WO2023026635A1 - 負極活物質、及びリチウムイオン電池 - Google Patents

負極活物質、及びリチウムイオン電池 Download PDF

Info

Publication number
WO2023026635A1
WO2023026635A1 PCT/JP2022/023408 JP2022023408W WO2023026635A1 WO 2023026635 A1 WO2023026635 A1 WO 2023026635A1 JP 2022023408 W JP2022023408 W JP 2022023408W WO 2023026635 A1 WO2023026635 A1 WO 2023026635A1
Authority
WO
WIPO (PCT)
Prior art keywords
negative electrode
electrode active
active material
lithium
ion battery
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2022/023408
Other languages
English (en)
French (fr)
Japanese (ja)
Inventor
和子 浅野
雪尋 沖
光宏 日比野
菜々美 竹田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Panasonic Intellectual Property Management Co Ltd
Original Assignee
Panasonic Intellectual Property Management Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Panasonic Intellectual Property Management Co Ltd filed Critical Panasonic Intellectual Property Management Co Ltd
Priority to CN202280056719.XA priority Critical patent/CN117836979A/zh
Priority to US18/681,201 priority patent/US20250140820A1/en
Priority to EP22860929.3A priority patent/EP4394934A4/en
Priority to JP2023543705A priority patent/JP7814016B2/ja
Publication of WO2023026635A1 publication Critical patent/WO2023026635A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Links

Images

Classifications

    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/38—Selection of substances as active materials, active masses, active liquids of elements or alloys
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/38—Selection of substances as active materials, active masses, active liquids of elements or alloys
    • H01M4/387—Tin or alloys based on tin
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/052—Li-accumulators
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/052—Li-accumulators
    • H01M10/0525—Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/056—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes
    • H01M10/0561—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes the electrolyte being constituted of inorganic materials only
    • H01M10/0562—Solid materials
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/13—Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
    • H01M4/134—Electrodes based on metals, Si or alloys
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/38—Selection of substances as active materials, active masses, active liquids of elements or alloys
    • H01M4/386—Silicon or alloys based on silicon
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
    • H01M4/50—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of manganese
    • H01M4/505—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of manganese of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/48—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides
    • H01M4/52—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron
    • H01M4/525—Selection of substances as active materials, active masses, active liquids of inorganic oxides or hydroxides of nickel, cobalt or iron of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M2004/026—Electrodes composed of, or comprising, active material characterised by the polarity
    • H01M2004/027—Negative electrodes
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
    • Y02E60/10—Energy storage using batteries

