WO2023100676A1 - 中空シリカ粒子及びその製造方法 - Google Patents

中空シリカ粒子及びその製造方法 Download PDF

Info

Publication number
WO2023100676A1
WO2023100676A1 PCT/JP2022/042755 JP2022042755W WO2023100676A1 WO 2023100676 A1 WO2023100676 A1 WO 2023100676A1 JP 2022042755 W JP2022042755 W JP 2022042755W WO 2023100676 A1 WO2023100676 A1 WO 2023100676A1
Authority
WO
WIPO (PCT)
Prior art keywords
hollow silica
silica particles
particles
density
oil
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2022/042755
Other languages
English (en)
French (fr)
Inventor
博道 加茂
肇 片山
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
AGC Si Tech Co Ltd
AGC Inc
Original Assignee
Asahi Glass Co Ltd
AGC Si Tech Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Asahi Glass Co Ltd, AGC Si Tech Co Ltd filed Critical Asahi Glass Co Ltd
Priority to CN202280079036.6A priority Critical patent/CN118317921A/zh
Priority to KR1020247017704A priority patent/KR20240112850A/ko
Priority to JP2023564875A priority patent/JPWO2023100676A1/ja
Publication of WO2023100676A1 publication Critical patent/WO2023100676A1/ja
Priority to US18/675,502 priority patent/US20240308858A1/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

本発明は、比誘電率および誘電損失のいずれもが十分に小さく、また樹脂への分散性にも優れる、新たな中空シリカ粒子を提供する。本発明の中空シリカ粒子は、シリカを含むシェル層を備え、シェル層の内部に空間部を有する中空シリカ粒子であって、アルゴンガスを用いた乾式ピクノメーターによる密度測定により求めた粒子の密度をＡ（ｇ／ｃｍ３）、ＢＥＴ比表面積をＢ（ｍ２／ｇ）とすると、密度とＢＥＴ比表面積との積（Ａ×Ｂ）が１～１２０ｍ２／ｃｍ３である。

Description

中空シリカ粒子及びその製造方法
　本発明は、中空シリカ粒子及びその製造方法に関する。
　近年、電子機器の小型化、信号の高速化および配線の高密度化が求められている。この要求を満たすために、接着フィルム、プリプレグ等の絶縁樹脂シート、並びにプリント配線板に形成される絶縁層に用いられる樹脂組成物を、低比誘電率化、低誘電正接化、低熱膨張化することが求められている。
　これらの要求を満たすために、充填材として中空粒子を用いた検討が行われており、種々の提案がなされている。例えば特許文献１では、（Ａ）エポキシ樹脂、（Ｂ）硬化剤、（Ｃ）中空シリカ、および（Ｄ）溶融シリカを含有する樹脂組成物が記載されている。また、特許文献２では、中空粒子と熱硬化性樹脂とを含有する低誘電樹脂組成物において、中空粒子として、シェル全体の９８質量％以上がシリカで形成されており、平均空隙率が３０～８０体積％であり、かつ平均粒径が０．１～２０μｍである低誘電樹脂組成物が記載されている。
　また、低比誘電率材料として使用される中空シリカ材料についても種々提案がされており、例えば特許文献３には、気孔を有するシェルを有する閉空洞構造を有し、空洞容積率が０～８６％、比誘電率が１．５～３．３、２０～４３．５ＧＨｚ周波数帯域での流動のための比誘電率が１．５～３．３、誘電損失角正接が０．０００５～０．００４である中空シリカ材料が提案されている。
日本国特開２０１３－１７３８４１号公報 日本国特開２００８－０３１４０９号公報 中国特許出願公開第１１１２３２９９３号明細書
　しかしながら、従来の中空シリカ粒子は、溶媒に添加したとき、粒子内部に溶媒が浸透してしまい、目的とする利用ができなくなるということがあった。例えば、中空シリカ粒子をメチルエチルケトンに添加した場合、粒子内部にメチルエチルケトンが含浸して、組成物の粘度が上がってしまい、中空シリカ粒子の添加量が上げられず、十分な低比誘電率化が達成できなかった。
　また、特許文献３に記載された中空シリカ材料は、その実施例では、テンプレートの無機化合物に対してシリカを被覆し、テンプレートを除去したのち、シリカゾルを添加して熟成し、中空シリカ粒子を得ているが、この方法ではテンプレートの無機化合物が凝集しやすく、一次粒子同士の凝集や、凝集径を制御できない問題があった。また一次粒子同士の凝集した点が中空シリカのシェルの欠点となりやすく、そこに樹脂ワニスを抱き込むため、分散性が悪化しやすかった。また、テンプレートの分散の制御が難しく、二次粒子径が大きくなりやすい問題があった。
　本発明は上記課題に鑑みてなされたものであり、比誘電率および誘電正接のいずれもが十分に小さく、また樹脂への分散性にも優れる、新たな中空シリカ粒子を提供することを課題とする。
　本発明は、下記（１）～（１８）に関するものである。
（１）シリカを含むシェル層を備え、前記シェル層の内部に空間部を有する中空シリカ粒子であって、アルゴンガスを用いた乾式ピクノメーターによる密度測定により求めた粒子の密度をＡ（ｇ／ｃｍ３）、ＢＥＴ比表面積をＢ（ｍ２／ｇ）とすると、前記密度と前記ＢＥＴ比表面積との積（Ａ×Ｂ）が１～１２０ｍ２／ｃｍ３である中空シリカ粒子。
（２）前記アルゴンガスを用いた乾式ピクノメーターによる密度測定により求めた粒子の密度が０．３５～２．００ｇ／ｃｍ３である、前記（１）に記載の中空シリカ粒子。
（３）ヘリウムガスを用いた乾式ピクノメーターによる密度測定により求めた粒子の密度が２．００～２．３５ｇ／ｃｍ３である、前記（１）又は（２）に記載の中空シリカ粒子。
（４）平均一次粒子径が５０ｎｍ～１０μｍである、前記（１）～（３）のいずれか１つに記載の中空シリカ粒子。
（５）一次粒子のうち、粒子全体の３５％以上が平均一次粒子径±４０％以内の粒子径である、前記（１）～（４）のいずれか１つに記載の中空シリカ粒子。
（６）前記ＢＥＴ比表面積が１～１００ｍ２／ｇである、前記（１）～（５）のいずれか１つに記載の中空シリカ粒子。
（７）真球度が０．７５～１．０である、前記（１）～（６）のいずれか１つに記載の中空シリカ粒子。
（８）二次粒子のメジアン径（Ｄ５０）が０．１～１０μｍである、前記（１）～（７）のいずれか１つに記載の中空シリカ粒子。
（９）二次粒子の粗大粒径（Ｄ９０）が１～３０μｍである、前記（１）～（８）のいずれか１つに記載の中空シリカ粒子。
（１０）前記中空シリカ粒子に含まれるＬｉ、Ｎａ、Ｋ、Ｒｂ、Ｃｓ、Ｍｇ、Ｃａ、Ｓｒ及びＢａからなる群から選択される１種以上の金属Ｍの濃度の総和が５０質量ｐｐｍ以上１質量％以下である、前記（１）～（９）のいずれか１つに記載の中空シリカ粒子。
（１１）前記中空シリカ粒子を含む混練物の、下記測定方法により測定される粘度が１００００ｍＰａ・ｓ以下である、前記（１）～（１０）のいずれか１つに記載の中空シリカ粒子。
（測定方法）
　アルゴンガスを用いた乾式ピクノメーターによる密度測定により求めた粒子の密度をＡ（ｇ／ｃｍ３）として、煮アマニ油６質量部と前記中空シリカ粒子（６×Ａ／２．２）質量部を混合し、２０００ｒｐｍで３分間混練して得た混練物を、回転式レオメータを用いてせん断速度１ｓ－１で３０秒測定し、３０秒時点での粘度を求める。
（１２）固体２９Ｓｉ－ＤＤ／ＭＡＳ－ＮＭＲにより測定した、シラノール基由来のＯＨ基を持たないＱ４構造に対するシラノール基由来のＯＨ基を１つ有するＱ３構造のモル比率（Ｑ３／Ｑ４）が、２～４０％である、前記（１）～（１１）のいずれか１つに記載の中空シリカ粒子。
（１３）前記（１）～（１２）のいずれか１つに記載の中空シリカ粒子の製造方法であって、水相、油相及び界面活性剤を含む水中油型エマルションを作製し、前記水中油型エマルションを０．５～２４０時間静置し、前記水中油型エマルション中でコアの外周にシリカを含むシェル層が形成された中空シリカ前駆体を得て、前記中空シリカ前駆体から前記コアを除去し、熱処理する中空シリカ粒子の製造方法。
（１４）熱処理後の粒子に対してシランカップリング剤で表面処理する、前記（１３）に記載の中空シリカ粒子の製造方法。
（１５）前記水中油型エマルションに、シリカ原料を添加する、前記（１３）又は（１４）に記載の中空シリカ粒子の製造方法。
（１６）シリカ源としてケイ酸ナトリウムを用いる、前記（１５）に記載の中空シリカ粒子の製造方法。
（１７）前記（１）～（１２）のいずれか１つに記載の中空シリカ粒子を、５～７０質量％含む樹脂組成物。
（１８）前記（１）～（１２）のいずれか１つに記載の中空シリカ粒子を、１～４０質量％含むスラリー組成物。
　本発明の中空シリカ粒子は、緻密なシェル層を有し、比表面積が小さいので、比誘電率および誘電正接のいずれも十分に小さくできる。本発明の中空シリカ粒子はメチルエチルケトンやＮ－メチルピロリドンなどの溶媒が浸透し難いので、樹脂組成物中でも優れた低比誘電率および低誘電正接が発揮できる。また、本発明の中空シリカ粒子は適度な比表面積を持っており、樹脂への分散性に優れている。
図１は、例１で得られた中空シリカ粒子の走査型電子顕微鏡像（ＳＥＭ像）を示す。
　以下、本発明について説明するが、以下の説明における例示によって本発明は限定されない。
　尚、本明細書において、「質量」は「重量」と同義である。
（中空シリカ粒子）
　本発明の中空シリカ粒子は、シリカを含むシェル層（固体膜）を備え、シェル層の内部に空間部を有する。中空シリカ粒子がシェル層の内部に空間部を持つことは、透過型電子顕微鏡（ＴＥＭ）観察や走査型電子顕微鏡（ＳＥＭ）観察により確認できる。ＳＥＭ観察の場合は、一部が開口した破損粒子を観察することにより、中空であることが確認できる。ＴＥＭ観察やＳＥＭ観察によって確認できる、内部に空間部を持つ球状の粒子を「一次粒子」と定義する。なお、中空シリカ粒子は、焼成や乾燥の工程によって一次粒子同士が一部結合するため、製造で得られた中空シリカ粒子は一次粒子が凝集した二次粒子の集合体となっていることが多い。
