WO2022158335A1 - 重合体、組成物、重合体の製造方法、膜形成用組成物、レジスト組成物、レジストパターン形成方法、感放射線性組成物、リソグラフィー用下層膜形成用組成物、リソグラフィー用下層膜の製造方法、回路パターン形成方法、光学部材形成用組成物 - Google Patents

重合体、組成物、重合体の製造方法、膜形成用組成物、レジスト組成物、レジストパターン形成方法、感放射線性組成物、リソグラフィー用下層膜形成用組成物、リソグラフィー用下層膜の製造方法、回路パターン形成方法、光学部材形成用組成物 Download PDF

Info

Publication number
WO2022158335A1
WO2022158335A1 PCT/JP2022/000590 JP2022000590W WO2022158335A1 WO 2022158335 A1 WO2022158335 A1 WO 2022158335A1 JP 2022000590 W JP2022000590 W JP 2022000590W WO 2022158335 A1 WO2022158335 A1 WO 2022158335A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
forming
film
composition
polymer
Prior art date
Application number
PCT/JP2022/000590
Other languages
English (en)
French (fr)
Inventor
耕大 松浦
淳矢 堀内
悠 岡田
禎 大松
雅敏 越後
Original Assignee
三菱瓦斯化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三菱瓦斯化学株式会社 filed Critical 三菱瓦斯化学株式会社
Priority to JP2022576612A priority Critical patent/JPWO2022158335A1/ja
Priority to CN202280010691.6A priority patent/CN116710500A/zh
Priority to US18/273,014 priority patent/US20240117102A1/en
Priority to KR1020237015895A priority patent/KR20230129974A/ko
Publication of WO2022158335A1 publication Critical patent/WO2022158335A1/ja

Abstract

下記式（０）で表されるモノマー由来の構成単位を有する含む重合体であって、前記構成単位同士が、前記式（０）で表されるモノマーの芳香環同士の直接結合によって連結している部位を有する、重合体。（式（０）中、Ｒは１価の基であり、ｍは１～５の整数であり、ここで、Ｒの少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基、又は、置換基を有していてもよい炭素数０～４０のアミノ基である。）

Description

重合体、組成物、重合体の製造方法、膜形成用組成物、レジスト組成物、レジストパターン形成方法、感放射線性組成物、リソグラフィー用下層膜形成用組成物、リソグラフィー用下層膜の製造方法、回路パターン形成方法、光学部材形成用組成物
　本発明は、重合体、組成物、重合体の製造方法、膜形成用組成物、レジスト組成物、レジストパターン形成方法、感放射線性組成物、リソグラフィー用下層膜形成用組成物、リソグラフィー用下層膜の製造方法、回路パターン形成方法、光学部材形成用組成物に関する。
　半導体用の封止剤、コーティング剤、レジスト用材料、半導体下層膜形成材料として、ヒドロキシ置換芳香族化合物等に由来する繰り返し単位を有するポリフェノール系樹脂が知られている。例えば、特許文献１～２には、特定の骨格を有するポリフェノール化合物又は樹脂を使用することが提案されている。
　一方、ポリフェノール系樹脂の製造方法としては、酸やアルカリ触媒によりフェノール類とホルマリンとを付加及び縮合させて、ノボラック樹脂やレゾール樹脂を製造する方法などが知られている。しかしながら、このフェノール樹脂の製造方法では、近年、ホルムアルデヒドを、前記フェノール樹脂の原材料として使用することから、安全性の点からホルムアルデヒドの代わりの物質を用いた他の方法が種々研究されている。この問題を解決するポリフェノール系樹脂の製造方法として、水や有機溶媒などの溶媒中において、ペルオキシターゼなどのペルオキシターゼ活性を有する酵素と過酸化水素などの過酸化物を用いて、フェノール類を酸化重合させてフェノール重合体を製造する方法などが提案されている。また、２，６－ジメチルフェノールを酸化重合させて、ポリフェニレンオキシド（ＰＰＯ）を製造する方法が知られている（下記非特許文献１参照。）。
　半導体デバイスの製造において、フォトレジスト材料を用いたリソグラフィーによる微細加工が行われているが、近年、ＬＳＩの高集積化と高速度化に伴い、パターンルールによる更なる微細化が求められている。現在の汎用技術として用いられている光露光を用いたリソグラフィーにおいては、光源の波長に由来する本質的な解像度の限界に近づきつつある。
　レジストパターン形成の際に使用するリソグラフィー用の光源は、ＫｒＦエキシマレーザー（２４８ｎｍ）からＡｒＦエキシマレーザー（１９３ｎｍ）へと短波長化されている。しかしながら、レジストパターンの微細化が進むにつれ、解像度の問題又は現像後にレジストパターンが倒れるといった問題が生じてくるため、レジストの薄膜化が望まれている。このような要望に対して、単にレジストの薄膜化を行うのみでは、基板加工に十分なレジストパターンの膜厚を得ることが難しくなる。そのため、レジストパターンだけではなく、レジストと加工する半導体基板との間にレジスト下層膜を作製し、このレジスト下層膜にも基板加工時のマスクとしての機能を持たせるプロセスが必要になってくる。
　現在、このようなプロセス用のレジスト下層膜として、種々のものが知られている。例えば、従来のエッチング速度の速いレジスト下層膜とは異なり、レジストに近いドライエッチング速度の選択比を持つリソグラフィー用レジスト下層膜を挙げることができる。このようなリソグラフィー用レジスト下層膜を形成するための材料としては、所定のエネルギーの印加によって末端基が脱離することでスルホン酸残基を生じる置換基を少なくとも有する樹脂成分と、溶媒と、を含有する多層レジストプロセス用下層膜形成材料が提案されている（例えば、下記特許文献３参照。）。また、レジストに比べて小さいドライエッチング速度の選択比を持つリソグラフィー用レジスト下層膜も挙げることができる。このようなリソグラフィー用レジスト下層膜を形成するための材料として、特定の構成単位を有する重合体を含むレジスト下層膜材料が提案されている（例えば、特許文献４参照。）。さらに、半導体基板に比べて小さいドライエッチング速度の選択比を持つリソグラフィー用レジスト下層膜も挙げることができる。このようなリソグラフィー用レジスト下層膜を形成するための材料として、アセナフチレン類の構成単位と、置換又は非置換の水酸基を有する構成単位とを共重合してなる重合体を含むレジスト下層膜材料が提案されている（例えば、下記特許文献５参照。）。また特定のビスナフトール体の酸化重合体を含むレジスト下層膜材料が提案されている（例えば、下記特許文献６参照。）。
　一方、この種のレジスト下層膜において高いエッチング耐性を持つ材料としては、メタンガス、エタンガス、アセチレンガスなどを原料に用いた化学蒸着薄膜成膜法（Ｃｈｅｍｉｃａｌ　Ｖａｐｏｒ　Ｄｅｐｏｓｉｔｉｏｎ、以下「ＣＶＤ」とも記す。）により形成されたアモルファスカーボン下層膜がよく知られている。しかしながら、プロセス上の観点から、スピンコート法やスクリーン印刷等の湿式プロセスでレジスト下層膜を形成できるレジスト下層膜材料が求められている。
　また最近は複雑な形状の被加工層に対し、リソグラフィー用レジスト下層膜を形成する要求があり、埋め込み性や膜表面の平坦化性に優れた下層膜を形成できるレジスト下層膜材料が求められている。
　なお、３層プロセスにおけるレジスト下層膜の形成において用いられる中間層の形成方法に関しては、例えば、シリコン窒化膜の形成方法（例えば、下記特許文献７参照。）や、シリコン窒化膜のＣＶＤ形成方法（例えば、下記特許文献８参照。）が知られている。また、３層プロセス用の中間層材料としては、シルセスキオキサンベースの珪素化合物を含む材料が知られている（例えば、下記特許文献９参照。）。
　本発明者らは、特定の化合物又は樹脂を含むリソグラフィー用下層膜形成用組成物を提案している（例えば、下記特許文献１０参照。）。
　光学部材形成組成物としても様々なものが提案されており、例えば、アクリル系樹脂（例えば、下記特許文献１１及び１２参照。）や、アリル基で誘導された特定の構造を有するポリフェノール（例えば、下記特許文献１３参照。）が提案されている。
国際公開２０１３／０２４７７８号 国際公開２０１３／０２４７７９号 特開２００４－１７７６６８号公報 特開２００４－２７１８３８号公報 特開２００５－２５０４３４号公報 特開２０２０－０２７３０２号公報 特開２００２－３３４８６９号公報 国際公開第２００４／０６６３７７号 特開２００７－２２６２０４号公報 国際公開第２０１３／０２４７７９号 特開２０１０－１３８３９３号公報 特開２０１５－１７４８７７号公報 国際公開第２０１４／１２３００５号
東村秀之、小林四郎、化学と工業、５３，５０１（２０００）
　特許文献１及び２に記載の材料は、耐熱性、耐エッチング性などの性能において未だ改善の余地があり、これらの物性においてさらに優れる新たな材料の開発が求められている。
　また、非特許文献１の方法に基づいて得られるポリフェノール系樹脂は、オキシフェノールユニットと、分子中にフェノール性水酸基を有するユニットとの両方を構成単位とするものである。オキシフェノールユニットは、通常、モノマーである一方のフェノール類の芳香環上の炭素原子と他方のフェノール類のフェノール性水酸基との間で結合が生じて得られる。また、上述の分子中にフェノール性水酸基を有するユニットは、モノマーであるフェノール類がその芳香環上の炭素原子間で結合されることにより得られる。かかるポリフェノール系樹脂は、芳香環同士が酸素原子を介して結合しているため、柔軟性を有する重合体となるが、架橋性及び耐熱性の観点からはフェノール性水酸基が消失するため好ましくない。
　上述したように、従来数多くのリソグラフィー用膜形成材料が提案されているが、耐熱性及びエッチング耐性を高い水準で両立させたものはなく、新たな材料の開発が求められている。
　さらに、従来、数多くの光学部材向け組成物が提案されているが、耐熱性、透明性及び屈折率を高い次元で両立させたものはなく、新たな材料の開発が求められている。
　本発明は、前記問題点に鑑みてなされたものであり、耐熱性、耐エッチング性に優れる重合体、組成物、重合体の製造方法、膜形成用組成物、レジスト組成物、レジストパターン形成方法、感放射線性組成物、リソグラフィー用下層膜形成用組成物、リソグラフィー用下層膜の製造方法、回路パターン形成方法、光学部材形成用組成物を提供することにある。
　本発明者らは、前記課題を解決するために鋭意検討を重ねた結果、特定の構造を有する重合体を用いることにより、前記課題を解決できることを見出し、本発明を完成するに到った。
　すなわち、本発明は以下の態様を包含する。
＜１＞　下記式（０）で表されるモノマー由来の構成単位を含む重合体であって、
　構成単位同士が芳香環同士の直接結合によって連結している部位を有する、重合体。
Figure JPOXMLDOC01-appb-C000006
  
（式（０）中、Ｒは１価の基であり、ｍは１～５の整数であり、ここで、Ｒの少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基、又は、置換基を有していてもよい炭素数０～４０のアミノ基である。）
＜２＞　前記式（０）におけるｍが２以上であり、Ｒの少なくとも２つが水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である、前記＜１＞に記載の重合体。
＜３＞　さらに、前記式（０）で表されるモノマーと共重合可能な、他の共重合可能な化合物に由来の構成単位を含み、前記式（０）で表されるモノマー由来の構成単位（ｘ）と、他の共重合可能な化合物（ｙ）に由来する構成単位とモル比（ｘ：ｙ）が、１：９９～９９：１である、前記＜１＞又は前記＜２＞に記載の重合体。
＜４＞　前記他の共重合可能な化合物が、下記式（１Ａ）～下記式（１Ｄ）で表されるモノマー、又は、ヘテロ原子含有芳香族モノマーで構成される群から選ばれる、前記＜３＞に記載の重合体。
Figure JPOXMLDOC01-appb-C000007
  
（式（１Ａ）中、Ｘは各々独立して酸素原子、硫黄原子、単結合又は無架橋であることを示し、Ｙ０は炭素数１～６０の２ｎ価の基又は単結合であり、ここで、Ｘが無架橋であるとき、Ｙ０は前記２ｎ１価の基であり、Ａは各々独立してベンゼン、ビフェニル、ターフェニル、ジフェニルメチレン又は縮合環であり、Ｒ０は各々独立して、水素原子、置換基を有していてもよい炭素数１～４０のアルキル基、置換基を有していてもよい炭素数６～４０のアリール基、置換基を有していてもよい炭素数２～４０のアルケニル基、炭素数２～４０のアルキニル基、置換基を有していてもよい炭素数１～４０のアルコキシ基、ハロゲン原子、チオール基、アミノ基、ニトロ基、カルボキシル基又は水酸基でありここで、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基であり、ｍ１は各々独立して１以上の整数であり、ｎ１は１～４の整数である。
　式（１Ｂ）中、Ａ、Ｒ０及びｍ１は、前記式（１Ａ）において説明したものと同義であり、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。
　式（１Ｃ）中、ｎ２は１～５００の整数であり、Ｙは、炭素数１～６０の２価の基又は単結合である。Ａ、Ｒ０及びｍ１は、前記式（１Ａ）において説明したものと同義であり、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。
　式（１Ｄ）中、ｎ３は１～１０の整数であり、Ｙは、前記式（１Ｃ）において説明したものと同義であり、Ａ、Ｒ０及びｍ１は、前記式（１Ａ）において説明したものと同義であり、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。）
＜５＞　下記式（１Ａ）で示される化合物が、下記式（１Ａ－１）で示される化合物である前記＜４＞に記載の重合体。
Figure JPOXMLDOC01-appb-C000008
  
（式（１Ａ－１）中、ｎ４は、各々独立して０～３の整数であり、Ｘ、Ｙ０、Ｒ０、ｍ１及びｎ１は、前記式（１Ａ）において説明したものと同義である。）
＜６＞　前記Ａが、ベンゼン、ビフェニル、ターフェニル、ジフェニルメチレン、ナフタレン、アントラセン、ナフタセン、ペンタセン、ベンゾピレン、クリセン、ピレン、トリフェニレン、コランニュレン、コロネン、オバレン及びフルオレンである、前記＜４＞に記載の重合体。
＜７＞　前記式（１Ｃ）で示される化合物が、下記式（１Ｃ－１）で示される化合物である前記＜４＞に記載の重合体。
Figure JPOXMLDOC01-appb-C000009
  
（式（１Ｃ）中、Ｒ１は、各々独立して、水素原子、置換基を有していてもよい炭素数１～４０のアルキル基、置換基を有していてもよい炭素数６～４０のアリール基置換基を有していてもよい炭素数２～４０のアルケニル基、炭素数２～４０のアルキニル基、置換基を有していてもよい炭素数１～４０のアルコキシ基、ハロゲン原子、チオール基、アミノ基、ニトロ基、カルボキシル基又は水酸基であり、Ａ、Ｒ０、ｍ１、ｎ２は、前記式（１Ｃ）において説明したものと同義であり、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。）
＜８＞　前記式（１Ｄ）で示される化合物が、下記式（１Ｄ－１）で示される化合物である前記＜４＞に記載の重合体。
Figure JPOXMLDOC01-appb-C000010
  
（式（１Ｄ－１）中、Ｒ１は、各々独立して、水素原子、置換基を有していてもよい炭素数１～４０のアルキル基、置換基を有していてもよい炭素数６～４０のアリール基、置換基を有していてもよい炭素数２～４０のアルケニル基、炭素数２～４０のアルキニル基、置換基を有していてもよい炭素数１～４０のアルコキシ基、ハロゲン原子、チオール基、アミノ基、ニトロ基、カルボキシル基又は水酸基であり、Ａ、Ｒ０、ｍ１、ｎ３は、前記式（１Ｄ）において説明したものと同義であり、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。）
＜９＞　前記ヘテロ原子含有芳香族モノマーが、複素環式芳香族化合物を含む、前記＜４に記載の重合体。
＜１０＞　前記＜１＞～前記＜９＞のいずれかに記載の重合体を含む、組成物。
＜１１＞　溶媒をさらに含む、前記＜１０＞に記載の組成物。
＜１２＞　前記溶媒が、プロピレングリコールモノメチルエーテル、プロピレングリコールモノメチルエーテルアセテート、シクロヘキサノン、シクロペンタノン、乳酸エチル及びヒドロキシイソ酪酸メチルで構成される群より選択される少なくとも１種を含む、前記＜１１＞に記載の組成物。
＜１３＞　不純物金属の含有量が金属種毎に５００ｐｐｂ未満である、前記＜１１＞又は前記＜１２＞に記載の組成物。
＜１４＞　前記不純物金属が、銅、マンガン、鉄、コバルト、ルテニウム、クロム、ニッケル、スズ、鉛、銀及びパラジウムで構成される群より選択される少なくとも１種を含有する、前記＜１３＞に記載の組成物。
＜１５＞　前記不純物金属の含有量が、１ｐｐｂ以下である、前記＜１３＞又は前記＜１４＞に記載の組成物。
＜１６＞　前記＜１＞～前記＜９＞のいずれかに記載の重合体の製造方法であって、１種又は２種以上の前記式（０）で表されるモノマーを酸化剤の存在下で重合させる工程を含む、重合体の製造方法。
＜１７＞　１種又は２種以上の前記式（０）で表されるモノマーと、前記式（０）で表されるモノマーと共重合可能な、他の共重合可能な化合物と、を酸化剤の存在下で重合させる工程を含む、前記＜１６＞に記載の重合体の製造方法。
＜１８＞　前記酸化剤が、銅、マンガン、鉄、コバルト、ルテニウム、クロム、ニッケル、スズ、鉛、銀及びパラジウムで構成される群より選択される少なくとも１種を含有する金属塩類又は金属錯体である、前記＜１６＞又は前記＜１７＞に記載の重合体の製造方法。
＜１９＞　前記＜１＞～前記＜９＞のいずれかに記載の重合体を含む、膜形成用組成物。
＜２０＞　前記＜１９＞に記載の膜形成用組成物を含む、レジスト組成物。
＜２１＞　溶媒、酸発生剤、塩基発生剤及び酸拡散制御剤で構成される群より選択される少なくとも１種をさらに含有する、前記＜２０＞に記載のレジスト組成物。
＜２２＞　前記＜２０＞又は前記＜２１＞に記載のレジスト組成物を用いて、基板上にレジスト膜を形成する工程と、
　形成された前記レジスト膜の少なくとも一部を露光する工程と、
　露光した前記レジスト膜を現像してレジストパターンを形成する工程と、
　を含む、レジストパターン形成方法。
＜２３＞　前記＜１９＞に記載の膜形成用組成物と、ジアゾナフトキノン光活性化合物と、溶媒と、を含有する感放射線性組成物であって、
　前記溶媒の含有量が、前記感放射線性組成物の総量１００質量部に対して２０～９９質量部であり、
　前記溶媒以外の固形分の含有量が、前記感放射線性組成物の総量１００質量部に対して１～８０質量部である、感放射線性組成物。
＜２４＞　前記＜２３＞に記載の感放射線性組成物を用いて、基板上にレジスト膜を形成する工程と、
　形成された前記レジスト膜の少なくとも一部を露光する工程と、
　露光した前記レジスト膜を現像して、レジストパターンを形成する工程を含む、レジストパターン形成方法。
＜２５＞　前記＜１９＞に記載の膜形成用組成物を含む、リソグラフィー用下層膜形成用組成物。
＜２６＞　溶媒、酸発生剤、塩基発生剤及び架橋剤で構成される群から選択される少なくとも１つをさらに含有する、前記＜２５＞に記載のリソグラフィー用下層膜形成用組成物。
＜２７＞　前記＜２５＞又は前記＜２６＞に記載のリソグラフィー用下層膜形成用組成物を用いて、基板上に下層膜を形成する工程を含む、リソグラフィー用下層膜の製造方法。
＜２８＞　前記＜２５＞又は前記＜２６＞に記載のリソグラフィー用下層膜形成用組成物を用いて、基板上に、下層膜を形成する工程と、
　前記下層膜上に、少なくとも１層のフォトレジスト層を形成する工程と、
　前記フォトレジスト層の所定の領域に放射線を照射し、現像してレジストパターンを形成する工程と、
　を有する、レジストパターン形成方法。
＜２９＞　前記＜２５＞又は前記＜２６＞に記載のリソグラフィー用下層膜形成用組成物を用いて、基板上に下層膜を形成する工程と、
　前記下層膜上に、珪素原子を含有するレジスト中間層膜材料を用いて中間層膜を形成する工程と、
　前記中間層膜上に、少なくとも１層のフォトレジスト層を形成する工程と、
　前記フォトレジスト層の所定の領域に放射線を照射し、現像してレジストパターンを形成する工程と、
　前記レジストパターンをマスクとして前記中間層膜をエッチングして、中間層膜パターンを形成する工程と、
　前記中間層膜パターンをエッチングマスクとして前記下層膜をエッチングして、下層膜パターンを形成する工程と、
　前記下層膜パターンをエッチングマスクとして前記基板をエッチングして、前記基板にパターンを形成する工程と、
　を有する、回路パターン形成方法。
＜３０＞　前記＜１９＞に記載の膜形成用組成物を含む、光学部材形成用組成物。
＜３１＞　溶媒、酸発生剤、塩基発生剤及び架橋剤で構成される群から選択される少なくとも１つをさらに含有する、前記＜３０＞に記載の光学部材形成用組成物。
＜３２＞
　前記＜１＞～前記＜９＞のいずれかに記載の重合体を、溶媒に溶解させて溶液（Ｓ）を得る工程と、得られた溶液（Ｓ）と酸性の水溶液とを接触させて、前記重合体中の不純物を抽出する工程（第一抽出工程）とを含み、前記溶液（Ｓ）を得る工程で用いる溶媒が、水と任意に混和しない有機溶媒を含む、精製方法。
　本発明によれば、耐熱性、耐エッチング性に優れる重合体、組成物、重合体の製造方法、膜形成用組成物、レジスト組成物、レジストパターン形成方法、感放射線性組成物、リソグラフィー用下層膜形成用組成物、リソグラフィー用下層膜の製造方法、回路パターン形成方法、光学部材形成用組成物を提供することができる。
　以下、本発明を実施するための形態（以下、「本実施形態」という。）について詳細に説明するが、本発明はこれに限定されるものではなく、その要旨を逸脱しない範囲で様々な変形が可能である。
［重合体］
　本実施形態の重合体は、式（０）で表されるモノマー由来の構成単位を有する重合体であって、前記構成単位同士が、前記式（０）で表されるモノマーの芳香環同士の直接結合によって連結している部位を有する。本実施形態の重合体は、このように構成されていることから、耐熱性、耐エッチング性などの性能において、より優れた性能を有する。
Figure JPOXMLDOC01-appb-C000011
  
　式（０）中、Ｒは１価の基であり、ｍは１～５の整数であり、ここで、Ｒの少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。）
　本実施形態の重合体は、以下に限定されないが、典型的には、下記（１）～（４）の特性を有する。
（１）本実施形態の重合体は、有機溶媒（特に安全溶媒）に対する優れた溶解性を有する。このため、例えば、本実施形態の重合体をリソグラフィー用膜形成材料として用いると、スピンコート法やスクリーン印刷等の湿式プロセスによりリソグラフィー用膜を形成できる。
（２）本実施形態の重合体では、炭素濃度が比較的高く、酸素濃度が比較的低い。また、分子中に反応活性部位を有するため、硬化剤との反応による硬化物の形成に有用であるが、単独でも高温ベーク時に反応活性部位が架橋反応することにより硬化物を形成できる。これらに起因して、本実施形態の重合体は、高い耐熱性を発現でき、リソグラフィー用膜形成材料として用いると、高温ベーク時の膜の劣化が抑制され、酸素プラズマエッチング等に対するエッチング耐性に優れたリソグラフィー用膜を形成できる。
（３）本実施形態の重合体は、上述のように、高い耐熱性及びエッチング耐性を発現できるとともに、レジスト層やレジスト中間層膜材料との密着性に優れる。このため、リソグラフィー用膜形成材料として用いると、レジストパターン形成性に優れたリソグラフィー用膜を形成できる。なお、ここでいう「レジストパターン形成性」とは、レジストパターン形状に大きな欠陥が見られず、解像性及び感度ともに優れる性質をいう。
（４）本実施形態の重合体は、芳香環密度が高いため高屈折率であり、加熱処理しても着色が抑制され、透明性に優れる。このため、本実施形態の重合体は、各種光学部材形成用組成物としても有用である。
　本実施形態の組成物は、本実施形態の重合体を含むため、当該組成物にも上述した特性が付与される。特に、２価の有機基や酸素原子等で架橋された樹脂に比べて芳香環密度が高く、直接芳香環の炭素－炭素同士が直接結合で連結されているため、比較的低分子量であっても、耐熱性、耐エッチング性などの性能において、より優れた性能を有するものと考えられる。
　なお、精製により不純物金属含有量を低減させることで、これら本実施形態の組成物の保存安定性をさらに高めることも可能である。
　本実施形態の重合体は、上述した特性により、リソグラフィー用膜形成材料として好ましく適用できる。すなわち、当該重合体を含む本実施形態の組成物は、膜形成用組成物、レジスト組成物、感放射線性組成物、リソグラフィー用下層膜形成用組成物、及び光学部材形成用組成物等、種々の用途に使用できる。
　さらに、本実施形態の組成物を用いた、レジストパターン形成方法、リソグラフィー用下層膜の製造方法、回路パターン形成方法によれば、パターンの耐熱性及びエッチング耐性に加えて、レジストパターンの電子線照射に対する反応性；下層膜の埋め込み性；解像性、感度、現像後のレジストパターン形状；屈折率、消衰係数、及び透明性等の光学特性；膜の欠陥数の低減などを優れたレジストパターン形成性を発揮することができる。
　以下、前述の式（０）について詳細に説明する。
　本実施形態において、「置換」とは、別段定義がない限り、芳香環を構成する炭素原子に結合した水素原子、及び或る官能基中の水素原子の少なくとも１つが、置換基で置換されることを意味する。
　「置換基」としては、別段定義がない限り、例えば、ハロゲン原子、水酸基、カルボキシル基、シアノ基、ニトロ基、チオール基、複素環基、炭素数１～３０のアルキル基、炭素数６～２０のアリール基、炭素数１～３０のアルコキシル基、炭素数２～３０のアルケニル基、炭素数２～３０のアルキニル基、炭素数１～３０のアシル基、炭素数０～３０のアミノ基等が挙げられる。
　本実施形態において、「アルキル基」は、別段定義がない限り、直鎖状脂肪族炭化水素基、分岐状脂肪族炭化水素基、及び環状脂肪族炭化水素基のいずれの態様でも構わない。
　式（０）中、Ｒは１価の基であり、各々独立して、例えば、水素原子、置換基を有していてもよい炭素数１～４０のアルキル基、置換基を有していてもよい炭素数６～４０のアリール基、置換基を有していてもよい炭素数２～４０のアルケニル基、炭素数２～４０のアルキニル基、置換基を有していてもよい炭素数１～４０のアルコキシ基、炭素数０～４０のアミノ基、ハロゲン原子、チオール基、ニトロ基、カルボキシル基又は水酸基である。ここで、前記アルキル基は、直鎖状、分岐状又は環状のいずれであってもよい。また、Ｒの少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である（ここで、炭素数０のアミノ基は“－ＮＨ２”を意味する）。
　式（０）中、Ｒとしては、各々独立して、ｉ）水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基、置換基を有していてもよい炭素数０～４０のアミノ基、置換基を有していてもよい炭素数１～４０のアルキル基、又は、置換基を有していてもよい炭素数６～４０のアリール基であり、Ｒの少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基であることが好ましく、ii）水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基、置換基を有していてもよい炭素数０～４０のアミノ基、又は、炭素数１～６のアルキル基、又は、水酸基、炭素数１～４０のアルコキシ基、炭素数０～４０のアミノ基若しくは炭素数１～６のアルキル基を有していてもよい炭素数６～１２のアリ―ル基であり、Ｒの少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基であることがさらに好ましく、iii）水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基、置換基を有していてもよい炭素数０～４０のアミノ基、メチル基、又は、水酸基、メチル基若しくはアミノ基を有していてもよいフェニル基であり、Ｒの少なくとも１つは、水酸基、又は置換基を有していてもよい炭素数０～４０のアミノ基であることが特に好ましい。
　また、式（０）中、ｍは１～５の整数であり、１～３が好ましく、１～２が好ましい。
　炭素数１～４０のアルキル基としては、以下に限定されないが、例えば、メチル基、エチル基、ｎ－プロピル、ｉ－プロピル基、ｎ－ブチル基、ｉ－ブチル基、ｔ－ブチル基、ｎ－ペンチル基、ｎ－ヘキシル基、ｎ－ドデシル基、バレル基等が挙げられる。
　炭素数６～４０のアリール基としては、以下に限定されないが、例えば、フェニル基、ナフタレン基、ビフェニル基、アントラシル基、ピレニル基、ペリレン基等が挙げられる。
　炭素数２～４０のアルケニル基としては、以下に限定されないが、例えば、エチニル基、プロペニル基、ブチニル基、ペンチニル基等が挙げられる。
　炭素数２～４０のアルキニル基としては、以下に限定されないが、例えば、等が挙げられる。アセチレン基、エチニル基が挙げられる。
　炭素数１～４０のアルコキシ基としては、以下に限定されないが、例えば、メトキシ基、エトキシ基、プロポキシ基、ブトキシ基、ペントキシ等が挙げられる。
　炭素数０～４０のアミノ基としては、以下に限定されないが、例えば、アミノ基、メチルアミノ基、ジメチルアミノ基、エチルアミノ基、ジエチルアミノ基、ジフェニルアミノ等が挙げられる。
　式（０）で表される化合物は特に限定されないが、例えば以下の化合物を挙げられ、中でも、水酸基を有する化合物としては、アルキル基を有していてもよいベンゼンジオールが好ましく、レゾルシノール、カテコール、３，３’－ジメチル－４，４’－ジヒドロキシビフェニルがさらに好ましい、レゾルシノールが特に好ましい。
Figure JPOXMLDOC01-appb-C000012
  
Figure JPOXMLDOC01-appb-C000013
  
 
Figure JPOXMLDOC01-appb-C000014
  
　溶解性、耐熱性及びエッチング耐性兼備の観点からｍが２以上であり、Ｒの少なくとも２つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である、式（０）で表されるモノマーを用いることが好ましく、Ｒの２～３つが水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基であることがより好ましく、Ｒの２つが水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基であることがさらに好ましく、Ｒの２つが水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４のアミノ基（例えば、－ＮＨ２、－ＮＨ（ＣＨ３）、－Ｎ（ＣＨ３）２、又は、－Ｎ（ＣＨ２ＣＨ３）２）であることが特に好ましい。
　また塗布性の観点からは、水酸基又は置換基を有していてもよい炭素数１～４０のアルコキシ基が好ましい。酸素ガスを併用する際のエッチング耐性の観点からは、アミノ基又は置換基を有していてもよい炭素数１～４０のアミノ基が好ましい。
　更に耐熱性及びエッチング耐性を向上させる観点から、本実施形態の重合物は、さらに式（０）で表されるモノマーと共重合可能な、他の共重合可能な化合物に由来の構成単位を含むことが好ましい。式（０）で表されるモノマー由来の構成単位（ｘ）と、他の共重合可能な化合物（ｙ）に由来する構成単位とモル比（ｘ：ｙ）である、重合体が好ましく、１９：８１～９９：１のモル比である、重合体がより好ましく、４９：５１～９９：１のモル比である、重合体がさらに好ましく、７９：２１～９１：１９のモル比である、重合体が特に好ましい。式（０）で表されるモノマー由来の構成単位と、他の共重合可能な化合物とは、芳香環同士で直接結合していることが好ましい。
　他の共重合可能な化合物が、式（１Ａ）～式（１Ｄ）で表されるモノマー又はヘテロ原子含有芳香族モノマーで構成される群から選ばれる、重合体であることが好ましい。
Figure JPOXMLDOC01-appb-C000015
  
