  • C09J175/00—Adhesives based on polyureas or polyurethanes; Adhesives based on derivatives of such polymers
  • C09J175/04—Polyurethanes
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
  • C08G18/40—High-molecular-weight compounds
  • C08G18/42—Polycondensates having carboxylic or carbonic ester groups in the main chain
  • C08G18/44—Polycarbonates
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/08—Processes
  • C08G18/0804—Manufacture of polymers containing ionic or ionogenic groups
  • C08G18/0819—Manufacture of polymers containing ionic or ionogenic groups containing anionic or anionogenic groups
  • C08G18/0823—Manufacture of polymers containing ionic or ionogenic groups containing anionic or anionogenic groups containing carboxylate salt groups or groups forming them
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/08—Processes
  • C08G18/0838—Manufacture of polymers in the presence of non-reactive compounds
  • C08G18/0842—Manufacture of polymers in the presence of non-reactive compounds in the presence of liquid diluents
  • C08G18/0861—Manufacture of polymers in the presence of non-reactive compounds in the presence of liquid diluents in the presence of a dispersing phase for the polymers or a phase dispersed in the polymers
  • C08G18/0866—Manufacture of polymers in the presence of non-reactive compounds in the presence of liquid diluents in the presence of a dispersing phase for the polymers or a phase dispersed in the polymers the dispersing or dispersed phase being an aqueous medium
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/08—Processes
  • C08G18/16—Catalysts
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
  • C08G18/2805—Compounds having only one group containing active hydrogen
  • C08G18/285—Nitrogen containing compounds
  • C08G18/2865—Compounds having only one primary or secondary amino group; Ammonia
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
  • C08G18/40—High-molecular-weight compounds
  • C08G18/409—Dispersions of polymers of C08G in organic compounds having active hydrogen
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
  • C08G18/40—High-molecular-weight compounds
  • C08G18/42—Polycondensates having carboxylic or carbonic ester groups in the main chain
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
  • C08G18/40—High-molecular-weight compounds
  • C08G18/48—Polyethers
  • C08G18/4825—Polyethers containing two hydroxy groups
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
  • C08G18/72—Polyisocyanates or polyisothiocyanates
  • C08G18/74—Polyisocyanates or polyisothiocyanates cyclic
  • C08G18/75—Polyisocyanates or polyisothiocyanates cyclic cycloaliphatic
  • C08G18/758—Polyisocyanates or polyisothiocyanates cyclic cycloaliphatic containing two or more cycloaliphatic rings
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
  • C08G18/72—Polyisocyanates or polyisothiocyanates
  • C08G18/77—Polyisocyanates or polyisothiocyanates having heteroatoms in addition to the isocyanate or isothiocyanate nitrogen and oxygen or sulfur
  • C08G18/78—Nitrogen
  • C08G18/79—Nitrogen characterised by the polyisocyanates used, these having groups formed by oligomerisation of isocyanates or isothiocyanates
  • C08G18/797—Nitrogen characterised by the polyisocyanates used, these having groups formed by oligomerisation of isocyanates or isothiocyanates containing carbodiimide and/or uretone-imine groups
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
  • C08G18/72—Polyisocyanates or polyisothiocyanates
  • C08G18/80—Masked polyisocyanates
  • C08G18/8061—Masked polyisocyanates masked with compounds having only one group containing active hydrogen
  • C08G18/807—Masked polyisocyanates masked with compounds having only one group containing active hydrogen with nitrogen containing compounds
  • C08G18/808—Monoamines
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L79/00—Compositions of macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing nitrogen with or without oxygen or carbon only, not provided for in groups C08L61/00 - C08L77/00
  • C08L79/04—Polycondensates having nitrogen-containing heterocyclic rings in the main chain; Polyhydrazides; Polyamide acids or similar polyimide precursors
  • C08L79/08—Polyimides; Polyester-imides; Polyamide-imides; Polyamide acids or similar polyimide precursors
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D175/00—Coating compositions based on polyureas or polyurethanes; Coating compositions based on derivatives of such polymers
  • C09D175/04—Polyurethanes
  • C09D175/06—Polyurethanes from polyesters
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D175/00—Coating compositions based on polyureas or polyurethanes; Coating compositions based on derivatives of such polymers
  • C09D175/04—Polyurethanes
  • C09D175/08—Polyurethanes from polyethers
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J175/00—Adhesives based on polyureas or polyurethanes; Adhesives based on derivatives of such polymers
  • C09J175/04—Polyurethanes
  • C09J175/06—Polyurethanes from polyesters
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J175/00—Adhesives based on polyureas or polyurethanes; Adhesives based on derivatives of such polymers
  • C09J175/04—Polyurethanes
  • C09J175/08—Polyurethanes from polyethers
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G2115/00—Oligomerisation
  • C08G2115/06—Oligomerisation to carbodiimide or uretone-imine groups
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G2170/00—Compositions for adhesives
  • C08G2170/80—Compositions for aqueous adhesives

