WO2021045203A1 - 高分子材料及びその製造方法 - Google Patents

高分子材料及びその製造方法 Download PDF

Info

Publication number
WO2021045203A1
WO2021045203A1 PCT/JP2020/033642 JP2020033642W WO2021045203A1 WO 2021045203 A1 WO2021045203 A1 WO 2021045203A1 JP 2020033642 W JP2020033642 W JP 2020033642W WO 2021045203 A1 WO2021045203 A1 WO 2021045203A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
polymer material
bis
polysiloxane
formula
Prior art date
Application number
PCT/JP2020/033642
Other languages
English (en)
French (fr)
Inventor
義徳 ▲高▼島
原田　明
浩靖 山口
基史 大▲崎▼
大地 吉田
Original Assignee
国立大学法人大阪大学
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 国立大学法人大阪大学 filed Critical 国立大学法人大阪大学
Priority to JP2021544057A priority Critical patent/JPWO2021045203A1/ja
Publication of WO2021045203A1 publication Critical patent/WO2021045203A1/ja

Abstract

機械特性に優れ、高い吸湿性を備えたポリシロキサン骨格を有する高分子材料及びその製造方法を提供する。　本発明は、ポリシロキサン骨格を有する高分子材料であって、前記ポリシロキサン骨格は側鎖に下記一般式（１） －Ｒ１－ＲＨ　（１） （式（１）中、Ｒ１はＮＨ又はＯを示し、ＲＨはホスト基を示す。） で表される構成単位を有し、前記ホスト基は、シクロデキストリン又はシクロデキストリン誘導体から１個の水素原子又は水酸基が除された１価の基であり、前記シクロデキストリン誘導体は、シクロデキストリンが有する少なくとも１個の水酸基の水素原子が炭化水素基、アシル基及び－ＣＯＮＨＲ（Ｒはメチル基又はエチル基）からなる群より選ばれる少なくとも１種の基で置換された構造を有する。

Description

高分子材料及びその製造方法
　本発明は、ポリシロキサン骨格を有する高分子材料及びその製造方法に関する。
　シロキサン結合（Ｓｉ－Ｏ結合）を主骨格に持つ合成高分子化合物（ポリシロキサン）は、有機高分子にはない特有の性質を有することが知られており、様々な分野で利用されている。シロキサン結合は、一般の有機高分子に存在する炭素－炭素あるいは炭素－酸素結合よりも強い結合力をもち、化学的に安定な性質を有することから、シロキサン結合を繰り返し有して形成されるポリシロキサンは、例えば、優れた耐熱性及び耐候性を備える。また、ポリシロキサンは、無機性のシロキサン結合が内側、有機性の側鎖置換基が外側に配置されたらせん構造を形成することができるので、柔軟かつ撥水性を有し、生体毒性も低い。従って、ポリシロキサンは、医用器具、ゴム、塗料、保護フィルム等の各種用途において、利用価値が高い材料である。
　一方で、近年では、ポリシロキサンをベースとするような材料に対して、さらに機能性を付与することも求められており、例えば、さらなる機械特性の向上、自己修復性の付与等が要望されている。この観点から、例えば、非特許文献１には、ポリシロキサン骨格中に水素結合可能な官能基を導入し、かかる官能基の水素結合を通じて自己修復性を発揮させる技術が提案されている。
Ａｄｖ．Ｍａｔｅｒ．２０１８，３０，１７０６８４６
　しかしながら、最近ではポリシロキサンを様々な用途に適用すべく、更なる機能をポリシロキサンに付加させることが強く望まれている。例えば、ポリシロキサンの一つの特長としては優れた撥水性にあるが、吸湿性を向上させることは難しかったことから、ポリシロキサンの用途が制限されることが多い。このため、吸湿性の高いポリシロキサンが求められている。このような観点から、優れた機械特性を有しつつ、吸湿性をさらに向上させたポリシロキサンを製造することができれば、従来のポリシロキサンでは適用することができなかった用途へ適用することが可能となるので、このようなポリシロキサンの利用価値は非常に高いといえる。
　本発明は、上記に鑑みてなされたものであり、機械特性に優れ、高い吸湿性を備えたポリシロキサン骨格を有する高分子材料及びその製造方法を提供することを目的とする。
　本発明者らは、上記目的を達成すべく鋭意研究を重ねた結果、ポリシロキサン骨格にホスト－ゲスト相互作用可能な特定の官能基を導入することにより、上記目的を達成できることを見出し、本発明を完成するに至った。
　すなわち、本発明は、例えば、以下の項に記載の主題を包含する。
項１
ポリシロキサン骨格を有する高分子材料であって、
前記ポリシロキサン骨格は側鎖に下記一般式（１）
－Ｒ１－ＲＨ　　　（１）
（式（１）中、Ｒ１はＮＨ又はＯを示し、ＲＨはホスト基を示す。）
で表される構成単位を有し、
前記ホスト基は、シクロデキストリン又はシクロデキストリン誘導体から１個の水素原子又は水酸基が除された１価の基であり、
前記シクロデキストリン誘導体は、シクロデキストリンが有する少なくとも１個の水酸基の水素原子が炭化水素基、アシル基及び－ＣＯＮＨＲ（Ｒはメチル基又はエチル基）からなる群より選ばれる少なくとも１種の基で置換された構造を有する、高分子材料。
項２
前記ホスト基は、ゲスト基を包接して包接錯体を形成すると共に、包接された前記ゲスト基は、前記ポリシロキサン骨格の側鎖に化学結合している、項１に記載の高分子材料。
項３
前記ホスト基の環内をポリシロキサンが貫通した構造を有する、項１に記載の高分子材料。
項４
項１又は２に記載の高分子材料の製造方法であって、
下記一般式（１ａ）
Ｒ２－ＲＨ　　　（１ａ）
（式（１ａ）中、Ｒ２はＮＨ２又はＯＨを示し、ＲＨは前記式（１）中のＲＨと同義である）
で表される化合物にゲスト分子が包接されてなる包接化合物と、
側鎖に反応性官能基を有するポリシロキサンと、
を反応する工程を備える、高分子材料の製造方法。
項５
前記反応性官能基はエポキシ基である、項４に記載の製造方法。
　本発明の高分子材料は、機械特性に優れ、高い吸湿性を有する。
本発明の高分子材料の一例を模式的に説明する図である。 本発明の高分子材料の他例を模式的に説明する図である。 （ａ）及び（ｂ）はそれぞれ、ＮＨ２－ＰＭβＣＤのマススペクトル及び、ＮＭＲスペクトルの結果を示す。 実施例１で行った反応の反応スキームである。 実施例１で得られた高分子材料の１Ｈ－ＮＭＲスペクトル（ＣＤＣｌ３、５００ＭＨｚ、２５℃）である。
　以下、本発明の実施形態について詳細に説明する。なお、本明細書中において、「含有」及び「含む」なる表現については、「含有」、「含む」、「実質的にからなる」及び「のみからなる」という概念を含む。
　１．高分子材料
　本発明の高分子材料は、ポリシロキサン骨格を有し、前記ポリシロキサン骨格は側鎖に下記一般式（１）
－Ｒ１－ＲＨ　　　（１）
（式（１）中、Ｒ１はＮＨ又はＯを示し、ＲＨはホスト基を示す。）