　本明細書において、シェル層が「シリカを含む」とは、シリカ（ＳｉＯ２）が５０質量％以上含まれることを意味する。シェル層の組成は、ＩＣＰ発光分析法やフレーム原子吸光法などによって測定できる。シェル層が含むシリカは８０質量％以上が好ましく、９５質量％以上がより好ましい。上限は理論的に１００質量％である。シェル層が含むシリカは１００質量％未満が好ましく、９９．９９質量％以下がより好ましい。残分としてはアルカリ金属酸化物およびケイ酸塩、アルカリ土類金属酸化物およびケイ酸塩、カーボン等が挙げられる。
　また、「シェル層の内側に空間部を有する」とは、１個の一次粒子の断面を観察した際に、１個の空間部の周囲をシェル層が囲んでいる中空状態を意味する。すなわち中空粒子１個は、大きな空間部を１個とそれを取り囲むシェル層とを有する。
　本発明の中空シリカ粒子がシェル内に空間部を有する構造であることで、当該粒子をフィラーとして溶媒に加えると、組成物中により多くの空間を確保できる。よって、電子機器等の絶縁層に用いたときには、誘電率を下げられる。
　本発明の中空シリカ粒子は、アルゴンガスを用いた乾式ピクノメーターによる密度測定により求めた粒子の密度（以下、Ａｒ密度ともいう。）をＡ（ｇ／ｃｍ３）、ＢＥＴ比表面積をＢ（ｍ２／ｇ）とすると、Ａｒ密度とＢＥＴ比表面積との積（Ａ×Ｂ）が１～１２０ｍ２／ｃｍ３である。Ａ×Ｂにより中空シリカ粒子を溶媒中に分散させたときの体積当たりの比表面積が示され、例えば、樹脂に添加したときには、樹脂中の所定体積に中空シリカ粒子が占める部分の比表面積を示す。粒子のＡｒ密度とＢＥＴ比表面積が前記の関係を満たすことで、本発明の中空シリカ粒子を含有した樹脂組成物を絶縁層に用いたときは、絶縁層の誘電率を下げて、誘電損失を低下できるので、高周波回路に十分対応できる基盤を提供できる。Ａ×Ｂが１２０ｍ２／ｃｍ３以下であると、溶媒中でのシリカの比表面積が小さいため、組成物の粘度が上がり過ぎることがない。組成物の粘度が上がり過ぎると、誘電正接が悪くなるおそれがあるが、１２０ｍ２／ｃｍ３以下であることで誘電正接の悪化を抑制できる。Ａ×Ｂは、８０ｍ２／ｃｍ３以下であるのが好ましく、４０ｍ２／ｃｍ３以下がより好ましく、２０ｍ２／ｃｍ３以下がさらに好ましい。また、Ａ×Ｂが上記より小さいものを作製することは実質困難である。Ａ×Ｂは、２ｍ２／ｃｍ３以上であるのが好ましく、２．５ｍ２／ｃｍ３以上がより好ましく、３ｍ２／ｃｍ３以上がさらに好ましい。
　本発明の中空シリカ粒子は、アルゴンガスを用いた乾式ピクノメーターによる密度測定により求めた粒子の密度（Ａｒ密度）が０．３５～２．００ｇ／ｃｍ３であるのが好ましい。Ａｒ密度が０．３５ｇ／ｃｍ３以上であると、例えば樹脂との比重差が大きくなり過ぎないので、樹脂組成物中での分散性を向上できる。Ａｒ密度が２．００ｇ／ｃｍ３以下であると、誘電率の低減効果を発揮しやすい。Ａｒ密度の下限は、０．４０ｇ／ｃｍ３以上であるのがより好ましく、また上限は、１．５０ｇ／ｃｍ３以下であるのがより好ましく、１．００ｇ／ｃｍ３以下がさらに好ましい。具体的に、Ａｒ密度は、０．３５～１．５０ｇ／ｃｍ３がより好ましく、０．４０～１．００ｇ／ｃｍ３がさらに好ましい。
　本発明の中空シリカ粒子は、ヘリウムガスを用いた乾式ピクノメーターによる密度測定により求めた粒子の密度（以下、Ｈｅ密度ともいう。）が２．００～２．３５ｇ／ｃｍ３であるのが好ましい。ヘリウムガスは微細な空隙を透過するため、内部に空間を有するシリカ粒子の、シリカ部分の真密度に対応する密度が得られる。Ｈｅ密度が２．００ｇ／ｃｍ３以上であると、中空シリカ粒子に含まれるシラノール残存量が少なくなるため、誘電正接を下げやすい。Ｈｅ密度が２．３５ｇ／ｃｍ３を上回るようなシリカ質を得るにはかなり高い温度での焼成が必要であり、また、粒子が破損しやすくなる。Ｈｅ密度が２．３５ｇ／ｃｍ３以下であると、中空シリカ粒子中に含まれる空間を維持できまたＡｒ密度を悪化させることがない。Ｈｅ密度の下限は、２．０５ｇ／ｃｍ３以上であるのがより好ましく、２．１０ｇ／ｃｍ３以上がさらに好ましく、また上限は、２．３３ｇ／ｃｍ３以下であるのがより好ましく、２．３０ｇ／ｃｍ３以下がさらに好ましい。具体的に、Ｈｅ密度は、２．０５～２．３５ｇ／ｃｍ３がより好ましく、２．１０～２．３３ｇ／ｃｍ３がさらに好ましい。
　中空シリカ粒子の見かけ密度は比重瓶を用いて測定することもできる。比重瓶に試料（中空シリカ粒子）と有機溶媒を入れ、２５℃で４８時間静置後測定する。中空シリカ粒子のシェルの緻密度によっては有機溶媒の浸透に時間を要することもあるため、上記の時間静置することが好ましい。この方法で測定した結果は、アルゴンガスを用いた乾式ピクノメーターによる密度測定の結果と対応する。
　本発明の中空シリカ粒子は一次粒子径と殻の厚みを調整することで、粒子の見かけ密度を調整できる。粒子の密度を変えることで、溶媒中に沈降するか、分散し続けるか、上に浮くかを調整できる。溶媒中に分散させたい場合は、溶媒の密度と粒子の見かけ密度が近いことが望ましい。例えば、密度が１．０ｇ／ｃｍ３の水に分散させたい場合は、粒子の見かけ密度を０．８ｇ／ｃｍ３以上１．２ｇ／ｃｍ３以下に調整するのが好ましい。
　中空シリカ粒子の試料中、シェル層が破損せず、内部に空間部を保有している完全な中空粒子の割合を中空粒子率という。本発明の中空シリカ粒子はシェル層が緻密であるため、各種溶媒やアルゴンガスおよびアルゴン分子より動的分子径が大きいガスは浸透し難いものであるが、シェル層が破損した粒子（破損粒子）が存在すると、その内部に侵入する。よって、中空粒子率で見かけ密度が変化する。中空粒子率が高いほど中空シリカ試料の見かけ密度は小さくなり、中空粒子率が低いほど、中空シリカ試料の見かけ密度は高くなる。これを利用して、収率１００％と仮定したとき、原料の仕込み量から求められる理論的な密度と、乾式ピクノメーターで測定した見かけ密度から中空粒子率が求められる。
　また、中空シリカ粒子を製造する際の、オイルコアを除去する前のろ過後のケーキを用いて、熱処理時の重量変化からも中空粒子率は求められる。ろ過後のケーキをほぐして一晩乾燥すると、破損粒子内のオイル成分は揮発し、完全な中空粒子内のオイル成分は保持される。仕込んだオイル成分が全て揮発した場合（中空粒子率０％）と、全て保持された場合（中空粒子率１００％）の熱処理時の重量変化量を原料の仕込み量から計算できるので、ろ過後一晩乾燥した試料を８００℃まで熱処理したときの重量変化から中空粒子率が求められる。
　また、本発明の中空シリカ粒子は、ＢＥＴ比表面積が１～１００ｍ２／ｇであるのが好ましい。ＢＥＴ比表面積を１ｍ２／ｇ未満とすることは実質的に困難である。また、ＢＥＴ比表面積が１００ｍ２／ｇ以下であると、樹脂組成物としたときの粘度上昇を抑制でき、樹脂組成物中での分散性が悪くなることがない。ＢＥＴ比表面積は、１～１００ｍ２／ｇが好ましく、１～５０ｍ２／ｇがより好ましく、１～２０ｍ２／ｇがさらに好ましく、１～１５ｍ２／ｇが最も好ましい。
　ここで、ＢＥＴ比表面積の測定は、比表面積測定装置（例えば、株式会社島津製作所製「トライスターＩＩ３０２０」）を用い、前処理として中空シリカ粒子を２３０℃で５０ｍＴｏｒｒとなるまで乾燥させた後、窒素ガスを用いた多点法で測定できる。
　中空シリカ粒子の真球度は、０．７５～１．０であることが好ましい。真球度が低くなると、中空シリカ粒子が破損しやすくなり、Ａｒ密度が低下して、比表面積が大きくなり、誘電正接が上昇する場合がある。
　真球度は、走査型電子顕微鏡（ＳＥＭ）により写真撮影して得られる写真投影図における任意の１００個の粒子について、それぞれの最大径（ＤＬ）と、これと直交する最小径（ＤＳ）とを測定し、最大径（ＤＬ）に対する最小径（ＤＳ）の比（ＤＳ／ＤＬ）を算出した平均値で表すことができる。
　分散性などの観点から、真球度は、０．８０以上であることがより好ましく、０．８２以上がさらに好ましく、０．８３以上がよりさらに好ましく、０．８５以上が特に好ましく、０．８７以上が殊更に好ましく、０．９０以上が最も好ましい。
　中空シリカ粒子の一次粒子の大きさは、ＳＥＭ観察によりその粒子径（直径）を直接観察することによって求められる。具体的には、ＳＥＭ画像より１００個の粒子の一次粒子の大きさを測定し、それらを集計して得られた一次粒子の大きさ（粒子径）の分布を、全体の一次粒子の大きさの分布と推定する。ＳＥＭ観察により、解凝集が難しい粒子の一次粒子径を直接測定できる。
　この一次粒子の大きさは、凝集粒子の粒子表面状態に反映されるため、比表面積および吸油量を決めるパラメータとなる。
　一次粒子の大きさの平均値（平均一次粒子径）は５０ｎｍ～１０μｍの範囲であることが好ましい。平均一次粒子径が５０ｎｍ未満であると、比表面積、吸油量および細孔容積が上昇し、粒子表面のＳｉＯＨ量と吸着水が増え、誘電正接が上昇しやすくなる。また、平均一次粒子径が１０μｍ以下であると、フィラーとしての取り扱いがしやすい。
　平均一次粒子径は、製造再現性の観点から、下限は、７０ｎｍ以上であることがより好ましく、１００ｎｍ以上が最も好ましく、また上限は、５μｍ以下であることがより好ましく、３μｍ以下が特に好ましい。
　本発明の中空シリカ粒子は、上記した平均一次粒子径を有し、その一次粒子のうち、粒子全体の３５％以上が平均一次粒子径±４０％以内の粒子径であるのが好ましい。３５％以上の粒子の粒子径が平均一次粒子径±４０％以内であると、中空シリカ粒子の大きさが均一となるので、中空シリカ粒子のシェルの欠点が生成しにくい。粒子全体の４０％以上が平均一次粒子径±４０％以内であるのがより好ましく、粒子全体の５０％以上が平均一次粒子径±４０％以内であるのがさらに好ましく、粒子全体の６０％以上が平均一次粒子径±４０％以内であるのが特に好ましく、粒子全体の７０％以上が平均一次粒子径±４０％以内であるのが最も好ましい。
　中空シリカ粒子の二次粒子のメジアン径（Ｄ５０）は、０．１～１０μｍであることが好ましい。
　メジアン径が０．１μｍ以上であると、樹脂組成物とした際の粘度上昇や、分散性の悪化を抑制できる。メジアン径（Ｄ５０）は、０．２μｍ以上であることがより好ましく、０．２５μｍ以上がさらに好ましく、０．３μｍ以上が特に好ましい。また、メジアン径が大き過ぎると、樹脂組成物を膜に成型した際、粒立ちの原因となるため、１０μｍであるのが好ましく、８μｍ以下がより好ましく、７μｍ以下がさらに好ましく、５μｍ以下が特に好ましく、３μｍ以下が最も好ましい。
　二次粒子の粒径（一次粒子の凝集時の凝集径）はレーザー散乱によって測定することが好ましい。ＳＥＭによって凝集径を測定することは、粒子間の境目が不明瞭で、ウエットな状態での分散を反映しないためである。また、コールターカウンターによる測定では、中空粒子と中実粒子での電場変化が異なり、中実粒子に対して対応した数値を出すことが困難であるためである。
　中空シリカ粒子の二次粒子の粗大粒径（Ｄ９０）は、１～３０μｍであることが好ましい。粗大粒径が小さい粒子を作製する場合は、反応液中のシリカ源の濃度を下げる必要があり、生産性が悪化するため、生産効率の観点から、粗大粒径は１μｍ以上であることが好ましい。また、粗大粒径が大きすぎると、樹脂組成物を膜に成型した際、粒立ちの原因となるため、３０μｍ以下であることが好ましい。粗大粒径は、下限は３μｍ以上であることがより好ましく、５μｍ以上が最も好ましく、また上限は３０μｍ以下であることが好ましく、２５μｍ以下がより好ましく、２０μｍ以下がさらに好ましく、１５μｍ以下が最も好ましい。
　なお、粗大粒径も上記したように、レーザー散乱によって二次粒子の粒径を測定することにより求められる。
