WO2022239747A1 - Fibre de verre et son procédé de production - Google Patents
Fibre de verre et son procédé de production Download PDFInfo
- Publication number
- WO2022239747A1 WO2022239747A1 PCT/JP2022/019716 JP2022019716W WO2022239747A1 WO 2022239747 A1 WO2022239747 A1 WO 2022239747A1 JP 2022019716 W JP2022019716 W JP 2022019716W WO 2022239747 A1 WO2022239747 A1 WO 2022239747A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- less
- glass
- glass fiber
- loss tangent
- dielectric loss
- Prior art date
Abstract
L'invention concerne : une fibre de verre avec laquelle à la fois une faible température de filage et une faible constante diélectrique et une tangente de perte diélectrique sont obtenues ; et son procédé de production. Une fibre de verre selon la présente invention est caractérisée en ce qu'elle contient 22,5 à 45 % en masse de SiO2, 0,1 à 30 % en masse d'Al2O3, 0 à 45 % en masse de B2O3, 0 à 60 % en masse de P2O5, 0,001 à 3 % en masse de Fe2O3 et 0 à 9 % en masse de Li2O+Na2O+K2O+MgO+CaO+BaO+SrO.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2023521018A JPWO2022239747A1 (fr) | 2021-05-13 | 2022-05-09 |
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2021-081593 | 2021-05-13 | ||
JP2021081593 | 2021-05-13 | ||
JP2021207991 | 2021-12-22 | ||
JP2021-207991 | 2021-12-22 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2022239747A1 true WO2022239747A1 (fr) | 2022-11-17 |
Family
ID=84029603
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2022/019716 WO2022239747A1 (fr) | 2021-05-13 | 2022-05-09 | Fibre de verre et son procédé de production |
Country Status (3)
Country | Link |
---|---|
JP (1) | JPWO2022239747A1 (fr) |
TW (1) | TW202311192A (fr) |
WO (1) | WO2022239747A1 (fr) |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS6296342A (ja) * | 1985-05-31 | 1987-05-02 | Hoya Corp | 燐酸系熱線吸収硬質ガラス |
JPH04228455A (ja) * | 1990-06-01 | 1992-08-18 | Isover Saint Gobain | 生理媒体で分解する鉱物繊維およびそれを含有する断熱、遮音用製品 |
JP2017508705A (ja) * | 2014-02-19 | 2017-03-30 | コーニング インコーポレイテッド | 抗菌性ガラス組成物、それを含むガラス、およびポリマー物品 |
WO2020256143A1 (fr) * | 2019-06-21 | 2020-12-24 | 日本板硝子株式会社 | Charge de verre ainsi que procédé de fabrication de celle-ci, et composition de résine contenant cette charge de verre |
WO2020256142A1 (fr) * | 2019-06-21 | 2020-12-24 | 日本板硝子株式会社 | Composition de verre, fibres de verre ainsi que procédé de fabrication de celles-ci, et tissu de verre |
-
2022
- 2022-04-29 TW TW111116331A patent/TW202311192A/zh unknown
- 2022-05-09 WO PCT/JP2022/019716 patent/WO2022239747A1/fr active Application Filing
- 2022-05-09 JP JP2023521018A patent/JPWO2022239747A1/ja active Pending
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS6296342A (ja) * | 1985-05-31 | 1987-05-02 | Hoya Corp | 燐酸系熱線吸収硬質ガラス |
JPH04228455A (ja) * | 1990-06-01 | 1992-08-18 | Isover Saint Gobain | 生理媒体で分解する鉱物繊維およびそれを含有する断熱、遮音用製品 |
JP2017508705A (ja) * | 2014-02-19 | 2017-03-30 | コーニング インコーポレイテッド | 抗菌性ガラス組成物、それを含むガラス、およびポリマー物品 |
WO2020256143A1 (fr) * | 2019-06-21 | 2020-12-24 | 日本板硝子株式会社 | Charge de verre ainsi que procédé de fabrication de celle-ci, et composition de résine contenant cette charge de verre |
WO2020256142A1 (fr) * | 2019-06-21 | 2020-12-24 | 日本板硝子株式会社 | Composition de verre, fibres de verre ainsi que procédé de fabrication de celles-ci, et tissu de verre |
Also Published As
Publication number | Publication date |
---|---|
TW202311192A (zh) | 2023-03-16 |
JPWO2022239747A1 (fr) | 2022-11-17 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JP7410450B2 (ja) | ガラス繊維及びその製造方法 | |
TWI406831B (zh) | 供電子應用之低介電玻璃及纖維玻璃 | |
US11479498B2 (en) | Glass composition and glass fiber having the same | |
CN102718406B (zh) | 一种拉丝温度低的低介电常数玻璃纤维 | |
CN110028249A (zh) | 一种低介电玻璃纤维组分及其制造方法 | |
JP2022522986A (ja) | 電子デバイス用の低誘電損失ガラス | |
JP2019112246A (ja) | ガラス繊維及びその製造方法 | |
WO2022239747A1 (fr) | Fibre de verre et son procédé de production | |
CN107298531A (zh) | 低介电常数玻璃纤维及其制备方法 | |
CN104761149B (zh) | 低拉丝温度低介电常数的玻璃纤维 | |
JP2023051778A (ja) | ガラス組成物、ガラス、ガラス繊維及びそのガラス繊維を含む製品 | |
JPH092839A (ja) | 低誘電正接ガラス繊維 | |
JP7348602B1 (ja) | ガラス繊維 | |
WO2023176689A1 (fr) | Fibres de verre | |
WO2023176688A1 (fr) | Fibres de verre | |
JP2023138225A (ja) | ガラス繊維 | |
WO2024101361A1 (fr) | Substrat en verre pour le renforcement d'un tableau de connexions | |
JP2024070324A (ja) | 配線基板補強用ガラス基板 | |
CN117700113A (zh) | 一种高频高速基板用玻璃纤维组合物及其应用 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 22807448 Country of ref document: EP Kind code of ref document: A1 |
|
ENP | Entry into the national phase |
Ref document number: 2023521018 Country of ref document: JP Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 22807448 Country of ref document: EP Kind code of ref document: A1 |