WO2023112883A1 - セラミック電子部品 - Google Patents

セラミック電子部品 Download PDF

Info

Publication number
WO2023112883A1
WO2023112883A1 PCT/JP2022/045631 JP2022045631W WO2023112883A1 WO 2023112883 A1 WO2023112883 A1 WO 2023112883A1 JP 2022045631 W JP2022045631 W JP 2022045631W WO 2023112883 A1 WO2023112883 A1 WO 2023112883A1
Authority
WO
WIPO (PCT)
Prior art keywords
identification mark
electronic component
base body
ceramic electronic
base
Prior art date
Application number
PCT/JP2022/045631
Other languages
English (en)
French (fr)
Inventor
卓也 後飯塚
Original Assignee
株式会社村田製作所
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社村田製作所 filed Critical 株式会社村田製作所
Publication of WO2023112883A1 publication Critical patent/WO2023112883A1/ja

Abstract

識別マークの認識精度の低下を抑制しつつ、外部からの物理的衝撃に対する識別マークの強度を高くすることができるセラミック電子部品を提供する。セラミック電子部品は、セラミックを主材料とする素体と、素体の主面に形成され、少なくとも一部が素体の主面から突出した識別マークと、を備える。素体は、素体の主面と直交する厚み方向から見て、識別マークを囲み且つ識別マークの外縁部と接触する第１部分と、厚み方向から見て、第１部分を囲む第２部分と、を備える。第１部分は、第２部分に対して隆起している。

Description

セラミック電子部品
　本発明は、セラミックを主材料とする素体と素体に形成された識別マークとを備えるセラミック電子部品に関する。
　セラミックを主材料とする素体と素体に形成された識別マークとを備えるセラミック電子部品の一例が、特許文献１，２に開示されている。
　特許文献１，２に開示された積層型の電子部品は、複数枚のセラミックシートが積層されたものである。最上層のセラミックシートに設けられた凹部に材料が充填されることによって、識別マークが形成されている。識別マークが凹部に充填されているため、電子部品の製造工程の焼成において、識別マークが消失する可能性を低くすることができる。
特開２００３－７５７３号公報 特開２００７－２４２８０６号公報
　特許文献１に開示された電子部品では、識別マークとセラミックシートの表面とが面一となっている。通常、識別マークは光学系のカメラで認識されるが、識別マークとセラミックシートの表面とが面一となっているため、識別マークの外周部に陰影が形成されにくい。これにより、カメラでの識別マークの認識精度が落ちるおそれがある。
　これに対して、特許文献２に開示された電子部品では、識別マークがセラミックシートの表面に対して膨らんでいる。そのため、特許文献１に開示された電子部品より、識別マークの外周部に陰影が形成されやすい。
　しかしながら、特許文献２に開示された電子部品では、識別マークがセラミックシートの表面に対して膨らんでいる。そのため、特許文献２に開示された電子部品では、識別マークとセラミックシートの表面とが面一となっている構成に比べて、外部からの物理的衝撃によって識別マークがセラミックシートから滑落する可能性が高くなってしまう。
　従って、本発明の目的は、前記課題を解決することにあって、識別マークの認識精度の低下を抑制しつつ、外部から物理的衝撃に対する識別マークの強度を高くすることができるセラミック電子部品を提供することにある。
　前記目的を達成するために、本発明は以下のように構成する。
　本発明の一態様に係るセラミック電子部品は、
　セラミックを主材料とする素体と、
　前記素体の表面に形成され、少なくとも一部が前記素体の表面から突出した識別マークと、を備え、
　前記素体は、
　前記素体の表面と直交する方向から見て、前記識別マークを囲み且つ前記識別マークの外縁部と接触する第１部分と、
　前記素体の表面と直交する方向から見て、前記第１部分を囲む第２部分と、を備え、
　前記第１部分は、前記第２部分に対して隆起している。
　本発明によれば、識別マークの認識精度の低下を抑制しつつ、外部からの物理的衝撃に対する識別マークの強度を高くすることができる。
本発明の第１実施形態に係るセラミック電子部品の平面図。 図１のＡ－Ａ断面を示す断面図。 図２の一点鎖線部の拡大図。 本発明の第１実施形態に係るセラミック電子部品の製造過程において基材に層間接続導体が形成されたときの断面図。 本発明の第１実施形態に係るセラミック電子部品の製造過程において基材に内部電極が印刷されたときの断面図。 本発明の第１実施形態に係るセラミック電子部品の製造過程において基材に識別マークが印刷されたときの断面図。 本発明の第１実施形態に係るセラミック電子部品の製造過程において複数の基材が積層されて素体が形成されたときの断面図。 本発明の第１実施形態に係るセラミック電子部品の製造過程において素体が圧着されたときの断面図。 本発明の第１実施形態に係るセラミック電子部品の製造過程の変形例において積層された複数の基材と識別マークが印刷されたフィルムとを示す断面図。 本発明の第２実施形態に係るセラミック電子部品における図２の一点鎖線部に対応する部分の拡大図。