　中空シリカ粒子のシェル厚さは、一次粒子の直径１に対して、０．０１～０．３であることが好ましい。シェル厚さが一次粒子の直径１に対して０．０１より小さいと、中空シリカ粒子の強度が低下することがある。この比が０．３より大きいと、内部の空間部が小さくなってしまい、中空形状であることによる特性が出なくなってしまう。
　シェル厚さは、一次粒子の直径１に対して、０．０２以上であることがより好ましく、０．０３以上がさらに好ましく、また０．２以下であることがより好ましく、０．１以下がさらに好ましい。
　ここで、シェル厚さは、透過型電子顕微鏡（ＴＥＭ）によって個々の粒子のシェル厚さを測定することによって求められる。
　中空シリカ粒子は内部に空間部を有するため、粒子内部に物質を内包できる。本発明の中空シリカ粒子はシェル層が緻密であるため各種溶媒が浸透し難いものであるが、破損粒子が存在すると、内部に溶媒が浸入する。よって、破損粒子の割合で吸油量が変化する。
　中空シリカ粒子の吸油量は、１５～１３００ｍＬ／１００ｇであることが好ましい。吸油量が１５ｍＬ／１００ｇ以上であると樹脂組成物に用いた際に樹脂との密着性が確保でき、１３００ｍＬ／１００ｇ以下であると樹脂組成物に用いた際に樹脂の強度が担保でき、組成物の粘度を低下できる。
　吸油量が多いと樹脂組成物に含有したときに該組成物の粘性が高くなることから、中空シリカ粒子の吸油量は、１０００ｍＬ／１００ｇ以下であることがより好ましく、７００ｍＬ／１００ｇ以下がさらに好ましく、５００ｍＬ／１００ｇ以下が特に好ましく、２００ｍＬ／１００ｇ以下が最も好ましい。また、吸油量が低すぎると粉体と樹脂との密着性が悪化する場合があるため、２０ｍＬ／１００ｇ以上であることがより好ましい。
　吸油量の測定は、ＪＩＳ　Ｋ５１０１－１３－２：２００４に従い測定でき、煮アマニ油を用いることが好ましい。
　なお、上記したような破損粒子の割合と吸油量との関係から、破損粒子の割合を調整することで吸油量を調整できる。さらに、一次粒子間の空間も油を保持できる空間であることから、一次粒子が凝集した二次粒子のメジアン径が大きいと吸油量が多くなり、二次粒子のメジアン径が小さいと吸油量が少なくなることが考えられる。
　中空シリカ粒子は、Ｌｉ、Ｎａ、Ｋ、Ｒｂ、Ｃｓ、Ｍｇ、Ｃａ、Ｓｒ及びＢａからなる群から選択される１種以上の金属Ｍを含有することが好ましい。中空シリカ粒子に金属Ｍが含まれることで、焼成時にフラックスとして働き、比表面積が低下して誘電正接を低くできる。
　金属Ｍは中空シリカ粒子の製造において、反応工程から洗浄工程の間に含有される。例えば、反応工程において、シリカのシェルを形成する際の反応溶液中に前記金属Ｍの金属塩を添加することや、中空シリカ前駆体を焼き締めする前に前記金属Ｍの金属イオンを含む溶液で洗浄することにより、中空シリカ粒子に金属Ｍを含有できる。
　本発明において、中空シリカ粒子に含まれる金属Ｍの濃度は、５０質量ｐｐｍ以上１質量％以下であることが好ましい。金属Ｍの濃度の総和が５０質量ｐｐｍ以上であると焼成時のフラックス効果により結合シラノール基の縮合が促進され、残存するシラノール基を減らせるので、誘電正接を低下できる。金属Ｍの濃度が高すぎると、シリカと反応してケイ酸塩となる成分が多くなり、中空シリカ粒子の吸湿性が悪化する場合があるため、１質量％以下で含有することが好ましい。金属Ｍの濃度は、１００質量ｐｐｍ以上がより好ましく、１５０ｐｐｍ以上がさらに好ましく、また、１質量％以下が好ましく、５０００質量ｐｐｍ以下がより好ましく、１０００質量ｐｐｍ以下が最も好ましい。
　金属Ｍの測定方法は、中空シリカ粒子に過塩素酸とフッ酸を加えて強熱し主成分のケイ素を除去したのちにＩＣＰ発光分析で測定できる。
　また、シリカ原料としてアルカリ金属ケイ酸塩を用いる場合は、シリカ原料としてケイ素アルコキシドを用いる場合に比べて、得られる中空シリカ粒子のシェル層に原料由来の炭素（Ｃ）成分は少なくなる。
　本発明の中空シリカ粒子は、該中空シリカ粒子を含む混練物を下記測定方法により測定したときの粘度が１００００ｍＰａ・ｓ以下であるのが好ましい。
（測定方法）
　アルゴンガスを用いた乾式ピクノメーターによる密度測定により求めた粒子の密度をＡ（ｇ／ｃｍ３）として、煮アマニ油６質量部と中空シリカ粒子（６×Ａ／２．２）質量部を混合し、２０００ｒｐｍで３分間混練して得た混練物を、回転式レオメータを用いてせん断速度１ｓ－１で３０秒測定し、３０秒時点での粘度を求める。
　上記測定方法により求めた混練物のせん断速度１ｓ－１での粘度が１００００ｍＰａ・ｓ以下であると、中空シリカ粒子を含む樹脂組成物の成形・成膜時に添加する溶剤量を減らせ、乾燥速度を早くでき、生産性を向上できる。また、シリカ粉末の粒径に応じた密度と比表面積の積が大きくなると、樹脂組成物に添加した際に粘度が上昇しやすくなるが、本発明の中空シリカ粒子は、密度と比表面積の積が小さいので樹脂組成物の粘度上昇を抑制できる。混練物の粘度は、８０００ｍＰａ・ｓ以下であるのがより好ましく、５０００ｍＰａ・ｓ以下がさらに好ましく、４０００ｍＰａ・ｓ以下が最も好ましい。
　前記混練物のせん断速度１ｓ－１での粘度は、低いほど樹脂組成物の塗工性が向上し、生産性が向上するため下限値は特に限定されない。
　シリカ粒子は、２９Ｓｉ－ＮＭＲによるスペクトルの帰属において、ＳｉＯ４四面体の連結度合いにより、Ｑ１～Ｑ４で表現される４種の基本構造に分類される。Ｑ１～Ｑ４は、それぞれ以下の通りである。
　Ｑ１は、Ｓｉの周りに酸素を介して１つのＳｉを有する構造単位のことで、ＳｉＯ４四面体が他の１つのＳｉＯ４四面体と連結していて、固体２９Ｓｉ－ＤＤ／ＭＡＳ－ＮＭＲスペクトルにおいて－８０ｐｐｍ付近にピークを有する。
　Ｑ２は、Ｓｉの周りに酸素を介して２つのＳｉを有する構造単位のことで、ＳｉＯ４四面体が他の２つのＳｉＯ４四面体と連結していて、固体２９Ｓｉ－ＤＤ／ＭＡＳ－ＮＭＲスペクトルにおいて－９１ｐｐｍ付近にピークを有する。
　Ｑ３は、Ｓｉの周りに酸素を介して３つのＳｉを有する構造単位のことで、ＳｉＯ４四面体が他の３つのＳｉＯ４四面体と連結していて、固体２９Ｓｉ－ＤＤ／ＭＡＳ－ＮＭＲスペクトルにおいて－１０１ｐｐｍ付近にピークを有する。
　Ｑ４は、Ｓｉの周りに酸素を介して４つのＳｉを有する構造単位のことで、ＳｉＯ４四面体が他の４つのＳｉＯ４四面体と連結していて、固体２９Ｓｉ－ＤＤ／ＭＡＳ－ＮＭＲスペクトルにおいて－１１０ｐｐｍ付近にピークを有する。
　本発明の中空シリカ粒子は、固体２９Ｓｉ－ＤＤ／ＭＡＳ－ＮＭＲにより測定した、シラノール基由来のＯＨ基を持たないＱ４構造に対するシラノール基由来のＯＨ基を１つ有するＱ３構造のモル比率（Ｑ３／Ｑ４）が、２～４０％であるのが好ましい。Ｑ３／Ｑ４が４０％以下であると、シラノール量を抑制でき、誘電正接が改善する。Ｑ３／Ｑ４が、２％未満のものを得るのは、高温で焼成する必要があり、その際に中空シリカの中空部が収縮してしまうため、得ることが実質的に難しい。また、Ｑ３／Ｑ４は３０％以下であるのがより好ましく、２０％以下がさらに好ましい。
　中空シリカ粒子のＱ３／Ｑ４は、以下のように測定する。
　中空シリカ粒子粉末を測定サンプルとする。４００ＭＨｚの核磁気共鳴装置を用い、直径７．５ｍｍのＣＰ／ＭＡＳ用プローブを装着し、観測核を２９Ｓｉとし、ＤＤ／ＭＡＳ法で測定する。測定条件は、２９Ｓｉ共鳴周波数を７９．４３ＭＨｚ、２９Ｓｉ９０°パルス幅を５μ秒、１Ｈ共鳴周波数を３９９．８４ＭＨｚ、１Ｈデカップリング周波数を５０ｋＨｚ、ＭＡＳ回転数を４ｋＨｚ、スペクトル幅を３０．４９ｋＨｚ、測定温度を２３℃とする。データ解析は、フーリエ変換後のスペクトルの各ピークについて、ローレンツ波形とガウス波形の混合により作成したピーク形状の中心位置、高さ、半値幅を可変パラメータとして、非線形最小二乗法により最適化計算を行う。Ｑ１、Ｑ２、Ｑ３及びＱ４の４つの構造単位を対象とし、得られたＱ１の含有率、Ｑ２の含有率、Ｑ３の含有率及びＱ４の含有率から、Ｑ３とＱ４のモル比率を算出する。
　本実施形態において、シリカ粒子のシラノール基の含有率は、ＣＰ／ＭＡＳ法（Cross Polarization/Magic Angle Spinning）でなく、ＤＤ／ＭＡＳ法（Dipolar Decoupling/Magic Angle Spinning）により測定されたものである。
　ＣＰ／ＭＡＳ法であると、１Ｈが近傍に存在するＳｉを増感して検出するため、得られるピークがＱ１の含有率、Ｑ２の含有率、Ｑ３の含有率及びＱ４の含有率を正確に反映しない。
　一方、ＤＤ／ＭＡＳ法は、ＣＰ／ＭＡＳ法のような増感効果がないため、得られるピークがＱ１の含有率、Ｑ２の含有率、Ｑ３の含有率及びＱ４の含有率を正確に反映し、定量的な解析に適する。
　中空シリカ粒子の細孔容積は、０．２ｃｍ３／ｇ以下であることが好ましい。
　細孔容積が０．２ｃｍ３／ｇより大きいと、水分を吸着しやすくなり、樹脂組成物の誘電損失が悪化することがある。細孔容積は、０．１５ｃｍ３／ｇ以下であることがより好ましく、０．１ｃｍ３／ｇ以下がさらに好ましく、０．０５ｃｍ３／ｇ以下が特に好ましい。
　細孔容積は、比表面積・細孔分布測定装置（例えば、マイクロトラック・ベル社製「ＢＥＬＳＯＲＰ－ｍｉｎｉＩＩ」、マイクロメリティック社製「トライスターＩＩ」等）を用いた窒素吸着法に基づくＢＪＨ法により求める。
　中空シリカ粒子の表面は、シランカップリング剤によって処理されていることが好ましい。
　中空シリカ粒子の表面がシランカップリング剤によって処理されていることで、表面シラノール基の残存量が少なくなり、表面が疎水化され、水分吸着を抑えて誘電損失を向上できるとともに、樹脂組成物とする際に、樹脂との親和性が向上し、分散性や、樹脂製膜後の強度が向上する。
　シランカップリング剤の種類としては、アミノシラン系カップリング剤、エポキシシラン系カップリング剤、メルカプトシラン系カップリング剤、シラン系カップリング剤、オルガノシラザン化合物等が挙げられる。シランカップリング剤は１種類を単独で用いてもよいし２種類以上を組み合わせて用いてもよい。
　シランカップリング剤の付着量としては、中空シリカ粒子の粒子１００質量部に対して、１質量部以上であることが好ましく、１．５質量部以上がより好ましく、２質量部以上がさらに好ましく、また１０質量部以下であることが好ましく、８質量部以下がより好ましく、５質量部以下がさらに好ましい。すなわち、シランカップリング剤の付着量は、中空シリカ粒子の粒子１００質量部に対して１～１０質量部の範囲であるのが好ましい。
　中空シリカ粒子の表面がシランカップリング剤で処理されていることはＩＲによるシランカップリング剤の置換基によるピークの検出により確認できる。また、シランカップリング剤の付着量は、炭素量により測定できる。
　本発明の中空シリカ粒子は、１ＧＨｚでの比誘電率が１．３～５．０であるのが好ましい。特に粉体の誘電率測定において、１０ＧＨｚ以上ではサンプルスペースが小さくなり測定精度が悪化するので、本発明では１ＧＨｚでの測定値を採用する。１ＧＨｚでの比誘電率が前記範囲であると、電子機器に求められる低比誘電率を達成できる。なお、１ＧＨｚでの比誘電率が１．３未満の中空シリカ粒子を合成することは、実質的に困難である。
　１ＧＨｚでの比誘電率は、下限が１．３以上であることが好ましく、１．４以上がより好ましい。また上限は４．５以下であることがより好ましく、４．０以下がさらに好ましく、３．５以下が特に好ましく、３．０以下が殊更に好ましく、２．５以下が最も好ましい。
