WO2020213684A1 - 吸音材 - Google Patents

吸音材 Download PDF

Info

Publication number
WO2020213684A1
WO2020213684A1 PCT/JP2020/016744 JP2020016744W WO2020213684A1 WO 2020213684 A1 WO2020213684 A1 WO 2020213684A1 JP 2020016744 W JP2020016744 W JP 2020016744W WO 2020213684 A1 WO2020213684 A1 WO 2020213684A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin film
sound absorbing
base material
material layer
absorbing material
Prior art date
Application number
PCT/JP2020/016744
Other languages
English (en)
French (fr)
Inventor
慧 高安
亜唯 横倉
智彦 小竹
Original Assignee
日立化成株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日立化成株式会社 filed Critical 日立化成株式会社
Priority to JP2021514219A priority Critical patent/JPWO2020213684A1/ja
Publication of WO2020213684A1 publication Critical patent/WO2020213684A1/ja

Abstract

本開示は、第一樹脂フィルムと、連通孔を有する第一基材層と、第二樹脂フィルムと、連通孔を有する第二基材層と、をこの順に備える吸音材に関する。

Description

吸音材
　本発明は、吸音材に関する。
　メルトブロー不織布からなる単一層の吸音構造体が知られている（例えば、特許文献１）。
特開２０１２－２１４９５７号公報
　不織布からなる単一層の吸音構造体の場合、特に低周波数領域における吸音特性が不充分である。
　本発明は上記事情に鑑みてなされたものであり、低周波数領域における吸音特性に優れる吸音材を提供することを目的とする。
　本発明は、第一樹脂フィルムと、連通孔を有する第一基材層と、第二樹脂フィルムと、連通孔を有する第二基材層と、をこの順に備える吸音材を提供する。
　一態様において、上記第一基材層及び上記第二基材層が、樹脂発泡体又は不織布であってよい。
　一態様において、上記第一樹脂フィルム及び上記第二樹脂フィルムが、ポリオレフィン、ポリエステル又はポリアミドから構成されていてよい。
　一態様において、吸音材が、上記第一樹脂フィルム及び上記第二樹脂フィルムの少なくともいずれかの表面に、金属蒸着層をさらに備えてよい。
　一態様において、吸音材が、上記第一樹脂フィルム及び上記第一基材層間、上記第一基材層及び上記第二樹脂フィルム間、並びに上記第二樹脂フィルム及び上記第二基材層間の少なくともいずれかに、接着剤層をさらに備えてよい。
　一態様において、吸音材の厚さが１～１００ｍｍであってよい。
　一態様において、吸音材が、１ｋＨｚ以下のいずれかの周波数において、ＪＩＳ　Ａ　１４０５－１に準拠して測定される０．４５以上の垂直入射吸音率を有してよい。
　本発明によれば、低周波数領域における吸音特性に優れる吸音材を提供することができる。
吸音材の模式断面図である。 実施例１及び比較例１の垂直入射吸音率を示す図である。 実施例２及び比較例２の垂直入射吸音率を示す図である。 実施例３及び比較例３の垂直入射吸音率を示す図である。 実施例４及び比較例４の垂直入射吸音率を示す図である。 実施例５及び比較例５の垂直入射吸音率を示す図である。 実施例６の垂直入射吸音率を示す図である。
＜吸音材＞
　図１は吸音材の模式断面図である。吸音材１０は、第一樹脂フィルム１と、連通孔を有する第一基材層２と、第二樹脂フィルム３と、連通孔を有する第二基材層４と、をこの順に備える。第一樹脂フィルム側から入射した音（音響エネルギー）は、吸音材を透過する際に熱エネルギーとして散逸される。これにより音の減衰が観察される。
（基材層）
　連通孔を有する基材層としては、樹脂発泡体、不織布、高分子多孔体、多孔質セラミック等が挙げられる。これらのうち、低周波数領域における吸音特性に優れる観点から、基材層は樹脂発泡体又は不織布であってよい。第一基材層及び第二基材層は、同じ素材から構成されていてもよく、異なる素材から構成されていてもよい。