　本発明の一態様に係るセラミック電子部品は、
　セラミックを主材料とする素体と、
　前記素体の表面に形成され、少なくとも一部が前記素体の表面から突出した識別マークと、を備え、
　前記素体は、
　前記素体の表面と直交する方向から見て、前記識別マークを囲み且つ前記識別マークの外縁部と接触する第１部分と、
　前記素体の表面と直交する方向から見て、前記第１部分を囲む第２部分と、を備え、
　前記第１部分は、前記第２部分に対して隆起している。
　この構成によれば、素体の表面と直交する方向から見て素体の第１部分は識別マークを囲んでおり、第１部分は素体の第２部分に対して隆起している。つまり、素体の表面と直交する方向から見て、識別マークの周りに、第１部分と第２部分との間の段差が形成される。そのため、光学系のカメラで識別マークが認識されるとき、当該段差によって陰影が形成される。これにより、識別マークを認識することができる。よって、識別マークの認識精度の低下が抑制される。
　この構成によれば、素体の表面と直交する方向から見て、隆起した第１部分に識別マークが囲まれている。これにより、第１部分が識別マークに対する外部からの物理的衝撃に対する障壁となる。その結果、外部からの物理的衝撃に対する識別マークの強度を高くすることができる。
　前記セラミック電子部品において、前記識別マークの熱収縮率は、前記素体の熱収縮率より低くてもよい。
　この構成によれば、識別マークの熱収縮率は、素体の熱収縮率より低い。この場合、セラミック電子部品の製造過程において、識別マークが形成された素体が焼成されるときに、識別マークと素体との熱収縮率の差に起因して、識別マークの外縁部付近の素体の収縮が識別マークによって阻害される。これにより、識別マークの外縁部付近において、素体が隆起して第１部分が形成される。つまり、この構成によれば、隆起した第１部分を容易に形成することができる。
　前記セラミック電子部品において、
　前記識別マークは、セラミックを主材料としていてもよく、
　前記素体は、前記第１部分と前記識別マークとの界面部に拡散層を有していてもよく、
　前記拡散層は、前記識別マークから拡散された前記識別マークを構成する物質によって前記素体の組成が変化した層であってもよい。
　この構成によれば、拡散層によって、識別マークと素体の第１部分との間の密着性が高まるため、識別マークが素体から滑落する可能性を低くすることができる。また、識別マークと素体の第１部分との間の密着性が高まるため、識別マークと素体の第１部分との間から素体の内部への液体の浸入を低減することができる。
　前記セラミック電子部品において、
　前記素体及び前記識別マークの各々は、ガラス材を含んでいてもよく、
　前記拡散層において、前記素体に含まれるガラス材と前記識別マークに含まれるガラス材とが結合されていてもよい。
　この構成によれば、セラミック電子部品の製造工程において、素体に含まれるガラス材と識別マークに含まれるガラス材とが結合することによって拡散層が形成される。この拡散層によって、識別マークと素体との密着性を高めることができる。
＜第１実施形態＞
　図１は、本発明の第１実施形態に係るセラミック電子部品の平面図である。図２は、図１のＡ－Ａ断面を示す断面図である。図３は、図２の一点鎖線部の拡大図である。セラミック電子部品は、素体に識別マークが設けられたものである。第１実施形態に係るセラミック電子部品は、識別マークの他に、例えば層間接続導体と内部電極と外部電極とめっき層とが素体に設けられている。セラミック電子部品は、外部電極を介してマザー基板等に実装され得る。
　図１及び図２に示すように、第１実施形態に係るセラミック電子部品１０は、素体２０と、層間接続導体３０と、内部電極４０と、外部電極５０と、識別マーク７０と、めっき層８０とを備える。
　素体２０は、全体として直方体形状である。素体２０の形状は、直方体形状に限らない。第１実施形態において、素体２０は、厚み方向１００に積層された基材２１～２９が一体化されたものである。つまり、第１実施形態において、素体２０は、９つの基材が一体化されたものである。素体２０を構成する基材の数は９つに限らない。基材２１～２９の各々は、絶縁性であり、板状である。
　素体２０は、セラミックを主材料とする。素体２０の主材料は、素体２０に含まれる複数種類の材料のうち最も高い割合の材料である。素体２０に含まれる材料が１種類である場合、素体２０を構成する１種類の材料が、素体２０の主材料である。主材料の定義は、素体２０以外においても同様である。例えば、識別マーク７０の主材料は、識別マーク７０に含まれる複数種類の材料のうち最も高い割合の材料である。
　第１実施形態において、素体２０（各基材２１～２９）は、主材料であって誘電体特性を決めるためのフィラー、ガラス材、及び収縮率等の物性を調整するための添加剤を含む。素体２０に含まれる各材料の割合は、例えば、フィラーが約６０％、ガラス材が約１０％、添加剤が約３０％である。フィラー及び添加剤は、アルミニウム（Ａｌ）（例えばアルミナ），マグネシウム（Ｍｇ），ケイ素（Ｓｉ），バリウム（Ｂａ），チタン（Ｔｉ），ジルコニウム（Ｚｒ）（例えばジルコニア）等で構成されている。第１実施形態では、素体２０は、セルシアン（ＢａＡｌ２Ｓｉ２Ｏ８）を含んでいる。セルシアンはバリウム及びケイ素を含んでいる。