で表される構成単位を有する。ここで、前記ホスト基は、シクロデキストリン又はシクロデキストリン誘導体から１個の水素原子又は水酸基が除された１価の基であり、前記シクロデキストリン誘導体は、シクロデキストリンが有する少なくとも１個の水酸基の水素原子が炭化水素基、アシル基及び－ＣＯＮＨＲ（Ｒはメチル基又はエチル基）からなる群より選ばれる少なくとも１種の基で置換された構造を有する。
　なお、本明細書において、「炭化水素基、アシル基及び－ＣＯＮＨＲ（Ｒはメチル基又はエチル基）からなる群より選ばれる少なくとも１種の基」を便宜上、「炭化水素基等」と表記することがある。
　本発明の高分子材料は、ポリシロキサン骨格を有する分子鎖で形成される材料である。ポリシロキサン骨格は、シロキサン結合を有する鎖状高分子であり、最小の構成単位として「－Ｓｉ－Ｏ－Ｓｉ－」構造を有する。ポリシロキサン骨格は直鎖状であってもよい。また、ポリシロキサン骨格において、「－Ｓｉ－Ｏ－Ｓｉ－」構造中のＳｉ原子がさらにシロキサン結合（－Ｏ－Ｓｉ）を有する場合は、ポリシロキサン骨格は、分岐構造であってもよいし、架橋構造であってもよい。高分子材料が適度な機械特性を有し、また、後記する自己修復性を発揮しやすいという観点から、ポリシロキサン骨格は直鎖状であることが好ましい。
　ポリシロキサン骨格が直鎖状である場合、ポリシロキサン骨格は、例えば、下記式（２）で表される構成単位を含有することができる。
Figure JPOXMLDOC01-appb-C000001
　式（２）中、Ｒ３及びＲ４は同一又は異なって、置換基で置換されていてもよい炭素数１から１０の直鎖又は分岐のアルキル基、もしくは置換基で置換されていてもよい炭素数６から２０のアリール基を示す。
　式（２）において、炭素数１から１０の直鎖又は分岐のアルキル基は、炭素数が１から４が好ましく、１又は２が特に好ましい。具体的にはアルキル基としては、メチル基、エチル基、ｎ－プロピル基、イソプロピル基、ｎ－ブチル基、ｓｅｃ－ブチル基、ｔｅｒｔ－ブチル基、ｎ－ペンチル基、ｎ－ヘキシル基、ｎ－ヘプチル基、ｎ－オクチル基、ｎ－ノニル基、ｎ－デシル基等が挙げられる。
　式（２）において、炭素数１から１０の直鎖又は分岐のアルキル基が置換基で置換されている場合、置換基の数は１又は２以上とすることができる。この場合の置換基としては、例えば、ヒドロキシ基、アルコキシ基、エステル基、シアノ基、ニトロ基、スルホ基、カルボキシ基、アリール基、ハロゲン原子（例えばフッ素原子、塩素原子、臭素原子、ヨウ素原子）等が挙げられる。
　式（２）において、炭素数６から２０のアリール基は、例えば、フェニル基、ナフチル基、テトラヒドロナフチル基等が挙げられる。アリール基が置換基で置換されている場合、置換基の数は１又は２以上とすることができる。この場合の置換基としては、例えば、ヒドロキシ基、アルコキシ基、エステル基、シアノ基、ニトロ基、スルホ基、カルボキシ基、アリール基、ハロゲン原子（例えばフッ素原子、塩素原子、臭素原子、ヨウ素原子）等が挙げられる。
　式（２）において、Ｒ３及びＲ４は同一とすることができ、あるいは、異なっていてもよい。式（２）において、Ｒ３及びＲ４はいずれも、メチル基、エチル基、ｎ－プロピル基、イソプロピル基であることが好ましく、メチル基が特に好ましい。Ｒ３及びＲ４はいずれもメチル基である場合、ポリシロキサン骨格はポリジメチルシロキサンを含む。
　ポリシロキサン骨格は、前述のように、側鎖に前記式（１）で表される構成単位「－Ｒ１－ＲＨ」を有する。かかる構成単位中の、Ｒ１は、ポリシロキサン骨格中のＳｉに直接結合することができ、あるいは、間接的に結合（つまり、Ｒ１とＳｉとの間に他の基を介在）することもできる。さらに別の態様として、Ｒ１は、ビニル系重合体の側鎖に直接結合することができる。
　Ｒ１がポリシロキサン骨格中のＳｉに直接結合、又は、間接的に結合（つまり、Ｒ１とＳｉとの間に他の基を介在）している場合、例えば、ポリシロキサン骨格は、下記式（３）で表される構成単位をさらに含むことができる。
Figure JPOXMLDOC01-appb-C000002
　式（３）中、Ｒ５は前記式（２）のＲ３及びＲ４と同義である。式（３）中、Ｒ６は、炭素数１～１０のアルキレンを含む２価の基を示し、ｎは０又は１の数である。ｎが０のときはＲ６がないことを意味し、つまり、Ｒ１がケイ素原子に直接結合していることを意味する。
　式（３）において、Ｒ５は、メチル基、エチル基、ｎ－プロピル基、イソプロピル基であることが好ましく、メチル基が特に好ましい。
　式（３）において、Ｒ６は、炭素数１～１０のアルキレンを含む２価の基である限り特に限定されない。Ｒ６において、アルキレンの炭素数は１～８が好ましく、２～６がより好ましい。Ｒ６は、例えば、ヘテロ原子を含むこともできる。ヘテロ原子としては、例えば、酸素、窒素等を挙げることができる。Ｒ６がヘテロ原子を含む場合、Ｒ６としては、エーテル結合、アミド結合、アミノ基等を有することもでき、中でもエーテル結合を有することが好ましい（例えば、－（ＣＨ２）３－Ｏ－（ＣＨ２）３－結合が例示される）。炭素数１～１０のアルキレンを含む１価の基はさらに置換基を有することができる。置換基の種類は特に限定されず、例えば、ヒドロキシ基、アルコキシ基、エステル基、シアノ基、ニトロ基、スルホ基、カルボキシ基、アリール基、ハロゲン原子（例えばフッ素原子、塩素原子、臭素原子、ヨウ素原子）等が挙げられ、ヒドロキシ基であることが特に好ましい。
　一方、前述のようにＲ１がビニル系重合体の側鎖に直接結合している場合、ビニル系重合体としては、例えば、公知のビニル系重合体を挙げることができ、例えば、各種のアクリル系ポリマーを例示することができる。中でも、（メタ）アクリル酸エステル、Ｎ置換（メタ）アクリルアミド等を挙げることができる。これらの場合は、Ｒ１は、（メタ）アクリル酸エステルのエステル部位、もしくは、Ｎ置換（メタ）アクリルアミドのアミド部位に結合することができる。Ｒ１がビニル系重合体の側鎖に直接結合してなる場合の例としては、例えば、国際公開第２０１８／１５９７９１号に記載のホスト基含有重合性単量体の重合体を挙げることができる。
　式（１）において、Ｒ１はＮＨ又はＯであり、ＮＨであることが特に好ましい。
　ＲＨ、つまり、ホスト基は、シクロデキストリン又はシクロデキストリン誘導体から１個の水素原子又は水酸基が除された１価の基である。中でもホスト基は、シクロデキストリン誘導体から１個の水素原子又は水酸基が除された１価の基であることが好ましい。前記シクロデキストリン誘導体は、シクロデキストリンが有する少なくとも１個の水酸基の水素原子が炭化水素基等（つまり、炭化水素基、アシル基及び－ＣＯＮＨＲ（Ｒはメチル基又はエチル基）からなる群より選ばれる少なくとも１種の基）で置換された構造を有する。つまり、シクロデキストリン誘導体とは、シクロデキストリン分子が他の有機基で置換された構造を有する分子をいう。ただし、シクロデキストリン誘導体は、少なくとも一つの水素原子又は一つの水酸基を有し、好ましくは少なくとも一つの水酸基を有する。
　なお、念のための注記に過ぎないが、本明細書でのシクロデキストリンなる表記は、α－シクロデキストリン、β－シクロデキストリン及びγ－シクロデキストリンからなる群より選ばれる少なくとも１種を意味する。従って、シクロデキストリン誘導体は、α－シクロデキストリン誘導体、β－シクロデキストリン誘導体及びγ－シクロデキストリン誘導体からなる群より選ばれる少なくとも１種である。
