WO2022123883A1 - 圧力容器および圧力容器の製造方法 - Google Patents

圧力容器および圧力容器の製造方法 Download PDF

Info

Publication number
WO2022123883A1
WO2022123883A1 PCT/JP2021/036919 JP2021036919W WO2022123883A1 WO 2022123883 A1 WO2022123883 A1 WO 2022123883A1 JP 2021036919 W JP2021036919 W JP 2021036919W WO 2022123883 A1 WO2022123883 A1 WO 2022123883A1
Authority
WO
WIPO (PCT)
Prior art keywords
pressure vessel
continuous reinforcing
layer
volume
resin
Prior art date
Application number
PCT/JP2021/036919
Other languages
English (en)
French (fr)
Inventor
信彦 松本
孝介 池内
淳 三田寺
Original Assignee
三菱瓦斯化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三菱瓦斯化学株式会社 filed Critical 三菱瓦斯化学株式会社
Priority to JP2021577940A priority Critical patent/JP7031806B1/ja
Priority to EP21902987.3A priority patent/EP4261027A4/en
Priority to CN202180080461.2A priority patent/CN116635662A/zh
Priority to US18/266,100 priority patent/US20240027024A1/en
Priority to KR1020237021714A priority patent/KR20230118879A/ko
Publication of WO2022123883A1 publication Critical patent/WO2022123883A1/ja

Abstract

ガスバリア性に優れ、かつ、クラックが発生しにくく、また、内圧疲労に優れた圧力容器およびその製造方法の提供。　樹脂成分と連続強化繊維を含む繊維強化樹脂材料から形成された層を少なくとも胴部に有する圧力容器であって、前記層のうち、内側から厚み方向に０．１％までの内側領域における連続強化繊維含有率（体積％）と前記層のうち外側から厚み方向に０．１％までの外側領域における連続強化繊維含有率（体積％）の比率（内側領域／外側領域）が、０．８０～０．９９であり、前記層のうち、内側から厚み方向に０．１％超から外側から厚み方向に０．１％超までの間の中心領域における連続強化繊維含有率（体積％）が４０～６０体積％である、圧力容器。

Description

圧力容器および圧力容器の製造方法
　本発明は、圧力容器および圧力容器の製造方法に関する。
　近年、環境に配慮した天然ガス自動車（ＣＮＧ車）や燃料電池自動車（ＦＣＶ）の普及が進んでいる。燃料電池自動車は燃料電池を動力源としており、その燃料となる水素を高圧に圧縮して自動車に充填する水素ステーションの整備が不可欠である。
　燃料電池自動車用の水素ステーションに設置されるタンクや、あるいは、ＣＮＧ車、燃料電池自動車等の車載用燃料タンクとして用いられる高圧ガス貯蔵タンクとして、これまで鋼製のタンクが使用されてきた。しかしながら、車体の軽量化の要請に伴い、タンクのライナーあるいはその外層に樹脂材料を用いた、より軽量な高圧ガス貯蔵タンクの開発が進められてきている。車載用燃料タンクを軽量化することにより、搭載車の燃費を改善できるなどのメリットがある。
　高圧ガス貯蔵タンクを構成する樹脂材料として、ガスバリア性を有する樹脂、および、前記樹脂を強化繊維に含浸させた繊維強化複合材（ＦＲＰ）を用いることが知られている。
　例えば、特許文献には、ライナーと、前記ライナーの外層とを有し、外層が連続繊維と前記連続繊維に含浸した所定のガスバリア性ポリアミド樹脂を含む複合材料から構成された圧力容器、および、前記複合材料から構成されるライナーが開示されている。
国際公開第２０１６／０８４４７５号
　ここで、上記特許文献１に記載の圧力容器は優れた圧力容器ではあるが、近年、多種多様な用途で圧力容器が用いられるようになり、さらに新規の繊維強化樹脂材料を用いた圧力容器が求められている。
　特に、ガスバリア性に優れ、かつ、様々な条件でクラックが発生しにくい圧力容器が求められている。
　本発明はかかる課題を解決することを目的とするものであって、ガスバリア性に優れ、かつ、様々な条件でクラックが発生しにくい圧力容器およびその製造方法を提供することを目的とする。
　上記課題のもと、本発明者が検討を行った結果、繊維強化樹脂材料から形成された層を有する圧力容器において、連続強化繊維の体積比率を調整することにより、上記課題を解決しうることを見出した。
　具体的には、下記手段により、上記課題は解決された。
＜１＞樹脂成分と連続強化繊維を含む繊維強化樹脂材料から形成された層を少なくとも胴部に有する圧力容器であって、前記層のうち、内側から厚み方向に０．１％までの内側領域における連続強化繊維含有率（体積％）と前記層のうち外側から厚み方向に０．１％までの外側領域における連続強化繊維含有率（体積％）の比率（内側領域／外側領域）が、０．８０～０．９９であり、前記層のうち、内側から厚み方向に０．１％超から外側から厚み方向に０．１％超までの間の中心領域における連続強化繊維含有率（体積％）が３０～７０体積％である、圧力容器。
＜２＞前記外側領域と前記中心領域における連続強化繊維含有率（体積％）の比率（外側領域／中心領域）が、１．０１～１．１１である、＜１＞に記載の圧力容器。
