WO2020175092A1 - 積層体 - Google Patents

積層体 Download PDF

Info

Publication number
WO2020175092A1
WO2020175092A1 PCT/JP2020/004755 JP2020004755W WO2020175092A1 WO 2020175092 A1 WO2020175092 A1 WO 2020175092A1 JP 2020004755 W JP2020004755 W JP 2020004755W WO 2020175092 A1 WO2020175092 A1 WO 2020175092A1
Authority
WO
WIPO (PCT)
Prior art keywords
pressure
sensitive adhesive
adhesive layer
layer
meth
Prior art date
Application number
PCT/JP2020/004755
Other languages
English (en)
French (fr)
Inventor
昇祐 李
正熙 金
Original Assignee
住友化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友化学株式会社 filed Critical 住友化学株式会社
Priority to KR1020217028628A priority Critical patent/KR20210132074A/ko
Priority to CN202080015815.0A priority patent/CN113490869B/zh
Publication of WO2020175092A1 publication Critical patent/WO2020175092A1/ja

Abstract

本発明は、前面板側を内側にして屈曲した場合であっても、気泡の発生が抑制され、高温環境下において粘着力に優れた積層体を提供することを目的とする。本発明は、前面板と、第１粘着剤組成物を用いて形成された第１粘着剤層と、偏光子層と、第２粘着剤組成物を用いて形成された第２粘着剤層と、背面板と、をこの順に含み、前記第１粘着剤層の熱分解質量減少率をＲ１［％］、前記第２粘着剤層の熱分解質量減少率をＲ２［％］とすると、下記の関係式（１）：　Ｒ１＞Ｒ２　（１）を満たし、前記第１粘着剤層と前記第２粘着剤層は、熱分解質量減少率が１０質量％以上２０質量％以下である、積層体を提供する。

Description

\¥0 2020/175092 1 卩（：17 2020 /004755 明 細 書
発明の名称 ： 積層体
技術分野
[0001 ] 本発明は、 積層体に関する。
背景技術
[0002] 特開 2 0 1 8 _ 2 8 5 7 3号公報 （特許文献 1） には、 複数の粘着剤層を 有するフレキシブル画像表示装置用積層体が記載されている。
先行技術文献
特許文献
[0003] 特許文献 1 :特開 2 0 1 8 _ 2 8 5 7 3号公報
発明の概要
発明が解決しようとする課題
[0004] 前面板及び複数の粘着剤層を有する積層体を含む表示装置について、 前面 板側を内側にして屈曲した場合に積層体中の粘着剤層に気泡が発生する場合 があった。 また、 高温環境下において粘着剤層の粘着力が弱く、 粘着剤層と 被着部材との間に浮きや剥がれが生じる場合があった。
[0005] 本発明の目的は、 前面板側を内側にして屈曲した場合であっても、 気泡の 発生が抑制され、 高温環境下において粘着力に優れた積層体を提供すること である。
課題を解決するための手段
[0006] 本発明は、 以下の積層体を提供する。
〔 1〕 前面板と、 第 1粘着剤組成物を用いて形成された第 1粘着剤層と 、 偏光子層と、 第 2粘着剤組成物を用いて形成された第 2粘着剤層と、 背面 板と、 をこの順に含み、
前記第 1粘着剤層の熱分解質量減少率を 8 1 [%] 、 前記第 2粘着剤層の 熱分解質量減少率を 8 2 [%] とすると、 下記の関係式 （1） :
Figure imgf000003_0001
〇 2020/175092 2 卩（：170? 2020 /004755
を満たし、
前記第 1粘着剤層と前記第 2粘着剤層は、 熱分解質量減少率が 1 0質量％ 以上 2 0質量％以下である、 積層体。
〔2〕 前記第 1粘着剤組成物及び前記第 2粘着剤組成物は、 いずれも （ メタ） アクリル系ポリマーを含み、
前記 （メタ） アクリル系ポリマーは、 反応性官能基を有するモノマーに由 来する構成単位が全質量を基準に 5質量％未満である、 〔 1 〕 に記載の積層 体。
〔3〕 前記第 1粘着剤層及び前記第 2粘着剤層は、 いずれも （メタ） ア クリル系ポリマーを含み、
前記 （メタ） アクリル系ポリマーは、 重量平均分子量 （IV! %） が 2 0万以 上 1 5 0万以下である、 〔 1 〕 又は 〔2〕 に記載の積層体。
〔4〕 前記背面板は、 タッチセンサパネルである、 〔 1 〕 〜 〔3〕 のい ずれか 1項に記載の積層体。
〔5〕 〔 1 〕 〜 〔4〕 のいずれか 1項に記載の積層体を含む表示装置。
〔6〕 前記前面板側を内側にして屈曲可能である、 〔5〕 に記載の表示 装置。
発明の効果
［0007］ 本発明によれば、 前面板側を内側にして屈曲した場合であっても、 気泡の 発生が抑制され、 高温環境下において粘着力に優れた積層体を提供すること ができる。
図面の簡単な説明
［0008］ ［図 1］本発明に係る積層体の一例を示す概略断面図である。
［図 2］本発明に係る積層体の一例を示す概略断面図である。
［図 3］屈曲性試験の方法を説明する概略図である。
［図 4］本発明の積層体の製造方法を模式的に示す断面図である。
発明を実施するための形態
［0009］ 以下、 図面を参照して、 本発明の一態様に係る積層体 （以下、 単に 「積層 〇 2020/175092 3 卩（：170? 2020 /004755
体」 ともいう） について説明する。
[0010] ＜積層体＞
図 1 に本発明の一態様に係る積層体の概略断面図を示す。 積層体 1 〇〇は 、 前面板 1 0 1 と、 第 1粘着剤層 1 0 2と、 偏光子層 1 0 3と、 第 2粘着剤 層 1 0 4と、 背面板 1 0 5とをこの順に含む。 第 1粘着剤層 1 0 2は第 1粘 着剤組成物から形成されており、 第 2粘着剤層 1 0 4は第 2粘着剤組成物か ら形成されている。 以下、 第 1粘着剤層 1 0 2および第 2粘着剤層 1 0 4は 総称して粘着剤層ということがある。
[001 1 ] 積層体 1 0 0の厚みは、 積層体に求められる機能および積層体の用途等に 応じて異なるため特に限定されないが、 例えば 5 0 以上 4 , 0 0 0 以下であり、 好ましくは 1 0 0 以上 2 0 0 0 以下であり、 より好ま しく 1 5 0 01以上 1 0 0 0 以下である。
[0012] 積層体 1 0 0の平面視形状は、 例えば方形形状であってよく、 好ましくは 長辺と短辺とを有する方形形状であり、 より好ましくは長方形である。 積層 体 1 0 0の面方向の形状が長方形である場合、 長辺の長さは、 例えば 1 〇
Figure imgf000005_0001
以下である。 短辺の長さは、 例えば 5
Figure imgf000005_0002
以下であり、 好ま 以下であり、 より好ましくは 5 0 以上 3
Figure imgf000005_0003
構成する各層は、 角部が 加工されたり、 端 部を切り欠き加工されたり、 穴あき加工されたりしていてもよい。
[0013] 積層体 1 0 0は、 例えば表示装置等に用いることができる。 表示装置は特 に限定されず、 例えば有機エレクトロルミネッセンス （有機巳 !_） 表示装置 、 無機エレクトロルミネッセンス （無機巳 !_） 表示装置、 液晶表示装置、 電 界発光表示装置等が挙げられる。 表示装置はタッチパネル機能を有していて よい。
[0014] [粘着剤層の物性]
