WO2022255177A1 - 仕上げ化粧料組成物 - Google Patents

仕上げ化粧料組成物 Download PDF

Info

Publication number
WO2022255177A1
WO2022255177A1 PCT/JP2022/021325 JP2022021325W WO2022255177A1 WO 2022255177 A1 WO2022255177 A1 WO 2022255177A1 JP 2022021325 W JP2022021325 W JP 2022021325W WO 2022255177 A1 WO2022255177 A1 WO 2022255177A1
Authority
WO
WIPO (PCT)
Prior art keywords
oil
composition according
composition
coating agent
sio
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2022/021325
Other languages
English (en)
French (fr)
Inventor
紗希 鎌田
俊 久保田
ターシャ 小畑
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shiseido Co Ltd
Original Assignee
Shiseido Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shiseido Co Ltd filed Critical Shiseido Co Ltd
Priority to CN202280032811.2A priority Critical patent/CN117279617A/zh
Priority to JP2023525750A priority patent/JP7866999B2/ja
Publication of WO2022255177A1 publication Critical patent/WO2022255177A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

［課題］化粧崩れを抑制できる仕上げ化粧料組成物を提供する。 ［解決手段］油分と、特定の構造を有するポリマーである油溶性被膜剤と、水とを含んでなる仕上げ化粧料組成物を用いる。

Description

仕上げ化粧料組成物
　本発明は、仕上げ化粧料組成物、および仕上げ化粧料組成物がディスペンサー型容器に充填されてなる化粧料に関する。
　化粧崩れを防いで、ファンデーション等のメイクアップ化粧料の化粧もちを高めるために、化粧を施した顔の上から、塗布して使用する仕上げ化粧料が開発されている（例えば、特許文献１）。この仕上げ化粧料は、皮脂を吸着したり、肌を乾燥から守ったり、花粉、ほこり等の外的要因から肌を守ったり、衣服等に化粧を移りにくくするような機能を使用者に訴求している。さらに、新型コロナウイルスの感染予防により、マスクを装着することが日常となる中、マスクにファンデーションが付着しにくいことを使用者は強く求めている。
　肌に直接適用される下地化粧料や一般的なメーキャップ化粧料に用いられる被膜形成剤として、有機高分子やシリコーン系樹脂等が提案されている（例えば特許文献２）。
特開２０２０－０２６４０１号公報 特開２０２０－０２９４５４号公報
　本発明者らは、驚くべきことに、油分と、特定の構造を有するポリマーである油溶性被膜剤と、水とを含んでなる仕上げ化粧料を化粧後に塗布することにより、化粧崩れを抑制できることを見いだした。
　本発明は、このような知見に基づくものであり、油分と、特定の構造を有するポリマーである油溶性被膜剤と、水とを含んでなる化粧料組成物が開示される。
　本発明によれば、以下の発明が提供される。
［１］（Ａ）油分、