　ホスト基は、シクロデキストリン又はシクロデキストリン誘導体から１個の水酸基が除された１価の基であることが好ましい。
　ホスト基は、シクロデキストリン又はシクロデキストリン誘導体から１個の水素原子又は水酸基が除された１価の基であるが、シクロデキストリン又はシクロデキストリン誘導体において除される水素原子又は水酸基は、シクロデキストリン又はシクロデキストリン誘導体のどの部位であってもよい。
　ここで、シクロデキストリン１分子が有する水酸基の全個数をＮとした場合、α－シクロデキストリンはＮ＝１８、β－シクロデキストリンはＮ＝２１、γ－シクロデキストリンはＮ＝２４である。
　仮に、ホスト基がシクロデキストリン誘導体から１個の「水酸基」が除された１価の基である場合は、シクロデキストリン誘導体は、シクロデキストリン１分子あたり最大Ｎ－１個の水酸基の水素原子が炭化水素基等で置換されて形成される。他方、ホスト基がシクロデキストリン誘導体から１個の「水素原子」が除された１価の基である場合は、シクロデキストリン誘導体は、シクロデキストリン１分子あたり最大Ｎ個の水酸基の水素原子が炭化水素基等で置換され得る。
　前記ホスト基は、前記シクロデキストリン１分子中に存在する全水酸基数のうちの７０％以上の水酸基の水素原子が前記炭化水素基等で置換された構造を有することが好ましい。この場合、式（１）で表される構成単位は、疎水性の単量体単位に対してより高い親和性を示すことができる。前記ホスト基は、前記シクロデキストリン１分子中に存在する全水酸基数のうちの８０％以上の水酸基の水素原子が前記炭化水素基等で置換されていることがより好ましく、全水酸基数のうちの９０％以上の水酸基の水素原子が前記炭化水素基等で置換されていることが特に好ましい。
　前記ホスト基は、α－シクロデキストリン１分子中に存在する全水酸基のうちの１３個以上の水酸基の水素原子が前記炭化水素基等で置換された構造を有することが好ましい。前記ホスト基は、α－シクロデキストリン１分子中に存在する全水酸基のうちの１５個以上の水酸基の水素原子が前記炭化水素基等で置換されていることがより好ましく、全水酸基のうちの１７個の水酸基の水素原子が前記炭化水素基等で置換されていることが特に好ましい。
　前記ホスト基は、β－シクロデキストリン１分子中に存在する全水酸基のうちの１５個以上の水酸基の水素原子が前記炭化水素基等で置換された構造を有することが好ましい。前記ホスト基は、β－シクロデキストリン１分子中に存在する全水酸基のうちの１７個以上の水酸基の水素原子が前記炭化水素基等で置換されていることがより好ましく、全水酸基のうちの１９個以上の水酸基の水素原子が前記炭化水素基等で置換されていることが特に好ましい。
　前記ホスト基は、γ－シクロデキストリン１分子中に存在する全水酸基のうちの１７個以上の水酸基の水素原子が前記炭化水素基等で置換された構造を有することが好ましい。前記ホスト基は、γ－シクロデキストリン１分子中に存在する全水酸基のうちの１９個以上の水酸基の水素原子が前記炭化水素基等で置換されていることがより好ましく、全水酸基のうちの２１個以上の水酸基の水素原子が前記炭化水素基等で置換されていることが特に好ましい。
　前記ホスト基が２以上の炭化水素基を有する場合は、それらはすべて同一でもよいし、一部が異なっていてもよい。
　シクロデキストリン誘導体において、前記炭化水素基の種類は特に限定されない。前記炭化水素基としては、例えば、アルキル基、アルケニル基、及びアルキニル基を挙げることができる。
　前記炭化水素基の炭素数の数は特に限定されず、例えば、炭化水素基の炭素数は１～４個であることが好ましい。
　炭素数が１～４個である炭化水素基の具体例としては、メチル基、エチル基、ｎ－プロピル基、イソプロピル基、ブチル基を挙げることができる。炭化水素基がブチル基である場合は、直鎖状及び分岐鎖状のいずれであってもよい。
　炭化水素基は、本発明の効果が阻害されない限りは、置換基を有していてもよい。
　シクロデキストリン誘導体において、アシル基は、アセチル基、プロピオニル、ホルミル基等を例示することができる。アシル基は、さらに置換基を有することもできる。ホスト－ゲスト相互作用を形成しやすく、また、靭性及び強度に優れる靭性及び強度に優れる高分子材料を得やすいという観点から、アシル基は、アセチル基であることが好ましい。
　シクロデキストリン誘導体において、－ＣＯＮＨＲ（Ｒはメチル基又はエチル基）は、メチルカルバメート基又はエチルカルバメート基である。ホスト－ゲスト相互作用が形成されやすいという観点から、－ＣＯＮＨＲは、エチルカルバメート基であることが好ましい。
　シクロデキストリン誘導体において、炭化水素基等は、メチル基及びアシル基が好ましく、メチル基、アセチル基、プロピオニル基がさらに好ましく、メチル基及びアセチル基が特に好ましい。
　ポリシロキサン骨格は、他の構成単位を有することができる。他の構成単位としては、例えば、反応性官能基がケイ素原子に直接又は間接的に結合したシロキサン単位を挙げることができる。具体的には、下記式（４）で表される構成単位をさらに含むことができる。
Figure JPOXMLDOC01-appb-C000003
　式（４）中、Ｒ７は前記式（２）のＲ３及びＲ４と同義である。式（４）中、Ｒ８は、炭素数１～８のアルキレンを含む１価の基を示し、Ａは反応性官能基を示す。
　式（４）において、Ｒ７は、メチル基、エチル基、ｎ－プロピル基、イソプロピル基であることが好ましく、メチル基が特に好ましい。
　式（４）において、Ｒ８は、炭素数１～８のアルキレンを含む２価の基である限り特に限定されない。Ｒ８において、アルキレンの炭素数は１～８が好ましく、２～７がより好ましく、２～６がさらに好ましく、２～５が特に好ましい。Ｒ８は、例えば、ヘテロ原子を含むこともできる。ヘテロ原子としては、例えば、酸素、窒素等を挙げることができる。Ｒ８がヘテロ原子を含む場合、Ｒ８としては、例えば、エーテル結合、アミド結合、アミノ基等を有することもでき、中でもエーテル結合を有することが好ましい（例えば、－（ＣＨ２）３－Ｏ－（ＣＨ２）－結合が例示される）。炭素数１～８のアルキレンを含む１価の基はさらに置換基を有することができる。置換基の種類は特に限定されず、例えば、ヒドロキシ基、アルコキシ基、エステル基、シアノ基、ニトロ基、スルホ基、カルボキシ基、アリール基、ハロゲン原子（例えばフッ素原子、塩素原子、臭素原子、ヨウ素原子）等が挙げられ、ヒドロキシ基であることが特に好ましい。
　式（４）において、反応性官能基であるＡは、例えば、エポキシ基、カルボキシ基、アミノ基、水酸基、エステル基等を挙げることができ、後記するゲスト分子との反応性が高いという点で、エポキシ基であることが好ましい。
　ポリシロキサン骨格において、前記式（２）で表される構成単位の含有割合は、前記式（２）、（３）及び（４）で表される構成単位の全量に対して、例えば、５～９５モル％とすることができる。高分子材料の吸湿性を制御しやすく、また、後記する自己修復性能が発揮されやすいという観点から、前記式（２）で表される構成単位の含有割合は、例えば、前記式（２）、（３）及び（４）で表される構成単位の全量に対して、２０モル％以上が好ましく、３０モル％以上がより好ましく、４０モル％以上が特に好ましく、また、９０モル％以下が好ましく、８０モル％以下がより好ましく、７５モル％以下が特に好ましい。
