WO2020196666A1 - Mélange de polyols liquide pour la production de mousse de polyuréthane d'halogénoalcène - Google Patents

Mélange de polyols liquide pour la production de mousse de polyuréthane d'halogénoalcène Download PDF

Info

Publication number
WO2020196666A1
WO2020196666A1 PCT/JP2020/013456 JP2020013456W WO2020196666A1 WO 2020196666 A1 WO2020196666 A1 WO 2020196666A1 JP 2020013456 W JP2020013456 W JP 2020013456W WO 2020196666 A1 WO2020196666 A1 WO 2020196666A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
formula
carbon atoms
polyol
tetrafluoropropene
Prior art date
Application number
PCT/JP2020/013456
Other languages
English (en)
Japanese (ja)
Inventor
徳本勝美
Original Assignee
東ソー株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 東ソー株式会社 filed Critical 東ソー株式会社
Publication of WO2020196666A1 publication Critical patent/WO2020196666A1/fr

Abstract

Relativement aux mélange de polyol liquides pour la production de mousse de polyuréthane d'halogénoalcène, la stabilité de stockage a été problématique pour des compositions de mélange de polyols. La présente invention concerne une composition de mélange de polyols liquide qui est destinée à produire une mousse de polyuréthane et qui contient un polyol, une hydrohalogéno-oléfine et un composé représenté par la formule (1) (dans la formule, Ar1 représente un groupe aromatique monocyclique, à cycle lié ou à cycle condensé ayant de 3 à 20 atomes de carbone et ayant éventuellement un substituant, R1 représente un groupe alkyle bivalent linéaire, ramifié ou cyclique ayant 2 à 6 atomes de carbone, chaque R2 représentant indépendamment un groupe alkyle ayant de 2 à 4 atomes de carbone ou un groupe hydroxy alkyle ayant 2 à 4 atomes de carbone, deux R2 pouvant être liés l'un à l'autre pour former un hétérocycle comprenant au moins un atome d'azote, et n représente 0 ou 1).
PCT/JP2020/013456 2019-03-26 2020-03-25 Mélange de polyols liquide pour la production de mousse de polyuréthane d'halogénoalcène WO2020196666A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2019-058437 2019-03-26
JP2019058437 2019-03-26

Publications (1)

Publication Number Publication Date
WO2020196666A1 true WO2020196666A1 (fr) 2020-10-01

Family

ID=72612024

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/013456 WO2020196666A1 (fr) 2019-03-26 2020-03-25 Mélange de polyols liquide pour la production de mousse de polyuréthane d'halogénoalcène

Country Status (2)

Country Link
JP (1) JP2020164854A (fr)
WO (1) WO2020196666A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2023221693A1 (fr) * 2022-05-20 2023-11-23 海信容声(广东)冰箱有限公司 Mousse de polyuréthane rigide, procédé de préparation et matériau de conservation de chaleur, réfrigérateur et congélateur comprenant une mousse de polyuréthane

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
PL118230B1 (en) * 1978-05-20 1981-09-30 Lozysk Tocznych Iskra Fab Cyanide-free alkaline bath for lustre zinc platingeskom,ne soderzhahhaja cianidov
JP2007516339A (ja) * 2003-12-23 2007-06-21 ダウ グローバル テクノロジーズ インコーポレイティド イミン結合および第３級アミンを含有する堅牢触媒（ｎｏｎ−ｆｕｇｉｔｉｖｅｃａｔａｌｙｓｔｓ）、ならびにそれから作製したポリウレタン製品

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
PL118230B1 (en) * 1978-05-20 1981-09-30 Lozysk Tocznych Iskra Fab Cyanide-free alkaline bath for lustre zinc platingeskom,ne soderzhahhaja cianidov
JP2007516339A (ja) * 2003-12-23 2007-06-21 ダウ グローバル テクノロジーズ インコーポレイティド イミン結合および第３級アミンを含有する堅牢触媒（ｎｏｎ−ｆｕｇｉｔｉｖｅｃａｔａｌｙｓｔｓ）、ならびにそれから作製したポリウレタン製品

Non-Patent Citations (4)