積層体 1 0 0は、 第 1粘着剤層 1 0 2の熱分解質量減少率を 1 [%] 、 第 2粘着剤層 1 0 4の熱分解質量減少率を 2 [%] とすると、 下記の関係 〇 2020/175092 4 卩（：170? 2020 /004755
式 （1）
Figure imgf000006_0001
を満たす。 粘着剤層の熱分解質量減少率 [%] は、 粘着剤層を形成する粘着 剤組成物の組成によって異なり、 粘着剤組成物の組成が同じであれば熱分解 質量減少率も同じであるとみなすことができる。 したがって、 第 1粘着剤層 1 02の熱分解質量減少率 1 [%] と、 第 2粘着剤層 1 04の熱分解質量 減少率 2 [%] とは、 第 1粘着剤層 1 02及び第 2粘着剤層 1 04を直接 測定しなくても同じ粘着剤組成物を用いて形成した粘着剤層を測定すること により得ることができる。 第 1粘着剤層 1 04の熱分解質量減少率 1 [% ] 及び第 2粘着剤層 1 04の熱分解質量減少率 2 [%] とは、 後述の実施 例の欄に記載の測定方法に従って測定される。
[0015] 第 1粘着剤層 1 02の熱分解質量減少率を 1 [%] 、 及び第 2粘着剤層
1 04の熱分解質量減少率を 2 [%] とすると、 下記の関係式 （2） 及び （3） :
Figure imgf000006_0002
1 〇 2£20 （3）
を満たし、 好ましくは下記の関係式 （23） 及び （33） :
Figure imgf000006_0003
を満たし、 より好ましくは下記の関係式 （2匕） 及び （3匕） ：
1 3£[¾ 1 £ 1 9 （2 b）
1 1 £[¾ 2£ 1 4 （3匕）
を満たす。
[0016] 積層体 1 00は、 前面板 1 01側を内側にして屈曲することが可能である 。 積層体を含む表示装置について、 前面板側を内側にして屈曲すると、 粘着 剤層中に気泡が発生する場合がある。 かかる気泡の発生は、 前面板側に近い 粘着剤層、 すなわち積層体 1 〇〇中では第 1粘着剤層 1 02において特に顕 著である。 本発明者による研究の結果、 第 1粘着剤層 1 02と第 2粘着剤層 〇 2020/175092 5 卩（：170? 2020 /004755
1 0 4の熱分解質量減少率が関係式 （1） , （2） , （3） を満たす場合、 前面板 1 0 1側を内側にして常温環境下で屈曲しても、 積層体 1 0 0中の粘 着剤層に発生する気泡を抑制でき、 高温環境下においても粘着剤層の性能が 維持されることを見出した。 より具体的には、 積層体 1 0 0の内面の屈曲半 径が 3 となるように 1 0万回繰り返し屈曲しても、 積層体 1 0 0中の粘 着剤層に発生する気泡を抑制できる （以下、 優れた 「常温屈曲性」 を有する ともいう。 ） ことを見出した。 常温屈曲性は、 後述の実施例の欄に記載の評 価方法に従って評価することができる。 積層体 1 0 0は、 前面板側を外側に して屈曲することが可能であってもよい。 積層体 1 0 0を適用した表示装置 は、 屈曲または巻回等が可能なフレキシブルディスプレイとして用いること ができる。 本明細書において、 屈曲には、 曲げ部分に曲面が形成される折り 曲げの形態が含まれ、 折り曲げた内面の屈曲半径は特に限定されない。 また 、 屈曲には、 内面の屈折角が 0度より大きく 1 8 0度未満である屈折、 およ び、 内面の屈曲半径がゼロに近似、 または内面の屈折角が〇度である折り畳 みも含む。
[0017] 第 1粘着剤層 1 0 2および第 2粘着剤層 1 0 4が、 関係式 （2） 及び （3 ） を満たすように第 1粘着剤組成物および第 2粘着剤組成物を調製する方法 として、 例えば粘着剤層を後述する粘着剤組成物 から構成したり、 後述す る （メタ） アクリル系ポリマー八を構成するモノマーの種類を変更したり、 （メタ） アクリル系ポリマー八の分子量を調節したり、 窒素原子及び （メタ ） アクリロイル基を有する化合物を含有させたりする方法等が挙げられる。
[0018] [粘着剤組成物]
第 1粘着剤層 1 0 2および第 2粘着剤層 1 0 4は、 一形態において、 （メ 夕） アクリル系ポリマーを含む粘着剤組成物 （以下、 粘着剤組成物八ともい う） から形成される。 粘着剤組成物 は、 活性エネルギー線硬化型、 熱硬化 型であってもよい。 なお本明細書において 「 （メタ） アクリル系ポリマー」 とは、 アクリル系ポリマーおよびメタクリル系ポリマーよりなる群から選ば れる少なくとも 1種を表す。 その他の 「 （メタ） 」 を付した用語においても 〇 2020/175092 6 卩（：170? 2020 /004755
同様である。 第 1粘着剤組成物及び第 2粘着剤組成物について、 いずれも （ メタ） アクリル系ポリマーを含む場合、 その （メタ） アクリル系ポリマーは 同じであっても、 異なっていてもよい。 以下、 粘着剤組成物八に含まれる （ メタ） アクリル系ポリマーを （メタ） アクリル系ポリマー八ともいう。
[0019] （メタ） アクリル系ポリマー八は、 得られる粘着剤層について、 関係式 （
2） 又は関係式 （3） を満たし易くなる観点から、 重量平均分子量 （!\/! %） が 2 0万以上 1 5 0万以下であることが好ましく、 3 0万以上 1 2 0万以下 であることがより好ましい。
[0020] 粘着剤組成物 に含まれる （メタ） アクリル系ポリマー は、 反応性官能 基を有するモノマーに由来する構成単位が、 好ましくは、 ポリマーの全質量 を基準に 5質量％未満である。 反応性官能基としては、 例えば水酸基、 カル ボキシル基、 アミノ基、 アミ ド基、 およびエポキシ基等が挙げられる。 これ により、 粘着剤層の柔軟性が向上し、 高温時の粘着剤層の気泡の発生を抑制 し易くなる傾向にある。 （メタ） アクリル系ポリマー八は、 反応性官能基を 有するモノマーに由来する構成単位が、 屈曲時の気泡抑制の観点からより好 ましくはポリマーの全質量を基準に〇. 0 1質量％以下であり、 さらに好ま しくは反応性官能基を有するモノマーに由来する構成単位を有さず、 なおさ らに好ましくは水酸基、 カルボキシル基、 アミノ基、 アミ ド基、 およびエポ キシ基を有しない。
[0021 ] （ 1） 活性エネルギー線硬化型粘着剤組成物
粘着剤組成物 が活性エネルギー線硬化型粘着剤組成物である場合、 粘着 剤組成物八に含まれる （メタ） アクリル系ポリマー八は、 直鎖状または分岐 鎖状の炭素原子数 1以上 2 4以下のアルキル基を有する （メタ） アクリル系 モノマーに由来する構成単位を含むことができる。 直鎖状または分岐鎖状の 炭素原子数 1以上 2 4以下のアルキル基を有する （メタ） アクリル系モノマ —としては、 例えば （メタ） アクリル酸アルキルエステル等であってよく、 その例としては、 （メタ） アクリル酸プチル、 （メタ） アクリル酸メチル、 （メタ） アクリル酸エチル、 （メタ） アクリル酸ヘキシル、 （メタ） アクリ 〇 2020/175092 7 卩（：170? 2020 /004755
ル酸オクチル、 （メタ） アクリル酸ラウリル、 （メタ） アクリル酸イソオク チル、 （メタ） アクリル酸イソデシル、 （メタ） アクリル酸 2 -エチルヘキ シル、 （メタ） アクリル酸イソボルニル等が挙げられる。 （メタ） アクリル 系ポリマー八は、 上記 （メタ） アクリル酸アルキルエステルの 1種または 2 種以上をモノマーとする重合体または共重合体であってよい。 粘着剤組成物 八中の （メタ） アクリル系ポリマー八の含有量は、 例えば粘着剤組成物八の 固形分 1 〇〇質量部に対して 5 0質量％以上 1 0 0質量％以下であってよく 、 好ましくは 8 0質量％以上 9 9 . 5質量％以下であり、 より好ましくは 9 〇質量％以上 9 9質量％以下である。
[0022] （メタ） アクリル系ポリマー八の重量平均分子量
Figure imgf000009_0001
は、 例えば 2 0 万以上 8 0万以下であってよく、 屈曲時の気泡抑制の観点から好ましくは 3 0万以上 7 0万以下である。 重量平均分子量 （1\/1 ） は、 後述する実施例の 欄において説明する測定方法に従って測定することができる。
