WO2022009676A1 - 感光性樹脂組成物及びその樹脂硬化膜 - Google Patents

感光性樹脂組成物及びその樹脂硬化膜 Download PDF

Info

Publication number
WO2022009676A1
WO2022009676A1 PCT/JP2021/023720 JP2021023720W WO2022009676A1 WO 2022009676 A1 WO2022009676 A1 WO 2022009676A1 JP 2021023720 W JP2021023720 W JP 2021023720W WO 2022009676 A1 WO2022009676 A1 WO 2022009676A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin composition
photosensitive resin
copolymer
meth
group
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2021/023720
Other languages
English (en)
French (fr)
Inventor
正偉 周
健宏 木下
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Resonac Holdings Corp
Original Assignee
Showa Denko KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Showa Denko KK filed Critical Showa Denko KK
Priority to CN202180047283.3A priority Critical patent/CN115867867A/zh
Priority to KR1020227044047A priority patent/KR20230013063A/ko
Priority to JP2022535006A priority patent/JPWO2022009676A1/ja
Publication of WO2022009676A1 publication Critical patent/WO2022009676A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

現像性が良好であるとともに、低温硬化性に優れた感光性樹脂組成物、感光性樹脂組成物を硬化させてなる樹脂硬化膜、及び樹脂硬化膜を具備する画像表示素子を提供する。本発明の感光性樹脂組成物は、（Ａ）共重合体と、（Ｂ）光酸発生剤と、（Ｃ）溶剤とを含有する。（Ａ）共重合体が、（Ａ－１）アルコキシシリル基を有する重合性不飽和化合物由来の構成単位（ａ－１）と、（Ａ－２）酸基を有する重合性不飽和化合物由来の構成単位（ａ－２）とを含む共重合体である。（Ａ）共重合体における全構成単位中の前記構成単位（ａ－１）の含有量が、４５～９９モル％である。

Description

感光性樹脂組成物及びその樹脂硬化膜
　本発明は、アルカリ現像可能な感光性樹脂組成物、該感光性樹脂組成物を硬化させてなるオーバーコート、層間絶縁膜、表面保護膜などの樹脂硬化膜に関する。これらの部材は、特にタッチパネル、液晶表示装置、有機ＥＬ装置などの画像表示装置を構成する部材として、好適に用いることができる。
　本願は、２０２０年７月６日に、日本に出願された特願２０２０－１１６５１８号に基づき優先権を主張し、その内容をここに援用する。
　従来より、画像表示装置の部材として用いるオーバーコート、層間絶縁膜、保護膜などを形成するため、光硬化性樹脂組成物が広く使用されている。例えば特許文献１には、特定の構成単位を有する重合体、エポキシ化合物、感放射線性化合物を含有する感放射線性樹脂組成物が開示されている。該感放射線性樹脂組成物は、基板への塗布、プレベーク、露光、現像、ポストベークなどの工程を経て、硬化膜を形成できることが記載されている。
特開２０１７－１０７０２４号公報
　一方、近年では折りたたみスマホやフレキシブルディスプレイの普及に伴い、基板の材質がガラスから樹脂に置き換わってきている。この変化に伴い、特許文献１のように高温でのポストベークを必要とする、従来の感光性樹脂組成物が使用できない問題がある。これは、基板や回路へのダメージを低減し、省エネルギー化する等の観点から、高温域での加熱工程を必要としない感光性樹脂組成物が求められるためである。
　従って、本発明は上記のような課題を解決するためになされた物であり、現像性、低温硬化性に優れ、硬度、透明性、密着性に優れた樹脂硬化膜が得られる感光性樹脂組成物を提供することを目的とする。
　本発明は以下の態様を含む。
［１］　（Ａ）共重合体と、（Ｂ）光酸発生剤と、（Ｃ）溶剤とを含有する感光性樹脂組成物であって、
　前記（Ａ）共重合体が、（Ａ－１）アルコキシシリル基を有する重合性不飽和化合物由来の構成単位（ａ－１）と、（Ａ－２）酸基を有する重合性不飽和化合物由来の構成単位（ａ－２）とを含む共重合体であり、
　前記（Ａ）共重合体における全構成単位中の前記構成単位（ａ－１）の含有量が、４５～９９モル％であることを特徴とする感光性樹脂組成物。
［２］　前記（Ａ）共重合体の酸価が１５～１５０ＫＯＨｍｇ／ｇである［１］に記載の感光性樹脂組成物。
［３］　前記構成単位（ａ－１）が（Ａ－１ａ）アルコキシシリル基含有（メタ）アクリレート由来の構成単位（ａ－１ａ）である［１］又は［２］に記載の感光性樹脂組成物。［４］　前記構成単位（ａ－１ａ）が、下記式（１）で表される［３］に記載の感光性樹脂組成物。
Figure JPOXMLDOC01-appb-C000002
 ［式（１）中、Ｒ１は水素原子又はメチル基を表し、Ｒ２～Ｒ４は各々独立に、水素原子、炭素原子数１～６のアルキル基又は炭素原子数１～６のアルコキシ基を表し、ｎは１～１０の整数である。ただし、Ｒ２～Ｒ４のうち少なくとも１つは炭素原子数１～６のアルコキシ基である。］
［５］　前記構成単位（ａ－２）が有する酸基がカルボキシ基である請求項［１］～［４］のいずれかに記載の感光性樹脂組成物。
［６］　前記（Ｃ）溶剤が、炭素原子数３～１０の第一級アルコール又は第二級アルコールのいずれかを少なくとも含む溶剤である［１］～［５］のいずれかに記載の感光性樹脂組成物。
［７］　前記（Ｂ）光酸発生剤が、スルホニウム塩化合物である［１］～［６］のいずれかに記載の感光性樹脂組成物。
［８］　前記（Ａ）共重合体の重量平均分子量が、２０００～３００００である［１］～［７］のいずれかに記載の感光性樹脂組成物。
［９］　（Ｄ）反応性希釈剤、および（Ｅ）光重合開始剤をさらに含む［１］～［８］のいずれかに記載の感光性樹脂組成物。
［１０］　前記（Ｂ）光酸発生剤の含有量が、前記（Ａ）共重合体１００質量部に対して、０．１～１０質量部である［１］～［９］のいずれかに記載の感光性樹脂組成物。
［１１］　前記（Ａ）共重合体と前記（Ｄ）反応性希釈剤との質量比が、４０：６０～９９：１であり、前記（Ｅ）光重合開始剤の含有量が前記（Ｄ）反応性希釈剤１００質量部に対して０．１～３０質量部である［９］に記載の感光性樹脂組成物。
［１２］　［１］～［１１］のいずれかに記載の感光性樹脂組成物を硬化させてなる樹脂硬化膜。
［１３］　前記樹脂硬化膜が、オーバーコート、保護膜、及び絶縁膜からなる群から選択される一種である［１２］に記載の樹脂硬化膜。
［１４］［１２］に記載の樹脂硬化膜を具備する画像表示装置。
　本発明によれば、現像性が良好であるとともに、低温硬化性に優れた感光性樹脂組成物を提供することができる。また、上記感光性樹脂組成物を硬化させてなる硬度、透明性、密着性に優れた樹脂硬化膜、これを具備する画像表示素子を提供することができる。
　以下、本発明の実施形態について詳細に説明する。ただし、本発明は、以下に示す実施形態に限定されるものではない。なお、本発明において、「（メタ）アクリル酸」は、メタクリル酸及びアクリル酸から選択される少なくとも１種を意味する。「（メタ）アクリレート」についても同様である。