* Cited by examiner, † Cited by third party
Title
ITO, ISOO ET AL.: "Studies on Diphenylmethane derivatives. V. Synthesis and pharmacology of N-alkylaminopropyl-1,1-diphenylmethylamine and N- alkylaminopropyl-1,2-diphenylethylamine derivatives", YAKUGAKU ZASSHI, vol. 95, no. 4, 1975, pages 383 - 389 *
LIN, HONG-WEI: "Synthesis and Crystal Structures of Two Zinc(II) Complexes with the Schiff Bases 2-[(3-Diethylaminopropylimino)methyl]phenol and 1-[(3- Diethylaminopropylimino)methyl]naphthalen-2-ol", SYNTHESIS AND REACTIVITY IN INORGANIC, METAL-ORGANIC, AND NANO-METAL CHEMISTRY, vol. 39, no. 2, 2009, pages 73 - 77, XP055743327 *
MKHITARYAN, A. G.: "Reactions of aziridine, its dimer, 2,2-dimethyl-aziridine dimer, and beta, beta -bis-N-aziridinoethylamine with aromatic aldehydes and dialdehydes", BULLETIN OF THE RUSSIAN ACADEMY OF SCIENCES DIVISION OF CHEMICAL SCIENCE, vol. 41, no. 9, 1992, pages 1665 - 1671 *
SURREY, ALEXANDER R.: "The Preparation of 4-thiazolidones. III. The reaction of methyl thioglycolate with benzylidene dialkylaminoalkylamines", JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, vol. 71, 1949, pages 3105 - 3107, XP002028435, DOI: 10.1021/ja01177a048 *

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2023221693A1 (fr) * 2022-05-20 2023-11-23 海信容声(广东)冰箱有限公司 Mousse de polyuréthane rigide, procédé de préparation et matériau de conservation de chaleur, réfrigérateur et congélateur comprenant une mousse de polyuréthane

Also Published As

Publication number Publication date
JP2020164854A (ja) 2020-10-08

Similar Documents

Publication Publication Date Title
US10526462B2 (en) Stabilization of polyurethane foam polyol premixes containing halogenated olefin blowing agents
KR102292151B1 (ko) 할로겐화 올레핀 발포제를 함유하는 안정화된 폴리우레탄 폴리올 배합물
US20170313806A1 (en) Stabilization of foam polyol premixes containing halogenated olefin blowing agents
JP6816016B2 (ja) 硬質ポリウレタンフォーム用ポリオールプレミックス組成物
KR20180004114A (ko) 발포체, 발포성 조성물 및 인테그랄 스킨 발포체를 제조하는 방법
JP2014058663A (ja) ポリウレタンフォーム製造用の原料配合組成物
JP7336436B2 (ja) ヒドロハロオレフィン発泡剤を含むポリオールプレミックスのための触媒系
AU2018215934A1 (en) HFO containing PU formulation
JP7047332B2 (ja) ハロアルケン発泡ポリウレタン製造用の触媒組成物
JP7416817B2 (ja) 安定したポリウレタンフォーム系の製造に有用なアミン組成物
WO2020196666A1 (fr) Mélange de polyols liquide pour la production de mousse de polyuréthane d'halogénoalcène
JP2022547881A (ja) 相関移動活性三量体化触媒塩
JP2017206598A (ja) ハロアルケン発泡ポリウレタン製造用のポリオール系配合液組成物
JP6926660B2 (ja) ハロアルケン発泡ポリウレタン製造用のアミン触媒組成物
WO2022239734A1 (fr) Composition liquide mélangée à base de polyol pour la production de mousse de polyuréthane moussée à base d'hydrochlorofluorooléfine, et son utilisation
JP6056421B2 (ja) ポリウレタンフォーム製造用の組成物
JP6848184B2 (ja) ハロゲン化オレフィン発泡ポリウレタン製造用のアミン触媒組成物
JP5206123B2 (ja) アミン化合物、ポリウレタンフォーム製造用のポリオール組成物及びそれを用いたポリウレタンフォームの製造法
JP2019104808A (ja) ハロアルケン発泡ポリウレタン製造用のアミン触媒組成物
JP2017155101A (ja) ハロアルケン発泡ポリウレタン製造用の原料配合組成物
JP2024514134A (ja) 硬質フォーム系用モルホリン触媒の製造法及びその使用
WO2024022832A1 (fr) Composition d'amino-amide tertiaire utile dans la fabrication de polymères de polyuréthane
JP2022174719A (ja) ヒドロクロロフルオロオレフィン発泡ポリウレタンフォーム製造用のポリオール系配合液組成物、及びその用途
WO2024022833A1 (fr) Procédé de préparation d'une mousse de polyuréthane pour plaque de mélange souple

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20778820

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20778820

Country of ref document: EP

Kind code of ref document: A1