[0023] 粘着剤組成物八は、 （メタ） アクリル系ポリマー八を 1種または 2種以上 含むものであってよい。 また、 粘着剤組成物 は、 その構成成分として （メ 夕） アクリル系ポリマー八のみを含むものであってもよいし、 架橋剤をさら に含有してもよい。 架橋剤としては、 2価以上の金属イオンであって、 カル ボキシル基との間でカルボン酸金属塩を形成するもの；ポリアミン化合物で あって、 カルボキシル基との間でアミ ド結合を形成するもの；ポリエポキシ 化合物やポリオールであって、 カルボキシル基との間でエステル結合を形成 するもの；ポリイソシアネート化合物であって、 カルボキシル基との間でア ミ ド結合を形成するもの等が挙げられる。 中でも、 ポリイソシアネート化合 物が好ましい。 粘着剤組成物 が架橋剤を含む場合、 架橋剤の含有量は、 （ メタ） アクリル系ポリマー八 1 0 0質量部に対して、 例えば 5質量部以下で あってよく、 好ましくは 1質量部以下、 より好ましくは〇. 5質量部以下、 さらに好ましくは〇. 1質量部以下であり、 粘着剤組成物 は架橋剤を含ま ないことが最も好ましい。
[0024] 活性エネルギー線硬化型粘着剤組成物とは、 紫外線や電子線のような活性 〇 2020/175092 8 卩（：170? 2020 /004755
エネルギー線の照射を受けて硬化する性質を有しており、 活性エネルギー線 照射前においても粘着性を有してフィルム等の被着体に密着させることがで き、 活性エネルギー線の照射によって硬化して密着力等の調整ができる性質 を有する粘着剤組成物である。
[0025] 活性エネルギー線硬化型粘着剤組成物は、 紫外線硬化型であることが好ま しい。
[0026] 粘着剤組成物 が活性エネルギー線硬化型粘着剤組成物である場合、 粘着 剤組成物 は、 活性エネルギー線重合性化合物、 光重合開始剤や光増感剤等 をさらに含有することができる。
[0027] 活性エネルギー線重合性化合物としては、 例えば、 分子内に少なくとも 1 個の （メタ） アクリロイルオキシ基を有する （メタ） アクリレートモノマー ;官能基含有化合物を 2種以上反応させて得られ、 分子内に少なくとも 2個 の （メタ） アクリロイルオキシ基を有する （メタ） アクリレートオリゴマ_ 等の （メタ） アクリロイルオキシ基含有化合物等の （メタ） アクリル系化合 物が挙げられる。 粘着剤組成物 は、 活性エネルギー線重合性化合物を、 粘 着剤組成物 の固形分 1 0 0質量部に対して〇. 1質量部以上 1 0質量部以 下含むことができる。
[0028] 光重合開始剤としては、 例えば、 ジフエニル （2 , 4 , 6—トリメチルべ ンゾイル） ホスフインオキシド、 ベンジルジメチルケタール、 1 —ヒドロキ シシクロヘキシルフエニルケトン等が挙げられる。 粘着剤組成物 が光重合 開始剤を含むとき、 1種または 2種以上を含むことができる。 粘着剤組成物 八が光重合開始剤を含む場合、 その全含有量は、 例えば粘着剤組成物 の固 形分 1 〇〇質量部に対し〇. 〇 1質量部以上·！ . 〇質量部以下であってよい
[0029] 粘着剤組成物 は、 窒素原子及び （メタ） アクリロイル基を有する化合物 を含むことが好ましい。 粘着剤組成物 は、 窒素原子及び （メタ） アクリロ イル基を有する化合物を 1種のみ含んでいてもよいし、 複数種を含んでいて もよい。 第 1粘着剤組成物及び第 2粘着剤組成物の少なくとも一方は、 窒素 〇 2020/175092 9 卩（：170? 2020 /004755
原子及び （メタ） アクリロイル基を有する化合物を含む粘着剤組成物 であ ることが好ましい。 窒素原子及び （メタ） アクリロイル基を有する化合物を 含む粘着剤組成物 により、 上記した関係式 （2） , （3） を満たす第 1基 準粘着剤層及び第 2基準粘着剤層を容易に形成することができる。 粘着剤組 成物 は、 窒素原子及び （メタ） アクリロイル基を有する化合物を、 粘着剤 組成物 の固形分 1 0 0質量部中に、 例えば〇. 1質量部以上 1 0質量部以 下、 好ましくは 1質量部以上 5質量部以下含むことができる。 窒素原子及び （メタ） アクリロイル基を有する化合物の含有量を調整することにより、 上 記した関係式 （2） 、 （3） を満たすように調整することができる。
[0030] 窒素原子及び （メタ） アクリロイル基を有する化合物は、 （メタ）アクリロ イル基に窒素原子が結合していることが好ましく、 すなわちアミ ド結合を有 することが好ましい。 窒素原子及び （メタ） アクリロイル基を有する化合物 は、 1級アミ ド、 2級アミ ド、 または 3級アミ ドであることができる。 窒素 原子及び （メタ） アクリロイル基を有する化合物としては、 特に限定されな いが、 例えば、 1\1—ブトキシメチルアクリルアミ ド、 1\1 , 1\1—ジメチルアク リルアミ ド等が挙げられる。
[0031 ] 粘着剤組成物 は、 光散乱性を付与するための微粒子、 ビーズ （樹脂ビー ズ、 ガラスビーズ等） 、 ガラス繊維、 ベースポリマー以外の樹脂、 粘着性付 与剤、 充填剤 （金属粉やその他の無機粉末等） 、 酸化防止剤、 紫外線吸収剤 、 染料、 顔料、 着色剤、 消泡剤、 腐食防止剤等の添加剤を含むことができる 。 粘着剤組成物 は、 残存溶剤による耐久性低下を防ぐ観点から有機溶剤を 含まないことが好ましい。
[0032] 粘着剤層が粘着剤組成物 から形成される場合、 粘着剤層は、 粘着剤組成 物八を基材上に塗布することにより形成することができる。 活性エネルギー 線硬化型粘着剤組成物を用いた場合は、 形成された粘着剤層に、 活性エネル ギー線を照射することにより所望の硬化度を有する硬化物とすることができ る。
[0033] 活性エネルギー線は、 紫外線であることが好ましい。 光源には、 低圧水銀 〇 2020/175092 10 卩（：170? 2020 /004755
灯、 中圧水銀灯、 高圧水銀灯、 超高圧水銀灯、 ケミカルランプ、 ブラックラ イ トランプ、 マイクロウエーブ厉力起水銀灯、 メタルハライ ドランプなどを用 いることができる。 活性エネルギー線の積算光量は、 〇.
Figure imgf000012_0001
0」 /〇〇! 2が好ましく、 〇. 2」/〇〇12〜〇. 9」/〇〇12がより好ましい 。 このような条件の活性エネルギー線照射は、 粘着剤層の熱分解質量減少率 を所定範囲に調整するのを容易にすることができる。
[0034] （2） 熱硬化型粘着剤組成物
粘着剤組成物 が熱硬化型粘着剤組成物である場合、 （メタ） アクリル系 ポリマー八は、 当該重合体を構成するモノマー単位として、 アルキル基の炭 素数が 2〜 20の （メタ） アクリル酸アルキルエステルと、 分子内に反応性 官能基を有するモノマー （反応性官能基含有モノマー） とを含有することが 好ましい。
[0035] （メタ） アクリル系ポリマー八は、 当該重合体を構成するモノマー単位と して、 アルキル基の炭素数が 2〜 20の （メタ） アクリル酸アルキルエステ ルを含有することで、 好ましい粘着性を発現することができる。 アルキル基 の炭素数が 2〜 20の （メタ） アクリル酸アルキルエステルとしては、 ホモ ポリマーとしてのガラス転移温度 （丁 9） が一 40°〇以下であるもの （以下 「低丁 9アルキルアクリレート」 という場合がある。 ） が好ましい。 かかる 低丁 9アルキルアクリレートを構成モノマー単位として含有することにより 、 粘着剤層の柔軟性が向上し、 屈曲時の気泡発生を抑制し易くなる傾向にあ る。
[0036] 低丁 9アルキルアクリレートとしては、 例えば、 アクリル酸 n -ブチル （ 丁 9 -55°〇） 、 アクリル酸门ーオクチル （丁 9 -65°〇） 、 アクリル酸イ ソオクチル （丁 9 -58°〇） 、 アクリル酸 2 -エチルヘキシル （丁 9 -70 °〇） 、 アクリル酸イソノニル （丁 9 -58°〇） 、 アクリル酸イソデシル （丁 9 - 60 °〇 、 メタクリル酸イソデシル （丁 9 - 4 1 °〇 、 メタクリル酸 n -ラウリル （丁 9 -65°〇 、 アクリル酸トリデシル （丁 9 -55°〇 、 メ タクリル酸トリデシル （_40°〇） 等が好ましく挙げられる。 中でも、 得ら 〇 2020/175092 1 1 卩（：170? 2020 /004755