Definitions

• the present invention relates to latently reactive adhesive preparations which contain solid polycarbodiimide resins, which have a softening temperature of above + 30 ° C., as crosslinking agents for adhesive dispersion polymers.
• solid polycarbodiimide resins which have a softening temperature of above + 30 ° C.
• crosslinking agents for adhesive dispersion polymers are themselves already storage-stable and are suitable for the production of storage-stable latent-reactive adhesive dispersions, latent-reactive adhesive layers, self-supporting latent-reactive adhesive films or latent-reactive adhesive powders.
• Suitable polycarbodiimides must therefore have an average minimum functionality of 2, that is to say have an average of at least 2 carbodiimide groups per molecule.
• EP-A 2 552 982 discloses a process for producing hydrophilically modified polycarbodiimides from aliphatic or cycloaliphatic diisocyanates, the carbon dioxide reaction gas formed during the carbodiimidization being removed temporarily (ie periodically) or permanently from the reaction mixture . Part of this procedure is the small amount of the catalyst required for the carbodiimidization.
• the polycarbodiimide resin is a highly viscous mass at 23 ° C.
• the hydrophilically modified polycarbodiimide resin thus obtained is dispersed in water.
• Such polycarbodiimide dispersions are used i.a. as a crosslinking agent for aqueous adhesives, coating agents or paints.
• a disadvantage of this teaching is that the crosslinking reaction in the adhesive or lacquer layer starts immediately when the aqueous coating dries and then proceeds at high speed.
• a dispersion polymer is therefore the polymer in the polymer particles (disperse phase) of a colloidally stable polymer dispersion.
• the continuous phase is usually water.
• a polymer dispersion thus consists of at least one disperse phase (polymer particles) and one continuous phase (the dispersion medium).
• the dispersion medium is water.
• the polymer dispersion is applied to a substrate and the dispersion medium is evaporated, then - if the temperature of the polymer is above the minimum film formation temperature (MFT) - a polymer film is formed from the dispersion polymer.
• the polymer film contains all components of the polymer dispersion that are non-volatile at the drying temperature.
• Latent-reactive preparations of dispersion polymers which contain solid isocyanates as crosslinking agents or are mixed with such solid isocyanates as a disperse phase of a dispersion are known.
• EP-A 0 922 720 discloses the use of at least one, essentially aqueous dispersion which contains at least one solid surface-deactivated polyisocyanate and at least one isocyanate-reactive polymer for producing dried, storage-stable, latently reactive layers or powders.
• solid isocyanates can be used according to this teaching.
• two solid isocyanates can preferably be used: the TDI dimer and the IPDI trimer. Both isocyanates are readily soluble in the molten polyurethane dispersion polymers or are well tolerated with them, which is necessary for the uniform and good crosslinking of the adhesive polymer before geous.
• 2,4-TDI is highly volatile and can be released from the adhesive layer, for example through porous substrates (textile), into the gas space above the adhesive connection.
• 2,4-TDI is a hazardous substance which, according to GF1S (Globally Flarmonized System of Classification, Labeling and Packaging of Chemicals), has to be labeled GF1S 06 due to its acute toxicity and GF1S08 due to various health hazards.
• GF1S Globally Flarmonized System of Classification, Labeling and Packaging of Chemicals
• the disadvantage of the IPDI trimer is that its aqueous formulations have only limited storage stability. So the max. Storage time of aqueous formulations with the IPDI-Trimer at 23 ° C only 1-2 months, at 30 ° C approx. 2 weeks and at 35 ° C only approx. 1 week.
• the IPDI trimer is significantly less reactive than the TDI dimer and is therefore almost exclusively processed using suitable catalysts (see EP-A 2 099 840 A1 and WO 2008/071307).
• crosslinking agents which make it possible to provide storage-stable aqueous adhesive systems from which latently reactive adhesive layers, adhesive films or adhesive powder can be produced.
• the crosslinking agents should be physiologically harmless, should not decompose during processing of the adhesive polymer and should have a sufficiently high reactivity.
• Polycarbodiimides which are solid at room temperature are known. These products are used as stabilizers / anti-hydrolysis agents for polymers containing ester groups, e.g. Polyester or thermoplastic polyurethanes. Solid polycarbodiimides are also used as crosslinking components in powder coating formulations.
• Carbodiimide-blocked isocyanate prepolymers are also described. These products can also be solids with a softening temperature above +23 ° C.
• EP-A 0 881 243 discloses the use of polycarbodiimide from aliphatic, araliphatic and aromatic diisocyanates as a crosslinking agent for powder coatings.
• the polycarbodiimides have a melting temperature between 40 ° C and 200 ° C.
• the degree of polymerization of the polycarbodiimides according to the invention is between 2 and 50 for a polycarbodiimide with terminal NCO groups, between 0 and 50 when monoisocyanates are also used for chain termination and between 2 and 50 when the chain is terminated by alcohol, amine, carboxylic acid or carboxylic acid anhydride.
• US Pat. No. 8,399,574 describes the composition of a powder mixture for a slush molding process consisting of a thermoplastic polyurethane and a polycarbodiimide with a molecular weight between 10,000 and 30,000 g / mol.
• the polycarbodiimide is produced from tetramethyl xylylene diisocyanate (TMXDI).
• TXDI tetramethyl xylylene diisocyanate
• EP-A 0 767 188 describes crosslinking agents for polyurethane basecoats.
• the crosslinking agents are isocyanate prepolymers blocked with carbodiimide groups.
• the crosslinking agents have a melting temperature of> 70 ° C.
• EP-A 0 005 230 discloses binders for powder coatings, the crosslinker component b), a blocked isocyanate, having a melting point between 60.degree. C. and 180.degree.
• Carbodiimide is also used as a blocking agent. The blocking reaction takes place by reaction of the intermediate carbodiimide segments with free NCO groups with the formation of uretonimine. When the powder coating is heated, the uretonimine splits back into carbodiimide and isocyanate, with the released isocyanate crosslinking the powder coating polymer.
• US 9 957 394 (WO 2018/048709) describes a powder coating composition consisting of a polymer containing carboxyl groups with a glass transition temperature of at least + 50 ° C. and a polycarbodiimide which contains urethane and / or urea segments.
• the polycarbodiimide also has a glass transition temperature of at least + 50 ° C. If the powder coating composition is applied to a substrate or a release liner, film formation does not occur.
• the aqueous mixture of polymer and polycarbodiimide is dried and the powder obtained is adjusted to the desired particle size by grinding.
• Chemically curing powder coatings consist of at least one film-forming system (binder) and a crosslinker. No noticeable crosslinking must occur during the processing of the premixed powder coating in the extruder.
• the ground powder coating must also not sinter or block during storage. For this reason, only largely amorphous binders / film formers with a glass transition temperature of at least + 40 ° C are used for powder coatings (industrial powder coating, Judith Pietschmann, ISBN 979-3-8348-0463-1).
• the present invention was based on the object of providing a new crosslinking agent for adhesive polymers which can be used in aqueous polymer dispersions and gives these preparations a long pot life and allows the production of latent-reactive adhesive layers, latent-reactive adhesive films and latent-reactive adhesive powders .
• the Ver- wetting agents should be physiologically harmless.
• the crosslinking reaction should be triggered by the action of heat on the adhesive polymer