　ポリシロキサン骨格において、前記式（３）で表される構成単位の含有割合は、前記式（３）及び（４）で表される構成単位の全量に対して、例えば、０．０１～３０モル％とすることができる。高分子材料の吸湿性を制御しやすく、また、後記する自己修復性能が発揮されやすいという観点から、前記式（３）で表される構成単位の含有割合は、前記式（３）及び（４）で表される構成単位の全量に対して、０．１モル％以上が好ましく、０．５モル％以上がより好ましく、１モル％以上が特に好ましく、また、２０モル％以下が好ましく、１５モル％以下がより好ましく、１０モル％以下が特に好ましい。
　本発明の高分子材料において、ポリシロキサン骨格は必要に応じて、前記式（２）、（３）及び（４）で表される構成単位以外に他の構成単位を有することができる。つまり、本発明の高分子材料は、前記式（２）、（３）及び（４）で表される構成単位と、これら以外構成単位を有する分子鎖で形成され得る。他の構成単位は、例えば、前記式（２）、（３）及び（４）で表される構成単位の全量に対して５質量％以下、好ましくは１質量％以下、より好ましくは、０．１質量％以下、特に好ましくは０．０５質量％以下とすることができる。ポリシロキサン骨格は、前記式（２）、（３）及び（４）で表される構成単位のみで形成することもできる。つまり、本発明の高分子材料は、前記式（２）、（３）及び（４）で表される構成単位のみを有する分子鎖で形成することもできる。
　本発明の高分子材料において、ポリシロキサン骨格は、ランダムポリマー、ブロックポリマー等のいずれの構造を有していてもよく、例えば、製造が容易である点で、ランダムポリマーであることが好ましい。
　高分子材料は、ポリシロキサン骨格の側鎖に式（１）で表される構成単位を有することで親水性が向上するので、従来のシリコン材料に比べて同等もしくはそれ以上の優れた吸湿性を有することができる。従って、高分子材料は、ポリシロキサン骨格を有しながらも、優れた吸湿性を有することができ、しかも、ポリシロキサン骨格の特長である柔軟性及び強靭性も備えるので、機械特性にも優れる。
　本発明の高分子材料において、前記ホスト基は、ゲスト基を包接して包接錯体を形成すると共に、包接された前記ゲスト基は、前記ポリシロキサン骨格の側鎖に化学結合（例えば、共有結合）していてもよい。
　ゲスト基は、ゲスト分子に由来する基であり、具体的には、ゲスト分子から、１個又は２個の水素原子が除されて形成される基である。ゲスト分子としては、前記ホスト基と包接錯体を形成することが可能な化合物を挙げることができる。
　ゲスト分子としては、前記ホスト基と包接錯体を形成することできる限りは特に限定されず、例えば、１又は２個（好ましくは１個）のアミノ基を有する化合物、１又は２個（好ましくは１個）の水酸基を有する化合物、１又は２個（好ましくは１個）のカルボキシ基を有する化合物、１又は２個（好ましくは１個）のエポキシ基を有する化合物、１又は２個（好ましくは１個）のイソシアネート基を有する化合物、１又は２個（好ましくは１個）のチオール基を有する化合物、１又は２個のカルボン酸塩化物を有する化合物を挙げることができる。
　１又は２個のアミノ基を有する化合物としては、例えば、１－アダマンタンアミン、ベンジルアミン、ｔｅｒｔ－ブチルアミン、ブチルアミン、１－アミノピレン、アミノフェロセン、４－アミノアゾベンゼン、４－アミノスチルベン、シクロヘキシルアミン、ヘキシルアミン、４，４’－ジアミノジフェニルメタン、ｐ－キシリレンジアミン、ジアミノフェロセン、４，４’－ジアミノアゾベンゼン、４，４’－ジアミノスチルベン、１，４－ジアミノシクロヘキサン、１，６－ジアミノシクロヘキサン、α、ω－ジアミノポリエチレングルコール、α、ω－ジアミノポリプロピレングルコール、２，２－ビス（４－アミノフェニル）プロパン１，１－ビス（４－アミノフェニル）－１－フェニルエタン、２、２－ビス（４-アミノフェニル）ヘキサフルオロプロパン、２、２－ビス（４-アミノフェニル）ブタン、ビス（４－アミノフェニル）ジフェニルメタン、２、２－ビス（３－メチル－４－アミノフェニル）プロパン、ビス（４－アミノフェニル）－２、２－ジクロロエチレン、１、１－ビス（４－アミノフェニル）エタン、２，２－ビス（４－アミノ－３－イソプロピルフェニル）プロパン、１，３－ビス（２－（４－アミノフェニル）－２－プロピル）ベンゼン、ビス（４－アミノフェニル）スルホン、１，４－ビス（２－（４－アミノフェニル）－２－プロピル）ベンゼン、５，５’－（１－メチルエチリデン）－ビス［１，１’－（ビスフェニル）－２－アミン］プロパン、１，１－ビス（４－アミノフェニル）－３，３，５－トリメチルシクロヘキサン、１，１－ビス（４－アミノフェニル）シクロヘキサン等を挙げることができる。
　１又は２個の水酸基を有する化合物としては、例えば、１－ヒドロキシアダマンタン、ベンジルアルコール、ｔｅｒｔ－ブチルアルコール、ブチルアルコール、１－ヒドロキシピレン、１－ヒドロキシメチルフェロセン、４－ヒドロキシアゾベンゼン、４－ヒドロキシスチルベン、シクロヘキサノール、ヘキサノール、４，４’－ジヒドロキシジフェニルメタン、２,２-ビス（４－ヒドロキシフェニル）プロパン、１，４－ベンゼンジメタノール、１，１’－ジヒドロキシメチルフェロセン、４，４’－ジヒドロキシアゾベンゼン、４，４’－ジヒドロキシスチルベン、１，４－シクロヘキノール、１，６－ヘキサンジオール、ポリエチレングルコール、ポリプロピレングルコール、１,１－ビス（４-ヒドロキシフェニル）－１－フェニルエタン、２、２－ビス（４－ヒドロキシフェニル）ヘキサフルオロプロパン、２、２－ビス（４－ヒドロキシフェニル）ブタン、ビス（４－ヒドロキシフェニル）ジフェニルメタン、２、２－ビス（３－メチル－４－ヒドロキシフェニル）プロパン、ビス（４－ヒドロキシフェニル）－２、２－ジクロロエチレン、１、１－ビス（４－ヒドロキシフェニル）エタン、２，２－ビス（４－ヒドロキシ－３－イソプロピルフェニル）プロパン、１，３－ビス（２－（４－ヒドロキシフェニル）－２－プロピル）ベンゼン、ビス（４－ヒドロキシフェニル）スルホン、１，４－ビス（２－（４－ヒドロキシフェニル）－２－プロピル）ベンゼン、５，５’－（１－メチルエチリデン）－ビス［１，１’－（ビスフェニル）－２－ヒドロキシ］プロパン、１，１－ビス（４－ヒドロキシフェニル）－３，３，５－トリメチルシクロヘキサン、１，１－ビス（４－ヒドロキシフェニル）シクロヘキサン、ビスフェノールＡ等を挙げることができる。
　１又は２個のカルボキシ基を有する化合物としては、例えば、１－カルボキシアダマンタン、安息香酸、ピバル酸、ブタン酸、１－カルボキシピレン、１－カルボキシフェロセン、４－カルボキシアゾベンゼン、４－カルボキシスチルベン、シクロヘキサン酸、ヘキサン酸、４，４’－ジカルボキシジフェニルメタン、１，４－ベンゼンジカルボン酸、１，４－フェニレン二酢酸、１，１’－ジカルボキシフェロセン、４，４’－ジカルボキシアゾベンゼン、４，４’－ジカルボキシスチルベン、１，４－シクロヘキサンジカルボン酸、１，６－ヘキサンジカルボン酸、α、ω－ジカルボキシポリエチレングルコール、α、ω－ジカルボキシポリプロピレングルコール、２，２－ビス（４－カルボキシフェニル）プロパン、１，１－ビス（４－カルボキシフェニル）－１－フェニルエタン、２、２－ビス（４-カルボキシフェニル）ヘキサフルオロプロパン、２、２－ビス（４-カルボキシフェニル）ブタン、ビス（４－カルボキシフェニル）ジフェニルメタン、２、２－ビス（３－メチル－４－カルボキシフェニル）プロパン、ビス（４－カルボキシフェニル）－２、２－ジクロロエチレン、１、１－ビス（４－カルボキシフェニル）エタン、２，２－ビス（４－カルボキシ３－イソプロピルフェニル）プロパン、１，３－ビス（２－（４－カルボキシフェニル）－２－プロピル）ベンゼン、ビス（４－カルボキシフェニル）スルホン、１，４－ビス（２－（４－カルボキシフェニル）－２－プロピル）ベンゼン、５，５’－（１－メチルエチリデン）－ビス［１，１’－（ビスフェニル）－２－カルボキシ］プロパン、１，１－ビス（４－カルボキシフェニル）－３，３，５－トリメチルシクロヘキサン、１，１－ビス（４－カルボキシフェニル）シクロヘキサン等を挙げることができる。