れる粘着剤層について、 関係式 （2） 又は関係式 （3） を満たし易くなる観 点から、 低丁 9アルキルアクリレートとして、 ホモポリマーの丁 9が、 一4 5 °◦以下であるものであることがより好ましく、 _ 5 0 °◦以下であるもので あることが特に好ましい。 具体的には、 アクリル酸 -ブチルおよびアクリ ル酸 2 -エチルヘキシルが特に好ましい。 これらは単独で用いてもよいし、
2種以上を組み合わせて用いてもよい。
[0037] （メタ） アクリル系ポリマー八は、 当該重合体を構成するモノマー単位と して、 低丁 9アルキルアクリ レートを、 下限値として 8 5質量％以上含有す ることが好ましく、 9 0質量％以上含有することがより好ましく、 9 5質量 %以上含有することがさらに好ましい。
このような範囲であると、 得られる粘着剤層について、 関係式 （2） 又は関 係式 （3） を満たしやすくなる。
[0038] また、 （メタ） アクリル系ポリマー八は、 当該重合体を構成するモノマー 単位として上記低丁 9アルキルアクリレートを、 上限値として 9 9 . 9質量 %以下含有することが好ましく、 9 9 . 5質量％以下含有することがより好 ましく、 9 9質量％以下含有することがさらに好ましい。 上記低丁 9アルキ ルアクリレートを 9 9 . 9質量％以下含有することにより、 （メタ） アクリ ル系ポリマー八中に他のモノマー成分 （特に反応性官能基含有モノマー） を 好適な量導入することができる。
[0039] （メタ） アクリル系ポリマー八は、 本実施形態に係る粘着剤の主ポリマー のガラス転移温度 （丁 9） を前述した範囲に設定し易くするために、 ホモポ リマーとしてのガラス転移温度 （丁 9） が 0 °〇を超えるモノマー （以下 「ハ —ドモノマー」 と称する場合がある。 ） の含有量を、 なるべく少なくするこ とが好ましい。 具体的には、 （メタ） アクリル系ポリマー八は、 当該重合体 を構成するモノマー単位として、 ハードモノマーの含有量を、 上限値として 1 5質量％以下とすることが好ましく、 1 0質量％以下とすることがより好 ましく、 5質量％以下とすることがさらに好ましい。 なお、 このハードモノ マーには、 後述する反応性官能基含有モノマーも含まれる。 〇 2020/175092 12 卩（：170? 2020 /004755
[0040] 上記ハードモノマーとしては、 例えば、 アクリル酸メチル （丁 9 1 0°〇 、 メタクリル酸メチル （丁 9 1 05°〇 、 メタクリル酸エチル （丁 965°〇 ） 、 メタクリル酸门ーブチル （丁 920°〇） 、 メタクリル酸イソプチル （丁 948°〇 、 メタクリル酸 I -ブチル （丁 9 1 07°〇 、 アクリル酸 n -ス テアリル （丁 930°〇） 、 メタクリル酸 -ステアリル （丁 938°〇） 、 ア クリル酸シクロヘキシル （丁 9 1 5°〇） 、 メタクリル酸シクロヘキシル （丁 966°〇 , アクリル酸フエノキシエチル （丁 95°〇） 、 メタクリル酸フエ ノキシエチル （丁 954°〇） 、 メタクリル酸ベンジル （丁 954°〇） 、 アク リル酸イソボルニル （丁 994°〇） 、 メタクリル酸イソボルニル （丁 9 1 8 〇°〇） 、 アクリロイルモルホリン （丁 9 1 45°〇） 、 アクリル酸アダマンチ ル （丁 9 1 1 5°〇 、 メタクリル酸アダマンチル （丁 9 1 4 1 °〇 、 アクリ ル酸 （丁 9 1 03°〇 、 ジメチルアクリルアミ ド （丁 989°〇 、 アクリル アミ ド （丁 9 1 65°〇 等のアクリル系モノマー、 酢酸ビニル （丁 932°〇 ） 、 スチレン （丁 980°〇） 等が挙げられる。
[0041] （メタ） アクリル系ポリマー八は、 当該重合体を構成するモノマー単位と して反応性官能基含有モノマーを含有することで、 当該反応性官能基含有モ ノマー由来の反応性官能基を介して、 後述する熱架橋剤と反応し、 これによ り架橋構造 （三次元網目構造） が形成され、 所望の凝集力を有する粘着剤が 得られる。
[0042] （メタ） アクリル系ポリマー八が、 当該重合体を構成するモノマー単位と して含有する反応性官能基含有モノマーとしては、 分子内に水酸基を有する モノマー （水酸基含有モノマー） 、 分子内にカルボキシ基を有するモノマー （カルボキシ基含有モノマー） 、 分子内にアミノ基を有するモノマー （アミ ノ基含有モノマー） などが好ましく挙げられる。 これらの中でも、 ガラス転 移温度 （丁 9） が 0°〇以下であるものが多いことから、 水酸基含有モノマー が特に好ましい。
[0043] 水酸基含有モノマーとしては、 例えば、 （メタ） アクリル酸 2 -ヒドロキ シエチル、 （メタ） アクリル酸 2—ヒドロキシプロピル、 （メタ） アクリル 〇 2020/175092 13 卩（：170? 2020 /004755
酸 3 -ヒドロキシプロピル、 （メタ） アクリル酸 2 -ヒドロキシブチル、 （ メタ） アクリル酸 3 -ヒドロキシブチル、 （メタ） アクリル酸 4 -ヒドロキ シブチルなどの （メタ） アクリル酸ヒドロキシアルキルエステル等が挙げら れる。 中でも、 ガラス転移温度 （丁 9） 、 得られる （メタ） アクリル系ポリ マー における水酸基の熱架橋剤との反応性、 および他の単量体との共重合 性の点から、 アクリル酸 2 -ヒドロキシエチル、 アクリル酸 2 -ヒドロキシ プロピル、 アクリル酸 3 -ヒドロキシプロピル、 およびアクリル酸 4 -ヒド ロキシブチルの少なくとも一つであることが好ましい。 これらは単独で用い てもよいし、 2種以上を組み合わせて用いてもよい。
[0044] カルボキシ基含有モノマーとしては、 例えば、 アクリル酸、 メタクリル酸 、 クロトン酸、 マレイン酸、 イタコン酸、 シトラコン酸等のエチレン性不飽 和カルボン酸が挙げられる。 これらは単独で用いてもよいし、 2種以上を組 み合わせて用いてもよい。
[0045] アミノ基含有モノマーとしては、 例えば、 （メタ） アクリル酸アミノエチ ル、 （メタ） アクリル酸门ーブチルアミノエチル等が挙げられる。 これらは 単独で用いてもよいし、 2種以上を組み合わせて用いてもよい。
[0046] （メタ） アクリル系ポリマー八は、 当該重合体を構成するモノマー単位と して、 反応性官能基含有モノマーを、 下限値として〇. 1質量％以上含有す ることが好ましく、 特に〇. 5質量％以上含有することが好ましく、 さらに は 1質量％以上含有することが好ましい。 また、 上限値として 1 〇質量％以 下含有することが好ましく、 特に 8質量％以下含有することが好ましく、 さ らには 5質量％未満含有することが好ましい。 （メタ） アクリル系ポリマー 八がモノマー単位として上記の量で反応性官能基含有モノマー、 特に水酸基 含有モノマーを含有すると、 得られる粘着剤層について関係式 （2） 又は関 係式 （3） を満たし易くなる。
[0047] （メタ） アクリル系ポリマー八は、 当該重合体を構成するモノマー単位と して、 カルボキシ基含有モノマー、 特にハードモノマーでもあるアクリル酸 を含まなくてもよい。 カルボキシ基は酸成分であるため、 カルボキシ基含有 〇 2020/175092 14 卩（：170? 2020 /004755
モノマーを含有しないことにより、 粘着剤の貼付対象に、 酸により不具合が 生じるもの、 例えばスズドープ酸化インジウム （丨 丁〇） 等の透明導電膜や 、 金属膜、 金属メッシュなどが存在する場合にも、 酸によるそれらの不具合 （腐食、 抵抗値変化等） を抑制することができる。