＜感光性樹脂組成物＞
　本実施形態の感光性樹脂組成物は、（Ａ）共重合体と、（Ｂ）光酸発生剤と、（Ｃ）溶剤とを含有するものである。前記感光性樹脂組成物は、必要に応じて、（Ｄ）反応性希釈剤と、（Ｅ）光重合開始剤とをさらに含有する。本実施形態の感光性樹脂組成物は、光照射されることにより重合硬化し、樹脂硬化膜を形成する。
［（Ａ）共重合体］
　本実施形態の（Ａ）共重合体は、（Ａ－１）アルコキシシリル基を有する重合性不飽和化合物由来の構成単位（ａ－１）（以下、単に「構成単位（ａ－１）」とも言う。）と、（Ａ－２）酸基を有する重合性不飽和化合物由来の構成単位（ａ－２）（以下、単に「構成単位（ａ－２）」とも言う。）とを含む。本実施形態の（Ａ）共重合体は、必要に応じて（Ａ－３）その他の重合性不飽和化合物由来の構成単位（ａ－３）（以下、単に「構成単位（ａ－３）」とも言う。）を含んでもよい。
［（Ａ－１）アルコキシシリル基を有する重合性不飽和化合物由来の構成単位（ａ－１）］
　本実施形態の（Ａ）共重合体に含まれる、（Ａ－１）アルコキシシリル基を有する重合性不飽和化合物由来の構成単位（ａ－１）について、（Ａ－１）アルコキシシリル基を有する重合性不飽和化合物は、アルコキシシリル基とエチレン性不飽和基を有するモノマーであれば特に限定されない。アルコキシシリル基のアルコキシ基は、炭素数１～６であることが好ましく、炭素数１～４であることがより好ましく、炭素数１～２であることがさらに好ましい。アルコキシシリル基におけるアルコキシ基の数が１以上であればよいが、３つであるトリアルコキシシリル基は架橋点が多くて硬化性がより良い面でより好ましい。
　構成単位（ａ－１）は、（Ａ）共重合体を合成する際の反応容易性や原料の入手容易性の観点から、（Ａ－１a）アルコキシシリル基含有（メタ）アクリレート由来の構成単位（ａ－１a）であることが好ましく、下記式（１）で表される構成単位であることがより好ましい。
Figure JPOXMLDOC01-appb-C000003
 ［式（１）中、Ｒ１は水素原子又はメチル基を表し、Ｒ２～Ｒ４は各々独立に、水素原子、炭素原子数１～６のアルキル基又は炭素原子数１～６のアルコキシ基を表し、ｎは１～１０の整数である。ただし、Ｒ２～Ｒ４のうち少なくとも１つは炭素原子数１～６のアルコキシ基である。］
　式（１）中、Ｒ１は水素原子またはメチル基を表し、メチル基が好ましい。
　式（１）中、Ｒ２～Ｒ４が示す炭素原子数１～６のアルキル基は、炭素原子数１～４が好ましく、炭素原子数１～２がより好ましい。Ｒ２～Ｒ４が示す炭素原子数１～６のアルコキシ基は、炭素数１～４であることが好ましく、炭素数１～２であることがより好ましい。Ｒ２～Ｒ４は各々独立に、炭素原子数１～６のアルキル基又は炭素原子数１～６のアルコキシ基であることが好ましく、Ｒ２～Ｒ４のうち２つが炭素原子数１～６のアルコキシ基であることがより好ましく、Ｒ２～Ｒ４のうち３つ全てが炭素原子数１～６のアルコキシ基であることがさらに好ましい。具体例としては、Ｒ２～Ｒ４は各々独立に、メチル基、エチル基、メトキシ基、又はエトキシ基が好ましく、Ｒ２～Ｒ４のうち少なくとも１つはメトキシ基又はエトキシ基であることがより好ましい。ｎは１～１０の整数であり、１～４であることが最も好ましい。
　上記式（１）で表される構成単位の具体例としては、例えば、
３－（メタ）アクリロイルオキシプロピルメチルジメトキシシラン（式（１）中、Ｒ１：水素原子又はメチル基；Ｒ２：メチル基；Ｒ３、Ｒ４：メトキシ基；ｎ：３）、
３－（メタ）アクリロイルオキシプロピルエチルジメトキシシラン（式（１）中、Ｒ１：水素原子又はメチル基；Ｒ２：エチル基；Ｒ３、Ｒ４：メトキシ基；ｎ：３）、
３－（メタ）アクリロイルオキシプロピルメチルジエトキシシラン（式（１）中、Ｒ１：水素原子又はメチル基；Ｒ２：メチル基；Ｒ３、Ｒ４：エトキシ基；ｎ：３）、
３－（メタ）アクリロイルオキシプロピルエチルジエトキシシラン（式（１）中、Ｒ１：水素原子又はメチル基；Ｒ２：エチル基；Ｒ３、Ｒ４：エトキシ基；ｎ：３）、
３－（メタ）アクリロイルオキシプロピルトリメトキシシラン（式（１）中、Ｒ１：水素原子又はメチル基；Ｒ２～Ｒ４：メトキシ基；ｎ：３）、
３－（メタ）アクリロイルオキシプロピルトリエトキシシラン（式（１）中、Ｒ１：水素原子又はメチル基；Ｒ２～Ｒ４：エトキシ基；ｎ：３）
等の化合物由来の構成単位が挙げられる。これらの中でも、材料入手のし易さ及び（Ａ）共重合体を合成する際の反応性の観点から、３－（メタ）アクリロイルオキシプロピルトリメトキシシラン及び３－（メタ）アクリロイルオキシプロピルトリエトキシシラン由来の構成単位が好ましい。
　本実施形態の（Ａ）共重合体を構成する全構成単位中の構成単位（ａ－１）の含有量は、４５モル％以上であり、５０モル%以上であることが好ましく、６０モル％以上であることがより好ましく、７３モル％以上であることがさらに好ましい。構成単位（ａ－１）の含有量が４５モル％未満であると、感光性樹脂組成物の保存安定性や現像性能が不十分であったり、樹脂硬化膜の硬度が不足することが懸念される。また構成単位（ａ－１）の含有量は、９９モル%以下であり、９０モル％以下であることが好ましく、８５モル％以下であることがより好ましい。構成単位（ａ－１）の含有量が９９モル％より大きいと、感光性樹脂組成物の現像性や塗膜の平坦性が劣ることが懸念される。
［（Ａ－２）酸基を有する重合性不飽和化合物由来の構成単位（ａ－２）］
　本実施形態の（Ａ）共重合体に含まれる、（Ａ－２）酸基を有する重合性不飽和化合物由来の構成単位（ａ－２）について、（Ａ－２）酸基を有する重合性不飽和化合物は、酸基とエチレン性不飽和基を有し、ケイ素を含まない化合物であれば特に限定されない。構成単位（ａ－２）が有する酸基は、特に限定されないが、通常、カルボキシ基、リン酸基（－Ｏ－Ｐ(＝Ｏ)(ＯＨ)２）、スルホン酸基（－Ｓ（＝Ｏ）２ＯＨ）等が好ましい。これらの中でも、感光性樹脂組成物としての現像性の観点から、カルボキシ基がより好ましい。
　構成単位（ａ－２）の具体例としては、例えば、（メタ）アクリル酸、クロトン酸、桂皮酸、ビニルスルホン酸、２－（メタ）アクリロイルオキシエチルコハク酸、２－アクリロイルオキシエチルフタル酸、２－（メタ）アクリロイルオキシエチルヘキサヒドロフタル酸、２－（メタ）アクリロイルオキシエチルアシッドホスフェート等に由来する構成単位が挙げられる。これらの中でも、入手のし易さ及び（Ａ）共重合体を合成する際の反応性の観点から、（メタ）アクリル酸由来の構成単位が好ましい。
　本実施形態の（Ａ）共重合体を構成する全構成単位中の構成単位（ａ－２）の含有量は、１～５５モル％であることが好ましく、１５～４０モル％であることがより好ましく、１５～３０モル％であることがさらに好ましい。構成単位（ａ－２）の含有量が１モル％以上であると、感光性樹脂組成物としての現像性が良好である。構成単位（ａ－２）の含有量が５５モル％以下であると、構成単位（ａ－１）の含有量が十分に多くなり、樹脂硬化膜として良好な硬度が得られる。
［（Ａ－３）その他の重合性不飽和化合物由来の構成単位（ａ－３）］
　本実施形態の（Ａ）共重合体は、構成単位（ａ－１）および構成単位（ａ－２）に加えて、（Ａ－３）その他の重合性不飽和化合物由来の構成単位（ａ－３）を有していてもよい。（Ａ－３）その他の重合性不飽和化合物は、（Ａ－１）アルコキシシリル基を有する重合性不飽和化合物や（Ａ－２）酸基を有する重合性不飽和化合物以外の酸基やアルコキシシリル基を有さない重合性不飽和化合物である。（Ａ－３）化合物の例は、ブタジエン等のジエン類、（メタ）アクリル酸エステル類、（メタ）アクリル酸アミド類、ビニル化合物類、スチレン類、不飽和ジカルボン酸ジエステル、不飽和多塩基酸無水物を含む。