　なお、主材料がセラミックであるとの条件を満たす限り、素体２０に含まれる材料は前述したものに限らず、素体２０に含まれる各材料の割合は前記の割合に限らない。また、フィラー及び添加剤は、前記の物質以外で構成されていてもよい。また、第１実施形態では、素体２０はセルシアンの結晶を含んでいるが、他の結晶を含んでいてもよい。例えば、素体２０は、セルシアンの代わりに、フレスノイト（例えばＢａ２ＴｉＳｉ２Ｏ８またはＢａ２ＴｉＧｅ２Ｏ８）を含んでいてもよい。
　図２に示すように、素体２０は、一対の主面２０Ａ，２０Ｂと側面２０Ｃとを備える。主面２０Ａは、基材２１の主面であって素体２０の外部に面している。主面２０Ｂは、基材２９の主面であって素体２０の外部に面している。主面２０Ｂは、主面２０Ａと反対を向いている。主面２０Ｂは、素体２０の表面の一例である。側面２０Ｃは、基材２１～２９の側面で構成されている。側面２０Ｃは、主面２０Ａ，２０Ｂを繋いでいる。
　第１実施形態において、一対の主面２０Ａ，２０Ｂは、厚み方向１００に直交している。図１の平面図は、セラミック電子部品１０を厚み方向１００（図２参照）から見たときの図である。また、第１実施形態において、主面２０Ａ，２０Ｂの長手方向の長さは２～４ｍｍであり、主面２０Ａ，２０Ｂの短手方向の長さは１～２ｍｍであり、素体２０の厚み方向１００の長さは４５～１０００μｍである。なお、各長さは、前述した長さに限らない。
　図１及び図２に示すように、素体２０は、第１部分６１と、第２部分６２とを備える。また、図２に示すように、素体２０の基材２９は、第１層２９１と第２層２９２とを備える。第１部分６１、第２部分６２、第１層２９１、及び第２層２９２については、後述される。
　図２に示すように、層間接続導体３０は、素体２０の内部に形成されている。層間接続導体３０は、基材２１～２９の少なくとも１つに形成され得る。第１実施形態では、層間接続導体３０は、基材２１～２７に形成されている。
　層間接続導体３０は、複数の基材２１～２９の少なくとも１つを厚み方向１００に貫通する貫通孔２０Ｄに、導電性のペーストが充填され、セラミックを主材料とする素体２０と共焼成されたものである。導電性のペーストは、例えば銅等の導電性粉末を含んでいる。導電性のペーストが含む導電性粉末は、銅に限らず、例えば銀でもよい。第１実施形態では、貫通孔２０Ｄは円柱形状であるため、層間接続導体３０は円柱形状である。貫通孔２０Ｄの形状は、円柱形状に限らず、例えば四角柱等の形状であってもよい。
　図２では、層間接続導体３０は、４つの層間接続導体３１～３４を備えている。層間接続導体３１は、基材２３～２７を貫通する貫通孔２０Ｄに充填されている。層間接続導体３２～３４は、基材２１，２２を貫通する貫通孔２０Ｄに充填されている。各層間接続導体３１～３４の厚み方向１００の長さ（貫通する基材の数）は、前述した長さに限らない。
　内部電極４０は、素体２０の内部に形成されており、素体２０の外部に露出していない。内部電極４０は、基材２１～２９の少なくとも１つに形成され得る。第１実施形態では、内部電極４０は、基材２２，２４，２５，２７，２８に形成されている。
　第１実施形態のように素体２０の主材料がセラミックである場合、内部電極４０は、基材（第１実施形態では基材２２，２４，２５，２７，２８）の主面に導電性のペーストを印刷し、基材と共焼成されたものである。導電性のペーストは、例えば銅や銀で構成されている。
　第１実施形態では、内部電極４０は、９つの内部電極４１～４９を備えている。内部電極４１は、基材２７に形成されている。内部電極４２～４４は、基材２２に形成されている（図３参照）。内部電極４５，４７は、基材２５に形成されている。内部電極４６，４８は、基材２４に形成されている。内部電極４９は、基材２８に形成されている。
　内部電極４０の各々は、他の内部電極４０または外部電極５０と電気的に接続されている。第１実施形態では、図２に示すように、内部電極４１は、層間接続導体３１を介して内部電極４４と電気的に接続されている。内部電極４２は、層間接続導体３２を介して外部電極５１と電気的に接続されている。内部電極４３は、層間接続導体３３を介して外部電極５２と電気的に接続されている。内部電極４４は、層間接続導体３１を介して内部電極４１と接続されており、層間接続導体３４を介して外部電極５３と電気的に接続されている。
　外部電極５０は、素体２０の外部に形成されている。つまり、外部電極５０は、素体２０の外部に露出している。第１実施形態では、外部電極５０は、基材２１の主面（素体２０の主面２０Ａ）に形成されている。なお、外部電極５０は、素体２０の主面２０Ａの代わりにまたは素体２０の主面２０Ａに加えて、素体２０の主面２０Ｂ及び素体２０の側面２０Ｃの少なくとも一方に形成されていてもよい。
　外部電極５０は、内部電極４０と同様にして構成されている。つまり、第１実施形態では、外部電極５０は、素体２０の主面２０Ａに導電性のペーストを印刷し、基材２１～２９と共焼成されたものである。第１実施形態において、外部電極５０は、３つの外部電極５１～５３を備えている。
　前述したように、外部電極５１は層間接続導体３２を介して内部電極４２と電気的に接続されており、外部電極５２は層間接続導体３３を介して内部電極４３と電気的に接続されており、外部電極５３は層間接続導体３４を介して内部電極４４と電気的に接続されている。
　識別マーク７０は、素体２０の主面２０Ｂに形成されている。識別マーク７０は、セラミック電子部品１０の姿勢や方向を示すためのものである。
　第１実施形態では、セラミック電子部品１０は、１つの識別マーク７０を備えているが、複数の識別マーク７０を備えていてもよい。