Definitions

  • the present disclosure relates to negative electrode active materials and lithium ion batteries.
  • Lithium-ion batteries which are charged and discharged by moving lithium ions (Li ions) between the positive and negative electrodes, are widely used.
  • Si which has a higher capacity than graphite, has been used as a negative electrode active material contained in the negative electrode of this lithium ion battery.
  • Si has a problem that its volume changes greatly during charging and discharging, and the battery capacity tends to decrease due to repeated charging and discharging.
  • Non-Patent Document 1 the alloy having the La 3 Ni 2 Sn 7 -type crystal structure described in Non-Patent Document 1 has a higher volume energy density but a lower weight energy density than graphite.
  • An object of the present disclosure is to provide a negative electrode active material having a La 3 Ni 2 Sn 7 -type crystal structure and high weight energy density, and a lithium ion battery using the same.
  • a negative electrode active material that is one aspect of the present disclosure is a negative electrode active material contained in a negative electrode of a lithium ion battery, and has the general formula M 3 Me 2 X 7 (wherein M is at least one of La and Ca, Me contains at least one element selected from the group consisting of Mn, Ni, Fe, and Co, and X contains at least one element selected from the group consisting of Ge, Si, Sn, and Al element), and the dislocation density of the negative electrode active material is 1 ⁇ 10 15 cm ⁇ 2 or more.
  • a lithium ion battery includes a negative electrode containing the negative electrode active material, a positive electrode, and a non-aqueous electrolyte.
  • weight energy density can be increased.
  • FIG. 1 is a vertical cross-sectional view of a cylindrical lithium-ion battery that is an example of an embodiment
  • Patent Document 1 discloses an alloy having a La 3 Ni 2 Sn 7 -type crystal structure as a negative electrode active material for high-capacity lithium-ion batteries.
  • the alloy disclosed in Patent Document 1 has a higher volume energy density but a lower weight energy density than graphite.
  • the present inventors have found that the weight energy density can be increased by increasing the dislocation density of the negative electrode active material to 1 ⁇ 10 15 cm ⁇ 2 or more.
  • defects, voids, etc. are formed in crystal structures with a high dislocation density of 1 ⁇ 10 15 cm ⁇ 2 or more, and Li ions are formed in these defects, voids, etc. presumed to have been inserted.
  • a lithium ion battery is charged and discharged by movement of lithium ions between a positive electrode and a negative electrode.
  • a cylindrical battery in which a wound electrode assembly is housed in a bottomed cylindrical outer can be exemplified.
  • it may be an exterior body composed of a laminate sheet including a metal layer and a resin layer.
  • the electrode body may be a laminated electrode body in which a plurality of positive electrodes and a plurality of negative electrodes are alternately laminated with separators interposed therebetween.
  • a liquid non-aqueous electrolyte is exemplified below, the non-aqueous electrolyte is not limited to a liquid and may be solid.
  • FIG. 1 is a vertical cross-sectional view of a cylindrical lithium-ion battery 10 that is an example of an embodiment.
  • an electrode body 14 and a non-aqueous electrolyte (not shown) are housed in an exterior body 15 .
  • the electrode body 14 has a wound structure in which the positive electrode 11 and the negative electrode 12 are wound with the separator 13 interposed therebetween.
  • the solvent organic solvent
  • carbonates, lactones, ethers, ketones, esters and the like can be used, and two or more of these solvents can be mixed and used.
  • a mixed solvent containing a cyclic carbonate and a chain carbonate For example, cyclic carbonates such as ethylene carbonate (EC), propylene carbonate (PC), and butylene carbonate (BC) can be used, and chain carbonates such as dimethyl carbonate (DMC), ethylmethyl carbonate (EMC), and diethyl carbonate ( DEC) or the like can be used.
  • cyclic carbonates such as ethylene carbonate (EC), propylene carbonate (PC), and butylene carbonate (BC)
  • chain carbonates such as dimethyl carbonate (DMC), ethylmethyl carbonate (EMC), and diethyl carbonate ( DEC) or the like can be used.
  • the electrolyte salt of the non-aqueous electrolyte LiPF 6 , LiBF 4 , LiCF 3 SO 3 and mixtures thereof can be used.
  • the amount of electrolyte salt dissolved in the solvent can be, for example, 0.5 to 2.0 mol/L.
  • the inside of the lithium ion battery 10 is hermetically sealed by closing the opening end of the exterior body 15 with the sealing body 16 .
  • Insulating plates 17 and 18 are provided above and below the electrode body 14, respectively.
  • the positive electrode lead 19 extends upward through the through hole of the insulating plate 17 and is welded to the lower surface of the filter 22 which is the bottom plate of the sealing member 16 .