• the present invention consists, inter alia, in the provision of the teaching of preparations containing finely particulate polymeric carbodiimides which have a softening temperature of at least + 30 ° C., preferably at least + 35 ° C., mixed with finely particulate polymers which are crosslinked with these polycarbodiimides can, be it (dry) as a powder mixture or (wet) as a dispersion or obtained by mixing and melting the powder as a then immediately reacting (in the sense of crosslinking of the polymer) mixture or by drying the dispersion as a latently reactive film on the substrate Coating, ready to provide.
• the present invention therefore also relates to latently reactive preparations based on dispersion polymers which have a minimum film formation temperature of ⁇ +23 ° C and a glass transition temperature measured with the DSC (heating rate 20K / min) of ⁇ 0 ° C, which are crosslinked with carbodiimides can, and at least one polycarbodiimide with a glass transition temperature of at least + 30 ° C and an average functionality of at least 2 contain.
• any solid polycarbodiimide powder which has a softening temperature of at least + 30.degree. C., preferably at least + 35.degree. C., is used as crosslinking agent for carbodiimide-reactive dispersion polymers.
• Polycarbodiimide powders of this type can be produced by methods known per se by grinding solid polycarbodiimide resins, for example with the aid of ball, bead, sand mills or jet mills, if appropriate at a reduced temperature (cryogenic milling).
• the particle size or the particle size distribution of the polycarbodiimide powder can then be further limited by sieving or sifting.
• the size of the particles obtained can, for example, be determined by the method according to ISO 13320 (laser diffraction). Five individual measurements are carried out each time and the arithmetic mean of the individual measurements is given.
• a Malvern Mastersizer 3000 for example, can be used as a measuring device.
• Polycarbodiimide powders with an average particle size dv (50) ⁇ 70 ⁇ m are suitable. preferably dv (50) ⁇ 20pm and particularly preferably particles with dv (50) ⁇ 3.4pm.
• the particle size is determined according to ISO 13320 (laser diffraction) with a Malvern Mastersizer 3000 as the measuring device. Five individual measurements are carried out each time and the arithmetic mean of the individual measurements is given.
• the polycarbodiimide resins used to produce the preparations according to the invention are any compounds containing at least two carbodiimide groups per molecule, such as those obtained, for example, by reacting organic polyisocyanates, optionally with hydroxy and / or amino functional compounds, in the presence of a carbodiimidization catalyst are obtainable with elimination of carbon dioxide.
• Suitable isocyanates for the preparation of the polycarbodiimide resins are any, in various ways, for example by phosgenation in the liquid or gas phase or in the phosgene-free route, such as. B. by thermal urethane cleavage, accessible mono-, di- and triisocyanates with aliphatically, cycloaliphatically, araliphatically and / or aromatically bound isocyanate groups.
• Preferred monoisocyanates are those of the molecular weight range 99 to 300, such as.
• Preferred diisocyanates are those in the molecular weight range 140 to 400, e.g. 1,4-diisocyanatobutane, 1,5-diisocyanatopentane (pentamethylene diisocyanate, PDI), 1,6-diisocyanatohexane (hexamethylene diisocyanate, HDI), 2-methyl-1,5-diisocyanatopentane, 1,5-diisocyanato-2,2- dimethylpentane, 2,2,4- or 2,4,4-trimethyl-l, 6-diisocyanatohexane, 1,10-diisocyanatodecane, 1,3- and 1,4-diisocyanatocyclohexane, 1,3- and l, 4-bis- (isocyanatomethyl) -cyclohexane, 1,3-diisocyanato-2 (4) -methylcyclohexane, 1-isocyanato-3,3,5-tri
• Diisocyanatodiphenylmethane (MDI), 3,3'-dimethyldiphenylmethane-4,4'-diisocyanate, 4,4'-diisocyanatodiphenylethane, 1,5-diisocyanatonaphthalene (naphthylene diisocyanate, NDI), diphenyl ether diisocyanate, ethylene glycol, diphenyl ether diisocyanate, diethylene glycol diisocyanate 1,3 Propylene glycol diphenyl ether diisocyanate, benzophenone diisocyanate, triisocyanatobenzene, 2,4,6-triisocyanatotoluene, trimethylbenzene triisocyanate, diphenylmethane-2,4,4'-triisocyanate, 3-methyldiphenylmethane-4,6,4'-triisocyanate, the isomeric naphaline-diisocyanates and methylene
• a particularly suitable triisocyanate is 4-isocyanatomethyl-1,8-octane diisocyanate (triisocyanatononane; TIN).
• Mixtures of at least two such mono-, di- and / or triisocyanates can also be used to produce the polycarbodiimide resins.
• Monomeric diisocyanates are preferably used to prepare the polycarbodiimide resins.
• PDI low-density polyethylene glycol
• HDI high-density polyethylene glycol
• IPDI low-density polyethylene glycol
• H12-MDI high-density polyethylene glycol
• TMXDI TDI
• / or MDI is particularly preferred.
• hydroxy- and / or amino-functional compounds are used as further structural components in the production of the polycarbodiimide resins.
• Suitable hydroxy-functional structural components are, for example, any simple aliphatic or cycloaliphatic monoalcohols, such as methanol, ethanol, n-propanol, isopropanol, n-butanol, isobutanol, sec-butanol, the isomeric pentanols, hexanols, octanols and nonanols, n-decanol, n Dodecanol, n-tetradecanol, n-hexadecanol, n-octadecanol, cyclohexanol, the isomeric methylcyclohexanols and hydroxymethylcyclohexane, ether alcohols such as 2-methoxyethanol, 2-ethoxyethanol, 2-propoxyethanol, 2-butoxyethanol, diethylene glycol ether, diethylene glycol monomethyl ether, diethylene glycol monomethyl ether, diethylene glycol ether
• suitable alcohols for the preparation of the polycarbodiimide resins are any at least difunctional polyols, in particular simple polyhydric alcohols having 2 to 14, preferably 4 to 10 carbon atoms, such as.
• Suitable alcohols for producing the polycarbodiimide resins are also the customary polymeric polyether polyols, polyester polyols, polycarbonate polyols and / or polyacrylate polyols known from polyurethane chemistry, which usually have a number average molecular weight of 200 to 22,000, preferably 250 to 18,000, particularly preferably 250 to 12,000.
• polyurethane chemistry usually have a number average molecular weight of 200 to 22,000, preferably 250 to 18,000, particularly preferably 250 to 12,000.
• a broad overview of such polymeric polyols for the production of the polycarbodiimide resins can be found, for example, in N. Adam et al .: “Polyurethanes", Ullmann's Encyclopedia of Industrial Chemistry, Electronic Release, 7th ed., Chap. 3.2 - 3.4, Wiley-VCH, Weinheim 2005.
• Suitable amino-functional structural components for preparing the polycarbodiimide resins are, for example, simple aliphatic or cycloaliphatic monoamines, such as. B. methylamine, ethylamine, n-propylamine, isopropylamine, the isomeric butylamine, pentylamine, hexylamine and octylamine, n-dodecylamine, n-tetradecylamine, n-hexadecylamine, n-octadecylamine, cyclohexylamine, the isomeric methylcyclohexylamine, and aminomethylcyclohexylamine and aminomethylcyclohexane amines, such as dimethylamine, diethylamine, dipropylamine, diisopropylamine, dibutylamine, diisobutylamine, bis (2-ethylhexyl) amine, N-methyl- and
• Suitable amines are also any aliphatic and cycloaliphatic amines with at least two primary and / or secondary bonded amino groups, such as.
• Suitable amines are also amino-functional polyalkylene glycols, such as. B. 1,2-bis (aminoethoxy) ethane, l, ll-diamino-3,6,9-trioxaundecane, l, 13-diamino-4,7,10-trioxatride-can and in particular those under the tradename Jeffamine ® from Huntsman Corp.
• Commercially sold amine-functionalized polyalkylene glycols with average molecular weights up to 5000, preferably up to 2000, particularly preferably up to 1000.
• sterically hindered aliphatic diamines with two secondary bound amino groups can be used for the preparation of the polycarbodiimide resins, such as. B. the reaction products known from EP-A 0 403 921 of aliphatic and / or cycloaliphatic diamines with maleic or fumaric acid esters, the bisadduct of acrylonitrile with isophoronediamine obtainable according to the teaching of EP-A 1 767 559 or the, for example, in DE-A 19 701 835 described hydrogenation products of aliphatic and / or cycloaliphatic diamines and ketones, such as. B. diisopropyl ketone, accessible Schiff bases.