　第１実施形態では、図１に示すように、厚み方向１００から見て、識別マーク７０は、円形であるが、円形に限らない。また、第１実施形態では、厚み方向１００から見た識別マーク７０の直径は１００～１５０μｍであるが、当該直径は１００～１５０μｍに限らない。
　図２及び図３に示すように、識別マーク７０の一部は、素体２０の基材２９に埋設されている。一方、識別マーク７０の残りの部分（言い換えると当該一部を除く部分）は、素体２０の主面２０Ｂから突出している。
　なお、識別マーク７０は、素体２０に埋設されていなくてもよい。この場合、識別マーク７０の全部が、素体２０の主面２０Ｂから突出している。つまり、識別マーク７０の少なくとも一部が、素体２０の主面２０Ｂから突出していればよい。
　各図において、識別マーク７０の色は白またはハッチングで示されているが、識別マーク７０の色は白に限らず、黒、グレー、赤等の他の色であってもよい。識別マーク７０の色は、識別マーク７０の周囲のもの（第１実施形態では基材２９）と異なる色であることが好ましい。
　第１実施形態において、識別マーク７０は、セラミックを主材料としており、主材料のアルミナと、ガラス材とを含む。識別マーク７０に含まれる各材料の割合は、アルミナが約７５％、ガラス材が約２５％である。第１実施形態において、識別マーク７０に含まれるガラス材の割合は、素体２０に含まれるガラス材の割合より多い。また、第１実施形態において、識別マーク７０の熱収縮率は、素体２０の熱収縮率より低い。例えば、素体２０は、前述した添加剤によって識別マーク７０より熱収縮率が低くるように調整される。また、例えば、素体２０は、識別マーク７０の主材料あるアルミナより熱収縮率の低い材料（例えば、ジルコニア（ＺｒＯ２））を主材料とする。識別マーク７０は、少なくとも焼成されるときの温度において無収縮であってもよい。
　なお、識別マーク７０の材料は、識別マーク７０の周囲のもの（第１実施形態では基材２９）と識別性が高い（視認性が高い）ことを条件として任意である。例えば、識別マーク７０は、樹脂や金属等を主材料としていてもよい。つまり、識別マーク７０は、セラミック以外を主材料としてもよい。また、識別マーク７０に含まれるガラス材の割合は、素体２０に含まれるガラス材の割合以下であってもよい。また、識別マーク７０は、ガラス材を含んでいなくてもよい。また、識別マーク７０は、識別マーク７０を基材２９と異なる色とするための着色材を含んでいてもよい。
　図１及び図３に示すように、素体２０は、第１部分６１と、第２部分６２とを備える。
　第１部分６１は、素体２０のうち、厚み方向１００から見て、識別マーク７０を囲み且つ識別マーク７０の外縁部７０Ａと接触する部分である。識別マーク７０の外縁部７０Ａは、厚み方向１００から見て、識別マーク７０の外縁と、当該外縁の近傍とよりなる部分である。第１実施形態において、厚み方向１００から見て、第１部分６１は、識別マーク７０の近傍に形成された円環状の部分である（図１参照）。
　第２部分６２は、素体２０のうち、厚み方向１００から見て、第１部分６１を囲む部分である。つまり、厚み方向１００から見て、第２部分６２は、第１部分６１より外側の部分である。第１実施形態において、第２部分６２は、第１部分６１の外縁部と接触している。第１部分６１の外縁部は、厚み方向１００から見て、第１部分６１の外縁と、当該外縁の近傍とよりなる部分である。以上より、厚み方向１００から見て、第２部分６２は、識別マーク７０との間に第１部分６１を挟んでいる。
　図３に示すように、第１部分６１は、第２部分６２に対して隆起している。第１実施形態において、第１部分６１の第２部分６２に対する隆起の高さ、言い換えると第１部分６１の第２部分６２からの厚み方向１００の突出長は、４μｍである。なお、第１部分６１の第２部分６２に対する隆起の高さは、４μｍに限らない。
　第１実施形態において、第１部分６１の隆起の高さは、識別マーク７０の突出先端部の高さと同一または略同一である。言い換えると、識別マーク７０の素体２０に対する突出方向において、第１部分６１の隆起先端部と、識別マーク７０の突出先端部とは、同位置または略同位置である。
　なお、第１部分６１の隆起の高さは、識別マーク７０の突出先端部の高さより低くてもよいし、識別マーク７０の突出先端部の高さより高くてもよい。
　図３に示すように、素体２０の基材２９は、第１層２９１と第２層２９２とを備える。
　第１層２９１は、第２層２９２に対して識別マーク７０の反対側に形成されており、第２層２９２に接している。第２層２９２は、識別マーク７０に接している。つまり、第２層２９２は、識別マーク７０及び第１層２９１の間に介在されている。
　前述したように、素体２０はセルシアンを含んでいる。つまり、素体２０の基材２９に設けられた第１層２９１及び第２層２９２の各々は、セルシアンを含んでいる。第２層２９２に含まれるセルシアンの割合は、第１層２９１に含まれるセルシアンの割合より低い。
　第１実施形態では、基材２９以外の基材２１～２８に含まれるセルシアンの割合は、第１層２９１に含まれるセルシアンの割合より低い。第１実施形態において、基材２１～２８は、第１層２９１と同様に、第１層に相当する。ここで、前述した内部電極４９は、基材２８，２９の間に介在されている。内部電極４９によって、基材２９の第２層２９２（つまり第１層２９１よりセルシアンの割合が低い領域）が、第１層に相当する基材２８にまで及ぶことが規制されている。言い換えると、内部電極４９は、第２層２９２の必要以上の拡がりを規制する防壁として機能している。