　（メタ）アクリル酸エステル類の具体例は、メチル（メタ）アクリレート、エチル（メタ）アクリレート、ｎ－プロピル（メタ）アクリレート、イソプロピル（メタ）アクリレート、ｎ－ブチル（メタ）アクリルレート、ｓｅｃ－ブチル（メタ）アクリレート、イソブチル（メタ）アクリレート、ｔｅｒｔ－ブチル（メタ）アクリルレート、ペンチル（メタ）アクリレート、ネオペンチル（メタ）アクリレート、ベンジル（メタ）アクリレート、イソアミル（メタ）アクリレート、ヘキシル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート、ベンジル（メタ）アクリレート、ラウリル（メタ）アクリレート、ドデシル（メタ）アクリレート、シクロペンチル（メタ）アクリレート、シクロヘキシル（メタ）アクリレート、メチルシクロヘキシル（メタ）アクリレート、エチルシクロヘキシル（メタ）アクリレート、１，４－シクロヘキサンジメタノールモノ（メタ）アクリレート、ロジン（メタ）アクリレート、ノルボルニル（メタ）アクリレート、５－メチルノルボルニル（メタ）アクリレート、５－エチルノルボルニル（メタ）アクリレート、アリル（メタ）アクリレート、テトラヒドロフルフリル（メタ）アクリレート、１，１，１－トリフルオロエチル（メタ）アクリレート、パーフルオロエチル（メタ）アクリレート、パーフルオロ－ｎ－プロピル（メタ）アクリレート、パーフルオロ－イソプロピル（メタ）アクリレート、トリフェニルメチル（メタ）アクリレート、クミル（メタ）アクリレート、３－（Ｎ，Ｎ－ジメチルアミノ）プロピル（メタ）アクリレート、グリセリロールモノ（メタ）アクリレート、ブタントリオールモノ（メタ）アクリレート、ペンタントリオールモノ（メタ）アクリレート、ジシクロペンテニル（メタ）アクリレート、ジシクロペンタニル（メタ）アクリレート、イソボルニル（メタ）アクリレート、アダマンチル（メタ）アクリレート、ナフタレン（メタ）アクリレート、アントラセン（メタ）アクリレート、２－（２－ビニロキシエトキシ）エチル（メタ）アクリレート、グリシジル（メタ）アクリレート、３，４－エポキシシクロヘキシルメチル（メタ）アクリレート、（３－エチルオキセタン－３－イル）メチル（メタ）アクリレート、イソシアナト基を有するエチレン性不飽和化合物、前記のイソシアナト基を有するエチレン性不飽和化合物のイソシアナト基を、ブロック剤を用いてブロック化したブロックイソシアナト基を有する化合物、Ｎ，Ｎ－ジメチルアミノエチル（メタ）アクリレート、Ｎ，Ｎ－ジエチルアミノエチル（メタ）アクリレート、Ｎ－ｔｅｒｔ－ブチルアミノエチル（メタ）アクリレート、テトラメチルピペリジル（メタ）アクリレート、ヘキサメチルピペリジル（メタ）アクリレート等を含む。前記のイソシアナト基を有するエチレン性不飽和化合物としては、例えば、２－イソシアナトエチル（メタ）アクリレート、２－イソシアナトプロピル（メタ）アクリレート、３－イソシアナトプロピル（メタ）アクリレート、２－イソシアナト－１－メチルエチル（メタ）アクリレート、２－イソシアナト－１，１－ジメチルエチル（メタ）アクリレート、４－イソシアナトシクロヘキシル（メタ）アクリレートが挙げられる。
　（メタ）アクリル酸アミド類の具体例は、（メタ）アクリル酸アミド、（メタ）アクリル酸Ｎ，Ｎ－ジメチルアミド、（メタ）アクリル酸Ｎ，Ｎ－ジエチルアミド、（メタ）アクリル酸Ｎ，Ｎ－ジプロピルアミド、（メタ）アクリル酸Ｎ，Ｎ－ジ－イソプロピルアミド、（メタ）アクリル酸アントラセニルアミド、Ｎ－イソプロピル（メタ）アクリルアミド、（メタ）アクリルモルフォリン、ダイアセトン（メタ）アクリルアミド等を含む。　ビニル化合物の具体例は、ノルボルネン（ビシクロ［２．２．１］ヘプト－２－エン）、５－メチルビシクロ［２．２．１］ヘプト－２－エン、５－エチルビシクロ［２．２．１］ヘプト－２－エン、テトラシクロ［４．４．０．１２，５．１７，１０］ドデカ－３－エン、８－メチルテトラシクロ［４．４．０．１２，５．１７，１０］ドデカ－３－エン、８－エチルテトラシクロ［４．４．０．１２，５．１７，１０］ドデカ－３－エン、ジシクロペンタジエン、トリシクロ［５．２．１．０２，６］デカ－８－エン、トリシクロ［５．２．１．０２，６］デカ－３－エン、トリシクロ［４．４．０．１２，５］ウンデカ－３－エン、トリシクロ［６．２．１．０１，８］ウンデカ－９－エン、トリシクロ［６．２．１．０１，８］ウンデカ－４－エン、テトラシクロ［４．４．０．１２，５．１７，１０．０１，６］ドデカ－３－エン、８－メチルテトラシクロ［４．４．０．１２，５．１７，１０．０１，６］ドデカ－３－エン、８－エチリデンテトラシクロ［４．４．０．１２，５．１７，１２］ドデカ－３－エン、８－エチリデンテトラシクロ［４．４．０．１２，５．１７，１０．０１，６］ドデカ－３－エン、ペンタシクロ［６．５．１．１３，６．０２，７．０９，１３］ペンタデカ－４－エン、ペンタシクロ［７．４．０．１２，５．１９，１２．０８，１３］ペンタデカ－３－エン、５－ノルボルネン－２，３－ジカルボン酸無水物、（メタ）アクリル酸アニリド、（メタ）アクリロイルニトリル、アクロレイン、塩化ビニル、塩化ビニリデン、フッ化ビニル、フッ化ビニリデン、ビニルピリジン、酢酸ビニル、ビニルトルエン等を含む。
　スチレン頼の具体例は、スチレン、スチレンのα－、ｏ－、ｍ－、ｐ－アルキル、ニトロ、シアノ、アミド誘導体を含む。
　不飽和ジカルボン酸ジエステルの具体例は、シトラコン酸ジエチル、マレイン酸ジエチル、フマル酸ジエチル、イタコン酸ジエチル等を含む。
　不飽和多塩基酸無水物の具体例は、無水マレイン酸、無水イタコン酸、無水シトラコン酸等を含む。
　これらの（Ａ－３）化合物は、１種を単独で用いてもよく、２種以上を組み合わせて用いてもよい。
　これらの中でも、入手のし易さ及び反応性の観点から、メチル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート、ベンジル（メタ）アクリレート、ジシクロペンタニル（メタ）アクリレート、グリシジル（メタ）アクリレート、（３－エチルオキセタン－３－イル）メチル（メタ）アクリレート、Ｎ，Ｎ－ジエチルアミノエチル（メタ）アクリレート、（メタ）アクリル酸Ｎ，Ｎ－ジメチルアミド、（メタ）アクリルモルフォリン、スチレン、ビニルトルエン及びノルボルネンが好ましい。メチル（メタ）アクリレート、ベンジル（メタ）アクリレート、ジシクロペンタニル（メタ）アクリレート、グリシジル（メタ）アクリレート、（３－エチルオキセタン－３－イル）メチル（メタ）アクリレート、スチレン及びビニルトルエンがより好ましい。
　これらの中でも耐熱分解性及び耐熱黄変性の観点から、アルキル（メタ）アクリレートが好ましく、メチル（メタ）アクリレート、ベンジル（メタ）アクリレート、ジシクロペンタニル（メタ）アクリレートがより好ましい。また、耐溶剤性向上の観点から、酸基と反応する官能基を有する重合性化合物が好ましく、具体的にはグリシジル基、オキセタニル基、イソシアナト基、又はブロックイソシアナト基を有する重合性化合物が挙げられる。より好ましくは、入手のし易さ及び反応性の観点から、グリシジル（メタ）アクリレート、（３－エチルオキセタン－３－イル）メチルメタクリレートなどが挙げられる。
　上記したブロック剤の例は、ε－カプロラクタム、δ－バレロラクタム、γ－ブチロラクタム、β－プロピオラクタム等のラクタム系；メタノール、エタノール、プロパノール、ブタノール、エチレングリコール、メチルセロソルブ、ブチルセロソルブ、メチルカルビトール、ベンジルアルコール、フェニルセロソルブ、フルフリルアルコール、シクロヘキサノール等のアルコール系；フェノール、クレゾール、キシレノール、エチルフェノール、ｏ－イソプロピルフェノール、ｐ－ｔｅｒｔ－ブチルフェノール等のブチルフェノール、ｐ－ｔｅｒｔ－オクチルフェノール、ノニルフェノール、ジノニルフェノール、スチレン化フェノール、オキシ安息香酸エステル、チモール、ｐ－ナフトール、ｐ－ニトロフェノール、ｐ－クロロフェノール等のフェノール系；マロン酸ジメチル、マロン酸ジエチル、アセト酢酸メチル、アセト酢酸エチル、アセチルアセトン等の活性メチレン系；ブチルメルカプタン、チオフェノール、ｔｅｒｔ－ドデシルメルカプタン等のメルカプタン系；ジフェニルアミン、フェニルナフチルアミン、アニリン、カルバゾール等のアミン系；アセトアニリド、アセトアニシジド、酢酸アミド、ベンズアミド等の酸アミド系；コハク酸イミド、マレイン酸イミド等の酸イミド系；イミダゾール、２－メチルイミダゾール、２－エチルイミダゾール等のイミダゾール系；尿素、チオ尿素、エチレン尿素等の尿素系；Ｎ－フェニルカルバミン酸フェニル、２－オキサゾリドン等のカルバミド酸塩系；エチレンイミン、ポリエチレンイミン等のイミン系；ホルムアルドオキシム、アセトアルドオキシム、アセトオキシム、メチルエチルケトオキシム、メチルイソブチルケトオキシム、シクロヘキサノンオキシム等のオキシム系；重亜硫酸ソーダ、重亜硫酸カリウム等の重亜硫酸塩系等を含む。