• amino alcohols such as. B. 2-aminoethanol
• the isomeric aminopropanols and butanols, 3-amino-l, 2-propanediol and 1,3-diamino-2-propanol are suitable as structural components.
• the preparation of the polycarbodiimide resins by reacting organic isocyanates, if necessary with hydroxy- and (or amino-functional compounds) is carried out according to methods known per se in the presence of a suitable carbodiimidization catalyst with elimination of carbon dioxide.
• Suitable catalysts for carbodiimide formation are described in a number of review articles, for example in Houben-Weyl, Methods of Organic Chemistry, Volume E4, carbon acid derivatives, Georg-Thieme-Verlag, Stuttgart, 1983, pp. 897 to 900 and 910, in Chemical Reviews, Volume 67, Number 2, 1967, pp. 107-113, in Angew. Chem., 1962, 74, 801-806 and in Angew. Chem. 1981, 93, 855-866. Further suitable catalysts can also be found in the patent literature, for example in DE 1130594, DE 3512918, US 2840589, US 2853473, US 2853518 or US 2941966.
• catalysts are, in particular, heterocyclic, phosphorus-containing compounds, such as phospholines, phospholenes and phospholidines and their oxides and sulfides.
• heterocyclic, phosphorus-containing compounds such as phospholines, phospholenes and phospholidines and their oxides and sulfides.
• examples of such catalysts are l-methyl-2-phospholene-1-oxide, l-methyl-3-phospholene-1-oxide, 3-methyl-l-phenyl-3-phospholene-1-oxide and 3- Methyl-l-phenyl-2-phospholene-l-oxide and the analogous phospholane types.
• the synthesis of the carbodiimides is generally carried out in a manner known per se, for example by a process described in the above-mentioned prior art, starting from isocyanates by catalysis with splitting off of carbon dioxide.
• isocyanates by catalysis with splitting off of carbon dioxide.
• solid mono- or polycarbodiimides with softening temperatures in the above range are obtained, which are preferably free of isocyanate groups and, if hydroxy and / or amino-functional structural components are used, urethane and / or urethane components Have urea groups.
• Suitable aqueous polymer dispersions are those with nucleophilic functional groups.
• Such functional groups are carboxyl, amino, mercapto and hydroxyl groups; carboxyl groups are very particularly preferred, if only because they generally react with the carbodiimides without the use of catalysts.
• the minimum film formation temperature of the dispersion polymers is ⁇ + 23 ° C. They have a glass transition temperature measured with the DSC (heating rate 20K / min) of ⁇ 0 ° C.
• Suitable polymer dispersions are, for example, those based on polymers of olefinically unsaturated monomers, as described, for example, in EP-A 0 206 059. These are, for example, homopolymers and copolymers based on vinyl esters of carboxylic acids with 2 to 18 carbon atoms, preferably with 2 to 4 carbon atoms, such as vinyl acetate.
• These can optionally contain up to 70% by weight, based on the total amount, of other olefinically unsaturated saturated monomers and / or homopolymers or copolymers of (meth) acrylic acid esters of alcohols with 1 to 18 carbon atoms, preferably with 1 to 4 carbon atoms, such as (meth) methyl, ethyl, propyl, hydroxyethyl or hydroxypropyl esters can be used.
• Preferred polymer dispersions are dispersions of polyurethane-polyurea polymers which have lateral and / or terminal carboxyl groups in the polymer chain.
• Polyurethane polyurea dispersions are available on an industrial scale and are commonly referred to as polyurethane dispersions (PUDs).
• the polymers contain as structural components:
• Suitable diol and / or polyol components A) are compounds having at least two isocyanate-reactive hydrogen atoms and an average molecular weight be preferably from 62 to 18,000, particularly preferably from 62 to 4000 g / mol.
• suitable structural components are polyethers, polyesters, polycarbonates, polylactones and polyamides.
• Preferred polyols A) preferably have 2 to 4, particularly preferably 2 to 3, hydroxyl groups, very particularly preferably 2 hydroxyl groups. Mixtures of various such compounds are also possible.
• polyester polyols are linear polyester diols or slightly branched polyester polyols, such as are known in the art from aliphatic, cycloaliphatic or aromatic di- or polycarboxylic acids, such as, for example, amber, methyl amber, glutaric, adipic, pimeline, cork, Azelaic, sebacic, nonanedicarboxylic, decanedicarboxylic, terephthalic, isophthalic, o-phthalic, tetrahydrophthalic, hexahydrophthalic, cyclohexanedicarboxylic, maleic, fumaric, malonic or trimellitic acid and acid anhydrides such as o-phthalic , Trimellitic or succinic anhydride or mixtures thereof with polyhydric alcohols, such as ethanediol, di-, tri-, tetraethylene glycol, 1,2-propanediol, di-, tri-, te
• Cycloaliphatic and / or aromatic di- and polyhydroxyl compounds are of course also suitable as polyhydric alcohols for the production of the polyester polyols.
• the corresponding polycarboxylic acid anhydrides or corresponding polycarboxylic acid esters of lower alcohols or mixtures thereof can also be used to prepare the polyesters.
• the polyester polyols can also be homopolymers or copolymers of lactones, which are preferably formed by the addition of lactones or lactone mixtures, such as butyrolactone, e-caprolactone and / or methyl-e-caprolactone, onto the suitable di- and / or higher-functional starter molecules, such as the low molecular weight, polyhydric alcohols mentioned above as structural components for polyester polyols are obtained.
• lactones or lactone mixtures such as butyrolactone, e-caprolactone and / or methyl-e-caprolactone
• suitable di- and / or higher-functional starter molecules such as the low molecular weight, polyhydric alcohols mentioned above as structural components for polyester polyols are obtained.
• the corresponding polymers of e-caprolactone are preferred.
• Polycarbonates containing hydroxyl groups are also suitable as polyhydroxyl components A), e.g. those obtained by reacting diols such as 1,4-butanediol and / or 1,6-hexanediol with diaryl carbonates, e.g. Diphenyl carbonate, dialkyl carbonates, such as. B. dimethyl carbonate or phosgene can be produced.
• diols such as 1,4-butanediol and / or 1,6-hexanediol
• diaryl carbonates e.g. Diphenyl carbonate, dialkyl carbonates, such as.
• B. dimethyl carbonate or phosgene can be produced.
• the at least partial use of polycarbonates containing hydroxyl groups can improve the hydrolysis resistance of the polyurethane or polyurethane-urea dispersion adhesives.
• Suitable polyether polyols are e.g. the polyaddition products of styrene oxides, ethylene oxide, propylene oxide, tetrahydrofuran, butylene oxide, epichlorohydrins, as well as their mixed addition and graft products, as well as those by condensation of polyhydric alcohols or mixtures thereof and those by alkoxylation of polyhydric alcohols, amines and amino alcohols obtained polyether polyols.
• Polyether polyols suitable as structural components A) are the homopolymers, copolymers and graft polymers of propylene oxide and ethylene oxide, which are formed by the addition of the epoxides mentioned to low molecular weight diols or triols, as mentioned above as structural components for polyester polyols, or to higher-functionality, low molecular weight polyols such as e.g. Pentaerythritol or sugar or water are accessible.
• suitable components A) are low molecular weight diols, triols and / or tetraoies such as ethanediol, di-, tri-, tetraethylene glycol, 1,2-propanediol, di-, tri-, tetrapropylene glycol, 1,3-propanediol, butanediol-1, 4, butanediol-1,3, butanediol-2,3, pentanediol-1,5, hexanediol-1,6, 2,2-dimethyl-1,3-propanediol, 1,4-dihydroxycyclohexane, 1,4-dimethylolcyclohexane, 1,8 octanediol, 1,10 decanediol, 1,12 dodecanediol, neopentyl glycol, 1,4-cyclohexanediol, 1,4-cyclohexan
• Reaction products of the polyols mentioned, in particular the low molecular weight polyols, with ethylene oxide and / or propylene oxide can also be used as polyols.