　また、本発明の中空シリカ粒子は、１ＧＨｚでの誘電正接が０．０００１～０．０５であるのが好ましい。１ＧＨｚでの誘電正接が０．０５以下であると、電子機器に求められる低比誘電率を達成できる。また、１ＧＨｚでの誘電正接が０．０００１未満の中空シリカ粒子を合成することは、実質的に困難である。
　１ＧＨｚでの誘電正接は、下限が０．０００２以上であることがより好ましく、０．０００３以上がさらに好ましい。また上限は０．０１以下であることがより好ましく、０．００５以下がさらに好ましく、０．００３以下がよりさらに好ましく、０．００２以下が特に好ましく、０．００１５以下が殊更に好ましく、０．００１０以下が最も好ましい。
　比誘電率及び誘電正接は、専用の装置（例えば、キーコム株式会社製「ベクトルネットワークアナライザ　Ｅ５０６３Ａ」）を用い、摂動方式共振器法にて測定できる。
（樹脂組成物及びスラリー組成物）
　本発明の中空シリカ粒子は、樹脂と混合し、樹脂組成物として利用できる。
　本実施形態に係る樹脂組成物は、本発明の中空シリカ粒子と樹脂とを含む。樹脂組成物中の中空シリカ粒子の含有率は５～７０質量％であることが好ましく、１０～５０質量％がより好ましい。
　樹脂としては、ポリブチレンテレフタレート、ポリエチレンテレフタレート、不飽和ポリエステル、芳香族ポリエステル等のポリエステル；ポリテトラフルオロエチレン（ＰＴＦＥ）、テトラフルオロエチレン－パーフルオロアルキルビニルエーテル共重合体（ＰＦＡ）、テトラフルオロエチレン－ヘキサフルオロプロピレン共重合体（ＦＥＰ）、テトラフルオロエチレン－エチレン共重合体（ＥＴＦＥ）等のフッ素樹脂；エポキシ樹脂；シリコーン樹脂；フェノール樹脂；メラミン樹脂；ユリア樹脂；ポリイミド；ポリアミドイミド；ポリエーテルイミド；ポリアミド；ポリフェニレンエーテル；ポリフェニレンスルフィド；ポリスルホン；液晶ポリマー；ポリエーテルスルホン；ポリカーボネート；マレイミド変成樹脂；ＡＢＳ（アクリロニトリル・ブタジエン・スチレン）樹脂；ＡＡＳ（アクリロニトリルーアクリルゴム・スチレン）樹脂；ＡＥＳ（アクリロニトリル・エチレン・プロピレン・ジエンゴム－スチレン）樹脂等から選ばれる１種または２種以上を使用できる。樹脂組成物における誘電正接は樹脂の特性にも依存するので、これらを考慮して使用する樹脂を選択すればよい。
　また、本発明の中空シリカ粒子は、スラリー組成物の充填材として用いることができる。スラリー組成物は、水系又は油系の媒体中に本発明の中空シリカ粒子を分散させた泥状の組成物をいう。
　スラリー組成物中、中空シリカ粒子を、１～４０質量％含むことが好ましく、５～４０質量％含むことがより好ましい。
　油系の媒体としては、アセトン、メタノール、エタノール、ブタノール、２－プロパノール、２－メトキシエタノール、２－エトキシエタノール、１－メトキシ－２－プロパノール、２－アセトキシ－１－メトキシプロパン、トルエン、キシレン、メチルエチルケトン、Ｎ，Ｎ－ジメチルホルムアミド、メチルイソブチルケトン、Ｎ－メチルピロリドン、ｎ－ヘキサン、シクロヘキサン、シクロヘキサノン及び混合物であるナフサ等が挙げられる。これらは単独で用いてもよいし、２種以上の混合物として用いてもよい。
　樹脂組成物及びスラリー組成物には、上記樹脂や媒体以外に任意の成分を含んでいてもよい。任意の成分としては、例えば、分散助剤、界面活性剤、シリカ以外のフィラー等が挙げられる。
　なお、本発明の中空シリカ粒子を含む樹脂組成物を用いて樹脂フィルムを作製したとき、その比誘電率が、周波数１０ＧＨｚにおいて２．０～３．５であるのが好ましく、下限は、２．２以上がより好ましく、２．３以上がさらに好ましく、また上限は、３．２以下がより好ましく、３．０以下がさらに好ましい。樹脂フィルムの周波数１０ＧＨｚでの比誘電率が前記範囲であると、電気特性に優れるので電子機器や通信機器等への利用が期待できる。
　また、樹脂フィルムの誘電正接は、周波数１０ＧＨｚにおいて０．０１以下であるのが好ましく、０．００８以下がより好ましく、０．００６５以下がさらに好ましい。樹脂フィルムの周波数１０ＧＨｚでの誘電正接が前記範囲であると、電気特性に優れるので電子機器や通信機器等への利用が期待できる。誘電正接が小さいほど、回路の伝送損失が抑えられるため、下限値は特に限定されない。
　樹脂フィルムの比誘電率及び誘電正接は、スプリットポスト誘電体共振器（ＳＰＤＲ）（例えば、Ａｇｉｌｅｎｔ　Ｔｅｃｈｎｏｌｏｇｉｅｓ社製）を用いて測定できる。
　また、上記樹脂フィルムの平均線膨張率が、１０～５０ｐｐｍ／℃であるのが好ましい。平均線膨張率が前記範囲であると、基材として広く使用される銅箔の熱膨張係数に近い範囲であるので、電気特性に優れる。平均線膨張率は、１２ｐｐｍ／℃以上であるのがより好ましく、１５ｐｐｍ／℃以上がさらに好ましく、また４０ｐｐｍ／℃以下であるのがより好ましく、３０ｐｐｍ／℃以下がさらに好ましい。
　平均線膨張率は、熱機械分析装置（例えば、島津製作所社製、「ＴＭＡ－６０」）を使用して、上記樹脂フィルムを荷重５Ｎ、昇温速度２℃／ｍｉｎで加熱し、３０℃から１５０℃までのサンプルの寸法変化を測定し、平均を算出することで求められる。
　また、上記樹脂フィルムを金属と積層した際のピール強度が、３０Ｎ／ｍｍ以上であることが好ましい。ピール強度が上記範囲にあることで、積層後の下流プロセス以降において金属と樹脂組成物の剥離が抑えられる。ピール強度は３０Ｎ／ｍｍ以上が好ましく、４０Ｎ／ｍｍ以上がより好ましく、５０Ｎ／ｍｍ以上が最も好ましい。
　ピール強度は、樹脂組成物を金属と積層した後、９０°剥離試験機等を用いて測定することが出来る。
（中空シリカ粒子の製造方法）
　本発明の中空シリカ粒子の製造方法としては、例えば、水相、油相、及び界面活性剤を含む水中油型エマルションを用い、エマルション中で中空シリカ前駆体を得て、この前駆体から中空シリカ粒子を得る方法が挙げられる。この水中油型エマルションは、水中に油相が分散したエマルションであり、このエマルションにシリカ原料が添加されると油滴にシリカ原料が付着し、オイルコア－シリカシェル粒子を形成できる。
　本発明の中空シリカ粒子の製造方法は、水相、油相及び界面活性剤を含む水中油型エマルションを作製し、この水中油型エマルションを０．５～２４０時間静置し、水中油型エマルション中でコアの外周にシリカを含むシェル層が形成された中空シリカ前駆体を得て、中空シリカ前駆体からコアを除去し、熱処理することを含む。前記中空シリカ前駆体を得る際には、水中油型エマルションに第１のシリカ原料を添加し、１段目シェルを形成し、１段目シェルが形成されたエマルションに第２のシリカ原料を添加し、２段目シェルを形成することによりコアの外周にシェル層を形成するのが好ましい。
　以下、水中油型エマルションを単にエマルションとも記す。また、第１のシリカ原料が添加されて生成しかつ第２のシリカ原料が添加される前のオイルコア－シリカシェル粒子が分散した分散液、及び、第２のシリカ原料が添加された後のオイルコア－シリカシェル粒子が分散した分散液も、エマルションと記すことがある。後者の第２のシリカ原料が添加された後のオイルコア－シリカシェル粒子が分散した分散液は中空シリカ前駆体分散液と同等のものであってもよい。
＜１段目シェルの形成＞
　まず、水相、油相、及び界面活性剤を含む水中油型エマルションに第１のシリカ原料を添加し、１段目シェルを形成する。
　エマルションの水相は、主として水を溶媒として含む。水相には、水溶性の有機液体、水溶性樹脂等の添加剤がさらに添加されてもよい。水相における水の割合は５０～１００質量％が好ましく、９０～１００質量％がより好ましい。
　エマルションの油相は、水相成分と相溶しない非水溶性の有機液体を含むことが好ましい。この有機液体がエマルション中で液滴となり、中空シリカ前駆体のオイル－コア部分を形成する。
　有機液体としては、例えば、ｎ－ヘキサン、イソヘキサン、ｎ－ヘプタン、イソヘプタン、ｎ－オクタン、イソオクタン、ｎ－ノナン、イソノナン、ｎ－ペンタン、イソペンタン、ｎ－デカン、イソデカン、ｎ－ドデカン、イソドデカン、ペンタデカン等の脂肪族炭化水素類、もしくはそれらの混合物であるパラフィン系基油、シクロペンタン、シクロヘキサン、シクロヘキセン等の脂環式炭化水素類、もしくはそれらの混合物であるナフテン系基油、ベンゼン、トルエン、キシレン、エチルベンゼン、プロピルベンゼン、クメン、メシチレン、テトラリン、スチレン等の芳香族炭化水素類、プロピルエーテル、イソプロピルエーテル等のエーテル類、酢酸エチル、酢酸－ｎ－プロピル、酢酸イソプロピル、酢酸－ｎ－ブチル、酢酸イソブチル、酢酸－ｎ－アミル、酢酸イソアミル、乳酸ブチル、プロピオン酸メチル、プロピオン酸エチル、プロピオン酸ブチル、酪酸メチル、酪酸エチル、酪酸ブチル等のエステル類、パーム油、大豆油、菜種油等の植物油、ハイドロフルオロカーボン、パーフルオロカーボン、パーフルオロポリエーテル等のフッ素系溶剤等が挙げられる。また、シェル形成反応温度で疎水性液体となるポリオキシアルキレングリコールを用いることもできる。例えば、ポリプロピレングリコール（分子量１０００以上）、オキシエチレン単位の割合が２０質量％未満で、曇点（１質量％水溶液）が４０℃以下、好ましくは、２０℃以下のポリオキシエチレン－ポリオキシプロピレンブロック共重合体などが挙げられる。中でも、ポリオキシプロピレン－ポリオキシエチレン－ポリオキシプロピレン型のブロック共重合体が好ましく用いられる。
　これらは単独で、又は、単一相で油相を形成する範囲で２種以上を組み合わせて用いてもよい。
　有機液体としては、炭素数８～１６、特に炭素数９～１２の炭化水素が好ましい。有機液体は、操作性、火気への安全性、中空シリカ前駆体と有機液体との分離性、中空シリカ粒子の形状特性、水への有機液体の溶解性などを総合的に考慮して選定される。炭素数が８～１６の炭化水素は、その化学的安定性が良好であれば、直鎖状、分岐状又は環状の炭化水素であってよく、炭素数の異なる炭化水素を混合して用いてもよい。炭化水素としては、飽和炭化水素が好ましく、直鎖状飽和炭化水素がより好ましい。
　有機液体の引火点としては、２０℃以上のものが好ましく、４０℃以上のものがより好ましい。引火点が２０℃未満の有機液体を用いる場合、引火点が低すぎるため、防火上、作業環境上の対策が必要である。
　エマルションは、乳化安定性を高めるために、界面活性剤を含む。界面活性剤は、水溶性又は水分散性が好ましく、水相へ添加して用いることが好ましい。好ましくは、非イオン性界面活性剤である。
　非イオン性界面活性剤としては、例えば、下記の界面活性剤を挙げることができる。
　ポリオキシエチレン－ポリオキシプロピレン共重合体系界面活性剤、
　ポリオキシエチレンソルビタン脂肪酸エステル系界面活性剤：ポリオキシエチレンソルビタンモノラウレート、ポリオキシエチレンソルビタンモノパルミテート、ポリオキシエチレンソルビタンモノステアレート、ポリオキシエチレンソルビタントリステアレート、ポリオキシエチレンソルビタンモノオレエート、
　ポリオキシエチレン高級アルコールエーテル系界面活性剤：ポリオキシエチレンラウリルエーテル、ポリオキシエチレンセチルエーテル、ポリオキシエチレンステアリルエーテル、ポリオキシエチレンオレイルエーテル、ポリオキシエチレンオクチルフェノールエーテル、ポリオキシエチレンノニルフェノールエーテル、
