WO2022024798A1 - Plaque de polarisation, plaque de polarisation avec couche de différence de phase, et dispositif d'affichage d'image utilisant ladite plaque de polarisation ou ladite plaque de polarisation avec couche de différence de phase - Google Patents

Plaque de polarisation, plaque de polarisation avec couche de différence de phase, et dispositif d'affichage d'image utilisant ladite plaque de polarisation ou ladite plaque de polarisation avec couche de différence de phase Download PDF

Info

Publication number
WO2022024798A1
WO2022024798A1 PCT/JP2021/026726 JP2021026726W WO2022024798A1 WO 2022024798 A1 WO2022024798 A1 WO 2022024798A1 JP 2021026726 W JP2021026726 W JP 2021026726W WO 2022024798 A1 WO2022024798 A1 WO 2022024798A1
Authority
WO
WIPO (PCT)
Prior art keywords
polarizing plate
polarizing element
resin
stretching
polarizing
Prior art date
Application number
PCT/JP2021/026726
Other languages
English (en)
Japanese (ja)
Inventor
幸佑 ▲高▼永
卓史 上条
洋 近野
Original Assignee
日東電工株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日東電工株式会社 filed Critical 日東電工株式会社
Priority to KR1020237003211A priority Critical patent/KR20230042028A/ko
Priority to JP2022540177A priority patent/JPWO2022024798A1/ja
Priority to CN202180059184.7A priority patent/CN116158208A/zh
Publication of WO2022024798A1 publication Critical patent/WO2022024798A1/fr

Abstract

L'invention concerne une plaque de polarisation dans laquelle l'apparition d'une fissuration dans une partie déformée est supprimée tout en étant extrêmement mince. Cette plaque de polarisation comprend un polariseur, et une couche de protection disposée sur au moins un côté du polariseur, et a une forme déformée autre qu'une forme rectangulaire. La couche de protection comprend un film de résine ayant une épaisseur de 10 µm ou moins. Le polariseur comprend un film de résine à base de PVA contenant un matériau dichroïque. Dans un mode de réalisation, l'expression (1) est satisfaite lorsque la transmittance unique du polariseur est définie comme x %, et la biréfringence de la résine à base de PVA est définie comme y. Dans un autre mode de réalisation, l'expression (2) est satisfaite lorsque la transmittance unique du polariseur est définie comme x %, et la différence de phase dans le plan du film de résine à base de PVA est définie comme z nm. Dans encore un autre mode de réalisation, l'expression (3) est satisfaite lorsque la transmittance unique du polariseur est définie comme x %, et la fonction d'orientation de la résine à base de PVA est définie comme f. Dans encore un autre mode de réalisation, la résistance au perçage du polariseur est de 30 gf/µm ou plus.　(1) : y < -0,011x+0,525 (2) : z < -60x+2875 (3) : f < -0,018x+1,11
PCT/JP2021/026726 2020-07-29 2021-07-16 Plaque de polarisation, plaque de polarisation avec couche de différence de phase, et dispositif d'affichage d'image utilisant ladite plaque de polarisation ou ladite plaque de polarisation avec couche de différence de phase WO2022024798A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
KR1020237003211A KR20230042028A (ko) 2020-07-29 2021-07-16 편광판, 위상차층 부착 편광판, 및 해당 편광판 또는 해당 위상차층 부착 편광판을 포함하는 화상 표시 장치
JP2022540177A JPWO2022024798A1 (fr) 2020-07-29 2021-07-16
CN202180059184.7A CN116158208A (zh) 2020-07-29 2021-07-16 偏光板、带相位差层的偏光板、以及包含该偏光板或该带相位差层的偏光板的图像显示装置

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2020-127940 2020-07-29
JP2020127940 2020-07-29
JP2020133463 2020-08-06
JP2020-133463 2020-08-06

Publications (1)

Publication Number Publication Date
WO2022024798A1 true WO2022024798A1 (fr) 2022-02-03

Family

ID=80036441

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2021/026726 WO2022024798A1 (fr) 2020-07-29 2021-07-16 Plaque de polarisation, plaque de polarisation avec couche de différence de phase, et dispositif d'affichage d'image utilisant ladite plaque de polarisation ou ladite plaque de polarisation avec couche de différence de phase

Country Status (5)

Country Link
JP (1) JPWO2022024798A1 (fr)
KR (1) KR20230042028A (fr)
CN (1) CN116158208A (fr)
TW (1) TW202208899A (fr)
WO (1) WO2022024798A1 (fr)

Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2006291173A (ja) * 2005-03-16 2006-10-26 Nippon Synthetic Chem Ind Co Ltd:The ポリビニルアルコール系フィルムおよびその製造方法
JP2016071350A (ja) * 2014-09-30 2016-05-09 住友化学株式会社 偏光フィルムの強度測定方法及び偏光板
WO2016093277A1 (fr) * 2014-12-12 2016-06-16 住友化学株式会社 Procédé de production de film polarisant et film polarisant
JP2017003954A (ja) * 2015-06-12 2017-01-05 住友化学株式会社 偏光フィルム及びそれを含む偏光板
WO2017010218A1 (fr) * 2015-07-16 2017-01-19 東海精密工業株式会社 Corps moulé polarisable
JP2017062517A (ja) * 2017-01-12 2017-03-30 日東電工株式会社 位相差層付偏光板および画像表示装置
JP2017182017A (ja) * 2016-03-31 2017-10-05 住友化学株式会社 偏光板、偏光フィルムの製造方法、偏光板の製造方法
JP2017187731A (ja) * 2016-03-30 2017-10-12 住友化学株式会社 延伸フィルムの製造方法及び偏光フィルムの製造方法
WO2018235630A1 (fr) * 2017-06-22 2018-12-27 日東電工株式会社 Stratifié et procédé de production d'un stratifié
WO2019244923A1 (fr) * 2018-06-20 2019-12-26 日東電工株式会社 Film de polarisation, film de polarisation à couche adhésive, et dispositif d'affichage d'image
JP2020101574A (ja) * 2018-12-11 2020-07-02 住友化学株式会社 偏光板