（式（１Ａ））
　式（１Ａ）中、Ｘは各々独立して酸素原子、硫黄原子、単結合又は無架橋であることを示し、Ｙ０は炭素数１～６０の２ｎ価の基又は単結合であり、ここで、Ｘが無架橋であるとき、Ｙ０は前記２ｎ価の基であり、Ａは各々独立してベンゼン、ビフェニル、ターフェニル、ジフェニルメチレン又は縮合環であり、Ｒ０は各々独立して、水素原子、置換基を有していてもよい炭素数１～４０のアルキル基、置換基を有していてもよい炭素数６～４０のアリール基、置換基を有していてもよい炭素数２～４０のアルケニル基、炭素数２～４０のアルキニル基、置換基を有していてもよい炭素数１～４０のアルコキシ基、ハロゲン原子、チオール基、アミノ基、ニトロ基、カルボキシル基又は水酸基であり、ここで、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基であり、ｍ１は各々独立して１以上の整数であり、ｎ１は１～４の整数である。なお、ｍ１の上限値は特に限定はなく、Ａが示す環構造におけるＲ０の結合可能部位の数に応じて変動する。このため、ｍ１の範囲は特に限定されるものではないが、例えば、ｍ１は各々独立して１～９の整数とすることができる。
　式（１Ａ）中、Ａは各々独立してベンゼン、ビフェニル、ターフェニル、ジフェニルメチレン又は縮合環を示す。前記縮合体としては、ナフタレン、アントラセン、ナフタセン、ペンタセン、ベンゾピレン、クリセン、ピレン、トリフェニレン、コランニュレン、コロネン及びオバレン及びフルオレンである、Ａとしては、耐熱性と溶解性とを兼備する観点から、ナフタレン、アントラセン、ピレン及びフルオレンが好ましい。また更なる高溶解性の観点からは、ベンゼンが好ましい。
　Ｘは、酸素原子、硫黄原子、単結合又は無架橋であることを示す。Ｘとしては、耐熱性の観点から、酸素原子が好ましい。またＸとしては、溶解性及びエッチング耐性の観点から無架橋が好ましい。
　Ｙ０は、炭素数１～６０の２ｎ１価の基又は単結合であり、ここで、Ｘが無架橋であるとき、Ｙ０は前記２ｎ１価の基である。炭素数１～６０の２ｎ価の基とは、例えば、２ｎ価の炭化水素基であり、当該炭化水素基は、置換基として、後述する種々の官能基を有するものであってもよい。また、２ｎ価の炭化水素基は、ｎ＝１のときには、炭素数１～６０のアルキレン基、ｎ＝２のときには、炭素数１～６０のアルカンテトライル基、ｎ＝３のときには、炭素数２～６０のアルカンヘキサイル基、ｎ＝４のときには、炭素数３～６０のアルカンオクタイル基のことを示す。該２ｎ価の炭化水素基としては、例えば、２ｎ＋１価の炭化水素基と、直鎖状炭化水素基、分岐状炭化水素基又は脂環式炭化水素基とが結合した基等が挙げられる。ここで、脂環式炭化水素基については、有橋脂環式炭化水素基も含まれる。
　２ｎ＋１価の炭化水素基としては、以下に限定されないが、例えば、３価のメチン基、エチン基等が挙げられる。
　また、前記２ｎ価の炭化水素基は、二重結合、三重結合、ヘテロ原子及び／又は炭素数６～５９のアリール基を有していてもよい。なお、Ｙ０はフルオレンやベンゾフルオレン等のフルオレン骨格を有する化合物に由来する基を含んでいてもよい。
　本実施形態において、該２ｎ価の基はハロゲン基、ニトロ基、アミノ基、水酸基、アルコキシ基、チオール基又は炭素数６～４０のアリール基を含んでいてもよい。さらに、該２ｎ価の基はエーテル結合、ケトン結合、エステル結合又は二重結合を含んでいてもよい。
　本実施形態において２ｎ価の基は耐熱性の観点から直鎖状炭化水素基よりも分岐状炭化水素基又は脂環式炭化水素基を含むことが好ましく、脂環式炭化水素基を含むことがより好ましい。また、本実施形態においては、２ｎ価の基が炭素数６～６０のアリール基を有することが特に好ましい。
　２ｎ価の基に含まれ得る置換基であって、直鎖状の炭化水素基及び分岐状炭化水素基としては、特に限定されないが、例えば、無置換のメチル基、エチル基、ｎ－プロピル基、ｉ－プロピル基、ｎ－ブチル基、ｉ－ブチル基、ｔ－ブチル基、ｎ－ペンチル基、ｎ－ヘキシル基、ｎ－ドデシル基、バレル基等が挙げられる。
　２ｎ価の基に含まれ得る置換基であって、脂環式炭化水素基及び炭素数６～６０の芳香族基としては、特に限定されないが、例えば、無置換のフェニル基、ナフタレン基、ビフェニル基、アントラシル基、ピレニル基、シクロヘキシル基、シクロドデシル基、ジシクロペンチル基、トリシクロデシル基、アダマンチル基、フェニレン基、ナフタレンジイル基、ビフェニルジイル基、アントラセンジイル基、ピレンジイル基、シクロヘキサンジイル基、シクロドデカンジイル基、ジシクロペンタンジイル基、トリシクロデカンジイル基、アダマンタンジイル基、ベンゼントリイル基、ナフタレントリイル基、ビフェニルトリイル基、アントラセントリイル基、ピレントリイル基、シクロヘキサントリイル基、シクロドデカントリイル基、ジシクロペンタントリイル基、トリシクロデカントリイル基、アダマンタントリイル基、ベンゼンテトライル基、ナフタレンテトライル基、ビフェニルテトライル基、アントラセンテトライル基、ピレンテトライル基、シクロヘキサンテトライル基、シクロドデカンテトライル基、ジシクロペンタンテトライル基、トリシクロデカンテトライル基、アダマンタンテトライル基等が挙げられる。
　式（１Ａ）中、Ｒ０は１価の基であり、各々独立して、置換基を有していてもよい炭素数１～４０のアルキル基、置換基を有していてもよい炭素数６～４０のアリール基、置換基を有していてもよい炭素数２～４０のアルケニル基、炭素数２～４０のアルキニル基、置換基を有していてもよい炭素数１～４０のアルコキシ基、炭素数０～４０のアミノ基、ハロゲン原子、チオール基、ニトロ基、カルボキシル基又は水酸基である。ここで、前記アルキル基は、直鎖状、分岐状又は環状のいずれであってもよい。ここで、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。
　炭素数１～４０のアルキル基としては、以下に限定されないが、例えば、メチル基、エチル基、ｎ－プロピル基、ｉ－プロピル基、ｎ－ブチル基、ｉ－ブチル基、ｔ－ブチル基、ｎ－ペンチル基、ｎ－ヘキシル基、ｎ－ドデシル基、バレル基、ベンジル基及びフェネチル基等が挙げられる。メチル基、エチル基、ベンジル基及びフェネチル基が好ましく、メチル基及びベンジル基がより好ましい。
　炭素数６～４０のアリール基としては、以下に限定されないが、例えば、フェニル基、ナフタレン基、ビフェニル基、アントラシル基、ピレニル基、ペリレン基等が挙げられる。フェニル基が好ましい。
　炭素数２～４０のアルケニル基としては、以下に限定されないが、例えば、エチニル基、プロペニル基、ブチニル基、ペンチニル基等が挙げられる。エチニル基が好ましい。
　炭素数２～４０のアルキニル基としては、以下に限定されないが、例えば、等が挙げられる。アセチレン基、エチニル基、エチニル基が好ましい。
　炭素数１～４０のアルコキシ基としては、以下に限定されないが、例えば、メトキシ基、エトキシ基、プロポキシ基、ブトキシ基、ペントキシ等が挙げられる。メトキシ基及びエトキシ基が好ましい。
　炭素数０～４０のアミノ基としては、以下に限定されないが、例えば、アミノ基、メチルアミノ基、ジメチルアミノ基、エチルアミノ基、ジエチルアミノ基、ジフェニルアミノ等が挙げられる。アミノ基、メチルアミノ基及びジメチルアミノ基が好ましい。
　ｍ１は各々独立して１～９の整数である。溶解性の観点から、１～６が好ましく、１～４がより好ましく、原料入手性の観点から、１～２が更に好ましい。
　ｎ１は１～４の整数である。溶解性の観点から、１～２が好ましく、原料入手性の観点から、１が更に好ましい。
（式（１Ｂ））
　式（１Ｂ）中、Ａ、Ｒ０及びｍ１は、前記式（１Ａ）において説明したものと同義である。また、式（１Ｂ）において、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。なお、式（１Ｂ）において、Ａは縮合環であることが好ましい。
（式（１Ｃ））
　式（１Ｃ）中、Ｙは炭素数１～６０の２ｎ価の基であり、ｎ２は１～５００の整数であり、Ａ、Ｒ０及びｍ１は、前記式（１Ａ）において説明したものと同義である。また、式（１Ｃ）において、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。
　式（１Ｃ）中、Ｙは、炭素数１～６０の２価の基又は単結合である。炭素数１～６０の２価の基とは、例えば、２価の炭化水素基であり、当該炭化水素基は、置換基として、後述する種々の官能基を有するものであってもよい。また、２価の炭化水素基は、炭素数１～６０のアルキレン基のことを示す。該２価の炭化水素基としては、例えば、２価の炭化水素基と、直鎖状炭化水素基、分岐状炭化水素基又は脂環式炭化水素基とが結合した基等が挙げられる。ここで、脂環式炭化水素基については、有橋脂環式炭化水素基も含まれる。
　２価の炭化水素基としては、以下に限定されないが、例えば、３価のメチン基、エチン基等が挙げられる。
　また、前記２価の炭化水素基は、二重結合、三重結合、ヘテロ原子及び／又は炭素数６～５９のアリール基を有していてもよい。なお、Ｙはフルオレンやベンゾフルオレン等のフルオレン骨格を有する化合物に由来する基を含んでいてもよい。
　本実施形態において、該２価の基はハロゲン基、ニトロ基、アミノ基、水酸基、アルコキシ基、チオール基又は炭素数６～４０のアリール基を含んでいてもよい。さらに、該２価の基はエーテル結合、ケトン結合、エステル結合又は二重結合を含んでいてもよい。
　本実施形態において２価の基は耐熱性の観点から直鎖状炭化水素基よりも分岐状炭化水素基又は脂環式炭化水素基を含むことが好ましく、脂環式炭化水素基を含むことがより好ましい。また、本実施形態においては、２価の基が炭素数６～６０のアリール基を有することが特に好ましい。
　２価の基に含まれ得る置換基であって、直鎖状の炭化水素基及び分岐状炭化水素基としては、特に限定されないが、例えば、無置換のメチル基、エチル基、ｎ－プロピル基、ｉ－プロピル基、ｎ－ブチル基、ｉ－ブチル基、ｔ－ブチル基、ｎ－ペンチル基、ｎ－ヘキシル基、ｎ－ドデシル基、バレル基等が挙げられる。
　２価の基に含まれ得る置換基であって、脂環式炭化水素基及び炭素数６～６０の芳香族基としては、特に限定されないが、例えば、無置換のフェニル基、ナフタレン基、ビフェニル基、アントラシル基、ピレニル基、シクロヘキシル基、シクロドデシル基、ジシクロペンチル基、トリシクロデシル基、アダマンチル基、フェニレン基、ナフタレンジイル基、ビフェニルジイル基、アントラセンジイル基、ピレンジイル基、シクロヘキサンジイル基、シクロドデカンジイル基、ジシクロペンタンジイル基、トリシクロデカンジイル基、アダマンタンジイル基、ベンゼントリイル基、ナフタレントリイル基、ビフェニルトリイル基、アントラセントリイル基、ピレントリイル基、シクロヘキサントリイル基、シクロドデカントリイル基、ジシクロペンタントリイル基、トリシクロデカントリイル基、アダマンタントリイル基、ベンゼンテトライル基、ナフタレンテトライル基、ビフェニルテトライル基、アントラセンテトライル基、ピレンテトライル基、シクロヘキサンテトライル基、シクロドデカンテトライル基、ジシクロペンタンテトライル基、トリシクロデカンテトライル基、アダマンタンテトライル基等が挙げられる。
（式（１Ｄ））
　式（１Ｄ）中、ｎ３は１～１０の整数であり、Ｙは、前記式（１Ｃ）において説明したものと同義であり、Ａ、Ｒ０及びｍ１は、前記式（１Ａ）において説明したものと同義である。また、式（１Ｄ）において、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。
　溶解性、耐熱性及びエッチング耐性兼備の観点から、式（１Ａ）で示される化合物が、下記式（１Ａ－１）で示される化合物である重合体が好ましい。
Figure JPOXMLDOC01-appb-C000016
  
　式（１Ａ－１）中、ｎ４は、各々独立して０～３の整数であり、Ｘ、Ｙ０、Ｒ０、ｍ１及びｎ１は、前記式（１Ａ）において説明したものと同義である。
　更なる耐熱性及びエッチング耐性向上の観点から、式（１Ａ－１）で示される化合物が、下記式（１Ａ－２ａ）で示される化合物である重合体がより好ましい。
Figure JPOXMLDOC01-appb-C000017
  
　式（１Ａ－２ａ）中、Ｚは、各々独立して酸素原子又は硫黄原子であり、Ｙ０、Ｒ０、ｍ１、ｎ１及びｎ４は、前記式（１Ａ－１）において説明したものと同義である。
　更なる耐熱性及びエッチング耐性向上の観点から、式（１Ａ－２ａ）で示される化合物が、下記式（１Ａ－２ａ－１）で示される化合物である重合体がより好ましい。
Figure JPOXMLDOC01-appb-C000018
  
　式（１Ａ－２ａ－１）中、Ｚ、Ｙ０、Ｒ０、ｍ１及びｎ１は、前記式（１Ａ－２ａ）において説明したものと同義である。
　更なる溶解性向上の観点から、式（１Ａ－１）で示される化合物が、下記式（１Ａ－２ｂ）で示される化合物である重合体がより好ましい。
Figure JPOXMLDOC01-appb-C000019
  
　式（１Ａ－２ｂ）中、Ｙ０、Ｒ０、ｍ１、ｎ１及びｎ４は、前記式（１Ａ－１）において説明したものと同義である。
　式（１Ａ－２ｂ）で示される化合物が、下記式（１Ａ－２ｂ－１）で示される化合物である重合体がより好ましい。
Figure JPOXMLDOC01-appb-C000020
  
　式（１Ａ－２ｂ－１）中、Ｙ０、Ｒ０、ｍ１及びｎ１は、前記式（１Ａ－２ｂ）において説明したものと同義である。
　更なる溶解性、耐熱性及びエッチング耐性向上の観点から、式（１Ａ－１）で示される化合物が、下記式（１Ａ－２ｃ）で示される少なくとの一つの化合物である重合体がより好ましい。
Figure JPOXMLDOC01-appb-C000021
  
　式（１Ａ－２ｃ）中、Ｚは、各々独立して酸素原子又は硫黄原子であり、Ｙ０、Ｒ０、ｍ１、ｎ１及びｎ４は、前記式（１Ａ－１）において説明したものと同義である。
　式（１Ａ－２ｃ）で示される化合物が、下記式（１Ａ－２ｃ－１）で示される少なくとの一つの化合物である重合体がより好ましい。
Figure JPOXMLDOC01-appb-C000022
  
　式（１Ａ－２ｃ－１）中、Ｚ、Ｙ０、Ｒ０、ｍ１、ｎ１及びｎ４は、前記式（１Ａ－２ｃ－１）において説明したものと同義である。
　式（１Ａ－２ｃ－１）で示される化合物が、下記式（１Ａ－２ｃ－１ａ）で示される少なくとの一つの化合物である重合体がさらに好ましい。
Figure JPOXMLDOC01-appb-C000023
  
　式（１Ａ－２ｃ－１ａ）中、Ｚ、Ｙ０、Ｒ０、ｍ１、ｎ１及びｎ４は、前記式（１Ａ－２ｃ－１）において説明したものと同義である。
　式（１Ａ－２ａ－１）で示される化合物が、下記式（１Ａ－３ａ）で示される少なくとも一つの化合物である重合体がさらに好ましい。
Figure JPOXMLDOC01-appb-C000024
  
　式（１Ａ－３ａ）中、Ｙ０、Ｒ０、ｍ１及びｎ１は、前記式（１Ａ－２ａ）において説明したものと同義である。
　式（１Ａ－２ｂ－１）で示される化合物が、下記式（１Ａ－３ｂ）で示される少なくとの一つの化合物である重合体がさらに好ましい。
Figure JPOXMLDOC01-appb-C000025
  
　式（１Ａ－３ｂ）中、Ｙ０、Ｒ０、ｍ１及びｎ１は、前記式（１Ａ－２ａ－１）において説明したものと同義である。
　式（１Ａ－２ｃ－１）で示される化合物が、下記式（１Ａ－３ｃ）で示される少なくとの一つの化合物である重合体がさらに好ましい。
Figure JPOXMLDOC01-appb-C000026
  
　式（１Ａ－３ｃ）中、Ｙ０、Ｒ０、ｍ１及びｎ１は、前記式（１Ａ－２ａ－１）において説明したものと同義である。
　更なる溶解性、耐熱性及びエッチング耐性向上の観点から、上述の各式において、前記Ｙ０が、「ＲＡ－ＲＢ」で表される基であることが好ましい。ここで、当該ＲＡはメチン基であり、当該ＲＢは置換基を有していてもよい炭素数が６～４０のアリール基であることが好ましい。
　平坦化性の観点から、上述の各式において、前記ｎ１が、１～２であることが好ましく、１であることがより好ましい。
　式（１Ａ）で示される化合物は特に限定されないが、例えば、以下の化合物を挙げることができる。
Figure JPOXMLDOC01-appb-C000027
  
Figure JPOXMLDOC01-appb-C000028
  
Figure JPOXMLDOC01-appb-C000029
  
Figure JPOXMLDOC01-appb-C000030
  
Figure JPOXMLDOC01-appb-C000031
  
Figure JPOXMLDOC01-appb-C000032
  
Figure JPOXMLDOC01-appb-C000033
  
Figure JPOXMLDOC01-appb-C000034
  
Figure JPOXMLDOC01-appb-C000035
  
Figure JPOXMLDOC01-appb-C000036
  
Figure JPOXMLDOC01-appb-C000037
  
Figure JPOXMLDOC01-appb-C000038
  
Figure JPOXMLDOC01-appb-C000039
  
Figure JPOXMLDOC01-appb-C000040
  
Figure JPOXMLDOC01-appb-C000041
  
Figure JPOXMLDOC01-appb-C000042
  
Figure JPOXMLDOC01-appb-C000043
  
　式（１Ｂ）で示される化合物は特に限定されないが、例えば、以下の化合物を挙げることができる。
Figure JPOXMLDOC01-appb-C000044
  
Figure JPOXMLDOC01-appb-C000045
  
Figure JPOXMLDOC01-appb-C000046
  
　溶解性、耐熱性及びエッチング耐性兼備の観点から、式（１Ｃ）で示される化合物が、下記式（１Ｃ－１）で示される化合物である重合体が好ましい。
Figure JPOXMLDOC01-appb-C000047
  
（式（１Ｃ－１）中、Ｒ１は、各々独立して、水素原子、置換基を有していてもよい炭素数１～４０のアルキル基、置換基を有していてもよい炭素数６～４０のアリール基置換基を有していてもよい炭素数２～４０のアルケニル基、炭素数２～４０のアルキニル基、置換基を有していてもよい炭素数１～４０のアルコキシ基、ハロゲン原子、チオール基、アミノ基、ニトロ基、カルボキシル基又は水酸基であり、Ａ、Ｒ０、ｍ１、ｎ２は、前記式（１Ｃ）において説明したものと同義であり、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。）
　溶解性、耐熱性及びエッチング耐性兼備の観点から、式（１Ｃ－１）で示される化合物が、下記式（１Ｃ－２）で示される化合物である重合体が好ましい。
Figure JPOXMLDOC01-appb-C000048
  
（式（１Ｃ－２）中、ｐ２は、各々独立して１～４の整数であり、ｑ２は、各々独立して０～４の整数であり、Ｒ１、Ａ、Ｒ０、ｍ１及びｎ２は、前記式（１Ｃ－１）において説明したものと同義であり、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。）
　更なる耐熱性及びエッチング耐性兼備の観点から、式（１Ｃ－２）で示される化合物が、下記式（１Ｃ－３）で示される化合物である重合体が好ましい。
Figure JPOXMLDOC01-appb-C000049
  
（式（１Ｃ－３）中、Ｒ１、Ａ、Ｒ０、ｍ１、ｎ２及びｐ２は、前記式（１Ｃ－２）において説明したものと同義であり、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。）
　更なる耐熱性及びエッチング耐性兼備の観点から、式（１Ｃ－３）で示される化合物が、下記式（１Ｃ－４）で示される少なくとも一つの化合物である重合体が好ましい。
Figure JPOXMLDOC01-appb-C000050
  
（式（１Ｃ－４）中、Ｒ１、Ａ、Ｒ０、ｍ１、ｎ２は、前記式（１Ｃ－３）において説明したものと同義であり、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。）
　更なる溶解性、耐熱性及びエッチング耐性兼備の観点から、式（１Ｃ）においては、Ａがベンゼン環及びナフタレン環であることが好ましく、Ａがベンゼン環であることがより好ましい。
　更なる溶解性、耐熱性及びエッチング耐性兼備の観点から、Ｒ１が水素原子であることが好ましい。
　式（１Ｃ）で示される化合物は特に限定されないが、例えば、以下の化合物を挙げることができる。
Figure JPOXMLDOC01-appb-C000051
  
（ｎ２は、前記式（１Ｃ）において説明したものと同義である。）
　溶解性、耐熱性及びエッチング耐性兼備の観点から、式（１Ｄ）で示される化合物が、下記式（１Ｄ－１）で示される化合物である重合体が好ましい。
Figure JPOXMLDOC01-appb-C000052
  
（式（１Ｄ－１）中、Ｒ１は、各々独立して、水素原子、置換基を有していてもよい炭素数１～４０のアルキル基、置換基を有していてもよい炭素数６～４０のアリール基、置換基を有していてもよい炭素数２～４０のアルケニル基、炭素数２～４０のアルキニル基、置換基を有していてもよい炭素数１～４０のアルコキシ基、ハロゲン原子、チオール基、アミノ基、ニトロ基、カルボキシル基又は水酸基であり、Ａ、Ｒ０、ｍ１、ｎ３は、前記式（１Ｄ）において説明したものと同義であり、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。）
　溶解性、耐熱性及びエッチング耐性兼備の観点から、式（１Ｄ）で示される少なくとの一つの化合物が、下記式（１Ｄ－２）で示される化合物である重合体が好ましい。
Figure JPOXMLDOC01-appb-C000053
  
　式（１Ｄ－２）中、ｐ３は、各々独立して１～３の整数であり、Ｒ０、Ｒ１、ｍ１及びｎ３は、前記式（１Ｄ）において説明したものと同義である。
　溶解性、耐熱性及びエッチング耐性兼備の観点から、式（１Ｄ－１）で示される化合物が、下記式（１Ｄ－３）で示される少なくとの一つの化合物である重合体が好ましい。
Figure JPOXMLDOC01-appb-C000054
  
（式（１Ｄ－３）中、各々独立して１～３の整数であり、Ｒ０、Ｒ１、ｍ１及びｎ３は、前記式（１Ｄ）において説明したものと同義である。）
　溶解性、耐熱性及びエッチング耐性兼備の観点から、式（１Ｂ）、式（１Ｃ）又は式（１Ｄ）で示される化合物のＡが、ベンゼン、ビフェニル、ターフェニル、ジフェニルメチレン、ナフタレン、アントラセン、ナフタセン、ペンタセン、ベンゾピレン、クリセン、ピレン、トリフェニレン、コランニュレン、コロネン、オバレン及びフルオレンである重合体が好ましく、エッチング耐性の観点からは、ベンゼン、ビフェニル、ターフェニル、ナフタレン、アントラセン、ナフタセン、ペンタセン、ベンゾピレン、クリセン、ピレン、トリフェニレン、コランニュレン、コロネン及びオバレン及びフルオレンである重合体がより好ましく、ビフェニル、ターフェニル、ナフタレン、アントラセン、ナフタセン、ペンタセン、ベンゾピレン、クリセン、ピレン、トリフェニレン、コランニュレン、コロネン、オバレン及びフルオレンである重合体がさらに好ましく、ビフェニル、ナフタレン、アントラセン及びフルオレンである重合体が特に好ましい。
　式（１Ｄ）で示される化合物は特に限定されないが、例えば、以下の化合物を挙げることができる。
Figure JPOXMLDOC01-appb-C000055
  
　（式中、Ｒ１及びｎ３は、前記式（１Ｄ）において説明したものと同義である。）
Figure JPOXMLDOC01-appb-C000056
  
　（式中、Ｒ１及びｎ３は、前記式（１Ｄ）において説明したものと同義である。）
　また、各式中における、前記Ｒ１は、水素原子又は下記で示される群から選ばれる構造であることがより好ましい。
Figure JPOXMLDOC01-appb-C000057
  
Figure JPOXMLDOC01-appb-C000058
  
　本実施形態において、ヘテロ原子含有芳香族モノマー中のヘテロ原子の位置は特に限定されないが、耐熱性、溶解性及びエッチング耐性兼備の観点から、ヘテロ原子が芳香環を構成することが好ましい。すなわち、前記ヘテロ原子含有芳香族モノマーが、複素環式芳香族化合物を含むことが好ましい。
　本実施形態において、前記ヘテロ原子含有芳香族モノマーにおけるヘテロ原子は特に限定されず、例えば、酸素原子、窒素原子、リン原子及び硫黄原子を挙げることができる。本実施形態においては、エッチング耐性の観点から、ヘテロ原子として酸素原子を含有するよりも、窒素原子、リン原子又は硫黄原子を含有する方が好ましい。すなわち、前記ヘテロ原子含有芳香族モノマーにおけるヘテロ原子が、窒素原子、リン原子及び硫黄原子で構成される群より選択される少なくとも１種を含むことが好ましい。
　耐熱性及びエッチング耐性兼備の観点から、ヘテロ原子含有芳香族モノマーが、置換若しくは非置換の下記式（１Ｅ－１）で表されるモノマー、又は置換若しくは非置換の下記式（１Ｅ－２）で表されるモノマーを含むことが好ましい。
Figure JPOXMLDOC01-appb-C000059
  
（前記式（１Ｅ－１）中、Ｘは、各々独立して、ＮＲ０で表される基、硫黄原子、酸素原子又はＰＲ０で表される基であり、Ｒ０及びＲ１は、各々独立して、水素原子、水酸基、置換若しくは非置換の炭素数１～３０のアルコキシ基、ハロゲン原子、置換若しくは非置換の炭素数１～３０のアルキル基又は置換若しくは非置換の炭素数６～３０のアリール基である。）
Figure JPOXMLDOC01-appb-C000060
  
（前記式（１Ｅ－２）中、
　Ｑ１及びＱ２は、単結合、置換若しくは非置換の炭素数１～２０のアルキレン基、置換若しくは非置換の炭素数３～２０のシクロアルキレン基、置換若しくは非置換の炭素数６～２０のアリーレン基、置換若しくは非置換の炭素数２～２０のヘテロアリーレン基、置換若しくは非置換の炭素数２～２０のアルケニレン基、置換若しくは非置換の炭素数２～２０のアルキニレン基、カルボニル基、ＮＲａで表される基、酸素原子、硫黄原子又はＰＲａで表される基であり、前記Ｒａは、各々独立して、水素原子、置換若しくは非置換の炭素数１～１０のアルキル基又はハロゲン原子であり、ここで、前記モノマーにおいてＱ１及びＱ２の双方が存在する場合、これらの少なくとも一方がヘテロ原子を含み、前記モノマーにおいてＱ１のみが存在する場合、当該Ｑ１はヘテロ原子を含み、　Ｑ３は、窒素原子、リン原子又はＣＲｂで表される基であり、ここで、前記モノマーにおいてＱ３はヘテロ原子を含み、　前記Ｒａ及びＲｂは、各々独立して、水素原子、置換若しくは非置換の炭素数１～１０のアルキル基又はハロゲン原子である。）
　以下、前述の式（１Ｅ－１）及び式（１Ｅ－２）について詳細に説明する。
　式（１Ｅ－１）中、Ｘは、各々独立して、ＮＲ０で表される基、硫黄原子、酸素原子又はＰＲ０で表される基であり、Ｒ０及びＲ１は、各々独立して、水素原子、水酸基、置換若しくは非置換の炭素数１～３０のアルコキシ基、ハロゲン原子、置換若しくは非置換の炭素数１～３０のアルキル基又は置換若しくは非置換の炭素数６～３０のアリール基である。
　式（１Ｅ－１）中、Ｘは、各々独立して、ＮＲ０で表される基、硫黄原子、又はＰＲ０で表される基であることが好ましい。
　置換若しくは非置換の炭素数１～３０のアルコキシ基としては、以下に限定されないが、例えば、メトキシ基、エトキシ基、プロポキシ基、ブトキシ基、ペントキシ、ヘキシルオキシ、オクチルオキシ、２－エチルヘキシルオキシ等が挙げられる。
　ハロゲン原子とは、以下に限定されないが、例えば、フッ素原子、塩素原子、臭素原子、ヨウ素原子等が挙げられる。
　置換若しくは非置換の炭素数１～３０のアルキル基としては、以下に限定されないが、例えば、メチル基、エチル基、ｎ－プロピル基、ｉ－プロピル基、ｎ－ブチル基、ｉ－ブチル基、ｔ－ブチル基、ｓｅｃ－ブチル基、ｎ－ペンチル基、ネオペンチル基、イソアミル基、ｎ－ヘキシル基、ｎ－ヘプチル基、ｎ－オクチル基、ｎ－ドデシル基、バレル基、２－エチルヘキシル等が挙げられる。
　置換若しくは非置換の炭素数６～３０のアリール基としては、以下に限定されないが、例えば、フェニル基、ナフチル基、ビフェニル基、フルオレニル基、アンスリル基、ピレニル基、アズレニル基、アセナフチレニル基、ターフェニル基、フェナンスリル基、ペリレン基等が挙げられる。
　本実施形態において、溶解性及びエッチング耐性兼備の観点から、式（１Ｅ－１）中、Ｒ１は、置換又は非置換のフェニル基であることが好ましい。
　式（１Ｅ－２）中、Ｑ１及びＱ２は、単結合、置換若しくは非置換の炭素数１～２０のアルキレン基、置換若しくは非置換の炭素数３～２０のシクロアルキレン基、置換若しくは非置換の炭素数６～２０のアリーレン基、置換若しくは非置換の炭素数２～２０のヘテロアリーレン基、置換若しくは非置換の炭素数２～２０のアルケニレン基、置換若しくは非置換の炭素数２～２０のアルキニレン基、カルボニル基、ＮＲａで表される基、酸素原子、硫黄原子又はＰＲａで表される基であり、前記Ｒａは、各々独立して、水素原子、置換若しくは非置換の炭素数１～１０のアルキル基又はハロゲン原子であり、ここで、前記モノマーにおいてＱ１及びＱ２の双方が存在する場合、これらの少なくとも一方がヘテロ原子を含み、前記モノマーにおいてＱ１のみが存在する場合、当該Ｑ１はヘテロ原子を含む。
　式（１Ｅ－２）中、Ｑ３は、窒素原子、リン原子又はＣＲｂで表される基であり、ここで、前記モノマーにおいてＱ３はヘテロ原子を含む。
　前記Ｒａ及びＲｂは、各々独立して、水素原子、置換若しくは非置換の炭素数１～１０のアルキル基又はハロゲン原子である。
　置換若しくは非置換の炭素数１～２０のアルキレン基としては、以下に限定されないが、例えば、メチレン基、エチレン基、ｎ－プロピレン基、ｉ－プロピレン基、ｎ－ブチレン基、ｉ－ブチレン基、ｔ－ブチレン基、ｎ－ペンチレン基、ｎ－ヘキシレン基、ｎ－ドデシレン基、バレレン基、メチルメチレン基、ジメチルメチレン基、メチルエチレン基等が挙げられる。
　置換若しくは非置換の炭素数３～２０のシクロアルキレン基としては、以下に限定されないが、例えば、シクロプロピレン基、シクロブチレン基、シクロペンチレン基、シクロヘキシレン基、シクロドデシレン基、シクロバレレン基等が挙げられる。
　置換若しくは非置換の炭素数６～２０のアリーレン基としては、以下に限定されないが、例えば、フェニレン基、ナフチレン基、アンスリレン基、フェナントリニレン基、ピレニレン基、ペリレニレン基、フルオレニレン基、ビフェニレン基等が挙げられる。
　置換若しくは非置換の炭素数２～２０のヘテロアリーレン基としては、以下に限定されないが、例えば、チエニレン基、ピリジニレン基、フリレン基等が挙げられる。
　置換若しくは非置換の炭素数２～２０のアルケニレン基としては、ビニレン基、プロペニレン基、ブテニレン基等が挙げられる。
　置換若しくは非置換の炭素数２～２０のアルキニレン基としては、エチニレン基、プロピニレン基、ブチニレン基等が挙げられる。
　置換若しくは非置換の炭素数１～１０のアルキル基としては、以下に限定されないが、例えば、メチル基、エチル基、ｎ－プロピル基、ｉ－プロピル基、ｎ－ブチル基、ｉ－ブチル基、ｔ－ブチル基、ｎ－ペンチル基、ｎ－ヘキシル基、ｎ－ドデシル基、バレル基等が挙げられる。
　ハロゲン原子としては、フッ素原子、塩素原子、臭素原子、ヨウ素原子等が挙げられる。
　本実施形態の重合体がヘテロ原子含有芳香族モノマーに由来する構成単位を有する場合、ヘテロ原子を有する芳香族モノマーが直接結合することにより耐熱性を向上しうる。またその構造単位内にＰ、Ｎ、Ｏ又はＳのようなヘテロ原子を含むことによって、重合体の耐エッチング耐性を確保できるだけで無く、ヘテロ原子によって重合体の極性が高くなることで、溶媒溶解性を向上させることができる。さらには、構造単位内に上述のヘテロ原子を有する芳香族モノマーが直接結合した重合体を用いた有機膜は優れた膜密度を確保でき、エッチングによる加工精度を向上しうる。
　上述した観点から、本実施形態において、ヘテロ原子含有芳香族モノマーは、置換若しくは非置換の下記式（１Ｅ－１）で表されるモノマーであることが好ましく、インドール、２－フェニルベンゾオキサゾール、２－フェニルベンゾチアゾール、カルバゾール及びジベンゾチオフェンで構成される群より選択される少なくとも１種を含むことがより好ましい。
　本実施形態の重合体は、更なる高い耐熱性、エッチング耐性と溶解性との兼備の観点から、下記式（１Ｅ－３）で表されるモノマー由来の構成単位をさらに有することが好ましい。
Figure JPOXMLDOC01-appb-C000061
  