（Ｂ）レジン構造とリニア構造とを含んでなる油溶性被膜剤であって、
　前記レジン構造が、ＳｉＯ４／２で表される単位またはＲ１ＳｉＯ３／２（Ｒ１はＣ１－６アルキル基またはＣ１－６アルコキシ基である）で表される単位を含んでなり、
　前記リニア構造が、Ｒ２ＳｉＯ２／２（Ｒ２はＣ１－６アルキル基またはＣ１－６アルコキシ基である）で表される単位を含んでなり、
　前記レジン構造と前記リニア構造がＳｉ－Ｏ－Ｓｉ結合によって連結されているポリマーである油溶性被膜剤、および
（Ｃ）水
を含んでなる、仕上げ化粧料組成物。
［２］前記レジン構造がＳｉＯ４／２で表される単位および（Ｒ３）３ＳｉＯ１／２（Ｒ３はＣ１－６アルキル基またはＣ１－６アルコキシ基である）で表される単位を含んでなる、［１］に記載の組成物。
［３］前記ポリマーがヒドロキシ基を有する、［１］または［２］に記載の組成物。
［４］前記油溶性被膜剤が、シリコーンレジンガムである、［１］～［３］のいずれかに記載の組成物。
［５］前記油溶性被膜剤が、（トリメチルシロキシケイ酸／ジメチコノール）クロスポリマーである、［１］～［４］のいずれかに記載の組成物。
［６］前記油溶性被膜剤の配合量が、組成物の総量に対して、０．０５～５質量％である、［１］～［５］のいずれかに記載の組成物。
［７］界面活性剤をさらに含んでなる、［１］～［６］のいずれかに記載の組成物。
［８］前記界面活性剤が、ベタイン型界面活性剤である、［７］に記載の組成物。
［９］静置時に相分離する、［１］～［８］のいずれかに記載の組成物。
［１０］［１］～［９］のいずれかに記載の組成物がディスペンサー型容器に充填されてなる化粧料。
［１１］前記組成物がミスト状に噴出される、［１０］に記載の化粧料。
［１２］使用前に振とうにより前記組成物を乳化させる、［１０］または［１１］に記載の化粧料。
　本発明による仕上げ化粧料は、化粧崩れを抑制できる。特に、ファンデーション等のメイクアップ化粧料のマスクへの付着を抑制できる。
発明の具体的説明
　本発明は、（Ａ）油分、（Ｂ）特定の構造を有する油溶性被膜剤、および（Ｃ）水を含んでなる、仕上げ化粧料組成物（以下、組成物と称することがある）に関するものである。
　ここで、本発明において、仕上げ化粧料組成物とは、化粧の上から適用して、化粧にフィクサー機能を付与するものを意味し、肌に直接適用される下地化粧料や一般的なメーキャップ化粧料とは異なるものである。
　具体的には、ファンデーション等のベースメイクや、アイシャドウ、チーク等のメイクアップを施した上に、仕上げ化粧料は適用される。本発明による好ましい形態において、本発明による仕上げ化粧料は、ファンデーションの上から適用される。これにより、マスク装着時にファンデーションのマスクへの付着を抑制することができる。
　本発明による組成物は、静置時に相分離する化粧料組成物であることが好ましい。静置時に２相以上であってよいが、好ましくは２相であり、典型的には静置時に上から油相、水相の順になる。相分離することにより、各相に見合った化粧料成分、特に有効成分を安定的に配合することができる。
　相分離された状態の組成物は、使用前に振とうすることにより、乳化させて用いることが好ましい。本発明の好ましい一形態において、振とうすることにより、分離されていた油相と水相が全体に均一に分散して全体が一相状態となり、その後静置することにより、再度分離する。
（Ａ）油分
　本発明による組成物は、（Ａ）油分（以下、（Ａ）成分と称することがある。（Ｂ）以降も同様である。）を含んでなる。（Ａ）成分としては、例えば、シリコーン油、炭化水素油、高級脂肪酸、高級アルコール、合成エステル油、液体油脂等が挙げられ、好ましくはシリコーン油または炭化水素油であり、より好ましくはシリコーン油である。