　ポリオキシエチレン脂肪族エステル系界面活性剤：ポリオキシエチレングリコールモノラウレート、ポリオキシエチレングリコールモノステアレート、ポリオキシエチレングリコールモノオレエート、
　グリセリン脂肪酸エステル系界面活性剤：ステアリン酸モノグリセライド、オレイン酸モノグリセライド。
　さらに、ポリオキシエチレンソルビトール脂肪酸エステル系界面活性剤、ショ糖脂肪酸エステル系界面活性剤、ポリグリセリン脂肪酸エステル系界面活性剤、ポリオキシエチレン硬化ヒマシ油系界面活性剤等を用いてもよい。
　これらは単独で、又は２種以上を組み合わせて用いてもよい。
　上記した非イオン性界面活性剤のなかでも、ソルビタン脂肪酸エステルおよびポリオキシエチレン－ポリオキシプロピレン共重合体系界面活性剤が好ましく用いられる。ポリオキシエチレン－ポリオキシプロピレン共重合体は、ポリオキシエチレンブロック（ＥＯ）とポリオキシプロピレンブロック（ＰＯ）とが結合したブロック共重合体である。ブロック共重合体としては、ＥＯ－ＰＯ－ＥＯブロックコポリマー、ＥＯ－ＰＯブロックコポリマー等が挙げられ、好ましくはＥＯ－ＰＯ－ＥＯブロックコポリマーである。ＥＯ－ＰＯ－ＥＯブロックコポリマーのオキシエチレン単位の割合は、２０質量％以上が好ましく、３０質量％以上がより好ましい。
　ポリオキシエチレン－ポリオキシプロピレン共重合体の重量平均分子量は、３，０００～２７，０００が好ましく、６，０００～１９，０００がより好ましい。
　ポリオキシエチレン－ポリオキシプロピレン共重合体全体に対して、ポリオキシエチレンブロックの合計量は４０～９０質量％が好ましく、ポリオキシプロピレンブロックの合計量は１０～６０質量％が好ましい。
　界面活性剤の使用量は、界面活性剤の種類、界面活性剤の親水性あるいは疎水性の程度を表す指標であるＨＬＢ（Ｈｙｄｒｏｐｈｉｌｅ－ｌｉｐｏｐｈｉｌｅ　ｂａｌａｎｃｅ）、目的とするシリカ粒子の粒子径等の条件により異なるが、水相中の含有量が５００～２０，０００質量ｐｐｍが好ましく、１，０００～１０，０００質量ｐｐｍがより好ましい。５００質量ｐｐｍ以上で、エマルションをより安定化できる。また、２０，０００質量ｐｐｍ以下で、中空シリカ粒子に残留する界面活性剤の量を少なくできる。
　水相と油相とは、質量比で、２００：１～５：１で配合してよく、好ましくは１００：１～９：１である。
　水中油型エマルションの作製方法は、以下に限定されない。事前に水相及び油相をそれぞれ調製しておき、水相に油相を添加して、十分に混合ないし撹拌させることで作製できる。さらに物理的に強いせん断力を与える超音波乳化、撹拌式乳化、高圧乳化などの方法を適用できる。また、微細孔を持つ膜を通して微細にした油相を水相中に分散させる膜乳化法や、界面活性剤を油相に溶解させた後に水相を加えて乳化を行う転相乳化法、界面活性剤が曇点付近の温度を境に水溶性から油溶性に変化することを利用した転相温度乳化法などの方法がある。これらの乳化方法は、目的とする粒子径、粒度分布等の特定により適宜選択できる。
　得られる中空シリカ粒子を小粒子径化し、粒度分布を狭めるために、水相中に油相が十分に分散し乳化されることが好ましい。例えば、混合液は、１０ｂａｒ以上、好ましくは２０ｂａｒ以上の圧力で高圧ホモジナイザーを用いて乳化できる。
　本発明において、得られた水中油型エマルションをエージングする工程を設ける。エージングする工程を行うことで、微小なエマルションが優先的に成長し、得られる中空シリカの１次粒径が均一になり、一次粒子径の分布が狭くなる。これにより、Ａｒ密度とＢＥＴ比表面積との積（Ａ×Ｂ）を小さくできる。エージングの時間は、０．５～２４０時間である。エージングの時間が０．５時間以上であると、一次粒子の粒径の均一性が高まり、２４０時間以内であると、生産性が良い。エージングの時間は、０．５～９６時間であるのが好ましく、０．５～４８時間が最も好ましい。
　また、エージングの温度は、５～８０℃が好ましく、２０～７０℃がより好ましく、２０～５５℃が最も好ましい。
　１段目シェルの形成工程では、水中油型エマルションに、第１のシリカ原料を添加する。
　第１のシリカ原料としては、例えば、水溶性シリカが溶解した水溶液、固体シリカが分散した水性分散液、これらの混合物、ならびに、アルカリ金属ケイ酸塩、活性ケイ酸及びケイ素アルコキシドからなる群から選ばれる１種以上またはそれらの水溶液または水分散液が挙げられる。これらのうちアルカリ金属ケイ酸塩、活性ケイ酸及びケイ素アルコキシドからなる群から選ばれる１種以上またはそれらの水溶液または水分散液が、入手容易性が高い点で好ましい。
　固体シリカとしては、例えば、有機ケイ素化合物を加水分解して得られたシリカゾル、市販のシリカゾルが挙げられる。
　アルカリ金属ケイ酸塩のアルカリ金属としては、リチウム、ナトリウム、カリウム、ルビジウム等が挙げられ、中でも入手の容易さ、経済的理由によりナトリウムが好ましい。すなわちアルカリ金属ケイ酸塩としては、ケイ酸ナトリウムが好ましい。ケイ酸ナトリウムは、Ｎａ２Ｏ・ｎＳｉＯ２・ｍＨ２Ｏで表される組成を有する。ナトリウムとケイ酸の割合は、Ｎａ２Ｏ／ＳｉＯ２のモル比ｎで１．０～４．０が好ましく、さらには２．０～３．５が好ましい。
　活性ケイ酸はアルカリ金属ケイ酸塩を陽イオン交換処理によりアルカリ金属を水素に置換して得られるものであり、この活性ケイ酸の水溶液は弱酸性を示す。陽イオン交換には、水素型陽イオン交換樹脂を用いることができる。
　アルカリ金属ケイ酸塩及び活性ケイ酸は、水に溶解ないし分散させてから、エマルションに添加することが好ましい。アルカリ金属ケイ酸塩及び活性ケイ酸水溶液の濃度は、ＳｉＯ２濃度として３～３０質量％が好ましく、さらには５～２５質量％が好ましい。
　ケイ素アルコキシドとしては、例えば、テトラメトキシシラン、テトラエトキシシラン、テトラプロポキシシラン等のテトラアルキルシラン類を好ましく用いることができる。
　また、シリカ原料とともに、他の金属酸化物等を混合することで、複合粒子を得ることも可能である。他の金属酸化物としては、二酸化チタン、酸化亜鉛、酸化セリウム、酸化銅、酸化鉄、酸化錫等が挙げられる。
　第１のシリカ原料としては、上記したシリカ原料を単独で、又は２種以上を混合して用いることができる。なかでも、第１のシリカ原料として、アルカリ金属ケイ酸塩水溶液、特にケイ酸ナトリウム水溶液を用いることが好ましい。
　第１のシリカ原料の水中油型エマルションへの添加は、酸性条件下で行うことが好ましい。酸性環境下でシリカ原料を添加することで、シリカ微粒子を発生させネットワークをつくることで１段目の被膜が形成される。反応温度は８０℃以下であることがエマルションの安定性維持のために好ましく、７０℃以下がより好ましく、６０℃以下がさらに好ましく、５０℃以下が特に好ましく、４０℃以下が最も好ましい。また、被膜の厚みを均一にするためにシリカ微粒子のネットワーク形成速度を制御する観点から、４℃以上であることが好ましく、１０℃以上がより好ましく、１５℃以上がさらに好ましく、２０℃以上が特に好ましく、２５℃以上が最も好ましい。すなわち、反応温度は４～８０℃の範囲であるのが好ましい。
　水中油型エマルションのｐＨは、被膜の厚さをより均一にし、得られる中空シリカのシリカシェル層をより緻密にするという観点から、３未満とすることがより好ましく、２．５以下がさらに好ましく、また、１以上であることがより好ましい。すなわち、水中油型エマルションのｐＨは１以上３未満の範囲であるのが好ましい。
　水中油型エマルションのｐＨを酸性にするには、酸を添加することが挙げられる。
　酸としては、例えば、塩酸、硝酸、硫酸、酢酸、過塩素酸、臭化水素酸、トリクロロ酢酸、ジクロロ酢酸、メタンスルホン酸、ベンゼンスルホン酸等が挙げられる。
　第１のシリカ原料の添加では、第１のシリカ原料の添加量は、エマルション中に含まれる油相１００質量部に対して、第１のシリカ原料中のＳｉＯ２が１～５０質量部となるようにすることが好ましく、３～３０質量部がより好ましい。
　第１のシリカ原料の添加では、第１のシリカ原料を添加後、エマルションのｐＨを酸性に維持した状態で、１分以上保持することが好ましく、５分以上がより好ましく、１０分以上がさらに好ましい。
　次に、第１のシリカ原料が添加されたエマルションのｐＨを３以上７以下（弱酸性から中性）で保持することが好ましい。これによって、第１のシリカ原料を油滴の表面に固定化できる。
　例えば、第１のシリカ原料を添加したエマルションに塩基を添加することで、エマルションのｐＨを３以上とする方法がある。
　塩基としては、例えば、水酸化ナトリウム、水酸化カリウム等のアルカリ金属水酸化物、水酸化マグネシウム、水酸化カルシウム等のアルカリ土類金属水酸化物、アンモニア、アミン類等が挙げられる。
　あるいは陰イオン交換処理によりハロゲンイオン等の陰イオンを水酸化物イオンに交換する方法を用いてもよい。
　塩基を添加する際は、第１のシリカ原料が添加されたエマルションを撹拌しながら塩基を徐々に添加して、エマルションのｐＨを徐々に上昇させることが好ましい。撹拌が弱かったり、多量の塩基を一度に投入したりすると、エマルションのｐＨが不均一になり、１層目の被膜の厚みが不均一になることがある。
　エマルションは、撹拌しながら保持することが好ましい。この保持時間は、１０分以上であるのが好ましく、１時間以上がより好ましく、４時間以上であってもよい。この保持温度は１００℃以下であることがエマルションの安定性維持のために好ましく、９５℃以下がより好ましく、９０℃以下がさらに好ましく、８５℃以下が特に好ましい。また、熟成を促進させるためには保持温度は、３５℃以上が好ましく、４０℃以上がより好ましく、４５℃以上が特に好ましい。すなわち、エマルションの保持温度は３５～１００℃の範囲であるのが好ましい。
＜２段目シェルの形成＞
　次に、アルカリ金属イオン存在下、エマルションに第２のシリカ原料を添加する。これによって、中空シリカ前駆体分散液が得られる。ここで、中空シリカ前駆体は、オイルコア－シリカシェル粒子となっている。
　第２のシリカ原料のエマルションへの添加は、アルカリ性条件下で行うことが好ましい。
　第１のシリカ原料の添加では、油滴への第１のシリカ原料の付着をより均一にするために、エマルションを一旦酸性とした後にｐＨを３以上７以下（弱酸性から中性）にする方法を用いている。この方法によって得られる１層目のシリカ層は多孔質であり、緻密性が不十分なため強度が低くなってしまう。第２のシリカ原料の添加において、エマルションをアルカリ性とすることで、先に得られた１層目のシリカ層上に、高密度な２層目のシリカ層を形成できる。
　第２のシリカ原料を添加する際のエマルションのｐＨは、新しい微粒子の発生を抑えるために、８以上であることが好ましく、８．５以上がより好ましく、８．７以上がさらに好ましく、８．９以上が特に好ましく、９以上が最も好ましい。また、ｐＨが高すぎるとシリカの溶解度が大きくなるため、１３以下であることが好ましく、１２．５以下がよりに好ましく、１２以下がさらに好ましく、１１．５以下が特に好ましく、１１以下が最も好ましい。すなわち、エマルションのｐＨは８～１３の範囲であるのが好ましい。
　水中油型エマルションのｐＨをアルカリ性にするには、塩基を添加することが挙げられる。塩基としては、上記したものと同様の化合物が用いられる。