　式（１Ｅ－３）中、Ｑ４及びＱ５は、単結合、置換若しくは非置換の炭素数１～２０のアルキレン基、置換若しくは非置換の炭素数３～２０のシクロアルキレン基、置換若しくは非置換の炭素数６～２０のアリーレン基、置換若しくは非置換の炭素数２～２０のアルケニレン基、置換若しくは非置換の炭素数２～２０のアルキニレン基である。
　Ｑ６は、ＣＲｂ’で表される基であり、前記Ｒｂ’は、水素原子又は置換若しくは非置換の炭素数１～１０のアルキル基である。
　置換若しくは非置換の炭素数１～２０のアルキレン基、置換若しくは非置換の炭素数３～２０のシクロアルキレン基、置換若しくは非置換の炭素数６～２０のアリーレン基、置換若しくは非置換の炭素数２～２０のアルケニレン基、置換若しくは非置換の炭素数２～２０のアルキニレン基は、前記式（１Ｅ－２）の定義と同様である。
　本実施形態の重合体において、各構成単位の数と比は、特に限定されないが、用途や下記の分子量の値を考慮して適宜調整することが好ましい。また、本実施形態の重合体は、式（０）のみで構成することや上述の他の共重合可能な成分と共重合して構成することができるが、用途に応じた性能を損なわない範囲において、さらに他の構成単位を含むものであってもよい。さらに他の構成単位には、例えば、フェノール性水酸基が縮合することにより形成されるエーテル結合を有する構成単位や、ケトン構造を有する構成単位等が含まれる。上述のようにこれら他の構成単位も、式（０）で表されるモノマー由来の構成単位と、芳香環同士で直接結合していてもよい。
　本実施形態の重合体の重量平均分子量は、特に限定されないが、耐熱性及び溶解性兼備の点で、４００～１０００００の範囲であることが好ましく、５００～２００００であることがより好ましく、１０００～１５０００であることがさらに好ましい。
　重量平均分子量（Ｍｗ）と数平均分子量（Ｍｎ）との比（Ｍｗ／Ｍｎ）は、その用途に応じて求められる比も異なることから、特にその範囲が限定されるものではないが、より均質な分子量を有するものとして、例えば、好ましいものは３．０以下の範囲のものが挙げられ、より好ましいものは１．０５以上３．０以下の範囲のものが挙げられ、特に好ましいものとして１．０５以上２．０未満のものが挙げられ、耐熱性の観点から一層好ましいものとして１．０５以上１．５未満のものが挙げられる。
　本実施形態の重合体が有する構成単位の、該重合体中における結合順序は、特に限定されない。例えば、式（０）で表される一種のモノマーに由来するひとつの単位のみが構成単位として２以上含まれるものであってもよいし、式（０）で表される二種以上のモノマーに由来する複数の単位が、それぞれ１以上含まれるものであってもよい。その順序もブロック共重合或いはランダム共重合のいずれでも良い。
　本実施形態の重合体において「構成単位同士が、芳香環同士の直接結合によって連結している部位を有する」とは、一例として、重合体中の式（０）で表されるモノマー由来の構成単位（以下、単に「構成単位（０）」ということがある。）同士が、一方の構成単位（０）のベンゼン環上の炭素原子と、他方の構成単位（０）ベンゼン環上の炭素原子とが単結合にて結合されている、即ち、炭素原子、酸素原子、硫黄原子など他の原子を介さずに、直接結合されている部位を有する態様が挙げられる。この際、「構成単位同士が、芳香環同士の直接結合によって連結している部位を有する」態様には、本実施形態の重合体が芳香環を有し他の共重合可能な化合物に由来の構成単位を含む場合、構成単位（０）のベンゼン環と、他の共重合可能な化合物に由来の構成単位における芳香環とが単結合にて結合されている、即ち、炭素原子、酸素原子、硫黄原子など他の原子を介さずに、直接結合されている部位を有する態様も含まれる。
　本実施形態の重合体における構成単位同士が直接結合する位置としては、特に限定されず、置換基が結合していないいずれか一つの炭素原子がモノマー同士の直接結合に関与する。
　耐熱性の観点から、モノマーのいずれか一つの炭素原子が芳香環同士の直接結合に関与することが好ましい。換言すると、構成単位（０）や他の共重合可能な化合物に由来の構成単位が２以上の芳香環を有する場合、一つの構成単位に対して２つの構成単位が結合する場合、各構成単位中の２以上のアリール構造の各々において、他の構成単位と結合している構造が好ましい。２以上の芳香環の各々において他の構成単位と結合している場合、各芳香環において他の構成単位と結合している炭素原子の位置は、各々異なっていてもよいし、各々対応する箇所（例えば、各々４位の位置に結合しているなど）であってもよい。
　また、本実施形態の重合体においては、全ての構成単位（０）が他の構成単位（０）又は他の共重合可能な芳香環を有する化合物に由来する構成単位と、芳香環同士の直接結合によって結合されていることが好ましいが、酸素や炭素など他原子等を介して他の構成単位と結合している構成単位（０）が含まれていてもよい。特に限定されるものではないが、耐熱性及びエッチング耐性などの本実施形態の効果を十分に発揮する観点からは、本実施形態の重合体中の全構成単位（０）のうち、結合基準で、好ましくは４５％以上、より好ましくは６５％以上、さらに好ましくは８５％以上、特に好ましくは９０％以上の構成単位（０）が芳香環同士の直接結合によって他の構成単位（０）と結合していることが好ましい。さらに、本実施形態の重合体は、構成単位（０）同士が、芳香環同士の直接結合によって連結している部位を有することが、耐熱性の観点から好ましい。
　本実施形態の重合体は、湿式プロセスの適用がより容易になる等の観点から、溶媒に対する溶解性が高いものであることが好ましい。より具体的には、本実施形態の重合体は、プロピレングリコールモノメチルエーテル（ＰＧＭＥ）、プロピレングリコールモノメチルエーテルアセテート（ＰＧＭＥＡ）、シクロヘキサノン（ＣＨＮ）、シクロペンタノン（ＣＰＮ）、乳酸エチル（ＥＬ）及びヒドロキシイソ酪酸メチル（ＨＢＭ）で構成される群から選ばれる一種以上に対する溶解度が１質量％以上であることが好ましい。具体的には、２３℃の温度下で当該溶媒に対する溶解度が１質量％以上であることが好ましく、より好ましくは５質量％以上であり、さらに好ましくは１０質量％以上、特に好ましくは２０重量％以上、とりわけ好ましいのは３０重量％以上である。ここで、ＰＧＭＥ、ＰＧＭＥＡ、ＣＨＮ、ＣＰＮ、ＥＬ及び／又はＨＢＭに対する溶解度は、「重合体の質量÷（重合体の質量＋溶媒の質量）×１００（質量％）」と定義される。例えば、重合体１０ｇがＰＧＭＥＡ９０ｇに対して溶解すると評価されるのは、重合体のＰＧＭＥＡに対する溶解度が「１０質量％以上」となる場合であり、溶解しないと評価されるのは、当該溶解度が「１０質量％未満」となる場合である。
　本実施形態の重合体は、架橋反応性のある化合物に由来する変性部分をさらに有していてもよい。すなわち、前述した構造を有する本実施形態の重合体は、架橋反応性のある化合物との反応によって得られる変性部分を有していてもよい。このような（変性）重合体も、耐熱性、耐エッチング性に優れており、半導体用のコーティング剤、レジスト用材料、半導体下層膜形成材料として使用可能である。
　架橋反応性のある化合物としては、以下に限定されないが、例えば、アルデヒド類、ケトン類、カルボン酸類、カルボン酸ハライド類、ハロゲン含有化合物、アミノ化合物、イミノ化合物、イソシアネート化合物、不飽和炭化水素基含有化合物等が挙げられる。これらは単独で用いることもできるし適宜複数を併用することもできる。
　本実施形態において、架橋反応性のある化合物は、アルデヒド類又はケトン類であることが好ましい。より詳細には、前述した構造を有する本実施形態の重合体に対して、アルデヒド類又はケトン類を、触媒の存在下で重縮合反応させることによって得られる重合体であることが好ましい。例えば、常圧下、必要に応じて加圧下において、所望とする構造に対応するアルデヒド類又はケトン類とを触媒下にてさらに重縮合反応させることによって、ノボラック型の重合体を得ることができる。
　前記アルデヒド類としては、例えば、ホルムアルデヒド、パラホルムアルデヒド、トリオキサン、ベンズアルデヒド、メチルベンズアルデヒド、ジメチルベンズアルデヒド、トリメチルベンズアルデヒド、エチルベンズアルデヒド、プロピルベンズアルデヒド、ブチルベンズアルデヒド、ペンタベンズアルデヒド、ブチルメチルベンズアルデヒド、ヒドロキシベンズアルデヒド、ジヒドロキシベンズアルデヒド、フロロメチルベンズアルデヒド等が挙げられるが、これらに特に限定されない。これらは、１種を単独で、又は２種以上を組み合わせて使用することができる。これらのなかでも、ベンズアルデヒド、メチルベンズアルデヒド、ジメチルベンズアルデヒド、トリメチルベンズアルデヒド、エチルベンズアルデヒド、プロピルベンズアルデヒド、ブチルベンズアルデヒド、ペンタベンズアルデヒド、ブチルメチルベンズアルデヒド等を用いることが、高い耐熱性を与える観点から好ましい。
　前記ケトン類としては、例えば、アセトフェノン、アセチルメチルベンゼン、アセチルジメチルベンゼン、アセチルトリメチルベンゼン、アセチルエチルベンゼン、アセチルプロピルベンゼン、アセチルブチルベンゼン、アセチルペンタベンゼン、アセチルブチルメチルベンゼン、アセチルヒドロキシベンゼン、アセチルジヒドロキシベンゼン、アセチルフロロメチルベンゼン等が挙げられるが、これらに特に限定されない。これらは、１種を単独で、又は２種以上を組み合わせて使用することができる。これらのなかでも、アセトフェノン、アセチルメチルベンゼン、アセチルジメチルベンゼン、アセチルトリメチルベンゼン、アセチルエチルベンゼン、アセチルプロピルベンゼン、アセチルブチルベンゼン、アセチルペンタベンゼン、アセチルブチルメチルベンゼンを用いることが、高い耐熱性を与える観点から好ましい。
　前記反応に用いる触媒については、公知のものから適宜選択して用いることができ、特に限定されない。触媒としては、酸触媒や塩基触媒が好適に使用される。これら塩基触媒としては、ＰＣＴ／ＪＰ２０２１／２６６６９に記載の酸触媒や塩基触媒を用いることができる。
　なお、触媒については、１種を単独で、又は２種以上を組み合わせて用いることができる。また、触媒の使用量は、使用する原料及び使用する触媒の種類、さらには反応条件などに応じて適宜設定でき、特に限定されないが、反応原料１００質量部に対して、０．００１～１００質量部であることが好ましい。
　前記反応の際には、反応溶媒を用いてもよい。反応溶媒としては、用いるアルデヒド類或いはケトン類と重合体との反応が進行するものであれば、特に限定されず、公知のものの中から適宜選択して用いることができるが、例えば、水、メタノール、エタノール、プロパノール、ブタノール、テトラヒドロフラン、ジオキサン、エチレングリコールジメチルエーテル、エチレングリコールジエチルエーテル又はこれらの混合溶媒等が例示される。なお、溶媒は、１種を単独で、或いは２種以上を組み合わせて用いることができる。また、これらの溶媒の使用量は、使用する原料及び使用する酸触媒の種類、さらには反応条件などに応じて適宜設定できる。前記溶媒の使用量としては、特に限定されないが、反応原料１００質量部に対して０～２０００質量部の範囲であることが好ましい。さらに、前記反応における反応温度は、反応原料の反応性に応じて適宜選択することができる。前記反応温度としては、特に限定されないが、通常１０～２００℃の範囲であることが好ましい。なお、反応方法は、公知の手法を適宜選択して用いることができ、特に限定されないが、本実施形態の重合体、アルデヒド類或いはケトン類、酸触媒を一括で仕込む方法や、アルデヒド類或いはケトン類を酸触媒存在下で滴下していく方法がある。重縮合反応終了後、得られた化合物の単離は、常法にしたがって行うことができ、特に限定されない。例えば、系内に存在する未反応原料や酸触媒等を除去するために、反応釜の温度を１３０～２３０℃にまで上昇させ、１～５０ｍｍＨｇ程度で揮発分を除去する等の一般的手法を採ることにより、目的物である化合物を得ることができる。
［重合体の製造方法］
　本実施形態の重合体の製造方法としては、以下に限定されないが、例えば、１種又は２種以上の前記モノマーを酸化剤の存在下で重合させる工程を含むものとすることができる。具体的には、１種又は２種以上の前記式（０）で表されるモノマーを酸化剤の存在下で重合させる工程を含む。また、本実施形態の重合体が、上述の他の共重合可能な化合物に由来の構成単位を含む場合、前記製造方法は、１種又は２種以上の前記式（０）で表されるモノマーと、前記式（０）で表されるモノマーと共重合可能な、他の共重合可能な化合物と、を酸化剤の存在下で重合させる工程を含んでいてもよい。
　かかる工程を実施するに際しては、Ｋ．　Ｍａｔｓｕｍｏｔｏ，　Ｙ．　Ｓｈｉｂａｓａｋｉ，　Ｓ．　Ａｎｄｏ　ａｎｄ　Ｍ．　Ｕｅｄａ，　Ｐｏｌｙｍｅｒ，　４７，　３０４３　（２００６）の内容を適宜参照することができる。すなわち、β－ナフトール型モノマーの酸化重合においては、そのモノマーに起因して一電子酸化されたラジカルがカップリングする酸化カップリング反応により、α－位のＣ－Ｃカップリングが選択的に生じるとされており、例えば、銅／ジアミン型触媒を用いることで、位置選択的重合を行うことができる。
　本実施形態における酸化剤としては、酸化カップリング反応を生ずるものであれば特に限定されないが、銅、マンガン、鉄、コバルト、ルテニウム、クロム、ニッケル、スズ、鉛、銀若しくはパラジウムなどを含有する金属塩類、過酸化水素又は過塩素酸類などの過酸化物、有機過酸化物が用いられる。これらの中でも銅、マンガン、鉄、コバルト、ルテニウム、クロム、ニッケル、スズ、鉛、銀及びパラジウムで構成される群から選択される少なくとも１種を含有する金属塩類又は金属錯体を好ましく用いることができる。
　銅、マンガン、鉄、コバルト、ルテニウム、鉛、ニッケル、銀、スズ、クロム若しくはパラジウムなどの金属は、反応系中で還元することにより酸化剤として使用することもできる。これらは金属塩類に含まれる。
　例えば、前記式（０）で表されるモノマーを有機溶媒に溶解又は分散させ、さらに銅、マンガン又はコバルトを含有する金属塩類を添加し、例えば酸素又は酸素含有気体と反応させて酸化重合することにより、所望の重合体を得ることができる。
　上述のような酸化重合による重合体の製造方法によれば、分子量制御が比較的容易であり、高分子量化に伴う原料モノマーや低分子成分を残さずに分子量分布の小さい重合体を得ることができるため、高耐熱性や低昇華物の観点から優位となる傾向にある。
　その他の製造方法としては、例えば、グリニャール試薬を用いたカップリング反応、鈴木・宮原カップリング反応等が挙げられる。
　金属塩類としては、以下に限定されないが、例えば、銅、マンガン、コバルト、ルテニウム、クロム、パラジウムなどのハロゲン化物、炭酸塩、酢酸塩、硝酸塩、フタル酸塩、若しくはリン酸塩を用いることができる。
　金属錯体としては、特に限定されず、公知のものを用いることができ。その具体例としては、以下に限定されないが、銅を含有する錯体触媒は、特公昭３６－１８６９２号、同４０－１３４２３号、特開昭４９－４９０号等各公報に記載の触媒が挙げられ、マンガンを含有する錯体触媒は、特公昭４０－３０３５４号、同４７－５１１１号、特開昭５６－３２５２３号、同５７－４４６２５号、同５８－１９３２９号、同６０－８３１８５号等各公報に記載の触媒が挙げられ、コバルトを含有する錯体触媒は、特公昭４５－２３５５５号公報に記載の触媒が挙げられる。
　有機過酸化物の例としては、以下に限定されないが、ｔ－ブチルハイドロパーオキサイド、ジ－ｔ－ブチルパーオキサイド、クメンハイドロパーオキサイド、ジクミルパーオキサイド、過酢酸、過安息香酸等を示すことができる。
　前記酸化剤は、単独で又は混合して用いることができる。これらの使用量は特に限定されないが、式（０）で表されるモノマー（他の共重合可能なモノマーを併用する場合には、式（０）で表されるモノマーと他の共重合可能なモノマーとの総量）１モルに対して０．００２モルから１０モルであることが好ましく、より好ましくは０．００３モルから３モルであり、さらに好ましくは０．００５モルから０．３モルである。すなわち、本実施形態における酸化剤は、モノマーに対して低濃度で使用できる。
　本実施形態においては、酸化重合する工程で用いられる酸化剤の他に塩基を使用することが好ましい。塩基としては、特に限定されず、公知のものを用いることができ、その具体例としては、アルカリ金属の水酸化物、アルカリ土類金属の水酸化物、アルカリ金属のアルコキサイドなどの無機塩基や、１級～３級モノアミン化合物、ジアミンなどの有機塩基であってもよい。それぞれ単独で又は組み合わせて使用することができる。
　酸化の方法については、特に限定されず、直接酸素ガス或いは空気を使用する方法があるが、安全性及びコスト面からは空気酸化が好ましい。大気圧下で空気を用いて酸化する場合、酸化重合の速度向上及び重合体の高分子量化の観点から反応溶媒中において、液中へのバブリングによって空気を導入する方法が好ましい。
　また、本実施形態における酸化反応は加圧下での反応とすることも可能であり、反応促進の観点から２ｋｇ／ｃｍ２～１５ｋｇ／ｃｍ２が好ましく、安全面と制御性の観点から３ｋｇ／ｃｍ２～１０ｋｇ／ｃｍ２がさらに好ましい。
　本実施形態において、モノマーの酸化反応は反応溶媒の不存在下においても行うことができるが、一般には溶媒の存在下に反応を行うことが好ましい。溶媒は、本実施形態の重合体を得る上で支障が無い限り、触媒をある程度溶解するものであれば種々公知の溶媒が使用できる。一般的には、メタノール、エタノール、プロパノール、ブタノールなどアルコール類、ジオキサン、テトラヒドロフラン又はエチレングリコールジメチルエーテルなどのエーテル類；アミド類又はニトリル類などの溶媒；アセトン、メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン、シクロペンタノンなどのケトン類；又はそれらと水とを混合して用いられる。また、水と混ざらないベンゼン、トルエン若しくはヘキサンなどの炭化水素類又はそれらと水との２相系で反応を行うことができる。
　また、反応条件は、基質濃度、酸化剤の種類及び濃度に応じて適宜調整すればよいが、反応温度は比較的低温に設定することができ、５～１５０℃とすることが好ましく、２０～１２０℃とすることがより好ましい。反応時間は３０分間～２４時間が好ましく、１時間～２０時間がより好ましい。また、反応時の撹拌方法は特に限定されず、振盪、回転子又は攪拌翼を用いた攪拌のいずれでもよい。本工程は、上述の条件を満たす攪拌条件であれば、溶媒中又は気流中のいずれでもよい。
［組成物］
　本実施形態の重合体は、種々の用途を想定し、組成物として使用することができる。すなわち、本実施形態の組成物は、本実施形態の重合体を含む。本実施形態の組成物は、湿式プロセスの適用によって膜形成が容易になる等の観点から、溶媒をさらに含むことが好ましい。
　溶媒の具体例としては、特に限定されないが、例えば、アセトン、メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン等のケトン系溶媒；プロピレングリコールモノメチルエーテル、プロピレングリコールモノメチルエーテルアセテート等のセロソルブ系溶媒；乳酸エチル、酢酸メチル、酢酸エチル、酢酸ブチル、酢酸イソアミル、メトキシプロピオン酸メチル、ヒドロキシイソ酪酸メチル等のエステル系溶媒；メタノール、エタノール、イソプロパノール、１－エトキシ－２－プロパノール等のアルコール系溶媒；トルエン、キシレン、アニソール等の芳香族系炭化水素等が挙げられる。これらの溶媒は、１種を単独で、或いは２種以上を組み合わせて用いることができる。
　前記溶媒の中で、安全性の点から、プロピレングリコールモノメチルエーテル、プロピレングリコールモノメチルエーテルアセテート、シクロヘキサノン、シクロペンタノン、乳酸エチル及びヒドロキシイソ酪酸メチルで構成される群から選ばれる１種以上が特に好ましい。
　本実施形態の組成物における溶媒の含有量は、特に限定されないが、溶解性及び製膜上の観点から、本実施形態の重合体１００質量部に対して、１００～１０，０００質量部であることが好ましく、２００～５，０００質量部であることがより好ましく、２００～１，０００質量部であることがさらに好ましい。
　本実施形態の重合体は、前記した酸化反応によって粗体として得た後、さらに精製を実施することにより、残留する酸化剤を除去したものであることが好ましい。具体的には、経時的な重合体の変質の防止及び保存安定性の観点から、酸化剤に由来する金属酸化剤として主に使用される銅、マンガン、鉄若しくはコバルトを含有する金属塩類又は金属錯体などの残留を避けることが好ましい。すなわち、本実施形態の組成物は、不純物金属の含有量が金属種毎に５００ｐｐｂ未満であることが好ましく、１ｐｐｂ以下であることがさらに好ましい。また、前記不純物金属としては、特に限定はないが、銅、マンガン、鉄、コバルト、ルテニウム、クロム、ニッケル、スズ、鉛、銀及びパラジウムで構成される群で構成されるより選択される群から選ばれる少なくとも１種が挙げられる。
　前記酸化剤由来の金属残留量（不純物金属の含有量）が５００ｐｐｂ未満であることにより、溶液形態においても、保存安定性が損なわれることなく使用できる傾向にある。
　精製方法としては、特に限定はされないが、重合体を、溶媒に溶解させて溶液（Ｓ）を得る工程と、得られた溶液（Ｓ）と酸性の水溶液とを接触させて、前記重合体中の不純物を抽出する工程（第一抽出工程）とを含み、前記溶液（Ｓ）を得る工程で用いる溶媒が、水と任意に混和しない有機溶媒を含む精製方法が挙げられる。
　前記精製方法によれば、重合体に不純物として含まれ得る種々の金属の含有量を低減することができる。
　より詳細には、前記重合体を、水と任意に混和しない有機溶媒に溶解させて溶液（Ｓ）を得て、さらにその溶液（Ｓ）を酸性水溶液と接触させて抽出処理を行うことができる。これにより、前記溶液（Ｓ）に含まれる金属分を水相に移行させたのち、有機相と水相とを分離して金属含有量の低減された重合体を得ることができる。
　前記精製方法で使用される水と任意に混和しない溶媒としては、特に限定されないが、半導体製造プロセスに安全に適用できる有機溶媒が好ましく、具体的には、室温下における水への溶解度が３０％未満である有機溶媒であり、より好ましくは２０％未満であり、特に好ましくは１０％未満である有機溶媒が好ましい。当該有機溶媒の使用量は、使用する重合体の合計量に対して、１～１００質量倍であることが好ましい。
　水と任意に混和しない溶媒の具体例としては、以下に限定されないが、例えば、ジエチルエーテル、ジイソプロピルエーテル等のエーテル類、酢酸エチル、酢酸ｎ－ブチル、酢酸イソアミル等のエステル類、メチルエチルケトン、メチルイソブチルケトン、エチルイソブチルケトン、シクロヘキサノン、シクロペンタノン、２－ヘプタノン、２－ペンタノン等のケトン類；エチレングリコールモノエチルエーテルアセテート、エチレングリコールモノブチルエーテルアセテート、プロピレングリコールモノメチルエーテルアセテート（ＰＧＭＥＡ）、プロピレングリコールモノエチルエーテルアセテート等のグリコールエーテルアセテート類；ｎ－ヘキサン、ｎ－ヘプタン等の脂肪族炭化水素類；トルエン、キシレン等の芳香族炭化水素類；塩化メチレン、クロロホルム等のハロゲン化炭化水素類等が挙げられる。これらの中でも、トルエン、２－ヘプタノン、シクロヘキサノン、シクロペンタノン、メチルイソブチルケトン、プロピレングリコールモノメチルエーテルアセテート、酢酸エチル等が好ましく、メチルイソブチルケトン、酢酸エチル、シクロヘキサノン、プロピレングリコールモノメチルエーテルアセテートがより好ましく、メチルイソブチルケトン、酢酸エチルがよりさらに好ましい。メチルイソブチルケトン、酢酸エチル等は、重合体の飽和溶解度が比較的高く、沸点が比較的低いことから、工業的に溶媒を留去する場合や乾燥により除去する工程での負荷を低減することが可能となる。これらの溶媒はそれぞれ単独で用いることもできるし、また２種以上を混合して用いることもできる。
　前記精製方法で使用される酸性の水溶液としては、一般に知られる有機系化合物若しくは無機系化合物を水に溶解させた水溶液の中から適宜選択される。以下に限定されないが、例えば、塩酸、硫酸、硝酸、リン酸等の鉱酸を水に溶解させた鉱酸水溶液、又は、酢酸、プロピオン酸、蓚酸、マロン酸、コハク酸、フマル酸、マレイン酸、酒石酸、クエン酸、メタンスルホン酸、フェノールスルホン酸、ｐ－トルエンスルホン酸、トリフルオロ酢酸等の有機酸を水に溶解させた有機酸水溶液が挙げられる。これら酸性の水溶液は、それぞれ単独で用いることもできるし、また２種以上を組み合わせて用いることもできる。これら酸性の水溶液の中でも、塩酸、硫酸、硝酸及びリン酸で構成される群から選ばれる１種以上の鉱酸水溶液、又は、酢酸、プロピオン酸、蓚酸、マロン酸、コハク酸、フマル酸、マレイン酸、酒石酸、クエン酸、メタンスルホン酸、フェノールスルホン酸、ｐ－トルエンスルホン酸及びトリフルオロ酢酸で構成される群から選ばれる１種以上の有機酸水溶液であることが好ましく、硫酸、硝酸、及び酢酸、蓚酸、酒石酸、クエン酸等のカルボン酸の水溶液がより好ましく、硫酸、蓚酸、酒石酸、クエン酸の水溶液がさらに好ましく、蓚酸の水溶液がよりさらに好ましい。蓚酸、酒石酸、クエン酸等の多価カルボン酸は金属イオンに配位し、キレート効果が生じるために、より効果的に金属を除去できる傾向にあるものと考えられる。また、ここで用いる水は、本実施形態における精製方法の目的に沿って、金属含有量の少ない水、例えばイオン交換水等を用いることが好ましい。
　前記精製方法で使用する酸性の水溶液のｐＨは特に限定されないが、前記重合体への影響を考慮し、水溶液の酸性度を調整することが好ましい。通常、ｐＨ範囲は０～５程度であり、好ましくはｐＨ０～３程度である。
　前記精製方法で使用する酸性の水溶液の使用量は特に限定されないが、金属除去のための抽出回数を低減する観点及び全体の液量を考慮して操作性を確保する観点から、当該使用量を調整することが好ましい。前記観点から、酸性の水溶液の使用量は、前記溶液（Ｓ）１００質量部に対して、好ましくは１０～２００質量部であり、より好ましくは２０～１００質量部である。
　前記精製方法においては、前記酸性の水溶液と、前記溶液（Ｓ）とを接触させることにより、溶液（Ｓ）中の前記重合体から金属分を抽出することができる。
　前記精製方法においては、前記溶液（Ｓ）が、さらに水と任意に混和する有機溶媒を含むこともできる。水と任意に混和する有機溶媒を含む場合、前記重合体の仕込み量を増加させることができ、また、分液性が向上し、高い釜効率で精製を行うことができる傾向にある。水と任意に混和する有機溶媒を加える方法は特に限定されない。例えば、予め有機溶媒を含む溶液に加える方法、予め水又は酸性の水溶液に加える方法、有機溶媒を含む溶液と水又は酸性の水溶液とを接触させた後に加える方法のいずれでもよい。これらの中でも、予め有機溶媒を含む溶液に加える方法が操作の作業性や仕込み量の管理のし易さの点で好ましい。
　前記精製方法で使用される水と任意に混和する有機溶媒としては、特に限定されないが、半導体製造プロセスに安全に適用できる有機溶媒が好ましい。水と任意に混和する有機溶媒の使用量は、溶液相と水相とが分離する範囲であれば特に限定されないが、使用する重合体の合計量に対して、０．１～１００質量倍であることが好ましく、０．１～５０質量倍であることがより好ましく、０．１～２０質量倍であることがさらに好ましい。
　前記精製方法において使用される水と任意に混和する有機溶媒の具体例としては、以下に限定されないが、テトラヒドロフラン、１，３－ジオキソラン等のエーテル類；メタノール、エタノール、イソプロパノール等のアルコール類；アセトン、Ｎ－メチルピロリドン等のケトン類；エチレングリコールモノエチルエーテル、エチレングリコールモノブチルエーテル、プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル等のグリコールエーテル類等の脂肪族炭化水素類が挙げられる。これらの中でも、Ｎ－メチルピロリドン、プロピレングリコールモノメチルエーテル等が好ましく、Ｎ－メチルピロリドン、プロピレングリコールモノメチルエーテルがより好ましい。これらの溶媒はそれぞれ単独で用いることもできるし、また２種以上を混合して用いることもできる。
　抽出処理を行う際の温度は通常、２０～９０℃であり、好ましくは３０～８０℃の範囲である。抽出操作は、例えば、撹拌等により、よく混合させたあと、静置することにより行われる。これにより、溶液（Ｓ）中に含まれていた金属分が水相に移行する。また、本操作により、溶液の酸性度が低下し、前記重合体の変質を抑制することができる。
　前記混合溶液は静置により、重合体と溶媒とを含む溶液相と、水相とに分離するので、デカンテーション等により、溶液相を回収する。静置する時間は特に限定されないが、溶媒を含む溶液相と水相との分離をより良好にする観点から、当該静置する時間を調整することが好ましい。通常、静置する時間は１分間以上であり、好ましくは１０分間以上であり、より好ましくは３０分間以上である。また、抽出処理は１回だけでもかまわないが、混合、静置、分離という操作を複数回繰り返して行うのも有効である。
　前記精製方法において、第一抽出工程後、前記重合体を含む溶液相を、さらに水に接触させて、前記重合体中の不純物を抽出する工程（第二抽出工程）を含むことが好ましい。具体的には、例えば、酸性の水溶液を用いて前記抽出処理を行った後に、該水溶液から抽出され、回収された重合体と溶媒を含む溶液相を、さらに水による抽出処理に供することが好ましい。上述の水による抽出処理は、特に限定されないが、例えば、前記溶液相と水とを、撹拌等により、よく混合させたあと、得られた混合溶液を、静置することにより行うことができる。当該静置後の混合溶液は、前記重合体と溶媒とを含む溶液相と、水相とに分離するのでデカンテーション等により、溶液相を回収することができる。
　また、ここで用いる水は、本実施形態の目的に沿って、金属含有量の少ない水、例えば、イオン交換水等であることが好ましい。抽出処理は１回だけでもかまわないが、混合、静置、分離という操作を複数回繰り返して行うのも有効である。また、抽出処理における両者の使用割合や、温度、時間等の条件は特に限定されないが、先の酸性の水溶液との接触処理の場合と同様で構わない。
　こうして得られた重合体と溶媒とを含む溶液に混入しうる水分については、減圧蒸留等の操作を施すことにより容易に除去できる。また、必要により前記溶液に溶媒を加え、重合体の濃度を任意の濃度に調整することができる。
　本実施形態に係る重合体の精製方法は、前記重合体を溶媒に溶解させた溶液をフィルターに通液することにより精製することもできる。
　本実施形態に係る重合体の精製方法によれば、前記重合体中の種々の金属分の含有量を効果的に著しく低減することができる。これらの金属成分量は後述する実施例に記載の方法で測定することができる。
　なお、本実施形態における「通液」とは、前記溶液がフィルターの外部から当該フィルターの内部を通過して再度フィルターの外部へと移動することを意味し、例えば、前記溶液を単にフィルターの表面で接触させる態様や、前記溶液を当該表面上で接触させつつイオン交換樹脂の外部で移動させる態様（すなわち、単に接触する態様）は除外される。
［フィルター精製工程（通液工程）］
　本実施形態におけるフィルター通液工程において、前記重合体と溶媒とを含む溶液中の金属分の除去に用いられるフィルターは、通常、液体ろ過用として市販されているものを使用することができる。フィルターの濾過精度は特に限定されないが、フィルターの公称孔径は０．２μｍ以下であることが好ましく、より好ましくは０．２μｍ未満であり、さらに好ましくは０．１μｍ以下であり、よりさらに好ましくは０．１μｍ未満であり、一層好ましくは０．０５μｍ以下である。また、フィルターの公称孔径の下限値は、特に限定されないが、通常、０．００５μｍである。ここでいう公称孔径とは、フィルターの分離性能を示す名目上の孔径であり、例えば、バブルポイント試験、水銀圧入法試験、標準粒子補足試験など、フィルターの製造元により決められた試験法により決定される孔径である。市販品を用いた場合、製造元のカタログデータに記載の値である。公称孔径を０．２μｍ以下にすることで、溶液を１回フィルターに通液させた後の金属分の含有量を効果的に低減することができる。本実施形態においては、溶液の各金属分の含有量をより低減させるために、フィルター通液工程を２回以上行ってもよい。
　フィルターの形態としては、中空糸膜フィルター、メンブレンフィルター、プリーツ膜フィルター、並びに不織布、セルロース、及びケイソウ土などの濾材を充填したフィルターなどを用いることができる。前記した中でも、フィルターが、中空糸膜フィルター、メンブレンフィルター及びプリーツ膜フィルターで構成される群から選ばれる１種以上であることが好ましい。また、特に高精細な濾過精度と他の形態と比較した濾過面積の高さから、中空糸膜フィルターを用いることが特に好ましい。
　前記フィルターの材質は、ポリエチレン、ポリプロピレン等のポリオレフィン、グラフト重合によるイオン交換能を有する官能基を施したポリエチレン系樹脂、ポリアミド、ポリエステル、ポリアクリロニトリルなどの極性基含有樹脂、フッ化ポリエチレン（ＰＴＦＥ）などのフッ素含有樹脂を挙げることができる。前記した中でも、フィルターの濾材が、ポリアミド製、ポレオレフィン樹脂製及びフッ素樹脂製で構成される群から選ばれる１種以上であることが好ましい。また、クロム等の重金属の低減効果の観点からポリアミドが特に好ましい。なお、濾材からの金属溶出を避ける観点から、焼結金属材質以外のフィルターを用いることが好ましい。
　ポリアミド系フィルターとしては、以下（以下、登録商標）に限定されないが、例えば、キッツマイクロフィルター（株）製のポリフィックスナイロンシリーズ、日本ポール（株）製のウルチプリーツＰ－ナイロン６６、ウルチポアＮ６６、スリーエム（株）製のライフアシュアＰＳＮシリーズ、ライフアシュアＥＦシリーズなどを挙げることができる。
　ポリオレフィン系フィルターとしては、以下に限定されないが、例えば、日本ポール（株）製のウルチプリーツＰＥクリーン、イオンクリーン、日本インテグリス（株）製のプロテゴシリーズ、マイクロガードプラスＨＣ１０、オプチマイザーＤ等を挙げることができる。
　ポリエステル系フィルターとしては、以下に限定されないが、例えば、セントラルフィルター工業（株）製のジェラフローＤＦＥ、日本フィルター（株）製のブリーツタイプＰＭＣ等を挙げることができる。
　ポリアクリロニトリル系フィルターとしては、以下に限定されないが、例えば、アドバンテック東洋（株）製のウルトラフィルターＡＩＰ－００１３Ｄ、ＡＣＰ－００１３Ｄ、ＡＣＰ－００５３Ｄ等を挙げることができる。
　フッ素樹脂系フィルターとしては、以下に限定されないが、例えば、日本ポール（株）製のエンフロンＨＴＰＦＲ、スリーエム（株）製のライフシュアＦＡシリーズ等を挙げることができる。
　これらのフィルターはそれぞれ単独で用いても２種類以上を組み合わせて用いてもよい。
　また、前記フィルターには陽イオン交換樹脂などのイオン交換体や、濾過される有機溶媒溶液にゼータ電位を生じさせるカチオン電荷調節剤などが含まれていてもよい。
　イオン交換体を含むフィルターとして、以下に限定されないが、例えば、日本インテグリス（株）製のプロテゴシリーズ、倉敷繊維加工（株）製のクラングラフト等を挙げることができる。
　また、ポリアミドポリアミンエピクロロヒドリンカチオン樹脂などの正のゼータ電位を有する物質を含むフィルターとしては（以下、登録商標）、以下に限定されないが、例えば、スリーエム（株）製ゼータプラス４０ＱＳＨやゼータプラス０２０ＧＮ、或いはライフアシュアＥＦシリーズ等が挙げられる。
　得られた重合体と溶媒とを含む溶液から、重合体を単離する方法は、特に限定されず、減圧除去、再沈殿による分離、及びそれらの組み合わせ等、公知の方法で行うことができる。必要に応じて、濃縮操作、ろ過操作、遠心分離操作、乾燥操作等の公知の処理を行うことができる。
［膜形成用組成物］
　本実施形態の組成物は、膜形成用途に使用できる。すなわち、本実施形態の膜形成用組成物は、本実施形態の重合体を含有するため、優れた耐熱性及びエッチング耐性を発揮できる。
　本明細書における「膜」とは、例えば、リソグラフィー用膜や光学部材等（ただし、これらに限定されるものではない。）に適用されうるものを意味し、そのサイズや形状は特に限定されず、典型的には、リソグラフィー用膜や光学部材として一般的な形態を有するものである。すなわち、「膜形成用組成物」とは、このような膜の前駆体であり、その形態及び／又は組成において、当該「膜」とは明確に区別されるものである。また、「リソグラフィー用膜」とは、例えば、レジスト用永久膜、リソグラフィー用下層膜等のリソグラフィー用途の膜を広く包含する概念である。
［膜形成用組成物の用途］
　本実施形態の膜形成用組成物は、上述した重合体を含有するものであるが、その具体的な用途に応じて様々な組成とすることができ、その用途ないし組成に応じ、以下では「レジスト組成物」、「感放射線性組成物」、「リソグラフィー用下層膜形成用組成物」と称する場合がある。
［レジスト組成物］
　本実施形態のレジスト組成物は、本実施形態の膜形成用組成物を含む。すなわち、本実施形態のレジスト組成物は、本実施形態の重合体を必須成分として含有するものであり、レジスト材料として用いられることを考慮し、種々の任意成分をさらに含有することができる。具体的には、本実施形態のレジスト組成物は、溶媒、酸発生剤、塩基発生剤及び酸拡散制御剤で構成される群から選択される少なくとも１つをさらに含有することが好ましい。
（溶媒）
　また、本実施形態のレジスト組成物が含みうる溶媒としては、特に限定されず、種々公知の有機溶媒を用いることができる。例えば、国際公開第２０１３／０２４７７８号に記載のものを用いることができる。これらの溶媒は、単独で又は２種以上を使用することができる。
　本実施形態で使用される溶媒は、安全溶媒であることが好ましく、より好ましくは、ＰＧＭＥＡ（プロピレングリコールモノメチルエーテルアセテート）、ＰＧＭＥ（プロピレングリコールモノメチルエーテル）、ＣＨＮ（シクロヘキサノン）、ＣＰＮ（シクロペンタノン）、２－ヘプタノン、アニソール、酢酸ブチル、プロピオン酸エチル及び乳酸エチルから選ばれる少なくとも１種であり、さらに好ましくはＰＧＭＥＡ、ＰＧＭＥ及びＣＨＮから選ばれる少なくとも１種である。
　本実施形態において固形成分（本実施形態のレジスト組成物において溶媒以外の成分）の量と溶媒との量は、特に限定されないが、固形成分の量と溶媒との合計質量１００質量部に対して、固形成分１～８０質量部及び溶媒２０～９９質量部であることが好ましく、より好ましくは固形成分１～５０質量部及び溶媒５０～９９質量部、さらに好ましくは固形成分２～４０質量部及び溶媒６０～９８質量部であり、特に好ましくは固形成分２～１０質量部及び溶媒９０～９８質量部である。
（酸発生剤（Ｃ））
　本実施形態のレジスト組成物において、可視光線、紫外線、エキシマレーザー、電子線、極端紫外線（ＥＵＶ）、Ｘ線及びイオンビームから選ばれるいずれかの放射線の照射により直接的又は間接的に酸を発生する酸発生剤（Ｃ）を一種以上含むことが好ましい。酸発生剤（Ｃ）は、特に限定されないが、例えば、国際公開第２０１３／０２４７７８号に記載のものを用いることができる。酸発生剤（Ｃ）は、単独で又は２種以上を使用することができる。
　酸発生剤（Ｃ）の使用量は、固形成分全質量の０．００１～４９質量％が好ましく、１～４０質量％がより好ましく、３～３０質量％がさらに好ましく、１０～２５質量％が特に好ましい。前記範囲内で使用することにより、高感度でかつ低エッジラフネスのパターンプロファイルが得られる。本実施形態では、系内に酸が発生すれば、酸の発生方法は限定されない。ｇ線、ｉ線などの紫外線の代わりにエキシマレーザーを使用すれば、より微細加工が可能であるし、また高エネルギー線として電子線、極端紫外線、Ｘ線、イオンビームを使用すればさらに微細加工が可能である。
（塩基発生剤（Ｂ））
　塩基発生剤（Ｂ）が光塩基発生剤である場合について説明する。
　光塩基発生剤とは、露光により塩基を発生するものであり、常温常圧の通常の条件下では活性を示さないが、外部刺激として電磁波の照射と加熱が行なわれると、塩基（塩基性物質）を発生するものであれば特に限定されるものではない。
　本発明に用いることができる光塩基発生剤は、特に限定されず公知のものを用いることができ、例えば、カルバメート誘導体、アミド誘導体、イミド誘導体、αコバルト錯体類、イミダゾール誘導体、桂皮酸アミド誘導体、オキシム誘導体等が挙げられる。
　光塩基発生剤から発生される塩基性物質としては特に限定されないが、アミノ基を有する化合物、特にモノアミンや、ジアミンなどのポリアミン、また、アミジンなどが挙げられる。
　発生される塩基性物質は、より塩基性度の高い（共役酸のｐＫａ値が高い）アミノ基を有する化合物が感度及び解像性の観点から好ましい。
　光塩基発生剤としては、例えば、特開２００９－８０４５２号公報及び国際公開第２００９／１２３１２２号パンフレットで開示されたような桂皮酸アミド構造を有する塩基発生剤、特開２００６－１８９５９１号公報及び特開２００８－２４７７４７号公報で開示されたようなカルバメート構造を有する塩基発生剤、特開２００７－２４９０１３号公報及び特開２００８－００３５８１号公報で開示されたようなオキシム構造、カルバモイルオキシム構造を有する塩基発生剤、特開２０１０－２４３７７３号公報に記載の化合物等が挙げられるが、これらに限定されず、その他にも公知の塩基発生剤の構造を用いることができる。
　光塩基発生剤は、１種類単独で又は２種類以上を組み合わせて使用することができる。
　光塩基発生剤の感活性光線性又は感放射線性樹脂組成物中の好ましい含有量は、前述の光酸発生剤の感活性光線性又は感放射線性樹脂組成物中の好ましい含有量と同様である。
（酸架橋剤（Ｇ））
　本実施形態においてレジスト組成物は、酸架橋剤（Ｇ）を一種以上含むことができる。酸架橋剤（Ｇ）とは、酸発生剤（Ｃ）から発生した酸の存在下で、本実施形態の重合体（成分（Ａ））を分子内又は分子間架橋し得る化合物である。このような酸架橋剤（Ｇ）としては、例えば成分（Ａ）を架橋し得る１種以上の基（以下、「架橋性基」という。）を有する化合物を挙げることができる。
　このような架橋性基としては、特に限定されないが、例えば（ｉ）ヒドロキシ（Ｃ１－Ｃ６アルキル基）、Ｃ１－Ｃ６アルコキシ（Ｃ１－Ｃ６アルキル基）、アセトキシ（Ｃ１－Ｃ６アルキル基）等のヒドロキシアルキル基又はそれらから誘導される基；（ｉｉ）ホルミル基、カルボキシ（Ｃ１－Ｃ６アルキル基）等のカルボニル基又はそれらから誘導される基；（ｉｉｉ）ジメチルアミノメチル基、ジエチルアミノメチル基、ジメチロールアミノメチル基、ジエチロールアミノメチル基、モルホリノメチル基等の含窒素基含有基；（ｉｖ）グリシジルエーテル基、グリシジルエステル基、グリシジルアミノ基等のグリシジル基含有基；（ｖ）ベンジルオキシメチル基、ベンゾイルオキシメチル基等の、Ｃ１－Ｃ６アリルオキシ（Ｃ１－Ｃ６アルキル基）、Ｃ１－Ｃ６アラルキルオキシ（Ｃ１－Ｃ６アルキル基）等の芳香族基から誘導される基；（ｖｉ）ビニル基、イソプロペニル基等の重合性多重結合含有基等を挙げることができる。本実施形態における酸架橋剤（Ｇ）の架橋性基としては、ヒドロキシアルキル基、及びアルコキシアルキル基等が好ましく、特にアルコキシメチル基が好ましい。
　前記架橋性基を有する酸架橋剤（Ｇ）としては、特に限定されないが、例えば、国際公開第２０１３／０２４７７８号に記載のものを用いることができる。酸架橋剤（Ｇ）は単独で又は２種以上を使用することができる。
　本実施形態において酸架橋剤（Ｇ）の使用量は、固形成分全質量の０．５～４９質量％が好ましく、０．５～４０質量％がより好ましく、１～３０質量％がさらに好ましく、２～２０質量％が特に好ましい。前記酸架橋剤（Ｇ）の配合割合を０．５質量％以上とすると、レジスト膜のアルカリ現像液に対する溶解性の抑制効果を向上させ、残膜率が低下したり、パターンの膨潤や蛇行が生じたりするのを抑制することができるので好ましく、一方、５０質量％以下とすると、レジストとしての耐熱性の低下を抑制できることから好ましい。
（酸拡散制御剤（Ｅ））
　本実施形態においては、放射線照射により酸発生剤から生じた酸のレジスト膜中における拡散を制御して、未露光領域での好ましくない化学反応を阻止する作用等を有する酸拡散制御剤（Ｅ）をレジスト組成物に配合してもよい。この様な酸拡散制御剤（Ｅ）を使用することにより、レジスト組成物の貯蔵安定性が向上する。また解像度が向上するとともに、放射線照射前の引き置き時間、放射線照射後の引き置き時間の変動によるレジストパターンの線幅変化を抑えることができ、プロセス安定性に極めて優れたものとなる。このような酸拡散制御剤（Ｅ）としては、特に限定されないが、例えば、窒素原子含有塩基性化合物、塩基性スルホニウム化合物、塩基性ヨードニウム化合物等の放射線分解性塩基性化合物が挙げられる。
　前記酸拡散制御剤（Ｅ）としては、特に限定されないが、例えば、国際公開第２０１３／０２４７７８号に記載のものを用いることができる。酸拡散制御剤（Ｅ）は、単独で又は２種以上を使用することができる。
　酸拡散制御剤（Ｅ）の配合量は、固形成分全質量の０．００１～４９質量％が好ましく、０．０１～１０質量％がより好ましく、０．０１～５質量％がさらに好ましく、０．０１～３質量％が特に好ましい。前記範囲内であると、解像度の低下、パターン形状、寸法忠実度等の劣化を防止することができる。さらに、電子線照射から放射線照射後加熱までの引き置き時間が長くなっても、パターン上層部の形状が劣化することがない。また、配合量が１０質量％以下であると、感度、未露光部の現像性等の低下を防ぐことができる。またこの様な酸拡散制御剤を使用することにより、レジスト組成物の貯蔵安定性が向上し、また解像度が向上するとともに、放射線照射前の引き置き時間、放射線照射後の引き置き時間の変動によるレジストパターンの線幅変化を抑えることができ、プロセス安定性に極めて優れたものとなる。
（その他の成分（Ｆ））
　本実施形態のレジスト組成物には、その他の成分（Ｆ）として、必要に応じて、溶解促進剤、溶解制御剤、増感剤、界面活性剤及び有機カルボン酸又はリンのオキソ酸若しくはその誘導体等の各種添加剤を１種又は２種以上添加することができる。これらその溶解促進剤、溶解制御剤、増感剤、界面活性剤及び有機カルボン酸又はリンのオキソ酸若しくはその誘導体としては、例えば、国際公開ＷＯ２０２０／１４５４０６号に記載のものが挙げられる。
　本実施形態のレジスト組成物において、任意成分（Ｆ）の合計量は、固形成分全質量の０～９９質量％であり、０～４９質量％が好ましく、０～１０質量％がより好ましく、０～５質量％がさらに好ましく、０～１質量％がさらに好ましく、０質量％が特に好ましい。
［レジスト組成物における各成分の配合割合］
　本実施形態のレジスト組成物において、本実施形態における重合体（成分（Ａ））の含有量は、特に限定されないが、固形成分の全質量（重合体（Ａ）、酸発生剤（Ｃ）又は塩基発生剤（Ｂ）、酸架橋剤（Ｇ）、酸拡散制御剤（Ｅ）及びその他の成分（Ｆ）（「任意成分（Ｆ）」とも記す。）などの任意に使用される成分を含む固形成分の総和、以下レジスト組成物について同様。）の５０～９９．４質量％であることが好ましく、より好ましくは５５～９０質量％、さらに好ましくは６０～８０質量％、特に好ましくは６０～７０質量％である。前記含有量の場合、解像度が一層向上し、ラインエッジラフネス（ＬＥＲ）が一層小さくなる傾向にある。
　本実施形態のレジスト組成物において、本実施形態における重合体（成分（Ａ））、酸発生剤（Ｃ）又は塩基発生剤（Ｂ）、酸架橋剤（Ｇ）、酸拡散制御剤（Ｅ）、任意成分（Ｆ）の含有量比（成分（Ａ）／酸発生剤（Ｃ）又は塩基発生剤（Ｂ）／酸架橋剤（Ｇ）／酸拡散制御剤（Ｅ）／任意成分（Ｆ））は、レジスト組成物の固形分１００質量％に対して、好ましくは５０～９９．４質量％／０．００１～４９質量％／０．５～４９質量％／０．００１～４９質量％／０～４９質量％であり、より好ましくは５５～９０質量％／１～４０質量％／０．５～４０質量％／０．０１～１０質量％／０～５質量％であり、さらに好ましくは６０～８０質量％／３～３０質量％／１～３０質量％／０．０１～５質量％／０～１質量％であり、特に好ましくは６０～７０質量％／１０～２５質量％／２～２０質量％／０．０１～３質量％／０質量％、である。成分の配合割合は、その総和が１００質量％になるように各範囲から選ばれる。前記配合にすると、感度、解像度、現像性等の性能に優れる傾向にある。なお、「固形分」とは、溶媒を除いた成分をいい、「固形分１００質量％」とは、溶媒を除いた成分を１００質量％とすることをいう。
　本実施形態のレジスト組成物は、通常は、使用時に各成分を溶媒に溶解して均一溶液とし、その後、必要に応じて、例えば、孔径０．２μｍ程度のフィルター等でろ過することにより調製される。
　本実施形態のレジスト組成物は、必要に応じて、本実施形態における重合体以外の他の樹脂を含むことができる。当該他の樹脂は、特に限定されず、例えば、ノボラック樹脂、ポリビニルフェノール類、ポリアクリル酸、ポリビニルアルコール、スチレン－無水マレイン酸樹脂、及びアクリル酸、ビニルアルコール、又はビニルフェノールを単量体単位として含む重合体或いはこれらの誘導体などが挙げられる。前記他の樹脂の含有量は、特に限定されず、使用する成分（Ａ）の種類に応じて適宜調節されるが、成分（Ａ）１００質量部に対して、３０質量部以下が好ましく、より好ましくは１０質量部以下、さらに好ましくは５質量部以下、特に好ましくは０質量部である。
［レジスト組成物の物性等］
　本実施形態のレジスト組成物は、スピンコートによりアモルファス膜を形成することができる。また、一般的な半導体製造プロセスに適用することができる。用いる現像液の種類によって、ポジ型レジストパターン及びネガ型レジストパターンのいずれかを作り分けることができる。
　ポジ型レジストパターンの場合、本実施形態のレジスト組成物をスピンコートして形成したアモルファス膜の２３℃における現像液に対する溶解速度は、５Å／ｓｅｃ以下が好ましく、０．０５～５Å／ｓｅｃがより好ましく、０．０００５～５Å／ｓｅｃがさらに好ましい。当該溶解速度が５Å／ｓｅｃ以下であると現像液に不溶で、レジストとすることができる。また、０．０００５Å／ｓｅｃ以上の溶解速度を有すると、解像性が向上する場合もある。これは、成分（Ａ）の露光前後の溶解性の変化により、現像液に溶解する露光部と、現像液に溶解しない未露光部との界面のコントラストが大きくなるからと推測される。また、ＬＥＲの低減、ディフェクトの低減効果がある。
　ネガ型レジストパターンの場合、本実施形態のレジスト組成物をスピンコートして形成したアモルファス膜の２３℃における現像液に対する溶解速度は、１０Å／ｓｅｃ以上であることが好ましい。当該溶解速度が１０Å／ｓｅｃ以上であると現像液に易溶で、レジストに一層向いている。また、１０Å／ｓｅｃ以上の溶解速度を有すると、解像性が向上する場合もある。これは、成分（Ａ）のミクロの表面部位が溶解し、ＬＥＲを低減するからと推測される。またディフェクトの低減効果がある。
　前記溶解速度は、２３℃にて、アモルファス膜を所定時間現像液に浸漬させ、その浸漬前後の膜厚を、目視、エリプソメーター又は走査型電子顕微鏡による断面観察等の公知の方法によって測定し決定できる。
　ポジ型レジストパターンの場合、本実施形態のレジスト組成物をスピンコートして形成したアモルファス膜のＫｒＦエキシマレーザー、極端紫外線、電子線又はＸ線等の放射線により露光した部分の２３℃における現像液に対する溶解速度は、１０Å／ｓｅｃ以上であることが好ましい。当該溶解速度が１０Å／ｓｅｃ以上であると現像液に易溶で、レジストに一層向いている。また、１０Å／ｓｅｃ以上の溶解速度を有すると、解像性が向上する場合もある。これは、成分（Ａ）のミクロの表面部位が溶解し、ＬＥＲを低減するからと推測される。またディフェクトの低減効果がある。