　シリコーン油としては、例えば、鎖状ポリシロキサン（例えば、ジメチルポリシロキサン、メチルフェニルポリシロキサン、ジフェニルポリシロキサン等）、環状ポリシロキサン（例えば、オクタメチルシクロテトラシロキサン、デカメチルシクロペンタシロキサン、ドデカメチルシクロヘキサシロキサン等）、３次元網目構造を形成しているシリコーン樹脂、シリコーンゴム、各種変性ポリシロキサン（アミノ変性ポリシロキサン、ポリエーテル変性ポリシロキサン、アルキル変性ポリシロキサン、フッ素変性ポリシロキサン等）、アクリルシリコーン類等が挙げられ、好ましくは鎖状ポリシロキサンである。
　炭化水素油としては、例えば、イソドデカン、イソヘキサデカン、イソパラフィン、流動パラフィン、オゾケライト、スクワラン、プリスタン、パラフィン、セレシン、スクワレン、ワセリン、マイクロクリスタリンワックス等が挙げられる。
　高級脂肪酸としては、例えば、ラウリン酸、ミリスチン酸、パルミチン酸、ステアリン酸、ベヘン酸、オレイン酸、ウンデシレン酸、トール酸、イソステアリン酸、リノール酸、リノレイン酸、エイコサペンタエン酸（ＥＰＡ）、ドコサヘキサエン酸（ＤＨＡ）等が挙げられる。
　高級アルコールとしては、例えば、直鎖アルコール（例えば、ラウリルアルコール、セチルアルコール、ステアリルアルコール、ベヘニルアルコール、ミリスチルアルコール、オレイルアルコール、セトステアリルアルコール等）、分枝鎖アルコール（例えば、モノステアリルグリセリンエーテル（バチルアルコール）－２－デシルテトラデシノール、ラノリンアルコール、コレステロール、フィトステロール、ヘキシルドデカノール、イソステアリルアルコール、オクチルドデカノール等）等が挙げられる。
　合成エステル油としては、例えば、オクタン酸オクチル、ノナン酸ノニル、オクタン酸セチル、ミリスチン酸イソプロピル、ミリスチン酸オクチルドデシル、パルミチン酸イソプロピル、パルミチン酸エチルヘキシル、ステアリン酸ブチル、ラウリン酸ヘキシル、ミリスチン酸ミリスチル、オレイン酸デシル、ジメチルオクタン酸ヘキシルデシル、乳酸セチル、乳酸ミリスチル、酢酸ラノリン、ステアリン酸イソセチル、イソステアリン酸イソセチル、１２－ヒドロキシステアリン酸コレステリル、ジ－２－エチルヘキサン酸エチレングリコール、ジペンタエリスリトール脂肪酸エステル、モノイソステアリン酸Ｎ－アルキルグリコール、ジカプリン酸ネオペンチルグリコール、ピバリン酸トリプロピレングリコール、リンゴ酸ジイソステアリル、ジ－２－ヘプチルウンデカン酸グリセリン、ジイソステアリン酸グリセリン、トリ－２－エチルヘキサン酸トリメチロールプロパン、トリイソステアリン酸トリメチロールプロパン、テトラ－２－エチルヘキサン酸ペンタエリスリトール、トリ－２－エチルヘキサン酸グリセリン、トリオクタン酸グリセリン、トリイソパルミチン酸グリセリン、トリイソステアリン酸トリメチロールプロパン、セチル２－エチルヘキサノエート－２－エチルヘキシルパルミテート、トリミリスチン酸グリセリン、トリ－２－ヘプチルウンデカン酸グリセライド、ヒマシ油脂肪酸メチルエステル、オレイン酸オレイル、アセトグリセライド、パルミチン酸２－ヘプチルウンデシル、アジピン酸ジイソブチル、Ｎ－ラウロイル－Ｌ－グルタミン酸－２－オクチルドデシルエステル、アジピン酸ジ－２－ヘプチルウンデシル、エチルラウレート、セバシン酸ジ－２－エチルヘキシル、ミリスチン酸２－ヘキシルデシル、パルミチン酸２－ヘキシルデシル、アジピン酸２－ヘキシルデシル、セバシン酸ジイソプロピル、コハク酸２－エチルヘキシル、クエン酸トリエチル、エチルヘキサン酸セチル等が挙げられる。
　液体油脂としては、例えば、アボガド油、ツバキ油、マカデミアナッツ油、トウモロコシ油、オリーブ油、ナタネ油、ゴマ油、パーシック油、小麦胚芽油、サザンカ油、ヒマシ油、アマニ油、サフラワー油、綿実油、エノ油、大豆油、落花生油、茶実油、カヤ油、コメヌカ油、シナギリ油、日本キリ油、ホホバ油、胚芽油、トリグリセリン等が挙げられる。固体油脂としては、例えば、カカオ脂、ヤシ油、硬化ヤシ油、パーム油、パーム核油、モクロウ核油、硬化油、モクロウ、硬化ヒマシ油等が挙げられる。