　第２層２９２の厚みＴ１は、識別マーク７０の最大厚みＴ２と同じである。ここで、第２層２９２の厚みＴ１は、例えば第２層２９２のうちの最大厚みまたは第２層２９２の平均厚みである。第１実施形態では、第２層２９２の厚みＴ１は、図３に示すように、位置にかかわらず同一である。第１実施形態では、識別マーク７０は、厚み方向１００から見て外縁部７０Ａから中央部へ向かうにしたがって、厚み方向１００に深くなっている。つまり、第１実施形態では、識別マーク７０の最大厚みＴ２は、識別マーク７０の中央部の厚みである。識別マーク７０の最大厚みＴ２に対応する位置は、識別マーク７０の形状、構成によって異なる位置となる。
　第２層２９２の厚みＴ１と識別マーク７０の最大厚みＴ２とは完全に同じでなくてもよい。例えば、セラミック電子部品１０の製造過程において、第２層２９２の厚みが位置毎に僅かなばらつきがある場合、厚みＴ１と最大厚みＴ２との間には当該ばらつき分の差が生じる。この場合、厚みＴ１は、最大厚みＴ２と略同じである。
　図２に示すように、めっき層８０は、外部電極５０を覆っている。めっき層８０は、外部電極５０に対する雰囲気や水分等の影響を抑制する。めっき層８０は、例えば、Ｎｉ（ニッケル）－Ｓｎ（スズ）やＮｉ（ニッケル）－無電解Ａｕ（金）等で構成された膜である。第１実施形態において、めっき層８０は、ニッケルで構成された内層８１と、金で構成された外層８２とを備える。内層８１は、外部電極５０の表面に形成されている。外層８２は、内層８１における外部電極５０の反対側に形成されている。
　第１実施形態において、めっき層８０は、２層（内層８１及び外層８２）で構成されているが、めっき層８０は、１層または３層以上で構成されていてもよい。
　第１実施形態によれば、厚み方向１００から見て素体２０の第１部分６１は識別マーク７０を囲んでおり、第１部分６１は素体２０の第２部分６２に対して隆起している。つまり、厚み方向１００から見て、識別マーク７０の周りに、第１部分６１と第２部分６２との間の段差が形成される。そのため、光学系のカメラで識別マーク７０が認識されるとき、当該段差によって陰影が形成される。これにより、識別マーク７０を認識することができる。よって、識別マーク７０の認識精度の低下が抑制される。
　第１実施形態によれば、厚み方向１００から見て、隆起した第１部分６１に識別マーク７０が囲まれている。これにより、第１部分６１が識別マーク７０に対する外部からの物理的衝撃に対する障壁となる。その結果、外部からの物理的衝撃に対する識別マーク７０の強度を高くすることができる。
　第１実施形態によれば、識別マーク７０の熱収縮率は、素体２０の熱収縮率より低い。この場合、セラミック電子部品１０の製造過程において、識別マーク７０が形成された素体２０が焼成されるときに、識別マーク７０と素体２０との熱収縮率の差に起因して、識別マーク７０の外縁部７０Ａ付近の素体２０の収縮が識別マーク７０によって阻害される。これにより、識別マーク７０の外縁部７０Ａ付近において、素体２０が隆起して第１部分６１が形成される。つまり、第１実施形態によれば、隆起した第１部分６１を容易に形成することができる。
　＜第１実施形態に係るセラミック電子部品の製造方法＞
　以下に、第１実施形態に係るセラミック電子部品１０の製造方法の一例が、図４～図８が参照されつつ説明される。図４は、本発明の第１実施形態に係るセラミック電子部品の製造過程において基材に層間接続導体が形成されたときの断面図である。図５は、本発明の第１実施形態に係るセラミック電子部品の製造過程において基材に内部電極が印刷されたときの断面図である。図６は、本発明の第１実施形態に係るセラミック電子部品の製造過程において基材に識別マークが印刷されたときの断面図である。図７は、本発明の第１実施形態に係るセラミック電子部品の製造過程において複数の基材が積層されて素体が形成されたときの断面図である。図８は、本発明の第１実施形態に係るセラミック電子部品の製造過程において素体が圧着されたときの断面図である。
　セラミック電子部品１０は、積層体を複数の素体２０に個片化することにより製造される。積層体は、複数の素体２０が配列された状態で一体化されたものである。図４～図８では、説明の便宜上、積層体のうち１つの素体２０に対応する部分のみが示される。第１実施形態に係るセラミック電子部品１０の製造方法は、シート成形工程、層間接続導体形成工程、電極形成工程、識別マーク形成工程、素体形成工程、圧着工程、個片化工程、焼成工程、及びめっき層積層工程を含む。
　（シート成形工程）
　最初に、シート成形工程が実行される。シート成形工程では、図２に示す基材２１～２９が個別に成形される。シート成形工程において成形される基材２１～２９は、各基材２１～２９に応じた主剤、可塑剤、バインダ等を含む原料を混合することにより、各基材２１～２９を構成するスラリが作製される。この段階での各基材２１～２９は、スラリで構成されたグリーンシートである。
　各基材２１～２９には、主剤として、例えば焼結性セラミック粉末等が使用される。可塑剤としては、例えば、フタル酸エステルやジ－ｎ－ブチルフタレート等が使用される。バインダとしては、例えば、アクリル樹脂やポリビニルブチラール等が使用される。
　各基材２１～２９を構成するスラリは、例えばリップコータやドクターブレード等を用いて、図４に示すキャリアフィルム１０１上にシート状に成形される。つまり、９枚の基材２１～２９の各々が、９枚のキャリアフィルム１０１の各々の上に成形される。キャリアフィルム１０１としては、例えば、ＰＥＴ（ポリエチレンテレフタレート）フィルム等が使用される。各基材２１～２９の厚さは、例えば５～１００（μｍ）である。
　図４には、キャリアフィルム１０１と、キャリアフィルム１０１上に成形された基材２６とが示されている。