　ネガ型レジストパターンの場合、本実施形態のレジスト組成物をスピンコートして形成したアモルファス膜のＫｒＦエキシマレーザー、極端紫外線、電子線又はＸ線等の放射線により露光した部分の２３℃における現像液に対する溶解速度は、５Å／ｓｅｃ以下が好ましく、０．０５～５Å／ｓｅｃがより好ましく、０．０００５～５Å／ｓｅｃがさらに好ましい。当該溶解速度が５Å／ｓｅｃ以下であると現像液に不溶で、レジストとすることができる。また、０．０００５Å／ｓｅｃ以上の溶解速度を有すると、解像性が向上する場合もある。これは、成分（Ａ）の露光前後の溶解性の変化により、現像液に溶解する未露光部と、現像液に溶解しない露光部との界面のコントラストが大きくなるからと推測される。またＬＥＲの低減、ディフェクトの低減効果がある。
［感放射線性組成物］
　本実施形態の感放射線性組成物は、本実施形態の膜形成用組成物と、ジアゾナフトキノン光活性化合物（Ｂ）と、溶媒と、を含有する感放射線性組成物であって、前記溶媒の含有量が、前記感放射線性組成物の総量１００質量部に対して、２０～９９質量部であり、前記溶媒以外の成分の含有量が、前記感放射線性組成物の総量１００質量部に対して、１～８０質量部である。すなわち、本実施形態の感放射線性組成物は、本実施形態における重合体と、ジアゾナフトキノン光活性化合物（Ｂ）と、溶媒とを必須成分として含有してもよく、感放射線性であることを考慮し、種々の任意成分をさらに含有することができる。
　本実施形態の感放射線性組成物には、重合体（成分（Ａ））が含まれており、ジアゾナフトキノン光活性化合物（Ｂ）と併用されるため、ｇ線、ｈ線、ｉ線、ＫｒＦエキシマレーザー、ＡｒＦエキシマレーザー、極端紫外線、電子線又はＸ線を照射することにより、現像液に易溶な化合物となるポジ型レジスト用基材として有用である。ｇ線、ｈ線、ｉ線、ＫｒＦエキシマレーザー、ＡｒＦエキシマレーザー、極端紫外線、電子線又はＸ線により、成分（Ａ）の性質は大きくは変化しないが、現像液に難溶なジアゾナフトキノン光活性化合物（Ｂ）が易溶な化合物に変化することで、現像工程によってレジストパターンを作り得る。
　本実施形態の感放射線性組成物に含有させる本実施形態の重合体（成分（Ａ））のガラス転移温度は、好ましくは１００℃以上、より好ましくは１２０℃以上、さらに好ましくは１４０℃以上、特に好ましくは１５０℃以上である。成分（Ａ）のガラス転移温度の上限値は、特に限定されないが、例えば、６００℃である。成分（Ａ）のガラス転移温度が前記範囲内であることにより、半導体リソグラフィープロセスにおいて、パターン形状を維持しうる耐熱性を有し、高解像度などの性能が向上する傾向にある。
　本実施形態の感放射線性組成物に含有させる成分（Ａ）のガラス転移温度の示差走査熱量分析により求めた結晶化発熱量は２０Ｊ／ｇ未満であるのが好ましい。また、（結晶化温度）－（ガラス転移温度）は好ましくは７０℃以上、より好ましくは８０℃以上、さらに好ましくは１００℃以上、特に好ましくは１３０℃以上である。結晶化発熱量が２０Ｊ／ｇ未満、又は（結晶化温度）－（ガラス転移温度）が前記範囲内であると、感放射線性組成物をスピンコートすることにより、アモルファス膜を形成しやすく、かつレジストに必要な成膜性が長期に渡り保持でき、解像性が向上する傾向にある。
　本実施形態において、前記結晶化発熱量、結晶化温度及びガラス転移温度は、島津製作所製ＤＳＣ／ＴＡ－５０ＷＳを用いた示差走査熱量分析により求めることができる。試料約１０ｍｇをアルミニウム製非密封容器に入れ、窒素ガス気流中（５０ｍＬ／分）昇温速度２０℃／分で融点以上まで昇温する。急冷後、再び窒素ガス気流中（３０ｍＬ／分）昇温速度２０℃／分で融点以上まで昇温する。さらに急冷後、再び窒素ガス気流中（３０ｍＬ／分）昇温速度２０℃／分で４００℃まで昇温する。ステップ状に変化したベースラインの段差の中点（比熱が半分に変化したところ）の温度をガラス転移温度（Ｔｇ）、その後に現れる発熱ピークの温度を結晶化温度とする。発熱ピークとベースラインに囲まれた領域の面積から発熱量を求め、結晶化発熱量とする。
　本実施形態の感放射線性組成物に含有させる成分（Ａ）は、常圧下、１００以下、好ましくは１２０℃以下、より好ましくは１３０℃以下、さらに好ましくは１４０℃以下、特に好ましくは１５０℃以下において、昇華性が低いことが好ましい。昇華性が低いとは、熱重量分析において、所定温度で１０分保持した際の重量減少が１０％以下、好ましくは５％以下、より好ましくは３％以下、さらに好ましくは１％以下、特に好ましくは０．１％以下であることを示す。昇華性が低いことにより、露光時のアウトガスによる露光装置の汚染を防止することができる。また低ラフネスで良好なパターン形状を得ることができる。
　本実施形態の感放射線性組成物に含有させる成分（Ａ）は、プロピレングリコールモノメチルエーテルアセテート（ＰＧＭＥＡ）、プロピレングリコールモノメチルエーテル（ＰＧＭＥ）、シクロヘキサノン（ＣＨＮ）、シクロペンタノン（ＣＰＮ）、２－ヘプタノン、アニソール、酢酸ブチル、プロピオン酸エチル及び乳酸エチルから選ばれ、かつ、成分（Ａ）に対して最も高い溶解能を示す溶媒に、２３℃で、好ましくは１質量％以上、より好ましくは５質量％以上、さらに好ましくは１０質量％以上溶解し、よりさらに好ましくは、ＰＧＭＥＡ、ＰＧＭＥ、ＣＨＮから選ばれ、かつ、成分（Ａ）に対して最も高い溶解能を示す溶媒に、２３℃で、２０質量％以上溶解し、特に好ましくはＰＧＭＥＡに対して、２３℃で、２０質量％以上溶解する。前記条件を満たしていることにより、実生産における半導体製造工程での使用が可能となる。
（ジアゾナフトキノン光活性化合物（Ｂ））
　本実施形態の感放射線性組成物に含まれるジアゾナフトキノン光活性化合物（Ｂ）は、ポリマー性及び非ポリマー性ジアゾナフトキノン光活性化合物を含む、ジアゾナフトキノン物質であり、一般にポジ型レジスト組成物において、感光性成分（感光剤）として用いられているものであれば特に限定されず、１種又は２種以上を任意に選択して用いることができる。
　このような感光剤としては、ナフトキノンジアジドスルホン酸クロライドやベンゾキノンジアジドスルホン酸クロライド等と、これら酸クロライドと縮合反応可能な官能基を有する低分子化合物又は高分子化合物とを反応させることによって得られた化合物が好ましいものである。ここで、酸クロライドと縮合可能な官能基としては、特に限定されないが、例えば、水酸基、アミノ基等が挙げられるが、特に水酸基が好適である。水酸基を含む酸クロライドと縮合可能な化合物としては、特に限定されないが、例えばハイドロキノン、レゾルシン、２，４－ジヒドロキシベンゾフェノン、２，３，４－トリヒドロキシベンゾフェノン、２，４，６－トリヒドロキシベンゾフェノン、２，４，４’－トリヒドロキシベンゾフェノン、２，３，４，４’－テトラヒドロキシベンゾフェノン、２，２’，４，４’－テトラヒドロキシベンゾフェノン、２，２’，３，４，６’－ペンタヒドロキシベンゾフェノン等のヒドロキシベンゾフェノン類、ビス（２，４－ジヒドロキシフェニル）メタン、ビス（２，３，４－トリヒドロキシフェニル）メタン、ビス（２，４－ジヒドロキシフェニル）プロパン等のヒドロキシフェニルアルカン類、４，４’，３”，４”－テトラヒドロキシ－３，５，３’，５’－テトラメチルトリフェニルメタン、４，４’，２”，３”，４”－ペンタヒドロキシ－３，５，３’，５’－テトラメチルトリフェニルメタン等のヒドロキシトリフェニルメタン類などを挙げることができる。
　また、ナフトキノンジアジドスルホン酸クロライドやベンゾキノンジアジドスルホン酸クロライドなどの酸クロライドとしては、例えば、１，２－ナフトキノンジアジド－５－スルフォニルクロライド、１，２－ナフトキノンジアジド－４－スルフォニルクロライドなどが好ましいものとして挙げられる。
　本実施形態の感放射線性組成物は、例えば、使用時に各成分を溶媒に溶解して均一溶液とし、その後、必要に応じて、例えば、孔径０．２μｍ程度のフィルター等でろ過することにより調製されることが好ましい。
（溶媒）
　本実施形態の感放射線性組成物に用いることにできる溶媒としては、特に限定されないが、例えば、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノメチルエーテル、シクロヘキサノン、シクロペンタノン、２－ヘプタノン、アニソール、酢酸ブチル、プロピオン酸エチル、及び乳酸エチルが挙げられる。このなかでもプロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノメチルエーテル、シクロヘキサノンが好ましい、溶媒は、１種単独で用いても２種以上を併用してもよい。
　溶媒の含有量は、感放射線性組成物の総量１００質量部に対して、２０～９９質量部であり、好ましくは５０～９９質量部であり、より好ましくは６０～９８質量部であり、特に好ましくは９０～９８質量部である。
　また、溶媒以外の成分（固形成分）の含有量は、感放射線性組成物の総量１００質量部に対して、１～８０質量部であり、好ましくは１～５０質量部であり、より好ましくは２～４０質量部であり、特に好ましくは２～１０質量部である。
［感放射線性組成物の特性］
　本実施形態の感放射線性組成物は、スピンコートによりアモルファス膜を形成することができる。また、一般的な半導体製造プロセスに適用することができる。用いる現像液の種類によって、ポジ型レジストパターン及びネガ型レジストパターンのいずれかを作り分けることができる。
　ポジ型レジストパターンの場合、本実施形態の感放射線性組成物をスピンコートして形成したアモルファス膜の２３℃における現像液に対する溶解速度は、５Å／ｓｅｃ以下が好ましく、０．０５～５Å／ｓｅｃがより好ましく、０．０００５～５Å／ｓｅｃがさらに好ましい。当該溶解速度が５Å／ｓｅｃ以下であると現像液に不溶で、レジストとすることができる。また、０．０００５Å／ｓｅｃ以上の溶解速度を有すると、解像性が向上する場合もある。これは、本実施形態の重合体（成分（Ａ））の露光前後の溶解性の変化により、現像液に溶解する露光部と、現像液に溶解しない未露光部との界面のコントラストが大きくなるからと推測される。またＬＥＲの低減、ディフェクトの低減効果がある。
　ネガ型レジストパターンの場合、本実施形態の感放射線性組成物をスピンコートして形成したアモルファス膜の２３℃における現像液に対する溶解速度は、１０Å／ｓｅｃ以上であることが好ましい。当該溶解速度が１０Å／ｓｅｃ以上であると現像液に易溶で、レジストに一層向いている。また、１０Å／ｓｅｃ以上の溶解速度を有すると、解像性が向上する場合もある。これは、成分（Ａ）のミクロの表面部位が溶解し、ＬＥＲを低減するからと推測される。またディフェクトの低減効果がある。
　前記溶解速度は、２３℃にて、アモルファス膜を所定時間現像液に浸漬させ、その浸漬前後の膜厚を、目視、エリプソメーター又はＱＣＭ法等の公知の方法によって測定し決定できる。
　ポジ型レジストパターンの場合、本実施形態の感放射線性組成物をスピンコートして形成したアモルファス膜のＫｒＦエキシマレーザー、極端紫外線、電子線又はＸ線等の放射線により照射した後、又は、２０～５００℃（好ましくは、５０～５００℃）で加熱した後の露光した部分の、２３℃における現像液に対する溶解速度は、１０Å／ｓｅｃ以上が好ましく、１０～１００００Å／ｓｅｃがより好ましく、１００～１０００Å／ｓｅｃがさらに好ましい。当該溶解速度が１０Å／ｓｅｃ以上であると現像液に易溶で、レジストに一層向いている。また、１００００Å／ｓｅｃ以下の溶解速度を有すると、解像性が向上する場合もある。これは、成分（Ａ）のミクロの表面部位が溶解し、ＬＥＲを低減するからと推測される。またディフェクトの低減効果がある。
　ネガ型レジストパターンの場合、本実施形態の感放射線性組成物をスピンコートして形成したアモルファス膜のＫｒＦエキシマレーザー、極端紫外線、電子線又はＸ線等の放射線により照射した後、又は、２０～５００℃（好ましくは、５０～５００℃）で加熱した後の露光した部分の、２３℃における現像液に対する溶解速度は、５Å／ｓｅｃ以下が好ましく、０．０５～５Å／ｓｅｃがより好ましく、０．０００５～５Å／ｓｅｃがさらに好ましい。当該溶解速度が５Å／ｓｅｃ以下であると現像液に不溶で、レジストとすることができる。また、０．０００５Å／ｓｅｃ以上の溶解速度を有すると、解像性が向上する場合もある。これは、成分（Ａ）の露光前後の溶解性の変化により、現像液に溶解する未露光部と、現像液に溶解しない露光部との界面のコントラストが大きくなるからと推測される。またＬＥＲの低減、ディフェクトの低減効果がある。
（感放射線性組成物における各成分の配合割合）
　本実施形態の感放射線性組成物において、本実施形態の重合体（成分（Ａ））の含有量は、固形成分全質量（本実施形態の重合体、ジアゾナフトキノン光活性化合物（Ｂ）及びその他の成分（Ｄ）などの任意に使用される固形成分の総和、感放射線性組成物について以下同様。）に対して、好ましくは１～９９質量％であり、より好ましくは５～９５質量％、さらに好ましくは１０～９０質量％、特に好ましくは２５～７５質量％である。本実施形態の感放射線性組成物は、本実施形態の重合体の含有量が前記範囲内であると、高感度でラフネスの小さなパターンを得ることができる。
　本実施形態の感放射線性組成物において、ジアゾナフトキノン光活性化合物（Ｂ）の含有量は、固形成分全質量に対して、好ましくは１～９９質量％であり、より好ましくは５～９５質量％、さらに好ましくは１０～９０質量％、特に好ましくは２５～７５質量％である。本実施形態の感放射線性組成物は、ジアゾナフトキノン光活性化合物（Ｂ）の含有量が前記範囲内であると、高感度でラフネスの小さなパターンを得ることができる。
（その他の成分（Ｄ））
　本実施形態の感放射線性組成物には、必要に応じて、溶媒、本実施形態の重合体及びジアゾナフトキノン光活性化合物（Ｂ）以外の成分として、上述の酸発生剤、酸架橋剤、酸拡散制御剤、溶解促進剤、溶解制御剤、増感剤、界面活性剤、有機カルボン酸又はリンのオキソ酸若しくはその誘導体等の各種添加剤を１種又は２種以上添加することができる。なお、本実施形態の感放射線性組成物に関して、その他の成分（Ｄ）を任意成分（Ｄ）ということがある。
　本実施形態の重合体（成分（Ａ））と、ジアゾナフトキノン光活性化合物（Ｂ）と、任意成分（Ｄ）と、の含有量比（（Ａ）／（Ｂ）／（Ｄ））は、感放射線性組成物の固形分１００質量％に対して、好ましくは１～９９質量％／９９～１質量％／０～９８質量％であり、より好ましくは５～９５質量％／９５～５質量％／０～４９質量％であり、さらに好ましくは１０～９０質量％／９０～１０質量％／０～１０質量％であり、特に好ましくは２０～８０質量％／８０～２０質量％／０～５質量％であり、最も好ましくは２５～７５質量％／７５～２５質量％／０質量％である。
　各成分の配合割合は、その総和が１００質量％になるように各範囲から選ばれる。本実施形態の感放射線性組成物は、各成分の配合割合を前記範囲にすると、ラフネスに加え、感度、解像度等の性能に優れる。
　本実施形態の感放射線性組成物は本実施形態における重合体以外の他の樹脂を含んでもよい。このような他の樹脂としては、ノボラック樹脂、ポリビニルフェノール類、ポリアクリル酸、ポリビニルアルコール、スチレン－無水マレイン酸樹脂、及びアクリル酸、ビニルアルコール、又はビニルフェノールを単量体単位として含む重合体或いはこれらの誘導体などが挙げられる。他の樹脂の配合量は、使用する本実施形態の重合体の種類に応じて適宜調節されるが、本実施形態の重合体１００質量部に対して、３０質量部以下が好ましく、より好ましくは１０質量部以下、さらに好ましくは５質量部以下、特に好ましくは０質量部である。
［アモルファス膜の製造方法］
　本実施形態のアモルファス膜の製造方法は、前記感放射線性組成物を用いて、基板上にアモルファス膜を形成する工程を含む。
［レジストパターン形成方法］
　本実施形態において、レジストパターンは、本実施形態のレジスト組成物を用いるか、或いは、本実施形態の感放射線性組成物を用いることにより、形成することができる。また、後述するが、本実施形態のリソグラフィー用下層膜形成用組成物を用いてレジストパターンを形成することもできる。
［レジスト組成物を用いたレジストパターンの形成方法］
　本実施形態のレジスト組成物を用いたレジストパターンの形成方法は、上述した本実施形態のレジスト組成物を用いて基板上にレジスト膜を形成する工程と、形成されたレジスト膜の少なくとも一部を露光する工程と、露光した前記レジスト膜を現像してレジストパターンを形成する工程とを備える。本実施形態におけるレジストパターンは多層プロセスにおける上層レジストとして形成することもできる。
［感放射線性組成物を用いたレジストパターン形成方法］
　本実施形態の感放射線性組成物を用いたレジストパターン形成方法は、前記感放射線性組成物を用いて、基板上にレジスト膜を形成する工程と、形成された前記レジスト膜の少なくとも一部を露光する工程と、露光した前記レジスト膜を現像してレジストパターンを形成する工程と、を含む。なお、詳細には以下の、レジスト組成物を用いたレジストパターン形成方法と同様の操作とすることができる。
　以下、本実施形態のレジスト組成物を用いる場合と本実施形態の感放射線性組成物を用いる場合とで共通しうるレジストパターン形成方法の実施条件に関して説明する。
　レジストパターンを形成する方法としては、特に限定されないが、例えば、以下の方法が挙げられる。まず、従来公知の基板上に前記本実施形態のレジスト組成物を、回転塗布、流延塗布、ロール塗布等の塗布手段によって塗布することによりレジスト膜を形成する。従来公知の基板とは、特に限定されず、例えば、電子部品用の基板や、これに所定の配線パターンが形成されたもの等を例表することができる。より具体的には、特に限定されないが、例えば、シリコンウェハー、銅、クロム、鉄、アルミニウム等の金属製の基板や、ガラス基板等が挙げられる。配線パターンの材料としては、特に限定されないが、例えば、銅、アルミニウム、ニッケル、金等が挙げられる。また必要に応じて、前述基板上に無機系及び／又は有機系の膜が設けられたものであってもよい。無機系の膜としては、特に限定されないが、例えば、無機反射防止膜（無機ＢＡＲＣ）が挙げられる。有機系の膜としては、特に限定されないが、例えば、有機反射防止膜（有機ＢＡＲＣ）が挙げられる。ヘキサメチレンジシラザン等による表面処理を行ってもよい。
　次に、必要に応じて、塗布した基板を加熱する。加熱条件は、レジスト組成物の配合組成等により変わるが、２０～２５０℃が好ましく、より好ましくは２０～１５０℃である。加熱することによって、レジストの基板に対する密着性が向上する場合があり好ましい。次いで、可視光線、紫外線、エキシマレーザー、電子線、極端紫外線（ＥＵＶ）、Ｘ線、及びイオンビームで構成される群から選ばれるいずれかの放射線により、レジスト膜を所望のパターンに露光する。露光条件等は、レジスト組成物の配合組成等に応じて適宜選定される。本実施形態においては、露光における高精度の微細パターンを安定して形成するために、放射線照射後に加熱するのが好ましい。
　次いで、露光されたレジスト膜を現像液で現像することにより、所定のレジストパターンを形成する。前記現像液としては、使用する成分（Ａ）に対して溶解度パラメーター（ＳＰ値）の近い溶剤を選択することが好ましく、ケトン系溶剤、エステル系溶剤、アルコール系溶剤、アミド系溶剤、エーテル系溶剤等の極性溶剤又は炭化水素系溶剤、或いはアルカリ水溶液を用いることができる。前記溶剤及びアルカリ水溶液としては、例えば、国際公開第２０１３／０２４７７８号に記載のものが挙げられる。
　上述の溶剤は、複数混合してもよいし、性能を有する範囲内で、前記以外の溶剤や水と混合し使用してもよい。ここで、本実施形態の所望の効果をより高める観点から、現像液全体としての含水率が７０質量％未満であり、５０質量％未満であることが好ましく、３０質量％未満であることがより好ましく、１０質量％未満であることがさらに好ましく、実質的に水分を含有しないことが特に好ましい。すなわち、現像液に対する有機溶剤の含有量は、現像液の全量に対して、３０質量％以上１００質量％以下であり、５０質量％以上１００質量％以下であることが好ましく、７０質量％以上１００質量％以下であることがより好ましく、９０質量％以上１００質量％以下であることがさらに好ましく、９５質量％以上１００質量％以下であることが特に好ましい。
　特に、現像液は、ケトン系溶剤、エステル系溶剤、アルコール系溶剤、アミド系溶剤及びエーテル系溶剤から選択される少なくとも１種類の溶剤を含有する現像液が、レジストパターンの解像性やラフネス等のレジスト性能を改善するため好ましい。
　現像液には、必要に応じて界面活性剤を適当量添加することができる。界面活性剤としては特に限定されないが、例えば、イオン性や非イオン性のフッ素系及び／又はシリコン系界面活性剤等を用いることができる。これらのフッ素及び／又はシリコン系界面活性剤として、例えば、特開昭６２－３６６６３号公報、特開昭６１－２２６７４６号公報、特開昭６１－２２６７４５号公報、特開昭６２－１７０９５０号公報、特開昭６３－３４５４０号公報、特開平７－２３０１６５号公報、特開平８－６２８３４号公報、特開平９－５４４３２号公報、特開平９－５９８８号公報、米国特許第５４０５７２０号明細書、同５３６０６９２号明細書、同５５２９８８１号明細書、同５２９６３３０号明細書、同５４３６０９８号明細書、同５５７６１４３号明細書、同５２９４５１１号明細書、同５８２４４５１号明細書記載の界面活性剤を挙げることができ、好ましくは、非イオン性の界面活性剤である。非イオン性の界面活性剤としては特に限定されないが、フッ素系界面活性剤又はシリコン系界面活性剤を用いることがさらに好ましい。
　界面活性剤の使用量は現像液の全量に対して、通常０．００１～５質量％、好ましくは０．００５～２質量％、さらに好ましくは０．０１～０．５質量％である。
　現像方法としては、特に限定されないが、例えば、現像液が満たされた槽中に基板を一定時間浸漬する方法（ディップ法）、基板表面に現像液を表面張力によって盛り上げて一定時間静止することで現像する方法（パドル法）、基板表面に現像液を噴霧する方法（スプレー法）、一定速度で回転している基板上に一定速度で現像液塗出ノズルをスキャンしながら現像液を塗出しつづける方法（ダイナミックディスペンス法）などを適用することができる。パターンの現像を行なう時間には特に制限はないが、好ましくは１０秒～９０秒である。
　また、現像を行う工程の後に、他の溶媒に置換しながら、現像を停止する工程を実施してもよい。
　現像の後には、有機溶剤を含むリンス液を用いて洗浄する工程を含むことが好ましい。当該リンス液を用いて洗浄する工程（リンス工程）は特に限定されるものではなく、例えば、国際公開ＷＯ２０２０／１４５４０６号に記載のリンス工程を適宜採用することができる。
　レジストパターンを形成した後、エッチングすることによりパターン配線基板が得られる。エッチングの方法はプラズマガスを使用するドライエッチング及びアルカリ溶液、塩化第二銅溶液、塩化第二鉄溶液等によるウェットエッチングなど公知の方法で行うことが出来る。
　レジストパターンを形成した後、めっきを行うこともできる。前記めっき法としては、例えば、銅めっき、はんだめっき、ニッケルめっき、金めっきなどがある。
　エッチング後の残存レジストパターンは有機溶剤で剥離することが出来る。前記有機溶剤として、特に限定されないが、例えば、ＰＧＭＥＡ（プロピレングリコールモノメチルエーテルアセテート）、ＰＧＭＥ（プロピレングリコールモノメチルエーテル）、ＥＬ（乳酸エチル）等が挙げられる。前記剥離方法としては、特に限定されないが、例えば、浸漬方法、スプレイ方式等が挙げられる。また、レジストパターンが形成された配線基板は、多層配線基板でもよく、小径スルーホールを有していてもよい。
　本実施形態において得られる配線基板は、レジストパターン形成後、金属を真空中で蒸着し、その後レジストパターンを溶液で溶かす方法、すなわちリフトオフ法により形成することもできる。
［リソグラフィー用下層膜形成用組成物］
　本実施形態のリソグラフィー用下層膜形成用組成物は、本実施形態の膜形成用組成物を含むものである。すなわち、本実施形態のリソグラフィー用下層膜形成用組成物は、本実施形態における重合体を必須成分として含有するものであり、リソグラフィー用下層膜形成材料として用いられることを考慮し、種々の任意成分をさらに含有することができる。具体的には、本実施形態のリソグラフィー用下層膜形成用組成物は、溶媒、酸発生剤、塩基発生剤及び架橋剤で構成される群から選択される少なくとも１つをさらに含有することが好ましい。
　本実施形態における重合体の含有量としては、塗布性及び品質安定性の点から、リソグラフィー用下層膜形成用組成物中、全固形分に対して、１～１００質量％であることが好ましく、１０～１００質量％であることがより好ましく、５０～１００質量％であることがさらに好ましく、１００質量％であることが特に好ましい。
　本実施形態のリソグラフィー用下層膜形成用組成物が溶媒を含む場合、本実施形態における重合体の含有量は、特に限定されないが、溶媒を含む総量１００質量部に対して、１～４０質量部であることが好ましく、より好ましくは２～３７．５質量部、さらに好ましくは３～３５質量部である。
　本実施形態のリソグラフィー用下層膜形成用組成物は、湿式プロセスへの適用が可能であり、耐熱性及びエッチング耐性に優れる。さらに、本実施形態のリソグラフィー用下層膜形成用組成物は本実施形態における重合体を含むため、高温ベーク時の膜の劣化が抑制され、酸素プラズマエッチング等に対するエッチング耐性にも優れた下層膜を形成することができる。さらに、本実施形態のリソグラフィー用下層膜形成用組成物はレジスト層との密着性にも優れるので、優れたレジストパターンを得ることができる。なお、本実施形態のリソグラフィー用下層膜形成用組成物は、本実施形態の所望の効果が損なわれない範囲において、既に知られているリソグラフィー用下層膜形成材料等を含んでいてもよい。
（溶媒）
　本実施形態のリソグラフィー用下層膜形成用組成物において用いられる溶媒としては、本実施形態の重合体が少なくとも溶解するものであれば、公知のものを適宜用いることができる。
　溶媒の具体例としては、特に限定されないが、例えば、国際公開第２０１３／０２４７７９号に記載のものが挙げられる。これらの溶媒は、１種を単独で、或いは２種以上を組み合わせて用いることができる。
　前記溶媒の中で、安全性の点からシクロヘキサノン、プロピレングリコールモノメチルエーテル、プロピレングリコールモノメチルエーテルアセテート、乳酸エチル、ヒドロキシイソ酪酸メチル、アニソールが特に好ましい。
　溶媒の含有量は、特に限定されないが、溶解性及び製膜上の観点から、本実施形態における重合体１００質量部に対して、１００～１０，０００質量部であることが好ましく、２００～５，０００質量部であることがより好ましく、２００～１，０００質量部であることがさらに好ましい。
（架橋剤）
　本実施形態のリソグラフィー用下層膜形成用組成物は、インターミキシングを抑制する等の観点から、必要に応じて架橋剤を含有していてもよい。本実施形態で使用可能な架橋剤としては、特に限定されないが、例えば、国際公開第２０１３／０２４７７８号、国際公開第２０１３／０２４７７９号や国際公開第２０１８／０１６６１４号に記載のものを用いることができる。なお、本実施形態において、架橋剤は、単独で又は２種以上を使用することができる。
　本実施形態で使用可能な架橋剤の具体例としては、例えば、フェノール化合物、エポキシ化合物、シアネート化合物、アミノ化合物、ベンゾオキサジン化合物、アクリレート化合物、メラミン化合物、グアナミン化合物、グリコールウリル化合物、ウレア化合物、イソシアネート化合物、アジド化合物等が挙げられるが、これらに特に限定されない。これらの架橋剤は、１種を単独で、或いは２種以上を組み合わせて用いることができる。これらの中でもベンゾオキサジン化合物、エポキシ化合物又はシアネート化合物が好ましく、エッチング耐性向上の観点から、ベンゾオキサジン化合物がより好ましい。また良好な反応性を有する点から、メラミン化合物、及びウレア化合物がより好ましい。これら架橋剤としては、例えば、PCT/JP2021/26669に記載の架橋剤を適宜用いることができる。
　本実施形態のリソグラフィー用下層膜形成用組成物において、架橋剤の含有量は、特に限定されないが、本実施形態における重合体１００質量部に対して、５～５０質量部であることが好ましく、より好ましくは１０～４０質量部である。上述の好ましい範囲にすることで、レジスト層とのミキシング現象の発生が抑制される傾向にあり、また、反射防止効果が高められ、架橋後の膜形成性が高められる傾向にある。
（架橋促進剤）
　本実施形態のリソグラフィー用下層膜形成用組成物には、必要に応じて架橋、硬化反応を促進させるための架橋促進剤を用いることができる。
　前記架橋促進剤としては、架橋、硬化反応を促進させるものであれば、特に限定されないが、例えば、アミン類、イミダゾール類、有機ホスフィン類、ルイス酸等が挙げられる。これらの架橋促進剤は、１種を単独で、或いは２種以上を組み合わせて用いることができる。これらの中でもイミダゾール類又は有機ホスフィン類が好ましく、架橋温度の低温化の観点から、イミダゾール類がより好ましい。
　前記架橋促進剤としては、公知のものが使用でき、特に限定されないが、例えば、国際公開２０１８／０１６６１４号に記載のものが挙げられる。耐熱性及び硬化促進の観点から、特に２－メチルイミダゾール、２－フェニルイミダゾール、２－エチル－４－メチルイミダゾールが好ましい。
　架橋促進剤の含有量としては、通常、組成物の合計質量１００質量部とした場合に１００質量部とした場合に、好ましくは０．１～１０質量部であり、より好ましくは、制御のし易さ及び経済性の観点から０．１～５質量部であり、さらに好ましくは０．１～３質量部である。
（ラジカル重合開始剤）
　本実施形態のリソグラフィー用下層膜形成用組成物には、必要に応じてラジカル重合開始剤を配合することができる。ラジカル重合開始剤としては、光によりラジカル重合を開始させる光重合開始剤であってもよいし、熱によりラジカル重合を開始させる熱重合開始剤であってもよい。ラジカル重合開始剤としては、例えば、ケトン系光重合開始剤、有機過酸化物系重合開始剤及びアゾ系重合開始剤で構成される群から選ばれる少なくとも１種とすることができる。
　このようなラジカル重合開始剤としては、特に制限されず、従来用いられているものを適宜採用することができる。例えば、国際公開２０１８／０１６６１４号に記載のものが挙げられる。これらの中でも特に好ましくは、原料入手性及び保存安定性の観点からジクミルパーオキサイド、２，５－ジメチル－２，５－ビス（ｔ－ブチルパーオキシ）ヘキサン、ｔ－ブチルクミルパーオキサイドである。
　本実施形態に用いるラジカル重合開始剤としては、これらのうちの１種を単独で用いても２種以上を組み合わせて用いてもよく、他の公知の重合開始剤をさらに組み合わせて用いてもよい。
（酸発生剤）
　本実施形態のリソグラフィー用下層膜形成用組成物は、熱による架橋反応をさらに促進させるなどの観点から、必要に応じて酸発生剤を含有していてもよい。酸発生剤としては、熱分解によって酸を発生するもの、光照射によって酸を発生するものなどが知られているが、いずれのものも使用することができる。
　酸発生剤としては、特に限定されないが、例えば、国際公開第２０１３／０２４７７９号に記載のものを用いることができる。なお、本実施形態において、酸発生剤は、単独で又は２種以上を組み合わせて使用することができる。
　本実施形態のリソグラフィー用下層膜形成用組成物において、酸発生剤の含有量は、特に限定されないが、本実施形態における重合体１００質量部に対して、０．１～５０質量部であることが好ましく、より好ましくは０．５～４０質量部である。上述の好ましい範囲にすることで、酸発生量が多くなって架橋反応が高められる傾向にあり、また、レジスト層とのミキシング現象の発生が抑制される傾向にある。
（塩基発生剤）
　塩基発生剤が光塩基発生剤である場合について説明する。
　光塩基発生剤とは、露光により塩基を発生するものであり、常温常圧の通常の条件下では活性を示さないが、外部刺激として電磁波の照射と加熱が行なわれると、塩基（塩基性物質）を発生するものであれば特に限定されるものではない。
　本発明に用いることができる光塩基発生剤は、特に限定されず公知のものを用いることができ、例えば、カルバメート誘導体、アミド誘導体、イミド誘導体、αコバルト錯体類、イミダゾール誘導体、桂皮酸アミド誘導体、オキシム誘導体等が挙げられる。
　光塩基発生剤から発生される塩基性物質としては特に限定されないが、アミノ基を有する化合物、特にモノアミンや、ジアミンなどのポリアミン、また、アミジンなどが挙げられる。
　発生される塩基性物質は、より塩基性度の高い（共役酸のｐＫａ値が高い）アミノ基を有する化合物が感度及び解像性の観点から好ましい。
　光塩基発生剤としては、例えば、特開２００９－８０４５２号公報及び国際公開第２００９／１２３１２２号パンフレットで開示されたような桂皮酸アミド構造を有する塩基発生剤、特開２００６－１８９５９１号公報及び特開２００８－２４７７４７号公報で開示されたようなカルバメート構造を有する塩基発生剤、特開２００７－２４９０１３号公報及び特開２００８－００３５８１号公報で開示されたようなオキシム構造、カルバモイルオキシム構造を有する塩基発生剤、特開２０１０－２４３７７３号公報に記載の化合物等が挙げられるが、これらに限定されず、その他にも公知の塩基発生剤の構造を用いることができる。
　光塩基発生剤は、１種類単独で又は２種類以上を組み合わせて使用することができる。
　光塩基発生剤の感活性光線性又は感放射線性樹脂組成物中の好ましい含有量は、前述の光酸発生剤の感活性光線性又は感放射線性樹脂組成物中の好ましい含有量と同様である。
（塩基性化合物）
　さらに、本実施形態のリソグラフィー用下層膜形成用組成物は、保存安定性を向上させる等の観点から、塩基性化合物を含有していてもよい。
　塩基性化合物は、酸発生剤より微量に発生した酸が架橋反応を進行させるのを防ぐための、酸に対するクエンチャーの役割を果たす。このような塩基性化合物としては、例えば、第一級、第二級又は第三級の脂肪族アミン類、混成アミン類、芳香族アミン類、複素環アミン類、カルボキシ基を有する含窒素化合物、スルホニル基を有する含窒素化合物、水酸基を有する含窒素化合物、ヒドロキシフェニル基を有する含窒素化合物、アルコール性含窒素化合物、アミド誘導体、イミド誘導体等が挙げられるが、これらに特に限定されない。
　本実施形態において用いられる塩基性化合物としては、特に限定されないが、例えば、国際公開第２０１３／０２４７７９号に記載のものを用いることができる。なお、本実施形態において、塩基性化合物は、単独で又は２種以上を組み合わせて使用することができる。
　本実施形態のリソグラフィー用下層膜形成用組成物において、塩基性化合物の含有量は、特に限定されないが、本実施形態における重合体１００質量部に対して、０．００１～２質量部であることが好ましく、より好ましくは０．０１～１質量部である。上述の好ましい範囲にすることで、架橋反応を過度に損なうことなく保存安定性が高められる傾向にある。
（その他の添加剤）
　また、本実施形態のリソグラフィー用下層膜形成用組成物は、熱硬化性の付与や吸光度をコントロールする目的で、他の樹脂及び／又は化合物を含有していてもよい。このような他の樹脂及び／又は化合物としては、例えば、ナフトール樹脂、キシレン樹脂ナフトール変性樹脂、ナフタレン樹脂のフェノール変性樹脂、ポリヒドロキシスチレン、ジシクロペンタジエン樹脂、（メタ）アクリレート、ジメタクリレート、トリメタクリレート、テトラメタクリレート、ビニルナフタレン、ポリアセナフチレンなどのナフタレン環、フェナントレンキノン、フルオレンなどのビフェニル環、チオフェン、インデンなどのヘテロ原子を有する複素環を含む樹脂や芳香族環を含まない樹脂；ロジン系樹脂、シクロデキストリン、アダマンタン（ポリ）オール、トリシクロデカン（ポリ）オール及びそれらの誘導体等の脂環構造を含む樹脂又は化合物等が挙げられるが、これらに特に限定されない。さらに、本実施形態のリソグラフィー用下層膜形成用組成物は、公知の添加剤を含有していてもよい。前記公知の添加剤としては、以下に限定されないが、例えば、紫外線吸収剤、界面活性剤、着色剤、ノニオン系界面活性剤等が挙げられる。
［リソグラフィー用下層膜の形成方法］
　本実施形態のリソグラフィー用下層膜の形成方法（製造方法）は、本実施形態のリソグラフィー用下層膜形成用組成物を用いて、基板上に下層膜を形成する工程を含む。
［リソグラフィー用下層膜形成用組成物を用いたレジストパターン形成方法］
　本実施形態のリソグラフィー用下層膜形成用組成物を用いたレジストパターン形成方法は、本実施形態のリソグラフィー用下層膜形成用組成物を用いて、基板上に下層膜を形成する工程（Ａ－１）と、前記下層膜上に、少なくとも１層のフォトレジスト層を形成する工程（Ａ－２）と、を含む。また、当該レジストパターン形成方法は、前記フォトレジスト層の所定の領域に放射線を照射し、現像してレジストパターンを形成する工程（Ａ－３）を含んでもよい。
［リソグラフィー用下層膜形成用組成物を用いた回路パターン形成方法］
　本実施形態のリソグラフィー用下層膜形成用組成物を用いた回路パターン形成方法は、本実施形態のリソグラフィー用下層膜形成用組成物を用いて、基板上に下層膜を形成する工程（Ｂ－１）と、前記下層膜上に、珪素原子を含有するレジスト中間層膜材料を用いて中間層膜を形成する工程（Ｂ－２）と、前記中間層膜上に、少なくとも１層のフォトレジスト層を形成する工程（Ｂ－３）と、前記工程（Ｂ－３）の後、前記フォトレジスト層の所定の領域に放射線を照射し、現像してレジストパターンを形成する工程（Ｂ－４）と、前記工程（Ｂ－４）の後、前記レジストパターンをマスクとして前記中間層膜をエッチングして、中間層膜パターンを形成する工程（Ｂ－５）と、得られた中間層膜パターンをエッチングマスクとして前記下層膜をエッチングして、下層膜パターンを形成する工程（Ｂ－６）と、得られた下層膜パターンをエッチングマスクとして基板をエッチングすることで基板にパターンを形成する工程（Ｂ－７）と、を有する。
　本実施形態のリソグラフィー用下層膜は、本実施形態のリソグラフィー用下層膜形成用組成物から形成されるものであれば、その形成方法は特に限定されず、公知の手法を適用することができる。例えば、本実施形態のリソグラフィー用下層膜形成用組成物をスピンコートやスクリーン印刷等の公知の塗布法或いは印刷法などで基板上に付与した後、有機溶媒を揮発させるなどして除去することで、下層膜を形成することができる。
　下層膜の形成時には、上層レジストとのミキシング現象の発生を抑制するとともに架橋反応を促進させるために、ベークをすることが好ましい。この場合、ベーク温度は、特に限定されないが、８０～４５０℃の範囲内であることが好ましく、より好ましくは２００～４００℃である。また、ベーク時間も、特に限定されないが、１０～３００秒の範囲内であることが好ましい。なお、下層膜の厚さは、要求性能に応じて適宜選定することができ、特に限定されないが、通常、３０～２０，０００ｎｍ程度であることが好ましく、より好ましくは５０～１５，０００ｎｍとすることが好ましい。
　下層膜を作製した後、２層プロセスの場合はその上に珪素含有レジスト層、或いは通常の炭化水素を含む単層レジスト、３層プロセスの場合はその上に珪素含有中間層、さらにその上に珪素を含まない単層レジスト層を作製することが好ましい。この場合、このレジスト層を形成するためのフォトレジスト材料としては公知のものを使用することができる。
　基板上に下層膜を作製した後、２層プロセスの場合はその下層膜上に珪素含有レジスト層又は通常の炭化水素を含む単層レジストを作製することができる。３層プロセスの場合はその下層膜上に珪素含有中間層、さらにその珪素含有中間層上に珪素を含まない単層レジスト層を作製することができる。これらの場合において、レジスト層を形成するためのフォトレジスト材料は、公知のものから適宜選択して使用することができ、特に限定されない。
　２層プロセス用の珪素含有レジスト材料としては、酸素ガスエッチング耐性の観点から、ベースポリマーとしてポリシルセスキオキサン誘導体又はビニルシラン誘導体等の珪素原子含有ポリマーを使用し、さらに有機溶媒、酸発生剤、必要により塩基性化合物等を含むポジ型のフォトレジスト材料が好ましく用いられる。ここで珪素原子含有ポリマーとしては、この種のレジスト材料において用いられている公知のポリマーを使用することができる。
　３層プロセス用の珪素含有中間層としてはポリシルセスキオキサンベースの中間層が好ましく用いられる。中間層に反射防止膜として効果を持たせることによって、効果的に反射を抑えることができる傾向にある。例えば、１９３ｎｍ露光用プロセスにおいて、下層膜として芳香族基を多く含み基板エッチング耐性が高い材料を用いると、ｋ値が高くなり、基板反射が高くなる傾向にあるが、中間層で反射を抑えることによって、基板反射を０．５％以下にすることができる。このような反射防止効果がある中間層としては、以下に限定されないが、１９３ｎｍ露光用としてはフェニル基又は珪素－珪素結合を有する吸光基を導入された、酸或いは熱で架橋するポリシルセスキオキサンが好ましく用いられる。
　また、Ｃｈｅｍｉｃａｌ　Ｖａｐｏｒ　Ｄｅｐｏｓｉｔｉｏｎ（ＣＶＤ）法で形成した中間層を用いることもできる。ＣＶＤ法で作製した反射防止膜としての効果が高い中間層としては、以下に限定されないが、例えば、ＳｉＯＮ膜が知られている。一般的には、ＣＶＤ法よりスピンコート法やスクリーン印刷等の湿式プロセスによる中間層の形成の方が、簡便でコスト的なメリットがある。なお、３層プロセスにおける上層レジストは、ポジ型でもネガ型でもどちらでもよく、また、通常用いられている単層レジストと同じものを用いることができる。
　さらに、本実施形態における下層膜は、通常の単層レジスト用の反射防止膜或いはパターン倒れ抑制のための下地材として用いることもできる。本実施形態の下層膜は、下地加工のためのエッチング耐性に優れるため、下地加工のためのハードマスクとしての機能も期待できる。
　前記フォトレジスト材料によりレジスト層を形成する場合においては、前記下層膜を形成する場合と同様に、スピンコート法やスクリーン印刷等の湿式プロセスが好ましく用いられる。また、レジスト材料をスピンコート法などで塗布した後、通常、プリベークが行われるが、このプリベークは、８０～１８０℃で１０～３００秒の範囲で行うことが好ましい。その後、常法にしたがい、露光を行い、ポストエクスポジュアーベーク（ＰＥＢ）、現像を行うことで、レジストパターンを得ることができる。なお、レジスト膜の厚さは特に制限されないが、一般的には、３０～５００ｎｍが好ましく、より好ましくは５０～４００ｎｍである。
　また、露光光は、使用するフォトレジスト材料に応じて適宜選択して用いればよい。一般的には、波長３００ｎｍ以下の高エネルギー線、具体的には２４８ｎｍ、１９３ｎｍ、１５７ｎｍのエキシマレーザー、３～２０ｎｍの軟Ｘ線、電子ビーム、Ｘ線等を挙げることができる。
　上述の方法により形成されるレジストパターンは、本実施形態における下層膜によってパターン倒れが抑制されたものとなる。そのため、本実施形態における下層膜を用いることで、より微細なパターンを得ることができ、また、そのレジストパターンを得るために必要な露光量を低下させ得る。
　次に、得られたレジストパターンをマスクにしてエッチングを行う。２層プロセスにおける下層膜のエッチングとしては、ガスエッチングが好ましく用いられる。ガスエッチングとしては、酸素ガスを用いたエッチングが好適である。酸素ガスに加えて、Ｈｅ、Ａｒなどの不活性ガスや、ＣＯ、ＣＯ２、ＮＨ３、ＳＯ２、Ｎ２、ＮＯ２、Ｈ２ガスを加えることも可能である。また、酸素ガスを用いずに、ＣＯ、ＣＯ２、ＮＨ３、Ｎ２、ＮＯ２、Ｈ２ガスだけでガスエッチングを行うこともできる。特に後者のガスは、パターン側壁のアンダーカット防止のための側壁保護のために好ましく用いられる。
　一方、３層プロセスにおける中間層のエッチングにおいても、ガスエッチングが好ましく用いられる。ガスエッチングとしては、上述の２層プロセスにおいて説明したものと同様のものが適用可能である。とりわけ、３層プロセスにおける中間層の加工は、フロン系のガスを用いてレジストパターンをマスクにして行うことが好ましい。その後、上述したように中間層パターンをマスクにして、例えば酸素ガスエッチングを行うことで、下層膜の加工を行うことができる。
　ここで、中間層として無機ハードマスク中間層膜を形成する場合は、ＣＶＤ法や原子層堆積（ＡＬＤ）法等で、珪素酸化膜、珪素窒化膜、珪素酸化窒化膜（ＳｉＯＮ膜）が形成される。窒化膜の形成方法としては、以下に限定されないが、例えば、特開２００２－３３４８６９号公報、国際公開第２００４／０６６３７７号に記載された方法を用いることができる。このような中間層膜の上に直接フォトレジスト膜を形成することができるが、中間層膜の上に有機反射防止膜（ＢＡＲＣ）をスピンコートで形成して、その上にフォトレジスト膜を形成してもよい。
　中間層として、ポリシルセスキオキサンベースの中間層も好ましく用いられる。レジスト中間層膜に反射防止膜として効果を持たせることによって、効果的に反射を抑えることができる傾向にある。ポリシルセスキオキサンベースの中間層の具体的な材料については、以下に限定されないが、例えば、特開２００７－２２６１７０号、特開２００７－２２６２０４号公報に記載されたものを用いることができる。
　また、次の基板のエッチングも、常法によって行うことができ、例えば、基板がＳｉＯ２、ＳｉＮであればフロン系ガスを主体としたエッチング、ｐ－ＳｉやＡｌ、Ｗでは塩素系、臭素系ガスを主体としたエッチングを行うことができる。基板をフロン系ガスでエッチングする場合、２層レジストプロセスの珪素含有レジストと３層プロセスの珪素含有中間層は、基板加工と同時に剥離される。一方、塩素系或いは臭素系ガスで基板をエッチングした場合は、珪素含有レジスト層又は珪素含有中間層の剥離が別途行われ、一般的には、基板加工後にフロン系ガスによるドライエッチング剥離が行われる。
　本実施形態における下層膜は、これら基板のエッチング耐性に優れる特徴がある。なお、基板は、公知のものを適宜選択して使用することができ、特に限定されないが、Ｓｉ、α－Ｓｉ、ｐ－Ｓｉ、ＳｉＯ２、ＳｉＮ、ＳｉＯＮ、Ｗ、ＴｉＮ、Ａｌ等が挙げられる。また、基板は、基材（支持体）上に被加工膜（被加工基板）を有する積層体であってもよい。このような被加工膜としては、Ｓｉ、ＳｉＯ２、ＳｉＯＮ、ＳｉＮ、ｐ－Ｓｉ、α－Ｓｉ、Ｗ、Ｗ－Ｓｉ、Ａｌ、Ｃｕ、Ａｌ－Ｓｉ等種々のＬｏｗ－ｋ膜及びそのストッパー膜等が挙げられ、通常、基材（支持体）とは異なる材質のものが用いられる。なお、加工対象となる基板或いは被加工膜の厚さは、特に限定されないが、通常、５０～１，０００，０００ｎｍ程度であることが好ましく、より好ましくは７５～５００，０００ｎｍである。
［レジスト永久膜］
　なお、本実施形態の膜形成用組成物を用いてレジスト永久膜を作製することもできる、本実施形態の膜形成用組成物を基材等に塗布してなるレジスト永久膜は、必要に応じてレジストパターンを形成した後、最終製品にも残存する永久膜として好適である。永久膜の具体例としては、特に限定されないが、例えば、半導体デバイス関係では、ソルダーレジスト、パッケージ材、アンダーフィル材、回路素子等のパッケージ接着層や集積回路素子と回路基板の接着層、薄型ディスプレー関連では、薄膜トランジスタ保護膜、液晶カラーフィルター保護膜、ブラックマトリクス、スペーサーなどが挙げられる。特に、本実施形態の膜形成用組成物からなる永久膜は、耐熱性や耐湿性に優れている上に昇華成分による汚染性が少ないという非常に優れた利点も有する。特に表示材料において、重要な汚染による画質劣化の少ない高感度、高耐熱、吸湿信頼性を兼ね備えた材料となる。
　本実施形態の膜形成用組成物をレジスト永久膜用途に用いる場合には、硬化剤の他、更に必要に応じてその他の樹脂、界面活性剤や染料、充填剤、架橋剤、溶解促進剤などの各種添加剤を加え、有機溶剤に溶解することにより、レジスト永久膜用組成物とすることができる。
　本実施形態の膜形成用組成物をレジスト永久膜用とする場合、前記各成分を配合し、攪拌機等を用いて混合することによりレジスト永久膜用組成物を調製できる。また、本実施形態の膜形成用組成物が充填剤や顔料を含有する場合には、ディゾルバー、ホモジナイザー、３本ロールミル等の分散装置を用いて分散或いは混合してレジスト永久膜用組成物を調製することができる。
［光学部材形成用組成物］
　本実施形態の膜形成用組成物は、光学部材形成（又は光学部品形成）用として使用することもできる。すなわち、本実施形態の光学部材形成用組成物は、本実施形態の膜形成用組成物を含有するものである。換言すると、本実施形態の光学部材形成用組成物は、本実施形態における重合体を必須成分として含有するものである。ここで、「光学部材」（又は「光学部品」）とは、フィルム状、シート状の部品の他、プラスチックレンズ（プリズムレンズ、レンチキュラーレンズ、マイクロレンズ、フレネルレンズ、視野角制御レンズ、コントラスト向上レンズ等）、位相差フィルム、電磁波シールド用フィルム、プリズム、光ファイバー、フレキシブルプリント配線用ソルダーレジスト、メッキレジスト、多層プリント配線板用層間絶縁膜、感光性光導波路をいう。本実施形態における重合体はこれら光学部材形成用途に有用である。本実施形態の光学部材形成用組成物は、光学部材形成材料として用いられることを考慮し、種々の任意成分をさらに含有することができる。具体的には、本実施形態の光学部材形成用組成物は、溶媒、酸発生剤及び架橋剤で構成される群から選択される少なくとも１つをさらに含有することが好ましい。溶媒、酸発生剤及び架橋剤として使用し得る具体例としては、前述した本実施形態のリソグラフィー用下層膜形成用組成物に含まれ得る各成分と同様とすることができ、その配合比としても、具体的な用途を考慮して適宜設定することができる。
　以下、実施例及び比較例を示し、本実施形態をさらに詳細に説明するが、本実施形態はこれらに限定されるものではない。
（化合物の構造）
　１Ｈ－ＮＭＲ測定については、Ｂｒｕｋｅｒ社製「Ａｄｖａｎｃｅ６００ＩＩ　ｓｐｅｃｔｒｏｍｅｔｅｒ」を用いて、以下の条件にて行った。
　周波数：４００ＭＨｚ
　溶媒：ｄ６－ＤＭＳＯ
　内部標準：ＴＭＳ
　測定温度：２３℃
（分子量）
　化合物の分子量は、ＬＣ－ＭＳ（Ｌｉｑｕｉｄ　Ｃｈｒｏｍａｔｏｇｒａｐｈｙ－Ｍａｓｓ　ｓｐｅｃｔｒｏｍｅｔｒｙ）分析により、Ｗａｔｅｒ社製Ａｃｑｕｉｔｙ　ＵＰＬＣ／ＭＡＬＤＩ－Ｓｙｎａｐｔ　ＨＤＭＳを用いて測定した。
（ポリスチレン換算分子量）
　ゲル浸透クロマトグラフィー（ＧＰＣ）分析により、ポリスチレン換算の重量平均分子量（Ｍｗ）、数平均分子量（Ｍｎ）を求め、分散度（Ｍｗ／Ｍｎ）を求めた。
　装置：Ｓｈｏｄｅｘ　ＧＰＣ－１０１型（昭和電工（株）製）
　カラム：ＫＦ－８０Ｍ×３
　溶離液：ＴＨＦ　１ｍＬ／ｍｉｎ
　温度：４０℃
［合成実施例１－１］重合体（Ｒ１－１）の合成
　攪拌機、冷却管及びビュレットを備えた内容積５００ｍＬの容器に、下記式で表されるレゾルシノール（東京化成工業（株）製）１１．０ｇ（１００ｍｍｏｌ）とフタル酸モノブチル銅１０．１ｇ（２０ｍｍｏｌ）とを仕込み、溶媒としてクロロホルムを１００ｍＬ加えて、反応液を６１℃で６時間撹拌して反応を行った。
Figure JPOXMLDOC01-appb-C000062
  