　１又は２個のカルボン酸塩化物を有する化合物としては、例えば、１－アダマンタンカルボニルクロリド、テレフタロイルクロリド、トリメチルアセチルクロリド、ブチリルクロリド、１－ピレンカルボニルクロリド、１－フェロセンカルボニルクロリド、４－アゾベンゼンカルボニルクロリド、４－スチルベンカルボニルクロリド、シクロヘキサンカルボニルクロリド、ヘキシルクロリド、４，４’－ジフェニルメタンジカルボニルクロリド、１，４－ベンゼンジカルボンニルクロリド、１，４－フェニレンジカルボニルクロリド、１，１’－フェロセンジカルボニルクロリド、４，４’－アゾベンゼンジカルボニルクロリド、４，４’－スチルベンカルボニルクロリド、１，４－シクロヘキサンジカルボニルクロリド、１，６－ヘキサンジカルボニルクロリド、α、ω－ポリエチレングルコールジカルボニルクロリド、α、ω－ポリプロピレングルコールジカルボニルクロリド、２，２－ビス（４－フェニルカルボニルクロリド）プロパン、１，１－ビス（４－フェニルカルボニルクロリド）－１－フェニルエタン、２、２－ビス（４－フェニルカルボニルクロリド）ヘキサフルオロプロパン、２、２－ビス（４－フェニルカルボニルクロリド）ブタン、ビス（４－フェニルカルボニルクロリド）ジフェニルメタン、２、２－ビス（３－メチル－４－フェニルカルボニルクロリド）プロパン、ビス（４－フェニルカルボニルクロリド）－２、２－ジクロロエチレン、１、１－ビス（４－フェニルカルボニルクロリド）エタン、２，２－ビス（３－イソプロピルフェニル－４－カルボニルクロリド）プロパン、１，３－ビス（２－（４－フェニルカルボニルクロリド）－２－プロピル）ベンゼン、ビス（４－フェニルカルボニルクロリド）スルホン、１，４－ビス（２－（４－フェニルカルボニルクロリド）－２－プロピル）ベンゼン、５，５’－（１－メチルエチリデン）－ビス［１，１’－（ビスフェニル）－２－カルボニルクロリド］プロパン、１，１－ビス（４－フェニルカルボニルクロリド）－３，３，５－トリメチルシクロヘキサン、１，１－ビス（４－フェニルカルボニルクロリド）シクロヘキサン等を挙げることができる。
　１又は２個のエポキシ基を有する化合物としては、例えば、アダマンタンオキシド、スチレンオキシド、１，２－エポキシブタン、１－エポキシピレン、エポキシフェロセン、４－エポキシアゾベンゼン、４－エポキシスチルベン、シクロヘキシルオキシド、１，２－エポキシヘキサン、２，２’－ビス（４－グリシジルオキシフェニル）プロパン、ｐ－ジグリシジルオキシベンゼン、ジグリシジルオキイシフェロセン、４，４’－ジグリシジルオキシアゾベンゼン、４，４’－ジグリシジルオキシフェロセン、１，４－ジグリシジルオキシシクロヘキサン、１，６－ジグリシジルオキシシクロヘキサン、α、ω－ジグリシジルオキシポリエチレングルコール、α、ω－ジグリシジルオキシポリプロピレングルコール、１，１－ビス（４－グリシジルオキシフェニル）－１－フェニルエタン、２、２－ビス（４－グリシジルオキシフェニル）ヘキサフルオロプロパン、２、２－ビス（４－グリシジルオキシフェニル）ブタン、ビス（４－グリシジルオキシフェニル）ジフェニルメタン、２、２－ビス（３－メチル－４－グリシジルオキシフェニル）プロパン、ビス（４－グリシジルオキシフェニル）－２、２－ジクロロエチレン、１、１－ビス（４－グリシジルオキシフェニル）エタン、２，２－ビス（４－グリシジルオキシ－３－イソプロピルフェニル）プロパン、１，３－ビス（２－（４－グリシジルオキシフェニル）－２－プロピル）ベンゼン、ビス（４－グリシジルオキシフェニル）スルホン、１，４－ビス（２－（４－グリシジルオキシフェニル）－２－プロピル）ベンゼン、５，５’－（１－メチルエチリデン）－ビス［１，１’－（ビスフェニル）－２－グリシジルオキシ］プロパン、１，１－ビス（４－グリシジルオキシフェニル）－３，３，５－トリメチルシクロヘキサン、１，１－ビス（４－グリシジルオキシフェニル）シクロヘキサン等を挙げることができる。
　１又は２個のイソシアネート基を有する化合物としては、例えば、１－アダマンタンイソシアネート、ベンジルイソシアネート、フェニルイソシアネート、ｔｅｒｔ－ブチルイソシアネート、ブチルイソシアネート、１－ピレンイソシアネート、フェロセンイソシアネート、アゾベンゼン－４－イソシアネート、スチルベン－４－イソシアネート、シクロヘキサンイソシアネート、ヘキサンイソシアネート、４，４’－ジイソシアネートフェニルメタン、ｐ－ベンゼンジイソシアネート、フェロセン－１，１’－ジイソシアネート、アゾベンゼン－４，４’－ジイソシアネート、スチルベン－４，４’－ジイソシアネート、シクロヘキサン－１，４－ジイソシアネート、シクロヘキサン－１，６－ジイソシアネート、ポリエチレングルコールジイソシアネート、ポリプロピレングルコールジイソシアネート、２，２－ビス（４－フェニルイソシアネート）プロパン、１，１－ビス（４－フェニルイソシアネート）－１－フェニルエタン、２、２－ビス（４－フェニルイソシアネート）ヘキサフルオロプロパン、２、２－ビス（４－フェニルイソシアネート）ブタン、ビス（４－フェニルイソシアネート）ジフェニルメタン、２、２－ビス（３－メチル－４－フェニルイソシアネート）プロパン、ビス（４－フェニルイソシアネート）－２、２－ジクロロエチレン、１、１－ビス（４－フェニルイソシアネート）エタン、２，２－ビス（３－イソプロピル－４－フェニルイソシアネート）プロパン、１，３－ビス（２－（４－フェニルイソシアネート）－２－プロピル）ベンゼン、ビス（４－フェニルイソシアネート）スルホン、１，４－ビス（２－（４－フェニルイソシアネート）－２－プロピル）ベンゼン、５，５’－（１－メチルエチリデン）－ビス［１，１’－（ビスフェニル）－２－イソシアネート］プロパン、１，１－ビス（４－フェニルイソシアネート）－３，３，５－トリメチルシクロヘキサン、１，１－ビス（４－フェニルイソシアネート）シクロヘキサン等を挙げることができる。
　１又は２個のチオール基を有する化合物としては、例えば、１－アダマンタンチオール、ベンジルチオール、ｔｅｒｔ－メルカプタン、ブタンチオール、１－チオールピレン、フェロセンチオール、４－チオアゾベンゼン、４－チオスチルベン、シクロヘキシルチオール、ヘキサンチオール、４，４’－ジチオフェニルメタン、ｐ－ベンゼンジチオール、１，１’－ジチオフェロセン、４，４’－ジチオアゾベンゼン、４，４’－ジチオスチルベン、１，４－ジチオシクロヘキサン、１，６－ジチオシクロヘキサン、α、ω－ジチオポリエチレングルコール、α、ω－ジチオポリプロピレングルコール、１，１－ビス（４－チオフェニル）－１－フェニルエタン、２、２－ビス（４－チオフェニル）ヘキサフルオロプロパン、２、２－ビス（４－チオフェニル）ブタン、ビス（４－チオフェニル）ジフェニルメタン、２、２－ビス（３－メチル－４－チオフェニル）プロパン、ビス（４－チオフェニル）－２、２－ジクロロエチレン、１、１－ビス（４－チオフェニル）エタン、２，２－ビス（４－チオ３－イソプロピルフェニル）プロパン、１，３－ビス（２－（４－チオフェニル）－２－プロピル）ベンゼン、ビス（４－チオフェニル）スルホン、１，４－ビス（２－（４－チオフェニル）－２－プロピル）ベンゼン、５，５’－（１－メチルエチリデン）－ビス［１，１’－（ビスフェニル）－２－チオール］プロパン、１，１－ビス（４－チオフェニル）－３，３，５－トリメチルシクロヘキサン、１，１－ビス（４－チオフェニル）シクロヘキサン等を挙げることができる。