＜３＞前記内側領域と前記中心領域における連続強化繊維含有率（体積％）の比率（内側領域／中心領域）が、０．９５～１．０５である、＜１＞または＜２＞に記載の圧力容器。
＜４＞前記層の厚さが１～１０ｃｍである、＜１＞～＜３＞のいずれか１つに記載の圧力容器。
＜５＞前記樹脂成分が熱硬化性樹脂を含む、＜１＞～＜４＞のいずれか１つに記載の圧力容器。
＜６＞前記樹脂成分が、エポキシ樹脂、および、下記の成分（ｘ１）と成分（ｘ２）との反応生成物を含むエポキシ樹脂硬化剤を含有するエポキシ樹脂組成物から形成されたものである、＜１＞～＜５＞のいずれか１つに記載の圧力容器。
（ｘ１）メタキシリレンジアミンおよびパラキシリレンジアミンからなる群から選ばれる少なくとも１種
（ｘ２）式（１）で表される不飽和カルボン酸およびその誘導体からなる群から選ばれる少なくとも１種
Figure JPOXMLDOC01-appb-C000002
 （式（１）中、Ｒ１およびＲ２は、それぞれ独立に、水素原子、炭素数１～８のアルキル基、炭素数６～１２のアリール基、または、炭素数７～１３のアラルキル基を表す。）
＜７＞前記連続強化繊維が、炭素繊維を含む、＜１＞～＜６＞のいずれか１つに記載の圧力容器。
＜８＞前記層のボイド率が１体積％以下である、＜１＞～＜７＞のいずれか１つに記載の圧力容器。
＜９＞前記圧力容器の胴部は、前記層の内側にライナーを有する、＜１＞～＜８＞のいずれか１つに記載の圧力容器。
＜１０＞前記圧力容器の胴部は、前記層の内側に層を有さない、＜１＞～＜８＞のいずれか１つに記載の圧力容器。
＜１１＞樹脂成分と連続強化繊維を含む繊維強化樹脂材料を、円筒状に巻き付けることを含み、前記円筒状に巻き付ける際の前記繊維強化樹脂材料の張力が、連続強化繊維一本当たり、０．０１ｇｆ～３ｇｆである、＜１＞～＜１０＞のいずれか１つに記載の圧力容器の製造方法。
　本発明により、ガスバリア性に優れ、かつ、様々な条件でクラックが発生しにくい圧力容器およびその製造方法を提供可能になった。
図１は本実施形態の圧力容器の一実施形態を示す断面模式図である。 図２は圧力容器の胴部が有する樹脂成分と連続強化繊維を含む繊維強化樹脂材料から形成された層（ガスバリア層）の断面拡大図である。
　以下、本発明を実施するための形態（以下、単に「本実施形態」という）について詳細に説明する。なお、以下の本実施形態は、本発明を説明するための例示であり、本発明は本実施形態のみに限定されない。
　なお、本明細書において「～」とはその前後に記載される数値を下限値および上限値として含む意味で使用される。
　本明細書において、各種物性値および特性値は、特に述べない限り、２３℃におけるものとする。
　本実施形態の圧力容器は、樹脂成分と連続強化繊維を含む繊維強化樹脂材料から形成された層（以下、「ガスバリア層」ということがある）を少なくとも胴部に有する圧力容器であって、前記ガスバリア層のうち、内側から厚み方向に０．１％までの内側領域における連続強化繊維含有率（体積％）と前記層のうち外側から厚み方向に０．１％までの外側領域における連続強化繊維含有率（体積％）の比率（内側領域／外側領域）が、０．８０～０．９９であり、前記ガスバリア層のうち、内側から厚み方向に０．１％超から外側から厚み方向に０．１％超までの間の中心領域における連続強化繊維含有率（体積％）が３０～７０体積％であることを特徴とする。
　このような構成とすることにより、ガスバリア性に優れ、かつ、様々な条件でクラックが発生しにくい圧力容器が得られる。
　このメカニズムは推定であるが、以下の通りと推測される。ガスバリア層における厚み方向の連続強化繊維の含有率について、内側から厚み方向に０．１％までのごく薄い内側領域の連続強化繊維の割合をやや低めとすることにより、内部ガスの充填による膨張を吸収し、クラックの発生が抑えられる。また、ガスバリア層における厚み方向の連続強化繊維の含有率について、外側から厚み方向に０．１％までのごく薄い外側領域の連続強化繊維の割合をやや高めとすることにより、圧力容器の機械物性がより改善されると推測される。そして、ガスバリア層の厚み方向における連続強化繊維の内側から厚み方向に０．１％超から外側から厚み方向に０．１％超までの間の中心領域における連続強化繊維含有率（体積％）を３０～７０体積％と密にし、さらに、上述のように、ガスバリア層の厚み方向における連続強化繊維の含有率を段階的ないしグラデーションを持つように設定することにより、気泡を放出しやすくでき、ボイド率を低下させることができ、ガスバリア性に優れた胴部とすることができると推測される。
　以下、本実施形態の詳細について説明する。
　図１は、本実施形態の圧力容器の一例を示す断面模式図であり、図２は圧力容器の胴部が有する樹脂成分と連続強化繊維を含む繊維強化樹脂材料から形成された層（ガスバリア層）の断面拡大図である。
　図１において、１は圧力容器を、２は胴部を、３は内層を、４は外層を、５は口金を、６はボスを、７はバルブを、図２において、８は内側領域を、９は中心領域を、１０は外側領域をそれぞれ示している。図１および図２は、模式図であり、尺度は、実際の値と必ずしも一致していない。
　本実施形態におけるガスバリア層は、例えば、図１における圧力容器１の胴部２を構成する層であり、内層３または外層４のいずれであってもよいが、外層４であることが好ましい。また、図１に示す圧力容器では、内層３と外層４の２層構成となっているが、さらに、他の層を有していてもよい。他の層については、後述する。