　次に、各基材２１～２９及びキャリアフィルム１０１を厚み方向に貫通する貫通孔２０Ｄが形成される。
　なお、図４では、１つの貫通孔２０Ｄが基材２７及びキャリアフィルム１０１に形成されているが、各基材２１～２９に形成される貫通孔２０Ｄの数は１つに限らない。また、基材２１～２９と各基材２１～２９に対応するキャリアフィルム１０１とに形成される貫通孔２０Ｄの数は、同数であってもよいし、異なる数であってもよい。また、基材２１～２９と各基材２１～２９に対応するキャリアフィルム１０１とに形成される貫通孔２０Ｄの位置は、同じ位置であってもよいし、異なる位置であってもよい。
　第１実施形態に係るセラミック電子部品１０の製造方法では、最終的に、図２に示すような素体２０が形成されるように、９枚の基材２１～２９及びキャリアフィルム１０１に形成される貫通孔２０Ｄの数及び位置が決定される。
　（層間接続導体形成工程）
　次に、層間接続導体形成工程が実行される。層間接続導体形成工程では、シート成形工程において各基材２１～２９及びキャリアフィルム１０１に形成された貫通孔２０Ｄに、導電性のペースト１０２が充填される（図４参照）。貫通孔２０Ｄに充填されたペースト１０２が、層間接続導体３０に対応する。
　ペースト１０２は、例えば、導電性粉末と可塑剤とバインダとを含む原料を混合することにより作製される。
　（電極形成工程）
　次に、電極形成工程が実行される。電極形成工程では、内部電極４０及び外部電極５０が形成される。
　第１実施形態に係るセラミック電子部品１０の製造方法では、例えば、図５に示すように、基材２８の主面に、内部電極４９に対応するペーストが形成される。ペーストは、例えば、スクリーン印刷、インクジェット印刷、グラビア印刷等により形成される。なお、他の内部電極４０（内部電極４２～４８）及び外部電極５０も、内部電極４１と同様にして、各基材２１～２９に形成される。
　内部電極４０及び外部電極５０に対応するペーストは、前述したペースト１０２と同様に、導電性粉末と可塑剤とバインダとを含む原料を主として混合することにより作製される。なお、内部電極４０及び外部電極５０に対応するペーストは、ペースト１０２と同じ原料で構成されていてもよいし、ペースト１０２と異なる原料で構成されていてもよい。
　（識別マーク形成工程）
　次に、識別マーク形成工程が実行される。識別マーク形成工程では、識別マーク７０が形成される。
　第１実施形態に係るセラミック電子部品１０の製造方法では、図６に示すように、基材２９の主面に、識別マーク７０に対応するペーストが形成される。識別マーク７０に対応するペーストは、例えば、スクリーン印刷、インクジェット印刷、グラビア印刷、及び後述する転写工法等により形成される。識別マーク７０に対応するペーストは、前述した識別マーク７０を構成する材料（本製造方法ではアルミナ及びガラス材）よりなる。前述したように、識別マーク７０の材料は、任意である。例えば、識別マーク７０が導電性の材料を含む場合、識別マーク７０に対応するペーストは導電性ペーストであり、識別マーク７０が導電性の材料を含まない場合、識別マーク７０に対応するペーストは非導電性ペーストである。本製造工程では、識別マーク７０を構成する材料の熱収縮率は、基材２１～２９のうち少なくとも基材２９を構成する材料の熱収縮率より低い。
　（素体形成工程）
　次に、素体形成工程が実行される。素体形成工程では、図７に示すように、キャリアフィルム１０１を除いた各基材２１～２９が積層される。これにより、素体２０が得られる。
　素体形成工程では、９つの基材２１～２９が、数値の小さい基材から数値の大きい基材への順序で、具体的には基材２１，２２，２３，２４，２５，２６，２７，２８，２９の順序で積層される。これにより、基材２１の主面が素体２０の主面２０Ａとなり、基材２９の主面が素体２０の主面２０Ｂとなる。また、基材２１～２９の側面が素体２０の側面２０Ｃとなる。
　第１実施形態では、９つの基材２１～２９のうちの一部の基材は、９つの基材２１～２９のうちの当該一部の基材以外の基材に対して反転して積層される。図７に示す例では、基材２２～２９がキャリアフィルム１０１側の面を紙面下向きとして積層される一方で、基材２１がキャリアフィルム１０１側の面を紙面上向きとして積層される。これにより、図７に示すように、基材２２，２４，２５，２７，２８，２９に形成された内部電極４０及び識別マーク７０の各々が各基材２２，２４，２５，２７，２８，２９の上方に位置し、基材２１に形成された外部電極５０が基材２１の下方に位置する。
　（圧着工程）
　次に、圧着工程が実行される。圧着工程では、積層された各基材２１～２９が金型内で圧着される。
　各基材２１～２９が圧着されることによって、図８に示すように、内部電極４０が基材２２，２４，２５，２７，２８内へ入り込み、外部電極５０が基材２１内へ入り込み、識別マーク７０が基材２９内へ入り込む。これにより、識別マーク７０は、素体２０に埋設される。
　なお、圧着工程は実行されなくてもよい。この場合、識別マーク７０は、素体２０に埋設されない。
　（個片化工程）
　次に、個片化工程が実行される。個片化工程では、複数の素体２０が配列された積層体が、複数の素体２０に切断される。積層体の切断には、例えば、ダイシングソー、ギロチンカッタ、レーザ等が使用される。積層体の切断後、素体２０の角部および縁部は、例えばバレル加工等により研磨されてもよい（図２参照）。前記の研磨は、焼成工程後に実行されてもよい。
　（焼成工程）
　次に、焼成工程が実行される。焼成工程では、素体２０が焼成される。これにより、素体２０を構成する各基材２１～２９が硬化される。つまり、柔軟性のあるグリーンシートである各基材２１～２９が、硬化されて基板へ変質する（図２参照）。