　第２のシリカ原料としては、上記した第１のシリカ原料と同様のものを単独で、又は２種以上を混合して用いることができる。なかでも、第２のシリカ原料の添加では、ケイ酸ナトリウム水溶液及び活性ケイ酸水溶液の少なくとも一方が好ましく用いられる。
　エマルションをアルカリ性条件下で第２のシリカ原料を添加する際には、第２のシリカ原料と同時にアルカリ金属水酸化物を添加する方法を用いてもよい。また、第２のシリカ原料にアルカリ金属ケイ酸塩としてケイ酸ナトリウムを用いる方法でもよい。この場合、第１のシリカ原料の添加後にｐＨを５以上とした弱酸性のエマルションに、アルカリ成分であるケイ酸ナトリウムを添加するため、第２のシリカ原料を添加しながらエマルションのｐＨをアルカリ性に保持できる。また、アルカリ金属イオンがエマルション中に存在するようになる。
　なお、第２のシリカ原料にケイ酸ナトリウム水溶液を用いる場合などで、ｐＨが上がりすぎてしまう場合は、ｐＨを調整するために酸を加えてもよい。ここで用いる酸には、第１のシリカ原料を添加する時と同じ酸を用いてもよい。
　第２のシリカ原料の添加はアルカリ金属イオンの存在下で行うことが好ましい。このアルカリ金属イオンは、第１のシリカ原料由来、第２のシリカ原料由来、ｐＨ調整のために加えた塩基由来であってよく、エマルションへの添加剤の添加等によっても配合が可能である。例えば、第１のシリカ原料及び第２のシリカ原料の少なくとも一方に、アルカリ金属ケイ酸塩を用いる場合である。また、エマルションの添加剤に、アルカリ金属のハロゲン化物、硫酸塩、硝酸塩、脂肪酸塩等を用いる場合である。
　第２のシリカ原料の添加は、例えば、第１のシリカ原料の添加後のエマルションに、ケイ酸ナトリウム水溶液及び活性ケイ酸水溶液のうち一方を添加してもよく、両方を添加してもよい。両方を添加する場合は、ケイ酸ナトリウム水溶液及び活性ケイ酸水溶液を一括して添加してもよいし、順番に添加してもよい。
　例えば、第２のシリカ原料の添加は、ｐＨ調整をしながら、１層目のシリカ層上へのシリカ原料の付着を促進するために、ケイ酸ナトリウム水溶液を添加する工程と、活性ケイ酸水溶液を添加する工程とを、１回行う又は２回以上繰り返すことができる。
　第２のシリカ原料は、１層目のシリカ層上へのシリカ原料の付着を促進するために、加熱されたエマルションに添加することが好ましい。エマルションの温度は、新しい微粒子の発生を抑えるため、３０℃以上が好ましく、３５℃以上がより好ましく、４０℃以上がさらに好ましく、４５℃以上が特に好ましく、５０℃以上が最も好ましい。温度が高くなり過ぎるとシリカの溶解度が高くなるため、１００℃以下が好ましく、９５℃以下がより好ましく、９０℃以下がさらに好ましく、８５℃以下が特に好ましく、８０℃以下が最も好ましい。すなわち、第２のシリカ原料を添加する際のエマルションの温度は３０～１００℃の範囲であるのが好ましい。加熱されたエマルションを用いた場合、第２のシリカ原料の添加後は、生成したエマルションを室温（約２３℃）まで徐冷することが好ましい。
　第２のシリカ原料の添加では、第２のシリカ原料の添加量は、油相１００質量部に対して、第２のシリカ原料中のＳｉＯ２が２０～５００質量部となるように調整されるのが好ましく、４０～３００質量部となるように調整されるのがより好ましい。
　第２のシリカ原料の添加では、第２のシリカ原料を添加後にエマルションのｐＨをアルカリ性に維持した状態で、１０分以上保持することが好ましい。
　第１のシリカ原料の添加及び第２のシリカ原料の添加を通して、第１のシリカ原料及び第２のシリカ原料の添加量の合計量は、油相１００質量部に対して、第１のシリカ原料中のＳｉＯ２と第２のシリカ原料中のＳｉＯ２の合計が３０～５００質量部となるように調整されるのが好ましく、５０～３００質量部となるように調整されるのがより好ましい。
　本発明のシリカシェル層は主としてシリカより構成されるが、屈折率調整など、必要に応じてＴｉやＺｒなどの他の金属成分を含有させてもよい。他の金属成分を含有させる方法は特に限定されないが、例えばシリカ原料を添加する工程で金属ゾル液や金属塩水溶液を同時に添加するなどの方法が用いられる。
　上記のようにして中空シリカ前駆体分散液が得られる。
　中空シリカ前駆体分散液から中空シリカ前駆体を得る方法としては、例えば、分散液をろ過する方法、加熱して水相を除去する方法、沈降分離もしくは遠心分離により前駆体を分離する方法等がある。
　一例としては、０．１μｍ～５μｍ程度のフィルターを用いて分散液をろ過し、ろ別された中空シリカ前駆体を乾燥する方法がある。
　また必要に応じて、得られた中空シリカ前駆体を、水や酸、アルカリ、有機溶剤等で洗浄してもよい。
＜中空シリカ前駆体の熱処理＞
　そして、中空シリカ前駆体からオイルコアを除去して熱処理する。オイルコアを除去する方法としては、例えば、中空シリカ前駆体を焼成しオイルを燃焼分解する方法、乾燥によりオイルを揮発させる方法、適切な添加剤を加えてオイルを分解させる方法、有機溶媒等を用いてオイルを抽出する方法等がある。中でも、オイルの残留物が少ない中空シリカ前駆体を焼成してオイルを燃焼分解する方法が好ましい。
　以下、中空シリカ前駆体を焼成してオイルコアを除去し、熱処理する方法を例に説明する。
　中空シリカ前駆体を焼成することによりオイルコアを除去し、中空シリカ粒子を得る方法では、少なくとも２段階の異なる温度で熱処理することが好ましい。１段目の熱処理によりオイルコアを除去し、２段目の熱処理で中空シリカ粒子のシェル層の緻密化を行う。
　１段目の熱処理では、オイルコアと界面活性剤の有機成分を除去する。中空シリカ前駆体内のオイルを熱分解する必要があるため、１００℃以上で行うのが好ましく、２００℃以上がより好ましく、３００℃以上が最も好ましい。１段目の熱処理が高温過ぎると、シリカシェルの緻密化が進み内部の有機成分の除去が難しくなるため、７００℃未満で行うのが好ましく、５５０℃以下が好ましく、５３０℃以下がより好ましく、５２０℃以下がさらに好ましく、５１０℃以下が特に好ましく、５００℃以下が最も好ましい。すなわち、１段目の熱処理温度は１００℃以上７００℃未満の範囲であるのが好ましい。１段目の熱処理は、１回で行ってもよいし、複数回行ってもよい。
　１段目の熱処理時間は、３０分以上が好ましく、１時間以上が好ましく、２時間以上がより好ましく、また、４８時間以下が好ましく、２４時間以下がより好ましく、１２時間以下がより好ましい。すなわち、１段目の熱処理時間は３０分以上４８時間以下の範囲であるのが好ましい。
　そして、２段目の熱処理では、中空シリカ粒子を焼きしめ、シェルの緻密化を行うとともに、表面シラノール基を減らし、誘電正接を低下させる。２段目の焼成温度は１段目の熱処理温度よりも高い温度で行うことが好ましい。
　２段目の熱処理を静置法で行う際は、７００℃以上で行うのが好ましく、８００℃以上がより好ましく、９００℃以上がさらに好ましく、１０００℃以上が最も好ましい。また、温度が高くなり過ぎると、アモルファスシリカの結晶化が起こって比誘電率が高くなるため、１２００℃以下で行うのが好ましく、１１５０℃以下がより好ましく、１１００℃以下が最も好ましい。すなわち、静置法で行う際の２段目の熱処理温度は、７００～１２００℃の範囲であるのが好ましい。
　なお、２段目の熱処理温度は、１段目の熱処理温度よりも２００℃以上高いことが好ましく、２００～８００℃高いことがより好ましく、４００～７００℃高いことがさらに好ましい。２段目の熱処理は、１回で行ってもよいし、複数回行ってもよい。
　静置法で行う際の２段目の熱処理時間は１０分以上が好ましく、３０分以上がより好ましく、また、２４時間以下が好ましく、１２時間以下がより好ましく、６時間以下が最も好ましい。すなわち、２段目の熱処理時間は１０分以上２４時間以下の範囲であるのが好ましい。
　また、２段目の熱処理は噴霧燃焼法を用いてもよい。その際の火炎温度は１０００℃以上が好ましく、１２００℃以上が好ましく、１４００℃以上が最も好ましい。また、火炎温度は２０００℃以下が好ましく、１８００℃以下がより好ましく、１６００℃以下が最も好ましい。すなわち、噴霧燃焼法で行う際の２段目の熱処理温度は、１０００～２０００℃の範囲であるのが好ましい。
　なお、１段目の焼成後、２段目の熱処理を行う前に中空シリカ前駆体を室温に戻してもよいし、１段目の焼成温度を維持した状態から２段目の熱処理温度に昇温してもよい。
＜中空シリカ焼成粒子の表面処理＞
　その後、前記工程で得られた熱処理後の中空シリカ焼成粒子をシランカップリング剤で表面処理してもよい。この工程により、中空シリカ焼成粒子の表面に存在するシラノール基とシランカップリング剤とが反応し、表面シラノール基量が減少して、誘電正接を減少できる。また、表面が疎水化して樹脂に対する親和性が改善するため、樹脂に対する分散性が向上する。
　表面処理の条件には特に制限はなく、一般的な表面処理条件でよく、湿式処理法や乾式処理法が用いられる。均一な処理を行う観点から、湿式処理法が好ましい。
　表面処理に用いるシランカップリング剤としては、アミノシラン系カップリング剤、エポキシシラン系カップリング剤、メルカプトシラン系カップリング剤、シラン系カップリング剤、オルガノシラザン化合物等が挙げられる。これらは１種または２種以上を組み合わせて使用してもよい。
　具体的に表面処理剤としては、アミノプロピルメトキシシラン、アミノプロピルトリエトキシシラン、ウレイドプロピルトリエトキシシラン、Ｎ－フェニルアミノプロピルトリメトキシシラン、Ｎ－２（アミノエチル）アミノプロピルトリメトキシシラン等のアミノシラン系カップリング剤；グリシドキシプロピルトリメトキシシラン、グリシドキシプロピルトリエトキシシラン、グリシドキシプロピルメチルジエトキシシラン、グリシジルブチルトリメトキシシラン、（３，４－エポキシシクロヘキシル）エチルトリメトキシシラン等のエポキシシラン系カップリング剤；メルカプトプロピルトリメトキシシラン、メルカプトプロピルトリエトキシシラン等のメルカプトシラン系カップリング剤；メチルトリメトキシシラン、ビニルトリメトキシシラン、オクタデシルトリメトキシシラン、フェニルトリメトキシシラン、メタクリロキシプロピルトリメトキシシラン、イミダゾールシラン、トリアジンシラン等のシラン系カップリング剤；ＣＦ３（ＣＦ２）７ＣＨ２ＣＨ２Ｓｉ（ＯＣＨ３）３、ＣＦ３（ＣＦ２）７ＣＨ２ＣＨ２ＳｉＣｌ３、ＣＦ３（ＣＦ２）７ＣＨ２ＣＨ２Ｓｉ（ＣＨ３）（ＯＣＨ３）２、ＣＦ３（ＣＦ２）７ＣＨ２ＣＨ２Ｓｉ（ＣＨ３）Ｃ１２、ＣＦ３（ＣＦ２）５ＣＨ２ＣＨ２ＳｉＣｌ３、ＣＦ３（ＣＦ２）５ＣＨ２ＣＨ２Ｓｉ（ＯＣＨ３）３、ＣＦ３ＣＨ２ＣＨ２ＳｉＣｌ３、ＣＦ３ＣＨ２ＣＨ２Ｓｉ（ＯＣＨ３）３、Ｃ８Ｆ１７ＳＯ２Ｎ（Ｃ３Ｈ７）ＣＨ２ＣＨ２ＣＨ２Ｓｉ（ＯＣＨ３）３、Ｃ７Ｆ１５ＣＯＮＨＣＨ２ＣＨ２ＣＨ２Ｓｉ（ＯＣＨ３）３、Ｃ８Ｆ１７ＣＯ２ＣＨ２ＣＨ２ＣＨ２Ｓｉ（ＯＣＨ３）３、Ｃ８Ｆ１７－Ｏ－ＣＦ（ＣＦ３）ＣＦ２－Ｏ－Ｃ３Ｈ６ＳｉＣｌ３、Ｃ３Ｆ７－Ｏ－（ＣＦ（ＣＦ３）ＣＦ２－Ｏ）２－ＣＦ（ＣＦ３）ＣＯＮＨ－（ＣＨ２）３Ｓｉ（ＯＣＨ３）３等のフッ素含有シランカップリング剤；ヘキサメチルジシラザン、ヘキサフェニルジシラザン、トリシラザン、シクロトリシラザン、１，１，３，３，５，５－ヘキサメチルシクロトリシラザン等のオルガノシラザン化合物等が挙げられる。