　ゲスト分子としては、１個のアミノ基を有する化合物及び１個の水酸基を有する化合物の少なくともいずれか一方であることが好ましく、１個のアミノ基を有する化合物であることがさらに好ましい。具体的にゲスト分子としては、１－アダマンタンアミン、ベンジルアミン、ｔｅｒｔ－ブチルアミン、ブチルアミン、１－アミノピレン、アミノフェロセン、４－アミノアゾベンゼン、４－アミノスチルベン、シクロヘキシルアミン、ヘキシルアミン、１－ヒドロキシアダマンタン、ベンジルアルコール、ｔｅｒｔ－ブチルアルコール、ブチルアルコール、１－ヒドロキシピレン、１－ヒドロキシメチルフェロセン、４－ヒドロキシアゾベンゼン及び４－ヒドロキシスチルベン等であることが好ましく、１－アダマンタンアミン及び１－ヒドロキシアダマンタン等であることがさらに好ましく、１－アダマンタンアミンであることが特に好ましい。この場合、ゲスト基はポリシロキサン骨格の側鎖に結合しやすく、自己修復性がより発揮されやすい。
　ゲスト分子は、ホスト基であるシクロデキストリン又はシクロデキストリン誘導体の環内の大きさに応じて適宜選択することができる。例えば、ゲスト分子が、１－アダマンタンアミン及び１－ヒドロキシアダマンタン等である場合、ホスト基はβ－シクロデキストリン又はβ－シクロデキストリン誘導体であることが好ましい。この場合、ゲスト基はホスト基に包接されやすい。
　本発明の高分子材料において、ホスト基に包接された前記ゲスト基は、前記ポリシロキサン骨格の側鎖に化学結合することができる。この場合、通常、ゲスト基とポリシロキサン骨格のＳｉとの間には他の官能基が介在する。他の官能基としては、例えば、前記式（３）中のＲ６が挙げられる。
　また、ポリシロキサン骨格が前記式（４）で表される構成単位を有する場合、ホスト基に包接されたゲスト分子は式（４）で表される構成単位中の反応性官能基と反応することで、ゲスト基がポリシロキサン骨格に結合した構造が形成され得る。
　本発明の高分子材料において、ゲスト基が結合するポリシロキサン分子鎖（ポリロタキサン骨格を有する分子鎖）は、該ゲスト基を包接しているホスト基が結合しているポリシロキサン分子鎖であってもよいし、該ゲスト基を包接しているホスト基が結合しているポリシロキサン分子鎖と異なるポリシロキサン分子鎖であってもよい。
　ポリシロキサン骨格の側鎖のホスト基がゲスト基を包接する場合、その包接割合は特に限定されず、例えば、ポリシロキサン骨格におけるホスト基の全量の内の１０モル％以上包接することができ、２０モル％以上であることが好ましく、３０モル％以上であることがより好ましく、４０モル％以上であることがさらに好ましく、５０モル％以上であることが特に好ましい。
　高分子材料は、ポリシロキサン骨格の側鎖に式（１）で表される構成単位を有することで（具体的には、前記式（３）で表される構成単位を有することで）、種々の高分子構造を形成することが可能となり、その一つが、上述のゲスト基導入によって形成される構造である。ポリシロキサン骨格において、上述のようにゲスト基がホスト基に包接されると共にゲスト基がポリシロキサン骨格に結合することで、高分子材料は分子内又は分子間で可逆的なホスト－ゲスト相互作用が生じ得る（後記する図１参照）。これにより、斯かるポリシロキサン骨格を含む高分子材料は、その靭性及び強度が向上し、しかも、自己修復性を発揮することが可能となる。例えば、高分子材料が切断されたとしても、切断面どうしを再接着等させることで、切断面間で再度、高分子材料どうしのホスト－ゲスト相互作用が生じて再結合し、高分子材料が修復される。つまり、高分子材料が特定の構造に制御された場合、切断された高分子材料が自己修復性を有することもできる。
　図１は、本発明の高分子材料において、ポリシロキサン骨格の側鎖のホスト基がゲスト基を包接して形成されている場合の形態を模式的に説明する図である。この形態では、高分子材料は、架橋構造、つまり、三次元網目構造を有する。
　図１の形態の高分子材料では、ゲスト基２０は、ポリシロキサン骨格３０の側鎖に結合している。より具体的には、ゲスト基２０は、ホスト基１０に包接されて包接錯体を形成し、ゲスト基２０の一端がポリシロキサン骨格３０に結合している。さらに、ホスト基１０に結合しているＲ１を含む基４０がポリシロキサン骨格３０の側鎖に結合している。つまり、図１の形態の高分子材料は、前記式（１）で表されるＲＨ－Ｒ１－がポリシロキサン骨格３０に結合している。図１の形態の高分子材料は、例えば、エラストマーとしての性質を有する。
　図１の高分子材料では、高分子材料にせん断等の力が加わると、高分子鎖中のゲスト基２０と、ホスト基ＲＨとが分離し、材料の切断等が起こることがある。しかし、切断面を再度接着させることで、再びゲスト基２０と、ホスト基ＲＨとが結合して、包接錯体が形成され得る。これにより、切断面が再結合し、高分子材料が修復され得る。
　図２は、本発明の高分子材料の別の態様を模式的に示している。図２の形態の高分子材料は、前記ホスト基の環内をポリシロキサンが貫通した構造を有する。ホスト基の環内を貫通するポリシロキサンは、ホスト基を有するポリシロキサンであってもよいし、あるいは、ホスト基を有さないポリシロキサン（例えば、ポリジメチルシロキサン等）であってもよい。
　図２の形態の高分子材料は、架橋構造、つまり、三次元網目構造を有すると共に、ポリシロキサン骨格３０がホスト基１０の環内を貫通した構造を有する。
　図２の形態の高分子材料では、図１の形態の高分子材料と同様、ホスト基１０に結合しているＲ１がポリシロキサン骨格３０に結合している。この高分子材料では、ホスト基１０がポリシロキサン骨格３０を包接しながらスライドすることができることから、例えば、応力緩和作用等に優れ、高い靭性及び強度を有し得ることから、機械的特性に優れる。
　高分子材料が図２の形態であるか否かについては、例えば、高分子材料の膨潤試験の結果から判定することができる。例えば、高分子材料を、化学架橋剤を使用せずに調製し、得られた高分子材料を溶媒に加えた場合において、溶解せずに膨潤現象が見られた場合を図２の形態（いわゆる可動性架橋重合体）が形成されていると判断でき、溶解した場合を可動性架橋重合体が形成されていないと判断できる。
　本発明において、高分子材料の形状は特に限定されない。例えば、高分子材料は、膜状、フィルム状、シート状、粒子状、板状、ブロック状、ペレット状、粉末状、発泡材料状、液状等の各種の形態を取り得る。
　高分子材料は、各種の用途に使用することができる。例えば、高分子材料は、自動車用途、接着用途、電子部品用途、建築部材用途、食品容器用途、輸送容器用途等の各種の部材に好適に使用することができる。特に、高分子材料は、吸湿性が高いので、衣料、医療機器、医療器具（具体的にはコンタクトレンズなど）等の用途にも使用できる。
　２．高分子材料の製造方法
　前記した高分子材料の製造方法は特に限定されない。例えば、前述の本発明の高分子材料は、下記一般式（１ａ）
Ｒ２－ＲＨ　　　（１ａ）
で表される化合物にゲスト分子が包接されてなる包接化合物と、
側鎖に反応性官能基を有するポリシロキサンと、
を反応する工程を備えることができる。