　次いで、冷却後に析出物を濾過し、得られた粗体をトルエン１００ｍＬに溶解させた。次に得られたトルエン溶液に塩酸５ｍＬを加え、室温で攪拌後、炭酸水素ナトリウムで中和処理を行った。トルエン溶液を濃縮し、メタノール２００ｍＬを加えて反応生成物を析出させ、室温まで冷却した後、濾過を行って固形物を分離した。得られた固形物を乾燥させることにより、下記式で表される構造を有する重合体（Ｒ１－１）２０．０ｇを得た。
　得られた重合体について、上述の方法によりポリスチレン換算分子量を測定した結果、Ｍｎ：８８０、Ｍｗ：１１５０、Ｍｗ／Ｍｎ：１．３であった。
　得られた重合体について、上述の測定条件でＮＭＲ測定を行ったところ、以下のピークが見出され、下記式の化学構造を有し且つ芳香環同士が直接結合していることを確認した。
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）；Ｐｈ－Ｈは芳香環のプロトンを示す。
Figure JPOXMLDOC01-appb-C000063
  
［合成実施例１－２～１－４］重合体（Ｒ１－２～Ｒ１－４）の合成
　合成実施例１－２～１－４において、レゾルシノールの代わりに、それぞれ、１，３－ジメトキシベンゼン、アニリン、又は、Ｎ，Ｎ－ジメチルアニリンを使用したことを除き、合成実施例１－１と同様に重合体（Ｒ１－２）～（Ｒ１－４）を合成した。
Figure JPOXMLDOC01-appb-C000064
  
　下記に示すように重合体（Ｒ１－２）～（Ｒ１－４）において、４００ＭＨｚ－１Ｈ－ＮＭＲにより以下のピークが見出され、各々前記式の化学構造を基本構造として有し且つ構成単位の芳香環同士が直接結合した構造を有する重合体であることを確認した。さらに、得られた各重合体について、上述の方法によりポリスチレン換算分子量を測定した結果を併せて示す。
（Ｒ１－２）
　Ｍｎ：８８８、Ｍｗ：１１８０、Ｍｗ／Ｍｎ：１．３
　δ（ｐｐｍ）６．３～７．３（２Ｈ，Ｐｈ－Ｈ）、３．８（６Ｈ，－ＣＨ３）
（Ｒ１－３）　Ｍｎ：６２８、Ｍｗ：８９８、Ｍｗ／Ｍｎ：１．４
　δ（ｐｐｍ）６．７～７．２（３Ｈ，Ｐｈ－Ｈ）、５．０（２Ｈ，－ＮＨ２）
（Ｒ１－４）
　Ｍｎ：６２２、Ｍｗ：８８６、Ｍｗ／Ｍｎ：１．４
　δ（ｐｐｍ）６．７～７．２（３Ｈ，Ｐｈ－Ｈ）、３．０（６Ｈ，－Ｎ（ＣＨ３）２）
［合成実施例１Ａ－１］重合体（Ｒ１Ａ－１）の合成
　攪拌機、冷却管及びビュレットを備えた内容積１０００ｍＬの容器に、下記式で表されるレゾルシノール（東京化成工業（株）製）１１．０ｇ（１００ｍｍｏｌ）、化合物（１Ａ－１）４６．７ｇ（１００ｍｍｏｌ）と、フタル酸モノブチル銅２０．２ｇ（４０ｍｍｏｌ）とを仕込み、溶媒としてクロロホルムを２００ｍＬ加えて、反応液を６１℃で６時間撹拌して反応を行った。
Figure JPOXMLDOC01-appb-C000065
  