　最初にガスバリア層について説明する。本実施形態におけるガスバリア層は、樹脂成分と連続強化繊維を含む繊維強化樹脂材料から形成された層である。ガスバリア層は、通常、前記繊維強化樹脂材料によって胴部２を覆うように形成されている。このような構成とすることにより、後述する圧力容器を透過するガス量を低くすることができる。ガスバリア層において連続強化繊維は、規則的に配列していることが好ましい。規則的に配列しているとは、ガスバリア層における連続強化繊維の７０質量％以上（好ましくは８０質量％以上、より好ましくは９０質量％以上、さらに好ましくは９５質量％以上）が、一定の方向性を持って並んでいることをいう。一定の方向性とは、螺旋状、縦方向、横方向またはこれらの組み合わせが例示される。尚、本実施形態における螺旋状、縦方向、横方向は、厳密な螺旋状等の配列に加え、当業者に一般的に解釈される程度の誤差を含む趣旨である。このように規則的に配列することにより、ガスバリア層（圧力容器）の胴部の表面に連続強化繊維が含まれていない領域を極力少なくすることができ、ガスバリア性がより向上する傾向にある。本実施形態におけるガスバリア層は、通常、その表面の９７質量％以上（好ましくは９９質量％以上）に連続強化繊維が存在するように連続強化繊維が配列されている。
　また、一つの圧力容器に対して複数の種類の連続強化繊維を用いてもよい。例えば、炭素繊維を配列した上から、ガラス繊維を配列することで、耐衝撃性を改善することができる。
　本実施形態におけるガスバリア層は、図２に示すように、内側領域８、中心領域９、外側領域１０で、連続強化繊維の含有量が異なっている。
　具体的には、内側領域８とは、胴部の内側から厚み方向に０．１％までの領域をいい、中心領域９とは胴部の内側から厚み方向に０．１％超から外側から厚み方向に０．１％超までの間の領域をいい、外側領域１０とは胴部の外側から厚み方向に０．１％までの領域をいう。
　そして、内側領域８における連続強化繊維の含有率（体積％）と外側領域１０における連続強化繊維の含有率（体積％）の比率（内側領域／外側領域）が、０．８０～０．９９である。前記下限値以上とすることにより、クラックの発生が抑えられる傾向にある。また、前記上限値以下とすることにより、機械物性により優れる傾向にある。
　前記内側領域８における連続強化繊維の含有率（体積％）／外側領域１０における連続強化繊維の含有率（体積％）は、０．８５以上であることが好ましく、０．９０以上であることがより好ましく、０．９５以上であることがさらに好ましい。
　また、ガスバリア層においては、外側領域１０と中心領域９における連続強化繊維含有率（体積％）の比率（外側領域／中心領域）が、１．０１～１．１１であることが好ましく、１．０１～１．０７であることがより好ましい。また、ガスバリア層においては、内側領域８と中心領域９における連続強化繊維含有率（体積％）の比率（内側領域／中心領域）が、０．９５～１．０５であることが好ましく、０．９５以上１．００未満であることがより好ましく、０．９６以上１．００未満であることがさらに好ましい。このような比率とすることにより、本発明の効果がより効果的に発揮される。
　また、本実施形態におけるガスバリア層においては、中心領域９における連続強化繊維含有率（体積％）が３０～７０体積％である。前記下限値以上とすることにより、機械物性により優れる。また、前記上限値以下とすることにより、ボイド率をより少なくすることができる。前記中心領域９の連続強化繊維含有率は、３３体積％以上であることが好ましく、３６体積％以上であることがより好ましく、また、６５体積％以下であることがより好ましい。
　本実施形態において、中心領域９は、厚み方向において連続強化繊維の含有率が一定であってもよいし、内側領域から外側領域に徐々に増加していてもよい。
　また、本実施形態におけるガスバリア層においては、内側領域８における連続強化繊維含有率（体積％）が、２９体積％以上であることが好ましく、３２体積％以上であることがより好ましく、３５体積％以上あることがさらに好ましく、また、６９体積％以下であることが好ましく、６４体積％以下であることがより好ましい。前記下限値以上とすることにより、機械物性により優れる傾向にある。また、前記上限値以下とすることにより、ボイド率がより少なくなる傾向にある。
　また、本実施形態におけるガスバリア層は、外側領域１０における連続強化繊維含有率（体積％）が、３０体積％以上であることが好ましく、３３体積％以上であることがより好ましく、３６体積％以上であることがさらに好ましく、また、７０体積％以下であることが好ましく、６５体積％以下であることがより好ましい。前記下限値以上とすることにより、機械物性により優れる傾向にある。また、前記上限値以下とすることにより、ボイド率がより少なくなる傾向にある。
　本実施形態におけるガスバリア層においては、内側領域８、中心領域９、外側領域１０を構成する連続強化繊維の組成は同一であってもよいし、異なっていてもよい。本実施形態では、内側領域８、中心領域９、外側領域１０を構成する連続強化繊維の組成はその９５質量％以上（好ましくは９９質量％以上）が共通することが好ましい。
　ガスバリア層は、連続強化繊維を１種のみ含んでいてもよいし、２種以上含んでいてもよい。２種以上含む場合、合計量が上記範囲となることが好ましい。
　本実施形態におけるガスバリア層の厚さは、ガスバリア層１層につき、１ｃｍ以上であることが好ましく、３ｃｍ以上であることがより好ましく、４ｃｍ以上であることがさらに好ましい。また、１５ｃｍ以下であることが好ましく、１０ｃｍ以下であることがより好ましく、８ｃｍ以下であることがさらに好ましい。
　また、本実施形態における胴部の厚さ（１層または２層以上のガスバリア層および他の層の合計厚さ）は、１ｃｍ以上であることが好ましく、３ｃｍ以上であることがより好ましく、４ｃｍ以上であることがさらに好ましい。また、３０ｃｍ以下であることが好ましく、２０ｃｍ以下であることがより好ましく、１５ｃｍ以下であることがさらに好ましく、１０ｃｍ以下であってもよく、さらには６ｃｍ以下であってもよい。
　本実施形態におけるガスバリア層においては、ボイド率が１体積％以下であることが好ましい。ボイド率とは、ガスバリア層中に含まれる気泡（ボイド）の割合であり、後述する実施例に記載の方法に従って測定される。ボイド率がこのように低いことにより透過ガス量がより低減する傾向にある。ボイド率は、０．７体積％以下であることが好ましく、０．５体積％以下であることがより好ましく、０．３体積％以下であることがさらに好ましく、０．１体積％未満であることが一層好ましい。ボイド率の下限値は０が理想である。