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001343521A (ja) 2000-05-31 2001-12-14 Sumitomo Chem Co Ltd 偏光板及びその製造方法

Patent Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2006291173A (ja) * 2005-03-16 2006-10-26 Nippon Synthetic Chem Ind Co Ltd:The ポリビニルアルコール系フィルムおよびその製造方法
JP2016071350A (ja) * 2014-09-30 2016-05-09 住友化学株式会社 偏光フィルムの強度測定方法及び偏光板
WO2016093277A1 (fr) * 2014-12-12 2016-06-16 住友化学株式会社 Procédé de production de film polarisant et film polarisant
JP2017003954A (ja) * 2015-06-12 2017-01-05 住友化学株式会社 偏光フィルム及びそれを含む偏光板
WO2017010218A1 (fr) * 2015-07-16 2017-01-19 東海精密工業株式会社 Corps moulé polarisable
JP2017187731A (ja) * 2016-03-30 2017-10-12 住友化学株式会社 延伸フィルムの製造方法及び偏光フィルムの製造方法
JP2017182017A (ja) * 2016-03-31 2017-10-05 住友化学株式会社 偏光板、偏光フィルムの製造方法、偏光板の製造方法
JP2017062517A (ja) * 2017-01-12 2017-03-30 日東電工株式会社 位相差層付偏光板および画像表示装置
WO2018235630A1 (fr) * 2017-06-22 2018-12-27 日東電工株式会社 Stratifié et procédé de production d'un stratifié
WO2019244923A1 (fr) * 2018-06-20 2019-12-26 日東電工株式会社 Film de polarisation, film de polarisation à couche adhésive, et dispositif d'affichage d'image
JP2020101574A (ja) * 2018-12-11 2020-07-02 住友化学株式会社 偏光板

Also Published As

Publication number Publication date
CN116158208A (zh) 2023-05-23
TW202208899A (zh) 2022-03-01
JPWO2022024798A1 (fr) 2022-02-03
KR20230042028A (ko) 2023-03-27

Similar Documents

Publication Publication Date Title
JP6890160B2 (ja) 位相差層付偏光板およびそれを用いた画像表示装置
JP6999059B2 (ja) 位相差層付偏光板およびそれを用いた画像表示装置
WO2021095527A1 (fr) Film polarisant, plaque polarisante et dispositif d&#39;affichage d&#39;image
WO2019003503A1 (fr) Film à différence de phase, plaque à polarisation circulaire, et procédé de fabrication d&#39;un film à différence de phase
JP6797499B2 (ja) 位相差層付偏光板およびそれを用いた画像表示装置
TW202041546A (zh) 偏光膜、偏光板及該偏光膜之製造方法
WO2022024798A1 (fr) Plaque de polarisation, plaque de polarisation avec couche de différence de phase, et dispositif d&#39;affichage d&#39;image utilisant ladite plaque de polarisation ou ladite plaque de polarisation avec couche de différence de phase
WO2021261344A1 (fr) Plaque de polarisation équipée d&#39;une couche de retard et dispositif d&#39;affichage d&#39;image l&#39;utilisant
WO2021095526A1 (fr) Film polarisant, plaque polarisante et dispositif d&#39;affichage d&#39;image
WO2021065107A1 (fr) Plaque de polarisation équipée d&#39;une couche de retard et dispositif d&#39;affichage d&#39;image l&#39;utilisant
JP7165805B2 (ja) 偏光膜、偏光板、および該偏光膜の製造方法
JP6890162B2 (ja) 位相差層付偏光板およびそれを用いた画像表示装置
JP6804168B2 (ja) 位相差層付偏光板およびそれを用いた画像表示装置
WO2021261276A1 (fr) Lame polarisante, lame polarisante équipée d&#39;une couche de retard et dispositif d&#39;affichage d&#39;image
JP7165813B2 (ja) 偏光膜、偏光板および該偏光膜の製造方法
WO2022107394A1 (fr) Plaque de polarisation équipée d&#39;une couche à différence de phase et dispositif d&#39;affichage électroluminescent organique l&#39;utilisant
WO2023218821A1 (fr) Procédé de fabrication de film polarisant
WO2023218822A1 (fr) Procédé de fabrication de film polarisant
WO2021261277A1 (fr) Plaque de polarisation équipée d&#39;une couche de retard et dispositif d&#39;affichage d&#39;image l&#39;utilisant
WO2023218820A1 (fr) Procédé de fabrication de film polarisant
WO2022024797A1 (fr) Plaque de polarisation et dispositif d&#39;affichage d&#39;image avec plaque de polarisation
WO2022044604A1 (fr) Film de cellulose triacétyle coloré, plaque de polarisation utilisant ledit film, procédé de production de plaque de polarisation, plaque de polarisation avec couche de retard, dispositif d&#39;affichage d&#39;image et procédé de réglage d&#39;image pour dispositif d&#39;affichage d&#39;image
KR20230152587A (ko) 위상차층 부착 편광판 및 화상 표시 장치
CN110858011A (zh) 相位差膜、带相位差层的偏振片及相位差膜的制造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21851209

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2022540177

Country of ref document: JP

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 20237003211

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 21851209

Country of ref document: EP

Kind code of ref document: A1