　本実施形態の（Ａ）共重合体が構成単位（ａ－３）を有する場合、全構成単位中の構成単位（ａ－３）の含有量は、０．１～４０モル％であることが好ましく、１～３０モル％であることがより好ましく、５～２０モル％であることがさらに好ましい。構成単位（ａ－３）の含有量が０．１モル％以上であると、感光性樹脂組成物に対して、構成単位（ａ－３）に起因する機能を十分に付与することができる。構成単位（ａ－３）の含有量が４０モル％以下であると、構成単位（ａ－１）および構成単位（ａ－２）の含有量が十分に多くなるため、感光性樹脂組成物として良好な現像性を有し、硬度や密着性に優れた樹脂硬化膜が得られる。
　本実施形態の（Ａ）共重合体の重量平均分子量（Ｍｗ）は、ポリスチレン換算で、２０００～３００００であることが好ましく、３０００～１００００であることがより好ましく、３０００～６０００であることがさらに好ましい。（Ａ）共重合体の重量平均分子量（Ｍｗ）が２０００以上であると、現像性が良好である。（Ａ）共重合体の重量平均分子量（Ｍｗ）が３００００以下であると、現像時間を適切な範囲に調整できる。
　本実施形態の（Ａ）共重合体の重量平均分子量（Ｍｗ）の値は、ゲル・パーミエーション・クロマトグラフィー（ＧＰＣ）を用いて、下記条件にて測定し、ポリスチレン換算にて算出されるものである。
　カラム：ショウデックス（登録商標）ＬＦ－８０４＋ＬＦ－８０４（昭和電工株式会社製）
　カラム温度：４０℃
　試料：（Ａ）共重合体の含有量が０．２質量％のテトラヒドロフラン溶液
　展開溶媒：テトラヒドロフラン
　検出器：示差屈折計（商品名：ショウデックス（登録商標）ＲＩ－７１Ｓ、昭和電工株式会社製）
　流速：１ｍＬ／ｍｉｎ
　本実施形態の（Ａ）共重合体の分子量分布（Ｍｗ／Ｍｎ）は、１．３～３．０であることが好ましく、１．５～２．５であることがより好ましく、１．５～２．０であることがさらに好ましい。（Ａ）共重合体の分子量分布（Ｍｗ／Ｍｎ）が１．３以上であると、重量平均分子量や酸価など、目標数値範囲の最適化や（Ａ）共重合体を製造する際の反応条件等を一定の幅をもって設定することができ、効率的である。（Ａ）共重合体の分子量分布（Ｍｗ／Ｍｎ）が３．０未満であると、現像性など感光性樹脂組成物としての性能にばらつきが生じることもない。分子量分布は、上記ＧＰＣ測定のクロマトグラムから測定する。
　本実施形態の（Ａ）共重合体の酸価は、特に限定されないが、好ましくは１５ＫＯＨｍｇ／ｇ～１５０ＫＯＨｍｇ／ｇ、より好ましくは２５ＫＯＨｍｇ／ｇ～１００ＫＯＨｍｇ／ｇ、さらに好ましくは３０ＫＯＨｍｇ／ｇ～７０ＫＯＨｍｇ／ｇである。（Ａ）共重合体の酸価が１５ＫＯＨｍｇ／ｇ以上であれば、より良好な現像性が得られる。一方、（Ａ）共重合体の酸価が１５０ＫＯＨｍｇ／ｇ以下であれば、アルカリ現像液に対して露光部分（光硬化部分）が溶解することなく良好な現像性が得られる。
　なお、（Ａ）共重合体の酸価とは、ＪＩＳ　Ｋ６９０１　５．３に従ってブロモチモールブルーとフェノールレッドの混合指示薬を用いて測定された値であって、（Ａ）共重合体１ｇ中に含まれる酸性成分を中和するのに要する水酸化カリウムのｍｇ数を意味する。
　本実施形態の（Ａ）共重合体のシリル基当量は、特に限定されないが、好ましくは２９０ｇ／ｍｏｌ～４５０ｇ／ｍｏｌ、より好ましくは３００ｇ／ｍｏｌ～４２０ｇ／ｍｏｌ、最も好ましくは３００ｇ／ｍｏｌ～４００ｇ／ｍｏｌである。（Ａ）共重合体のシリル基当量が２９０ｇ／ｍｏｌ以上であれば、硬度及び現像性をより高めるのに効果的である。一方、（Ａ）共重合体のシリル基当量が４５０ｇ／ｍｏｌ以下であれば、樹脂硬化膜として十分な硬度を確保できる。
　なお、（Ａ）共重合体のシリル基当量は、（Ａ）共重合体の分子量を１分子当たりのシリル基の平均個数で割った値であり、（Ａ）共重合体を合成する際の（Ａ－１）アルコキシシリル基を有する重合性不飽和化合物の仕込み量に基づいて算出される計算値とする。
［（Ｂ）光酸発生剤］
　本実施形態の（Ｂ）光酸発生剤としては、光照射によって分解し、酸を発生するものであれば特に限定されないが、波長１９０～５００ｎｍの光を照射することによって酸を発生するものが好ましい。中でも入手が容易で、感光性樹脂組成物としての保存安定性が良好である点から、スルホニウム塩化合物またはヨードニウム塩化合物が好ましく、芳香族スルホニウム塩化合物または芳香族ヨードニウム塩化合物がより好ましく、芳香族スルホニウム塩化合物がさらに好ましく、トリアリールスルホニウム塩化合物が特に好ましい。　本実施形態の（Ｂ）光酸発生剤が有するアニオン種としては、特に限定されないが、ボレートアニオンやリン系アニオンが好ましく、感光性樹脂組成物としての低温硬化性の観点から、ボレートアニオンが特に好ましい。ボレートアニオンとしては、ＢＦ４ －、（Ｃ６Ｆ５）４Ｂ－、（Ｃ６Ｈ５）（Ｃ６Ｆ５）３Ｂ－、（（ＣＦ３）２Ｃ６Ｈ３）４Ｂ－等が挙げられる。中でもフルオロアルキル基含有ボレートアニオンが好ましい。リン系アニオンとしては、ＰＦ６ －、（ＣＦ３ＣＦ２）３ＰＦ３ －、（ＣＦ３ＣＦ２ＣＦ２ＣＦ２）３ＰＦ３ －等が挙げられる。中でもフルオロアルキル基含有リン系アニオンが好ましい。
　前記（Ｂ）光酸発生剤の具体例としては、特開２０１２－２７２９０号公報、特開２０１１－２０１８０３号公報、特開２０１１－１９５４９９号公報等に開示の光酸発生剤；サンアプロ（株）化学社製の商品名ＣＰＩ－２００Ｋ、ＣＰＩ－２１０Ｓ、ＣＰＩ－３１０Ｂ、ＣＰＩ－４１０Ｓ等のスルホニウム塩化合物；ＩＫ－１等のヨードニウム塩化合物等が挙げられる。中でも、感光性樹脂組成物としての低温硬化性が良好であり、樹脂硬化膜としての硬度や透過率が優れる点からＣＰＩ－２１０Ｓ、ＣＰＩ－３１０Ｂが好ましい。これらの（Ｂ）光酸発生剤は、単独で用いてもよく、２種以上を組み合わせて用いてもよい。
　前記（Ｂ）光酸発生剤の含有量は、生成する酸の発生量、発生速度に応じて調整が必要である。例えば（Ａ）共重合体１００質量部に対して、０．１～１０質量部であることが好ましく、０．１～５質量部であることがより好ましく、０．３～３質量部であることがさらに好ましい。（Ｂ）光酸発生剤の含有量が、０．１質量部以上であると、発生する酸の量が十分であり、硬化膜として十分な硬度が得られる。含有量が１０質量部以下であると、樹脂硬化膜の外観が良好であり、（Ｂ）光酸発生剤の添加に起因する着色も発生しない。
［（Ｃ）溶剤］
　本実施形態の（Ｃ）溶剤は、感光性樹脂組成物の各成分に対し不活性で、各成分を溶解可能な溶剤であれば特に限定されない。（Ａ）共重合体の合成の際に、（Ｃ）溶剤と同様の溶剤を用いて合成し、この溶媒を分離、除去することなくそのまま感光性樹脂組成物の（Ｃ）溶剤として用いてもよいし、感光性樹脂組成物の各成分を混合する際に新たに追加してもよい。感光性樹脂組成物の各成分を混合する際にそれらの成分と共存する溶剤であってもよい。中でも、感光性樹脂組成物としての保存安定性の観点から、炭素原子数３～１０の第一級アルコール又は第二級アルコールのいずれかを少なくとも含むことが好ましく、炭素原子数３～１０の第一級アルコールを含むことがより好ましい。炭素原子数３～１０の第一級アルコール又は第二級アルコール溶剤の具体例としては、例えば、モノアルコール類、（ポリ）アルキレングリコールモノアルキルエーテル類等が挙げられる。
　モノアルコール類の具体例は、プロピルアルコール、ブチルアルコール、ペンチルアルコール、ヘキシルアルコール、オクチルアルコール、ノニルアルコール、デシルアルコール、ドデシルアルコール、ベンジルアルコール等を含む。