• the low molecular weight components A) have a molecular weight preferably from 62 to 400 g / mol and are preferably used in combination with the polyester polyols, polylactones, polyethers and / or polycarbonates described above.
• the polyol component A) is contained in the polyurethane according to the invention preferably in an amount of from 20 to 95, particularly preferably from 30 to 90 and very particularly preferably from 65 to 90% by weight.
• Diisocyanates Y (NCO) 2 are preferably used, where Y is a divalent aliphatic hydrocarbon radical with 4 to 12 carbon atoms, a divalent cycloaliphatic hydrocarbon radical with 6 to 15 carbon atoms, and a divalent aromatic hydrocarbon radical with 6 to 15 carbon atoms or a divalent araliphatic hydrocarbon radical having 7 to 15 carbon atoms.
• diisocyanates examples include tetramethylene diisocyanate, methylpentamethylene diisocyanate, hexamethylene diisocyanate, dodecamethylene diisocyanate, 1,4-diisocyanato-cyclohexane, 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethyl-cyclohexane (isophorone diisocyanate; IPDI), 4,4 '-Diisocyanato-dicyclohexyl-methane, 4,4'-diisocyanatodicyclohexylpropane- (2,2), 1,4-di-isocyanatobenzene, 2,4-diisocyanatotoluene, 2,6-diisocyanatotoluene, 4,4'-diisocyanato- diphenylmethane, 2,2'- and 2,4'-diisocyanatodip
• those polyisocyanates are also suitable which contain heteroatoms in the radical linking the isocyanate groups and / or have a functionality of more than 2 isocyanate groups per molecule.
• the former are e.g. polyisocyanates made up of at least two diisocyanates with uretdione, isocyanurate, urethane, allophanate, biuret, carbodiimide, imino-oxadiazinedione and / or oxadiazinetrione, produced by modifying simple aliphatic, cycloaliphatic, araliphatic and / or aromatic diisocyanates .
• Preferred diisocyanates B) are hexamethylene diisocyanate (HDI), dodecamethylene diisocyanate, 1,4-diisocyanato-cyclohexane, 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethyl-cyclohexane (IPDI), 4,4'-diisocyanatodicyclohexylmethane, 2,4-diisocyanatotoluene, 2,6-diisocyanatotoluene, 4,4'-diisocyanatodiphenylmethane, 2,2'- and 2,4'-diisocyanatodiphenylmethane , as well as mixtures consisting of these compounds.
• HDI hexamethylene diisocyanate
• IPDI 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethyl-cyclohexane
• Particularly preferred components B) are 2,4-diisocyanatotoluene, 2,6-diisocyanatotoluene, hexamethylene diisocyanate and 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethylcyclohexane, as well as mixtures consisting of these compounds.
• Component B) is contained in the polyurethane according to the invention in amounts from 5 to 60, preferably from 6 to 45 and particularly preferably in amounts from 7 to 25% by weight.
• Suitable components C) are, for example, components containing sulphonate or carboxylate groups, e.g. Diamino compounds or dihydroxy compounds which additionally carry sulfonate and / or carboxylate groups, such as, for example, the sodium, lithium, potassium, tert-amine salts of N- (2-aminoethyl) -2-aminoethanesulfonic acid, N - (3-Aminopropyl) -2-aminoethanesulphonic acid, N- (3-aminopropyl) -3-aminopropanesulphonic acid, N- (2-aminoethyl) -3-aminopropanesulphonic acid, the analogous carboxylic acids, dimethylolpropionic acid, dimethylolbutyric acid, the Reaction products in the sense of a Michael addition of 1 mol of diamine such as 1,2-ethanediamine or isophoronediamine with 2 mol of acrylic acid or maleic acid.
• diamine
• the acids are often used directly in their salt form as sulphonate or carboxylate. However, it is also possible to add some or all of the neutralizing agents necessary for salt formation during or after the production of the polyurethanes.
• Amines are e.g. Triethylamine, dimethylcyclohexylamine, ethyldiisopropylamine.
• Other amines can also be used for salt formation, e.g. Ammonia, diethanolamine, triethanolamine, dimethylethanolamine, methydiethanolamine, aminomethylpropanol and also mixtures of the above and also other amines. It makes sense to add these amines only after the prepolymer has been formed.
• suitable components C) are nonionically hydrophilizing, mono- or di-functional polyethers based on ethylene oxide polymers or ethylene oxide / propylene oxide copolymers started on alcohols or amines, such as polyether LB 25 (Covestro Deutschland AG, Leverkusen, Germany or MPEG 750) : methoxy, molecu large weight 750 g / mol (eg Pluriol® ® 750, BASF AG, Germany).
• polyether LB 25 Covestro Deutschland AG, Leverkusen, Germany or MPEG 750
• methoxy, molecu large weight 750 g / mol eg Pluriol® ® 750, BASF AG, Germany.
• Preferred components C) are N- (2-aminoethyl) -2-aminoethanesulfonate, N- (2-aminoethyl) -2-aminoethanecarboxylate and the salts of dimethylolpropionic acid and dimethylolbutyric acid.
• Component C) in the polyurethane according to the invention is preferably from 0.1 to 15% by weight, particularly preferably from 0.5 to 10% by weight, very particularly preferably from 0.8 to 5% by weight and even more preferably from 0.9 to 3.0% by weight.
• Suitable components D) are mono-, di-, trifunctional amines and / or mono-, di-, bifunctional hydroxyamines, such as e.g. aliphatic and / or alicyclic primary and / or secondary monoamines such as ethylamine, diethylamine, the isomeric propyl and butylamines, higher linearaliphati cal monoamines and cycloaliphatic monoamines such as cyclohexylamine.
• Further examples are amino alcohols, i. H. Compounds containing th amino and hydroxyl groups in a molecule, such as. B.
• ethanolamine N-methylethanolamine, diethanolamine, diisopropanolamine, 1,3-diamino-2-propanol, N- (2-hydroxyethyl) -ethylene diamine, N, N-bis (2-hydroxyethyl) -ethylene diamine and 2-propanolamine.
• diamines and triamines such as e.g. 1,2-ethanediamine, 1,6-hexamethylenediamine, l-amino-3,3,5-trimethyl-5-aminomethyl-cyclohexane (isophoronediamine), piperazine, 1,4-diaminocyclohexane, bis- (4-aminocyclohexyl) methane and diethylenetriamine.
• Adipic acid dihydrazide, hydrazine or hydrazine hydrate are also suitable. It is of course also possible to use mixtures of several of the compounds D) mentioned, possibly also together with compounds D) not mentioned.
• Preferred components D) are 1,2-ethanediamine, l-amino-3,3,5-trimethyl-5-aminomethyl-cyclohexane, diethylenetriamine, diethanolamine, ethanolamine, N- (2-hydroxyethyl) -ethylenediamine and N, N-bis (2-hydroxyethyl) ethylenediamine.
• Components D) are used as di- or trifunctional chain extenders, preferably to build up higher molecular weights or, as monofunctional compounds, to limit molecular weights and / or, if necessary, additional reactive groups, such as e.g. to incorporate free hydroxyl groups. If the (poly) amines (D) are not used, the polymers are pure polyurethanes (which do not contain any urea groups).
• Component D) is contained in the polyurethane according to the invention in amounts of preferably from 0 to 10, particularly preferably from 0 to 5 and very particularly preferably in amounts from 0.2 to 3% by weight.
• Components E) to be used with can be, for example, aliphatic, cycloaliphatic or aromatic monoalcohols with 2 to 22 carbon atoms such as ethanol, butanol, hexanol, cyclohexanol, isobutanol, benzyl alcohol, stearyl alcohol, 2-ethylethanol and isocyanate groups used again at elevated temperatures
• Removable blocking agents such as, for example, butanone oxime, dimethylpyrazole, caprolactam, malonic ester, triazole, dimethyltriazole, tert-butylbenzylamine, cycloentanone carboxyethyl ester.
• Components E) can be contained in the polyurethane according to the invention in amounts preferably from 0 to 20, very preferably from 0 to 10% by weight.
• component E) can e.g. lead to polyurethane dispersions according to the invention which contain further reactive groups in addition to the reactive carboxyl groups, which e.g. the use of various cross-linking mechanisms (dual cure) enables special properties, such as to achieve a two-stage, possibly staggered curing or particularly high crosslinking density.
• the lateral and / or terminal carboxyl groups can in principle be incorporated into the polymer structure via any of the structural components A) to E). They are preferably installed via components C), D) and E).