[0048] （メタ） アクリル系ポリマー八は、 所望により、 当該重合体を構成するモ ノマー単位として、 他のモノマーを含有してもよい。 他のモノマーとしては 、 反応性官能基含有モノマーの作用を妨げないためにも、 反応性を有する官 能基を含まないモノマーが好ましい。 かかる他のモノマーとしては、 例えば 、 （メタ） アクリル酸メ トキシエチル、 （メタ） アクリル酸エトキシエチル 等の （メタ） アクリル酸アルコキシアルキルエステルの他、 ホモポリマーと してのガラス転移温度 （丁 9） が一 4 0 °〇超、 0 °〇以下であるモノマー （以 下 「中丁 9アルキルアクリレート」 という場合がある。 ） などが挙げられる 。 中丁 9アルキルアクリレートとしては、 例えば、 アクリル酸エチル （丁 9 _ 2 0 °〇 、 アクリル酸イソプチル （丁 9 - 2 6 °〇 、 メタクリル酸 2 -エ チルヘキシル （丁 9 - 1 0 °〇） 、 アクリル酸门ーラウリル （丁 9 - 2 3 °〇）
、 アクリル酸イソステアリル （丁 9 - 1 8 °〇 等が挙げられる。 これらは単 独で用いてもよいし、 2種以上を組み合わせて用いてもよい。
[0049] （メタ） アクリル系ポリマー八の重合態様は、 ランダム共重合体であって もよいし、 ブロック共重合体であってもよい。
[0050] （メタ） アクリル系ポリマー八の重量平均分子量の下限値は、 2 0万以上 であることが好ましく、 特に 3 0万以上であることが好ましく、 さらには 4 0万以上であることが好ましい。 （メタ） アクリル系ポリマー八の重量平均 分子量の下限値が上記以上であると、 粘着剤の浸み出し等の不具合が抑制さ れる。 なお、 本明細書における重量平均分子量は、 ゲルパーミエーションク ロマトグラフィー （〇 〇） 法により測定した標準ポリスチレン換算の値で ある。
[0051 ] また、 （メタ） アクリル系ポリマー八の重量平均分子量の上限値は、 1 5
0万以下であることが好ましく、 特に 1 3 5万以下であることが好ましく、 〇 2020/175092 15 卩（：170? 2020 /004755
さらには 1 2 0万以下であることが好ましい。 （メタ） アクリル酸エステル 重合体 （ ） の重量平均分子量の上限値が上記以下であると、 得られる粘着 剤層について関係式 （2） 又は関係式 （3） を満たし易くなる。
[0052] なお、 粘着剤組成物八において、 （メタ） アクリル系ポリマー八は、 1種 を単独で用いてもよいし、 2種以上を組み合わせて用いてもよい。
[0053] 熱架橋剤を含有する粘着剤組成物 を加熱すると、 熱架橋剤は （メタ） ア クリル系ポリマー八を架橋し、 三次元網目構造を形成する。 これにより、 得 られる粘着剤の凝集力が向上するとともに、 得られる粘着剤層について関係 式 （2） 又は関係式 （3） を満たし易くなる。
[0054] 上記熱架橋剤としては、 （メタ） アクリル系ポリマー八が有する反応性基 と反応するものであればよく、 例えば、 イソシアネート系架橋剤、 エポキシ 系架橋剤、 アミン系架橋剤、 メラミン系架橋剤、 アジリジン系架橋剤、 ヒド ラジン系架橋剤、 アルデヒド系架橋剤、 オキサゾリン系架橋剤、 金属アルコ キシド系架橋剤、 金属キレ _卜系架橋剤、 金属塩系架橋剤、 アンモニウム塩 系架橋剤等が挙げられる。 上記の中でも、 （メタ） アクリル系ポリマー八が 有する反応性基が水酸基の場合、 水酸基との反応性に優れたイソシアネート 系架橋剤を使用することが好ましい。 なお、 熱架橋剤は、 1種を単独で、 ま たは 2種以上を組み合わせて使用することができる。
[0055] イソシアネート系架橋剤は、 少なくともポリイソシアネート化合物を含む ものである。
ポリイソシアネート化合物としては、 例えば、 トリレンジイソシアネート、 ジフエニルメタンジイソシアネート、 キシリレンジイソシアネート等の芳香 族ポリイソシアネート、 ヘキサメチレンジイソシアネート等の脂肪族ポリイ ソシアネート、 イソホロンジイソシアネート、 水素添加ジフエニルメタンジ イソシアネート等の脂環式ポリイソシアネートなど、 及びそれらのピウレツ 卜体、 イソシアヌレート体、 さらにはエチレングリコール、 プロピレングリ コール、 ネオペンチルグリコール、 トリメチロールプロパン、 ヒマシ油等の 低分子活性水素含有化合物との反応物であるアダクト体などが挙げられる。 〇 2020/175092 16 卩（：170? 2020 /004755
中でも水酸基との反応性の観点から、 トリメチロールプロパン変性の芳香族 ポリイソシアネート、 特にトリメチロールプロパン変性トリレンジイソシア ネートおよびトリメチロールプロパン変性キシリレンジイソシアネートが好 ましい。
[0056] エポキシ系架橋剤としては、 例えば、 1 , 3 -ビス （ 1\1 , 1\1 -ジグリシジ ルアミノメチル） シクロヘキサン、 1\1 , 1\1 , 1\1’ ， 1\1’ ーテトラグリシジル キシリレンジアミン、 エチレングリコールジグリシジルエーテル、 1 , 6—ヘキサンジオールジグリシジルエーテル、 トリメチロールプロパンジ グリシジルエーテル、 ジグリシジルアニリン、 ジグリシジルアミン等が挙げ られる。
[0057] 粘着剤組成物 中における熱架橋剤の含有量は、 （メタ） アクリル系ポリ マー八 1 0 0質量％に対して、 〇. 0 1質量％以上であることが好ましく、 0 . 0 5質量％以上であることがより好ましく、 0 . 1質量％以上であるこ とがさらに好ましい。 また、 当該含有量は、 1質量％以下であることが好ま しく、 〇. 8質量％以下であることがより好ましく、 〇. 5質量％以下であ ることがさらに好ましい。 熱架橋剤の含有量が上記の範囲にあることで、 得 られる粘着剤層について関係式 （2） 又は関係式 （3） を満たし易くなる。
[0058] 粘着剤組成物 は、 上記のシランカップリング剤を含有することが好まし い。 これにより、 得られる粘着剤層は、 被着体となるフレキシブル積層体中 における各部材との密着性が向上し、 屈曲に対する耐久性がより優れたもの となる。
[0059] シランカップリング剤としては、 分子内にアルコキシシリル基を少なくと も 1個有する有機ケイ素化合物であって、 （メタ） アクリル系ポリマー八と の相溶性がよく、 光透過性を有するものが好ましい。
[0060] シランカップリング剤としては、 例えば、 ビニルトリメ トキシシラン、 ビ ニルトリエトキシシラン、 メタクリロキシプロピルトリメ トキシシラン等の 重合性不飽和基含有ケイ素化合物、 3—グリシドキシプロピルトリメ トキシ シラン、 2 - （3 , 4—エポキシシクロヘキシル） エチルトリメ トキシシラ 〇 2020/175092 17 卩（：170? 2020 /004755
ン等のエポキシ構造を有するケイ素化合物、 3—メルカプトプロピルトリメ トキシシラン、 3—メルカプトプロピルトリエトキシシラン、 3—メルカプ トプロピルジメ トキシメチルシラン等のメルカプト基含有ケイ素化合物、 3 —アミノプロピルトリメ トキシシラン、 1\1— （2—アミノエチル） 一3—ア ミノプロピルトリメ トキシシラン、 1\1— （2—アミノエチル） 一3—アミノ プロピルメチルジメ トキシシラン等のアミノ基含有ケイ素化合物、 3—クロ ロプロピルトリメ トキシシラン、 3—イソシアネートプロピルトリエトキシ シラン、 あるいはこれらの少なくとも 1つと、 メチルトリエトキシシラン、 エチルトリエトキシシラン、 メチルトリメ トキシシラン、 エチルトリメ トキ シシラン等のアルキル基含有ケイ素化合物との縮合物などが挙げられる。 こ れらは、 1種を単独で用いてもよく、 2種以上を組み合わせて用いてもよい
[0061 ] 粘着剤組成物 中におけるシランカップリング剤の含有量は、 （メタ） ア クリル系ポリマー八 1 0 0質量％に対して、 〇. 0 1質量％以上であること が好ましく、 0 . 0 5質量％以上であることがより好ましく、 0 . 1質量％ 以上であることがさらに好ましい。 また、 当該含有量は、 1質量％以下であ ることが好ましく、 〇. 5質量％以下であることがより好ましく、 〇. 3質 量％以下であることがさらに好ましい。 シランカップリング剤の含有量が上 記の範囲にあることで、 得られる粘着剤層は、 被着体となるフレキシブル積 層体中における各部材との密着性がより好ましいものとなる。