　ボイド率を低くする方法としては、連続強化繊維含有率の調整、樹脂の粘度調整、成形温度の調整、フィラメントワインド時のワインド角度やクリール張力の調整などが例示される。
　次に、本実施形態の圧力容器の胴部の層構成について説明する。
　本実施形態の圧力容器は、上述の通り、胴部に上記ガスバリア層のみを有していてもよいし、他の層を有していてもよい。
　本実施態様の圧力容器の一例は、胴部が、ガスバリア層の内側に層を有さない態様（態様１）である。態様１におけるガスバリア層は、ライナーとしての機能を果たしつつ、ライナーを補強する外層としての役割も果たす。本実施態様で用いるガスバリア層は、クラックが発生しにくく、ガスの充填と使用による容器の膨張・収縮等の影響を受けにくいため、好ましく用いることができる。
　また、態様１においては、胴部が１層または２層のガスバリア層のみから構成されていてもよいし、ガスバリア層の外側に層を有していてもよい。前記外側の層としては、第二のガスバリア層、意匠性層、金属層（例えば、アルミニウム層）、前記ガスバリア層以外の繊維強化樹脂層などが例示される。例えば、第一のガスバリア層を構成する樹脂成分が熱硬化性樹脂を含むものであり、第二のガスバリア層を構成する樹脂成分が熱可塑性樹脂を含むものとすることができる。このような構成とすることにより、熱硬化性樹脂のメリットと熱可塑性樹脂のメリットの両方を有する圧力容器とすることができる。
　本実施形態の圧力容器においては、前記内側領域／外側領域の比率等を満たしているガスバリア層に加え、前記内側領域／外側領域の比率等を満たしていないガスバリア性を有する層を有していてもよい。
　ガスバリア層は、内層（例えばライナー）であってもよいし、樹脂製ライナーの外側に設けられた外層であってもよい。好ましくは内層であり、より好ましくは最内層である。
　態様１における胴部の合計厚さは、１ｃｍ以上であることが好ましく、３ｃｍ以上であることがより好ましく、４ｃｍ以上であることがさらに好ましい。また、２０ｃｍ以下であることが好ましく、１８ｃｍ以下であることがより好ましく、１６ｃｍ以下であることがさらに好ましい。
　本実施形態の圧力容器の他の一例は、胴部が、ガスバリア層の内側に他の層を有する態様（態様２）である。態様２における他の層としては、ライナーや、ライナーおよびガスバリア層の間に設けられた粘着層などが例示される。態様２では、ライナーと前記ライナーと接しているガスバリア層を有する態様が挙げられる。態様２においては、さらに、ガスバリア層の外側に他の層を有していてもよい。この場合の他の層としては、意匠性層などが挙げられる。
　態様２におけるライナーは、金属製ライナー、樹脂製ライナーが例示され、樹脂製ライナーが好ましい。樹脂製ライナーを用いる場合であって、ガスバリア層を構成する樹脂成分が熱硬化性樹脂である場合、樹脂製ライナーの樹脂成分は、熱可塑性樹脂が好ましい。また、樹脂製ライナーを用いる場合であって、ガスバリア層を構成する樹脂成分が熱可塑性樹脂である場合、樹脂製ライナーの樹脂成分も熱可塑性樹脂が好ましい。
　態様２におけるライナーの厚さは、１００μｍ以上であることが好ましく、２００μｍ以上であることがより好ましく、５００μｍ以上であることがさらに好ましい。また、１０，０００μｍ以下であることが好ましく、７，０００μｍ以下であることがより好ましく、５，０００μｍ以下であることがさらに好ましい。
　態様２における胴部の合計厚さは、１ｃｍ以上であることが好ましく、３ｃｍ以上であることがより好ましく、４ｃｍ以上であることがさらに好ましい。また、２０ｃｍ以下であることが好ましく、１８ｃｍ以下であることがより好ましく、１６ｃｍ以下であることがさらに好ましい。
　さらに、本実施形態の圧力容器は、図１に示すように、ガスバリア層を有する胴部２に加え、口金５、ボス６、バルブ７などを有している。また、胴部を延長する形で、胴部の口金５側およびボス６側に胴部を封止するドーム部を有する。ドーム部は、通常、胴部（内層３、内層４）等と同じ組成で形成されている。
　その他、他部材との着脱を行うための着脱部等（非図示）を設けることもできる。
　次に、ガスバリア層を構成する繊維強化樹脂材料について説明する。
　本実施形態におけるガスバリア層は、樹脂成分と連続強化繊維を含む繊維強化樹脂材料から形成された層である。連続強化繊維を用いることにより、ガスバリア性を高めることができ、また、圧力容器の強度を高くすることができる。また、連続強化繊維だけでは隙間を完全に密に埋めることができないが、樹脂成分を設けることにより、このような隙間を埋めることができる。
　本実施形態における繊維強化樹脂材料は樹脂成分を含む。樹脂成分は、熱可塑性樹脂であっても、熱硬化性樹脂であってもよいし、両者の混合物であってもよい。樹脂成分の態様の一例は、樹脂成分が熱可塑性樹脂を含む態様であり、樹脂成分の９０質量％以上が熱可塑性樹脂である態様である。樹脂成分の態様の他の一例は、樹脂成分が熱硬化性樹脂を含む態様であり、樹脂成分の９０質量％以上が熱硬化性樹脂である態様である。
　熱硬化性樹脂としては、エポキシ樹脂、フェノール樹脂、（メタ）アクリレート樹脂、不飽和ポリエステル樹脂、ジアリル二レート樹脂、シアネート樹脂、マレイミド樹脂が例示され、エポキシ樹脂が好ましい。
　エポキシ樹脂を用いる場合、樹脂成分として、エポキシ樹脂、および、下記の成分（ｘ１）と成分（ｘ２）との反応生成物を含むエポキシ樹脂硬化剤を含有するエポキシ樹脂組成物を用いることが好ましい。
（ｘ１）メタキシリレンジアミンおよびパラキシリレンジアミンからなる群から選ばれる少なくとも１種
（ｘ２）式（１）で表される不飽和カルボン酸およびその誘導体からなる群から選ばれる少なくとも１種
Figure JPOXMLDOC01-appb-C000003
 （式（１）中、Ｒ１およびＲ２は、それぞれ独立に、水素原子、炭素数１～８のアルキル基、炭素数６～１２のアリール基、または、炭素数７～１３のアラルキル基を表す。）
　また、エポキシ樹脂組成物としては、特開２０１７－００８３１６号公報に記載のエポキシ樹脂組成物および特開２０１６－１９０９２０号公報に記載のエポキシ樹脂組成物も用いることができ、これらの内容は本明細書に組み込まれる。