  • the cap 26, which is the top plate of the sealing member 16 electrically connected to the filter 22, serves as a positive electrode terminal.
  • the negative electrode lead 20 passes through the through hole of the insulating plate 18 , extends to the bottom side of the exterior body 15 , and is welded to the bottom inner surface of the exterior body 15 .
  • the exterior body 15 becomes a negative electrode terminal.
  • the negative electrode lead 20 When the negative electrode lead 20 is installed at the terminal end, the negative electrode lead 20 extends through the outside of the insulating plate 18 toward the bottom of the package 15 and is welded to the inner surface of the bottom of the package 15 .
  • the exterior body 15 is, for example, a bottomed cylindrical metal exterior can.
  • a gasket 27 is provided between the exterior body 15 and the sealing body 16 to ensure hermetic sealing of the inside of the lithium ion battery 10 .
  • the exterior body 15 has a grooved portion 21 that supports the sealing body 16 and is formed, for example, by pressing the side portion from the outside.
  • the grooved portion 21 is preferably annularly formed along the circumferential direction of the exterior body 15 and supports the sealing body 16 via a gasket 27 on its upper surface.
  • the sealing body 16 has a filter 22, a lower valve body 23, an insulating member 24, an upper valve body 25, and a cap 26 which are stacked in order from the electrode body 14 side.
  • Each member constituting the sealing member 16 has, for example, a disk shape or a ring shape, and each member other than the insulating member 24 is electrically connected to each other.
  • the lower valve body 23 and the upper valve body 25 are connected to each other at their central portions, and an insulating member 24 is interposed between their peripheral edge portions.
  • the positive electrode 11, the negative electrode 12, and the separator 13 that make up the electrode body 14 will be described in detail below, particularly the negative electrode active material that makes up the negative electrode 12.
  • the positive electrode 11 has, for example, a positive electrode core and a positive electrode mixture layer provided on the surface of the positive electrode core.
  • a foil of a metal such as aluminum that is stable in the potential range of the positive electrode 11, a film having the metal on the surface layer, or the like can be used.
  • the thickness of the positive electrode core is, for example, 10 ⁇ m to 30 ⁇ m.
  • the positive electrode material mixture layer contains a positive electrode active material, a binder, and a conductive agent, and is preferably provided on both sides of the positive electrode core excluding the portion where the positive electrode lead 19 is connected.
  • a positive electrode mixture slurry containing a positive electrode active material, a binder, a conductive agent, and the like is applied to the surface of a positive electrode core, the coating film is dried, and then compressed to convert the positive electrode mixture layer into a positive electrode. It can be produced by forming on both sides of the core.
  • the positive electrode active material contains lithium transition metal oxide as its main component.
  • the positive electrode active material may be substantially composed only of the lithium transition metal oxide, and inorganic compound particles such as aluminum oxide and lanthanoid-containing compounds are adhered to the surfaces of the lithium transition metal oxide particles. good too.
  • One type of lithium transition metal oxide may be used, or two or more types may be used in combination.
  • Metal elements contained in the lithium transition metal oxide include nickel (Ni), cobalt (Co), manganese (Mn), aluminum (Al), boron (B), magnesium (Mg), titanium (Ti), vanadium. (V), chromium (Cr), iron (Fe), copper (Cu), zinc (Zn), gallium (Ga), strontium (Sr), zirconium (Zr), niobium (Nb), indium (In), tin (Sn), tantalum (Ta), tungsten (W), and the like.
  • An example of a suitable lithium transition metal oxide has the general formula: Li ⁇ Ni x M (1 ⁇ x) O 2 (0.1 ⁇ 1.2, 0.3 ⁇ x ⁇ 1, M is Co, Mn , including at least one of Al).
  • Examples of the conductive agent contained in the positive electrode mixture layer include carbon materials such as carbon black, acetylene black, ketjen black, carbon nanotubes, carbon nanofibers, and graphite.
  • Examples of the binder contained in the positive electrode mixture layer include fluororesins such as polytetrafluoroethylene (PTFE) and polyvinylidene fluoride (PVdF), polyacrylonitrile (PAN), polyimide resins, acrylic resins, and polyolefin resins. . These resins may be used in combination with cellulose derivatives such as carboxymethyl cellulose (CMC) or salts thereof, polyethylene oxide (PEO), and the like.
  • the negative electrode 12 has, for example, a negative electrode core and a negative electrode mixture layer provided on the surface of the negative electrode core.