　（ポリ）アルキレングリコールモノアルキルエーテル類の具体例は、エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノ－ｎ－プロピルエーテル、ジエチレングリコールモノ－ｎ－ブチルエーテル、トリエチレングリコールモノメチルエーテル、トリエチレングリコールモノエチルエーテル、プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル、ジプロピレングリコールモノメチルエーテル、ジプロピレングリコールモノエチルエーテル、ジプロピレングリコールモノ－ｎ－プロピルエーテル、ジプロピレングリコールモノ－ｎ－ブチルエーテル、トリプロピレングリコールモノメチルエーテル、トリプロピレングリコールモノエチルエーテル、３－メトキシ－１－ブタノール等を含む。
　これらの中でも、入手のし易さおよび感光性樹脂組成物としての保存安定性の観点から、（ポリ）アルキレングリコールモノアルキルエーテル類が好ましい。これらの溶剤は、１種を単独で用いてもよいし、２種以上を組み合わせて用いてもよい。
　本実施形態の（Ｃ）溶剤は、上記記載の溶剤の以外に、その他の溶剤を含んでもよい。その他の溶剤の具体例は、ｔｅｒｔ－ブチルアルコール、ダイアセトンアルコール等の第三級アルコール類；エチレングリコールモノメチルエーテルアセテート、エチレングリコールモノエチルエーテルアセテート、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート等の（ポリ）アルキレングリコールモノアルキルエーテルアセテート類；ジエチレングリコールジメチルエーテル、ジエチレングリコールメチルエチルエーテル、ジエチレングリコールジエチルエーテル、テトラヒドロフラン等の他のエーテル類；メチルエチルケトン、シクロヘキサノン、２－ヘプタノン、３－ヘプタノン等のケトン類；２－ヒドロキシプロピオン酸メチル、２－ヒドロキシプロピオン酸エチル、２－ヒドロキシ－２－メチルプロピオン酸メチル、２－ヒドロキシ－２－メチルプロピオン酸エチル、３－メトキシプロピオン酸メチル、３－メトキシプロピオン酸エチル、３－エトキシプロピオン酸メチル、３－エトキシプロピオン酸エチル、エトキシ酢酸エチル、ヒドロキシ酢酸エチル、２－ヒドロキシ－３－メチル酪酸メチル、３－メチル－３－メトキシブチルアセテート、３－メチル－３－メトキシブチルプロピオネート、酢酸エチル、酢酸ｎ－ブチル、酢酸ｎ－プロピル、酢酸ｉ－プロピル、酢酸ｎ－ブチル、酢酸ｉ－ブチル、酢酸ｎ－アミル、酢酸ｉ－アミル、プロピオン酸ｎ－ブチル、酪酸エチル、酪酸ｎ－プロピル、酪酸ｉ－プロピル、酪酸ｎ－ブチル、ピルビン酸メチル、ピルビン酸エチル、ピルビン酸ｎ－プロピル、アセト酢酸メチル、アセト酢酸エチル、２－オキソ酪酸エチル等のエステル類；トルエン、キシレン等の芳香族炭化水素類；Ｎ－メチルピロリドン、Ｎ，Ｎ－ジメチルホルムアミド、Ｎ，Ｎ－ジメチルアセトアミド等のカルボン酸アミド類等を含む。これらの中でも、炭素原子数３～１０の第一級アルコール又は第二級アルコールとの相溶性や感光性樹脂組成物の各成分の溶解性の観点から、プロピレングリコールモノメチルエーテルアセテート等の（ポリ）アルキレングリコールモノアルキルエーテルアセテート系溶剤が好ましい。
　（Ｃ）溶剤の含有量は、感光性樹脂組成物の（Ｃ）溶剤を除く成分の総和を１００質量部としたときに、好ましくは３０質量部～１０００質量部、より好ましくは５０質量部～８００質量部、最も好ましくは１００質量部～５００質量部である。（Ｃ）溶剤の配合量が、上記範囲内であると、感光性樹脂組成物の粘度を適切な範囲に調整することができる。
［（Ｄ）反応性希釈剤］
　本実施形態の感光性樹脂組成物は必要に応じて（Ｄ）反応性希釈剤を配合してもよい。（Ｄ）反応性希釈剤としては、ビニル基、アリル基、（メタ）アクリロイルオキシ基等のエチレン性不飽和基を有する低分子量化合物であれば特に限定されない。（Ｄ）反応性希釈剤の具体例は、芳香族ビニル系モノマー類；酢酸ビニル、アジピン酸ビニル等のポリカルボン酸モノマー類；（メタ）アクリレート類；多官能（メタ）アクリレート類；トリアリルシアヌレート等を含む。
　芳香族ビニル系モノマー類の具体例は、スチレン、α－メチルスチレン、α－クロロメチルスチレン、ビニルトルエン、ジビニルベンゼン、ジアリルフタレート、ジアリルベンゼンホスホネート等を含む。
　（メタ）アクリレート類の具体例は、メチル（メタ）アクリレート、エチル（メタ）アクリレート、プロピル（メタ）アクリレート、ブチル（メタ）アクリレート、β－ヒドロキシエチル（メタ）アクリレート、ヒドロキシプロピル（メタ）アクリレート等を含む。　多官能（メタ）アクリレート類の具体例は、エチレングリコールジ（メタ）アクリレート、ジエチレングリコールジ（メタ）アクリレート、プロピレングリコールジ（メタ）アクリレート、エチレングリコールジ（メタ）アクリレート、トリメチロールプロパンジ（メタ）アクリレート、トリメチロールプロパントリ（メタ）アクリレート、ペンタエリスリトールテトラ（メタ）アクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレート、トリス（ヒドロキシエチル）イソシアヌレートのトリ（メタ）アクリレート等を含む。これらの中でも、多官能（メタ）アクリレート類が特に好ましい。これらの（Ｄ）反応性希釈剤は、１種を単独で用いてもよいし、２種以上を組み合わせて用いてもよい。
　（Ｄ）反応性希釈剤の配合量は、（Ａ）共重合体と（Ｄ）反応性希釈剤との質量比が、４０：６０～９９：１となるように配合することが好ましく、５０：５０～９５：５がより好ましく、６０：４０～９０：１０がさらに好ましい。（Ｄ）反応性希釈剤の配合量が上記範囲内であると、感光性樹脂組成物としての粘度および光硬化性を適切に調整することができる。
［（Ｅ）光重合開始剤］
　本実施形態の感光性樹脂組成物が（Ｄ）反応性希釈剤を含有する場合には、併せて（Ｅ）光重合開始剤を用いる。（Ｅ）光重合開始剤としては、光照射によりラジカルを発生する化合物であれば特に限定されないが、例えば、ベンゾイン、ベンゾインメチルエーテル、ベンゾインエチルエーテル等のベンゾインとそのアルキルエーテル類；アセトフェノン、２，２－ジメトキシ－２－フェニルアセトフェノン、１，１－ジクロロアセトフェノン、４－（１－ｔ－ブチルジオキシ－１－メチルエチル）アセトフェノン等のアセトフェノン類；１－ヒドロキシシクロヘキシルフェニルケトン、２－ヒドロキシ－２－メチル－１－フェニルプロパン－１－オン等のアルキルフェノン類；２－メチルアントラキノン、２－アミルアントラキノン、２－ｔ－ブチルアントラキノン、１－クロロアントラキノン等のアントラキノン類；２，４－ジメチルチオキサントン、２，４－ジイソプロピルチオキサントン、２－クロロチオキサントン等のチオキサントン類；アセトフェノンジメチルケタール、ベンジルジメチルケタール等のケタール類；ベンゾフェノン、４－（１－ｔ－ブチルジオキシ－１－メチルエチル）ベンゾフェノン、３，３’，４，４’－テトラキス（ｔ－ブチルジオキシカルボニル）ベンゾフェノン等のベンゾフェノン類；１，２－オクタンジオン，１－［４－（フェニルチオ）－２－（ｏ－ベンゾイルオキシム）］、エタノン，１－［９－エチル－６－（２－メチルベンゾイル）－９Ｈ－カルバゾール－３－イル］，１－（ｏ－アセチルオキシム）等のオキシムエステル類；２－メチル－１－［４－（メチルチオ）フェニル］－２－モルホリノ－プロパン－１－オン；２－ベンジル－２－ジメチルアミノ－１－（４－モルホリノフェニル）ブタノン－１；２，４，６－トリメチルベンゾイルジフェニルホスフィンオキサイド、ビス（２，４，６－トリメチルベンゾイル）フェニルホスフィンオキサイド等のアシルホスフィンオキサイド類；キサントン類等が挙げられる。これらの（Ｅ）光重合開始剤は、１種を単独で用いてもよいし、２種以上を組み合わせて用いてもよい。
　（Ｅ）光重合開始剤の含有量は、（Ｄ）反応性希釈剤１００質量部に対して、０．１～３０質量部であることが好ましく、０．５～２０質量部であることがより好ましく、１～１５質量部であることがさらに好ましい。（Ｅ）光重合開始剤の含有量が０．１質量部以上であると、感光性樹脂組成物が十分な光硬化性を有する。含有量が３０質量部以下であると、感光性樹脂組成物の保存安定性や樹脂硬化膜の性能に悪影響を及ぼすことがない。