　熱可塑性樹脂としては、ポリオレフィン樹脂、ポリエチレン樹脂、ポリプロピレン樹脂、ポリアミド樹脂、アクリロニトリル－ブタジエン－スチレン共重合体（ＡＢＳ）樹脂、ポリブチレンテレフタレート樹脂、ポリアセタール樹脂、ポリカーボネート樹脂等が例示され、ポリアミド樹脂が好ましい。ポリアミド樹脂は、脂肪族ポリアミド樹脂であっても、半芳香族ポリアミド樹脂であってもよいが、半芳香族ポリアミド樹脂が好ましい。半芳香族ポリアミド樹脂としては、ジアミン由来の構成単位とジカルボン酸由来の構成単位を含み、ジアミン由来の構成単位の５０モル％以上（好ましくは７０モル％以上、より好ましくは９０モル％以上）がキシリレンジアミンに由来し、ジカルボン酸由来の構成単位の５０モル％以上が炭素数４～２０のα，ω－直鎖脂肪族ジカルボン酸由来の構成単位（好ましくは、アジピン酸、セバシン酸およびドデカンニ酸のいずれか１種以上由来の構成単位）であるポリアミド樹脂が好ましい。
　前記樹脂成分は、水素透過係数が低いことが好ましい。水素透過係数が低いことにより、水素ガス用の圧力容器として好ましく用いることができる。樹脂成分の水素透過係数は、１５．０×１０－１１ｃｃ・ｃｍ／（ｃｍ２・ｓ・ｃｍＨｇ）以下であることが好ましく、１２．０×１０－１１ｃｃ・ｃｍ／（ｃｍ２・ｓ・ｃｍＨｇ）以下であることがより好ましく、５．０×１０－１１ｃｃ・ｃｍ／（ｃｍ２・ｓ・ｃｍＨｇ）以下であることがさらに好ましく、３．０×１０－１１ｃｃ・ｃｍ／（ｃｍ２・ｓ・ｃｍＨｇ）以下であることが一層好ましく、２．５×１０－１１ｃｃ・ｃｍ／（ｃｍ２・ｓ・ｃｍＨｇ）以下であることがより一層好ましい。下限値は、０が理想であるが、１．０×１０－１１ｃｃ・ｃｍ／（ｃｍ２・ｓ・ｃｍＨｇ）以上が実際的である。
　樹脂成分が２種以上の樹脂を含む場合、混合物の水素透過係数とする。
　本実施形態においては、樹脂成分は、本発明の趣旨を逸脱しない範囲で他の成分を含んでいてもよい。具体的には、カップリング剤、反応性希釈剤、溶剤、溶剤以外の反応性希釈剤、硬化促進剤、湿潤剤、粘着付与剤、消泡剤、艶消剤、防錆剤、滑剤、着色剤、酸素捕捉剤、紫外線吸収剤、酸化防止剤、可塑剤、分散剤、難燃剤、帯電防止剤、着色防止剤、ゲル化防止剤等の添加剤が例示される。これらの合計量は、樹脂成分の１０質量％以下であることが好ましい。
　本実施形態においては、繊維強化樹脂材料は連続強化繊維を含む。
　本実施形態のガスバリア層に用いる連続強化繊維は、１００ｍｍを超える繊維長を有する強化繊維である。
　連続強化繊維の形状としては、トウ、糸、フィラメント、シート、テープ等と称されるものが挙げられ、シートまたはテープを構成する連続強化繊維としては、一方向（ＵＤ）材、織物、不織布等が挙げられる。
　繊維強化樹脂材料における連続強化繊維のフィラメント数は、２４００本以上であることが好ましく、また、２４００００本以下であることが好ましい。前記下限値以上とすることにより、生産性に優れる傾向にある。前記上限値以下とすることにより、成形性に優れる傾向にある。
　連続強化繊維束の平均繊維長には特に制限はないが、成形加工性の観点から、好ましくは５ｃｍ以上であり、より好ましくは１ｍ以上であり、さらに好ましくは１００ｍ以上であり、また、好ましくは１０，０００ｍ以下である。
　連続強化繊維束の平均繊度は、成形加工性の観点、高強度および高弾性率が得られやすいという観点から、好ましくは５０ｔｅｘ（ｇ／１０００ｍ）以上であり、より好ましくは２００ｔｅｘ以上であり、さらに好ましくは５００ｔｅｘ以上である。また、好ましくは、２，０００ｔｅｘ以下であり、より好ましくは１，５００ｔｅｘ以下であり、さらに好ましくは１，０００ｔｅｘ以下である。
　また、連続強化繊維束の平均引張弾性率は、好ましくは５０ＧＰａ以上であり、また、好ましくは１０００ＧＰａ以下である。
　連続強化繊維の材質としては、ガラス繊維、炭素繊維、金属繊維、ボロン繊維、バサルト繊維、セラミック繊維等の無機繊維；アラミド繊維、ポリオキシメチレン繊維、芳香族ポリアミド繊維、ポリパラフェニレンベンゾビスオキサゾール繊維、超高分子量ポリエチレン繊維等の有機繊維が挙げられる。これらの中でも、高強度を得る観点からは無機繊維が好ましく、軽量でかつ高強度、高弾性率であることからガラス繊維、炭素繊維およびバサルト繊維からなる群から選ばれる少なくとも１種がより好ましく、炭素繊維がさらに好ましい。
　炭素繊維としては、ポリアクリロニトリル系炭素繊維、ピッチ系炭素繊維等が挙げられる。また、リグニンやセルロースなど、植物由来原料の炭素繊維も用いることができる。
　本実施形態に用いる連続強化繊維は、処理剤で処理されたものでもよい。処理剤としては、表面処理剤または集束剤が例示される。
　上記表面処理剤としては、シランカップリング剤が好ましい。シランカップリング剤としては、ビニル基を有するシランカップリング剤、アミノ基を有するシランカップリング剤、エポキシ基を有するシランカップリング剤、（メタ）アクリル基を有するシランカップリング剤、メルカプト基を有するシランカップリング剤等が挙げられる。
　上記集束剤としては、例えば、ウレタン系集束剤、エポキシ系集束剤、アクリル系集束剤、ポリエステル系集束剤、ビニルエステル系集束剤、ポリオレフィン系集束剤、ポリエーテル系集束剤、およびカルボン酸系集束剤等が挙げられ、これらのうち１種または２種以上を組み合わせて用いることができる。２種以上を組み合わせた集束剤としては、例えば、ウレタン／エポキシ系集束剤、ウレタン／アクリル系集束剤、ウレタン／カルボン酸系集束剤等が挙げられる。
　上記の中でも、熱硬化性樹脂、特にエポキシ樹脂組成物の硬化物との界面接着性を向上させ、得られるガスバリア層の強度および耐衝撃性をより向上させる観点から、連続強化繊維はウレタン系集束剤、エポキシ系集束剤およびウレタン／エポキシ系集束剤からなる群から選ばれる１種以上により処理されたものであることが好ましく、エポキシ系集束剤により処理されたものであることがより好ましい。