　次いで、冷却後に析出物を濾過し、得られた粗体をトルエン２００ｍＬに溶解させた。次に得られたトルエン溶液に塩酸１０ｍＬを加え、室温で攪拌後、炭酸水素ナトリウムで中和処理を行った。トルエン溶液を濃縮し、メタノール４００ｍＬを加えて反応生成物を析出させ、室温まで冷却した後、濾過を行って固形物を分離した。得られた固形物を乾燥させることにより、下記式で表される構造を有する重合体（Ｒ１Ａ－１）５２．０ｇを得た。
　得られた重合体について、上述の方法によりポリスチレン換算分子量を測定した結果、Ｍｎ：４６８２、Ｍｗ：５８５０、Ｍｗ／Ｍｎ：１．２であった。
　得られた重合体について、上述の測定条件でＮＭＲ測定を行ったところ、以下のピークが見出され、下記式の化学構造を有し且つ構成単位の芳香環同士が直接結合していることを確認した。
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．３～９．７（２Ｈ，Ｏ－Ｈ）、７．２～８．５（１７Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
Figure JPOXMLDOC01-appb-C000066
  
　　　　　　　　　　　　　　　（Ｒ１Ａ－１）
［合成実施例１Ａ－１ａ～１Ａ－１ｂ］重合体（Ｒ１Ａ－１ａ）～（Ｒ１Ａ－１ｂ）の合成
　合成実施例１Ａ－１ａにおいて、クロロホルムの代わりにブタノールを用い、フタル酸モノブチル銅の代わりに酢酸銅一水和物を用い、反応液を“６１℃で６時間撹拌”の代わりに“１１０℃で１２時間撹拌”を適用したことを除き、合成実施例１Ａ－１と同様に重合体（Ｒ１Ａ－１ａ）を合成した。
　合成実施例１Ａ－１ｂにおいて、さらに、レゾルシノール１１．０ｇ（１００ｍｍｏｌ）、及び、化合物（１Ａ－１）４６．７ｇ（１００ｍｍｏｌ）の代わりに、レゾルシノール７．４ｇ（６７ｍｍｏｌ）、及び、化合物（１Ａ－１）１５．４ｇ（３３ｍｍｏｌ）を用いたことを除き、合成実施例１Ａ－１ａと同様に重合体（Ｒ１Ａ－１ｂ）を合成した。
　なお、下記に示すように、重合体（Ｒ１Ａ－１ａ）～（Ｒ１Ａ－１ｂ）において、４００ＭＨｚ－１Ｈ－ＮＭＲにより以下のピークが見出され、各々前記式の化学構造を基本構造として有し且つ構成単位の芳香環同士が直接結合した構造を有することを確認した。さらに、得られた各重合体について、上述の方法によりポリスチレン換算分子量を測定した結果を併せて示す。
（Ｒ１Ａ－１ａ）
　Ｍｎ：４２６４、Ｍｗ：６８６１、Ｍｗ／Ｍｎ：１．６
δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．３～９．７（２Ｈ，Ｏ－Ｈ）、７．２～８．５（１７Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
（Ｒ１Ａ－１ｂ）
　Ｍｎ：６３８０、Ｍｗ：１１０５０、Ｍｗ／Ｍｎ：１．７
δ（ｐｐｍ）１０．０（１３Ｈ，－ＯＨ）、９．３～９．７（６Ｈ，Ｏ－Ｈ）、７．２～８．５（５１Ｈ，Ｐｈ－Ｈ）、６．３～７．０（１３Ｈ，Ｐｈ－Ｈ）、６．７～６．９（３Ｈ，Ｃ－Ｈ）
［合成実施例１Ａ－２～１Ａ－１５］重合体（Ｒ１Ａ－２）～（Ｒ１Ａ－１５）の合成
　合成実施例１Ａ－２～１Ａ－１５において、化合物（１Ａ－１）の代わりに、それぞれ、下記化合物（１Ａ－２）～（１Ａ－１５）を使用したことを除き、合成実施例１Ａ－１と同様に重合体（Ｒ１Ａ－２）～（Ｒ１Ａ－１５）を合成した。
Figure JPOXMLDOC01-appb-C000067
  
Figure JPOXMLDOC01-appb-C000068
  
　なお、下記に示すように、重合体（Ｒ１Ａ－２）～（Ｒ１Ａ－１５）において、４００ＭＨｚ－１Ｈ－ＮＭＲにより以下のピークが見出され、各々前記式の化学構造を基本構造として有し且つ構成単位の芳香環同士が直接結合した構造を有することを確認した。さらに、得られた各重合体について、上述の方法によりポリスチレン換算分子量を測定した結果を併せて示す。
（Ｒ１Ａ－２）
　Ｍｎ：８２４、Ｍｗ：１１２２、Ｍｗ／Ｍｎ：１．４
δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．３～９．７（２Ｈ，Ｏ－Ｈ）、７．２～８．５（１３Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
（Ｒ１Ａ－３）
　Ｍｎ：８５７、Ｍｗ：１１０２、Ｍｗ／Ｍｎ：１．３
δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．３～９．７（２Ｈ，Ｏ－Ｈ）、７．２～８．５（１５Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
（Ｒ１Ａ－４）
　Ｍｎ：９０４、Ｍｗ：１２４８、Ｍｗ／Ｍｎ：１．４
δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．３～９．７（２Ｈ，Ｏ－Ｈ）、７．２～８．５（１７Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
（Ｒ１Ａ－５）
　Ｍｎ：８９２、Ｍｗ：１０５５、Ｍｗ／Ｍｎ：１．２
δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．３～９．７（２Ｈ，Ｏ－Ｈ）、７．２～８．５（１７Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
（Ｒ１Ａ－６）
　Ｍｎ：９０２、Ｍｗ：１２１２、Ｍｗ／Ｍｎ：１．３
δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．３～９．７（２Ｈ，Ｏ－Ｈ）、７．２～８．５（１７Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
（Ｒ１Ａ－７）
　Ｍｎ：８５６、Ｍｗ：１１９２、Ｍｗ／Ｍｎ：１．４
δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．３～９．７（２Ｈ，Ｏ－Ｈ）、７．２～８．５（１７Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
（Ｒ１Ａ－８）
　Ｍｎ：８７６、Ｍｗ：１１４０、Ｍｗ／Ｍｎ：１．３
δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．３～９．７（４Ｈ，Ｏ－Ｈ）、７．２～８．５（１７Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
（Ｒ１Ａ－９）
　Ｍｎ：８５２、Ｍｗ：１１０４、Ｍｗ／Ｍｎ：１．３
δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．３～９．７（４Ｈ，Ｏ－Ｈ）、７．２～８．５（１５Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
（Ｒ１Ａ－１０）
　Ｍｎ：９００、Ｍｗ：１２０２、Ｍｗ／Ｍｎ：１．３
δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．３～９．７（４Ｈ，Ｏ－Ｈ）、７．２～８．５（１７Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
（Ｒ１Ａ－１１）
　Ｍｎ：９２２、Ｍｗ：１２４６、Ｍｗ／Ｍｎ：１．４
δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．３～９．７（２Ｈ，Ｏ－Ｈ）、７．２～８．５（２３Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
（Ｒ１Ａ－１２）
　Ｍｎ：８５６、Ｍｗ：１１６８、Ｍｗ／Ｍｎ：１．４
δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．３～９．７（２Ｈ，Ｏ－Ｈ）、７．２～８．５（２１Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
（Ｒ１Ａ－１３）
　Ｍｎ：８９２、Ｍｗ：１１９６、Ｍｗ／Ｍｎ：１．３
δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．３～９．７（２Ｈ，Ｏ－Ｈ）、７．２～８．５（１３Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）、２．０～２．１（６Ｈ，ーＣＨ３）
（Ｒ１Ａ－１４）
　Ｍｎ：８９８、Ｍｗ：１１９２、Ｍｗ／Ｍｎ：１．３
δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．３～９．７（４Ｈ，Ｏ－Ｈ）、７．２～８．５（２１Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
（Ｒ１Ａ－１５）
　Ｍｎ：８９８、Ｍｗ：１２２２、Ｍｗ／Ｍｎ：１．４
δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．３～９．７（２Ｈ，Ｏ－Ｈ）、７．２～８．５（１９Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
［合成実施例１Ｂ－１］重合体（Ｒ１Ｂ－１）の合成
　攪拌機、冷却管及びビュレットを備えた内容積１０００ｍＬの容器に、下記式で表されるレゾルシノール（東京化成工業（株）製）１１．０ｇ（１００ｍｍｏｌ）と、２－ナフトール（東京化成工業（株）製）（下記化合物１Ｂ－１）１４．４ｇ（１００ｍｍｏｌ）と、フタル酸モノブチル銅２０．２ｇ（４０ｍｍｏｌ）と、を仕込み、溶媒としてクロロホルムを２００ｍＬ加えて、反応液を６１℃で６時間撹拌して反応を行った。
Figure JPOXMLDOC01-appb-C000069
  
　次いで、冷却後に析出物を濾過し、得られた粗体をトルエン２００ｍＬに溶解させた。次に得られたトルエン溶液に塩酸１０ｍＬを加え、室温で攪拌後、炭酸水素ナトリウムで中和処理を行った。トルエン溶液を濃縮し、メタノール４００ｍＬを加えて反応生成物を析出させ、室温まで冷却した後、濾過を行って固形物を分離した。得られた固形物を乾燥させることにより、下記式で表される構造を有する重合体（Ｒ１Ｂ－１）２１．０ｇを得た。
　得られた重合体について、上述の方法によりポリスチレン換算分子量を測定した結果、Ｍｎ：８２４、Ｍｗ：１００２、Ｍｗ／Ｍｎ：１．２であった。
　得られた重合体について、上述の測定条件でＮＭＲ測定を行ったところ、以下のピークが見出され、下記式の化学構造を有し且つ構成単位の芳香環同士が直接結合していることを確認した。
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．２（１Ｈ，－ＯＨ）、７．１～８．０（５Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）
Figure JPOXMLDOC01-appb-C000070
  
［合成実施例１Ｂ－２～１Ｂ－８］重合体（Ｒ１Ｂ－２）～（Ｒ１Ｂ－８）の合成
　合成実施例１Ｂ－２～１Ｂ－８において、化合物（１Ｂ－１）の代わりに、それぞれ、下記化合物（１Ｂ－２）～（１Ｂ－８）を使用したことを除き、合成実施例１Ｂ－１と同様に重合体（Ｒ１Ｂ－２）～（Ｒ１Ｂ－８）を合成した。
Figure JPOXMLDOC01-appb-C000071
  
　なお、下記に示すように、重合体（Ｒ１Ｂ－２）～（Ｒ１Ｂ－８）において、４００ＭＨｚ－１Ｈ－ＮＭＲにより以下のピークが見出され、各々前記式の化学構造を基本構造として有し且つ構成単位の芳香環同士が直接結合した構造を有することを確認した。さらに、得られた各重合体について、上述の方法によりポリスチレン換算分子量を測定した結果を併せて示す。
（Ｒ１Ｂ－２）
　Ｍｎ：８９８、Ｍｗ：１１１５、Ｍｗ／Ｍｎ：１．２
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．２（１Ｈ，－ＯＨ）、７．１～８．０（５Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）
（Ｒ１Ｂ－３）
　Ｍｎ：９２０、Ｍｗ：１２２２、Ｍｗ／Ｍｎ：１．３
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．２（２Ｈ，－ＯＨ）、７．１～８．０（４Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）
（Ｒ１Ｂ－４
　Ｍｎ：９００、Ｍｗ：１１５６、Ｍｗ／Ｍｎ：１．３
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．２（２Ｈ，－ＯＨ）、７．１～８．０（４Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）
（Ｒ１Ｂ－５）
　Ｍｎ：８０２、Ｍｗ：９６６、Ｍｗ／Ｍｎ：１．２
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．２（２Ｈ，－ＯＨ）、７．１～８．０（４Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）
（Ｒ１Ｂ－６）
　Ｍｎ：８２２、Ｍｗ：１０１２、Ｍｗ／Ｍｎ：１．２
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．２（２Ｈ，－ＯＨ）、７．１～８．０（４Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）
（Ｒ１Ｂ－７）
　Ｍｎ：８０２、Ｍｗ：９６５、Ｍｗ／Ｍｎ：１．２
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．２（２Ｈ，－ＯＨ）、７．１～８．０（４Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）
（Ｒ１Ｂ－８）
　Ｍｎ：８００、Ｍｗ：９７０、Ｍｗ／Ｍｎ：１．２
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．２（２Ｈ，－ＯＨ）、７．１～８．０（４Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）
［合成実施例１Ｃ－１］重合体（Ｒ１Ｃ－１）の合成
　攪拌機、冷却管及びビュレットを備えた内容積１０００ｍＬの容器に、下記式で表されるレゾルシノール（東京化成工業（株）製）１１．０ｇ（１００ｍｍｏｌ）と、化合物１Ｃ－１（２９．０ｇ（１００ｍｍｏｌ）と、フタル酸モノブチル銅２０．２ｇ（４０ｍｍｏｌ）と、を仕込み、溶媒としてクロロホルムを２００ｍＬ加えて、反応液を６１℃で６時間撹拌して反応を行った。
Figure JPOXMLDOC01-appb-C000072
  
　次いで、冷却後に析出物を濾過し、得られた粗体をトルエン２００ｍＬに溶解させた。次にトルエン溶液に塩酸１０ｍＬを加え、室温で攪拌後、炭酸水素ナトリウムで中和処理を行った。トルエン溶液を濃縮し、メタノール４００ｍＬを加えて反応生成物を析出させ、室温まで冷却した後、濾過を行って固形物を分離した。得られた固形物を乾燥させることにより、下記式で表される構造を有する重合体（Ｒ１Ｃ－１）２９．０ｇを得た。
　得られた重合体について、上述の方法によりポリスチレン換算分子量を測定した結果、Ｍｎ：１０２４、Ｍｗ：１２４２、Ｍｗ／Ｍｎ：１．２であった。
　得られた重合体について、上述の測定条件でＮＭＲ測定を行ったところ、以下のピークが見出され、下記式の化学構造を有し且つ構成単位の芳香環同士が直接結合していることを確認した。
　δ（ｐｐｍ）δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．１（２Ｈ，－ＯＨ）、６．２～７．１（１４Ｈ，－Ｐｈ）、４．１（４Ｈ，－ＣＨ２－）
Figure JPOXMLDOC01-appb-C000073
  
［合成実施例１Ｃ－２～１Ｃ－４］重合体（Ｒ１Ｃ－２）～（Ｒ１Ｃ－４）の合成
　合成実施例１Ｃ－２～１Ｃ－４において、化合物（１Ｃ－１）の代わりに、それぞれ、下記化合物（１Ｃ－２）～（１Ｃ－４）を使用したことを除き、合成実施例１Ｃ－１と同様に重合体（Ｒ１Ｃ－２）～（Ｒ１Ｃ－４）を合成した。
Figure JPOXMLDOC01-appb-C000074
  
　なお、下記に示すように重合体、重合体（Ｒ１Ｃ－２）～（Ｒ１Ｃ－４）において、４００ＭＨｚ－１Ｈ－ＮＭＲにより以下のピークが見出され、各々前記式の化学構造を基本構造として有し且つ構成単位の芳香環同士が直接結合した構造を有することを確認した。さらに、得られた各重合体について、上述の方法によりポリスチレン換算分子量を測定した結果を併せて示す。
（Ｒ１Ｃ－２）
Ｍｎ：１００１、Ｍｗ：１２２１、Ｍｗ／Ｍｎ：１．２
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．１（２Ｈ，－ＯＨ）、６．２～７．１（１６Ｈ，－Ｐｈ）、４．１（４Ｈ，－ＣＨ２－）
（Ｒ１Ｃ－３）
Ｍｎ：１００２、Ｍｗ：１１９８、Ｍｗ／Ｍｎ：１．２
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．１（２Ｈ，－ＯＨ）、６．２～７．１（１８Ｈ，－Ｐｈ）、４．１（４Ｈ，－ＣＨ２－）
（Ｒ１Ｃ－４）
Ｍｎ：１００２、Ｍｗ：１１２０、Ｍｗ／Ｍｎ：１．１
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．１（２Ｈ，－ＯＨ）、６．２～７．１（２２Ｈ，－Ｐｈ）、４．１（４Ｈ，－ＣＨ２－）
［合成実施例１Ｄ－１］重合体（Ｒ１Ｄ－１）の合成
　攪拌機、冷却管及びビュレットを備えた内容積１０００ｍＬの容器に、下記式で表されるレゾルシノール（東京化成工業（株）製）１１．０ｇ（１００ｍｍｏｌ）、４－ｔ－ブチルカリックス［４］アレーン（東京化成工業（株）製）（化合物１Ｄ－１）６４．９ｇ（１００ｍｍｏｌ）と、フタル酸モノブチル銅２０．２ｇ（４０ｍｍｏｌ）と、を仕込み、溶媒としてクロロホルムを２００ｍＬ加えて、反応液を６１℃で６時間撹拌して反応を行った。
Figure JPOXMLDOC01-appb-C000075
  
　次いで、冷却後に析出物を濾過し、得られた粗体をトルエン２００ｍＬに溶解させた。次に得られたトルエン溶液に塩酸１０ｍＬを加え、室温で攪拌後、炭酸水素ナトリウムで中和処理を行った。トルエン溶液を濃縮し、メタノール４００ｍＬを加えて反応生成物を析出させ、室温まで冷却した後、濾過を行って固形物を分離した。得られた固形物を乾燥させることにより、下記式で表される構造を有する重合体（Ｒ１Ｄ－１）６４．０ｇを得た。
　得られた重合体について、上述の方法によりポリスチレン換算分子量を測定した結果、Ｍｎ：４０８４、Ｍｗ：５２１２、Ｍｗ／Ｍｎ：１．３であった。
　得られた重合体について、上述の測定条件でＮＭＲ測定を行ったところ、以下のピークが見出され、下記式の化学構造を有し且つ構成単位の芳香環同士が直接結合していることを確認した。
　δ（ｐｐｍ）１０．２（４Ｈ，Ｏ－Ｈ）、１０．０（２Ｈ，－ＯＨ）、７．１～７．３（６Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、３．５～４．３（８Ｈ，Ｃ－Ｈ）、１．２（３６Ｈ，－ＣＨ３）
Figure JPOXMLDOC01-appb-C000076
  
［合成実施例１Ｄ－２～１Ｄ－５］重合体（Ｒ１Ｄ－２）～（Ｒ１Ｄ－５）の合成
　合成実施例１Ｄ－２～１Ｄ－５において、化合物（１Ｄ－１）の代わりに、それぞれ、下記化合物（１Ｄ－２）～（１Ｄ－５）を使用したことを除き、合成実施例１Ｄ－１と同様に重合体（Ｒ１Ｄ－２）～（Ｒ１Ｄ－５）を合成した。
Figure JPOXMLDOC01-appb-C000077
  
　なお、下記に示すように、重合体（Ｒ１Ｄ－２）～（Ｒ１Ｄ－５）において、４００ＭＨｚ－１Ｈ－ＮＭＲにより以下のピークが見出され、各々前記式の化学構造を基本構造として有し且つ構成単位の芳香環同士が直接結合した構造を有することを確認した。さらに、得られた各重合体について、上述の方法によりポリスチレン換算分子量を測定した結果を併せて示す。
（Ｒ１Ｄ－２）
　Ｍｎ：４０２４、Ｍｗ：５２０２、Ｍｗ／Ｍｎ：１．３
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、８．４～８．５（８Ｈ，Ｏ－Ｈ）、６．０～７．０（２４Ｈ，Ｐｈ－Ｈ）、５．５～５．６（４Ｈ，Ｃ－Ｈ）、０．８～１．９（４４Ｈ，－シクロヘキシル基）
（Ｒ１Ｄ－３）
　Ｍｎ：３９８０、Ｍｗ：５００２、Ｍｗ／Ｍｎ：１．３
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、８．４～８．５（８Ｈ，Ｏ－Ｈ）、６．０～７・０（２４Ｈ，Ｐｈ－Ｈ）、５．５～５．６（４Ｈ，Ｃ－Ｈ）
（Ｒ１Ｄ－４）
　Ｍｎ：３８９８、Ｍｗ：４９８８、Ｍｗ／Ｍｎ：１．３
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．０～９．６（１２Ｈ，Ｏ－Ｈ）、５．９～８．７（３６Ｈ，Ｐｈ－Ｈ，Ｃ－Ｈ）
（Ｒ１Ｄ－５）
　Ｍｎ：４０３４、Ｍｗ：５１１２、Ｍｗ／Ｍｎ：１．３
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．２～９．６（８Ｈ，Ｏ－Ｈ）、５．９～８．７（３６Ｈ，Ｐｈ－Ｈ，Ｃ－Ｈ）
［合成実施例１Ｅ－１］重合体（Ｒ１Ｅ－１）の合成
　攪拌機、冷却管及びビュレットを備えた内容積１０００ｍＬの容器に、下記式で表されるレゾルシノール（東京化成工業（株）製）１１．０ｇ（１００ｍｍｏｌ）、インドール（化合物１Ｅ－１）１１．７ｇ（１００ｍｍｏｌ）とフタル酸モノブチル銅を２０．２ｇ（４０ｍｍｏｌ）仕込み、溶媒としてクロロホルムを２００ｍＬ加えて、反応液を６１℃で６時間撹拌して反応を行った。
Figure JPOXMLDOC01-appb-C000078
  
　次いで、冷却後に析出物を濾過し、得られた粗体をトルエン２００ｍＬに溶解させた。次に得られたトルエン溶液に塩酸１０ｍＬを加え、室温で攪拌後、炭酸水素ナトリウムで中和処理を行った。トルエン溶液を濃縮し、メタノール４００ｍＬを加えて反応生成物を析出させ、室温まで冷却した後、濾過を行って固形物を分離した。得られた固形物を乾燥させることにより、下記式で表される構造を有する重合体（Ｒ１Ｅ－１）１２．２ｇを得た。
　得られた重合体について、上述の方法によりポリスチレン換算分子量を測定した結果、Ｍｎ：１０５０、Ｍｗ：１２５０、Ｍｗ／Ｍｎ：１．２であった。
　得られた重合体について、上述の測定条件でＮＭＲ測定を行ったところ、以下のピークが見出され、下記式の化学構造を有し且つ構成単位の芳香環同士が直接結合していることを確認した。
　δ（ｐｐｍ）１０．１（１Ｈ，Ｎ－Ｈ）、１０．０（２Ｈ，－ＯＨ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．４～７．６（４Ｈ，Ｐｈ－Ｈ）
Figure JPOXMLDOC01-appb-C000079
  
［合成実施例１Ｅ－２～１Ｅ－６］重合体（Ｒ１Ｅ－２）～（Ｒ１Ｅ－６）の合成
　合成実施例１Ｅ－２～１Ｅ－６において、化合物（１Ｄ－１）の代わりに、それぞれ、下記化合物（１Ｅ－２）～（１Ｅ－６）を使用したことを除き、合成実施例１Ｄ－１と同様に重合体を合成した。
Figure JPOXMLDOC01-appb-C000080
  
　なお、下記に示すように重合体（Ｒ１Ｅ－２）～（Ｒ１Ｅ－６）において、４００ＭＨｚ－１Ｈ－ＮＭＲにより以下のピークが見出され、各々前記式の化学構造を基本構造として有し且つ構成単位の芳香環同士が直接結合した構造を有することを確認した。さらに、得られた各重合体について、上述の方法によりポリスチレン換算分子量を測定した結果を併せて示す。
（Ｒ１Ｅ－２）
　Ｍｎ：１０００、Ｍｗ：１２２８、Ｍｗ／Ｍｎ：１．２
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、７．３～８．２（７Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）
（Ｒ１Ｅ－３）
　Ｍｎ：１０１２、Ｍｗ：１２２０、Ｍｗ／Ｍｎ：１．２
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、７．５～８．２（７Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）（Ｒ１Ｅー４）
（Ｒ１Ｅ－４）
　Ｍｎ：９８９、Ｍｗ：１１９８、Ｍｗ／Ｍｎ：１．２
　δ（ｐｐｍ）１２．１（１Ｈ，Ｎ－Ｈ）、１０．０（２Ｈ，－ＯＨ）、７．２～８．２（６Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）（Ｒ１Ｅー５）
（Ｒ１Ｅ－５）
　Ｍｎ：９９６、Ｍｗ：１１８６、Ｍｗ／Ｍｎ：１．２
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、７．４～８．５（６Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）（Ｒ１Ｅー６）
（Ｒ１Ｅ－６）
　Ｍｎ：９９８、Ｍｗ：１１９８、Ｍｗ／Ｍｎ：１．２
　δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、７．３～８．０（６Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）
［比較合成例１］ＮＢｉｓＮ－１の合成
　攪拌機、冷却管及びビュレットを備えた内容積５００ｍＬの容器に、２，７－ナフタレンジオール（シグマ－アルドリッチ社製試薬）３２．０ｇ（２００ｍｍｏｌ）と、４－ビフェニルアルデヒド（三菱瓦斯化学（株）製）１８．２ｇ（１００ｍｍｏｌ）と、１，４－ジオキサン２００ｍＬと、を仕込み、９５％の硫酸１０ｍＬを加えて、１００℃で６時間撹拌して反応を行った。次に、２４％水酸化ナトリウム水溶液にて反応液を中和し、純水１００ｇを加えて反応生成物を析出させ、室温まで冷却した後、濾過を行って固形物を分離した。得られた固形物を乾燥させた後、カラムクロマトによる分離精製を行うことにより、下記式で表される目的化合物（ＢｉｓＮ－１）２５．５ｇを得た。
　なお、４００ＭＨｚ－１Ｈ－ＮＭＲにより以下のピークが見出され、得られた化合物が下記式の化学構造を有することを確認した。また、２，７－ジヒドロキシナフトールの置換位置が１位であることは、３位と４位のプロトンのシグナルがダブレットであることから確認した。
　１Ｈ－ＮＭＲ：（ｄ－ＤＭＳＯ、内部標準ＴＭＳ）
　δ（ｐｐｍ）９．６（２Ｈ，Ｏ－Ｈ）、７．２～８．５（１９Ｈ，Ｐｈ－Ｈ）、６．６（１Ｈ，Ｃ－Ｈ）
　また、ＬＣ－ＭＳ分析により、分子量が下記化学構造相当の４６６であることが確認された。
Figure JPOXMLDOC01-appb-C000081
  
　攪拌機、冷却管及びビュレットを備えた内容積１００ｍｌの容器に、ＢｉｓＮ－１を１０ｇ（２１ｍｍｏｌ）と、パラホルムアルデヒドを０．７ｇ（４２ｍｍｏｌ）と、氷酢酸を５０ｍＬと、ＰＧＭＥを５０ｍＬとを仕込み、９５％の硫酸を８ｍＬ加えて、反応液を１００℃で６時間撹拌して反応を行った。次に、反応液を濃縮し、メタノール１０００ｍＬを加えて反応生成物を析出させ、室温まで冷却した後、濾過を行って固形物を分離した。得られた固形物を濾過し、乾燥させることにより、下記式で示される構造を有する重合体（ＮＢｉｓＮ－１）７．２ｇを得た。
　得られた重合体について、上述の方法によりポリスチレン換算分子量を測定した結果、Ｍｎ：１２７８、Ｍｗ：１９９３、Ｍｗ／Ｍｎ：１．５６であった。
　得られた重合体について、前記測定条件でＮＭＲ測定を行ったところ、以下のピークが見出され、下記式の化学構造を有することを確認した。
　δ（ｐｐｍ）９．７（２Ｈ，Ｏ－Ｈ）、７．２～８．５（１７Ｈ，Ｐｈ－Ｈ）、６．６（１Ｈ，Ｃ－Ｈ）、４．１（２Ｈ，－ＣＨ２）
Figure JPOXMLDOC01-appb-C000082
  
［比較合成例２］
　ジムロート冷却管、温度計及び攪拌翼を備えた、底抜きが可能な内容積１０Ｌの四つ口フラスコを準備した。この四つ口フラスコに、窒素気流中、１，５－ジメチルナフタレン１．０９ｋｇ（７ｍｏｌ、三菱ガス化学（株）製）、４０質量％ホルマリン水溶液２．１ｋｇ（ホルムアルデヒドとして２８ｍｏｌ、三菱ガス化学（株）製）及び９８質量％硫酸（関東化学（株）製）０．９７ｍＬを仕込み、常圧下、１００℃で還流させながら７時間反
応させた。その後、希釈溶媒としてエチルベンゼン（和光純薬工業（株）製試薬特級）１．８ｋｇを反応液に加え、静置後、下相の水相を除去した。さらに、中和及び水洗を行い、エチルベンゼン及び未反応の１，５－ジメチルナフタレンを減圧下で留去することにより、淡褐色固体のジメチルナフタレンホルムアルデヒド樹脂１．２５ｋｇを得た。
　続いて、ジムロート冷却管、温度計及び攪拌翼を備えた内容積０．５Ｌの四つ口フラスコを準備した。この四つ口フラスコに、窒素気流下で、上述のようにして得られたジメチルナフタレンホルムアルデヒド樹脂１００ｇ（０．５１ｍｏｌ）とパラトルエンスルホン酸０．０５ｇとを仕込み、１９０℃まで昇温させて２時間加熱した後、攪拌した。その後さらに、１－ナフトール５２．０ｇ（０．３６ｍｏｌ）を加え、さらに２２０℃まで昇温させて２時間反応させた。溶剤希釈後、中和及び水洗を行い、溶剤を減圧下で除去することにより、黒褐色固体の変性樹脂（ＣＲ－１）１２６．１ｇを得た。
［実施例１～４２］
　各合成実施例、及び比較合成例１で得られた重合体を用いて、以下に示す評価方法によって、耐熱性を評価した結果を表１に示す。
＜熱分解温度の測定＞
　エスアイアイ・ナノテクノロジー社製のＥＸＳＴＡＲ６０００ＴＧ／ＤＴＡ装置を使用し、試料約５ｍｇをアルミニウム製非密封容器に入れ、窒素ガス（３０ｍＬ／ｍｉｎ）気流中昇温速度１０℃／ｍｉｎで７００℃まで昇温した。その際、１０重量％の熱減量が観測される温度を熱分解温度（Ｔｇ）とし、以下の基準で耐熱性を評価した。
　Ａ：熱分解温度が４３０℃以上
　Ｂ：熱分解温度が３７５℃以上４３０未満
　Ｃ：熱分解温度が３２０℃未満３７５℃未満
＜溶解性の測定＞
　２３℃にて、各例で得られた重合体をシクロヘキサノン（ＣＨＮ）に対して５質量％溶液になるよう溶解させた。その後、１０℃にて３０日間静置したときのＣＨＮ溶液の外観を以下の基準にて評価した。
　Ａ：目視にて析出物がないことを確認した。
　Ｃ：目視にて析出物があることを確認した。
Figure JPOXMLDOC01-appb-T000083
  
　表１から明らかなように、実施例で用いた重合体は、耐熱性が良好であるが、比較例１で用いた重合体は、耐熱性が劣ることが確認できた。また、いずれの重合体も、溶解性が良好であることが確認できた。
［実施例４３～６６］
《リソグラフィー用下層膜形成用組成物の調製》
　表２に示す組成となるように、リソグラフィー用下層膜形成用組成物を調製した。次に、これらのリソグラフィー用下層膜形成用組成物をシリコン基板上に回転塗布し、その後、窒素雰囲気下において、２４０℃で６０秒間、さらに４００℃で１２０秒間ベークして、膜厚２００～２５０ｎｍの下層膜を各々作製した。
　次いで、下記に示す条件でエッチング試験を行い、エッチング耐性を評価した。評価結果を表２に示す。なお、評価方法の詳細は後述する。
＜エッチング試験＞
　エッチング装置：サムコインターナショナル社製「ＲＩＥ－１０ＮＲ」
　出力：５０Ｗ
　圧力：２０Ｐａ
　時間：２ｍｉｎ
　エッチングガス
　Ａｒガス流量：ＣＦ４ガス流量：Ｏ２ガス流量＝５０：５：５（ｓｃｃｍ）
（エッチング耐性の評価）
　エッチング耐性の評価は、以下の手順で行った。まず、ノボラック（群栄化学（株）製「ＰＳＭ４３５７」）を用いること以外は、上述の条件と同様にしてノボラックの下層膜を作製した。このノボラックの下層膜を対象として、上述のエッチング試験を行い、そのときのエッチングレートを測定した。
　次に、各実施例及び比較例２の下層膜について、前記エッチング試験を同様に行い、エッチングレートを測定した。ノボラックの下層膜のエッチングレートを基準として、以下の評価基準で各実施例及び比較例２のエッチング耐性を評価した。
［評価基準］
　Ａ：ノボラックの下層膜に比べてエッチングレートが、－２０％未満
　Ｂ：ノボラックの下層膜に比べてエッチングレートが、－２０％以上－１０％以下
　Ｃ：ノボラックの下層膜に比べてエッチングレートが、－１０％超
Figure JPOXMLDOC01-appb-T000084
  