　本実施形態の感光性樹脂組成物には、上記の成分に加えて、所定の特性を付与するために、公知のレベリング剤、熱重合禁止剤等の公知の添加剤を配合してもよい。感光性樹脂組成物におけるこれらの添加剤の配合量は、本発明の効果を阻害しない範囲であれば特に限定されない。
　本実施形態の感光性樹脂組成物の粘度は、目的とする樹脂硬化膜の厚さに応じて適宜調整することができる。例えば、樹脂硬化膜の厚さを１～４μmに調整する場合、感光性樹脂組成物の粘度は、４～２５ｍＰ・ｓが好ましく、６～２０ｍＰ・ｓがより好ましく、８～１５ｍＰ・ｓがさらに好ましい。
　本実施形態の感光性樹脂組成物に含まれるケイ素の総含有量は、感光性樹脂組成物から（Ｃ）溶剤を除いた全成分の合計質量に対し、４．０～２０質量％であり、４．５～１０質量％であることが好ましく、５．０～９．５質量％であることがより好ましい。ケイ素の総含有量が４．０質量％以上であると、樹脂硬化膜が十分な硬度を有する。ケイ素の総含有量が２０質量％以下であると、感光性樹脂組成物の現像性や樹脂硬化膜の平坦性が良好である。ケイ素の総含有量は、原料の仕込み量から算出した計算値である。
＜（Ａ）共重合体の製造方法＞
　本実施形態の（Ａ）共重合体は、（Ｃ－１）溶剤の存在下で、（Ａ－１）アルコキシシリル基を有する重合性不飽和化合物、（Ａ－２）酸基を有する重合性不飽和化合物、および必要に応じて用いる（Ａ－３）その他の重合性不飽和化合物からなるモノマー混合物を、当該技術分野において公知のラジカル重合方法に従って共重合させることにより調製することができる。例えば、（Ａ－１）化合物、（Ａ－２）化合物及び（Ａ－３）化合物を（Ｃ－１）溶剤に溶解して、溶液を調製した後、その溶液に重合開始剤を添加し、５０℃～１３０℃にて１時間～２０時間反応させればよい。（Ａ）共重合体における、それぞれの化合物の繰り返し数や、それぞれの化合物が結合する順番は特に限定されない。また、構成単位（ａ－１）、構成単位（ａ－２）及び構成単位（ａ－３）のいずれかを含まない共重合体を調製した後に、不足する構成単位を変性反応により共重合体内に導入することで、構成単位（ａ－１）、構成単位（ａ－２）及び構成単位（ａ－３）を含む共重合体を調製してもよい。
　前記（Ａ－１）～（Ａ－３）化合物については、上述の各構成単位（ａ－１）～（ａ－３）を構成する化合物として挙げたものを用いることができる。
　上記した（Ａ）共重合体を構成する構成単位（ａ－１）～（ａ－３）の含有比率を規定したのと同様の理由で、（Ａ－１）化合物、（Ａ－２）化合物及び（Ａ－３）化合物の配合量を規定することができる。すなわち、（Ａ－１）～（Ａ－３）化合物の合計を１００モル％としたときに、（Ａ－１）化合物の配合量は、４５～９９モル％であり、５０～９０モル％であることが好ましく、６０～８５モル％であることがより好ましく、７０～８５モル％であることがさらに好ましい。（Ａ－２）化合物の配合量は、１～５５モル％であることが好ましく、１５～４０モル％であることがより好ましく、１５～３０モル％であることがさらに好ましい。（Ａ－３）化合物を用いる場合の配合量は、０．１～４０モル％であることが好ましく、１～３０モル％であることがより好ましく、５～２０モル％であることがさらに好ましい。
　前記（Ｃ－１）溶剤については、重合反応に不活性の溶剤であれば特に限定されない。前述の感光性樹脂組成物として用いる（Ｃ）溶剤と同様の溶剤を使用すれば、重合反応用溶媒を分離、除去する必要が無いので好ましい。また、（Ａ）共重合体の重量平均分子量（Ｍｗ）及び分子量分布（Ｍｗ／Ｍｎ）を所定の範囲に制御すると共に、所望の保存安定性を有する感光性樹脂組成物を得る観点から、炭素原子数３～１０の第一級アルコール又は第二級アルコールのいずれかを少なくとも含む溶剤を使用することが好ましい。
　溶剤が炭素原子数３～１０の第一級アルコール又は第二級アルコールのいずれかの溶剤を含む場合、炭素原子数３～１０の第一級アルコール又は第二級アルコール溶剤の含有比率は、溶剤の合計量に対して、１０～１００質量％であることが好ましく、２０～１００質量部であることがより好ましい。含有比率が上記範囲内であると、（Ａ）共重合体の重量分子量及び分子量分布（Ｍｗ／Ｍｎ）を所定の範囲により制御し易く、該溶剤を感光性樹脂組成物の（Ｃ）溶剤としてそのまま使用すれば、感光性樹脂組成物の保存安定性をより向上させることができる。
　（Ａ）共重合体の製造に用いる溶剤の使用量は、特に限定されないが、（Ａ－１）～（Ａ－３）化合物の仕込み量の合計を１００質量部としたときに、好ましくは３０質量部～１０００質量部、より好ましくは５０質量部～８００質量部である。使用量が３０質量部以上であると、重合反応を安定して行うことができ、（Ａ）共重合体の着色やゲル化を防止できる。使用量が１０００質量部以下であると、連鎖移動作用による（Ａ）共重合体の分子量の低下を抑制し、反応溶液の粘度を適切な範囲に制御することができる。
　この共重合反応に用いることが可能な重合開始剤としては、特に限定されないが、例えば、２，２’－アゾビス（イソブチロニトリル）、２，２’－アゾビス（２，４－ジメチルバレロニトリル）、２，２’－アゾビス（イソ酪酸）ジメチル、過酸化ベンゾイル、ｔ－ブチルパーオキシ－２－エチルヘキサノエート等が挙げられる。これらの重合開始剤は、１種を単独で用いてもよく、２種以上を組み合わせて用いてもよい。
　重合開始剤の使用量は、特に限定されないが、（Ａ－１）化合物、（Ａ－２）化合物及び（Ａ－３）化合物の仕込み量の合計を１００質量部としたときに、好ましくは０．１質量部～２０質量部、より好ましくは０．５質量部～１６質量部である。
＜感光性樹脂組成物の製造方法＞
　本実施形態の感光性樹脂組成物は、公知の混合装置を用い、上記の成分を混合することによって調製してもよい。あるいは、本実施形態の感光性樹脂組成物は、先に、（Ａ）共重合体及び（Ｃ－１）溶剤を含む組成物を調製した後、（Ｂ）光酸発生剤、および任意成分の（Ｄ）反応性希釈剤、（Ｅ）光重合開始剤を添加し、混合することによって調製してもよい。「（Ａ）共重合体及び（Ｃ－１）溶剤を含む組成物を調製した後」ということは、即ち、「（Ａ－１）化合物、（Ａ－２）化合物及び（Ａ－３）化合物からなるモノマー混合物を、（Ｃ－１）溶剤の存在下で共重合させた後」のことである。後者の調製方法では、必要に応じて、共重合後に（Ｃ－２）溶剤を追加で添加してもよい。共重合後に（Ｃ－２）溶剤を追加で添加する場合、感光性樹脂組成物に含まれている（Ｃ）溶剤は、（Ｃ－１）溶剤と（Ｃ－２）溶剤を含む。（Ｃ－２）溶剤は、（Ｃ－１）溶剤と同じでも、異なってもよく、（Ｃ－１）溶剤と同じであることが好ましい。すなわち、感光性樹脂組成物に含まれている（Ｃ）溶剤は、光重合体の製造用溶剤と同じであることが好ましい。
　本実施形態の感光性樹脂組成物は、アルカリ現像性を有しているので、アルカリ水溶液を用いることによって現像を行うことができる。特に、本実施形態の感光性樹脂組成物は、現像性に優れたパターンを与えることができる。そのため、本実施形態の感光性樹脂組成物は、有機ＥＬ表示装置、液晶表示装置、固体撮像素子に組み込まれるオーバーコート、保護膜、絶縁膜を製造するために用いられるレジストとして好適に用いられる。
＜樹脂硬化膜＞
　本実施形態の樹脂硬化膜は、前記感光性樹脂組成物を基材に塗布、プリベーク、露光、ポストベークすることにより形成される。フォトリソグラフィ法によりパターンを形成する場合には、前記感光性樹脂組成物を基材に塗布、プリベークした後、形成した塗布膜を所定のパターンのフォトマスクを介して露光することにより露光部分を光硬化させる。そして、必要に応じて露光後加熱処理をした後、未露光部分をアルカリ水溶液で溶解して現像した後、ポストベークすることにより所定のパターンを形成することができる。
（１）塗布工程
　感光性樹脂組成物の塗布方法としては、特に限定されないが、スクリーン印刷法、ロールコート法、カーテンコート法、スプレーコート法、スピンコート法、スリットコート法等が用いられる。
（２）プリベーク工程
　塗布工程により塗膜を形成させたのち、その塗膜を乾燥させて塗膜中の溶剤残存量を減少させるため、プリベーク（前加熱処理）することが好ましい。プリベーク工程は、一般に７０～１２０℃、好ましくは９０～１１０℃の温度で、ホットプレートによる場合には１０～６００秒間、好ましくは１２０～１８０秒間実施することができる。