[0062] 粘着剤組成物 には、 所望により、 上述の各種添加剤を添加することがで きる。 なお、 重合溶媒や希釈溶媒は、 粘着剤組成物 を構成する添加剤に含 まれないものとする。
[0063] （メタ） アクリル系ポリマー八は、 重合体を構成するモノマーの混合物を 通常のラジカル重合法で重合することにより製造することができる。 （メタ ） アクリル系ポリマー の重合は、 所望により重合開始剤を使用して、 溶液 重合法により行うことが好ましい。 重合溶媒としては、 例えば、 酢酸エチル 、 酢酸 1·! -ブチル、 酢酸イソプチル、 トルエン、 アセトン、 ヘキサン、 メチ 〇 2020/175092 18 卩（：170? 2020 /004755
ルエチルケトン等が挙げられ、 2種類以上を併用してもよい。
[0064] 重合開始剤としては、 アゾ系化合物、 有機過酸化物等が挙げられ、 2種類 以上を併用してもよい。 アゾ系化合物としては、 例えば、 2 , 2’ ーアゾビ スイソプチロニトリル、 2 , 2’ ーアゾビス （2—メチルプチロニトリル）
、 1 , 1’ ーアゾビス （シクロヘキサン ·！ ーカルボニトリル） 、 2 , 2’ 一 アゾビス （2 , 4 -ジメチルバレロニトリル） 、 2 , 2’ ーアゾビス （2 ,
4—ジメチルー 4—メ トキシバレロニトリル） 、 ジメチル 2 , 2’ ーアゾビ ス （2 -メチルプロビオネート） 、 4 , 4’ ーアゾビス （4 -シアノバレリ ック酸） 、 2 , 2’ ーアゾビス （2—ヒドロキシメチルプロピオニトリル）
、 2 , 2’ ーアゾビス [ 2— （2—イミダゾリンー 2—イル） プロパン] 等 が挙げられる。
[0065] 有機過酸化物としては、 例えば、 過酸化べンゾイル、 1 -ブチルパーベン ゾエイ ト、 クメンヒドロパーオキシド、 ジイソプロピルパーオキシジカーボ ネート、 ジ _门 _プロピルパーオキシジカーボネート、 ジ （2—エトキシエ チル） パーオキシジカーボネート、 I _ブチルパーオキシネオデカノエート 、 1—ブチルパーオキシビバレート、 （3 , 5 , 5—トリメチルへキサノイ ル） パーオキシド、 ジプロピオニルパーオキシド、 ジアセチルパーオキシド 等が挙げられる。
[0066] なお、 上記重合工程において、 2 -メルカプトエタノール等の連鎖移動剤 を配合することにより、 得られる重合体の重量平均分子量を調節することが できる。
[0067] （メタ） アクリル系ポリマー八が得られたら、 （メタ） アクリル系ポリマ _八の溶液に、 熱架橋剤、 シランカップリング剤ならびに所望により添加剤 および希釈溶剤を添加し、 十分に混合することにより、 溶剤で希釈された粘 着剤組成物 （塗布溶液） を得る。
[0068] なお、 上記各成分のいずれかにおいて、 固体状のものを用いる場合、 ある いは、 希釈されていない状態で他の成分と混合した際に析出を生じる場合に は、 その成分を単独で予め希釈溶媒に溶解もしくは希釈してから、 その他の 〇 2020/175092 19 卩（：170? 2020 /004755
成分と混合してもよい。
[0069] 上記希釈溶剤としては、 例えば、 ヘキサン、 ヘプタン、 シクロヘキサン等 の脂肪族炭化水素、 トルエン、 キシレン等の芳香族炭化水素、 塩化メチレン 、 塩化エチレン等のハロゲン化炭化水素、 メタノール、 エタノール、 プロパ ノール、 ブタノール、 1 —メ トキシ _ 2—プロパノール等のアルコール、 ア セトン、 メチルエチルケトン、 2—ペンタノン、 イソホロン、 シクロへキサ ノン等のケトン、 酢酸エチル、 酢酸プチル等のエステル、 エチルセロソルブ 等のセロソルブ系溶剤などが用いられる。
[0070] このようにして調製された塗布溶液の濃度 ·粘度としては、 コーティング 可能な範囲であればよく、 特に制限されず、 状況に応じて適宜選定すること ができる。 例えば、 粘着剤組成物八の濃度が 1 〇〜 6 0質量％となるように 希釈する。 なお、 塗布溶液を得るに際して、 希釈溶剤等の添加は必要条件で はなく、 粘着剤組成物 がコーティング可能な粘度等であれば、 希釈溶剤を 添加しなくてもよい。 この場合、 粘着剤組成物八は、 （メタ） アクリル系ポ リマー の重合溶媒をそのまま希釈溶剤とする塗布溶液となる。
[0071 ] 本実施形態に係る粘着剤として好ましい粘着剤は、 粘着剤組成物 を架橋 してなるものである。 粘着剤組成物八の架橋は、 加熱処理により行うことが できる。 なお、 この加熱処理は、 所望の対象物に塗布した粘着剤組成物八の 塗膜から希釈溶剤等を揮発させる際の乾燥処理で兼ねることもできる。
[0072] 加熱処理の加熱温度は、 5 0〜 1 5 0 °〇であることが好ましく、 7 0〜 1
2 0 °〇であることがより好ましい。 また、 加熱時間は、 1 0秒〜 1 0分であ ることが好ましく、 5 0秒〜 2分であることがより好ましい。
[0073] 加熱処理後、 必要に応じて、 常温 （例えば、 2 3 °〇、 5 0 % [¾ 1~1） で 1〜
2週間程度の養生期間を設けてもよい。 この養生期間が必要な場合は、 養生 期間経過後、 養生期間が不要な場合には、 加熱処理終了後、 粘着剤が形成さ れる。
[0074] 上記の加熱処理 （及び養生） により、 架橋剤を介して （メタ） アクリル系 ポリマー が十分に架橋されて架橋構造が形成され、 粘着剤が得られる。 か 〇 2020/175092 20 卩（：170? 2020 /004755
かる粘着剤は、 得られる粘着剤層について関係式 （2） 又は関係式 （3） を 満たし易くなる。
[0075] 本発明にかかる粘着シートは、 上記の本発明に係る粘着剤組成物 から形成 された粘着剤層を含む。 粘着剤層は、 粘着剤組成物 を基材上に塗布するこ とにより形成することができる。 粘着剤組成物 として、 熱硬化型の粘着剤 組成物を用いた場合は、 形成された粘着剤層に加熱処理 （及び養生） を施す ことにより、 所望の硬化度を有する硬化物とすることができる。 なお、 加熱 処理および養生の条件については、 前述した通りである。
[0076] 基材は離型処理が施された剥離フィルムであってもよい。 粘着シートは、 離 型フィルム上に粘着剤からなる層をシート状に形成しておき、 その粘着剤層 上にさらに別の剥離フィルムを貼合することにより作製することができる。
[0077] 上記粘着剤組成物 の塗布液を塗布する方法としては、 例えばバーコート 法、 ナイフコート法、 口ールコート法、 ブレードコート法、 ダイコート法、 グラビアコート法等を利用することができる。
[0078] 粘着剤組成物 は、 公知の方法により、 例えば各成分をミキサー等を用い て一括混合することにより製造することができる。
[0079] [前面板]
前面板 1 0 1は、 光を透過可能な板状体であれば、 材料および厚みは限定 されることはなく、 また 1層のみから構成されてよく、 2層以上から構成さ れてもよい。 その例としては、 樹脂製の板状体 （例えば樹脂板、 樹脂シート 、 樹脂フィルム等） 、 ガラス製の板状体 （例えばガラス板、 ガラスフィルム 等） 、 後述のタッチセンサパネルが挙げられる。 前面板は、 表示装置の最表 面を構成するものであることができる。
[0080] 前面板 1 0 1の厚みは、 例えば 1 0 以上 5 0 0 以下であってよく 、 好ましくは 3 0 以上 2 0 0 以下であり、 より好ましくは 5 0 以上 1 〇〇 以下である。 本発明において、 各層の厚みは、 後述する実施 例において説明する厚み測定方法にしたがって測定することができる。
[0081 ] 前面板 1 0 1が樹脂製の板状体である場合、 樹脂製の板状体は、 光を透過 〇 2020/175092 21 卩（：170? 2020 /004755