　シランカップリング剤の処理量としては、中空シリカ粒子の粒子１００質量部に対して、１質量部以上であることが好ましく、１．５質量部以上がより好ましく、２質量部以上がさらに好ましく、また１０質量部以下であることが好ましく、８質量部以下がより好ましく、５質量部以下がさらに好ましい。すなわち、シランカップリング剤の処理量は、中空シリカ粒子の粒子１００質量部に対して１～１０質量部の範囲であるのが好ましい。
　シランカップリング剤で処理する方法としては、例えば、中空シリカ焼成粒子にシランカップリング剤をスプレーする乾式法や、中空シリカ焼成粒子を溶剤に分散させてからシランカップリング剤を加えて反応させる湿式法等が挙げられる。
　上記工程により得られた中空シリカ粒子は、乾燥や焼成の工程により凝集していることがあるため、取り扱いやすい凝集径にするために解砕してもよい。解砕の方法としては、例えば、乳鉢を使う方法、乾式あるいは湿式のボールミルを使う方法、振とう式篩を使う方法、ピンミル、カッターミル、ハンマーミル、ナイフミル、ローラーミル、ジェットミルなどの解砕機を使う方法等がある。なお、二次粒子の好ましい凝集径（具体的に、メジアン径及び粗大粒径）は上記したとおりである。
　本発明の中空シリカ粒子は緻密化されたシェル層を有するので、メチルエチルケトンやＮ－メチルピロリドン等の有機溶媒に添加した際に各種溶媒の浸透性が低い。よって各種溶媒における分散性が良好であり、また、溶媒中における中空粒子特有の性質を維持できる。
　本発明の中空シリカ粒子は、各種充填材として使用でき、特にパソコン、ノートパソコン、デジタルカメラ等の電子機器や、スマートフォン、ゲーム機等の通信機器等に用いられる電子基板の作製に用いられる樹脂組成物の充填材として好適に使用できる。具体的には、本発明のシリカ粉末は、低誘電率化、低伝送損失化、低吸湿化、剥離強度向上のために、樹脂組成物、プリプレグ、金属箔張積層板、プリント配線板、樹脂シート、接着層、接着フィルム、ソルダーレジスト、バンプリフロー用、再配線絶縁層、ダイボンド材、封止材、アンダーフィル、モールドアンダーフィルおよび積層インダクタ等への応用も期待される。
　以下、本発明を実施例により詳しく説明するが、本発明はこれらに限定されるものではない。以下の説明において、共通する成分は同じものを用いている。また、特に説明のない限り、「％」、「部」はそれぞれ「質量％」、「質量部」を表す。
　また、例１～１２は実施例であり、例１３～１５は比較例である。
＜試験例１＞
（例１）
「エマルションの作製」
　純水１２５０ｇにＥＯ－ＰＯ－ＥＯブロックコポリマー（ＡＤＥＫＡ社製プルロニックＦ６８）を４ｇ添加し溶解するまで撹拌した。この水溶液にソルビタン酸モノオレート（三洋化成社製イオネットＳ－８０）４ｇを溶解したｎ－デカン４２ｇを加え、ＩＫＡ社製ホモジナイザーを使って液全体が均一になるまで撹拌し、粗エマルションを作製した。
　この粗エマルションを、高圧乳化機（エスエムテー社製ＬＡＢ１０００）を使い、圧力５０ｂａｒで乳化を行い、エマルション径が１μｍの微細エマルションを作製した。
「乳化液エージング」
　得られた微細エマルションを４０℃で１２時間静置することで、エージング後エマルションを得た。
「１段目シェル形成」
　得られたエージング後エマルション１３００ｇに、ｐＨが２となるよう、希釈したケイ酸ナトリウム水溶液（ＳｉＯ２濃度１０．４質量％、Ｎａ２Ｏ濃度３．６質量％）２３ｇと２Ｍ塩酸を加え、３０℃で保持しながら良く撹拌した。
　この液を良く撹拌しながら１Ｍ水酸化ナトリウム水溶液をｐＨが６となるようゆっくり滴下し、オイルコア－シリカシェル粒子分散液を得た。得られたオイルコア－シリカシェル粒子分散液を保持し、熟成させた。
「２段目シェル形成」
　１段目シェル形成で得られたオイルコア－シリカシェル粒子分散液全量を７０℃に加熱し、撹拌しながら１Ｍ　ＮａＯＨをゆっくり添加し、ｐＨを９とした。
　次に、希釈したケイ酸ナトリウム水溶液（ＳｉＯ２濃度１０．４質量％、Ｎａ２Ｏ濃度３．６質量％）３３０ｇを、ｐＨ９になるように０．５Ｍ塩酸とともに徐々に添加した。
　この懸濁液を８０℃で１日間保持した後、室温まで冷却し、中空シリカ前駆体分散液を得た。
「ろ過、洗浄、乾燥、焼成」
　中空シリカ前駆体分散液全量を、２Ｍ塩酸でｐＨ２まで中和後、定量ろ紙５Ｃを用いてろ過を行った。その後、８０℃のイオン交換水３５０ｍｌを加えて再度加圧濾過し、中空シリカケーキを洗浄した。
　ろ過後のケーキを、窒素雰囲気下で、１００℃で１時間、続けて４００℃で２時間乾燥し（昇温時間１０℃／ｍｉｎ）、有機分を除去することで中空シリカ前駆体を得た。
　得られた中空シリカ前駆体を、１０００℃で１時間焼成（昇温時間１０℃／ｍｉｎ）することでシェルの焼き締めを行い、中空シリカ焼成粒子を得た。
「表面処理」
　２００ｍｌガラスビーカーに、前記中空シリカ焼成粒子１０ｇ、イソプロパノール１５０ｍｌ、ビニルトリメトキシシラン０．１ｇを添加し、１００℃で１時間還流した。その後、疎水性ＰＴＦＥメンブレンフィルターを用いて減圧濾過し、イソプロパノール２０ｍｌで洗浄後、１５０℃に温度調整した真空乾燥機で２時間真空乾燥し、表面処理された中空シリカ粒子を得た。
「評価」
１．乾式ピクノメーターを用いた密度測定
　乾式ピクノメーター（Ｍｉｃｒｏｍｅｒｉｔｉｃｓ社製ＡｃｃｕＰｙｃＩＩ　１３４０）を用いて密度を測定した。測定条件は下記の通りである。結果を表１に示す。
・試料セル：１０ｃｍ３セル
・試料重量：１．０ｇ
・測定ガス：ヘリウム、あるいは、アルゴン
・パージ回数：１０回
・パージ処理充填圧力：１３５ｋＰａｇ
・サイクル回数：１０回
・サイクル充填圧力：１３５ｋＰａｇ
・圧力平衡を終了するレート：０．０５ｋＰａｇ／分
２．真球度、平均一次粒子径±４０％以内の粒子径となる粒子の割合
　例１で得られた中空シリカ粒子の走査型電子顕微鏡像（ＳＥＭ像）を図１に示す。ＳＥＭ像は日立ハイテク社製のＳ４８００を用いて、加速電圧５ｋＶで観察した。
　図１から任意の１００個の粒子について、それぞれの外接円の径（ＤＬ）と、内接円の径（ＤＳ）とを測定し、外接円の径（ＤＬ）に対する内接円の径（ＤＳ）の比（ＤＳ／ＤＬ）を算出した平均値から真球度を求めた。また、任意の１００個の粒子の一次粒子径を測定し、それらを集計して得られた分布から、平均一次粒子径±４０％以内の粒子径となる粒子の割合を求めた。
３．メジアン径（Ｄ５０）、粗大粒径（Ｄ９０）
　得られた中空シリカ粒子（二次粒子）をマイクロトラック・ベル社製の回折散乱式粒子分布測定装置（ＭＴ３３００）によって測定し、粒子分布（直径）の中央値（メジアン径、Ｄ５０）及び粗大粒径（９０％径、Ｄ９０）を測定した。測定は２回行い、平均値を求めた。結果を表１に示す。
４．比表面積
　中空シリカ粒子を２３０℃で減圧乾燥して水分を完全に除去し、試料とした。この試料について、マイクロメリティック社製の自動比表面積、細孔分布測定装置「トライスターＩＩ」にて、窒素ガスを用いて多点ＢＥＴ法比表面積測定した。結果を表１に示す。
５．金属Ｍ（Ｍ＝Ｌｉ，Ｎａ，Ｋ，Ｒｂ，Ｃｓ，Ｍｇ，Ｃａ，Ｓｒ，Ｂａ）の濃度
　球状中空シリカ粒子に過塩素酸とフッ酸を加えて強熱し、主成分のケイ素を除去したのちにＩＣＰＥ－９０００（島津製作所社製）を用いてＩＣＰ－ＡＥＳ（高周波誘導結合プラズマ発光分光分析法）により測定した。前記測定により、金属ＭとしてＮａ、Ｋ、Ｍｇ、Ｃａが検出された。金属Ｍの総量を表１に示す。
６．粘度
　アルゴンガスを用いた乾式ピクノメーターによる密度測定により求めた粒子の密度をＡ（ｇ／ｃｍ３）として、煮アマニ油６質量部と中空シリカ粒子（６×Ａ／２．２）質量部を混合し、２０００ｒｐｍで３分間混練して得た混練物を、回転式レオメータを用いてせん断速度１ｓ－１で３０秒測定し、３０秒時点での粘度を求めた。結果を表１に示す。
７．Ｑ３／Ｑ４
　４００ＭＨｚの核磁気共鳴装置を用い、直径７．５ｍｍのＣＰ／ＭＡＳ用プローブを装着し、観測核を２９Ｓｉとし、ＤＤ／ＭＡＳ法で測定した。測定条件は、２９Ｓｉ共鳴周波数を７９．４３ＭＨｚ、２９Ｓｉ９０°パルス幅を５μ秒、１Ｈ共鳴周波数を３９９．８４ＭＨｚ、１Ｈデカップリング周波数を５０ｋＨｚ、ＭＡＳ回転数を４ｋＨｚ、スペクトル幅を３０．４９ｋＨｚ、測定温度を２３℃とした。データ解析は、フーリエ変換後のスペクトルの各ピークについて、ローレンツ波形とガウス波形の混合により作成したピーク形状の中心位置、高さ、半値幅を可変パラメータとして、非線形最小二乗法により最適化計算を行った。Ｑ１、Ｑ２、Ｑ３及びＱ４の４つの構造単位を対象とし、得られたＱ１の含有率、Ｑ２の含有率、Ｑ３の含有率及びＱ４の含有率から、Ｑ３とＱ４のモル比率を算出した。結果を表１に示す。
８．比誘電率、誘電正接
　比誘電率、誘電正接は、専用の装置（ベクトルネットワークアナライザ「Ｅ５０６３Ａ」、キーコム社製）を用い、摂動方式共振器法にて、試験周波数１ＧＨｚ、試験温度約２４℃、湿度約４５％、測定回数３回で測定を実施した。
　具体的には、中空シリカ粒子を１５０℃で真空乾燥後、ＰＴＦＥの筒に粉末を十分にタップしながら充填し、容器ごと比誘電率を測定した後、対数混合則を用いて粉末の比誘電率および誘電正接に換算した。結果を表１に示す。
（例２）
　ＥＯ－ＰＯ－ＥＯブロックコポリマー（ＡＤＥＫＡ社製「プルロニックＦ６８」）を２ｇに、ソルビタン酸モノオレート（三洋化成社製イオネットＳ－８０）を２ｇに変更した以外は例１と同じ条件で実施した。
（例３）
　ＥＯ－ＰＯ－ＥＯブロックコポリマー（ＡＤＥＫＡ社製「プルロニックＦ６８」）を１０ｇに変更し、ソルビタン酸モノオレート（三洋化成社製イオネットＳ－８０）を使用せず、圧力１００ｂａｒで乳化を行ったこと以外は例１と同じ条件で実施した。
（例４）
　得られた中空シリカ前駆体を、１１００℃で１時間焼成（昇温時間１０℃／ｍｉｎ）した以外は例１と同じ条件で実施した。
（例５）
　得られた中空シリカ前駆体を、８００℃で１時間焼成（昇温時間１０℃／ｍｉｎ）した以外は例１と同じ条件で実施した。
（例６）
　得られた中空シリカ前駆体を、７００℃で１時間焼成（昇温時間１０℃／ｍｉｎ）した以外は例１と同じ条件で実施した。
（例７）
　イオン交換水の代わりに水道水３５０ｍｌを加えて再度加圧濾過して中空シリカケーキを洗浄した以外は、例１と同じ条件で実施した。
（例８）
　表面処理を実施しなかった以外は、例１と同じ条件で実施した。
（例９）
　得られた微細エマルションを８０℃で４時間静置してエージングを行った以外は、例１と同じ条件で実施した。
（例１０）
　ＥＯ－ＰＯ－ＥＯブロックコポリマー（ＡＤＥＫＡ社製「プルロニックＦ６８」）を３ｇに、ソルビタン酸モノオレート（三洋化成社製イオネットＳ－８０）を５ｇに変更した以外は例１と同じ条件で実施した。
（例１１）
　１段目シェル形成、２段目シェル形成を以下により行った以外は例１と同じ条件で実施した。
　「１段目シェル形成」
　得られた微細エマルション１３００ｇに、ｐＨが２となるよう、オルトケイ酸メチル０．９０ｇと２Ｍ塩酸を加え、３０℃で保持しながら良く撹拌した。
　この液を良く撹拌しながら１Ｍアンモニア水をｐＨが６となるようゆっくり滴下し、オイルコア－シリカシェル粒子分散液を得た。得られたオイルコア－シリカシェル粒子分散液を保持し、熟成させた。
「２段目シェル形成」