• component C It can be incorporated via component C), for example, by using dimethylol propionic acid or dimethylol butyric acid, in that no neutralizing agent or neutralizing agent is added in a stoichiometric deficit.
• Suitable for incorporating carboxyl groups as components D) are, for example, compounds which each contain only one isocyanate-reactive amino group and thus lead to terminal carboxyl groups in the preparation of the polyurethanes according to the invention by reaction with the isocyanate component.
• Linear aliphatic, branched aliphatic, aliphatic-aromatic and aromatic aminocarboxylic acids are suitable.
• aminocarboxylic acids with a primary or secondary amino group such as alanine, 6-aminohexanoic acid, aminoundecanoic acid, 8-aminooctanoic acid, 5-aminopentanoic acid, 4-aminobutyric acid, aminobenzoic acid, 4-aminomethylcyclohexanecarboxylic acid, 2-
• carboxyl groups as components D) are, for example, diaminocarboxylic acids, each of which has 2 isocyanate-reactive amino groups and thus lead to lateral carboxyl groups in the production of the polyurethanes according to the invention by reaction with the isocyanate component.
• diaminocarboxylic acids each of which has 2 isocyanate-reactive amino groups and thus lead to lateral carboxyl groups in the production of the polyurethanes according to the invention by reaction with the isocyanate component.
• examples are lysine, arginine and histidine.
• hydroxycarboxylic acids which each contain only one hydroxyl group, such as hydroxypivalic acid, hydroxyacetic acid and 2-hydroxpropanoic acid, are suitable for incorporating carboxyl groups as components E).
• Particularly preferred polymer dispersions are dispersions of partially crystalline or crystalline polymers with lateral and / or terminal carboxyl groups in the polymer chain.
• a polymer is referred to as partially crystalline or crystalline if it has a melting peak in the DSC measurement according to DIN 65467 at a heating rate of 20 K / min.
• the melting peak is caused by the melting of regular substructures in the polymer.
• the melting temperature of the polymers or polymer layers obtained from the formulations according to the invention is preferably in a range from 30 ° C. to 110 ° C., particularly preferably from 35 ° C. to 90 ° C., very particularly preferably from 42 ° C. to 60 ° C.
• the enthalpy of fusion of the polymer layers obtained from the formulations according to the invention is> 5 J / g, preferably> 15 J / g.
• the first heating is evaluated in order to detect slowly crystallizing polymers.
• the partially crystalline or crystalline polymer preferably contains one or more crystalline or partially crystalline difunctional polyester polyols as component A).
• the production of crystalline or partially crystalline polyester polyols is known from the prior art.
• Particularly suitable crystalline or partially crystalline polyester polyols A) are linear or slightly branched polyester polyols which are based on dicarboxylic acids and / or their derivatives, such as anhydrides, esters or acid chlorides and preferably aliphatic, linear polyols. Also mixtures of dicarboxylic acids and / or their derivatives are suitable. Suitable dicarboxylic acids are, for example, adipic acid.
• succinic acid, sebacic acid or dodecanedioic acid are examples of adipic acid.
• Succinic acid, adipic acid and sebacic acid and mixtures thereof are preferred, succinic acid and adipic acid and mixtures thereof are particularly preferred, and adipic acid is very particularly preferred. These are used in amounts of at least 90 mol%, preferably from 95 to 100 mol%, based on the total amount of all carboxylic acids.
• the difunctional polyester polyols can be prepared, for example, by polycondensation of dicarboxylic acids with polyols.
• the polyols preferably have a molecular weight of 62 to 399 g / mol, consist of 2 to 12 carbon atoms, are preferably unbranched, that is to say functional, and preferably have primary OH groups.
• polyols which can be used for the production of the polyester polyols are polyhydric alcohols, such as ethanediol, di-, tri-, tetraethylene glycol, 1,2-propanediol, di-, tri-, tetrapropylene glycol, 1,3-propanediol, 1,4-butanediol, 1,3-butanediol, 2,3-butanediol, 1,5-pentanediol, 1,6-hexanediol, 2,2-dimethyl-1,3-propanediol, 1,4-dihydroxycyclohexane, 1, 4-dimethylolcyclohexane, 1,8-octanediol, 1,10-decanediol, 1,12-dodecanediol or mixtures thereof.
• polyhydric alcohols such as ethanediol, di-, tri-, t
• Preferred polyol components for the polyester polyols are 1,2-ethanediol, 1,4-butanediol and 1,6-hexanediol, 1,4-butanediol and 1,6-hexanediol are particularly preferred, and 1,4-butanediol is very particularly preferred.
• aqueous polyurethane or polyurethane-urea dispersions according to the invention, all processes known from the prior art such as emulsifier, shear force, acetone, prepolymer mixing, melt-emulsifying, ketimine and solid spontaneous Dispersing methods or derivatives thereof can be used.
• emulsifier emulsifier, shear force, acetone, prepolymer mixing, melt-emulsifying, ketimine and solid spontaneous Dispersing methods or derivatives thereof
• melt-emulsifying, prepolymer mixing and acetone processes are preferred.
• the acetone process is particularly preferred.
• the application and implementation of the acetone process is state of the art and the skilled person e.g. known from EP-A 0 232 778.
• the pulverulent polycarbodiimide can be stirred directly into the polymer dispersion with the aid of suitable agitators (dissolver, propeller stirrer, disk stirrer, speed mixer or the like).
• suitable agitators dissolver, propeller stirrer, disk stirrer, speed mixer or the like.
• the direct stirring takes place, if appropriate, with the use of additives such as protective colloids, emulsifiers, thickeners, fillers, defoamers, dyes and other auxiliaries customary for the production of dispersion adhesives.
• the separate production of the aqueous formulation of the polycarbodiimide powder may be advantageous.
• the powdery polycarbodiimide is dispersed in an aqueous mixture of protective colloids, emulsifiers, thickeners, defoamers, if necessary other additives, with the aid of suitable agitators (dissolver, propeller stirrer, disk stirrer, speed mixer or the like).
• suitable agitators dissolver, propeller stirrer, disk stirrer, speed mixer or the like.
• the aqueous formulation can then be stirred into the polymer dispersion by means of suitable stirring units (dissolver, propeller stirrer, disk stirrer, speed mixer or the like).
• the amount of polycarbodiimide powder in the adhesive dispersion or the dried adhesive layer, the adhesive film or the adhesive powder depends on the concentration of the nucleophilic groups (carboxyl, amino, mercapto or OH groups) in the dispersion polymer.
• the preparations according to the invention are used for the production of adhesive bonds.
• brief heating of the adhesive polymer by means of infrared radiation, in a heating channel or in a heated press) increases the polymer to a temperature> Tm (above the melting temperature) and liquefied to the extent that it can flow well onto the surfaces of the substrates to be bonded, ie can wet them.
• the preparations according to the invention can also be equipped with ferromagnetic particles.
• the adhesive polymer can also be heated by induction. Heating with microwaves is also possible.
• Typical substrates are e.g. Textiles, polymer films e.g. made of PVC, metallic substrates, also in the form of foils, thermoplastics such as polyamide (PA), acrylic butadiene styrene (ABS), polycarbonate (PC) or blends of ABS and PC, polyester, polyolefinic substrates, if necessary after suitable pretreatment or Application of a primer to achieve the necessary surface energy, wood or wood fiber containing substances such as Plywood, medium-density fibreboard (MDF), decorative foils such as e.g. are used in automobile interiors (PVC foam film, PU film or polyolefinic film with and without embossing).
• thermoplastics such as polyamide (PA), acrylic butadiene styrene (ABS), polycarbonate (PC) or blends of ABS and PC, polyester, polyolefinic substrates, if necessary after suitable pretreatment or Application of a primer to achieve the necessary surface energy, wood or wood fiber containing substances such as P