可能なものであれば限定されることはない。 樹脂フィルム等の樹脂製の板状 体を構成する樹脂としては、 例えばトリアセチルセルロース、 アセチルセル 口ースブチレート、 エチレンー酢酸ビニル共重合体、 プロピオニルセルロー ス、 プチリルセルロース、 アセチルプロピオニルセルロース、 ポリエステル 、 ポリスチレン、 ポリアミ ド、 ポリエーテルイミ ド、 ポリ （メタ） アクリル 、 ポリイミ ド、 ポリエーテルスルホン、 ポリスルホン、 ポリエチレン、 ポリ プロピレン、 ポリメチルペンテン、 ポリ塩化ビニル、 ポリ塩化ビニリデン、 ポリビニルアルコール、 ポリビニルアセタール、 ポリエーテルケトン、 ポリ エーテルエーテルケトン、 ポリエーテルスルホン、 ポリメチルメタアクリレ —卜、 ポリエチレンテレフタレート、 ポリプチレンテレフタレート、 ポリエ チレンナフタレート、 ポリカーボネート、 ポリアミ ドイミ ドなどの高分子で 形成されたフィルムが挙げられる。 これらの高分子は、 単独でまたは 2種以 上混合して用いることができる。 強度および透明性向上の観点から好ましく はポリイミ ド、 ポリアミ ド、 ポリアミ ドイミ ドなどの高分子で形成された樹 脂フィルムである。
[0082] 前面板 1 0 1は、 硬度を高める観点から好ましくは基材フィルムの少なく とも一方の面にハードコート層が設けられたフィルムである。 基材フィルム としては、 上記樹脂からできたフィルムを用いることができる。 ハードコー 卜層は、 基材フィルムの一方の面に形成されていてもよいし、 両方の面に形 成されていてもよい。 ハードコート層を設けることにより、 硬度およびスク ラッチ性を向上させた樹脂フィルムとすることができる。 ハードコート層は 、 例えば紫外線硬化型樹脂の硬化層である。 紫外線硬化型樹脂としては、 例 えばアクリル系樹脂、 シリコーン系樹脂、 ポリエステル系樹脂、 ウレタン系 樹脂、 アミ ド系樹脂、 エポキシ系樹脂等が挙げられる。 ハードコート層は、 硬度を向上させるために、 添加剤を含んでいてもよい。 添加剤は限定される ことはなく、 無機系微粒子、 有機系微粒子、 またはこれらの混合物が挙げら れる。
[0083] 前面板 1 0 1がガラス板である場合、 ガラス板は、 ディスプレイ用強化ガ 〇 2020/175092 22 卩（：170? 2020 /004755
ラスが好ましく用いられる。 ガラス板の厚みは、 例えば 3 0 以上 1 , 0 0 0 以下であってよい。 ガラス板を用いることにより、 優れた機械的強 度および表面硬度を有する前面板 1 0 1 を構成することができる。
［0084］ 積層体 1 0 0が表示装置に用いられる場合、 前面板 1 0 1は、 表示装置の 前面 （画面） を保護する機能 （ウィンドウフィルムとしての機能） を有する のみではなく、 タッチセンサとしての機能、 ブルーライ トカッ ト機能、 視野 角調整機能等を有するものであってもよい。
［0085］ ［第 1粘着剤層］
第 1粘着剤層 1 0 2は、 前面板 1 0 1 と偏光子層 1 0 3との間に介在して これらを貼合する層であり、 例えば粘着剤や接着剤から構成される層または 該層に対して何らかの処理を施してなる層であってよい。 第 1粘着剤層は、 積層体を構成する粘着剤層の中で、 最も前面板に近い位置に配置される粘着 剤層であることができる。 粘着剤とは、 感圧式接着剤とも呼ばれるものであ る。 本明細書において 「接着剤」 とは、 粘着剤 （感圧式接着剤） 以外の接着 剤をいい、 粘着剤とは明確に区別される。 第 1粘着剤層 1 0 2は、 1層から なるものであってもよく、 または 2層以上からなるものであってもよいが、 好ましくは 1層である。
［0086］ 第 1粘着剤層 2 0は粘着剤組成物から直接、 又は粘着剤組成物を用いて形 成された粘着剤層を有する粘着シートを用いて形成することができる。 粘着 剤組成物は、 上述の通り粘着剤組成物 から形成することができる。
［0087］ 第 1粘着剤層 1 0 2の厚みは、 例えば 3 以上 1 〇〇 以下であるこ とが好ましく、 5 以上 5〇 以下であることがより好ましく、 2 0 01以上であってもよい。
［0088］ ［偏光子層］
偏光子層 1 0 3としては、 二色性色素を吸着させた延伸フィルムまたは延 伸層、 二色性色素及び重合性化合物を含む組成物を塗布し硬化させてなる層 等が挙げられる。 二色性色素として、 具体的には、 ヨウ素や二色性の有機染 料が用いられる。 二色性有機染料には、 〇. 丨 . 0 丨 ［¾巳〇丁 3 〇 2020/175092 23 卩（：170? 2020 /004755
9等のジスアゾ化合物からなる二色性直接染料、 トリスアゾ、 テトラキスア ゾ等の化合物からなる二色性直接染料が包含される。
[0089] 二色性色素及び重合性化合物を含む組成物を塗布し硬化させてなる偏光子 層としては、 液晶性を有する二色性色素を含む組成物または二色性色素と重 合性液晶とを含む組成物を塗布し硬化させて得られる層等の重合性液晶化合 物の硬化物を含む偏光子層が挙げられる。
二色性色素及び重合性化合物を含む組成物を塗布し硬化させてなる偏光子 層は、 二色性色素を吸着させた延伸フィルムまたは延伸層に比べて、 屈曲方 向に制限がないため好ましい。
[0090] [延伸フィルムまたは延伸層である偏光子層]
二色性色素を吸着させた延伸フィルムである偏光子層は、 通常、 ポリビニ ルアルコール系樹脂フィルムを一軸延伸する工程、 ポリビニルアルコール系 樹脂フィルムを二色性色素で染色することにより、 その二色性色素を吸着さ せる工程、 二色性色素が吸着されたポリビニルアルコール系樹脂フィルムを ホウ酸水溶液で処理する工程、 およびホウ酸水溶液による処理後に水洗する 工程を経て製造することができる。
偏光子層 1 0 3の厚みは、 例えば 2 以上 4 0 以下である。 偏光子 層 1 0 3の厚みは 5 以上であってもよく、 2 0 〇!以下、 さらには 1 5 以下、 なおさらには 1 0 以下であってもよい。
[0091 ] ポリビニルアルコール系樹脂は、 ポリ酢酸ビニル系樹脂をケン化すること によって得られる。 ポリ酢酸ビニル系樹脂としては、 酢酸ビニルの単独重合 体であるポリ酢酸ビニルのほか、 酢酸ビニルとそれに共重合可能な他の単量 体との共重合体が用いられる。 酢酸ビニルに共重合可能な他の単量体として は、 例えば、 不飽和カルボン酸類、 オレフィン類、 ビニルエーテル類、 不飽 和スルホン酸類、 アンモニウム基を有する （メタ） アクリルアミ ド類等が挙 げられる。
[0092] ポリビニルアルコール系樹脂のケン化度は、 通常 8 5モル％以上 1 0 0モ ル％以下程度であり、 好ましくは 9 8モル％以上である。 ポリビニルアルコ 〇 2020/175092 24 卩（：170? 2020 /004755
—ル系樹脂は変性されていてもよく、 例えば、 アルデヒド類で変性されたポ リビニルホルマールやポリビニルアセタールも使用することができる。 ポリ ビニルアルコール系樹脂の重合度は、 通常 1 , 0 0 0以上 1 0 , 0 0 0以下 であり、 好ましくは 1 , 5 0 0以上 5 , 0 0 0以下である。
[0093] 二色性色素を吸着させた延伸層である偏光子層は、 通常、 上記ポリビニル アルコール系樹脂を含む塗布液を基材フィルム上に塗布する工程、 得られた 積層フィルムを _軸延伸する工程、 _軸延伸された積層フィルムのポリビニ ルアルコール系樹脂層を二色性色素で染色することにより、 その二色性色素 を吸着させて偏光子層とする工程、 二色性色素が吸着されたフィルムをホウ 酸水溶液で処理する工程、 およびホウ酸水溶液による処理後に水洗する工程 を経て製造することができる。
必要に応じて、 基材フィルムを偏光子層から剥離除去してもよい。 基材フ ィルムの材料および厚みは、 後述する熱可塑性樹脂フィルムの材料および厚 みと同様であってよい。