　前述したように、識別マーク７０を構成する材料の熱収縮率は、基材２９を構成する材料の熱収縮率より低い。そのため、焼成工程において、識別マーク７０の収縮量は、基材２９の収縮量よりも小さい。よって、基材２９の識別マーク７０側への収縮は、識別マーク７０の外縁部７０Ａ（図８参照）によって阻害される。これにより、基材２９は、外縁部７０Ａ近傍において隆起する。この基材２９が隆起した部分が、第１部分６１（図１及び図３参照）である。
　また、焼成工程において、素体２０における識別マーク７０の周辺部では、素体２０における当該周辺部以外よりセルシアンが結晶化しにくい。これにより、素体２０において、当該周辺部に含まれるセルシアンの割合は、当該周辺部以外に含まれるセルシアンの割合より低くなる。素体２０における当該周辺部が第２層２９２に相当する。素体２０における当該周辺部以外が第１層２９１に相当する。
　（めっき層積層工程）
　次に、めっき層積層工程が実行される。めっき層積層工程では、外部電極５０に、公知のめっき処理が施される。これにより、図２に示すように、めっき層８０が、外部電極５０を覆うように積層される。
　図９は、本発明の第１実施形態に係るセラミック電子部品の製造過程の変形例において積層された複数の基材と識別マークが印刷されたフィルムとを示す断面図である。識別マーク７０は、転写工法によって基材２９に形成されてもよい。
　転写工法の場合、図９に示すように、転写シート１０３の主面１０３Ａに識別マーク７０が印刷される。その後、素体形成工程において、転写シート１０３の主面１０３Ａが基材２９側となるように、転写シート１０３が基材２９に積層される。これにより、識別マーク７０が、転写シート１０３から基材２９に転写される（図７参照）。
　前述したセラミック電子部品１０の製造方法では、熱収縮率の異なる素体２０及び識別マーク７０が焼成されることによって、素体２０に第１部分６１が形成される。しかし、第１部分６１が形成される製造方法は、これに限らない。
　例えば、圧着工程の前に、基材２９の主面の識別マーク７０及びその外周近傍を除く領域（言い換えると第２部分６２に対応する領域）に、熱によって焼失する材料からなるペーストが形成される。その後の圧着工程において、当該ペーストが基材２９に埋設される。その後の焼成工程において、当該ペーストが焼失する。これにより、当該ペーストが形成されていた領域に、当該ペーストが形成されていなかった領域に対して凹んだ第２部分６２が形成される。つまり、当該ペーストが形成されていなかった領域に、当該ペーストが形成されていた領域に対して隆起した第１部分６１が形成される。
＜第１実施形態の変形例＞
　第１実施形態では、識別マーク７０の熱収縮率が素体２０の熱収縮率より低い例が説明されたが、これに限らない。識別マーク７０の熱収縮率は、素体２０の熱収縮率と同じでもよいし、素体２０の熱収縮率より高くてもよい。
　識別マーク７０の熱収縮率が素体２０の熱収縮率以上の場合、例えば、以下のようにして、素体２０の第１部分６１が形成される。以下に詳述する。例えば、焼成工程において、銅等の金属は、セラミックよりも先に焼結が進む。この焼結の進行の差は、例えば金属とセラミックとの融点や粒径の差による。すると、識別マーク７０の主材料が銅等の金属である場合、セラミック電子部品１０の製造工程の焼成工程において、金属を主材料とする識別マーク７０が収縮して固まるタイミングが、セラミックを主材料とする素体２０が収縮して固まるタイミングより早い。この場合、素体２０が収縮するときに、既に固まった識別マーク７０が壁となる。これにより、基材２９の識別マーク７０側への収縮は、識別マーク７０によって阻害される。その結果、基材２９は、識別マーク７０の外縁部７０Ａ近傍において隆起する。この基材２９が隆起した部分が、第１部分６１（図１及び図３参照）である。
　なお、識別マーク７０の熱収縮率が素体２０の熱収縮率より低い場合には、熱収縮率の差による識別マーク７０と素体２０との収縮量の差と、識別マーク７０と素体２０との収縮タイミングの違いとの双方に起因して、基材２９の隆起が起こり得る。
＜第２実施形態＞
　図１０は、本発明の第２実施形態に係るセラミック電子部品における図２の一点鎖線部に対応する部分の拡大図である。第２実施形態に係るセラミック電子部品１０Ａが第１実施形態に係るセラミック電子部品１０と異なる点は、素体２０に拡散層９０が形成されている点である。なお、第１実施形態に係るセラミック電子部品１０においても、素体２０に拡散層９０が形成されていてもよい。
　図１０に示すように、セラミック電子部品１０Ａの素体２０には、拡散層９０が形成されている。拡散層９０は、素体２０の基材２９における識別マーク７０との界面部に形成されている。素体２０の基材２９における識別マーク７０との界面部は、基材２９の識別マーク７０との界面と、基材２９における当該界面の近傍とよりなる部分である。
　拡散層９０は、識別マーク７０から拡散された物質（識別マーク７０を構成する物質）によって素体２０の組成が変化した層である。例えば、セラミック電子部品１０の製造過程の焼成工程において、識別マーク７０を構成する物質であるアルミナが素体２０の基材２９の界面部へ拡散する。拡散したアルミナによって、基材２９を構成する材料の組成が変化する。具体的には、基材２９の識別マーク７０との界面部におけるアルミナの割合が、基材２９の当該界面部以外の部分におけるアルミナの割合より高くなる。このアルミナの割合が高くなった部分（基材２９の識別マーク７０との界面部）が、拡散層９０である。なお、図３では、拡散層９０は一定の厚みに示されているが、拡散層９０の厚みにはばらつきが生じ得る。
