WO2023115572A1 - Procédé de préparation de composant et appareil de traitement au plasma - Google Patents

Procédé de préparation de composant et appareil de traitement au plasma Download PDF

Info

Publication number
WO2023115572A1
WO2023115572A1 PCT/CN2021/141347 CN2021141347W WO2023115572A1 WO 2023115572 A1 WO2023115572 A1 WO 2023115572A1 CN 2021141347 W CN2021141347 W CN 2021141347W WO 2023115572 A1 WO2023115572 A1 WO 2023115572A1
Authority
WO
WIPO (PCT)
Prior art keywords
protective layer
metal ion
connection layer
layer
functional group
Prior art date
Application number
PCT/CN2021/141347
Other languages
English (en)
Chinese (zh)
Inventor
侯磊
何敏博
林军
Original Assignee
华为技术有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 华为技术有限公司 filed Critical 华为技术有限公司
Priority to PCT/CN2021/141347 priority Critical patent/WO2023115572A1/fr
Priority to CN202180044297.XA priority patent/CN116648771A/zh
Publication of WO2023115572A1 publication Critical patent/WO2023115572A1/fr

Abstract

Les modes de réalisation de la présente demande se rapportent au domaine technique du traitement au plasma. Sont prévus un procédé de préparation de composant et un appareil de traitement au plasma, qui sont utilisés pour résoudre le problème de la manière d'améliorer la durabilité d'un composant dans un appareil de traitement au plasma. L'appareil de traitement au plasma comprend une chambre pour exécuter un traitement au plasma, et un composant possédant au moins une partie de sa structure exposée dans la chambre. Le composant comprend un substrat, une première couche de liaison, qui recouvre une surface externe du substrat, et une première couche de protection, qui recouvre une surface externe de la première couche de liaison. Le matériau du substrat comprend un premier ion métallique; le matériau de la première couche de connexion comprend un premier groupe fonctionnel, qui a la fonction d'être lié à un ion métallique; et le matériau de la première couche de protection comprend un premier oxyde métallique, qui comprend un second ion métallique, le premier groupe fonctionnel étant respectivement lié au premier ion métallique dans le substrat et au second ion métallique dans la première couche de protection.
PCT/CN2021/141347 2021-12-24 2021-12-24 Procédé de préparation de composant et appareil de traitement au plasma WO2023115572A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
PCT/CN2021/141347 WO2023115572A1 (fr) 2021-12-24 2021-12-24 Procédé de préparation de composant et appareil de traitement au plasma
CN202180044297.XA CN116648771A (zh) 2021-12-24 2021-12-24 部件的制备方法、等离子体处理装置

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/CN2021/141347 WO2023115572A1 (fr) 2021-12-24 2021-12-24 Procédé de préparation de composant et appareil de traitement au plasma

Publications (1)

Publication Number Publication Date
WO2023115572A1 true WO2023115572A1 (fr) 2023-06-29

Family

ID=86901126

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2021/141347 WO2023115572A1 (fr) 2021-12-24 2021-12-24 Procédé de préparation de composant et appareil de traitement au plasma

Country Status (2)

Country Link
CN (1) CN116648771A (fr)
WO (1) WO2023115572A1 (fr)

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20060183344A1 (en) * 2003-03-31 2006-08-17 Tokyo Electron Limited Barrier layer for a processing element and a method of forming the same
CN109976097A (zh) * 2017-12-27 2019-07-05 三星电子株式会社 形成微图案的方法及基板处理设备

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20060183344A1 (en) * 2003-03-31 2006-08-17 Tokyo Electron Limited Barrier layer for a processing element and a method of forming the same
CN109976097A (zh) * 2017-12-27 2019-07-05 三星电子株式会社 形成微图案的方法及基板处理设备

Also Published As

Publication number Publication date
CN116648771A (zh) 2023-08-25

Similar Documents

Publication Publication Date Title
CN108878246B (zh) 用于腔室部件的多层等离子体侵蚀保护
CN111900084B (zh) 抗等离子体腐蚀的稀土氧化物基薄膜涂层
JP4608159B2 (ja) 半導体処理装置の耐腐食性部材およびその製造方法
CN107646136B (zh) 用于高温处理的具有金属结合背板的静电定位盘组件
JP6278584B2 (ja) プラズマチャンバ部品用耐プラズマコーティング
CN105408987B (zh) 稀土氧化物的顶部涂层的离子辅助沉积
US8968537B2 (en) PVD sputtering target with a protected backing plate
JP2004526054A (ja) 反応室壁上のダイヤモンド被膜及びその製造方法
WO2014089244A1 (fr) Ensemble de support de substrat ayant une couche protectrice résistant au plasma
TW201209957A (en) Substrate supports for semiconductor applications
TW201545198A (zh) 電感耦合型等離子體處理腔室及其抗腐蝕絕緣視窗及製造方法
KR20170035988A (ko) 고체 탄소 이산화물 입자들을 이용한 챔버 컴포넌트들의 세정
CN105990081B (zh) 等离子体处理装置及其制作方法
CN104241183A (zh) 静电吸盘的制造方法,静电吸盘及等离子体处理装置
EP2883644B1 (fr) Dispositif de collage à température ordinaire et procédé de collage à température ordinaire
WO2023115572A1 (fr) Procédé de préparation de composant et appareil de traitement au plasma
TW202202469A (zh) 基於氧化釔之塗層及塊體組成物
CN104241182B (zh) 静电吸盘的制造方法，静电吸盘及等离子体处理装置
JP4181069B2 (ja) プラズマ処理装置
CN104241181A (zh) 静电吸盘的制造方法,静电吸盘及等离子体处理装置
US20230039670A1 (en) Mixed metal baseplates for improved thermal expansion matching with thermal oxide spraycoat
US20050199183A1 (en) Plasma processing apparatus
WO2021207418A1 (fr) Composition de revêtement à base d'oxyde d'yttrium
US20230234160A1 (en) Diffusion bonding of pure metal bodies
US20240240304A1 (en) Metal oxy-fluoride coating for chamber components and method of coating thereof

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 202180044297.X

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21968701

Country of ref document: EP

Kind code of ref document: A1