組成物の各成分は、常温で混合しても、加熱して混合してもよく、混合する際の温度は25~200℃が好ましく、より好ましくは50~180℃である。さらに加熱または25℃での混合の際に脱気を行ってもよい。
[熱伝導性シリコーン組成物の物性]
本発明のシリコーン組成物の粘度は、マルコム回転粘度計(回転数10rpm)で25℃で測定する場合、50~1000Pa・Sが好ましく、より好ましくは100~700Pa・S、さらにより好ましくは150~400Pa・Sである。50Pa・S以上であると、保存時に熱伝導性充填剤が沈降せず不均一にならず、1000Pa・S以下であると、伸展性を確保でき、作業効率が落ちない。
本発明のシリコーン組成物の粘度は、マルコム回転粘度計(回転数10rpm)で25℃で測定する場合、50~1000Pa・Sが好ましく、より好ましくは100~700Pa・S、さらにより好ましくは150~400Pa・Sである。50Pa・S以上であると、保存時に熱伝導性充填剤が沈降せず不均一にならず、1000Pa・S以下であると、伸展性を確保でき、作業効率が落ちない。
本発明のシリコーン組成物の硬化物は、高速加速寿命試験(130℃、湿度85%、96h)後でも、熱抵抗値が試験前と比べて1.5mm2・K/W以上上昇して悪化しないため、長期的に熱抵抗性能を持続することができる。尚、この熱抵抗値は、低ければ低いほど熱性能が優れるため、試験前から試験後にどれほど低下しても問題はない。
本発明のシリコーン組成物は、高温下でもボイドの発生を抑制することができ、ガラス板2枚に組成物を挟み、150℃、60分で組成物を硬化させた後、260℃、5分の加熱を5回繰り返してもボイドが観測されない。
本発明のシリコーン組成物の硬化物は、高温下に曝されても高引張弾性率化を抑制することができ、260℃のチャンバーに5分間入れた後に取り出す工程を3回繰り返す加熱試験を実施しても、前記加熱試験前から引張弾性率が20MPa以上上昇しない。尚、この引張弾性率は、前記加熱試験前と比べて、変化しなければしないほど、一定の熱性能が保持されるため、変化がどれほど小さくても問題はない。
本発明のシリコーン組成物の硬化物の硬度をAskerCで25℃で測定をした場合、10以上が好ましく、より好ましくは20~90であり、さらにより好ましくは30~85である。上記の硬度が10以上であると、加熱試験後に硬化物が脆くならず、破損するおそれがない。
以下、実施例及び比較例を用いて本発明を具体的に説明するが、本発明はこれらに限定されるものではない。
まず、以下の成分を用意した。
(A)成分
A-1:両末端がジメチルビニルシリル基で封鎖され、25℃における粘度が600mm2/sのジメチルポリシロキサン
A-2:両末端がジメチルビニルシリル基で封鎖され、25℃における粘度が30,000mm2/sのジメチルポリシロキサン
A-3:両末端がトリビニルシリル基で封鎖され、25℃における粘度が1,500mm2/sのジメチルポリシロキサン
(A)成分
A-1:両末端がジメチルビニルシリル基で封鎖され、25℃における粘度が600mm2/sのジメチルポリシロキサン
A-2:両末端がジメチルビニルシリル基で封鎖され、25℃における粘度が30,000mm2/sのジメチルポリシロキサン
A-3:両末端がトリビニルシリル基で封鎖され、25℃における粘度が1,500mm2/sのジメチルポリシロキサン
(B)成分
B-1:側鎖に2個のケイ素原子結合水素原子を有する、粘度が30mm2/sのオルガノハイドロジェンポリシロキサン
B-2:両末端にケイ素原子結合水素原子を有し、側鎖に2個のケイ素原子結合水素原子を有する、粘度が40mm2/sのオルガノハイドロジェンポリシロキサン
B-1:側鎖に2個のケイ素原子結合水素原子を有する、粘度が30mm2/sのオルガノハイドロジェンポリシロキサン
B-2:両末端にケイ素原子結合水素原子を有し、側鎖に2個のケイ素原子結合水素原子を有する、粘度が40mm2/sのオルガノハイドロジェンポリシロキサン
(C)成分
C-1:平均粒径10μmのアルミニウム粉末
C-2:平均粒径0.25μmの酸化亜鉛粉末
C-1:平均粒径10μmのアルミニウム粉末
C-2:平均粒径0.25μmの酸化亜鉛粉末
(E)成分
E-1: C10H21Si(OCH3)3(比較例用)
E-2: C12H25Si(OCH3)3(比較例用)
E-3: C16H33Si(OCH3)3