　第２実施形態では、第１実施形態と同様に、素体２０はガラス材を含んでおり、識別マーク７０はガラス材を含んでいる。拡散層９０は、識別マーク７０から界面部に拡散された物質であるガラス材が素体２０の界面部に含まれるガラス材と結合することによって、素体２０の組成が変化した層である。つまり、拡散層９０において、前記素体に含まれるガラス材と前記識別マークに含まれるガラス材とが結合されている。なお、素体２０に含まれるガラス材と識別マーク７０に含まれるガラス材とは、同じ種類であってもよいし、異なる種類であってもよい。
　第２実施形態によれば、セラミック電子部品１０Ａの製造工程において、素体２０に含まれるガラス材と識別マーク７０に含まれるガラス材とが結合することによって拡散層９０が形成される。これにより、素体２０と識別マーク７０とにガラス材が含まれていない構成（拡散層９０において、素体２０に含まれるガラス材と識別マーク７０に含まれるガラス材とが結合されていない構成）よりも、識別マーク７０と素体２０との密着性を高めることができる。
　なお、拡散層９０は、前述したように、識別マーク７０から拡散された物質（識別マーク７０を構成する物質）によって素体２０の組成が変化した層である。この限りにおいて、拡散層９０はガラス材以外で構成されていてもよい。例えば、識別マーク７０から拡散された物質は、ガラス材以外であるアルミナであってもよいし、前述したようにガラス材であってもよい。また、例えば、アルミナ及びガラス材の双方が識別マーク７０から拡散された物質であってもよい。
　第２層２９２は、拡散層９０に対して識別マーク７０の反対側に形成されており、拡散層９０に接している。つまり、第２層２９２は、識別マーク７０との間に拡散層９０を挟んでいる。
　なお、各実施形態において、識別マーク７０に含まれるガラス材が識別マーク７０のうちの外部に露出した部分に堆積されていてもよい。この場合、第２実施形態に係るセラミック電子部品１０Ａにおいて、識別マーク７０は、拡散層９０と前記の堆積されたガラス材の層とによって囲まれる。
　第２実施形態によれば、拡散層９０によって、識別マーク７０と素体２０の第１部分６１との間の密着性が高まるため、識別マーク７０が素体２０から滑落する可能性を低くすることができる。また、識別マーク７０と素体２０の第１部分６１との間の密着性が高まるため、識別マーク７０と素体２０の第１部分６１との間から素体２０の内部への液体の浸入を低減することができる。
　セラミック電子部品１０Ａの製造工程は、第１実施形態に係るセラミック電子部品１０の製造工程と同様である。但し、セラミック電子部品１０Ａの製造工程では、焼成工程において、識別マーク７０に含まれるアルミナが基材２９へ拡散することによって、拡散層９０が形成される。
　拡散層９０が形成された状態で、識別マーク７０と基材２９とが収縮する。この場合、識別マーク７０と基材２９とは拡散層９０によって互いに密着した状態で収縮する。収縮した識別マーク７０が拡散層９０を通じて基材２９を引っ張り、また、基材２９自身が拡散層９０側へ収縮する。これにより、基材２９は、拡散層９０における外縁部７０Ａ近傍において隆起する。この基材２９が隆起した部分が、第１部分６１（図１及び図３参照）である。
　第２実施形態では、前記のように、拡散層９０が形成されていることによって基材２９の隆起が起こる。そのため、第２実施形態では、識別マーク７０の熱収縮率は、素体２０の熱収縮率より低くてもよいし、素体２０の熱収縮率以上でもよい。
　なお、前記様々な実施形態のうちの任意の実施形態を適宜組み合わせることにより、それぞれの有する効果を奏するようにすることができる。
　本発明は、適宜図面を参照しながら好ましい実施の形態に関連して充分に記載されているが、この技術に熟練した人々にとっては種々の変形や修正は明白である。そのような変形や修正は、添付した請求の範囲による本発明の範囲から外れない限りにおいて、その中に含まれると理解されるべきである。
　　１０　セラミック電子部品
　　２０　素体
　２０Ｂ　主面（表面）
　　６１　第１部分
　　６２　第２部分
　　７０　識別マーク
　７０Ａ　外縁部
　　９０　拡散層

Claims (4)

  1. 　セラミックを主材料とする素体と、
    　前記素体の表面に形成され、少なくとも一部が前記素体の表面から突出した識別マークと、を備え、
    　前記素体は、
    　前記素体の表面と直交する方向から見て、前記識別マークを囲み且つ前記識別マークの外縁部と接触する第１部分と、
    　前記素体の表面と直交する方向から見て、前記第１部分を囲む第２部分と、を備え、
    　前記第１部分は、前記第２部分に対して隆起しているセラミック電子部品。
  2. 　前記識別マークの熱収縮率は、前記素体の熱収縮率より低い請求項１に記載のセラミック電子部品。
  3. 　前記識別マークは、セラミックを主材料とし、
    　前記素体は、前記第１部分と前記識別マークとの界面部に拡散層を有し、
    　前記拡散層は、前記識別マークから拡散された前記識別マークを構成する物質によって前記素体の組成が変化した層である請求項１または２に記載のセラミック電子部品。
  4. 　前記素体及び前記識別マークの各々は、ガラス材を含み、
    　前記拡散層において、前記素体に含まれるガラス材と前記識別マークに含まれるガラス材とが結合されている請求項３に記載のセラミック電子部品。
PCT/JP2022/045631 2021-12-17 2022-12-12 セラミック電子部品 WO2023112883A1 (ja)