　ここで、式（１ａ）中、Ｒ２はＮＨ２又はＯＨを示し、ＲＨは前記式（１）中のＲＨと同義である。つまり、ＲＨは前記ホスト基である。上記製造方法における工程を「工程１」と表記する。
　前記式（１ａ）で表される化合物の具体例としては、下記式（２１）で表される化合物を挙げることができる。
Figure JPOXMLDOC01-appb-C000004
　式（２１）において、Ｒ２は、前記式（１ａ）のＲ２に等しい、つまり、ＮＨ２又はＯＨを示し、式（２１）式中のＲ５は前記炭化水素基等を示し、ｎは５、６又は７である。
　なお、式（２１）において、Ｒ５（炭化水素基等）のすべてがメチル基、アセチル基、メチルカルバメート基及びエチルカルバメート基からなる群より選ばれる１種である場合もある。式（２１）において、すべてのＲ５はメチル基又はアセチル基であることが好ましく、すべてのＲ５はメチル基であることが特に好ましい。
　式（２１）で表される化合物としては、６－モノデオキシ－６－モノアミノ－トリメチル－シクロデキストリン、６－モノヒドロキシ－トリメチル－シクロデキストリン、６－モノデオキシ－６－モノアミノ－トリアセチル－シクロデキストリン、６－モノヒドロキシ－トリアセチル－シクロデキストリン、６－モノデオキシ－６－モノアミノ－トリエチルカルバメート－シクロデキストリン、６－モノヒドロキシ－トリエチルカルバメート－シクロデキストリン等を挙げることができる。
　包接化合物におけるゲスト分子の種類は、前述の「１．高分子材料」の項で説明したゲスト基を形成するための前記ゲスト分子と同様である。
　工程１で使用する包接化合物の製造方法も特に限定されず、公知の包接化合物の製造方法を広く採用することができる、例えば、式（１ａ）で表される化合物と、ゲスト分子とを混合して、包接化合物を得る工程を備える方法によって製造することができる。
　包接化合物を得る工程において、式（１ａ）で表される化合物と、ゲスト分子との混合比は、例えば、モル比で、式（１ａ）で表される化合物：ゲスト分子＝１０：１～１：１０とすることができ、好ましくは３：１～１：３とすることができ、より好ましくは、２：１～１：２とすることができる。式（１ａ）で表される化合物：ゲスト分子は１：１（モル比）とすることもできる。
　工程１で使用する側鎖に反応性官能基を有するポリシロキサンの種類は特に限定されない。以下、工程１で使用する側鎖に反応性官能基を有するポリシロキサンを「ポリシロキサンＰ」と表記する。
　ポリシロキサンＰは、側鎖に反応性官能基を有する限り、その種類は特に限定されず、例えば、公知のポリシロキサンを広く使用することができる。反応性官能基は、前記式（４）における反応性官能基Ａと同様である。つまり、反応性官能基は、例えば、エポキシ基、カルボキシ基、アミノ基、水酸基、エステル基等を挙げることができ、包接化合物の反応性が高いという点で、エポキシ基であることが好ましい。
　ポリシロキサンＰは、前記式（２）で表される構成単位及び前記式（４）で表される構成単位を有することが好ましい。この場合、ポリシロキサンＰは、ランダムポリマー、ブロックポリマー等のいずれの構造を有していてもよく、例えば、製造が容易である点で、ランダムポリマーであることが好ましい。
　ポリシロキサンＰが前記式（２）で表される構成単位及び前記式（４）で表される構成単位を有する場合、前記式（２）で表される構成単位の含有割合は、前記式（２）及び（４）で表される構成単位の全量に対して、例えば、５～９５モル％とすることができる。高分子材料の吸湿性を制御しやすく、また、自己修復性能が発揮されやすいという観点から、前記式（２）で表される構成単位の含有割合は、例えば、前記式（２）及び（４）で表される構成単位の全量に対して、２０モル％以上が好ましく、３０モル％以上がより好ましく、４０モル％以上が特に好ましく、また、９０モル％以下が好ましく、８０モル％以下がより好ましく、７５モル％以下が特に好ましい。
　ポリシロキサンＰの数平均分子量Ｍｎは特に限定されず、例えば、５００～１０００００とすることができ、好ましくは１０００～５００００である。
　ポリシロキサンＰの製造方法は特に限定されず、例えば、公知の製造方法で得ることができ、また、市販品から入手することも可能である。
　工程１において、前記包接化合物と、側鎖に反応性官能基を有するポリシロキサンとを反応する方法は特に限定されない。例えば、前記一般式（１ａ）で表される化合物と、ゲスト分子と、ポリシロキサンＰとを所定の混合割合で混合させる方法を挙げることができる。この混合は、例えば、適宜の溶媒中で行うことができる。溶媒の種類は特に限定されず、例えば、ヘキサン、ヘプタン等の脂肪族炭化水素；シクロヘキサン等の脂環式炭化水素；ベンゼン、トルエンおよびキシレン等の芳香族炭化水素；クロロホルム、１，２－ジクロロエタン等の塩素系炭化水素；メタノール、エタノール、イソプロピルアルコールおよびｔ－ブタノール等のアルコール等が挙げられる。溶媒は、単独又は２種以上の混合物として使用することができる。工程１の反応温度も特に限定されず、例えば、１０～２００℃、好ましくは５０～１５０℃、より好ましくは８０～１２０℃とすることができる。
　工程１の反応後、必要に応じて乾燥等の処理をすることで、目的のポリシロキサン骨格を有する高分子材料を得ることができる。斯かる方法で得られる高分子材料は、例えば、前述の図１に示す構造を有するものであり、エラストマーとしての性質を有する。
　また、前述の図２の形態の高分子材料を製造する場合は、前記式（１ａ）で表される化合物と、前記ポリシロキサンＰとを混合する工程（以下、「工程２」という）を含む製造方法を採用することができる。この製造方法における工程２では、ゲスト分子を使用しないことを除いては、前述の工程１と同様の条件とすることができる。工程２の混合では必要に応じて、前記ポリシロキサンＰ以外のポリシロキサン（つまり、側鎖に反応性官能基Ａを有さないポリシロキサン）を使用することができ、ポリシロキサンＰ以外のポリシロキサン（例えばジメチルポリシロキサン）を使用することが好ましい。
　ここで、前記式（１ａ）で表される化合物を製造する方法は特に限定されず、公知の製造方法を広く採用することができる。例えば、前記式（１ａ）で表される化合物は、国際公開第２０１８／１５９７９１号に記載のホスト基含有重合性単量体の製造方法（具体的には、ホスト基含有ビニル系単量体の製造方法又はホスト基含有非ビニル系単量体の製造方法）と同様の製造方法を採用することができる。
　以下、実施例により本発明をより具体的に説明するが、本発明はこれら実施例の態様に限定されるものではない。
　　（製造例１）
　まず、下記式（２１－１）のスキームに従って、ＮＨ２－ＰＭβＣＤを製造した。
Figure JPOXMLDOC01-appb-C000005
　原料のホスト分子の原料として、６－デオキシ－６－モノアジド－β－シクロデキストリン６．９ｍｍｏｌをナスフラスコに加え、さらに、脱水Ｎ，Ｎ－ジメチルホルムアミド５００ｍＬを加え、氷冷下で撹拌し、さらにそこへ水素化ナトリウム１５０ｍｍｏｌ、ヨウ化メチル１５０ｍｍｏｌを加え、１２時間撹拌した。その後、そのナスフラスコにメタノール２０ｍＬを加え、更に水２０ｍＬを加えてクエンチした。得られた溶液をエバポレーターで減圧乾燥後、ジクロロメタン１００ｍＬを加え、飽和炭酸水素ナトリウム水溶液５０ｍＬ、チオ硫酸ナトリウム五水和物を２．５ｇ含む５０ｍＬ水溶液、飽和食塩水５０ｍＬで洗浄した。