　前記処理剤の量は、熱硬化性樹脂または熱硬化性樹脂組成物の硬化物との界面接着性を向上させ、得られるガスバリア層の強度および耐衝撃性をより向上させる観点から、連続強化繊維に対し、好ましくは０．００１～５質量％、より好ましくは０．１～３質量％、さらに好ましくは０．５～２質量％である。
　連続強化繊維として市販品を用いることもできる。連続強化繊維である炭素繊維の市販品としては、例えば東レ（株）製のトレカ糸「Ｔ３００」、「Ｔ３００Ｂ」、「Ｔ４００ＨＢ」、「Ｔ７００ＳＣ」、「Ｔ８００ＳＣ」、「Ｔ８００ＨＢ」、「Ｔ８３０ＨＢ」、「Ｔ１０００ＧＢ」、「Ｔ１００ＧＣ」、「Ｍ３５ＪＢ」、「Ｍ４０ＪＢ」、「Ｍ４６ＪＢ」、「Ｍ５０ＪＢ」、「Ｍ５５Ｊ」、「Ｍ５５ＪＢ」、「Ｍ６０ＪＢ」、「Ｍ３０ＳＣ」、「Ｚ６００」の各シリーズ、トレカクロス「ＣＯ６１４２」「ＣＯ６１５１Ｂ」、「ＣＯ６３４３」、「ＣＯ６３４３Ｂ」、「ＣＯ６３４７Ｂ」、「ＣＯ６６４４Ｂ」、「ＣＫ６２４４Ｃ」、「ＣＫ６２７３Ｃ」、「ＣＫ６２６１Ｃ」、「ＵＴ７０」シリーズ、「ＵＭ４６」シリーズ、「ＢＴ７０」シリーズ等が挙げられる。
　本実施形態における繊維強化樹脂材料においては、本実施形態の効果を得る観点から、樹脂成分（上述の添加剤を含む）と連続強化繊維の合計が、好ましくは９０質量％以上であり、より好ましくは９５質量％以上であり、さらに好ましくは９９質量％以上であり、上限は１００質量％である。
　次に、圧力容器の製造方法について説明する。
　本実施形態の圧力容器は、公知の方法で製造することができる。特に、胴部は、繊維強化樹脂材料を用いて、ブレーディング法、ワインディング法、３Ｄプリント法等により成形される。このときの、繊維強化樹脂材料は、一方向または二方向以上に連続強化繊維が規則的に配列したものに樹脂成分が含浸している材料が好ましく、プリプレグなどが代表例として例示される。
　胴部は、上述の通り、通常、上記繊維強化樹脂材料を円筒状に連続強化繊維がほぼ隙間なく存在するように成形して形成される。
　本実施形態においては、上述のように内側領域、中心領域および外側領域の連続強化繊維含有率およびガスバリア層の厚さを達成するために、公知の手段で調整することができる。
　具体的には、繊維強化樹脂材料を調整する方法が挙げられる。すなわち、フィラメントワインド成形品は、通常、常温での樹脂の流動性が高いため、内側ほど絞られて、連続強化繊維の割合が高くなる。また、通常、最後にラッピングフィルムを巻く際に、外側の樹脂が流出するため、外側の連続強化繊維の割合が高くなる。本実施形態では、例えば、常温での樹脂粘度が高い樹脂を用いることで、内側の連続強化繊維の割合を外側よりも低くすることができる。このような樹脂成分として、上述のエポキシ樹脂、および、上記の成分（ｘ１）と成分（ｘ２）との反応生成物を含むエポキシ樹脂硬化剤を含有するエポキシ樹脂組成物が例示される。また、トウプリプレグを用いることでも、内側領域が絞られにくく、また、外側の樹脂も流出しにくくし、内側領域および外側領域の連続強化繊維の割合を調整することができる。
　また、繊維強化樹脂材料を円筒状の胴部に形成する際に、その巻き付け方などを工夫することもできる。具体的には、繊維強化樹脂材料としてテープ状または紐状の材料を用い、その巻き付ける角度を調整すること、繊維強化樹脂材料を胴部に成形加工する際の加熱条件を調整すること、繊維強化樹脂材料を巻き付ける際のテンションなどを調整することが例示される。例えば、樹脂成分と連続強化繊維を含む繊維強化樹脂材料を、円筒状に巻き付けることを含み、前記円筒状に巻き付ける際の前記繊維強化樹脂材料の張力が、連続強化繊維一本当たり、０．０１ｇｆ～３ｇｆ（好ましくは、０．０５～２．５ｇｆ）である、圧力容器の製造方法が例示される。
　なお、円筒状とは、筒の長手方向に垂直な断面が円形であることが例示されるが、本発明の趣旨を逸脱しない範囲で楕円形なども含む趣旨である。
　本実施形態の圧力容器は、高圧ガス貯蔵タンクとして好ましく用いることができる。高圧ガス貯蔵タンクの貯蔵対象となるガスは、２５℃、１ａｔｍで気体のものであればよく、水素の他、酸素、二酸化炭素、窒素、アルゴン、ＬＰＧ、代替フロン、メタン等が挙げられる。これらの中でも、好ましくは水素である。
　本実施形態の圧力容器は、水素ガス等のガスバリア性が良好で、軽量性、耐圧性、耐衝撃性にも優れるものとなる。
　本実施形態の高圧ガス貯蔵タンクは、胴部が前記ガスバリア層のみで構成されていてもよく、ガスバリア層と他の層とを備えたものでもよい。これらの詳細は、上述の胴部の説明を参酌できる。本実施形態におけるガスバリア層は耐圧性、耐衝撃性に優れるため、さらに他の層を設ける場合でも、その厚みを薄くすることが可能である。
　以下に実施例を挙げて本発明をさらに具体的に説明する。以下の実施例に示す材料、使用量、割合、処理内容、処理手順等は、本発明の趣旨を逸脱しない限り、適宜、変更することができる。従って、本発明の範囲は以下に示す具体例に限定されるものではない。
　実施例で用いた測定機器等が廃番等により入手困難な場合、他の同等の性能を有する機器を用いて測定することができる。
１．原料
＜アミン系エポキシ樹脂硬化剤Ａの調製＞
　反応容器に１ｍｏｌのメタキシリレンジアミンを仕込んだ。窒素気流下６０℃に昇温し、８８ｍｏｌのアクリル酸メチルを１時間かけて滴下した。生成するメタノールを留去しながら１６５℃に昇温し、２．５時間１６５℃を保持した。メタノールを、固形分濃度が６５質量％相当になるよう、１．５時間かけて滴下し、６５℃に冷却した後、溶融したエチレンカーボネート０．２７ｍｏｌを３０分かけて滴下し、５時間６５℃に保持し、アミン系エポキシ樹脂硬化剤Ａを得た。
＜アミン系エポキシ樹脂硬化剤Ｂの調製＞
　反応容器に１ｍｏｌのメタキシリレンジアミンを仕込んだ。窒素気流下６０℃に昇温し、９３ｍｏｌのアクリル酸メチルを１時間かけて滴下した。生成するメタノールを留去しながら１６５℃に昇温し、２．５時間１６５℃を保持した。メタノールを、固形分濃度が６５質量％相当になるよう、１．５時間かけて滴下し、６５℃に冷却し、アミン系エポキシ樹脂硬化剤Ｂを得た。
