WO2021000927A1 - Matériau thermo-isolant et ignifuge et son application - Google Patents

Matériau thermo-isolant et ignifuge et son application Download PDF

Info

Publication number
WO2021000927A1
WO2021000927A1 PCT/CN2020/100076 CN2020100076W WO2021000927A1 WO 2021000927 A1 WO2021000927 A1 WO 2021000927A1 CN 2020100076 W CN2020100076 W CN 2020100076W WO 2021000927 A1 WO2021000927 A1 WO 2021000927A1
Authority
WO
WIPO (PCT)
Prior art keywords
heat
insulating
layer
fire
fireproof
Prior art date
Application number
PCT/CN2020/100076
Other languages
English (en)
Chinese (zh)
Inventor
张尤娟
武庭轩
石彦芳
二宫有希
原田大
Original Assignee
东丽纤维研究所（中国）有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 东丽纤维研究所（中国）有限公司 filed Critical 东丽纤维研究所（中国）有限公司
Priority to CN202080044134.7A priority Critical patent/CN113939942A/zh
Publication of WO2021000927A1 publication Critical patent/WO2021000927A1/fr

Abstract

La présente invention concerne un matériau thermo-isolant et ignifuge et son application. Le matériau thermo-isolant et ignifuge contient au moins une couche d'isolation thermique. Un matériau poreux et des particules creuses sont contenus dans la couche d'isolation thermique, la densité volumique du matériau poreux est de 0,05 à 0,30 g/cm3, le diamètre moyen des particules creuses est de 30 à 1000 µm, et le coefficient de conductivité thermique du matériau thermo-isolant et ignifuge après traitement de carbonisation à température normale est de 0.040 W/(m•K) ou en dessous. Le matériau thermo-isolant et ignifuge de la présente invention présente les caractéristiques de bon caractère ignifugeant, d'une résistance à haute température, d'un faible coefficient de conductivité thermique, et est léger, et peut être appliqué entre des cellules de batterie d'une batterie d'alimentation.
PCT/CN2020/100076 2019-07-03 2020-07-03 Matériau thermo-isolant et ignifuge et son application WO2021000927A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
CN202080044134.7A CN113939942A (zh) 2019-07-03 2020-07-03 一种隔热防火材料及其用途

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
CN201910594449.8 2019-07-03
CN201910594449 2019-07-03
CN201910909245 2019-09-25
CN201910909245.9 2019-09-25

Publications (1)

Publication Number Publication Date
WO2021000927A1 true WO2021000927A1 (fr) 2021-01-07

Family

ID=74101202

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2020/100076 WO2021000927A1 (fr) 2019-07-03 2020-07-03 Matériau thermo-isolant et ignifuge et son application

Country Status (2)

Country Link
CN (1) CN113939942A (fr)
WO (1) WO2021000927A1 (fr)

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113025226A (zh) * 2021-03-22 2021-06-25 朗缪环保科技(天津)有限公司 气凝胶防火保温隔热涂料
CN113637233A (zh) * 2021-07-23 2021-11-12 浙江理工大学 一种全生物质节能防火用气凝胶的制备方法
CN113785431A (zh) * 2021-02-05 2021-12-10 气凝胶研发私人有限公司 用于电池的隔热装置
CN113858723A (zh) * 2021-09-29 2021-12-31 湖北三江航天红阳机电有限公司 一种梯度热防护层结构试板及其制备方法
CN114395336A (zh) * 2021-12-02 2022-04-26 广东航邦新材料科技有限公司 一种新型隔热防护材料及其生产工艺
CN114628844A (zh) * 2022-03-24 2022-06-14 广州小鹏汽车科技有限公司 电池箱、动力电池总成及车辆
CN114643762A (zh) * 2022-03-09 2022-06-21 苏州中纺学面料产业研究院 一种阻燃隔热面料的制备方法
WO2022199642A1 (fr) * 2021-03-25 2022-09-29 东丽纤维研究所（中国）有限公司 Feutre ignifuge
CN115180836A (zh) * 2022-07-11 2022-10-14 南通金鹏玻纤制品有限公司 一种阻燃玻纤布及其生产工艺
CN115799729A (zh) * 2023-02-01 2023-03-14 中创新航科技股份有限公司 电池组以及电池装置
CN116166073A (zh) * 2023-04-26 2023-05-26 深圳市博硕科技股份有限公司 具有学习功能的动力电池隔热棉裁切温控系统