（３）露光工程
　形成した塗膜表面を、光照射により露光する。パターンを形成する場合には、塗膜表面を所定のパターンのフォトマスクを介して露光する。光照射に用いられる光源としては、特に限定されないが、例えば、低圧水銀ランプ、中圧水銀ランプ、高圧水銀ランプ、キセノンランプ、メタルハライドランプ等が用いられる。また、露光量も、特に限定されず、感光性樹脂組成物の組成に応じて適宜設定される。
（４）露光後加熱工程
　パターンを形成する場合には、露光工程後に必要に応じて露光後加熱処理（Ｐｏｓｔ Ｅｘｐｏｓｕｒｅ Ｂａｋｉｎｇ）を行うことができる。この工程により、塗膜の露光部と未露光部の溶解コントラストをより顕著に出すことができる。この工程は、後述する（６）ポストベークの工程とは異なり、塗膜を完全に硬化させるために行うものではなく、現像工程後に露光部のパターンだけを基板上に残し、未露光部の塗膜を現像により確実に除去することが可能となるように行う。従って、本実施形態の樹脂硬化膜の形成において、必須の工程ではない。露光後加熱処理を行う場合、ホットプレート、オーブン、またはファーネス等を使用することができる。加熱温度の範囲としては、４０℃～７０℃が好ましく、５０℃～６０℃が更に好ましい。加熱温度が４０℃以上であれば、塗膜の露光部と未露光部の溶解コントラストを向上させて、露光後加熱処理の効果を十分に発揮することができる。加熱温度が７０℃以下であれば、露光部に発生した酸が未露光部まで拡散することもなく良好な溶解コントラストを得られる。加熱時間の範囲としては、２０秒～６００秒が好ましい。２０秒以上であれば塗膜全体の温度履歴を均一にすることができる。６００秒以下であれば、露光部に発生した酸が未露光部まで拡散することもなく良好な溶解コントラストを得られる。
（５）現像工程
　　露光後、必要に応じて露光後加熱を行ったあと、塗膜を現像処理する。現像の際に用いられる現像液としては、従来、感光性組成物の現像に用いられている任意の現像液を用いることができる。現像に用いられるアルカリ水溶液としては、特に限定されないが、例えば、炭酸ナトリウム、炭酸カリウム、炭酸カルシウム、水酸化ナトリウム、水酸化カリウム等の水溶液；エチルアミン、ジエチルアミン、ジメチルエタノールアミン等のアミン系化合物の水溶液；水酸化テトラメチルアンモニウム等の第４級アンモニウム塩の水溶液；３－メチル－４－アミノ－Ｎ，Ｎ－ジエチルアニリン、３－メチル－４－アミノ－Ｎ－エチル－Ｎ－β－ヒドロキシエチルアニリン、３－メチル－４－アミノ－Ｎ－エチル－Ｎ－β－メタンスルホンアミドエチルアニリン、３－メチル－４－アミノ－Ｎ－エチル－Ｎ－β－メトキシエチルアニリン及びこれらの硫酸塩、塩酸塩又はｐ－トルエンスルホン酸塩等のｐ－フェニレンジアミン系化合物の水溶液等が用いられる。これらの中でも、ｐ－フェニレンジアミン系化合物の水溶液を用いることが好ましい。なお、これらのアルカリ水溶液には、必要に応じて、消泡剤や界面活性剤を添加してもよい。また、上記のアルカリ水溶液による現像の後、水洗して乾燥させることが好ましい。
（６）ポストベーク工程
　現像工程後にポストベークを行い、樹脂硬化膜を得る。ポストベークの条件は、特に限定されず、感光性樹脂組成物の組成に応じて加熱処理を行えばよい。例えば、８０℃～２５０℃の温度にて、１０分～６０分間加熱すればよい。基材に各種樹脂フィルムなどを用いる場合には、基材や回路の熱によるダメージ低減の観点からポストベーク工程の温度範囲を、８０℃～１３０℃とすることが好ましく、８０℃～１００℃とすることがより好ましい。
　本実施形態の樹脂硬化膜は、光透過率が高く透明性に優れる。また、樹脂硬化膜の硬度が良好であるため、カラーフィルター上部のオーバーコート、各種保護膜などに好適に用いることができる。また、タッチパネルのＩＴＯなど電極間の絶縁膜やＴＦＴの層間絶縁膜など、各種絶縁材料としても好適に用いることができる。
＜画像表示装置＞
　本実施形態の画像表示装置は、上述した樹脂硬化膜を具備した画像表示素子を有する。前記画像表示素子としては、上述した樹脂硬化膜を具備していれば特に限定されないが、例えば、液晶表示素子、有機ＥＬ表示素子等が挙げられる。特に、本実施形態の感光性樹脂組成物は、高温域の加熱工程を有することなく樹脂硬化膜を作製することができるため、折りたたみスマホやフレキシブルディスプレイなど、ガラス基板を用いない画像表示装置に対しても有効である。
　以下、実施例及び比較例により本発明をさらに具体的に説明するが、本発明は以下の実施例に限定されるものではない。
　（Ａ）共重合体の合成例を以下に示す。
［合成例１］
　攪拌装置、滴下ロート、コンデンサー、温度計及びガス導入管を備えたフラスコに、３－メトキシ－１－ブタノール７００ｇを入れ、窒素置換しながら攪拌し、１０５℃に昇温した。
　次に、アクリル酸７．１ｇ（０．１モル）、３－メタクリロイルオキシプロピルトリエトキシシラン２５８．４ｇ（０．９モル）からなるモノマー混合物に、２，２’－アゾビス（イソ酪酸）ジメチル（重合開始剤）３４．５ｇを添加したものを、滴下ロートから前記フラスコ中に滴下した。
　滴下終了後、１０５℃にて２時間攪拌して共重合反応を行い、（Ａ）共重合体と溶剤を含む試料１（重量平均分子量（Ｍｗ）：３８００、数平均分子量（Ｍｎ）：２５００、分子量分布（Ｍｗ／Ｍｎ）：１．５、酸価：５．６ＫＯＨｍｇ／ｇ、シリル基当量：３３７ｇ／ｍｏｌ）を得た。試料１の固形分濃度３０質量％とした。なお、固形分とは、試料を１３０℃で２時間加熱したときの加熱残分を意味し、試料１の固形分は（Ａ）共重合体が主成分となる。
［合成例２～１０、比較合成例１～３］
　表１に記載の原料を用い、また、得られた試料の固形分濃度が３０質量％になるようにそれぞれの３－メトキシ－１－ブタノールの添加量を調整した。また表１に示す各分子量（重量平均分子量（Ｍｗ）、数平均分子量（Ｍｎ））になるように重合開始剤の添加量を調整した以外は合成例１と同様にして、共重合反応を行い、（Ａ）共重合体と溶剤を含む試料２～１３を得た。得られた試料の重量平均分子量（Ｍｗ）、数平均分子量（Ｍｎ）、分子量分布（Ｍｗ／Ｍｎ）、酸価及びシリル基当量を、表１に示す。
Figure JPOXMLDOC01-appb-T000004
＜（Ａ）共重合体の評価＞
（１）保存安定性
　得られた試料１～１３を用いて、以下の方法に従い、保存安定性の評価を行った。
　試料を２０ｍｌのガラス容器に１０ｇずつ計り取ってサンプルとし、ＧＰＣ（ＧＰＣ－１０１、Ｓｈｏｄｅｘ製）を使用して重量平均分子量を測定した。続いて、これらのサンプルをそれぞれ１２℃に保った恒温器の中に３ヶ月間静置して保存した後、再び重量平均分子量を測定した。保存安定性試験前後の重量平均分子量を用いて、下記式（Ｉ）より分子量の増加率を求めた。
　分子量の増加率＝（（［試験後の分子量］－［試験前の分子量］）／［試験前の分子量］）×１００％　　　　（Ｉ）
　この評価の基準は以下の通りである。
　○：増加率３０％未満
　×：増加率３０％以上
　上記の保存安定性の評価結果を表１に示す。
＜感光性樹脂組成物の調製＞
　得られた試料１～１３を用いて、表２および表３に示す配合成分及び配合割合に従って、感光性樹脂組成物を調製した。
　なお、表２および表３における（Ａ）共重合体の配合量は、（Ａ）共重合体を合成する際に用いた溶剤の量を含まない。
［実施例１］
　得られた試料１（固形分濃度３０質量％）を用いて、（Ａ）共重合体として固形分を１００ｇ、光酸発生剤としてＣＰＩ－３１０Ｂを０．５ｇ、溶剤として３－メトキシ－１－ブタノールを３００ｇの配合で感光性樹脂組成物を調整した。３００ｇの溶剤には、試料１に含まれている溶剤を含む。調整した感光性樹脂組成物について、以下の方法で硬度、透過率、密着性、現像性の評価を行った。結果を表２に示す。
［実施例２～１６、比較例１～４］
　表２および表３に記載の原料を用いる以外は実施例１と同様にして感光性樹脂組成物を調整し、硬度、透過率、密着性、現像の評価を行った。結果を表２および表３に示す。
Figure JPOXMLDOC01-appb-T000005