  • a foil of a metal such as copper that is stable in the potential range of the negative electrode 12, a film having the metal on the surface layer, or the like can be used.
  • the thickness of the negative electrode core is, for example, 5 ⁇ m to 15 ⁇ m.
  • the negative electrode mixture layer contains a negative electrode active material and a binder, and is preferably provided on both sides of the negative electrode substrate except for the portion where the negative electrode lead 20 is connected, for example.
  • a negative electrode mixture slurry containing a negative electrode active material, a binder, a conductive agent, and the like is applied to the surface of a negative electrode core, the coating film is dried, and then compressed to turn the negative electrode mixture layer into a negative electrode. It can be produced by forming on both sides of the core.
  • the negative electrode 12 may be formed by mixing a negative electrode active material and copper powder, and then compressing the mixture into pellets.
  • the negative electrode active material contained in the negative electrode 12 has the general formula M 3 Me 2 X 7 (wherein M contains at least one of La and Ca, and Me is selected from the group consisting of Mn, Ni, Fe, and Co). and X contains at least one element selected from the group consisting of Ge, Si, Sn, and Al) (hereinafter referred to as M 3 Me 2 X (sometimes referred to as type 7 alloys).
  • M 3 Me 2 X 7 type alloy is, for example, La 3 Ni 2 Sn 7 .
  • the negative electrode 12 may contain a negative electrode active material other than the M 3 Me 2 X 7 type alloy.
  • the negative electrode active material other than the M 3 Me 2 X 7 type alloy is not particularly limited as long as it can reversibly absorb and release lithium ions.
  • Examples include graphite (natural graphite, artificial graphite), silicon (Si), A metal alloying with lithium such as tin (Sn), or an oxide containing a metal element such as Si or Sn can be used.
  • the dislocation density of the M 3 Me 2 X 7 type alloy is, for example, 1 ⁇ 10 15 cm ⁇ 2 or more. This can increase the gravimetric energy density of the M 3 Me 2 X 7 type alloy.
  • the dislocation density of the M 3 Me 2 X 7 type alloy is preferably 1 ⁇ 10 17 cm ⁇ 2 or more, more preferably 1 ⁇ 10 19 cm ⁇ 2 or more.
  • the dislocation density can be calculated, for example, by observing a cross section of the M 3 Me 2 X 7 type alloy using a TEM (Transmission Electron Microscope).
  • the dislocation density of a general M 3 Me 2 X 7 type alloy is about 1 ⁇ 10 6 to 1 ⁇ 10 8 , and the dislocation density of the M 3 Me 2 X 7 type alloy according to the present disclosure is generally The dislocation density is higher than that of the M 3 Me 2 X 7 type alloy.
  • the volume-based median diameter (D50) of the M 3 Me 2 X 7 type alloy may be, for example, 0.1 ⁇ m to 50 ⁇ m, or may be 1 ⁇ m to 10 ⁇ m.
  • the D50 of the M 3 Me 2 X 7 type alloy can be reduced, for example, by grinding with a ball mill, and can be adjusted by grinding conditions.
  • D50 means a particle size at which the cumulative frequency is 50% from the smaller particle size in the volume-based particle size distribution, and is also called median diameter.
  • the particle size distribution of the M 3 Me 2 X 7 type alloy can be measured using a laser diffraction particle size distribution analyzer (eg MT3000II manufactured by Microtrack Bell Co., Ltd.) using water as a dispersion medium.
  • the M 3 Me 2 X 7 type alloy according to the present disclosure can be produced, for example, as follows.
  • M metal, Me metal, and X metal are prepared as raw materials, and these raw materials are mixed in a predetermined ratio and then arc-melted to produce an M 3 Me 2 X 7 type alloy ingot.
  • the annealing conditions are, for example, an annealing temperature of 400° C. to 1000° C. and a holding time of 10 hours to 720 hours.
  • the lump of M 3 Me 2 X 7 type alloy after annealing is pulverized, for example, by a mortar or a planetary ball mill.
  • Ball mill processing conditions are, for example, a rotation speed of 100 rpm to 500 rpm and a processing time of 1 hour to 720 hours.
  • the ball-milled M 3 Me 2 X 7 type alloy is classified, for example, with a mesh to remove coarse particles.
  • the M 3 Me 2 X 7 type alloy produced by the above production method has a dislocation density of 1 ⁇ 10 15 cm ⁇ 2 or more. It is believed that the pulverization forms defects, voids, etc. in the crystal structure of the M 3 Me 2 X 7 type alloy and increases the dislocation density of the M 3 Me 2 X 7 type alloy.
  • fluorine resin, PAN, polyimide resin, acrylic resin, polyolefin resin, or the like can be used as the binder contained in the negative electrode mixture layer.
  • fluorine resin, PAN, polyimide resin, acrylic resin, polyolefin resin, or the like can be used as the binder contained in the negative electrode mixture layer.
  • CMC styrene-butadiene rubber
  • PAA polyacrylic acid