＜樹脂成分Ａ１の調製＞
　上記アミン系エポキシ樹脂硬化剤Ａに、メタノールおよびＴＥＴＲＡＤ－Ｘ（エポキシ樹脂、三菱瓦斯化学（株）製）を、固形分濃度が４０質量％、かつ、アミン系エポキシ樹脂硬化剤中の活性アミン水素数／エポキシ樹脂中のエポキシ基の数が１．０になるように加え、十分に攪拌した。
＜樹脂成分Ａ２の調製＞
　上記アミン系エポキシ樹脂硬化剤Ａに、メタノールを、次いでＴＥＴＲＡＤ－Ｘ（エポキシ樹脂、三菱瓦斯化学（株）製）を、固形分濃度が４０質量％かつ、アミン系エポキシ樹脂硬化剤中の活性アミン水素数／エポキシ樹脂中のエポキシ基の数が１．２になるように加え、十分に攪拌した。
＜樹脂成分Ｂの調製＞
　上記アミン系エポキシ樹脂硬化剤Ｂに、メタノールを、次いでＴＥＴＲＡＤ－Ｘ（エポキシ樹脂、三菱瓦斯化学（株）製）を、固形分濃度が４０質量％かつ、エポキシ樹脂硬化剤中の活性アミン水素数／エポキシ樹脂中のエポキシ基の数が１．０になるように加え、十分に攪拌した。
＜樹脂成分Ｃの調製＞
　ｊＥＲ　８２８（エポキシ樹脂、三菱ケミカル社製）に、アミン系エポキシ樹脂硬化剤として、ジアミノジフェニルエタン（東京化成工業社製）をアミン系エポキシ樹脂硬化剤中の活性アミン水素数／エポキシ樹脂中のエポキシ基の数が１．０になるように加え、十分に攪拌した。
＜樹脂成分Ｄの調製＞
　ｊＥＲ　８２８に、アミン系エポキシ樹脂硬化剤として、イソホロンジアミン（東京化成工業社製）をエポキシ樹脂硬化剤中の活性アミン水素数／エポキシ樹脂中のエポキシ基の数が１．０になるように加え、十分に攪拌した。
炭素繊維：東レ（株）製、連続炭素繊維「トレカ糸　Ｔ８００ＳＣ－２４０００」（フィラメント数：２４，０００、繊度：１，０３０ｔｅｘ、引張弾性率：２９４ＧＰａ）
＜樹脂成分の水素透過係数［ｃｃ・ｃｍ／（ｃｍ２・ｓ・ｃｍＨｇ）］の測定＞
　上記樹脂成分Ａ～Ｄの水素透過係数は、樹脂を厚み１００μｍに試験片に成形し、２３℃の乾燥状態（相対湿度０％）における値を、蒸気透過率測定装置を用いて測定した。
　具体的には、樹脂成分Ａ～Ｄを、バーコーターを用いて、離型剤を塗布した平滑な金属板に厚み１００μｍで２００ｍｍ角に塗工した後、１００℃で５分間加熱して硬化させ、硬化物を作製した。この硬化物を用いて、蒸気透過率測定装置を使用して、２３℃の乾燥状態で水素ガス透過係数を測定した。
　蒸気透過率測定装置は、ＧＴＲテック（株）製「Ｇ２７００Ｔ・Ｆ」を用いた。
実施例１～９、比較例１
＜圧力容器の作製＞
　表１または表２に示す樹脂成分および連続炭素繊維を用いた。
　樹脂成分を上記連続炭素繊維に含浸させた後、８０℃の熱風乾燥機内で８０秒間加熱して乾燥させ、トウプリプレグを作製した。次いで、フィラメントワインディング法により、トウプリプレグを直径５００ｍｍ、長さ１０００ｍｍ、両端が半球状の高密度ポリエチレン製ライナー（厚み５００μｍ）に、連続炭素繊維が螺旋構造となるよう、また、連続炭素繊維の張力が炭素繊維一本当たり１．２ｇｆとなるように巻き付けた。１００℃で１８０分加熱硬化させて、外径６００ｍｍ、長さ１１００ｍｍの圧力容器を得た。このとき、胴部における連続強化繊維の内側領域、中心領域および外側領域の含有率、ならびに、ガスバリア層の厚さが表１または表２に示す値となるように調整した。
＜強化繊維の体積含有率およびその比率＞
　胴部の強化繊維体積含有率（内側、中心、外側）（体積％）は以下の方法に従って測定した。
　胴部を外側から内側に、長手方向（図１の矢印Ａの方向）から胴部の中心部に向かって垂直となるように切断し、目的箇所の内側、中心、外側の試験片を切り出した。切り出した試験片をエポキシ樹脂で包埋し、前記包埋した試験片の切断面を研磨し、断面を、超深度カラー３Ｄ形状測定顕微鏡を使用して撮影した。得られた断面写真に対し、内側、中心および外側領域における連続強化繊維の領域を、画像解析ソフトを用いて選択し、各領域について、その合計面積を測定した。強化繊維体積含有率は、連続強化繊維の合計面積／撮影断面面積（単位％）として示した。本測定を５回繰り返し、その数平均値とした。
　超深度カラー３Ｄ形状測定顕微鏡は、ＶＫ－９５００（コントローラー部）／ＶＫ－９５１０（測定部）（キーエンス製）を使用した。画像解析ソフトは、ＩｍａｇｅＪを用いた。
　なお、内側領域、中心領域、外側領域は、図２にその概略図を示す通り、ガスバリア層の断面において、順に、胴部の内側から厚み方向に０．１％までの領域（内側領域８）、胴部の内側から厚み方向に０．１％超から外側から厚み方向に０．１％超までの間の領域（中心領域９）をいい、胴部の外側から厚み方向に０．１％までの領域（外側領域１０）をいう。
＜圧力容器の２４時間で透過するガス量［ｃｍ３］＞
　圧力容器に水素ガスを３０ＭＰａ充填し、室温、常圧で２４時間静置した。２４時間経過した時点での内圧から透過したガス量を算出した。
＜ガスバリア層のボイド率（体積％）＞
　得られた胴部から１ｃｍｘ１ｃｍの試料を切り取り、Ｘ線にて、断面写真を撮影した。得られた断面写真に対し、胴部のガスバリア層中のボイドを、画像解析ソフトを用いて選択し、その面積を測定した。ボイド率は、ボイド領域の面積／撮影した領域の面積（単位％）として示した。
　断面写真の測定は、Ｘ線ＣＴ－ｓｃａｎ（ヤマト製、ＴＤＭ　１０００Ｈ－ＩＩ）を使用した。画像解析ソフトは、Ａ像くん（旭化成エンジニアリング社製）を用いた。
＜吸水時の疲労特性＞
　容器の外面を１０日間水に浸した後に、試験片を切り出し、Ｂ－７０型（東洋精機製）の疲労試験機を用いて、２３℃、１００ｋｇ／ｍｍ２の応力で疲労試験を実施した。クラックの発生までの状態を以下の通り評価した。
　評価は専門家５人が行い、多数決とした。
Ａ：クラックが発生するまでに十分な時間が確保された（実用レベル）。
Ｂ：ＡおよびＣ以外（実用レベル）。
Ｃ：速やかにクラックが発生した（実用レベル外）。
＜内圧疲労特性＞
　電気油圧サーボ疲労試験機に油圧ジャッキを取り付け、高圧配管を通して容器に接続し、圧力媒体を導入した。疲労試験機を加振させて容器に３０ＭＰａの内圧疲労負荷を与えた。クラックが発生するまで繰り返し、クラックの発生までの状態を以下の通り評価した。