　樹脂発泡体の素材としては、例えば、ポリエチレン樹脂、ポリプロピレン樹脂、ポリウレタン樹脂、ポリエステル樹脂、アクリル樹脂、ポリスチレン樹脂、メラミン樹脂、シリコーン樹脂、天然ゴム、合成ゴム等が挙げられる。耐熱性、難燃性等の観点から、樹脂発泡体の素材はメラミン樹脂であってよい。
　不織布を構成する繊維としては、有機繊維及び無機繊維が挙げられる。有機繊維としては、例えば、ポリエチレン（低密度又は高密度）、ポリプロピレン、共重合ポリエチレン、共重合ポリプロピレン等のポリオレフィン繊維、ポリエチレンテレフタレート、ポリトリメチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート、ポリブチレンナフタレート等のポリエステル繊維、アクリル繊維、ポリアミド繊維、ナイロン繊維、レーヨン繊維、ウール等の天然繊維などが挙げられる。また、無機繊維としては、ガラス繊維、金属繊維、セラミックス繊維、炭素繊維等が挙げられる。不織布を構成する繊維は、これらを１種又は２種以上を含むことができる。
　基材層の厚さは、低周波数領域における吸音特性に優れる観点から、０．１～５０ｍｍとすることができ、０．５～２０ｍｍであってもよく、２．０～２０ｍｍであってもよく、２．０～１０ｍｍであってもよい。第一基材層及び第二基材層は、同じ厚さを有していてもよく、異なる厚さを有していてもよい。低周波数領域における吸音特性に優れる観点から、第一基材層（音の入射側の基材層）の厚さが、第二基材層の厚さよりも薄くてよい。
　基材層の目付は、低周波数領域における吸音特性に優れる観点から、１０～１０００ｇ／ｍ２とすることができ、３０～７００ｇ／ｍ２であってもよく、５０～５００ｇ／ｍ２であってもよく、１５０～３００ｇ／ｍ２であってもよい。第一基材層及び第二基材層は、同じ目付を有していてもよく、異なる目付を有していてもよい。
　基材層の密度は、低周波数領域における吸音特性に優れる観点から、０．００５～１．０ｇ／ｃｍ３とすることができ、０．０１０～０．５０ｇ／ｃｍ３であってもよく、０．０１０～０．２０ｇ／ｃｍ３であってもよく、０．０２０～０．２０ｇ／ｃｍ３であってもよく、０．０２０～０．１５ｇ／ｃｍ３であってもよい。第一基材層及び第二基材層は、同じ密度を有していてもよく、異なる密度を有していてもよい。
（樹脂フィルム）
　樹脂フィルムを構成する樹脂としては、例えば、ポリエチレン（低密度又は高密度）、ポリプロピレン、共重合ポリエチレン、共重合ポリプロピレン等のポリオレフィン系樹脂、ポリエチレンテレフタレート、ポリトリメチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート、ポリブチレンナフタレート等のポリエステル系樹脂、ＰＴＦＥ、ＦＥＰ、ＰＦＡ等のフッ素系樹脂、ポリイミド系樹脂、ポリアミド系樹脂、アラミド系樹脂、塩化ビニル系樹脂、アクリル系樹脂、ポリカーボネート系樹脂、ポリフェニレンサルファイド系樹脂、ポリビニルアルコール系樹脂、ポリスチレン系樹脂、ポリアクリロニトリル系樹脂、エチレン・酢酸ビニル系樹脂などが挙げられる。第一樹脂フィルム及び第二樹脂フィルムは、同じ素材から構成されていてもよく、異なる素材から構成されていてもよい。
　樹脂フィルムの厚さは、低周波数領域における吸音特性に優れる観点から、０．５～５００μｍとすることができ、５～２５０μｍであってもよく、１０～１００μｍであってもよい。第一樹脂フィルム及び第二樹脂フィルムは、同じ厚さを有していてもよく、異なる厚さを有していてもよい。また、低周波数領域における吸音特性に優れる観点から、基材層の厚さに対する樹脂フィルムの厚さの比率（基材層の厚さ/樹脂フィルムの厚さ）は、１～２００００とすることができ、１０～１００００であってもよく、１００～１０００であってもよい。
　樹脂フィルムは、フィルム特性の調整による吸音効果の向上機能、及び熱線反射機能の付与の観点から、その表面に金属蒸着層を備えていてもよい。すなわち、吸音材は、上記第一樹脂フィルム及び上記第二樹脂フィルムの少なくともいずれかの表面に、金属蒸着層をさらに備えてよい。金属蒸着層は、アルミニウム、銅、亜鉛、亜鉛合金、銀等の金属を真空蒸着等の物理蒸着又は化学蒸着により形成できる。金属蒸着層は樹脂フィルムの両面に設けられていてもよく、一方の面に設けられていてもよい。
　樹脂フィルムは、低周波領域の吸音効果の向上及び吸音周波数ピークの調整の観点から、有孔フィルムであってもよい。有孔フィルムは格子状や菱形状に配列した孔を有してよい。当該孔は、低周波数領域における吸音特性に優れる観点から、直径が０．１～５０．０ｍｍの円形状であってよく、０．２～１０．０ｍｍの円形状であってよく、０．３～５．０ｍｍの円形状であってよい。孔の形状は、円形、楕円形、長方形、多角形等であってよい。
（他の樹脂フィルム及び他の基材層）