　洗浄後のジクロロメタン層に硫酸マグネシウムを１０ｇ加え、室温で撹拌した後にろ過し、そのろ液をエバポレーターで乾固した。得られた固形物をテトラヒドロフラン１００ｍＬに溶解し、トリフェニルホスフィン１５ｍｍｏｌと２８％アンモニア水３０ｍＬを加えて、室温にて１２時間撹拌した。次いで、エバポレーターで減圧乾燥後、得られた乾燥物をジクロロメタン１００ｍＬに溶解し、水１００ｍＬ、飽和食塩水１００ｍＬで洗浄した。
　洗浄後のジクロロメタン層に硫酸マグネシウムを１０ｇ加え、室温で撹拌した後にろ過し、そのろ液をエバポレーターで乾固した。得られた固形物をシリカカラムクロマトグラフィー（溶出液組成ジクロロメタン：メタノール＝９：１）により精製した。このホスト基含有重合性単量体をＮＨ２－ＰＭβＣＤと表記した
　図３（ａ）及び（ｂ）はそれぞれ、ＮＨ２－ＰＭβＣＤのマススペクトル及び、ＮＭＲスペクトルの結果を示す。これらの結果から、目的のＮＨ２－ＰＭβＣＤが生成していることを確認した。ＮＨ２－ＰＭβＣＤは、ホスト分子の原料１分子中に存在していた全水酸基数のうちの１００％（つまり、Ｎ－１個＝２０個）がメチル基に置換されていることがわかった。
　（実施例１）
　図４に示す反応スキームに従って、高分子材料を合成した。まず、側鎖に反応性官能基を有するポリシロキサンＰとして、信越シリコーン社性「エポキシ変性シリコーンＫＦ－１０１」（分子量約１６００、エポキシ導入率は約３３モル％）を準備した。このポリシロキサンＰを３６０ｍｇと、製造例１で得たＮＨ２－ＰＭβＣＤを７２ｍｇと、１－アダマンタンアミン（ゲスト分子）７．７ｍｇとをサンプルビンに入れ、トルエン４００μＬを加えて混合した。この混合では、ポリシロキサンＰのエポキシ基の全モル数に対して、ＮＨ２－ＰＭβＣＤのモル数及び１－アダマンタンアミンがいずれも５モル％となるように各配合量が調節された。前記混合により、均一溶液が得られ、その後、１００℃の油浴で６時間加熱すると粘性が上がった黄色透明オイルが得られた。これを２晩６０℃で減圧乾燥させることで高分子材料を得た。
　図５は、実施例１で得られた高分子材料の１Ｈ－ＮＭＲスペクトル（ＣＤＣｌ３、５００ＭＨｚ、２５℃）である。この１Ｈ－ＮＭＲスペクトルから、目的の高分子材料が合成されていることを確認した。
　（実施例２）
　ポリシロキサンＰのエポキシ基の全モル数に対して、ＮＨ２－ＰＭβＣＤのモル数及び１－アダマンタンアミンがいずれも３モル％となるように各配合量を調節したこと以外は実施例１と同様の方法で高分子材料を得た。
　（比較例１）
　ポリシロキサンＰとして、信越シリコーン社性「エポキシ変性シリコーンＫＦ－１０１」（分子量約１６００、エポキシ導入率は約３３モル％）を１．８ｇ（５．１ｍｍｏｌ、１ｅｑ．）、エチレンジアミン（ＥＤＡ）を１７μＬ（０．２５ｍｍｏｌ、０．０５ｅｑ．)をサンプルビンに入れ、トルエン２．０ｍＬを加え混合した。この混合では、ポリシロキサンＰのエポキシ基の全モル数に対して、ＥＤＡのモル数が５モル％となるように各配合量が調節された。前記混合により、均一溶液を得た後、１００℃の油浴で１７時間加熱した後、２晩にわたって６０℃で減圧乾燥させることで高分子材料を得た。
　（引張り試験）
　実施例及び比較例で得られた高分子材料（厚み１ｍｍ）について、「ストローク－試験力曲線」試験（島津製作所社製「ＡＵＴＯＧＲＡＰＨ」（型番：ＡＧＸ－ｐｌｕｓ）を行い、得られた破断応力曲線（応力－歪曲線）から高分子材料の破断点（破断ひずみ）を観測した。また、この破断点を終点として、終点までの最大応力を高分子材料の破断応力とした。また、応力－歪曲線から、高分子材料の破壊エネルギーを算出した。この引張り試験は、高分子材料の下端を固定し上端を引張り速度０．１～１ｍｍ／ｍｉｎで稼動させるアップ方式で実施した。
　なお、「ストローク－試験力曲線」試験において、破断応力及び破断歪（単に歪ともいう）の一方又は両方が高い値を示す材料は、高分子材料の靭性及び強度が優れると判断できる。特に、破断応力及び破断歪（単に歪ともいう）の両方が高い値を示す材料は、破壊エネルギーが優れる材料であると判断できる。
　引張り試験の結果、実施例１で得られた高分子材料は、破断応力が３０ｋＰａ、破断ひずみが２８％、ヤング率が１２０ｋＰａであり、また、破壊エネルギーは５．５Ｊｍ２であり、従来の高分子材料に比べて靭性及び強度が優れる材料であった。また、実施例２で得られた高分子材料は、破断応力が１９ｋＰａ、破断ひずみが７７％、ヤング率が３６ｋＰａであり、また、破壊エネルギーは８．７Ｊｍ２であり、従来の高分子材料に比べて靭性及び強度が優れる材料であった。これに対し、比較例１で得られた高分子材料（化学架橋構造体）は、そもそも引張り試験用サンプルを作製できないほど脆い材料であり、明らかに靭性及び強度を有していない材料であった。比較例１で得られた高分子材料は、実施例１のようなホスト－ゲスト相互作用により架橋構造は有しておらず、従来の化学架橋構造を有するものであるので、ポリシロキサン骨格を有する高分子材料の機械特性を向上させる手段としては適していないといえる。
　（自己修復性評価）
　実施例１及び２で得られた高分子材料（厚み１ｍｍ）の中央部を切断して２つに分けた後、両者を常温（２５℃）で２４時間接触させたところ、いずれも再接着することが確認された。また、再接着後の破断応力は切断前の約３０％であり、自己修復によって、約３０％は回復することがわかった。
　（吸湿性評価）
　実施例１及び比較例１で得られた高分子材料をそれぞれサンプルビンに入れ、水６ｍＬに２０時間浸漬させた。その後、各エラストマーを取り出し、軽く表面の水をふき取った後で質量を測定し、水に浸漬する前後の質量変化から含水率を算出した。その結果、実施例１で得られた高分子材料の含水率は、８．７％、比較例１で得られた高分子材料の含水率は、０．４％であった。この結果から、実施例１で得られた高分子材料は、高い吸湿性を備えていることもわかった。

Claims (5)

  1. ポリシロキサン骨格を有する高分子材料であって、
    前記ポリシロキサン骨格は側鎖に下記一般式（１）
    －Ｒ１－ＲＨ　　　（１）
    （式（１）中、Ｒ１はＮＨ又はＯを示し、ＲＨはホスト基を示す。）
    で表される構成単位を有し、
    前記ホスト基は、シクロデキストリン又はシクロデキストリン誘導体から１個の水素原子又は水酸基が除された１価の基であり、
    前記シクロデキストリン誘導体は、シクロデキストリンが有する少なくとも１個の水酸基の水素原子が炭化水素基、アシル基及び－ＣＯＮＨＲ（Ｒはメチル基又はエチル基）からなる群より選ばれる少なくとも１種の基で置換された構造を有する、高分子材料。
  2. 前記ホスト基は、ゲスト基を包接して包接錯体を形成すると共に、包接された前記ゲスト基は、前記ポリシロキサン骨格の側鎖に化学結合している、請求項１に記載の高分子材料。
  3. 前記ホスト基の環内をポリシロキサンが貫通した構造を有する、請求項１に記載の高分子材料。
  4. 請求項１又は２に記載の高分子材料の製造方法であって、
    下記一般式（１ａ）
    Ｒ２－ＲＨ　　　（１ａ）
    （式（１ａ）中、Ｒ２はＮＨ２又はＯＨを示し、ＲＨは前記式（１）中のＲＨと同義である）
    で表される化合物にゲスト分子が包接されてなる包接化合物と、
    側鎖に反応性官能基を有するポリシロキサンと、
    を反応する工程を備える、高分子材料の製造方法。
  5. 前記反応性官能基はエポキシ基である、請求項４に記載の製造方法。
PCT/JP2020/033642 2019-09-05 2020-09-04 高分子材料及びその製造方法 WO2021045203A1 (ja)