　評価は専門家５人が行い、多数決とした。
Ａ：クラックが発生するまでに十分な時間が確保された（実用レベル）。
Ｂ：ＡおよびＣ以外（実用レベル）。
Ｃ：速やかにクラックが発生した。
実施例１０
　下記の要領で、圧力容器用ライナーおよび高圧ガス貯蔵タンクを作製した。
＜ライナーの胴部の作製＞
　熱硬化性樹脂としてＡ１、連続強化繊維として炭素繊維を用いた。
　Ａ１を上記連続炭素繊維に含浸させた後、８０℃の熱風乾燥機内で８０秒間加熱して乾燥させ、トウプリプレグを作製した。次いで、ブレーディング法により、前記トウプリプレグを直径５００ｍｍ、長さ１０００ｍｍの中空の金属マンドレル上に、組紐構造となるよう製紐して、外径６００ｍｍ、長さ１１００ｍｍ、厚さ５０ｍｍの円筒状プリプレグを作製した。この円筒状プリプレグを金属マンドレル上で、１２０℃で３０分加熱硬化させた後、金属マンドレルを取り外し、炭素繊維強化複合材から構成されるライナー胴部を作製した。このとき、胴部における連続強化繊維の内側領域、中心領域および外側領域の含有率、ならびに、厚さ（ガスバリア層の厚さ）が表２に示す値となるように調整した。
＜ライナーのドーム部の作製＞
　樹脂成分Ａ１、連続強化繊維として東レ（株）製の連続炭素繊維「トレカクロス　ＵＴ７０－３０Ｇ」（一方向クロス、シート厚さ０．１６７ｍｍ）を用いた。
　樹脂成分Ａ１を上記連続炭素繊維に含浸させた後、８０℃の熱風乾燥機内で８０秒間加熱して乾燥させ、プリプレグを作製した。次いで、鋳型を用いて、熱プレス成形法により、プレス圧力０．５ＭＰａ、プレス温度１４０℃、プレス時間１２０分にて、直径５０ｍｍの開口部を有する中空のドーム部と、開口部のない中空のドーム部とを作製した。これらのドーム部は、外径３００ｍｍ、ドーム部高さ１２５ｍｍ、厚さ２５ｍｍであり、連続炭素繊維の体積比率（Ｖｆ）は５９．１％であった。
＜ライナーおよび高圧ガス貯蔵タンクの作製＞
　前記方法で得られたライナー円筒部の両端に、上記ドーム部をそれぞれボルトで接合して、ライナーを得た。さらにライナーの外表面に、フィラメントワインディング法により、ライナーの胴部の作製に用いたものと同じトウプリプレグを巻き付けて１２０℃で２４０分加熱し、厚さ６０ｍｍの外層を形成して、高圧ガス貯蔵タンクを得た。
　実施例１と同様に評価した。ただし、連続強化繊維の体積含有率およびその比率、ならびに、ボイド率は、ライナー部分についての値を測定した。
Figure JPOXMLDOC01-appb-T000004
Figure JPOXMLDOC01-appb-T000005
　上記表１および表２において、「０．１＞」は０．１体積％未満であることを示す。
　上記結果から明らかなとおり、本発明の圧力容器は、ガスバリア性に優れ、かつ、様々な条件でクラックが発生しにくかった。特に、吸水時の疲労特性や内圧疲労特性に優れた圧力容器が得られた。
１　　圧力容器
２　　胴部
３　　内層
４　　外層
５　　口金
６　　ボス
７　　バルブ
８　　内側領域
９　　中心領域
１０　外側領域

Claims (11)

  1. 樹脂成分と連続強化繊維を含む繊維強化樹脂材料から形成された層を少なくとも胴部に有する圧力容器であって、
    前記層のうち、内側から厚み方向に０．１％までの内側領域における連続強化繊維含有率（体積％）と前記層のうち外側から厚み方向に０．１％までの外側領域における連続強化繊維含有率（体積％）の比率（内側領域／外側領域）が、０．８０～０．９９であり、
    前記層のうち、内側から厚み方向に０．１％超から外側から厚み方向に０．１％超までの間の中心領域における連続強化繊維含有率（体積％）が３０～７０体積％である、圧力容器。
  2. 前記外側領域と前記中心領域における連続強化繊維含有率（体積％）の比率（外側領域／中心領域）が、１．０１～１．１１である、請求項１に記載の圧力容器。
  3. 前記内側領域と前記中心領域における連続強化繊維含有率（体積％）の比率（内側領域／中心領域）が、０．９５～１．０５である、請求項１または２に記載の圧力容器。
  4. 前記層の厚さが１～１０ｃｍである、請求項１～３のいずれか１項に記載の圧力容器。
  5. 前記樹脂成分が熱硬化性樹脂を含む、請求項１～４のいずれか１項に記載の圧力容器。
  6. 前記樹脂成分が、エポキシ樹脂、および、下記の成分（ｘ１）と成分（ｘ２）との反応生成物を含むエポキシ樹脂硬化剤を含有するエポキシ樹脂組成物から形成されたものである、請求項１～５のいずれか１項に記載の圧力容器。
    （ｘ１）メタキシリレンジアミンおよびパラキシリレンジアミンからなる群から選ばれる少なくとも１種
    （ｘ２）式（１）で表される不飽和カルボン酸およびその誘導体からなる群から選ばれる少なくとも１種
    Figure JPOXMLDOC01-appb-C000001
     （式（１）中、Ｒ１およびＲ２は、それぞれ独立に、水素原子、炭素数１～８のアルキル基、炭素数６～１２のアリール基、または、炭素数７～１３のアラルキル基を表す。）
  7. 前記連続強化繊維が、炭素繊維を含む、請求項１～６のいずれか１項に記載の圧力容器。
  8. 前記層のボイド率が１体積％以下である、請求項１～７のいずれか１項に記載の圧力容器。
  9. 前記圧力容器の胴部は、前記層の内側にライナーを有する、請求項１～８のいずれか１項に記載の圧力容器。
  10. 前記圧力容器の胴部は、前記層の内側に層を有さない、請求項１～８のいずれか１項に記載の圧力容器。
  11. 樹脂成分と連続強化繊維を含む繊維強化樹脂材料を、円筒状に巻き付けることを含み、前記円筒状に巻き付ける際の前記繊維強化樹脂材料の張力が、連続強化繊維一本当たり、０．０１ｇｆ～３ｇｆである、請求項１～１０のいずれか１項に記載の圧力容器の製造方法。
PCT/JP2021/036919 2020-12-11 2021-10-06 圧力容器および圧力容器の製造方法 WO2022123883A1 (ja)