WO2022185802A1 - Plaque de polarisation circulaire et dispositif d'affichage d'image l'utilisant - Google Patents
Plaque de polarisation circulaire et dispositif d'affichage d'image l'utilisant Download PDFInfo
- Publication number
- WO2022185802A1 WO2022185802A1 PCT/JP2022/003086 JP2022003086W WO2022185802A1 WO 2022185802 A1 WO2022185802 A1 WO 2022185802A1 JP 2022003086 W JP2022003086 W JP 2022003086W WO 2022185802 A1 WO2022185802 A1 WO 2022185802A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polarizing plate
- liquid crystal
- layer
- resin
- circularly polarizing
- Prior art date
Abstract
L'invention concerne une plaque de polarisation circulaire mince dans laquelle des changements de différence de phase dans des environnements à haute température sont supprimés, et le phénomène selon lequel la teinte de réflexion apparaît rouge est supprimé. Cette plaque de polarisation circulaire comprend une plaque de polarisation, une première couche fixe d'orientation de cristaux liquides, une seconde couche fixe d'orientation de cristaux liquides, et une couche de protection, dans cet ordre à partir du côté de visualisation, la perméabilité à l'humidité de la couche de protection étant de 920 (g/m2・ 24 h) ou moins.
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN202280013415.5A CN116848443A (zh) | 2021-03-04 | 2022-01-27 | 圆偏振片及使用了其的图像显示装置 |
KR1020237026552A KR20230151987A (ko) | 2021-03-04 | 2022-01-27 | 원편광판 및 그를 이용한 화상 표시 장치 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2021034318A JP2022134862A (ja) | 2021-03-04 | 2021-03-04 | 円偏光板およびそれを用いた画像表示装置 |
JP2021-034318 | 2021-03-04 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2022185802A1 true WO2022185802A1 (fr) | 2022-09-09 |
Family
ID=83154987
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2022/003086 WO2022185802A1 (fr) | 2021-03-04 | 2022-01-27 | Plaque de polarisation circulaire et dispositif d'affichage d'image l'utilisant |
Country Status (5)
Country | Link |
---|---|
JP (1) | JP2022134862A (fr) |
KR (1) | KR20230151987A (fr) |
CN (1) | CN116848443A (fr) |
TW (1) | TW202246818A (fr) |
WO (1) | WO2022185802A1 (fr) |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2008163107A (ja) * | 2006-12-27 | 2008-07-17 | Mitsubishi Gas Chem Co Inc | 光学部材 |
JP2017102443A (ja) * | 2015-11-20 | 2017-06-08 | 日東電工株式会社 | 光学積層体および該光学積層体を用いた有機エレクトロルミネセンス表示装置 |
JP2019120951A (ja) * | 2017-12-28 | 2019-07-22 | 住友化学株式会社 | 偏光板 |
WO2020174787A1 (fr) * | 2019-02-28 | 2020-09-03 | 日東電工株式会社 | Composition de résine pour protéger un polariseur et plaque de polarisation comprenant une couche de protection formée à partir de ladite composition |
JP2020201507A (ja) * | 2020-08-25 | 2020-12-17 | 日東電工株式会社 | 光学補償層付偏光板およびそれを用いた有機elパネル |
Family Cites Families (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP1045261B1 (fr) | 1998-10-30 | 2005-02-02 | Teijin Limited | Film a differences de phase et dispositif optique dans lequel il est utilise |
-
2021
- 2021-03-04 JP JP2021034318A patent/JP2022134862A/ja active Pending
-
2022
- 2022-01-27 KR KR1020237026552A patent/KR20230151987A/ko unknown
- 2022-01-27 WO PCT/JP2022/003086 patent/WO2022185802A1/fr active Application Filing
- 2022-01-27 CN CN202280013415.5A patent/CN116848443A/zh active Pending