Figure JPOXMLDOC01-appb-T000006
　表２および表３に記載の材料は以下のものを用いた。
・光酸発生剤：ＣＰＩ－３１０Ｂ（トリアリールスルホニウムボレート塩、サンアプロ（株）化学社製）
・光酸発生剤：ＣＰＩ－２１０Ｓ（トリアリールスルホニウム・特殊リン系アニオン塩、サンアプロ（株）化学社製）
・反応性希釈剤：ＤＰＨＡ（ジペンタエリスリトールヘキサアクリレート、東亞合成（株）社製）
・光重合開始剤：ＯＸＥ－０１（商品名、ＢＡＳＦジャパン社製）
＜感光性樹脂組成物の評価＞
（１）現像性
　調製された感光性樹脂組成物を、スピンコーター法により５ｃｍ角のガラス基板（無アルカリガラス基板）上に塗布し、１００℃にて３分間加熱（プリベーク）することで溶剤を揮発させ、ガラス基板上に塗布膜を形成した。次に、幅３～１００μｍのライン＆スペースのパターンを有するフォトマスクを、塗布膜から１００μｍの距離に配置し、このフォトマスクを介して超高圧水銀灯の光を２００ｍＪ／ｃｍ２照射した。次いで、６０℃の露光後加熱処理を、表２および表３に記載の処理時間で行った。その後、セミクリーンＤＬ－Ａ１０現像液（５倍希釈）を使用し、温度２３℃、圧力０．１ＭＰａ、現像時間６０秒の条件で未露光部を除去し、膜厚１．７μｍの塗膜を得た。上記のようにして作製したパターンを有する塗膜の顕微鏡観察を行い、解像された最小ライン幅（最小現像寸法）および未露光部の残渣の有無を評価した。最小現像寸法については、良好に現像できずパターンが判別できなかったものについては「×」で示した。
　残渣の有無については、以下の基準で示す。
　　残渣○：未露光部に残渣無し
　　残渣×：未露光部に残渣あり
　上記の現像性の評価結果を表２および表３に示す。
＜樹脂硬化膜の評価＞
（１）鉛筆硬度
　調製された感光性樹脂組成物を、スピンコーター法により５ｃｍ角のガラス基板（無アルカリガラス基板）上に塗布し、１００℃にて３分間加熱することで溶剤を揮発させ、ガラス基板上に塗布膜を形成した。次に、塗布膜に波長３６５ｎｍの光を２００ｍＪ／ｃｍ２の露光量で照射し、塗布膜を光硬化させた。次いで、乾燥機中に１３０℃３０分又は８０℃６０分の条件で静置して加熱処理（ポストベーク）を行い、膜厚１．５μｍの樹脂硬化膜を得た。
　上記のようにして作製した樹脂硬化膜の鉛筆硬度を、鉛筆硬度計（Ｎｏ．５５３－Ｍ、安田精機製作所製）を用いて、ＪＩＳ　Ｋ５６００－５－４に従い測定した。結果を表２～４に示す。
（２）透過率
　上記（１）鉛筆硬度の評価と同様にして作製した樹脂硬化膜を有する基板について、分光光度計（ＵＶ－１６５０ＰＣ、島津製作所製）を用いて４００～８００ｎｍの分光透過率を測定した。４００ｎｍにおける透過率を表２に示す。
（３）密着性
　上記（１）鉛筆硬度の評価と同様にして作製した樹脂硬化膜を有する基板について、ＪＩＳ　Ｋ５６００－５－６のクロスカット法により樹脂硬化膜の密着性を評価した。碁盤目１００個中、残った塗膜の面積の割合を算出した。以下の基準に従って判定し、結果を表２および表３に示す。
　判定の基準は以下の通りである。
　　判定○：密着性１００
　　判定×：密着性１００未満
　総合判定の基準は以下の通りである。結果を表２および表３に示す。
Figure JPOXMLDOC01-appb-T000007
［実施例１７～１８］
　表５に記載の組成を用いる以外は実施例１と同様にして感光性樹脂組成物を調整した。表５に記載のポストベーク条件を用いる以外は、上記（１）鉛筆硬度の評価方法と同様にして、樹脂硬化膜を作製し、鉛筆硬度の測定を行った。結果を表５に示す。
Figure JPOXMLDOC01-appb-T000008
　表２及び表３に示される通り、実施例１～１６の感光性樹脂組成物は現像性に優れ、硬度、透明性、密着性に優れた樹脂硬化膜を得ることができた。一方、光酸発生剤を使用しなかった比較例１は、現像性に劣り、硬度や密着性が十分な樹脂硬化膜が得られなかった。これは、ポストベーク工程等の加熱工程において、より高い温度条件が必要であるために、硬化不足が生じているためと考えられる。アクリル酸を使用しなかった比較例２は、現像性が得られない結果となった。（Ａ）共重合体における、（Ａ－１）アルコキシシリル基を有する重合性不飽和化合物由来の構成単位（ａ－１）の含有量が少ない比較例３および４は現像性が劣る結果となった。アルコキシシリル基に由来する架橋度が低いので、パターンで塗膜の露光部と未露光部も溶解して現像性に劣った。
　表５に示される通り、実施例１７～１８の感光性樹脂組成物は、ポストベークの温度条件を８０℃に下げても十分な硬度の樹脂硬化膜が得られることが分かった。
　本発明によれば、優れた硬度、透明性および密着性を有する樹脂硬化膜を与え、現像性が良好であると共に、保存安定性にも優れる感光性樹脂組成物が提供される。また、硬度、透明性および密着性に優れた樹脂硬化膜、これを具備する画像表示素子が提供される。該感光性樹脂組成物は、透明膜、保護膜、絶縁膜、オーバーコート、フォトスペーサー、ブラックマトリックス、ブラックカラムスペーサー、カラーフィルター用のレジストとして好ましく用いることができる。

Claims (14)

  1. 　（Ａ）共重合体と、（Ｂ）光酸発生剤と、（Ｃ）溶剤とを含有する感光性樹脂組成物であって、
    　前記（Ａ）共重合体が、（Ａ－１）アルコキシシリル基を有する重合性不飽和化合物由来の構成単位（ａ－１）と、（Ａ－２）酸基を有する重合性不飽和化合物由来の構成単位（ａ－２）とを含む共重合体であり、
    　前記（Ａ）共重合体における全構成単位中の前記構成単位（ａ－１）の含有量が、４５～９９モル％であることを特徴とする感光性樹脂組成物。
  2. 　前記（Ａ）共重合体の酸価が１５～１５０ＫＯＨｍｇ／ｇである請求項１に記載の感光性樹脂組成物。
  3. 　前記構成単位（ａ－１）が（Ａ－１ａ）アルコキシシリル基含有（メタ）アクリレート由来の構成単位（ａ－１ａ）である請求項１又は２に記載の感光性樹脂組成物。
  4. 　前記構成単位（ａ－１ａ）が、下記式（１）で表される請求項３に記載の感光性樹脂組成物。
    Figure JPOXMLDOC01-appb-C000001
     ［式（１）中、Ｒ１は水素原子又はメチル基を表し、Ｒ２～Ｒ４は各々独立に、水素原子、炭素原子数１～６のアルキル基又は炭素原子数１～６のアルコキシ基を表し、ｎは１～１０の整数である。ただし、Ｒ２～Ｒ４のうち少なくとも１つは炭素原子数１～６のアルコキシ基である。］
  5. 　前記構成単位（ａ－２）が有する酸基がカルボキシ基である請求項１～４のいずれか一項に記載の感光性樹脂組成物。
  6. 　前記（Ｃ）溶剤が、炭素原子数３～１０の第一級アルコール又は第二級アルコールのいずれかを少なくとも含む溶剤である請求項１～５のいずれか一項に記載の感光性樹脂組成物。
  7. 　前記（Ｂ）光酸発生剤が、スルホニウム塩化合物である請求項１～６のいずれか一項に記載の感光性樹脂組成物。
  8. 　前記（Ａ）共重合体の重量平均分子量が、２０００～３００００である請求項１～７のいずれか一項に記載の感光性樹脂組成物。
  9. 　（Ｄ）反応性希釈剤、および（Ｅ）光重合開始剤をさらに含む請求項１～８のいずれか一項に記載の感光性樹脂組成物。
  10. 　前記（Ｂ）光酸発生剤の含有量が、前記（Ａ）共重合体１００質量部に対して、０．１～１０質量部である請求項１～９のいずれか一項に記載の感光性樹脂組成物。
  11. 　前記（Ａ）共重合体と前記（Ｄ）反応性希釈剤との質量比が、４０：６０～９９：１であり、前記（Ｅ）光重合開始剤の含有量が前記（Ｄ）反応性希釈剤１００質量部に対して０．１～３０質量部である請求項９に記載の感光性樹脂組成物。
  12. 　請求項１～１１のいずれか一項に記載の感光性樹脂組成物を硬化させてなる樹脂硬化膜。
  13. 　オーバーコート、保護膜、及び絶縁膜からなる群から選択される一種である請求項１２に記載の樹脂硬化膜。
  14. 　請求項１２に記載の樹脂硬化膜を具備する画像表示装置。
PCT/JP2021/023720 2020-07-06 2021-06-23 感光性樹脂組成物及びその樹脂硬化膜 Ceased WO2022009676A1 (ja)