WO2023054940A1 - 음극 활물질, 이의 제조방법, 이를 포함하는 음극 및 이차전지 - Google Patents
음극 활물질, 이의 제조방법, 이를 포함하는 음극 및 이차전지 Download PDFInfo
- Publication number
- WO2023054940A1 WO2023054940A1 PCT/KR2022/013728 KR2022013728W WO2023054940A1 WO 2023054940 A1 WO2023054940 A1 WO 2023054940A1 KR 2022013728 W KR2022013728 W KR 2022013728W WO 2023054940 A1 WO2023054940 A1 WO 2023054940A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- active material
- negative electrode
- electrode active
- natural graphite
- coating layer
- Prior art date
Abstract
Description
음극 활물질 | 음극 | |||
구형화도 | 수은 포로시미터 측정법에 의해 측정된 공극 부피(mL/g) | BET 질소 흠착법에 의해 측정된 비표면적(m2/g) | 배향지수 I(004)/I(110) | |
실시예 1 | 0.91 | 0.09 | 1.6 | 16 |
실시예 2 | 0.94 | 0.12 | 1.8 | 19 |
실시예 3 | 0.88 | 0.07 | 1.1 | 13 |
비교예 1 | 0.93 | 0.27 | 2.6 | 37 |
비교예 2 | 0.71 | 0.67 | 2.3 | 29 |
비교예 3 | 0.89 | 0.26 | 1.7 | 32 |
비교예 4 | 0.79 | 0.04 | 1.0 | 12 |
Li-plating SOC(%) | 용량 유지율(%, @45℃, 200cycle) | Swelling ratio(%) | |
실시예 1 | 34 | 88 | 25 |
실시예 2 | 32 | 84 | 28 |
실시예 3 | 35 | 82 | 27 |
비교예 1 | 27 | 78 | 36 |
비교예 2 | 27 | 79 | 40 |
비교예 3 | 29 | 75 | 34 |
비교예 4 | 33 | 79 | 35 |
Claims (15)
- 2 이상의 1차 입자가 응집된 2차 입자를 포함하고,상기 1차 입자는 1차 천연흑연 입자 및 상기 1차 천연흑연 입자 표면의 적어도 일부에 위치하는 비정질 탄소 코팅층을 포함하고,수은 포로시미터 측정법에 의해 측정된 공극 부피가 0.06mL/g 내지 0.15mL/g인 음극 활물질.
- 청구항 1에 있어서,상기 음극 활물질의 BET 질소 흡착법에 의해 측정된 BET 비표면적은 0.9m2/g 내지 3.0m2/g인 음극 활물질.
- 청구항 1에 있어서,상기 음극 활물질은 구형인 음극 활물질.
- 청구항 1에 있어서,상기 1차 천연흑연 입자 및 상기 비정질 탄소 코팅층의 중량비는 75:25 내지 99:1인 음극 활물질.
- 청구항 1에 있어서,상기 2차 입자 상에 위치하는 추가 비정질 탄소 코팅층을 더 포함하는 음극 활물질.
- 청구항 5에 있어서,상기 추가 비정질 탄소 코팅층은 상기 음극 활물질에 1중량% 내지 15중량%로 포함되는 음극 활물질.
- 청구항 1에 있어서,상기 음극 활물질의 평균 입경(D50)은 10㎛ 내지 30㎛인 음극 활물질.
- 2 이상의 1차 천연흑연 입자를 응집시키고 1차 구형화하는 단계;상기 1차 구형화 후, 상기 1차 천연흑연 입자 표면의 적어도 일부에 비정질 탄소 코팅층을 형성하여 중간 구조체를 형성하는 단계; 및상기 중간 구조체를 2차 구형화하는 단계;를 포함하는 청구항 1에 따른 음극 활물질의 제조방법.
- 청구항 8에 있어서,상기 1차 천연흑연 입자는 인편상 천연흑연 입자인 음극 활물질의 제조방법.
- 청구항 8에 있어서,상기 2차 구형화된 중간 구조체를 해쇄하는 단계를 더 포함하는 음극 활물질의 제조방법.
- 청구항 8에 있어서,상기 2차 구형화된 중간 구조체를 열처리하는 단계를 더 포함하는 음극 활물질의 제조방법.
- 청구항 8에 있어서,상기 2차 구형화된 중간 구조체 상에 추가 비정질 탄소 코팅층을 형성하는 단계를 더 포함하는 음극 활물질의 제조방법.
- 음극 집전체; 및상기 음극 집전체의 적어도 일면에 배치된 음극 활물질층;을 포함하고,상기 음극 활물질층은 청구항 1에 따른 음극 활물질을 포함하는 음극.
- 청구항 13에 있어서,상기 음극의 배향 지수 I(004)/I(110)은 10 내지 25인 음극.
- 청구항 13에 따른 음극;양극;상기 음극 및 상기 양극 사이에 개재되는 분리막; 및전해질;을 포함하는 이차전지.