- 2022-02-11 TW TW111105067A patent/TW202246818A/zh unknown
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2008163107A (ja) * | 2006-12-27 | 2008-07-17 | Mitsubishi Gas Chem Co Inc | 光学部材 |
JP2017102443A (ja) * | 2015-11-20 | 2017-06-08 | 日東電工株式会社 | 光学積層体および該光学積層体を用いた有機エレクトロルミネセンス表示装置 |
JP2019120951A (ja) * | 2017-12-28 | 2019-07-22 | 住友化学株式会社 | 偏光板 |
WO2020174787A1 (fr) * | 2019-02-28 | 2020-09-03 | 日東電工株式会社 | Composition de résine pour protéger un polariseur et plaque de polarisation comprenant une couche de protection formée à partir de ladite composition |
JP2020201507A (ja) * | 2020-08-25 | 2020-12-17 | 日東電工株式会社 | 光学補償層付偏光板およびそれを用いた有機elパネル |
Also Published As
Publication number | Publication date |
---|---|
KR20230151987A (ko) | 2023-11-02 |
CN116848443A (zh) | 2023-10-03 |
JP2022134862A (ja) | 2022-09-15 |
TW202246818A (zh) | 2022-12-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2017170019A1 (fr) | Ensemble de plaques de polarisation, et afficheur à cristaux liquides en mode ips utilisant cet ensemble | |
JP2024007555A (ja) | 位相差層付偏光板およびそれを用いた画像表示装置 | |
JP2018060152A (ja) | Ipsモード用の偏光板のセット及びそれを用いたipsモード液晶表示装置 | |
JP7114664B2 (ja) | 位相差層付偏光板およびそれを用いた画像表示装置 | |
WO2022185802A1 (fr) | Plaque de polarisation circulaire et dispositif d'affichage d'image l'utilisant | |
JP7273769B2 (ja) | 偏光板および位相差層付偏光板ならびにこれらを用いた画像表示装置 | |
JP2018060150A (ja) | Ipsモード用の偏光板のセット及びそれを用いたipsモード液晶表示装置 | |
JP7258829B2 (ja) | 位相差層付偏光板およびそれを用いた画像表示装置 | |
JP7114665B2 (ja) | 位相差層付偏光板およびそれを用いた画像表示装置 | |
JP7046127B6 (ja) | 光学積層体および該光学積層体の位相差層付偏光板を含む画像表示装置 | |
WO2021149311A1 (fr) | Plaque de polarisation équipée d'une couche de retard et dispositif d'affichage d'image l'utilisant | |
JP7273768B2 (ja) | 偏光板および位相差層付偏光板ならびにこれらを用いた画像表示装置 | |
WO2022201907A1 (fr) | Plaque de polarisation avec couche de retard et son procédé de production, et dispositif d'affichage d'image utilisant ladite plaque de polarisation avec couche de retard | |
WO2021149312A1 (fr) | Plaque de polarisation équipée d'une couche de retard et dispositif d'affichage d'image l'utilisant | |
JP7411520B2 (ja) | 偏光板、位相差層付偏光板および有機エレクトロルミネセンス表示装置 | |
JP2018060149A (ja) | 偏光板のセット及びそれを用いたipsモード液晶表示装置 | |
WO2021149314A1 (fr) | Plaque de polarisation, plaque de polarisation avec couche de retard et dispositif d'affichage d'image utilisant lesdites plaques | |
WO2021149313A1 (fr) | Plaque de polarisation et plaque de polarisation équipée d'une couche de différence de phase, et dispositif d'affichage d'image l'utilisant | |
JP6699514B2 (ja) | Ipsモード用の偏光板のセット及びそれを用いたipsモード液晶表示装置 | |
JP2018054887A (ja) | 偏光板のセット及びそれを用いたipsモード液晶表示装置 | |
JP6699513B2 (ja) | 偏光板のセット及びそれを用いたipsモード液晶表示装置 | |
JP2022141116A (ja) | 位相差層付偏光板 | |
JP2023075790A (ja) | 位相差層付偏光板およびそれを用いた画像表示装置 | |
JP2023075748A (ja) | 位相差層付偏光板およびそれを用いた画像表示装置 | |
JP2018060147A (ja) | 偏光板のセット及びそれを用いたipsモード液晶表示装置 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 22762861 Country of ref document: EP Kind code of ref document: A1 |
|
WWE | Wipo information: entry into national phase |
Ref document number: 202280013415.5 Country of ref document: CN |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 22762861 Country of ref document: EP Kind code of ref document: A1 |