　１段目シェル形成で得られたオイルコア－シリカシェル粒子分散液全量を７０℃に加熱し、撹拌しながら５Ｍアンモニア水をゆっくり添加し、ｐＨを９とした。
　次に、希釈したオルトケイ酸メチル１３ｇを、ｐＨ９になるように０．５Ｍ塩酸とともに徐々に添加した。
　この懸濁液を７０℃で２日間保持した後、ゆっくり室温まで冷却し、中空シリカ前駆体分散液を得た。
（例１２）
　ＳＯ－Ｃ２（メジアン径０．５μｍの爆燃法シリカ、中実シリカ、アドマテックス社製）を水に分散させ、３質量％水分散液を得た。スプレードライヤー（日本ビュッヒ株式会社製、ミニスプレードライヤーＢ２９０）により１２０℃で乾燥して、メジアン径３μｍの前駆体シリカを得た。この前駆体シリカを１３００℃で焼成し、内部に空間部を有する中空シリカ粒子を得た。
（例１３）
　例１で得られた中空シリカ前駆体を、焼成せずにそのまま使用した。
（例１４）
　ＳＯ－Ｃ２（メジアン径０．５μｍの爆燃法シリカ、中実シリカ、アドマテックス社製）をそのまま用いた。
（例１５）
　ｉＭ１６Ｋ（メジアン径１８μｍのガラスバルーン、３Ｍ社）をそのまま用いた。
　上記の結果を表１にまとめて示す。
Figure JPOXMLDOC01-appb-T000001
　表１に示したように、例１～１２は、乾式ピクノメーターを用いた密度測定では、測定ガスにヘリウムを用いた場合は密度が１．９５～２．２８ｇ／ｃｍ３であり、シリカの真密度と同等の値が得られており、ヘリウムガスがシェルを通過し、中空シリカの内腔へ侵入することがわかった。一方、アルゴンガスを用いた場合は、いずれの例でもヘリウムピクノメーター法による値より小さい値が得られており、アルゴンガスがシェルを通過する速度が遅いため、中空シリカの内腔を含まない粒子密度が得られたと考えられる。
　また、例１～１２は１ＧＨｚでの比誘電率が小さかったのに対し、例１４は１ＧＨｚでの比誘電率が大きく、本発明の所望の効果を得られないものであった。これは、例１～１２のシリカ粒子の内部に空間が存在することで、空気の含有分比誘電率が低下したためと考えられる。また、例１３および１５は１ＧＨｚでの誘電正接が大きく、本発明の所存の効果を得られないものであった。これは例１３の中空シリカはＡｒ密度×ＢＥＴ比表面積の値が大きく、さらにＱ３／Ｑ４の値が大きく、シリカあたりに含まれるシラノール基が多くなりやすいため、誘電正接が悪化したと考えられる。また、例１５はシリカでなくガラスバルーンのため、アルカリ成分が多く、シラノール基が多くなりやすいため、誘電正接が悪化したと考えられる。
＜試験例２＞
（評価サンプルＡ（樹脂フィルム）の作製）
　例１、２、１４、１５の粒子粉末を用いて樹脂フィルムを作製した。
　ビフェニル型エポキシ樹脂（エポキシ当量２７６、日本化薬（株）製「ＮＣ－３０００」）２５質量部をメチルエチルケトン（ＭＥＫ）１３質量部に攪拌しながら加熱溶解させた。室温にまで冷却後、そこへ活性エステル系硬化剤（ＤＩＣ（株）製「ＨＰ８０００－６５Ｔ」、活性基当量２２３、不揮発成分６５質量％のトルエン溶液）３２質量部を混合し、自転公転式の撹拌機であるあわとり練太郎（シンキー社製）で２０００ｒｐｍ、５分間混練し、硬化促進剤として４－ジメチルアミノピリジン（ＤＭＡＰ）０．９質量部、２－エチル－４－メチルイミダゾール（四国化成工業株式会社製「２Ｅ４ＭＺ」）１．６質量部を混合し、あわとり練太郎で２０００ｒｐｍ、５分間混練した。そこへアルゴンガスを用いた乾式ピクノメーターによる密度測定により求めた粒子の密度をＡ（ｇ／ｃｍ３）として、（６×Ａ／２．２）質量部の粒子粉末を混合し、あわとり練太郎で２０００ｒｐｍ、５分間混合した。
　次に、離型処理された透明なポリエチレンテレフタレート（ＰＥＴ）フィルム（リンテック社製「ＰＥＴ５０１１　５５０」、厚み５０μｍ）を用意した。このＰＥＴフィルムの離型処理面に、アプリケーターを用いて、得られたワニスを乾燥後の厚みが４０μｍとなるように塗工し、１００℃のギアオーブン内で１０分間乾燥したあと裁断し、縦２００ｍｍ×横２００ｍｍ×厚み４０μｍの樹脂フィルムの未硬化物（Ｂステージフィルム）を備えた未硬化積層フィルムを作製した。
　得られた未硬化積層フィルムを、ギアオーブン内で１９０℃、９０分加熱して樹脂フィルムの未硬化物を硬化させて、樹脂フィルムを作製した。
（評価サンプルＢ（積層体）の作製）
（１）ラミネート工程
　片面粗化銅箔（Ｆ０－ＷＳ、厚み１８μｍ、表面粗さＲｚ＝１．２μｍ、古河電気工業社製）を用意した。この銅箔に、名機製作所社製「バッチ式真空ラミネーターＭＶＬＰ－５００－ＩＩＡ」を用いて、上記で作製した未硬化積層フィルムを、未硬化樹脂フィルム（Ｂステージフィルム）の表面が銅箔粗化面に対向するようにラミネートして、銅箔／Ｂステージフィルム／ＰＥＴフィルムからなる積層構造体を得た。ラミネートの条件は、３０秒減圧して気圧を１３ｈＰａ以下とし、その後３０秒間、１００℃及び圧力０．８ＭＰａでプレスする条件とした。
（２）フィルム剥離工程
　積層構造体のＰＥＴフィルムを剥離した。
（３）硬化工程
　内部の温度が１８０℃のギアオーブン内に積層板を３０分間入れ、Ｂステージフィルムを硬化させて、絶縁層を形成した。
「評価」
１．比誘電率、誘電正接の評価
　得られた評価サンプルＡについて、縦スプリットポスト誘電体共振器（Ａｇｉｌｅｎｔ　Ｔｅｃｈｎｏｌｏｇｉｅｓ社製）にて、比誘電率と誘電正接（測定周波数：１０ＧＨｚ）とを測定した。結果を表２に示す。
２．平均線膨張率の測定
　評価サンプルＡを、３ｍｍ×２５ｍｍの大きさに裁断した。このサンプルについて、熱機械分析装置（島津製作所社製、「ＴＭＡ－６０」）を使用して、荷重５Ｎ、昇温速度２℃／ｍｉｎで加熱した。そして、３０℃から１５０℃までのサンプルの寸法変化を測定し、長辺の寸法変化を温度で割って、平均線膨張率（ｐｐｍ／℃）を求めた。結果を表２に示す。
３．ピール強度の測定
　評価サンプルＢについて、銅箔側に１ｃｍ幅となるように短冊状に切込みを入れた。９０°剥離試験機に基板をセットし、つかみ具で切込みの入った銅めっきの端部をつまみあげ、銅めっきを２０ｍｍ剥離してピール強度（Ｎ／ｃｍ）を測定した。結果を表２に示す。
Figure JPOXMLDOC01-appb-T000002
　表２の結果より、Ａｒ密度とＢＥＴ比表面積との積（Ａ×Ｂ）が小さい中空シリカ粒子である例１、２を用いた場合は、比誘電率、誘電正接ともに良好で、平均線膨張率が小さいことが分かった。樹脂組成物中でも優れた低比誘電率および低誘電正接が発揮されていることから、溶媒であるメチルエチルケトンが浸透し難いことが確認でき、メチルエチルケトンよりも分子が大きいＮ－メチルピロリドン、シクロヘキサノン、メチルイソブチルケトンなどの溶媒も浸透し難いことが分かった。例１４のように中実シリカを用いると、比誘電率が高く、ピール強度が悪化した。また、例１５のようにホウケイ酸ガラスバルーンを用いると、ホウケイ酸ガラスに含まれるアルカリ分によって表面シラノールが多いため、誘電正接が高く、またシリカと比較してホウケイ酸ガラスの熱膨張率は大きいため、平均線膨張率も高くなることが分かった。
　本発明を詳細にまた特定の実施形態を参照して説明したが、本発明の精神と範囲を逸脱することなく様々な変更や修正を加えることができることは当業者にとって明らかである。本出願は、２０２１年１１月３０日出願の日本特許出願（特願２０２１－１９４３７１）に基づくものであり、その内容はここに参照として取り込まれる。

Claims (18)

  1. 　シリカを含むシェル層を備え、前記シェル層の内部に空間部を有する中空シリカ粒子であって、
    　アルゴンガスを用いた乾式ピクノメーターによる密度測定により求めた粒子の密度をＡ（ｇ／ｃｍ３）、ＢＥＴ比表面積をＢ（ｍ２／ｇ）とすると、前記密度と前記ＢＥＴ比表面積との積（Ａ×Ｂ）が１～１２０ｍ２／ｃｍ３である中空シリカ粒子。
  2. 　前記アルゴンガスを用いた乾式ピクノメーターによる密度測定により求めた粒子の密度が０．３５～２．００ｇ／ｃｍ３である、請求項１に記載の中空シリカ粒子。
  3. 　ヘリウムガスを用いた乾式ピクノメーターによる密度測定により求めた粒子の密度が２．００～２．３５ｇ／ｃｍ３である、請求項１又は２に記載の中空シリカ粒子。
  4. 　平均一次粒子径が５０ｎｍ～１０μｍである、請求項１～３のいずれか１項に記載の中空シリカ粒子。
  5. 　一次粒子のうち、粒子全体の３５％以上が平均一次粒子径±４０％以内の粒子径である、請求項１～４のいずれか１項に記載の中空シリカ粒子。
  6. 　前記ＢＥＴ比表面積が１～１００ｍ２／ｇである、請求項１～５のいずれか１項に記載の中空シリカ粒子。
  7. 　真球度が０．７５～１．０である、請求項１～６のいずれか１項に記載の中空シリカ粒子。
  8. 　二次粒子のメジアン径（Ｄ５０）が０．１～１０μｍである、請求項１～７のいずれか１項に記載の中空シリカ粒子。
  9. 　二次粒子の粗大粒径（Ｄ９０）が１～３０μｍである、請求項１～８のいずれか１項に記載の中空シリカ粒子。
  10. 　前記中空シリカ粒子に含まれるＬｉ、Ｎａ、Ｋ、Ｒｂ、Ｃｓ、Ｍｇ、Ｃａ、Ｓｒ及びＢａからなる群から選択される１種以上の金属Ｍの濃度の総和が５０質量ｐｐｍ以上１質量％以下である、請求項１～９のいずれか１項に記載の中空シリカ粒子。
  11. 　前記中空シリカ粒子を含む混練物の、下記測定方法により測定される粘度が１００００ｍＰａ・ｓ以下である、請求項１～１０のいずれか１項に記載の中空シリカ粒子。
    （測定方法）
    　アルゴンガスを用いた乾式ピクノメーターによる密度測定により求めた粒子の密度をＡ（ｇ／ｃｍ３）として、煮アマニ油６質量部と前記中空シリカ粒子（６×Ａ／２．２）質量部を混合し、２０００ｒｐｍで３分間混練して得た混練物を、回転式レオメータを用いてせん断速度１ｓ－１で３０秒測定し、３０秒時点での粘度を求める。
  12. 　固体２９Ｓｉ－ＤＤ／ＭＡＳ－ＮＭＲにより測定した、シラノール基由来のＯＨ基を持たないＱ４構造に対するシラノール基由来のＯＨ基を１つ有するＱ３構造のモル比率（Ｑ３／Ｑ４）が、２～４０％である、請求項１～１１のいずれか１項に記載の中空シリカ粒子。
  13. 　請求項１～１２のいずれか１項に記載の中空シリカ粒子の製造方法であって、
    　水相、油相及び界面活性剤を含む水中油型エマルションを作製し、前記水中油型エマルションを０．５～２４０時間静置し、前記水中油型エマルション中でコアの外周にシリカを含むシェル層が形成された中空シリカ前駆体を得て、前記中空シリカ前駆体から前記コアを除去し、熱処理する中空シリカ粒子の製造方法。
  14. 　熱処理後の粒子に対してシランカップリング剤で表面処理する、請求項１３に記載の中空シリカ粒子の製造方法。
  15. 　前記水中油型エマルションに、シリカ原料を添加する、請求項１３又は１４に記載の中空シリカ粒子の製造方法。
  16. 　シリカ源としてケイ酸ナトリウムを用いる、請求項１５に記載の中空シリカ粒子の製造方法。
  17. 　請求項１～１２のいずれか１項に記載の中空シリカ粒子を、５～７０質量％含む樹脂組成物。
  18. 　請求項１～１２のいずれか１項に記載の中空シリカ粒子を、１～４０質量％含むスラリー組成物。
PCT/JP2022/042755 2021-11-30 2022-11-17 中空シリカ粒子及びその製造方法 Ceased WO2023100676A1 (ja)