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3346180A1 (de) * 1983-12-21 1985-08-29 Grünzweig + Hartmann und Glasfaser AG, 6700 Ludwigshafen Starrer waermedaemmkoerper
CN1205751A (zh) * 1995-12-21 1999-01-20 德国赫彻斯特研究技术两合公司 含有至少一种热塑性纤维材料的纤维组织－气凝胶-复合材料,其制备方法及其应用
CN1622852A (zh) * 2002-01-29 2005-06-01 卡伯特公司 耐热气凝胶绝缘复合材料及其制备方法,气凝胶粘合剂组合物及其制备方法
WO2007011750A3 (fr) * 2005-07-15 2009-04-16 Aspen Aerogels Inc Composites aerogel renforces et procedes de fabrication
CN103249560A (zh) * 2010-10-08 2013-08-14 日东电工株式会社 热功能性阻燃聚合物构件
CN108883597A (zh) * 2016-01-27 2018-11-23 W.L.戈尔及同仁股份有限公司 包含增强的气凝胶复合物的层叠体

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5081464B2 (ja) * 2007-02-14 2012-11-28 ニチアス株式会社 断熱材及びその製造方法
CN204144345U (zh) * 2014-08-01 2015-02-04 北京新能源汽车股份有限公司 一种用于电动汽车的动力电池箱体
JP2017166610A (ja) * 2016-03-17 2017-09-21 イビデン株式会社 断熱保温部材
CN107914428A (zh) * 2017-12-19 2018-04-17 深圳市德镒盟电子有限公司 一种新能源汽车动力电池用隔热防火材料
CN207697181U (zh) * 2017-12-19 2018-08-07 深圳市德镒盟电子有限公司 一种新能源汽车动力电池用隔热防火材料

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3346180A1 (de) * 1983-12-21 1985-08-29 Grünzweig + Hartmann und Glasfaser AG, 6700 Ludwigshafen Starrer waermedaemmkoerper
CN1205751A (zh) * 1995-12-21 1999-01-20 德国赫彻斯特研究技术两合公司 含有至少一种热塑性纤维材料的纤维组织－气凝胶-复合材料,其制备方法及其应用
CN1622852A (zh) * 2002-01-29 2005-06-01 卡伯特公司 耐热气凝胶绝缘复合材料及其制备方法,气凝胶粘合剂组合物及其制备方法
WO2007011750A3 (fr) * 2005-07-15 2009-04-16 Aspen Aerogels Inc Composites aerogel renforces et procedes de fabrication
CN103249560A (zh) * 2010-10-08 2013-08-14 日东电工株式会社 热功能性阻燃聚合物构件
CN108883597A (zh) * 2016-01-27 2018-11-23 W.L.戈尔及同仁股份有限公司 包含增强的气凝胶复合物的层叠体