　（Ａ）成分の配合量は、本発明による組成物の総量に対して、好ましくは１～２０質量％であり、より好ましくは３～１５質量％である。この範囲とすることで、相分離を良好なものとすることができるとともに、肌に適用した場合のべたつきや、てかりを抑制することができる。
（Ｂ）油溶性被膜剤
　本発明による組成物は、レジン構造とリニア構造とを含んでなる油溶性被膜剤であって、
　レジン構造が、ＳｉＯ４／２で表される単位またはＲ１ＳｉＯ３／２（Ｒ１はＣ１－６アルキル基またはＣ１－６アルコキシ基である）で表される単位を含んでなり、リニア構造が、Ｒ２ＳｉＯ２／２（Ｒ２はＣ１－６アルキル基またはＣ１－６アルコキシ基である）で表される単位を含んでなり、
　レジン構造とリニア構造がＳｉ－Ｏ－Ｓｉ結合によって連結されているポリマーである油溶性被膜剤（以下、油溶性被膜剤、ポリマー、または（Ｂ）成分と称することがある）を含んでなる。
　本発明に用いられる油溶性被膜剤は、レジン構造とリニア構造の両方の構造を有することが特徴の１つである。一般に、ポリマーがレジン構造のみからなると、その構造に由来する造膜性および粘着性とに優れるが、柔軟性や追従性が不足することがある。ところがポリマーにリニア構造を組み合わせると、ポリマーが柔軟性および追従性を兼ね備えるようになる。このような特徴を有する油溶性被膜剤を含む化粧料を適用すると、柔軟で粘着性のある被膜を形成することができる。これにより、化粧後にこのような被膜が形成されると、マスクや衣服等との擦れや、皮脂や汗等に対して、化粧を保護する層として機能することができるため、化粧崩れを効果的に抑制できると考えられる。
　レジン構造は、ＳｉＯ４／２で表される単位（以下、Ｑ単位と称することがある）またはＲ１ＳｉＯ３／２（Ｒ１はＣ１－６アルキル基またはＣ１－６アルコキシ基であり、好ましくはメチル基、エチル基、プロピル基、メトキシ基、エトキシ基またはプロポキシ基であり、より好ましくはメチル基である）（以下、Ｔ単位と称することがある）で表される単位を含んでなり、好ましくはＱ単位を含んでなる。
　レジン構造は、上記の単位に加えて、（Ｒ３）３ＳｉＯ１／２（Ｒ３はＣ１－６アルキル基またはＣ１－６アルコキシ基であり、好ましくはメチル基、エチル基、プロピル基、メトキシ基、エトキシ基またはプロポキシ基であり、より好ましくはメチル基である）で表される単位（以下、Ｍ単位と称することがある）をさらに含むこともできる。
　好ましい一形態において、レジン構造は、Ｍ単位およびＱ単位を含んでなり、より好ましくはＭ単位およびＱ単位からなる構造（ＭＱ構造）である。
　リニア構造は、Ｒ２ＳｉＯ２／２（Ｒ２はＣ１－６アルキル基またはＣ１－６アルコキシ基であり、好ましくはメチル基、エチル基、プロピル基、メトキシ基、エトキシ基またはプロポキシ基であり、より好ましくはメチル基である）で表される単位（以下、Ｄ単位と称することがある）を含んでなる。リニア構造は、Ｄ単位が５単位以上鎖状に連結していることが好ましく、鎖状に連続して結合している数は、より好ましくは５～１０００であり、よりさらに好ましくは１０～３００である。言い換えれば、Ｄ単位が複数、好ましくは５以上、連結した部分がリニア構造であり、それ以外のＱ単位、Ｔ単位、Ｄ単位およびＭ単位が混在している部分がレジン構造である。
　リニア構造は、分子鎖の末端にヒドロキシ基（シラノール基）を有することが好ましい。
　レジン構造とリニア構造の連結部は、Ｓｉ－Ｏ－Ｓｉ結合によって連結されており、このＳｉ－Ｏ－Ｓｉ結合により連結された構造は、分子内に複数あってもよい。好適な一形態において、レジン構造に結合するＳｉ原子がＴ単位である。
　ポリマー１分子中に含まれるレジン構造とリニア構造の質量比は、好ましくは５０：５０～９５：５であり、より好ましくは６０：４０～９０：１０である。
　（Ｂ）成分は、好ましくはシリコーン系被膜剤であり、より好ましくはシリコーンレジンガムである。具体的には、（トリメチルシロキシケイ酸／ジメチコノール）クロスポリマーが挙げられる。