　吸音材は、低周波領域の吸音効果の向上及び吸音周波数ピークの調整の観点から、さらに他の樹脂フィルム及び連通孔を有する他の基材層を、備えていてもよい。すなわち、吸音材は、第一樹脂フィルム、連通孔を有する第一基材層、第二樹脂フィルム、及び連通孔を有する第二基材層に加えて、さらに第三樹脂フィルム及び連通孔を有する第三基材層、第四樹脂フィルム及び連通孔を有する第四基材層等をこの順に備えていてもよい。他の樹脂フィルム及び他の基材層には、上記樹脂フィルム及び基材層の項にて説明した事項を適用できる。
（接着剤層）
　吸音材は、上記の各層間にさらに接着剤層を備えていてもよい。例えば、吸音材は、第一樹脂フィルム及び第一基材層間、第一基材層及び第二樹脂フィルム間、並びに第二樹脂フィルム及び第二基材層間の少なくともいずれかに接着剤層を備えていてもよい。接着剤層としては、ポリエステル樹脂、酢酸ビニル樹脂、エチレン・酢酸ビニル共重合樹脂、イソブテン・無水マレイン酸共重合樹脂、アクリル共重合樹脂、アクリルモノマー、アクリルオリゴマー、塩化ビニル樹脂、ウレタン樹脂（湿気硬化型含む）、シリル化ウレタン樹脂、エポキシ樹脂、変性エポキシ樹脂、ポリエチレン樹脂等のポリオレフィン樹脂、アイオノマー樹脂、シリコーン樹脂、変性シリコーン樹脂、スチレン・ブタジエンゴム、クロロプレンゴム、ニトリルゴム等の合成ゴム、イソプレンゴム等の天然ゴム、水ガラス、シリケート等の接着成分を含む層、あるいは紙、布、不織布、繊維、樹脂フィルム、金属テープ等から構成される支持体の両面にこれらの接着成分を含む層を備える積層物などが挙げられる。各接着剤層は、同じ素材から構成されていてもよく、異なる素材から構成されていてもよい。
　接着剤層の厚さは特に限定されないが、０．０１～５００μｍとすることができ、１～２５０μｍであってもよい。各接着剤層は、同じ厚さを有していてもよく、異なる厚さを有していてもよい。
　吸音材の厚さは、吸音特性の発現、材料の施工性、省スペース化等の観点から、１～１００ｍｍとすることができ、２～５０ｍｍであってもよく、５～３０ｍｍであってもよい。
　吸音材は、１ｋＨｚ以下のいずれかの周波数において、具体的には例えば２５０Ｈｚ、５００Ｈｚ及び１ｋＨｚの少なくともいずれかの周波数において、ＪＩＳ　Ａ　１４０５－１に準拠して測定される０．４５以上、又は０．５以上の垂直入射吸音率を有することができる。当該垂直入射吸音率は、１ｋＨｚにおいて０．３以上とすることができ、０．４以上であってもよい。当該垂直入射吸音率は、７５０Ｈｚにおいて０．２５以上とすることができ、０．３以上であってもよい。当該垂直入射吸音率は、５００Ｈｚにおいて０．１以上とすることができ、０．１２５以上であってもよい。
＜吸音材の製造方法＞
　吸音材は、各層を積層することにより製造することができる。吸音材は、上記のとおり接着剤層を備えることにより各層が接着された状態で用いられてもよいが、各層が接着されずに用いられてもよい。また、一部の層間のみに接着剤層が設けられてもよい。吸音材を構成する積層体は、筐体に収納された状態で用いてもよい。
＜吸音材の用途＞
　上記吸音材は低周波数領域における吸音特性に優れる。そのため、上記吸音材は、自動車、鉄道車両、航空機、船舶、住宅等の建築物、電子機器、精密機械などの用途において好適に用いることができる。ここでいう低周波領域とは、周波数が１ｋＨｚ以下の領域とすることができ、８００Ｈｚ以下の領域であってもよく、７５０Ｈｚ以下の領域であってもよく、５００Ｈｚ以下の領域であってもよい。
　以下、実施例によって本発明を更に詳細に説明するが、本発明はこれらの実施例に限定されるものではない。
（基材層の準備）
　表１に示す基材層を準備した。
Figure JPOXMLDOC01-appb-T000001
（樹脂フィルムの準備）
　樹脂フィルムとして、厚さ１２μｍの両面アルミニウム蒸着ポリエチレンテレフタレートフィルム（Ａｌ蒸着ＰＥＴ）を準備した。
（接着剤層の準備）
　以下の接着剤層を準備した。
　　両面テープ：スリーエムジャパン株式会社、ＰＧＤ－１００、厚さ０．１２ｍｍ
　　スプレー糊：スリーエムジャパン株式会社、スプレーのり７７
（吸音材の作製）
　表２に示す構成を有する吸音材を作製した。各層の接着には、両面テープ又はスプレー糊を用いた。
Figure JPOXMLDOC01-appb-T000002
（吸音材の吸音特性評価）
　作製した各吸音材の垂直入射吸音率を、以下に従って測定した。表２中の左に記載した層側から音を入射した。測定結果を表３に示す。
　　装置名：４２０６型インピーダンス管（ブリュエル・ケアー社）
　　測定方法：垂直入射吸音率（ＪＩＳ　Ａ　１４０５－１に準拠）
　　測定範囲：５０～１６００Ｈｚ
Figure JPOXMLDOC01-appb-T000003
　図２～図７は、各実施例及び比較例の垂直入射吸音率を示す図である。同図に示されるように、実施例の吸音材は低周波数領域における吸音特性に優れることが分かる。
　１…第一樹脂フィルム、２…連通孔を有する第一基材層、３…第二樹脂フィルム、４…連通孔を有する第二基材層、１０…吸音材。