  • the negative electrode mixture layer may contain a conductive agent.
  • the conductive agent can make the conductive paths uniform.
  • Carbon black (CB), acetylene black (AB), ketjen black, carbon nanotubes (CNT), graphene, graphite, and other carbon-based particles can be exemplified as the conductive agent contained in the negative electrode mixture layer. These may be used alone or in combination of two or more.
  • the conductive agent contains CNTs.
  • the CNTs may be single-walled carbon nanotubes (SWCNTs) or multi-walled carbon nanotubes (MWCNTs). Since SWCNTs can form a conductive path in the negative electrode mixture layer in a smaller amount than MWCNTs, the CNTs preferably contain SWCNTs.
  • a porous sheet having ion permeability and insulation is used for the separator 13 .
  • porous sheets include microporous membranes, woven fabrics, and non-woven fabrics.
  • Suitable materials for the separator 13 include olefin resins such as polyethylene and polypropylene, and cellulose.
  • the separator 13 may have either a single layer structure or a laminated structure.
  • a heat-resistant layer containing a heat-resistant material may be formed on the surface of the separator 13 . Examples of heat-resistant materials include polyamide resins such as aliphatic polyamides and aromatic polyamides (aramids), and polyimide resins such as polyamideimides and polyimides.
  • Example 1 [Preparation of negative electrode active material] A metal piece of La, a wire of Ni, and a metal piece of Sn were used as raw materials. A metal piece made of yttrium and having a purity of 3N was arc-melted once, the gas was removed, and then the surface was polished with a metal brush. The Ni wire used was made by Kojundo Chemical Co., Ltd. and had a purity of 3N and a diameter of 3 mm. As the Sn metal piece, a shot-shaped one with a purity of 4N manufactured by Furuuchi Chemical Co., Ltd. was used.
  • the ball mill treatment was performed with a 5-minute pause every time it was performed for 5 minutes.
  • the powder after ball milling was classified with a mesh of 45 ⁇ m to remove coarse particles.
  • the volume-based median diameter (D50) of the produced negative electrode active material (powdered La 3 Ni 2 Sn 7 ) was 6.8 ⁇ m.
  • Li metallic lithium
  • Lithium ion batteries generally use a lithium transition metal oxide such as LiNiO 2 (generally containing a transition metal such as Co, Mn, Ni) as a positive electrode active material.
  • a lithium metal foil cut into ⁇ 17 mm was used as the counter electrode instead of the positive electrode active material generally used for the electrode. Such methods are often used to evaluate active materials.
  • a non-aqueous electrolyte was prepared by dissolving 1.0 mol/L of LiPF 6 as an electrolyte salt in a non-aqueous solvent in which ethylene carbonate (EC) and ethyl methyl carbonate (EMC) were mixed at a volume ratio of 1:3.
  • EC ethylene carbonate
  • EMC ethyl methyl carbonate
  • An electrode body was constructed by arranging the above negative electrode and a positive electrode made of a lithium metal foil so as to face each other with a separator interposed therebetween, and the electrode body was accommodated in a coin-shaped outer can. After injecting the non-aqueous electrolyte into the outer can, the outer can was sealed to obtain a coin-shaped test cell (non-aqueous electrolyte secondary battery).
  • Example 2 A test cell was produced in the same manner as in Example 1, except that the ball milling time using a planetary ball mill was lengthened in the production of the negative electrode active material.
  • Example 2 A test cell was produced in the same manner as in Example 1, except that the ball mill treatment using a planetary ball mill was not performed in the production of the negative electrode active material.
  • the battery capacity (charge capacity and discharge capacity) was evaluated by the following method. Table 1 shows the evaluation results. Table 1 also shows the dislocation density of the negative electrode active material and the charge/discharge efficiency.
  • the test cells of the example containing the negative electrode active material with a dislocation density of 1 ⁇ 10 15 cm ⁇ 2 or more were compared with the comparative example containing the negative electrode active material with a dislocation density of less than 1 ⁇ 10 15 cm ⁇ 2 .
  • the battery capacity was higher than that of the test cell of
  • the battery of Example had higher charge-discharge efficiency than the battery of Comparative Example 1.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Electrochemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Manufacturing & Machinery (AREA)
  • Materials Engineering (AREA)
  • Inorganic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Condensed Matter Physics & Semiconductors (AREA)
  • General Physics & Mathematics (AREA)
  • Battery Electrode And Active Subsutance (AREA)
PCT/JP2022/023408 2021-08-27 2022-06-10 負極活物質、及びリチウムイオン電池 Ceased WO2023026635A1 (ja)