　（Ｂ）成分の質量平均分子量は、被膜剤としての機能および溶解性の観点から、好ましくは５，０００～１００，０００であり、より好ましくは１０，０００～５０，０００である。ここで、質量平均分子量は、ゲル浸透クロマトグラフィーによるポリスチレン換算の値である。
　（Ｂ）成分は、１種または２種以上を配合することができる。（Ｂ）成分の配合量は、本発明による組成物の総量に対して、好ましくは０．０５～５質量％であり、より好ましくは１～５質量％である。
（Ｃ）水
　本発明による組成物は、（Ｃ）水を含んでなる。水としては、化粧品、医薬部外品等に使用される水を使用することができ、例えば、精製水、イオン交換水、水道水等を使用することができる。
　水の配合量は、本発明による組成物の総量に対して、好ましくは４０～９５質量％であり、より好ましくは６０～９５質量％である。
　本発明による組成物は、界面活性剤をさらに含むことが好ましい。界面活性剤としては、アニオン性界面活性剤、カチオン性界面活性剤、両性界面活性剤、非イオン性界面活性剤が挙げられ、好ましくは非イオン界面活性剤または両性界面活性剤であり、より好ましくは両性界面活性剤である。
　両性界面活性剤としては、例えば、イミダゾリン系両性界面活性剤（例えば、２－ウンデシル－Ｎ，Ｎ，Ｎ－（ヒドロキシエチルカルボキシメチル）－２－イミダゾリンナトリウム、２－ココイル－２－イミダゾリニウムヒドロキサイド－１－カルボキシエチロキシ２ナトリウム塩等）；ベタイン型界面活性剤（例えば、ラウリルベタイン、コカミドプロピルベタイン、アミノベタイン、スルホベタイン等）等が挙げられ、好ましくは、ベタイン型界面活性剤である。
　界面活性剤は、１種または２種以上を配合することができる。
　界面活性剤の配合量は、本発明による組成物の総量に対して、好ましくは０．０１～０．２質量％であり、より好ましくは０．０２～０．１質量％である。
　本発明による組成物は、塩化ナトリウムを含むことができる。塩化ナトリウムを含むことで、相分離する化粧料組成物である場合に、相界面をクリアにすることができるとともに、分離速度を調整することができる。
　塩化ナトリウムの配合量は、本発明による組成物の総量に対して、好ましくは０．０１～０．５質量％であり、より好ましくは０．０５～０．３質量％である。この範囲とすることで、塩化ナトリウムによるべたつきを抑制するとともに、界面をクリアにし、分離速度を早くすることができる。
　本発明による組成物は、低級アルコールを含むことができる。低級アルコールを配合することにより、組成物の比重を軽くすることができる。また、さっぱりとした使用感を付与することができる。低級アルコールとしては、例えば、エタノール、プロパノール、イソプロパノール、イソブチルアルコール、ｔ－ブチルアルコール等が挙げられる。
　低級アルコールの配合量は、本発明による組成物の総量に対して、好ましくは１～４５質量％であり、より好ましくは５～３０質量％である。
　上記以外の任意成分として、化粧料に通常用いられる成分、例えば、保湿剤、増粘剤、殺菌剤、防腐剤、ｐＨ調整剤、紫外線吸収剤、酸化防止剤、有機および無機粉体、香料、顔料、染料、美白剤、ビタミン類、各種アミノ酸等が挙げられる。
　本発明による組成物は、常法に従って製造することができる。
　本発明による化粧料は、本発明による組成物がディスペンサー型容器に充填されてなる化粧料である。本発明による組成物が、この容器から、本発明による組成物がミスト状に噴出されることが好ましい。本発明による組成物がミスト状に噴出されることで、肌に直接触れることなく、かつ均一に塗布することができるため、化粧を崩すことなく、化粧の上に、薄く、均一で、よれにくい膜を形成することができる。
　以下の例に基づいて本発明を具体的に説明するが、本発明はこれらの例に限定されるものではない。含有量は特記しない限り、総量に対する質量％で示す。
［実施例１～６および比較例１～３］