Claims (7)

  1. 　第一樹脂フィルムと、連通孔を有する第一基材層と、第二樹脂フィルムと、連通孔を有する第二基材層と、をこの順に備える吸音材。
  2. 　前記第一基材層及び前記第二基材層が、樹脂発泡体又は不織布である、請求項１に記載の吸音材。
  3. 　前記第一樹脂フィルム及び前記第二樹脂フィルムが、ポリオレフィン、ポリエステル又はポリアミドから構成される、請求項１又は２に記載の吸音材。
  4. 　前記第一樹脂フィルム及び前記第二樹脂フィルムの少なくともいずれかの表面に、金属蒸着層をさらに備える、請求項１～３のいずれか一項に記載の吸音材。
  5. 　前記第一樹脂フィルム及び前記第一基材層間、前記第一基材層及び前記第二樹脂フィルム間、並びに前記第二樹脂フィルム及び前記第二基材層間の少なくともいずれかに、接着剤層をさらに備える、請求項１～４のいずれか一項に記載の吸音材。
  6. 　厚さが１～１００ｍｍである、請求項１～５のいずれか一項に記載の吸音材。
  7. 　１ｋＨｚ以下のいずれかの周波数において、ＪＩＳ　Ａ　１４０５－１に準拠して測定される０．４５以上の垂直入射吸音率を有する、請求項１～６のいずれか一項に記載の吸音材。
PCT/JP2020/016744 2019-04-18 2020-04-16 吸音材 WO2020213684A1 (ja)