Priority Applications (4)

Application Number Priority Date Filing Date Title
CN202280056719.XA CN117836979A (zh) 2021-08-27 2022-06-10 负极活性物质以及锂离子电池
US18/681,201 US20250140820A1 (en) 2021-08-27 2022-06-10 Negative electrode active substance and lithium-ion battery
EP22860929.3A EP4394934A4 (en) 2021-08-27 2022-06-10 NEGATIVE ELECTRODE ACTIVE SUBSTANCE AND LITHIUM-ION BATTERY
JP2023543705A JP7814016B2 (ja) 2021-08-27 2022-06-10 負極活物質、及びリチウムイオン電池

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2021-138760 2021-08-27
JP2021138760 2021-08-27

Publications (1)

Publication Number Publication Date
WO2023026635A1 true WO2023026635A1 (ja) 2023-03-02

Family

ID=85321743

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2022/023408 Ceased WO2023026635A1 (ja) 2021-08-27 2022-06-10 負極活物質、及びリチウムイオン電池

Country Status (5)

Country Link
US (1) US20250140820A1 (https=)
EP (1) EP4394934A4 (https=)
JP (1) JP7814016B2 (https=)
CN (1) CN117836979A (https=)
WO (1) WO2023026635A1 (https=)

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005310739A (ja) * 2004-03-23 2005-11-04 Toshiba Corp 非水電解質二次電池
JP2007073215A (ja) * 2005-09-05 2007-03-22 Toshiba Corp 非水電解質電池
JP2010218855A (ja) * 2009-03-17 2010-09-30 Sanyo Electric Co Ltd 非水電解質二次電池用負極及び非水電解質二次電池

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102729770B1 (ko) * 2016-12-21 2024-11-14 일진전기 주식회사 이차전지용 음극활물질 및 이를 포함한 이차전지
US20210184214A1 (en) * 2017-11-24 2021-06-17 Semiconductor Energy Laboratory Co., Ltd. Secondary battery and method for manufacturing secondary battery

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005310739A (ja) * 2004-03-23 2005-11-04 Toshiba Corp 非水電解質二次電池
JP2007073215A (ja) * 2005-09-05 2007-03-22 Toshiba Corp 非水電解質電池
JP2010218855A (ja) * 2009-03-17 2010-09-30 Sanyo Electric Co Ltd 非水電解質二次電池用負極及び非水電解質二次電池

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
See also references of EP4394934A4
SHINSUKE MATSUNO ET AL.: "La3Ni2Sn7 Ternary Intermetallic Phase for Lithium Insertion and Deinsertion", ELECTROCHEMICAL AND SOLID-STATE LETTERS, vol. 8, no. 4, 2005, pages A234 - A236, XP055850603, DOI: 10.1149/1.1870692

Also Published As

Publication number Publication date
CN117836979A (zh) 2024-04-05
US20250140820A1 (en) 2025-05-01
JPWO2023026635A1 (https=) 2023-03-02
EP4394934A1 (en) 2024-07-03
JP7814016B2 (ja) 2026-02-16
EP4394934A4 (en) 2025-01-29

Similar Documents

Publication Publication Date Title
CN114467199B (zh) 非水电解质二次电池
WO2021059706A1 (ja) リチウムイオン二次電池用負極及びリチウムイオン二次電池
US11031600B2 (en) Lithium ion secondary battery including aluminum silicate
JP7804945B2 (ja) 非水電解質二次電池
JPWO2018179934A1 (ja) 負極材料および非水電解質二次電池
CN112655103B (zh) 非水电解质二次电池用正极活性物质、非水电解质二次电池和非水电解质二次电池用正极活性物质的制造方法
CN112751019B (zh) 非水电解质二次电池用正极活性物质和非水电解质二次电池
WO2023120493A1 (ja) 二次電池用正極及び二次電池
WO2023203952A1 (ja) 正極活物質、及び非水電解質二次電池
JP7668469B2 (ja) 非水電解質二次電池用負極、及び非水電解質二次電池
JP7607266B2 (ja) 非水電解質二次電池用負極活物質、及び非水電解質二次電池
JP7814016B2 (ja) 負極活物質、及びリチウムイオン電池
WO2023032482A1 (ja) 非水電解質二次電池
WO2023026642A1 (ja) 負極活物質、及びリチウムイオン電池
WO2022138846A1 (ja) 非水電解質二次電池用正極活物質、及び非水電解質二次電池
WO2021200397A1 (ja) 二次電池用正極及び二次電池
WO2021049318A1 (ja) 非水電解質二次電池用正極活物質、及び非水電解質二次電池
CN114503307B (zh) 非水电解质二次电池用负极活性物质、和非水电解质二次电池
CN110402515A (zh) 非水电解质二次电池
CN117836980A (zh) 负极活性物质以及锂离子电池
WO2022163531A1 (ja) 非水電解質二次電池用活物質、及び非水電解質二次電池
WO2024161962A1 (ja) 非水電解質二次電池用正極および非水電解質二次電池
WO2023145443A1 (ja) リチウムイオン電池
WO2023189507A1 (ja) 非水電解質二次電池用正極活物質および非水電解質二次電池
WO2024062848A1 (ja) 二次電池用正極活物質および二次電池

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22860929

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 18681201

Country of ref document: US

WWE Wipo information: entry into national phase

Ref document number: 2023543705

Country of ref document: JP

WWE Wipo information: entry into national phase

Ref document number: 202280056719.X

Country of ref document: CN

WWE Wipo information: entry into national phase

Ref document number: 2022860929

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2022860929

Country of ref document: EP

Effective date: 20240327

WWP Wipo information: published in national office

Ref document number: 18681201

Country of ref document: US