E-4: C18H37Si(OCH3)3
E-1: C10H21Si(OCH3)3(比較例用)
E-2: C12H25Si(OCH3)3(比較例用)
E-3: C16H33Si(OCH3)3
E-4: C18H37Si(OCH3)3
(F)成分
F-1:白金濃度が1質量%である白金-ジビニルテトラメチルジシロキサン錯体
F-1:白金濃度が1質量%である白金-ジビニルテトラメチルジシロキサン錯体
(G)成分
G-1:1-エチニル-1-シクロヘキサノール
G-1:1-エチニル-1-シクロヘキサノール
上記(A)~(G)成分を以下のように混合して、実施例1~7及び比較例1~8の熱伝導性シリコーン組成物を得た。即ち、5リットルプラネタリーミキサー(井上製作所(株)製)に(A)、(C)、(D)、(E)成分を加え、170℃で90分間混合した。常温になるまで冷却し、次に(B)、(F)、(G)成分をそれぞれ加えて15分間ずつ混合した。
得られた組成物について、下記方法でその特性を評価した。結果を表1,2に示す。
(1)粘度:マルコム回転粘度計(回転数10rpm)で25℃における粘度を測定した。
(2)熱伝導率:京都電子工業(株)製熱物性測定装置TPS-2500Sを用いて25℃における組成物の硬化前の熱伝導率を測定した。
(3)熱抵抗値:15mm×15mm×1mmtのSiチップと15mm×15mm×1mmtのNiプレートの間に、組成物を挟み込み、150℃、60分で組成物を硬化させ、熱抵抗測定用の試験片を作製し、熱抵抗値を測定した。さらにその後、試験片を130℃、湿度85%のチャンバーに96時間入れ、高速加速寿命試験を実施した。高速加速寿命試験後に熱抵抗値を測定し、高速加速寿命試験前と後の熱抵抗値を比較した。なお、この熱抵抗測定はナノフラッシュ(ニッチェ社製、LFA447)によって行った。
(4)ボイド試験:ガラス板2枚に組成物を挟み、両端をそれぞれクリップで挟み、150℃、60分で組成物を硬化させた。さらにその後260℃、5分の加熱を5回繰り返して、ガラス板に挟まれている組成物の様子を目視で確認した。
組成物にボイド無し:○
組成物にボイド有り:×
組成物にボイド無し:○
組成物にボイド有り:×
(5)引張弾性率:シリコーン組成物を150℃、60分で2mm厚のシート状に硬化させ、TAインスツルメント(株)製ARES-G2を用いて25℃における引張弾性率を測定した。その後、シリコーン組成物の硬化物を260℃の高温チャンバー(エスペック(株)製高温小型チャンバーSTH-120)に5分間入れた後、高温チャンバーから取り出し、硬化物を室温に戻す工程を3回繰り返す加熱試験を実施し、前記と同様の装置で25℃における引張弾性率を測定した。
(6)硬度:シリコーン組成物を150℃、60分で硬化させた後、AskerCで25℃における硬度を測定した。
※2 ペースト状にならなかった。
※3 ボイド発生により硬化物が脆くなり、引張弾性率の測定中に破損したため、測定不可能。
表1及び表2の結果より、本発明の要件を満たす実施例1~7の熱伝導性シリコーン組成では、熱伝導性でありながら、低粘度を保ち、高速加熱寿命試験後でも熱抵抗値の劣化が少なく、加熱試験後もボイドの発生や弾性率の上昇が小さい組成物を実現することが可能であった。
一方で、比較例1では長鎖アルキル基を有するオルガノシランを配合していないため、高速加速寿命試験後に熱抵抗値が大幅に上昇してしまった。
比較例2では、C10H21Si(OCH3)3を添加しており、アルキル鎖長が短いオルガノシランであることから、高速加速寿命試験後の熱抵抗値が大幅に悪化し、ボイド試験でボイドがでてしまった。
比較例3では、C12H25Si(OCH3)3を添加しており、アルキル鎖の長さが十分でないことから、高速加速寿命試験後の熱抵抗値の悪化は殆どないが、硬度が低く、ボイド試験後にボイドがでてしまった。
比較例4では、比較例3と同様のC12H25Si(OCH3)3を添加し、{(B)成分のSi-H基の個数}/{(A)成分のSi-Vi基の個数}の比を高くしたが、加熱後の引張弾性率が大幅に上昇してしまった。
比較例5では、比較例3および4と同様のC12H25Si(OCH3)3の添加量を減らしたため、高速加速寿命試験後の熱抵抗値が悪化し、加熱後の引張弾性率も大幅に上昇した。
比較例6では、充填剤を多量に配合したため、粘度が著しく上昇し、ペースト状にはならず、塊状になった。