• aqueous preparations according to the invention can be used in any manner, e.g. can be applied to flat or three-dimensional surfaces using spray, squeegee, brush or roller application methods. After drying, latently reactive (pre) coatings are obtained.
• the formulations can also be applied to release paper (e.g. silicone paper or polyolefinic non-stick paper or similar carrier materials) by spraying, squeegee, brush or roller application. After drying, self-supporting, latent-reactive films or fleeces are obtained which, if necessary after inserting a release paper, can be wound up and stored as an adhesive film until use.
• release paper e.g. silicone paper or polyolefinic non-stick paper or similar carrier materials
• the solids in the form of granules or powder can be obtained from the preparations according to the invention with (partially) crystalline polyurethane dispersion polymers by suitable technical processes.
• the formulations according to the invention can be freed from water by spray drying. This gives latently reactive powders which, if necessary, can be ground to small particle sizes by a subsequent grinding process.
• Fat-reactive powders can also be obtained by coagulating polymer dispersions with solid carbodiimide particles.
• Mixtures of, for example, anionically stabilized polymer dispersions and solid polycarbodiimide are converted into a salt solution with polyvalent cations (e.g. Ca 2+ , Mg 2+ , Al 3+ ) using a rotor / stator mixer (e.g. from Kotthoff) or a jet disperser ) dispersed.
• polyvalent cations e.g. Ca 2+ , Mg 2+ , Al 3+
• a rotor / stator mixer e.g. from Kotthoff
• a jet disperser e.g. from Kotthoff
• the anionic groups come into contact on the surface of the polymer Particles with the polyvalent cations coagulate the polymer particles immediately, the polycarbodiimide particles being included in the coagulate.
• the coagulate is largely freed from water by filtration, centrifugation, etc. and then dried at temperatures below the reaction temperature of the polycarbodiimide or the melting temperature of the dispersion polymer. Possibly. After drying, the coagulate can be ground to the required particle sizes in a grinding process - e.g. in ball, bead, sand or jet mills.
• Another possibility for producing latently reactive powders is to freeze the mixture of polymer and polycarbodiimide out of the aqueous preparations at temperatures below 0 ° C.
• the precipitated polymer / polycarbodiimide mixture is then largely freed from water by filtration, centrifugation, etc. and finally dried.
• the coarse-grained powder obtained can then be milled appropriately - if necessary, the milling process must take place at low temperatures (i.e. well below the glass transition temperature) - e.g. can be ground to the required particle sizes in ball, bead, sand mills or jet mills.
• the latently reactive coatings, films, fleeces or powders must be dried at temperatures below the softening temperature of the polymer or the softening temperature (Tg or Tm) of the polycarbodiimide.
• Tg or Tm softening temperature
• the lowest of the softening or melting temperatures should be used. If one of the temperatures mentioned were exceeded, this would inevitably lead to (premature and therefore undesirable) crosslinking of the polymer.
• the largely dry, latently reactive coatings, films or powders can still have a residual moisture content of 0.1-5%.
• latent-reactive adhesive dispersions according to the invention latent-reactive adhesive layers, self-supporting latent-reactive adhesive films or the latent-reactive adhesive powders are used for bonding a wide variety of substrate combinations:
• the aqueous formulation according to the invention can e.g. applied to a substrate by spray, squeegee or roller application and dried (if necessary at an elevated temperature).
• a substrate equipped with a latent-reactive adhesive polymer is obtained in this way.
• the latently reactive adhesive film can be laminated to a film web using pressure and at a temperature below the reaction temperature of the reactive adhesive polymer (e.g., a calender). In this way, the substrate equipped with the latently reactive adhesive polymer is held.
• a reactive adhesive polymer e.g., a calender
• the adhesive powder can be sprinkled onto a substrate, for example film web, textile, spring, etc., and heated by heating the adhesive powder (for example with an infrared radiator, with a heated fuft, or a Heating channel) are sintered onto the substrate.
• a substrate for example film web, textile, spring, etc.
• the joining process can be carried out with the adhesive polymer applied on one side (i.e. the adhesive polymer is only on one surface of the substrates provided for the joining process) or with the adhesive polymer applied on both sides (i.e. the adhesive polymer is on both surfaces of the substrates provided for the joining process).
• the optimal procedure for the respective application is i.a. depending on the wetting behavior of the substrate surfaces during the heat activation with the thermoplastically softened adhesive layer and can easily be determined by a person skilled in this technical field as part of his routine work.
• the latently reactive adhesive polymer must be heated and liquefied at least to the extent that it a) can wet the adhesive-free substrate surface well (or can flow well onto the substrate surface), and / or b) the polymer chains of the adhesive polymer as well as flowable ones that they flow into one another (when applying adhesive on both sides).
• the crosslinking reaction is triggered.
• the joining conditions pressure, temperature and duration
• the adhesive polymer can be heated immediately before the joining process by means of IR beams, in a heating channel, by microwaves, by blowing hot air or in an induction field.
• the joining process is then carried out by e.g. Deep-drawing the substrate with the heated adhesive layer onto the second substrate.
• the substrates intended for bonding are placed in a heated press and pressed under the action of pressure and temperature.
• the latently reactive adhesive film can also be inserted separately between the substrates to be bonded during press lamination.
• the particle size is determined according to ISO 13320 (laser diffraction). Five individual measurements are carried out each time and the arithmetic mean of the individual measurements is given. Measuring device: Malvern Mastersizer 3000.
• dicyclohexylcarbodiimide DCC was dissolved in ethanol (concentrations: 0.1 mmol / g, 0.2 mmol / g, 0.5 mmol / g, 1.0 mmol / g, 1.5 mmol / g and 2 mmol / G).
• the IR spectra were recorded from these solutions.
• the peak areas (PA) of the carbodiimide band at approx. 2118 cm 1 were determined.
• a calibration line was created from the data (concentration c of the DCC solutions and the determined PA):
• PA m ⁇ c [meq DCC / g], where m represents the slope of the calibration line.
• aqueous preparation was dried at RT.
• 10 g of the dried residue were dissolved in 20 g of xylene.
• the peak area of the xylene solution was then determined at approx. 2118 cm-1 by means of ATR infrared spectroscopy.
• the carbodiimide concentration of the polycarbodiimide resin in the aqueous preparation [meq DCC / g] was calculated by P AX 3 ⁇ 100 / (axm).
• the change in the carbodiimide concentration is given in% based on the initial value. Due to the measurement conditions, an inaccuracy for the specification of the change in the carbodiimide concentration of ⁇ 5 percentage points is assumed.
• the glass transition characterizes the temperature range in which the connection changes from the brittle state to the visco-elastic state.
• the glass transition temperature is determined using DSC (differential scanning calorimetry).
• the glass transition temperature (Tg) is the temperature at half the height of the difference in specific heat capacity between the beginning and end of the glass transition (graphic evaluation, tangent section).
• the heating rate during the measurement is 20K / min.
• the melting temperature is determined using DSC (differential scanning calorimetry).
• the melting temperature (Tm) is the temperature at which the melting peak in the DSC diagram reaches its maximum height.