　表１に示される配合で、実施例１～６および比較例１～３の組成物を調製した。調製された組成物を静置した状態で外観を観察すると、全て、２相に分離していた。
Figure JPOXMLDOC01-appb-T000001
 表中、
（トリメチルシロキシケイ酸／ジメチコノール）クロスポリマーは、「ＤＯＷＳＩＬ　ＦＣ－５００４　ＤＭ（１．５ｃＳｔ　Ｓｉｌｉｃｏｎｅ　Ｒｅｓｉｎ　Ｇｕｍ）」（ダウ・東レ株式会社）を用いた。なお、「ＤＯＷＳＩＬ　ＦＣ－５００４　ＤＭ（１．５ｃＳｔ　Ｓｉｌｉｃｏｎｅ　Ｒｅｓｉｎ　Ｇｕｍ）」は、低粘度ジメチコン液に溶解された（トリメチルシロキシケイ酸／ジメチコノール）クロスポリマーを含む製品であるが、表に記載している質量％は（トリメチルシロキシケイ酸／ジメチコノール）クロスポリマーのみを指し、商品に含まれる溶媒等は含まれない。
［マスクへのメイクの付きにくさ評価］
　上記で調製した組成物をディスペンサー型の噴霧容器に収容した。
　人工皮革上にリキッドファンデーションを一定量塗布し、３０分間乾燥させた。その後、人工皮革から１５ｃｍ離れた距離から、噴霧容器を３回噴霧して組成物を塗布した。その後、イオン交換水を１５ｃｍ離れた距離から噴霧容器にて３回噴霧し、そしてオレイン酸（０．５ｍｇ／ｃｍ２）を塗布し、３０分間乾燥させ、不織布を取り付けたタッピング試験機を用いて、１０回のタッピングを行った。不織布への色移りを目視により観察し、以下の基準により評価した。得られた結果は表１のとおりであった。
Ａ：不織布への色移りが確認されなかった。
Ｂ：不織布への色移りがわずかに確認された。
Ｃ：不織布への色移りがＢよりも多く確認された。
　実施例１～６の組成物をディスペンサー型の噴霧容器に収容し、噴霧によりメイク後の顔に塗布した。８時間経過後確認したところ、化粧崩れやよれが認められず、またメイクも薄れることがなかった。

Claims (12)

  1. （Ａ）油分、
    （Ｂ）レジン構造とリニア構造とを含んでなる油溶性被膜剤であって、
    　前記レジン構造が、ＳｉＯ４／２で表される単位またはＲ１ＳｉＯ３／２（Ｒ１はＣ１－６アルキル基またはＣ１－６アルコキシ基である）で表される単位を含んでなり、
    　前記リニア構造が、Ｒ２ＳｉＯ２／２（Ｒ２はＣ１－６アルキル基またはＣ１－６アルコキシ基である）で表される単位を含んでなり、
    　前記レジン構造と前記リニア構造がＳｉ－Ｏ－Ｓｉ結合によって連結されているポリマーである油溶性被膜剤、および
    （Ｃ）水
    を含んでなる、仕上げ化粧料組成物。
  2. 　前記レジン構造がＳｉＯ４／２で表される単位および（Ｒ３）３ＳｉＯ１／２（Ｒ３はＣ１－６アルキル基またはＣ１－６アルコキシ基である）で表される単位を含んでなる、請求項１に記載の組成物。
  3. 　前記ポリマーがヒドロキシ基を有する、請求項１または２に記載の組成物。
  4. 　前記油溶性被膜剤が、シリコーンレジンガムである、請求項１または２に記載の組成物。
  5. 　前記油溶性被膜剤が、（トリメチルシロキシケイ酸／ジメチコノール）クロスポリマーである、請求項１または２に記載の組成物。
  6. 　前記油溶性被膜剤の配合量が、組成物の総量に対して、０．０５～５質量％である、請求項１または２に記載の組成物。
  7. 　界面活性剤をさらに含んでなる、請求項１または２に記載の組成物。
  8. 　前記界面活性剤が、ベタイン型界面活性剤である、請求項７に記載の組成物。
  9. 　静置時に相分離する、請求項１または２に記載の組成物。
  10. 　請求項１または２に記載の組成物がディスペンサー型容器に充填されてなる化粧料。
  11. 　前記組成物がミスト状に噴出される、請求項１０に記載の化粧料。
  12. 　使用前に振とうにより前記組成物を乳化させる、請求項１０または１１に記載の化粧料。
PCT/JP2022/021325 2021-06-03 2022-05-25 仕上げ化粧料組成物 Ceased WO2022255177A1 (ja)