比較例7では、{(B)成分のSi-H基の個数}/{(A)成分のSi-Vi基の個数}の比が0.5未満と低すぎたため、材料の強度が十分にとれず、ボイド試験後にボイドが発生したり、加熱すると硬化物が脆く、引張弾性率が測定不可となった。
比較例8では、長鎖アルキル基を有するオルガノシランを多量に配合したために、ボイド試験後にボイドが発生したり、硬化物が脆いために引張弾性率が測定不可となった。
上記の実施例の結果より、本発明の熱伝導性シリコーン組成物であれば、高温高湿下に曝されても熱抵抗値が悪化せず、高温下に曝されても高弾性率化せず、ボイドが発生しない高い熱伝導率をもつ熱伝導性シリコーン組成物を提供することができることが示された。
なお、本発明は、上記実施形態に限定されるものではない。上記実施形態は例示であり、本発明の特許請求の範囲に記載された技術的思想と実質的に同一な構成を有し、同様な作用効果を奏するものは、いかなるものであっても本発明の技術的範囲に包含される。
Claims (11)
- (A)1分子中に少なくとも2個のアルケニル基を有するオルガノポリシロキサン:100質量部
(B)1分子中に少なくとも2個のケイ素原子結合水素原子を有するオルガノハイドロジェンポリシロキサン:前記(B)成分のSi-H基の個数と、前記(A)成分のアルケニル基の個数比(Si-H基の個数)/(アルケニル基の個数)が0.5~3.0となる量
(C)熱伝導性粉末を一種類以上含む充填剤:800~20,000質量部
(D)下記一般式(1)で表される加水分解性オルガノポリシロキサン:20~400質量部
(E)下記一般式(2)で示されるオルガノシラン:0.01~100質量部
R2 bSi(OR3)4-b (2)
(式中、R2は炭素数14~20の、置換基を有していてもよい飽和又は不飽和の一価炭化水素基、エポキシ基、(メタ)アクリル基の中から選択される1種類以上の基であり、R3は炭素数1~6のアルキル基である。bは1~3の整数である。)
(F)白金又は白金化合物の触媒:白金原子として前記(A)成分の0.1~500ppmとなる量
(G)反応制御剤:0.01~1質量部
を含むものであることを特徴とする熱伝導性シリコーン組成物。 - 前記(A)成分の粘度は25℃で10~100,000mm2/sであることを特徴とする請求項1に記載の熱伝導性シリコーン組成物。
- 前記(C)成分はアルミニウム粉末と酸化亜鉛粉末を含むものであることを特徴とする請求項1又は請求項2に記載の熱伝導性シリコーン組成物。
- 前記(E)成分の前記R2は炭素数14~20のアルキル基であることを特徴とする請求項1から請求項3のいずれか1項に記載の熱伝導性シリコーン組成物。
- 前記(E)成分の前記R2は炭素数16~20のアルキル基であることを特徴とする請求項1から請求項4のいずれか1項に記載の熱伝導性シリコーン組成物。
- 前記(G)成分はアセチレン化合物、窒素化合物、有機りん化合物、オキシム化合物、及び有機クロロ化合物のいずれか一つ以上を含むものであることを特徴とする請求項1から請求項5のいずれか1項に記載の熱伝導性シリコーン組成物。
- 前記熱伝導性シリコーン組成物は、25℃における粘度が50~1,000Pa・sの範囲のものであることを特徴とする請求項1から請求項6のいずれか1項に記載の熱伝導性シリコーン組成物。
- 前記熱伝導性シリコーン組成物の硬化物は、高速加速寿命試験(130℃、湿度85%、96h)後でも、熱抵抗値が、高速加速寿命試験前と比べて1.5mm2・K/W以上高くならないものであることを特徴とする請求項1から請求項7のいずれか1項に記載の熱伝導性シリコーン組成物。
- 前記熱伝導性シリコーン組成物をガラス板2枚に挟み、150℃、60分で硬化させた硬化物は、260℃で5分間加熱する工程を5回繰り返した後にボイドが観測されないものであることを特徴とする請求項1から請求項8のいずれか1項に記載の熱伝導性シリコーン組成物。
- 前記熱伝導性シリコーン組成物の硬化物は、25℃においてAskerCで10以上の硬度のものであることを特徴とする請求項1から請求項9のいずれか1項に記載の熱伝導性シリコーン組成物。
- 前記熱伝導性シリコーン組成物の硬化物は、260℃のチャンバーに5分間入れた後に取り出す工程を3回繰り返す加熱試験を実施しても、前記加熱試験実施前から引張弾性率が20MPa以上上昇しないものであることを特徴とする請求項1から請求項10のいずれか1項に記載の熱伝導性シリコーン組成物。