• the heating rate during the measurement is 20K / min.
• the softening temperature is synonymous with the glass transition temperature or the melting point of the compound.
• MFT Minimum film formation temperature
• the MFT is the lowest temperature at which an adhesive or paint formulation can form a cohesive film.
• the MFT is determined in accordance with DIN ISO 2115 for aqueous dispersions.
• a polymer that contains both crystalline and amorphous areas (domains) is referred to as partially crystalline.
• the term plays a raw role in polymer physics.
• One method for determining the crystallinity of a polymer is DSC. DSC can be used to determine the melting temperature (temperature at the maximum of the melting peak) and the heat of fusion (area of the melting peak).
• 5 cm x 2 cm canvas strips are coated on one end with 1 cm x 2 cm adhesive dispersion (brush application approx. 100 g / m 2 wet).
• the adhesive layer is dry after 1 hour.
• the adhesive-coated surfaces are placed one on top of the other so that the joined test specimen can be tested in the tensile shear test.
• the test specimens are placed in a heated membrane press and placed over Imin. or 5min. pressed under the action of heat at 4 bar.
• the temperature on the membrane press is set so that the temperature in the glue joint after 1min. or 5min. reaches the value of 70 ° C, 80 ° C, 90 ° C, 100 ° C, 110 ° C and 120 ° C.
• the Canvar strips coated with adhesive dispersions were stored for 1 month and 2 months in a standard climate (23 ° C., 50% relative humidity) before pressing. Determination of the softening temperature of the adhesive bond:
• the softening temperature is determined in the tensile shear test.
• the samples are hung in a heating cabinet, loaded with a 4 kg weight and carried out within 30 minutes. tempered to 40 ° C.
• the heating cabinet is then heated linearly at a heating rate of 0.5K / min.
• the failure (the softening temperature) of the adhesive bond is automatically registered when the adhesive bond is opened.
• the final temperature of the method is 150 ° C.
• the polymer sample is placed in the measuring unit (plate-plate geometry with a diameter of 7.9 mm and plate spacing 0.65 mm) of the oscillation rheometer (Rheometrics ARES), which is heated to 25 ° C. Hz and a deformation of 0.02 applied. During the measurement, the temperature of the measuring unit is heated from 25 ° C to 150 ° C at a heating rate of 5K / min.
• the values for the storage modulus [G ‘] (elastic component) and the loss modulus [G‘ ‘] (viscous component) are calculated from the measured torque, the phase shift between stress and strain and the measurement geometry (1).
• the two modules [G ‘] and [G‘ ‘] enable the qualitative evaluation of the flow behavior of the polymer and thus allow conclusions to be drawn about the durability of an adhesive bond.
• Cycloaliphatic polyisocyanate H12MDI 4,4 'diisocyanatodicyclohexyl methane, CAS no.
• Stabaxol ® P Aromatic polycarbodiimide in powder form. Use of Stabaxol ® P as a hydrolysis protection agent for thermoplastic polyurethanes (TPU), polyesters (PET), polyamides (PA) etc. Stabaxol ® P has a melting point between 60 ° C and 90 ° C. The carbodiimide content is at least 12.5%. (Lanxess AG, Cologne, DE)
• Stabaxol ® P100 polycarbodiimide in powder form.
• Stabaxol ® P is used as an anti-hydrolysis agent for polyester (PET), polyamides (PA), etc., among others.
• Stabaxol ® P 100 has a melting point between 100 ° C and 120 ° C. The carbodiimide content is at least 13%.
• Disperbyk ® 191 VOC- and solvent-free wetting and dispersing additive for aqueous coating systems and adhesives. Suitable for binder-free and binder-containing pigment concentrates. Especially optimized for emulsion systems. (BYK-Chemie GmbH 46483 Wesel)
• BYK ® 024 VOC-free silicone-containing defoamer for aqueous dispersion coatings, printing inks and overprint varnishes as well as dispersion adhesives. (BYK-Chemie GmbH 46483 Wesel)
• PUD 1 Dispercoll ® U 2824 XP: polyurethane dispersion based on polyester diol from Covestro GmbH AG, 51365 Leverkusen; Solids content approx. 40% by weight.
• the polymer contains approx. 18 mmol COOH groups / 100 g.
• the polymer has a glass transition temperature of approx. -40 ° C.
• the melting point of the crystalline segments in the polyurethane polymer chain is + 47 ° C.
• PUD 2 Dispercoll ® U XP 2643: polyurethane dispersion based on polypropylene glycol from Covestro Deutschland AG, 51365 Leverkusen; Solids content approx. 40% by weight.
• the polymer contains approx. 18 mmol COOH groups / 100 g.
• the polymer has a glass transition temperature of approx. -50 ° C.
• the polycarbodiimide resin has a glass transition temperature of + 35 ° C
• the solid polycabodiimide (Example 1) was ground to the suitable particle size dv50 ⁇ 100pm by grinding in a knife mill or a jet mill (Hosowaka-Alpine Type 100 AFG).
• polycarbodiimide powders are used as hydrolysis inhibitors for polymers containing polyester segments (polyesters, TPUs, etc.).
• Example 3a and 3b 100g polycarbodiimide la or lb, 135g water, 10g Goalamul ® 1820- liquid and 2.6g Borchigel ALA ® are placed in a beaker and with a dissolver disc at 3000 rpm for 5 min. mixed. The result is a pseudoplastic paste that can be stirred directly into the polymer dispersion.
• Example 4 100g polycarbodiimide lc, 142g water, 20g Disperbyk ® 191, 1.4 g of BYK ® 024 and 4g Borchigel L ® 75N are placed in a beaker and with a dissolver disc at 3000rpm for 5 minutes. mixed. The result is a viscous paste that can be stirred directly into the polymer dispersion.
• Examples 5 and 6 100g polycarbodiimide Example 2a or 2b, 136g water, 20g Disperbyk ®
• the examples marked with * are comparative examples
• the oscillation measurements are carried out on dried adhesive films.
• the dispersions Example 7 *, 10, 11, 14 *, 18 and 19 were poured into Teflon dishes in such a way that the adhesive polymers had a layer thickness of about 1 mm after drying.
• the aqueous polycarbodiimide subspersion Example 3 was stored at 23 ° C.
• the carbodiimide concentration of the fresh polycarbodiimide suspension and that of the polycarbodiimide suspension stored for 1 month or 2 months was determined after the dried polycarbodiimide resin had been dissolved in xylene.
• aqueous formulations of the solid polycarbodiimide are sufficiently stable for at least 2 months.
• FIG. 2 shows that the crosslinking of the polymer chains of the dispersion polymer from PUD 2 by the solid polycarbodiimide (Example 3b) is evident.
• Fig. 3 shows that the Staboxol P ® used as hydrolysis has 100 (Example 2a) and 160 ° C no Vernetzer Ober. The value for G 'is below the value of G ”over the entire temperature range.
• Fig. 4 shows that the Staboxol P ® used as hydrolysis to 160 ° C (Example 2b) not Vernetzer Ober.
• the value for G ' is below the value of G “over the entire temperature range.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Polymers & Plastics (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Dispersion Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Manufacturing & Machinery (AREA)
• Life Sciences & Earth Sciences (AREA)
• Materials Engineering (AREA)
• Wood Science & Technology (AREA)
• Polyurethanes Or Polyureas (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Paints Or Removers (AREA)
• Adhesives Or Adhesive Processes (AREA)

Priority Applications (5)

Applications Claiming Priority (2)

Publications (1)

Family

ID=66251656

Family Applications (1)

Country Status (6)

Cited By (4)

Families Citing this family (4)

Citations (25)

Family Cites Families (10)

• 2019
  • 2019-04-24 EP EP19170799.1A patent/EP3730528A1/de active Pending
• 2020
  • 2020-04-17 EP EP20719190.9A patent/EP3959251B1/de active Active
  • 2020-04-17 KR KR1020217033916A patent/KR20220005459A/ko not_active Withdrawn
  • 2020-04-17 CN CN202080030762.XA patent/CN113710717B/zh active Active
  • 2020-04-17 JP JP2021562842A patent/JP2022530013A/ja active Pending
  • 2020-04-17 WO PCT/EP2020/060803 patent/WO2020216680A1/de not_active Ceased
  • 2020-04-17 US US17/603,392 patent/US20220177751A1/en active Pending

Patent Citations (28)

Non-Patent Citations (9)

Also Published As

Similar Documents

Legal Events