Cited By (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113785431A (zh) * 2021-02-05 2021-12-10 气凝胶研发私人有限公司 用于电池的隔热装置
CN113785431B (zh) * 2021-02-05 2024-02-06 气凝胶研发私人有限公司 用于电池的隔热装置
EP4064423A4 (fr) * 2021-02-05 2022-11-30 Aerogel R&D Pte. Ltd. Élément d'isolation thermique pour batteries
CN113025226A (zh) * 2021-03-22 2021-06-25 朗缪环保科技(天津)有限公司 气凝胶防火保温隔热涂料
WO2022199642A1 (fr) * 2021-03-25 2022-09-29 东丽纤维研究所（中国）有限公司 Feutre ignifuge
CN113637233A (zh) * 2021-07-23 2021-11-12 浙江理工大学 一种全生物质节能防火用气凝胶的制备方法
CN113637233B (zh) * 2021-07-23 2022-11-29 浙江理工大学 一种全生物质节能防火用气凝胶的制备方法
CN113858723A (zh) * 2021-09-29 2021-12-31 湖北三江航天红阳机电有限公司 一种梯度热防护层结构试板及其制备方法
CN113858723B (zh) * 2021-09-29 2023-09-19 湖北三江航天红阳机电有限公司 一种梯度热防护层结构试板及其制备方法
CN114395336A (zh) * 2021-12-02 2022-04-26 广东航邦新材料科技有限公司 一种新型隔热防护材料及其生产工艺
CN114643762A (zh) * 2022-03-09 2022-06-21 苏州中纺学面料产业研究院 一种阻燃隔热面料的制备方法
CN114643762B (zh) * 2022-03-09 2024-03-08 苏州中纺学面料产业研究院 一种阻燃隔热面料的制备方法
CN114628844A (zh) * 2022-03-24 2022-06-14 广州小鹏汽车科技有限公司 电池箱、动力电池总成及车辆
CN115180836A (zh) * 2022-07-11 2022-10-14 南通金鹏玻纤制品有限公司 一种阻燃玻纤布及其生产工艺
CN115799729A (zh) * 2023-02-01 2023-03-14 中创新航科技股份有限公司 电池组以及电池装置
CN116166073B (zh) * 2023-04-26 2023-07-21 深圳市博硕科技股份有限公司 具有学习功能的动力电池隔热棉裁切温控系统
CN116166073A (zh) * 2023-04-26 2023-05-26 深圳市博硕科技股份有限公司 具有学习功能的动力电池隔热棉裁切温控系统

Also Published As

Publication number Publication date
CN113939942A (zh) 2022-01-14

Similar Documents

Publication Publication Date Title
WO2021000927A1 (fr) Matériau thermo-isolant et ignifuge et son application
CN207587926U (zh) 电池模块的吸热隔热结构
US8592076B2 (en) Battery pack
KR20220143100A (ko) 배터리용 열 관리 다층 시트
KR20220150347A (ko) 배터리용 열 관리 다층 시트
JP7144629B2 (ja) 断熱層を有するシングルセル用ケース
US20240250334A1 (en) Thermal runaway suppression sheet and battery pack and/or battery module using the same
CN113443889A (zh) 电动汽车蓄电池用二氧化硅气凝胶玻纤毡复合材料薄板、隔热垫制品及其应用
CN212077450U (zh) 具有二氧化硅气凝胶陶瓷纤维布复合薄板的隔热垫制品
CN113506935A (zh) 电池模组用热蔓延防护板、电池模组和电池包
TW202319232A (zh) 用於緩解電能儲存熱事件之材料、系統及方法
US12062770B2 (en) Thermal barrier component for mitigating thermal runaway in batteries
CN217704995U (zh) 热防护层及电动汽车电池用热防护结构
WO2023229042A1 (fr) Feuille de suppression de transfert de chaleur et bloc-batterie
CN115286942B (zh) 一种耐高温防火涂层及其制备方法与应用
US20240124670A1 (en) Fire-resistant, fire retardant and/or thermal insulation
JP7364742B1 (ja) 熱伝達抑制シート及び組電池
JP7364739B2 (ja) 熱伝達抑制シート及び組電池
CN219778976U (zh) 用于电力系统的阻隔件元件、电池模块、电力系统、设备或车辆
KR20240126782A (ko) 열반응형 방화재 조성물 및 이를 이용한 열반응형 방화재
WO2023229043A1 (fr) Feuille de suppression de transfert de chaleur et bloc-batterie
WO2023239306A1 (fr) Feuille intumescente utilisée dans une batterie de véhicule électrique pour la gestion d'emballement thermique
EP4357124A1 (fr) Matériau de prévention de propagation du feu, son procédé de production, stratifié, batterie assemblée et automobile
JP2023170065A (ja) 防炎シート及びその製造方法、並びに電池モジュール
CN117157806A (zh) 用于缓解基于电池的能量存储系统中热传递的系统及方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20835454

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20835454

Country of ref document: EP

Kind code of ref document: A1