　各実施例では、ノボラックの下層膜及び比較例２の重合体に比べて同等又は優れたエッチングレートが発揮されることがわかった。一方、比較例２の重合体では、ノボラックの下層膜に比べてエッチングレートが劣っているであることがわかった。
《重合体の精製》
　重合体の精製前後の金属含有量と溶液の保存安定性とを以下の方法で評価した。
＜各種金属含有量測定＞
　ＩＣＰ－ＭＳ（Ｉｎｄｕｃｔｉｖｅｌｙ　Ｃｏｕｐｌｅｄ　Ｐｌａｓｍａ　Ｍａｓｓ　Ｓｐｅｃｔｒｏｍｅｔｒｙ）を用いて下記測定条
件にて、以下の実施例、比較例によって得られた各種重合体のプロピレングリコールモノメチルエーテルアセテート（ＰＧＭＥＡ）溶液中の金属含有量を測定した。
　装置：アジレント社製ＡＧ８９００
　温度：２５℃
　環境：クラス１００クリーンルーム
＜保存安定性評価＞
　以下の各例によって得られたＰＧＭＥＡ溶液を２３℃にて２４０時間保持した後の溶液の濁度（ＨＡＺＥ）を色差・濁度計を用いて測定し、以下の基準にて溶液の保存安定性を評価した。
　装置：色差・濁度計ＣＯＨ４００（日本電色（株）製）
　光路長：１ｃｍ
　石英セル使用
［評価基準］
　０　　≦ＨＡＺＥ≦１．０　：良好
　１．０＜ＨＡＺＥ≦２．０　：可
　２．０＜ＨＡＺＥ　　　　　：不良
［実施例１Ｆ］重合体（Ｒ１－１）の酸による精製
　１０００ｍＬ容量の四つ口フラスコ（底抜き型）に、合成実施例１－１で得られた重合体（Ｒ１－１）をＣＨＮに溶解させた溶液（１０質量％）を１５０ｇ仕込み、攪拌しながら８０℃まで加熱した。次いで、得られた溶液に蓚酸水溶液（ｐＨ１．３）３７．５ｇを加え、５分間攪拌後、３０分間静置した。これにより油相と水相とに分離したのち、水相を除去した。この操作を１回繰り返した後、得られた油相に、超純水３７．５ｇを仕込み、５分間攪拌後、３０分静置し、水相を除去した。この操作を３回繰り返した後、８０℃に加熱しながらフラスコ内を２００ｈＰａ以下に減圧することで、残留水分及びＣＨＮを濃縮留去した。その後、ＥＬグレードのＣＨＮ（関東化学（株）製試薬）で希釈し、１０質量％に濃度調整を行うことにより、金属含有量の低減された重合体（Ｒ１－１）のＣＨＮ溶液を得た。
［参考例１］重合体（Ｒ１－１）の超純水による精製
　蓚酸水溶液の代わりに、超純水を用いる以外は実施例Ｆ１と同様に実施し、１０質量％に濃度調整を行うことにより、重合体（Ｒ１－１）のＣＨＮ溶液を得た。
　処理前の重合体（Ｒ１－１）の１０質量％ＣＨＮ溶液、実施例１Ｆ及び参考例１において得られた溶液について、各種金属含有量をＩＣＰ－ＭＳによって測定した。測定結果を表３に示す。
［実施例２Ｆ］重合体（Ｒ１Ａ－１）の酸による精製
　１０００ｍＬ容量の四つ口フラスコ（底抜き型）に、合成実施例１Ａ－１で得られた重合体（Ｒ１Ａ－１）をＣＨＮに溶解させた溶液（１０質量％）を１４０ｇ仕込み、攪拌しながら６０℃まで加熱した。次いで、得られた溶液に蓚酸水溶液（ｐＨ１．３）３７．５ｇを加え、５分間攪拌後、３０分間静置した。これにより油相と水相とに分離したのち、水相を除去した。この操作を１回繰り返した後、得られた油相に、超純水３７．５ｇを仕込み、５分間攪拌後、３０分静置し、水相を除去した。この操作を３回繰り返した後、８０℃に加熱しながらフラスコ内を２００ｈＰａ以下に減圧することで、残留水分及びＣＨＮを濃縮留去した。その後、ＥＬグレードのＣＨＮ（関東化学（株）製試薬）で希釈し、１０質量％に濃度調整を行うことにより、金属含有量の低減された重合体（Ｒ１Ａ－１）のＣＨＮ溶液を得た。
［参考例２］重合体（Ｒ１Ａ－１）の超純水による精製
　蓚酸水溶液の代わりに、超純水を用いる以外は実施例２Ｆと同様に実施し、１０質量％に濃度調整を行うことにより、重合体（Ｒ１Ａ－１）のＣＨＮ溶液を得た。
　処理前の重合体（Ｒ１Ａ－１）の１０質量％ＣＨＮ溶液、実施例Ｆ２及び参考例２において得られた溶液について、各種金属含有量をＩＣＰ－ＭＳによって測定した。測定結果を表３に示す。
［実施例３Ｆ］フィルター通液による精製
　クラス１０００のクリーンブース内にて、１０００ｍＬ容量の四つ口フラスコ（底抜き型）に、合成実施例１－１で得られた重合体（Ｒ１－１）をＣＨＮに溶解させた濃度１０質量％の溶液を５００ｇ仕込み、続いて釜内部の空気を減圧除去した後、窒素ガスを導入して大気圧まで戻し、窒素ガスを毎分１００ｍＬで通気下、内部の酸素濃度を１％未満に調整した後、攪拌しながら３０℃まで加熱した。底抜きバルブから前記溶液を抜き出し、フッ素樹脂製の耐圧チューブを経由してダイヤフラムポンプで毎分１００ｍＬの流量で公称孔径が０．０１μｍのナイロン製中空糸膜フィルター（キッツマイクロフィルター（株）製、商品名：ポリフィックスナイロンシリーズ）に通液した。得られた重合体（Ｒ１－１）の溶液の各種金属含有量をＩＣＰ－ＭＳによって測定した。なお、酸素濃度はアズワン（株）製の酸素濃度計「ＯＭ－２５ＭＦ１０」により測定した（以下も同様）。測定結果を表３に示す。
［実施例４Ｆ］
　公称孔径が０．０１μｍのポリエチレン（ＰＥ）製の中空糸膜フィルター（キッツマイクロフィルター（株）製、商品名：ポリフィックス）を使用した以外は、実施例３Ｆと同様に通液し、得られた重合体（Ｒ１－１）溶液の各種金属含有量をＩＣＰ－ＭＳによって測定した。測定結果を表３に示す。
［実施例５Ｆ］
　公称孔径が０．０４μｍのナイロン製中空糸膜フィルター（キッツマイクロフィルター（株）製、商品名：ポリフィックス）を使用した以外は、実施例３Ｆと同様に通液し、得られた重合体（Ｒ１－１）溶液の各種金属含有量をＩＣＰ－ＭＳによって測定した。測定結果を表３に示す。
［実施例６Ｆ］
　公称孔径が０．２μｍのゼータ電位フィルター（ゼータプラスフィルター４０ＱＳＨ（スリーエム（株）製、イオン交換能あり））を使用した以外は、実施例３Ｆと同様に通液し、得られた重合体（Ｒ１－１）溶液の各種金属含有量をＩＣＰ－ＭＳによって測定した。測定結果を表３に示す。
［実施例７Ｆ］
　公称孔径が０．２μｍのゼータ電位フィルター（ゼータプラスフィルター０２０ＧＮ（スリーエム（株）製、イオン交換能あり、ゼータプラスフィルター４０ＱＳＨとはろ過面積及びろ材厚みが異なる））を使用した以外は、実施例３Ｆと同様に通液し、得られた重合体（Ｒ１－１）溶液の各種金属含有量をＩＣＰ－ＭＳによって測定した。測定結果を表３に示す。
［実施例８Ｆ］
　実施例３Ｆにおける重合体（Ｒ１－１）の代わりに、合成実施例１Ａ－１で得られた重合体（Ｒ１Ａ－１）を使用した以外は、実施例３Ｆと同様に通液し、得られた重合体（Ｒ１Ａ－１）溶液の各種金属含有量をＩＣＰ－ＭＳによって測定した。測定結果を表３に示す。
［実施例９Ｆ］
　実施例４Ｆにおける重合体（Ｒ１－１）の代わりに、合成実施例１Ａ－１で得られた重合体（Ｒ１Ａ－１）を使用した以外は、実施例４Ｆと同様に通液し、得られた重合体（Ｒ１Ａ－１）溶液の各種金属含有量をＩＣＰ－ＭＳによって測定した。測定結果を表３に示す。
［実施例１０Ｆ］
　実施例５Ｆにおける重合体（Ｒ１－１）の代わりに、合成実施例１Ａ－１で得られた重合体（Ｒ１Ａ－１）を使用した以外は、実施例５Ｆと同様に通液し、得られた重合体（Ｒ１Ａ－１）溶液の各種金属含有量をＩＣＰ－ＭＳによって測定した。測定結果を表３に示す。
［実施例１１Ｆ］
　実施例６Ｆにおける重合体（Ｒ１－１）の代わりに、合成実施例１Ａ－１で得られた重合体（Ｒ１Ａ－１）を使用した以外は、実施例６Ｆと同様に通液し、得られた重合体（Ｒ１Ａ－１）溶液の各種金属含有量をＩＣＰ－ＭＳによって測定した。測定結果を表３に示す。
［実施例１２Ｆ］
　実施例７Ｆにおける重合体（Ｒ１－１）の代わりに、合成実施例１Ａ－１で得られた重合体（Ｒ１Ａ－１）を使用した以外は、実施例７Ｆと同様に通液し、得られた重合体（Ｒ１Ａ－１）溶液の各種金属含有量をＩＣＰ－ＭＳによって測定した。測定結果を表３に示す。
［実施例１３Ｆ］酸洗浄、フィルター通液併用１
　クラス１０００のクリーンブース内にて、３００ｍＬ容量の四つ口フラスコ（底抜き型）に、実施例１Ｆによって得られた金属含有量の低減された重合体（Ｒ１－１）の１０質量％ＣＨＮ溶液を１４０ｇ仕込み、続いて釜内部の空気を減圧除去した後、窒素ガスを導入して大気圧まで戻し、窒素ガスを毎分１００ｍＬで通気下、内部の酸素濃度を１％未満に調整した後、攪拌しながら３０℃まで加熱した。底抜きバルブから前記溶液を抜き出し、フッ素樹脂製の耐圧チューブを経由してダイヤフラムポンプで毎分１０ｍＬの流量で公称孔径が０．０１μｍのイオン交換フィルター（日本ポール（株）製、商品名：イオンクリーンシリーズ）に通液した。その後、回収された溶液を前記３００ｍＬ容量の四つ口フラスコに戻し、フィルターを公称口径１ｎｍの高密度ＰＥ製フィルター（日本インテグリス（株）製）に変え、同様にポンプ通液を実施した。得られた重合体（Ｒ１－１）の溶液の各種金属含有量をＩＣＰ－ＭＳによって測定した。なお、酸素濃度はアズワン（株）製の酸素濃度計「ＯＭ－２５ＭＦ１０」により測定した。測定結果を表３に示す。
［実施例１４Ｆ］酸洗浄、フィルター通液併用２
　クラス１０００のクリーンブース内にて、３００ｍＬ容量の四つ口フラスコ（底抜き型）に、実施例１Ｆによって得られた金属含有量の低減された重合体（Ｒ１－１）の１０質量％ＣＨＮ溶液を１４０ｇ仕込み、続いて釜内部の空気を減圧除去した後、窒素ガスを導入して大気圧まで戻し、窒素ガスを毎分１００ｍＬで通気下、内部の酸素濃度を１％未満に調整した後、攪拌しながら３０℃まで加熱した。底抜きバルブから前記溶液を抜き出し、フッ素樹脂製の耐圧チューブを経由してダイヤフラムポンプで毎分１０ｍＬの流量で公称孔径が０．０１μｍのナイロン製中空糸膜フィルター（キッツマイクロフィルター（株）製、商品名：ポリフィックス）に通液した。その後、回収された溶液を前記３００ｍＬ容量の四つ口フラスコに戻し、フィルターを公称口径１ｎｍの高密度ＰＥ製フィルター（日本インテグリス社製）に変え、同様にポンプ通液を実施した。得られた重合体（Ｒ１－１）の溶液の各種金属含有量をＩＣＰ－ＭＳによって測定した。なお、酸素濃度はアズワン（株）製の酸素濃度計「ＯＭ－２５ＭＦ１０」により測定した。測定結果を表３に示す。
［実施例１５Ｆ］酸洗浄、フィルター通液併用３
　実施例１Ｆで使用した重合体（Ｒ１－１）の１０質量％ＣＨＮ溶液を実施例２Ｆによって得られた重合体（Ｒ１Ａ－１）の１０質量％ＣＨＮ溶液に変えた以外は実施例１３Ｆと同様の操作を行い、金属量の低減された重合体（Ｒ１Ａ－１）の１０質量％ＰＧＭＥＡ溶液を回収した。得られた溶液の各種金属含有量をＩＣＰ－ＭＳによって測定した。なお、酸素濃度はアズワン（株）製の酸素濃度計「ＯＭ－２５ＭＦ１０」により測定した。測定結果を表３に示す。
［実施例１６Ｆ］酸洗浄、フィルター通液併用４
　実施例１Ｆで使用した重合体（Ｒ１－１）の１０質量％ＣＨＮ溶液を実施例２Ｆによって得られた重合体（Ｒ１Ａ－１）の１０質量％ＣＨＮ溶液に変えた以外は実施例１４Ｆと同様の操作を行い、金属量の低減された重合体（Ｒ１Ａ－１）の１０質量％ＰＧＭＥＡ溶液を回収した。得られた溶液の各種金属含有量をＩＣＰ－ＭＳによって測定した。なお、酸素濃度はアズワン（株）製の酸素濃度計「ＯＭ－２５ＭＦ１０」により測定した。測定結果を表３に示す。
Figure JPOXMLDOC01-appb-T000085
  
　表３に示すように、各種精製方法によって、酸化剤に由来する金属を低減することにより、本実施形態における重合体溶液の保存安定性が良好となることが確認された。
　特に酸洗浄方法とイオン交換フィルター或いはナイロンフィルターを使用することで、イオン性の金属を効果的に低減し、高精細な高密度ポリエチレン製の微粒子除去フィルターを併用することで、劇的な金属除去効果を得ることができる。
［実施例１Ｒ～７Ｒ、比較例３］
＜レジスト性能＞
　表４中に記載の合成実施例及び比較合成例１で得られた重合体を用いて、下記のレジスト性能評価を行った結果を表４に示す。
（レジスト組成物の調製）
　前記で合成した各重合体を用いて、表４に示す配合でレジスト組成物を調製した。なお、表４中のレジスト組成物の各成分のうち、酸発生剤（Ｃ）、酸拡散制御剤（Ｅ）及び溶媒については、以下のものを用いた。
　酸発生剤（Ｃ）
　Ｐ－１：トリフェニルベンゼンスルホニウム　トリフルオロメタンスルホネート（みどり化学（株））
　酸架橋剤（Ｇ）
　Ｃ－１：ニカラックＭＷ－１００ＬＭ（三和ケミカル（株））
　酸拡散制御剤（Ｅ）
　Ｑ－１：トリオクチルアミン（東京化成工業（株））
　溶媒
　Ｓ－１：ＣＨＮ（東京化成工業（株））
（レジスト組成物のレジスト性能の評価方法）
　均一なレジスト組成物を清浄なシリコンウェハー上に回転塗布した後、１１０℃のオーブン中で露光前ベーク（ＰＢ）して、厚さ６０ｎｍのレジスト膜を形成した。得られたレジスト膜に対して、電子線描画装置（ＥＬＳ－７５００、（株）エリオニクス社製）を用いて、５０ｎｍ間隔の１：１のラインアンドスペース設定の電子線を照射した。電子線照射後に、レジスト膜を、それぞれ所定の温度で、９０秒間加熱し、テトラメチルアンモニウムヒドロキシド（ＴＭＡＨ）２．３８質量％のアルカリ現像液に６０秒間浸漬して現像を行った。その後、レジスト膜を、超純水で３０秒間洗浄、乾燥して、レジストパターンを形成した。
　形成されたレジストパターンについて、ラインアンドスペースを走査型電子顕微鏡（（株）日立ハイテクノロジー製「Ｓ－４８００」）により観察し、レジスト組成物の電子線照射による反応性を評価した。
Figure JPOXMLDOC01-appb-T000086
  
　レジストパターン評価については、実施例では５０ｎｍ間隔の１：１のラインアンドスペース設定の電子線を照射することにより、良好なレジストパターンを得た。なお、ラインエッジラフネスはパターンの凹凸が５ｎｍ未満を良好とした。一方、比較例３では良好なレジストパターンを得ることはできなかった。
　このように本実施形態の要件を満たす重合体を用いた場合は、当該要件を満たさない比較例３の重合体（ＮＢｉｓＮ－１）に比べて、良好なレジストパターン形状を付与できる。前記した本実施形態の要件を満たす限り、実施例に記載した重合体以外についても同様の効果を示す。
［実施例１Ｓ～６Ｓ、比較例４］
（感放射線性組成物の調製）
　表５に記載の配合で成分を調合し、均一溶液としたのち、得られた均一溶液を、孔径０．１μｍのテフロン（登録商標）製メンブランフィルターで濾過して、感放射線性組成物を調製した。調製した各々の感放射線性組成物について以下の評価を行った。
Figure JPOXMLDOC01-appb-T000087
  
　なお、比較例４におけるレジスト基材（成分（Ａ））として、次のものを用いた。
　ＰＨＳ－１：ポリヒドロキシスチレン　Ｍｗ＝８０００（シグマ－アルドリッチ社）
　また、光活性化合物（Ｂ）として、次のものを用いた。
　Ｂ－１：下記化学構造式（Ｇ）のナフトキノンジアジド系感光剤（製品名「４ＮＴ－３００」、東洋合成工業（株））
　さらに、溶媒として、次のものを用いた。
　Ｓ－１：ＣＨＮ（東京化成工業（株））
Figure JPOXMLDOC01-appb-C000088
  
＜感放射線性組成物のレジスト性能の評価＞
　前記で得られた感放射線性組成物を清浄なシリコンウェハー上に回転塗布した後、１１０℃のオーブン中で露光前ベーク（ＰＢ）して、厚さ２００ｎｍのレジスト膜を形成した。該レジスト膜に対して、紫外線露光装置（ミカサ製マスクアライナＭＡ－１０）を用いて紫外線を露光した。紫外線ランプは超高圧水銀ランプ（相対強度比はｇ線：ｈ線：ｉ線：ｊ線＝１００：８０：９０：６０）を使用した。照射後に、レジスト膜を、１１０℃で９０秒間加熱し、ＴＭＡＨ２．３８質量％アルカリ現像液に６０秒間浸漬して現像を行った。その後、レジスト膜を、超純水で３０秒間洗浄し、乾燥して、５μｍのレジストパターンを形成した。
　形成されたレジストパターンにおいて、得られたラインアンドスペースを走査型電子顕微鏡（（株）日立ハイテクノロジー製Ｓ－４８００）により観察した。ラインエッジラフネスはパターンの凹凸が５ｎｍ未満を良好とした。
　表５中の実施例における感放射線性組成物を用いた場合は、解像度５μｍの良好なレジストパターンを得ることができた。また、そのパターンのラフネスも小さく良好であった。
　一方、比較例４における感放射線性組成物を用いた場合は、解像度５μｍの良好なレジストパターンを得ることができた。しかしながら、そのパターンのラフネスは大きく不良であった。
　上述のように、実施例１Ｓ～実施例６Ｓにおける感放射線性組成物は、比較例４における感放射線性組成物に比べて、ラフネスが小さく、かつ良好な形状のレジストパターンを形成することができることがわかった。前記した本実施形態の要件を満たす限り、実施例に記載した以外の感放射線性組成物も同様の効果を示す。
＜リソグラフィー用下層膜形成用組成物のエッチング耐性＞
　なお、各合成実施例で得られた重合体は、比較的に低分子量で低粘度であることから、これを用いたリソグラフィー用下層膜形成材料は埋め込み特性や膜表面の平坦性が比較的に有利に高められ得ると評価された。また、熱分解温度はいずれも４３０℃以上（評価Ａ）であり、高い耐熱性を有するので、高温ベーク条件でも使用することができると評価された。これらの点を確認するべく、下層膜用途を想定し、以下の評価を行った。
［実施例１Ｕ～７Ｕ、比較例５～６］
（リソグラフィー用下層膜形成用組成物の調製）
　表６に示す組成となるように、リソグラフィー用下層膜形成用組成物を調製した。次に、これらのリソグラフィー用下層膜形成用組成物をシリコン基板上に回転塗布し、その後、２４０℃で６０秒間、さらに４００℃で１２０秒間ベークして、膜厚２００ｎｍの下層膜を各々作製した。酸発生剤、架橋剤及び有機溶媒については以下のものを用いた。
 
・酸発生剤：
　みどり化学（株）製　ジターシャリーブチルジフェニルヨードニウムノナフルオロメタンスルホナート（ＤＴＤＰＩ）
・架橋剤：
　三和ケミカル（株）製　ニカラックＭＸ２７０（ニカラック）
　本州化学工業社製　ＴＭＯＭ－ＢＰ（下記式で表される化合物）
Figure JPOXMLDOC01-appb-C000089
  
・有機溶媒：ＣＨＮ，ＰＧＭＥＡ
・ノボラック：群栄化学（株）製　ＰＳＭ４３５７
　次に、下記に示す条件でエッチング試験を行い、エッチング耐性を評価した。評価結果を表６に示す。なお、評価方法の詳細は後述する。
＜エッチング試験＞
　エッチング装置：サムコインターナショナル社製　ＲＩＥ－１０ＮＲ
　出力：５０Ｗ
　圧力：２０Ｐａ
　時間：２ｍｉｎ
　エッチングガス
　Ａｒガス流量：ＣＦ４ガス流量：Ｏ２ガス流量＝５０：５：５（ｓｃｃｍ）
＜エッチング耐性の評価＞
　エッチング耐性の評価は、以下の手順で行った。まず、ノボラック（群栄化学（株）製「ＰＳＭ４３５７」）を用いること以外は、前記条件と同様にしてノボラックの下層膜を作製した。このノボラックの下層膜を対象として、上述のエッチング試験を行い、そのときのエッチングレートを測定した。
　次に、表６に記載の実施例と比較例５～６の下層膜を、ノボラックの下層膜と同様の条件で作製し、前記エッチング試験を同様に行い、そのときのエッチングレートを測定した。ノボラックの下層膜のエッチングレートを基準として、以下の評価基準で各実施例及び比較例のエッチング耐性を評価した。
［評価基準］
　Ａ：ノボラックの下層膜に比べてエッチングレートが、－２０％未満
　Ｂ：ノボラックの下層膜に比べてエッチングレートが、－２０％以上０％以下
　Ｃ：ノボラックの下層膜に比べてエッチングレートが、＋０％超
Figure JPOXMLDOC01-appb-T000090
  
　表６に示すように表中の各実施例では、ノボラックの下層膜及び比較例５～６の下層膜に比べて優れたエッチングレートが発揮されることがわかった。一方、比較例５又は比較例６の下層膜では、ノボラックの下層膜に比べてエッチングレートが同等或いは劣ることがわかった。
［実施例８Ｕ～１４Ｕ、比較例７］
　次に、表６中の各実施例，比較例５で調製したリソグラフィー用下層膜形成用組成物を膜厚８０ｎｍの６０ｎｍラインアンドスペースのＳｉＯ２基板上に塗布して、２４０℃で６０秒間ベークすることにより９０ｎｍの下層膜を形成した。
（埋め込み性の評価）
　埋め込み性の評価は、以下の手順で行った。前記条件で得られた膜の断面を切り出し、電子線顕微鏡にて観察し、埋め込み性を評価した。評価結果を表７に示す。
［評価基準］
　Ａ：５０ｎｍラインアンドスペースのＳｉＯ２基板の凹凸部分に欠陥無く下層膜が埋め込まれている。
　Ｃ：５０ｎｍラインアンドスペースのＳｉＯ２基板の凹凸部分に欠陥があり下層膜が埋め込まれていない。
Figure JPOXMLDOC01-appb-T000091
  
　表７中の各実施例では、埋め込み性が良好であることがわかった。一方、比較例７では、ＳｉＯ２基板の凹凸部分に欠陥が見られ埋め込み性が劣ることがわかった。
［実施例１５Ｕ～２１Ｕ］
　次に、表６中の各実施例で調製したリソグラフィー用下層膜形成用組成物を膜厚３００ｎｍのＳｉＯ２基板上に塗布して、２４０℃で６０秒間、さらに４００℃で１２０秒間ベークすることにより、膜厚８５ｎｍの下層膜を形成した。この下層膜上に、ＡｒＦ用レジスト溶液を塗布し、１３０℃で６０秒間ベークすることにより、膜厚１４０ｎｍのフォトレジスト層を形成した。
　なお、ＡｒＦレジスト溶液としては、下記式（１６）の化合物：５質量部、トリフェニルスルホニウムノナフルオロメタンスルホナート：１質量部、トリブチルアミン：２質量部、及びＰＧＭＥＡ：９２質量部を配合して調製したものを用いた。
　下記式（１６）の化合物は、次のように調製した。すなわち、２－メチル－２－メタクリロイルオキシアダマンタン４．１５ｇ、メタクリルロイルオキシ－γ－ブチロラクトン３．００ｇ、３－ヒドロキシ－１－アダマンチルメタクリレート２．０８ｇ、アゾビスイソブチロニトリル０．３８ｇを、テトラヒドロフラン８０ｍＬに溶解させて反応溶液とした。この反応溶液を、窒素雰囲気下、反応温度を６３℃に保持して、２２時間重合させた後、反応溶液を４００ｍＬのｎ－ヘキサン中に滴下した。このようにして得られる生成樹脂を凝固精製させ、生成した白色粉末をろ過し、減圧下４０℃で一晩乾燥させて下記式（１６）で表される化合物を得た。
Figure JPOXMLDOC01-appb-C000092
  
（式（１６）中、４０、４０、２０とあるのは、各構成単位の比率を示すものであり、ブロック共重合体を示すものではない。）
　次いで、電子線描画装置（エリオニクス社製；ＥＬＳ－７５００，５０ｋｅＶ）を用いて、フォトレジスト層を露光し、１１５℃で９０秒間ベーク（ＰＥＢ）し、２．３８質量％テトラメチルアンモニウムヒドロキシド（ＴＭＡＨ）水溶液で６０秒間現像することにより、ポジ型のレジストパターンを得た。
［比較例８］
　下層膜の形成を行わないこと以外は、実施例５０と同様にしてフォトレジスト層をＳｉＯ２基板上に直接形成し、ポジ型のレジストパターンを得た。
［評価］
　表８中に記載の各実施例及び比較例８のそれぞれについて、得られた４０ｎｍＬ／Ｓ（１：１）及び８０ｎｍＬ／Ｓ（１：１）のレジストパターンの形状を（株）日立製作所製電子顕微鏡「Ｓ－４８００」を用いて観察した。現像後のレジストパターンの形状については、パターン倒れがなく、矩形性が良好なものを「良好」とし、そうでないものを「不良」として評価した。また、当該観察の結果、パターン倒れが無く、矩形性が良好な最小の線幅を解像性として評価の指標とした。さらに、良好なパターン形状を描画可能な最小の電子線エネルギー量を感度として、評価の指標とした。その結果を表８に示す。
Figure JPOXMLDOC01-appb-T000093
  
　表８から明らかなように、表中の各実施例におけるレジストパターンは、比較例８に比して、解像性及び感度ともに有意に優れていることが確認された。かかる結果は、ヘテロ原子の影響によるものと考えられる。また、現像後のレジストパターン形状もパターン倒れがなく、矩形性が良好であることが確認された。さらに、現像後のレジストパターン形状の相違から、表中の各実施例におけるリソグラフィー用下層膜形成組成物は、レジスト材料との密着性がよいことが示された。
［実施例２２Ｕ］
　実施例２２Ｕで調製したリソグラフィー用下層膜形成用組成物を膜厚３００ｎｍのＳｉＯ２基板上に塗布して、２４０℃で６０秒間、さらに４００℃で１２０秒間ベークすることにより、膜厚９０ｎｍの下層膜を形成した。この下層膜上に、珪素含有中間層材料を塗布し、２００℃で６０秒間ベークすることにより、膜厚３５ｎｍの中間層膜を形成した。さらに、この中間層膜上に、前記ＡｒＦ用レジスト溶液を塗布し、１３０℃で６０秒間ベークすることにより、膜厚１５０ｎｍのフォトレジスト層を形成した。なお、珪素含有中間層材料としては、特開２００７－２２６１７０号公報＜合成例１＞に記載の珪素原子含有ポリマー（ポリマー１）を用いた。
　次いで、電子線描画装置（エリオニクス社製；ＥＬＳ－７５００，５０ｋｅＶ）を用いて、フォトレジスト層をマスク露光し、１１５℃で９０秒間ベーク（ＰＥＢ）し、２．３８質量％テトラメチルアンモニウムヒドロキシド（ＴＭＡＨ）水溶液で６０秒間現像することにより、４５ｎｍＬ／Ｓ（１：１）のポジ型のレジストパターンを得た。
　その後、サムコインターナショナル社製「ＲＩＥ－１０ＮＲ」を用いて、得られたレジストパターンをマスクにして珪素含有中間層膜（ＳＯＧ）のドライエッチング加工を行った。続いて、得られた珪素含有中間層膜パターンをマスクにした下層膜のドライエッチング加工と、得られた下層膜パターンをマスクにしたＳｉＯ２膜のドライエッチング加工とを順次行った。
　各々のエッチング条件は、下記に示すとおりである。
（レジストパターンのレジスト中間層膜へのエッチング条件）
　出力：５０Ｗ
　圧力：２０Ｐａ
　時間：１ｍｉｎ
・エッチングガス
　Ａｒガス流量：ＣＦ４ガス流量：Ｏ２ガス流量＝５０：８：２（ｓｃｃｍ）
（レジスト中間膜パターンのレジスト下層膜へのエッチング条件）
　出力：５０Ｗ
　圧力：２０Ｐａ
　時間：２ｍｉｎ
・エッチングガス
　Ａｒガス流量：ＣＦ４ガス流量：Ｏ２ガス流量＝５０：５：５（ｓｃｃｍ）
（レジスト下層膜パターンのＳｉＯ２膜へのエッチング条件９
　出力：５０Ｗ
　圧力：２０Ｐａ
　時間：２ｍｉｎ
・エッチングガス
　Ａｒガス流量：Ｃ５Ｆ１２ガス流量：Ｃ２Ｆ６ガス流量：Ｏ２ガス流量
　＝５０：４：３：１（ｓｃｃｍ）
＜パターン形状の評価＞
　上述のようにして得られた実施例２２Ｕのパターン断面（エッチング後のＳｉＯ２膜の形状）を、（株）日立製作所製電子顕微鏡「Ｓ－４８００」を用いて観察したところ、本実施形態の下層膜を用いた実施例は、多層レジスト加工におけるエッチング後のＳｉＯ２膜の形状は矩形であり、欠陥も認められず良好であることが確認された。
＜樹脂膜（樹脂単独膜）の特性評価＞
＜樹脂膜の作製＞
［実施例Ａ０１］
　溶媒としてＰＧＭＥＡを用い、合成実施例１のＲ１－１を溶解して固形分濃度１０質量％の樹脂溶液を調製した（実施例Ａ０１の樹脂溶液）。
　調製した樹脂溶液を、スピンコーターＬｉｔｈｉｕｓＰｒｏ（東京エレクトロン社製）を用いて１２インチシリコンウエハ上に成膜し、２００ｎｍの膜厚となるように回転数を調整しながら成膜後、ベーク温度を２５０℃１分の条件でベーク処理して重合体（Ｒ１－１）からなる膜を積層した基板を作製した。作製した基板を更に高温処理可能なホットプレートを使用し、３５０℃、１分の条件でベークすることで硬化した樹脂膜を得た。この際、得られた硬化した樹脂膜をＣＨＮ槽に１分間浸漬する前後の膜厚変化が３％以下であれば、硬化したと判断した。硬化が不十分と判断される場合は硬化温度を５０℃ずつ変更して硬化する温度を調査し、硬化する温度範囲の中で一番温度が低い条件で硬化するベーク処理を行った。
＜光学特性値評価＞
　作製した樹脂膜について、分光エリプソメトリーＶＵＶ－ＶＡＳＥ（Ｊ．Ａ．Ｗｏｏｌｌａｍ社製）を用いて光学特性値（光学定数として、屈折率ｎと、消衰係数ｋ）の評価を行った。
［実施例Ａ０２～実施例Ａ０６及び比較例Ａ０１］
　使用した重合体を重合体（Ｒ１－１）から表９に示す重合体に変更したこと以外は実施例Ａ０１と同様にして樹脂膜を作製し、光学特性値評価を実施した。
［評価基準］屈折率ｎ
　Ａ：１．４以上
　Ｃ：１．４未満
［評価基準］消衰係数ｋ
　Ａ：０．５未満
　Ｃ：０．５以上
Figure JPOXMLDOC01-appb-T000094
  
　実施例Ａ０１～Ａ０６の結果から、本実施形態の重合体を含む膜形成用組成物によりＡｒＦ露光で使用する波長１９３ｎｍにおけるｎ値が高くｋ値の低い樹脂膜を形成できることがわかった。
＜硬化膜の耐熱性評価＞
［実施例Ｂ０１］
　実施例Ａ０１で作製した樹脂膜について、ランプアニール炉を用いた耐熱性評価を行った。耐熱処理条件としては窒素雰囲気下４５０℃で加熱を継続し、加熱開始からの経過時間４分間後及び１０分間後の膜厚を比較した膜厚変化率を求めた。また、窒素雰囲気下５５０℃で加熱を継続し、加熱開始からの経過時間４分間後及び５５０℃１０分間後の膜厚を比較した膜厚変化率を求めた。これらの膜厚変化率を硬化膜耐熱性の指標として評価した。耐熱試験前後の膜厚は、干渉膜厚計で計測して膜厚の変動値を耐熱試験処理前の膜厚に対する比を膜厚変化率（百分率％）として求めた。
［評価基準］
　Ａ：膜厚変化率が、１０％未満
　Ｂ：膜厚変化率が、１０％以上１５％以下
　Ｃ：膜厚変化率が、１５％超
［実施例Ｂ０２～実施例Ｂ０６、比較例Ｂ０１～比較例Ｂ０２］
　使用した重合体を重合体（Ｒ１－１）から表１０に示す重合体に変更したこと以外は実施例Ｂ０１と同様にして耐熱性評価を実施した。
Figure JPOXMLDOC01-appb-T000095
  
　実施例Ｂ０１～Ｂ０６の結果から、比較例Ｂ０１及びＢ０２に比して、本実施形態の重合体を含む膜形成用組成物により５５０℃の温度においても膜厚変化が少ない耐熱性の高い樹脂膜を形成できることがわかった。
［実施例Ｃ０１］
＜ＰＥ－ＣＶＤ成膜評価＞
　１２インチシリコンウエハに熱酸化処理を実施し、得られたシリコン酸化膜を有する基板上に、実施例Ａ０１と同様の方法により、実施例Ａ０１の樹脂溶液を用いて１００ｎｍの厚みで樹脂膜を作製した。当該樹脂膜上に、成膜装置ＴＥＬＩＮＤＹ（東京エレクトロン（株）製）を用い、原料としてＴＥＯＳ（テトラエチルシロキサン）を使用し、基板温度３００℃にて膜厚７０ｎｍの酸化シリコン膜の成膜を行った。作製した酸化シリコン膜を積層した硬化膜付きウエハについて、更に欠陥検査装置「ＳＰ５」（ＫＬＡ－Ｔｅｎｃｏｒ社製）を用いて欠陥検査を行い、２１ｎｍ以上となる欠陥の個数を指標として、下記の基準に従い、成膜した酸化膜の欠陥数の評価を行った。
（基準）
　Ａ　欠陥数≦２０個
　Ｂ　２０個＜欠陥数≦５０個
　Ｃ　５０個＜欠陥数≦１００個
　Ｄ　１００個＜欠陥数≦１０００個
　Ｅ　１０００個＜欠陥数≦５０００個
　Ｆ　５０００個＜欠陥数
＜ＳｉＮ膜評価＞
　前記と同様の方法により１２インチシリコンウエハ上に１００ｎｍの厚みで熱酸化処理されたシリコン酸化膜を有する基板上に作製した硬化膜上に、成膜装置ＴＥＬＩＮＤＹ（東京エレクトロン社製）を用い、原料としてＳｉＨ４（モノシラン）、アンモニアを使用し、基板温度３５０℃にて膜厚４０ｎｍ、屈折率１．９４、膜応力－５４ＭＰａのＳｉＮ膜の成膜を行った。作製したＳｉＮ膜を積層した硬化膜付きウエハについて、更に欠陥検査装置「ＳＰ５」（ＫＬＡ－ｔｅｎｃｏｒ社製）を用いて欠陥検査を行い、２１ｎｍ以上となる欠陥の個数を指標として、下記基準に従い、成膜した酸化膜の欠陥数の評価を行った。
（基準）
　Ａ　欠陥数≦２０個
　Ｂ　２０個＜欠陥数≦５０個
　Ｃ　５０個＜欠陥数≦１００個
　Ｄ　１００個＜欠陥数≦１０００個
　Ｅ　１０００個＜欠陥数≦５０００個
　Ｆ　５０００個＜欠陥数
［実施例Ｃ０２～実施例Ｃ０６及び比較例Ｃ０１～比較例Ｃ０２］
　使用した樹脂を重合体（Ｒ１－１）から表１１に示す樹脂に変更したこと以外は実施例Ｃ０１と同様にして膜の欠陥評価を実施した。
Figure JPOXMLDOC01-appb-T000096
  
　実施例Ｃ０１～Ｃ０６の樹脂膜上に形成されたシリコン酸化膜又はＳｉＮ膜は２１ｎｍ以上となる欠陥の個数が５０個以下（Ｂ評価以上）であり、比較例Ｃ０１又はＣ０２の欠陥の個数に比べ、少なくなることが示された。
［実施例Ｄ０１］
＜高温処理後のエッチング評価＞
　１２インチシリコンウエハに熱酸化処理を実施し、得られたシリコン酸化膜を有する基板上に、実施例Ａ０１と同様の方法により、実施例Ａ０１の樹脂溶液を用いて１００ｎｍの厚みで樹脂膜を作製した。当該樹脂膜に対して、更に窒素雰囲気下で高温処理可能なホットプレートにより６００℃４分の条件で加熱によるアニーリング処理を行い、アニーリングされた樹脂膜が積層されたウエハを作製した。作製したアニーリングされた樹脂膜を削り出し、元素分析により炭素含有率を求めた。
　更に、１２インチシリコンウエハに熱酸化処理を実施し、得られたシリコン酸化膜を有する基板上に、実施例Ａ０１と同様の方法により、実施例Ａ０１の樹脂溶液を用いて１００ｎｍの厚みで樹脂膜を作製した。当該樹脂膜について、更に窒素雰囲気下で６００℃４分間の条件で加熱によりアニーリングされた樹脂膜を形成したのち、該基板をエッチング装置「ＴＥＬＩＵＳ」（東京エレクトロン社製）を用い、エッチングガスとしてＣＦ４／Ａｒを用いた条件、及びＣｌ２／Ａｒを用いた条件でエッチング処理を行い、エッチングレートの評価を行った。エッチングレートの評価はリファレンスとして日本化薬（株）製のフォトレジスト「ＳＵ８　３０００」を２５０℃１分間アニーリング処理して作製した２００ｎｍ膜厚の樹脂膜を用い、ＳＵ８　３０００に対するエッチングレートの速度比を相対値として求めて、下記評価基準に従って、評価した。
［評価基準］
　Ａ：ＳＵ８　３０００の樹脂膜に比べてエッチングレートが、－２０％未満
　Ｂ：ＳＵ８　３０００の樹脂膜に比べてエッチングレートが、－２０％以上０％以下
　Ｃ：ＳＵ８　３０００の樹脂膜に比べてエッチングレートが、＋０％超
［実施例Ｄ０２～実施例Ｄ０６、参考例Ｄ０１及び比較例Ｄ０１～比較例Ｄ０２］
　使用した重合体を重合体（Ｒ１－１）から表１２に示す重合体に変更したこと以外は実施例Ｄ０１と同様にしてエッチングレート評価を実施した。
Figure JPOXMLDOC01-appb-T000097
  
　実施例Ｄ０１～Ｄ０６の結果から、比較例Ｄ０１及びＤ０２に比して、本実施形態の重合体を含む組成物を用いた場合、高温処理後のエッチング耐性に優れた樹脂膜を形成できることがわかった。
［精製処理前後の欠陥評価］
＜積層膜でのエッチング欠陥評価＞
　以下において合成実施例で得られた重合体について、精製処理前後での品質評価を実施した。すなわち、後述する精製処理前後の各々において、重合体を用いてウエハ上に成膜した樹脂膜をエッチングにより基板側に転写したのち、欠陥評価を行うことで評価した。
　１２インチシリコンウエハに熱酸化処理を実施し、１００ｎｍの厚みのシリコン酸化膜を有する基板を得た。当該基板上に、重合体の樹脂溶液を１００ｎｍの厚みとなるようにスピンコート条件を調整して成膜後、１５０℃ベーク１分、続いて３５０℃ベーク１分を行うことで重合体を熱酸化膜付きシリコン上に積層した積層基板を作製した。
　エッチング装置として「ＴＥＬＩＵＳ」（東京エレクトロン社製）を用い、ＣＦ４／Ｏ２／Ａｒの条件で樹脂膜をエッチングし、酸化膜表面の基板を露出させた。更にＣＦ４／Ａｒのガス組成比にて酸化膜を１００ｎｍエッチングする条件でエッチング処理を行い、エッチングしたウエハを作製した。
　作製したエッチングウエハを欠陥検査装置ＳＰ５（ＫＬＡ－ｔｅｎｃｏｒ社製）にて１９ｎｍ以上の欠陥数を測定し、下記基準に従い、積層膜でのエッチング処理による欠陥評価として実施した。
（基準）
　Ａ　欠陥数≦２０個
　Ｂ　２０個＜欠陥数≦５０個
　Ｃ　５０個＜欠陥数≦１００個
　Ｄ　１００個＜欠陥数≦１０００個
　Ｅ　１０００個＜欠陥数≦５０００個
　Ｆ　５０００個＜欠陥数
［実施例Ｅ０１］重合体（Ｒ１－１）の酸による精製
　１０００ｍＬ容量の四つ口フラスコ（底抜き型）に、合成実施例１で得られた重合体（Ｒ１－１）をＣＨＮに溶解させた溶液（１０質量％）を１５０ｇ仕込み、攪拌しながら８０℃まで加熱した。次いで、蓚酸水溶液（ｐＨ１．３）３７．５ｇを加え、５分間攪拌後、３０分静置した。これにより油相と水相に分離したので、水相を除去した。この操作を１回繰り返した後、得られた油相に、超純水３７．５ｇを仕込み、５分間攪拌後、３０分間静置し、水相を除去した。この操作を３回繰り返した後、８０℃に加熱しながらフラスコ内を２００ｈＰａ以下に減圧することで、残留水分及びＣＨＮを濃縮留去した。その後、ＥＬグレードのＣＨＮ（関東化学（株）製試薬）で希釈し、１０質量％に濃度調整を行うことにより、金属含有量の低減されたＲ１－１のＣＨＮ溶液を得た。作製した重合体溶液を日本インテグリス（株）製の公称孔径３ｎｍのＵＰＥフィルターにより０．５ＭＰａの条件で濾過した溶液サンプルを作製した。
　当該精製処理前後の各々の溶液サンプルについて、上述のようにウエハ上に樹脂膜を成膜し、樹脂膜をエッチングにより基板側に転写したのち、積層膜でのエッチング欠陥評価を実施した。
［実施例Ｅ０２］重合体（Ｒ１Ａ－１）の酸による精製
　１０００ｍＬ容量の四つ口フラスコ（底抜き型）に、合成実施例１Ａ－１で得られた重合体（Ｒ１Ａ－１）をＣＨＮに溶解させた溶液（１０質量％）を１４０ｇ仕込み、攪拌しながら６０℃まで加熱した。次いで、蓚酸水溶液（ｐＨ１．３）３７．５ｇを加え、５分間攪拌後、３０分間静置した。これにより油相と水相とに分離したのち、水相を除去した。この操作を１回繰り返した後、得られた油相に、超純水３７．５ｇを仕込み、５分間攪拌後、３０分静置し、水相を除去した。この操作を３回繰り返した後、８０℃に加熱しながらフラスコ内を２００ｈＰａ以下に減圧することで、残留水分及びＣＨＮを濃縮留去した。その後、ＥＬグレードのＣＨＮ（関東化学（株）製試薬）で希釈し、１０質量％に濃度調整を行うことにより、金属含有量の低減された重合体（Ｒ１Ａ－１）のＣＨＮ溶液を得た。作製した重合体溶液を日本インテグリス（株）製の公称孔径３ｎｍのＵＰＥフィルターにより０．５ＭＰａの条件で濾過した溶液サンプルを作製した後、実施例Ｅ０１と同様に積層膜でのエッチング欠陥評価を実施した。
［実施例Ｅ０３］　フィルター通液による精製
　クラス１０００のクリーンブース内にて、１０００ｍＬ容量の四つ口フラスコ（底抜き型）に、合成実施例１－１で得られた重合体（Ｒ１－１）をＣＨＮに溶解させた濃度１０質量％の溶液を５００ｇ仕込み、続いて釜内部の空気を減圧除去した後、窒素ガスを導入して大気圧まで戻し、窒素ガスを毎分１００ｍＬで通気下、内部の酸素濃度を１％未満に調整した後、攪拌しながら３０℃まで加熱した。底抜きバルブから前記溶液を抜き出し、フッ素樹脂製の耐圧チューブを経由してダイヤフラムポンプで毎分１００ｍＬの流量で公称孔径が０．０１μｍのナイロン製中空糸膜フィルター（キッツマイクロフィルター（株）製、商品名：ポリフィックスナイロンシリーズ）に濾過圧が０．５ＭＰａの条件となるように加圧濾過にて通液した。濾過後の樹脂溶液をＥＬグレードのＣＨＮ（関東化学（株）製試薬）で希釈し、１０質量％に濃度調整を行うことにより、金属含有量の低減された重合体（Ｒ１－１）のＣＨＮ溶液を得た。作製した重合体溶液を日本インテグリス（株）製の公称孔径３ｎｍのＵＰＥフィルターにより０．５ＭＰａの条件で濾過した溶液サンプルを作製した後、実施例Ｅ０１と同様に積層膜でのエッチング欠陥評価を実施した。なお、酸素濃度はアズワン（株）製の酸素濃度計「ＯＭ－２５ＭＦ１０」により測定した（以下も同様）。
［実施例Ｅ０４］
　フィルターによる精製工程として、日本ポール社製の「ＩＯＮＫＬＥＥＮ」、日本ポール社製の「ナイロンフィルター」、更に日本インテグリス社製の公称孔径３ｎｍのＵＰＥフィルターをこの順番に直列に接続し、フィルターラインとして構築した。０．１μｍのナイロン製中空糸膜フィルターの代わりに、作製したフィルターラインを使用した以外は、実施例Ｅ０３と同様にして濾過圧が０．５ＭＰａの条件となるように加圧濾過により通液した。ＥＬグレードのＣＨＮ（関東化学（株）製試薬）で希釈し、１０質量％に濃度調整を行うことにより、金属含有量の低減された重合体（Ｒ１－１）のＣＨＮ溶液を得た。作製した重合体溶液を日本インテグリス（株）製の公称孔径３ｎｍのＵＰＥフィルターにより濾過圧が０．５ＭＰａの条件となるように加圧濾過した溶液サンプルを作製した後、実施例Ｅ０１と同様に積層膜でのエッチング欠陥評価を実施した。
［実施例Ｅ０５］
　実施例Ｅ０１で作製した溶液サンプルを、さらに実施例Ｅ０４で作製したフィルターラインを使用して濾過圧が０．５ＭＰａの条件となるように加圧濾過した溶液サンプルを作製した後、実施例Ｅ０１と同様に積層膜でのエッチング欠陥評価を実施した。
［実施例Ｅ０６］
　合成実施例１Ａ－１で作製した重合体（Ｒ１Ａ－１）について、実施例Ｅ０５と同様の方法により精製した溶液サンプルを作製した後、実施例Ｅ０１と同様に積層膜でのエッチング欠陥評価を実施した。
［実施例Ｅ０６－１］
　合成実施例１Ｅ－１で作製した重合体（Ｒ１Ｅ－１）について、実施例Ｅ０５と同様の方法により精製した溶液サンプルを作製した後、実施例Ｅ０１と同様に積層膜でのエッチング欠陥評価を実施した。
［実施例Ｅ０７］
　合成実施例３で作製した重合体（Ｒ１Ｂ－１）について、実施例Ｅ０５と同様の方法により精製した溶液サンプルを作製した後、積層膜でのエッチング欠陥評価を実施した。
Figure JPOXMLDOC01-appb-T000098
  
　実施例Ｅ０１～Ｅ０７の結果から、本実施形態の重合体を含む組成物を用いた場合、精製処理前の重合体を用いた場合に比して、さらに、得られる樹脂膜の品質が向上していることがわかった。
［実施例１Ｌ～７Ｌ及び比較例９］
　表６中の各実施例及び比較例５で調製したリソグラフィー用下層膜形成組成物と同組成の光学部材形成用組成物を膜厚３００ｎｍのＳｉＯ２基板上に塗布して、２６０℃で３００秒間ベークすることにより、膜厚１００ｎｍの光学部材用の膜を形成した。次いで、ジェー・エー・ウーラム・ジャパン社製　真空紫外域多入射角分光エリプソメーター「ＶＵＶ－ＶＡＳＥ」を用いて、６３３ｎｍの波長における屈折率及び透明性試験を行い、以下の基準に従って屈折率及び透明性を評価した。評価結果を表１４に示す。
［屈折率の評価基準］
　Ａ：屈折率が１．６０以上
　Ｃ：屈折率が１．６０未満
［透明性の評価基準］
　Ａ：消衰定数が０．０３未満
　Ｃ：消衰定数が０．０３以上
Figure JPOXMLDOC01-appb-T000099
  
　表中の各実施例の光学部材形成用組成物では、屈折率が高いのみならず、吸光係数が低く、透明性に優れることが分かった。一方で、比較例９の組成物は光学部材としての性能に劣ることが分かった。
［合成実施例Ｘ１～Ｘ２］重合体（Ｒ１Ａ－１６）～重合体（Ｒ１Ａ－１７）の合成
　化合物（１Ａ－１）の代わりに、それぞれ、下記化合物（１Ａ－１６）～（１Ａ－１７）を使用したことを除き、合成実施例１Ａ－１と同様に重合体（Ｒ１Ａ－１６）～（Ｒ１Ａ－１７）を合成した。なお、化合物（１Ａ－１６）は、ｏ－，ｍ－，ｐ－位置換体の混合物である。
　なお、下記に示すように、重合体（Ｒ１Ａ－１６）～（Ｒ１Ａ－１７）において、４００ＭＨｚ－１Ｈ－ＮＭＲにより以下のピークが見出され、各々前記式の化学構造を基本構造として有し且つ構成単位の芳香環同士が直接結合した構造を有することを確認した。さらに、得られた各重合体について、上述の方法によりポリスチレン換算分子量を測定した結果を併せて示す。
（Ｒ１Ａ－１６）
　Ｍｎ：８６３、Ｍｗ：１１２６、Ｍｗ／Ｍｎ：１．３
　δ（ｐｐｍ）９．５―１０．０（４Ｈ，Ｏ－Ｈ）、７．２～８．５（２３Ｈ，Ｐｈ－Ｈ）、６．２―６．９（２Ｈ，　Ｐｈ―Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
（Ｒ１Ａ－１７）
Ｍｎ：７８９、Ｍｗ：９１６、Ｍｗ／Ｍｎ：１．２
　δ（ｐｐｍ）９．５―１０．０（４Ｈ，Ｏ－Ｈ）、７．２～８．５（２３Ｈ，Ｐｈ－Ｈ）、６．２―６．９（２Ｈ，　Ｐｈ―Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
Figure JPOXMLDOC01-appb-C000100
 　　　　　　　　　　　　　　　　　 
［合成実施例Ｘ３～Ｘ５］重合体（Ｒ１Ｂ－９）～（Ｒ１Ｂ－１１）の合成
　化合物（１Ｂ－１）の代わりに、それぞれ、下記化合物（１Ｂ－９）～（１Ｂ－１１）を使用したことを除き、合成実施例１Ｂ－１と同様に重合体（Ｒ１Ｂ－９）～（Ｒ１Ｂ－１１）を合成した。なお、化合物（１Ｂ－１１）は、ｏ－，ｍ－，ｐ－位置換体の混合物である。
　なお、下記に示すように、重合体（Ｒ１Ｂ－９）～（Ｒ１Ｂ－１１）において、４００ＭＨｚ－１Ｈ－ＮＭＲにより以下のピークが見出され、各々前記式の化学構造を基本構造として有し且つ構成単位の芳香環同士が直接結合した構造を有することを確認した。さらに、得られた各重合体について、上述の方法によりポリスチレン換算分子量を測定した結果を併せて示す。
（Ｒ１Ｂ－９）
　Ｍｎ：７００、Ｍｗ：８７０、Ｍｗ／Ｍｎ：１．２
　δ（ｐｐｍ）１０．０（２Ｈ、―ＯＨ）９．０―９．２（１Ｈ，－ＯＨ）、７．１～８．０（７Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）
（Ｒ１Ｂ－１０）
　Ｍｎ：１８０５、Ｍｗ：２１２２、Ｍｗ／Ｍｎ：１．２
　δ（ｐｐｍ）１０．０（２Ｈ、―ＯＨ）９．０―９．２（１Ｈ，－ＯＨ）、７．０～８．０（７Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）
（Ｒ１Ｂ－１１）
　Ｍｎ：１５０８、Ｍｗ：１９１２、Ｍｗ／Ｍｎ：１．３
　δ（ｐｐｍ）１０．０（２Ｈ、―ＯＨ）９．０―９．２（１Ｈ，－ＯＨ）、７．０～８．０（７Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）
Figure JPOXMLDOC01-appb-C000101
 　　　　　　　　　　　　　　　　　 
　　　　　　　　　　　　　　　　　 
［合成実施例Ｘ６～Ｘ８］重合体（ＲＸ６）～（ＲＸ８）の合成
　レゾルシノールの代わりに、それぞれ、下記化合物（Ｘ６；カテコール）、（Ｘ７；３，３’－ジメチルビフェニル－４，４’－ジオール）、（Ｘ８；ジアミノベンゼン）を使用したことを除き、合成実施例１Ａ－５と同様に重合体（ＲＸ６）～（ＲＸ８）を合成した。
　なお、下記に示すように、重合体（ＲＸ６）～（ＲＸ８）において、４００ＭＨｚ－１Ｈ－ＮＭＲにより以下のピークが見出され、各々前記式の化学構造を基本構造として有し且つ構成単位の芳香環同士が直接結合した構造を有することを確認した。さらに、得られた各重合体について、上述の方法によりポリスチレン換算分子量を測定した結果を併せて示す。
（ＲＸ６）
　Ｍｎ：１０２１、Ｍｗ：１１２５、Ｍｗ／Ｍｎ：１．１
δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、８．６～９．１（２Ｈ，Ｏ－Ｈ）、７．２～８．５（１７Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）
（ＲＸ７）
　Ｍｎ：７４３、Ｍｗ：８１０、Ｍｗ／Ｍｎ：１．１
δ（ｐｐｍ）１０．０（２Ｈ，－ＯＨ）、９．４～９．６（２Ｈ，Ｏ－Ｈ）、７．２～６．３（２３Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）、
２．０～２．１（６Ｈ，ＣＨ２－Ｈ）
（ＲＸ８）
　Ｍｎ：１０２１、Ｍｗ：１１２５、Ｍｗ／Ｍｎ：１．１
δ（ｐｐｍ）１０．３（２Ｈ、ＮＨ－Ｈ）、９．４～９．６（２Ｈ，－ＯＨ）、７．０～８．５（１８Ｈ，Ｐｈ－Ｈ）、６．７～６．９（１Ｈ，Ｃ－Ｈ）、５．８～６．２（１Ｈ，Ｐｈ－Ｈ）
Figure JPOXMLDOC01-appb-C000102
  
［合成実施例Ｘ９～Ｘ１１］重合体（ＲＸ９）～（ＲＸ１１）の合成
　レゾルシノールの代わりに、それぞれ、上記化合物（Ｘ６；カテコール）、上記化合物（Ｘ７；３，３’－ジメチルビフェニル－４，４’－ジオール）、上記化合物（Ｘ８；ジアミノベンゼン）を使用したことを除き、合成実施例Ｘ３と同様に重合体（ＲＸ９）～（ＲＸ１１）を合成した。
　なお、下記に示すように、重合体（ＲＸ９）～（ＲＸ１１）において、４００ＭＨｚ－１Ｈ－ＮＭＲにより以下のピークが見出され、各々前記式の化学構造を基本構造として有し且つ構成単位の芳香環同士が直接結合した構造を有することを確認した。さらに、得られた各重合体について、上述の方法によりポリスチレン換算分子量を測定した結果を併せて示す。
（ＲＸ９）
　Ｍｎ：７５０、Ｍｗ：８６０、Ｍｗ／Ｍｎ：１．１
　δ（ｐｐｍ）１０．０（２Ｈ、―ＯＨ）、９．０－９．３（１Ｈ，－ＯＨ）、７．１～８．０（７Ｈ，Ｐｈ－Ｈ）、６．３～７．０（２Ｈ，Ｐｈ－Ｈ）
（ＲＸ１０）
　Ｍｎ：７０４、Ｍｗ：８０１、Ｍｗ／Ｍｎ：１．１
　δ（ｐｐｍ）１０．０（２Ｈ、―ＯＨ）、９．０―９．５（３Ｈ，－ＯＨ）、６．３～８．０（１１Ｈ，Ｐｈ－Ｈ）、２．０～２．１（６Ｈ，ＣＨ２－Ｈ）
（ＲＸ１１）
　Ｍｎ：７００、Ｍｗ：８７０、Ｍｗ／Ｍｎ：１．２
　δ（ｐｐｍ）１０．３（２Ｈ、ＮＨ－Ｈ）、９．０―９．２（１Ｈ，－ＯＨ）、７．１～８．０（７Ｈ，Ｐｈ－Ｈ）、７．０～５．７（２Ｈ，Ｐｈ－Ｈ）
Figure JPOXMLDOC01-appb-C000103
  
（実施例Ｘ１～Ｘ１１）
　合成実施例Ｘ１～Ｘ１１により得られた各重合体について、実施例１と同様に、耐熱性評価、溶解性評価を行った。結果を下記表に示す。
Figure JPOXMLDOC01-appb-T000104
（実施例Ｘ１Ａ～Ｘ１１Ａ）
　実施例４３において、合成実施例１－１で得られた重合体Ｒ１－１の代わりに下記表に記載の重合体を用いた以外は実施例４３と同様にして、リソグラフィー用下層膜形成用組成物を調製した。次に、これらのリソグラフィー用下層膜形成用組成物をシリコン基板上に回転塗布し、その後、窒素雰囲気下において、２４０℃で６０秒間、さらに４００℃で１２０秒間ベークして、膜厚２００～２５０ｎｍの下層膜を各々作製した。得られた下層膜について、実施例４３と同様に、エッチング試験を行い、エッチング耐性を評価した。
Figure JPOXMLDOC01-appb-T000105
　上記表に示すようにジアミノベンゼンに由来する単位を有する実施例Ｘ９Ａ及びＸ１１Ａはエッチング評価が“Ｂ”であったが、他の実施例は評価“Ａ”とさらに優れていた。
（実施例Ｚ１～Ｚ４）
〔安定性試験〕
　２３℃にて、下記表に記載の実施例で得られた重合体をプロピレングリコールモノメチルエーテル（ＰＧＭＥ）に対して１０質量％溶液になるよう溶解させ表中に示す組成のリソグラフィー用下層膜形成用組成物を調製した。その後、１０℃にて３０日間、保存した。これらのリソグラフィー用下層膜形成用組成物をシリコン基板上に回転塗布し、その後、４００℃で６０秒間ベークして、膜厚２００ｎｍの下層膜を各々作製した。作製した下層膜について、更に欠陥検査装置「ＳＰ５」（ＫＬＡ－Ｔｅｎｃｏｒ社製）を用いて欠陥検査を行い、２１ｎｍ以上となる欠陥の個数を指標として、下記の基準に従い、成膜した下層膜の欠陥数の評価を行った。
〔基準〕
Ａ　欠陥数≦２０個
Ｂ　２０個＜欠陥数≦５０個
Ｃ　５０個＜欠陥数≦１００個
Figure JPOXMLDOC01-appb-T000106
  
　上記表に示すように式（０）で表されるモノマーとしてレゾルシノールを用いた実施例Ｚ１は、に式（０）で表されるモノマーとしてカテコール、３，３’－ジメチルビフェニル－４，４’－ジオー、ジアミノベンゼンでジアミノベンゼンを用いた実施例Ｚ２～Ｚ４に比して、安定性評価の結果が優れたものであった。
　本発明は、式（０）で表されるモノマーの芳香環同士が架橋基を介さずに連結してなる部位を有する、すなわち、芳香環が直接結合によって連結してなる、新規な重合体を提供するものである。かかる重合体は耐熱性、耐エッチング性、溶媒溶解性などに優れており、とりわけ耐熱性、耐エッチング性に優れており、半導体用のコーティング剤、レジスト用材料、半導体下層膜形成材料として使用可能である。
　また本発明は、光学部材、フォトレジストの成分や、電気・電子部品用材料の樹脂原料、光硬化性樹脂等の硬化性樹脂原料、構造用材料の樹脂原料、又は樹脂硬化剤等に用いることのできる組成物として、産業上の利用可能性を有する。
　２０２１年１月１９日に出願された日本国特許出願２０２１－００６６５５号の開示は、その全体が参照により本明細書に取り込まれる。
　また、明細書に記載された全ての文献、特許出願、及び技術規格は、個々の文献、特許出願、及び技術規格が参照により取り込まれることが具体的かつ個々に記された場合と同程度に、本明細書中に参照により取り込まれる。
 

Claims (32)

  1. 　下記式（０）で表されるモノマー由来の構成単位を含む重合体であって、
    　構成単位同士が芳香環同士の直接結合によって連結している部位を有する、重合体。
    Figure JPOXMLDOC01-appb-C000001
      
    （式（０）中、Ｒは１価の基であり、ｍは１～５の整数であり、ここで、Ｒの少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基、又は、置換基を有していてもよい炭素数０～４０のアミノ基である。）
  2. 　前記式（０）におけるｍが２以上であり、Ｒの少なくとも２つが水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である、請求項１に記載の重合体。
  3. 　さらに、前記式（０）で表されるモノマーと共重合可能な、他の共重合可能な化合物に由来の構成単位を含み、前記式（０）で表されるモノマー由来の構成単位（ｘ）と、他の共重合可能な化合物（ｙ）に由来する構成単位とモル比（ｘ：ｙ）が、１：９９～９９：１である、請求項１又は請求項２に記載の重合体。
  4. 　前記他の共重合可能な化合物が、下記式（１Ａ）～下記式（１Ｄ）で表されるモノマー、又は、ヘテロ原子含有芳香族モノマーで構成される群から選ばれる、請求項３に記載の重合体。
    Figure JPOXMLDOC01-appb-C000002
      
    （式（１Ａ）中、Ｘは各々独立して酸素原子、硫黄原子、単結合又は無架橋であることを示し、Ｙ０は炭素数１～６０の２ｎ価の基又は単結合であり、ここで、Ｘが無架橋であるとき、Ｙ０は前記２ｎ１価の基であり、Ａは各々独立してベンゼン、ビフェニル、ターフェニル、ジフェニルメチレン又は縮合環であり、Ｒ０は各々独立して、水素原子、置換基を有していてもよい炭素数１～４０のアルキル基、置換基を有していてもよい炭素数６～４０のアリール基、置換基を有していてもよい炭素数２～４０のアルケニル基、炭素数２～４０のアルキニル基、置換基を有していてもよい炭素数１～４０のアルコキシ基、ハロゲン原子、チオール基、アミノ基、ニトロ基、カルボキシル基又は水酸基でありここで、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基であり、ｍ１は各々独立して１以上の整数であり、ｎ１は１～４の整数である。
    　式（１Ｂ）中、Ａ、Ｒ０及びｍ１は、前記式（１Ａ）において説明したものと同義であり、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。
    　式（１Ｃ）中、ｎ２は１～５００の整数であり、Ｙは、炭素数１～６０の２価の基又は単結合である。Ａ、Ｒ０及びｍ１は、前記式（１Ａ）において説明したものと同義であり、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。
    　式（１Ｄ）中、ｎ３は１～１０の整数であり、Ｙは、前記式（１Ｃ）において説明したものと同義であり、Ａ、Ｒ０及びｍ１は、前記式（１Ａ）において説明したものと同義であり、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。）
  5. 　下記式（１Ａ）で示される化合物が、下記式（１Ａ－１）で示される化合物である請求項４に記載の重合体。
    Figure JPOXMLDOC01-appb-C000003
      
    （式（１Ａ－１）中、ｎ４は、各々独立して０～３の整数であり、Ｘ、Ｙ０、Ｒ０、ｍ１及びｎ１は、前記式（１Ａ）において説明したものと同義である。）
  6. 　前記Ａが、ベンゼン、ビフェニル、ターフェニル、ジフェニルメチレン、ナフタレン、アントラセン、ナフタセン、ペンタセン、ベンゾピレン、クリセン、ピレン、トリフェニレン、コランニュレン、コロネン、オバレン及びフルオレンである、請求項４に記載の重合体。
  7. 　前記式（１Ｃ）で示される化合物が、下記式（１Ｃ－１）で示される化合物である請求項４に記載の重合体。
    Figure JPOXMLDOC01-appb-C000004
      
    （式（１Ｃ）中、Ｒ１は、各々独立して、水素原子、置換基を有していてもよい炭素数１～４０のアルキル基、置換基を有していてもよい炭素数６～４０のアリール基置換基を有していてもよい炭素数２～４０のアルケニル基、炭素数２～４０のアルキニル基、置換基を有していてもよい炭素数１～４０のアルコキシ基、ハロゲン原子、チオール基、アミノ基、ニトロ基、カルボキシル基又は水酸基であり、Ａ、Ｒ０、ｍ１、ｎ２は、前記式（１Ｃ）において説明したものと同義であり、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。）
  8. 　前記式（１Ｄ）で示される化合物が、下記式（１Ｄ－１）で示される化合物である請求項４に記載の重合体。
    Figure JPOXMLDOC01-appb-C000005
      
    （式（１Ｄ－１）中、Ｒ１は、各々独立して、水素原子、置換基を有していてもよい炭素数１～４０のアルキル基、置換基を有していてもよい炭素数６～４０のアリール基、置換基を有していてもよい炭素数２～４０のアルケニル基、炭素数２～４０のアルキニル基、置換基を有していてもよい炭素数１～４０のアルコキシ基、ハロゲン原子、チオール基、アミノ基、ニトロ基、カルボキシル基又は水酸基であり、Ａ、Ｒ０、ｍ１、ｎ３は、前記式（１Ｄ）において説明したものと同義であり、Ｒ０の少なくとも１つは水酸基、置換基を有していてもよい炭素数１～４０のアルコキシ基又は置換基を有していてもよい炭素数０～４０のアミノ基である。）
  9. 　前記ヘテロ原子含有芳香族モノマーが、複素環式芳香族化合物を含む、請求項４に記載の重合体。
  10. 　請求項１～請求項９のいずれか１項に記載の重合体を含む、組成物。
  11. 　溶媒をさらに含む、請求項１０に記載の組成物。
  12. 　前記溶媒が、プロピレングリコールモノメチルエーテル、プロピレングリコールモノメチルエーテルアセテート、シクロヘキサノン、シクロペンタノン、乳酸エチル及びヒドロキシイソ酪酸メチルで構成される群より選択される少なくとも１種を含む、請求項１１に記載の組成物。
  13. 　不純物金属の含有量が金属種毎に５００ｐｐｂ未満である、請求項１１又は請求項１２に記載の組成物。
  14. 　前記不純物金属が、銅、マンガン、鉄、コバルト、ルテニウム、クロム、ニッケル、スズ、鉛、銀及びパラジウムで構成される群より選択される少なくとも１種を含有する、請求項１３に記載の組成物。
  15. 　前記不純物金属の含有量が、１ｐｐｂ以下である、請求項１３又は請求項１４に記載の組成物。
  16. 　請求項１～請求項９のいずれか１項に記載の重合体の製造方法であって、１種又は２種以上の前記式（０）で表されるモノマーを酸化剤の存在下で重合させる工程を含む、重合体の製造方法。
  17. 　１種又は２種以上の前記式（０）で表されるモノマーと、前記式（０）で表されるモノマーと共重合可能な、他の共重合可能な化合物と、を酸化剤の存在下で重合させる工程を含む、請求項１６に記載の重合体の製造方法。
  18. 　前記酸化剤が、銅、マンガン、鉄、コバルト、ルテニウム、クロム、ニッケル、スズ、鉛、銀及びパラジウムで構成される群より選択される少なくとも１種を含有する金属塩類又は金属錯体である、請求項１６又は請求項１７に記載の重合体の製造方法。
  19. 　請求項１～請求項９のいずれか１項に記載の重合体を含む、膜形成用組成物。
  20. 　請求項１９に記載の膜形成用組成物を含む、レジスト組成物。
  21. 　溶媒、酸発生剤、塩基発生剤及び酸拡散制御剤で構成される群より選択される少なくとも１種をさらに含有する、請求項２０に記載のレジスト組成物。
  22. 　請求項２０又は請求項２１に記載のレジスト組成物を用いて、基板上にレジスト膜を形成する工程と、
    　形成された前記レジスト膜の少なくとも一部を露光する工程と、
    　露光した前記レジスト膜を現像してレジストパターンを形成する工程と、
    　を含む、レジストパターン形成方法。
  23. 　請求項１９に記載の膜形成用組成物と、ジアゾナフトキノン光活性化合物と、溶媒と、を含有する感放射線性組成物であって、
    　前記溶媒の含有量が、前記感放射線性組成物の総量１００質量部に対して２０～９９質量部であり、
    　前記溶媒以外の固形分の含有量が、前記感放射線性組成物の総量１００質量部に対して１～８０質量部である、感放射線性組成物。
  24. 　請求項２３に記載の感放射線性組成物を用いて、基板上にレジスト膜を形成する工程と、
    　形成された前記レジスト膜の少なくとも一部を露光する工程と、
    　露光した前記レジスト膜を現像して、レジストパターンを形成する工程を含む、レジストパターン形成方法。
  25. 　請求項１９に記載の膜形成用組成物を含む、リソグラフィー用下層膜形成用組成物。
  26. 　溶媒、酸発生剤、塩基発生剤及び架橋剤で構成される群から選択される少なくとも１つをさらに含有する、請求項２５に記載のリソグラフィー用下層膜形成用組成物。
  27. 　請求項２５又は請求項２６に記載のリソグラフィー用下層膜形成用組成物を用いて、基板上に下層膜を形成する工程を含む、リソグラフィー用下層膜の製造方法。
  28. 　請求項２５又は請求項２６に記載のリソグラフィー用下層膜形成用組成物を用いて、基板上に、下層膜を形成する工程と、
    　前記下層膜上に、少なくとも１層のフォトレジスト層を形成する工程と、
    　前記フォトレジスト層の所定の領域に放射線を照射し、現像してレジストパターンを形成する工程と、
    　を有する、レジストパターン形成方法。
  29. 　請求項２５又は請求項２６に記載のリソグラフィー用下層膜形成用組成物を用いて、基板上に下層膜を形成する工程と、
    　前記下層膜上に、珪素原子を含有するレジスト中間層膜材料を用いて中間層膜を形成する工程と、
    　前記中間層膜上に、少なくとも１層のフォトレジスト層を形成する工程と、
    　前記フォトレジスト層の所定の領域に放射線を照射し、現像してレジストパターンを形成する工程と、
    　前記レジストパターンをマスクとして前記中間層膜をエッチングして、中間層膜パターンを形成する工程と、
    　前記中間層膜パターンをエッチングマスクとして前記下層膜をエッチングして、下層膜パターンを形成する工程と、
    　前記下層膜パターンをエッチングマスクとして前記基板をエッチングして、前記基板にパターンを形成する工程と、
    　を有する、回路パターン形成方法。
  30. 　請求項１９に記載の膜形成用組成物を含む、光学部材形成用組成物。
  31. 　溶媒、酸発生剤、塩基発生剤及び架橋剤で構成される群から選択される少なくとも１つをさらに含有する、請求項３０に記載の光学部材形成用組成物。
  32. 　請求項１～請求項９のいずれか１項に記載の重合体を、溶媒に溶解させて溶液（Ｓ）を得る工程と、得られた溶液（Ｓ）と酸性の水溶液とを接触させて、前記重合体中の不純物を抽出する工程（第一抽出工程）とを含み、前記溶液（Ｓ）を得る工程で用いる溶媒が、水と任意に混和しない有機溶媒を含む、精製方法。
     
PCT/JP2022/000590 2021-01-19 2022-01-11 重合体、組成物、重合体の製造方法、膜形成用組成物、レジスト組成物、レジストパターン形成方法、感放射線性組成物、リソグラフィー用下層膜形成用組成物、リソグラフィー用下層膜の製造方法、回路パターン形成方法、光学部材形成用組成物 WO2022158335A1 (ja)