[0094] 延伸フィルムまたは延伸層である偏光子層は、 その片面または両面に熱可 塑性樹脂フィルムが貼合されている形態で積層体に組み込まれてもよい。 こ の熱可塑性樹脂フィルムは、 偏光子層 1 0 3用の保護フィルム、 または位相 差フィルムとして機能し得る。 熱可塑性樹脂フィルムは、 例えば、 鎖状ポリ オレフィン系樹脂 （ポリプロピレン系樹脂など） 、 環状ポリオレフィン系樹 月旨 （ノルボルネン系樹脂など） 等のポリオレフィン系樹脂； トリアセチルセ ルロース等のセルロース系樹脂；ポリエチレンテレフタレート、 ポリエチレ ンナフタレート、 ポリプチレンテレフタレート等のポリエステル系樹脂；ポ リカーボネート系樹脂； （メタ） アクリル系樹脂； またはこれらの混合物等 からなるフィルムであることができる。
[0095] 熱可塑性樹脂フィルムの厚みは、 薄型化の観点から、 通常 3 0 0 以下 であり、 好ましくは 2 0 0 以下であり、 より好ましくは 1 0 0 以下 であり、 さらに好ましくは 8 0 以下であり、 なおさらに好ましくは 6 0 以下であり、 また、 通常 5 以上であり、 好ましくは 2 0 〇!以上で 〇 2020/175092 25 卩（：170? 2020 /004755
ある。
[0096] 熱可塑性樹脂フィルムは位相差を有していても、 有していなくてもよい。
[0097] 熱可塑性樹脂フィルムは、 例えば、 接着剤層を用いて偏光子層 1 0 3に貼 合することができる。
[0098] [二色性色素及び重合性化合物を含む組成物を塗布し硬化させてなる偏光 子層]
二色性色素及び重合性化合物を含む組成物を塗布し硬化させてなる偏光子 層としては、 液晶性を有する重合性の二色性色素を含む組成物または二色性 色素と重合性液晶とを含む組成物を基材フィルムに塗布し硬化させて得られ る層等の重合性液晶化合物の硬化物を含む偏光子層が挙げられる。
[0099] 必要に応じて、 基材フィルムを偏光子層から剥離除去してもよい。 基材フ ィルムの材料および厚みは、 上述した熱可塑性樹脂フィルムの材料および厚 みと同様であってよい。 偏光子層は、 配向膜を備えてもよい。 配向膜は、 剥 離されてもよい。
[0100] 二色性色素及び重合性化合物を含む組成物を塗布し硬化させてなる偏光子 層は、 その片面または両面に熱可塑性樹脂フィルムが貼合されている形態で 光学積層体に組み込まれてもよい。 熱可塑性樹脂フィルムとしては、 延伸フ ィルムまたは延伸層である偏光子層に用い得る熱可塑性樹脂フィルムと同様 のものを用いることができる。 熱可塑性樹脂フィルムは、 例えば、 接着剤層 を用いて偏光子層に貼合することができる。
[0101 ] 二色性色素及び重合性化合物を含む組成物を塗布し硬化させてなる偏光子 層は、 その片面または両面に、 保護層として才ーバーコート （〇〇 層が形 成されてもよい。 光硬化性樹脂や水溶性ポリマー等が挙げられる。 光硬化性 樹脂としては、 例えば、 （メタ） アクリル系樹脂、 ウレタン系樹脂、 （メタ ） アクリルウレタン系樹脂、 エポキシ系樹脂、 シリコーン系樹脂等が挙げら れる。 水溶性ポリマーとしては、 例えば、 ポリ （メタ） アクリルアミ ド系ポ リマー ；ポリビニルアルコール、 およびエチレンービニルアルコール共重合 体、 エチレンー酢酸ビニル共重合体、 （メタ） アクリル酸又はその無水物一 〇 2020/175092 26 卩（：170? 2020 /004755
ビニルアルコール共重合体等のビニルアルコール系ポリマー；カルボキシビ ニル系ポリマー；ポリビニルピロリ ドン；デンプン類； アルギン酸ナトリウ ム；ポリエチレンオキシド系ポリマー等が挙げられる。 〇〇層の厚みは、 2 0 以下であることが好ましくは、 1 5 以下であることがより好まし く、 1 〇 以下であることがさらに好ましく、 5 以下であってもよく 、 また、 〇. 0 5 以上であり、 〇. 5 〇!以上であってもよい。
[0102] 二色性色素及び重合性化合物を含む組成物を塗布し硬化させてなる偏光子 層の厚みは、 通常 1 〇 以下であり、 好ましくは〇. 5 以上 8 〇1以 下であり、 より好ましくは 1 以上 5 以下である。
[0103] [第 2粘着剤層]
第 2粘着剤層 1 0 4は、 偏光子層 1 0 3と背面板 1 0 5との間に配置され る粘着剤層である。 第 2粘着剤層は、 積層体を構成する粘着剤層の中で、 最 も背面板に近い位置に配置される粘着剤層であることができる。 第 2粘着剤 層 1 0 4は、 1層であってもよく、 または 2層以上からなるものであっても よいが、 好ましくは 1層である。
[0104] 第 2粘着剤層 1 0 4を構成する粘着剤組成物の組成および配合成分、 粘着 剤組成物のタイプ （活性エネルギー線硬化型や熱硬化型であるか否か等） 、 粘着剤組成物に配合され得る添加剤、 第 2粘着剤層の作製方法、 第 2粘着剤 層の厚み、 については、 上述の第 1粘着剤層 1 0 2の説明において示したも のと同じである。
第 2粘着剤層 1 0 4は、 粘着剤組成物の組成および配合成分、 厚み等にお いて、 第 1粘着剤層 1 0 2と同じであってもよいし、 異なっていてもよい。
[0105] [背面板]
背面板 1 0 5としては、 光を透過可能な板状体や通常の表示装置に用いら れる構成要素等を用いることができる。
[0106] 背面板 1 0 5の厚みは、 例えば 5 以上 2 , 0 0 0 以下であってよ く、 好ましくは 1 0 以上 1 , 0 0 0 以下であり、 より好ましくは 1 5 以上 5 0 0 〇1以下である。 〇 2020/175092 27 卩（：170? 2020 /004755
[0107] 背面板 1 0 5に用いる板状体としては、 1層のみから構成されてよく、 2 層以上から構成されたものであってよく、 前面板 1 0 1 において述べた板状 体について例示したものを用いることができる。
[0108] 背面板 1 0 5に用いる通常の表示装置に用いられる構成要素としては、 例 えばセパレータ、 タッチセンサパネル、 有機巳 !_表示素子等が挙げられる。 表示装置における構成要素の積層順としては、 例えば前面板/円偏光板/セ パレータ、 前面板/円偏光板/有機日 !_表示素子、 前面板/円偏光板/タッ チセンサパネル/有機巳 !_表示素子、 前面板/タッチセンサパネル/円偏光 板/有機巳 !_表示素子等が挙げられる。
[0109] （タッチセンサパネル）
タッチセンサパネルとしては、 タッチされた位置を検出可能なセンサであ れば、 検出方式は限定されることはなく、 抵抗膜方式、 静電容量結合方式、 光センサ方式、 超音波方式、 電磁誘導結合方式、 表面弾性波方式等のタッチ センサパネルが例示される。 低コストであることから、 抵抗膜方式、 静電容 量結合方式のタッチセンサパネルが好適に用いられる。
[01 10] 抵抗膜方式のタッチセンサパネルの _例は、 互いに対向配置された _対の 基板と、 それら一対の基板の間に挟持された絶縁性スぺーサーと、 各基板の 内側の前面に抵抗膜として設けられた透明導電膜と、 タッチ位置検知回路と により構成されている。 抵抗膜方式のタッチセンサパネルを設けた画像表示 装置においては、 前面板の表面がタッチされると、 対向する抵抗膜が短絡し て、 抵抗膜に電流が流れる。 タッチ位置検知回路が、 このときの電圧の変化 を検知し、 タッチされた位置が検出される。
[01 1 1 ] 静電容量結合方式のタッチセンサパネルの一例は、 基板と、 基板の全面に 設けられた位置検出用透明電極と、 タッチ位置検知回路とにより構成されて いる。 静電容量結合方式のタッチセンサパネルを設けた画像表示装置におい ては、 前面板の表面がタッチされると、 タッチされた点で人体の静電容量を 介して透明電極が接地される。 タッチ位置検知回路が、 透明電極の接地を検 知し、 タッチされた位置が検出される。 〇 2020/175092 28 卩（：170? 2020 /004755
[01 12] タッチセンサパネルの厚みは、 例えば 5 以上 2 , 0 0 0 以下であ ってよく、 5 〇!以上 1 0 0 以下であってもよい。
[01 13] [位相差層]
積層体 1 0 0は、 1層又は 2層以上の位相差層をさらに含むことができる 。 位相差層は通常、 偏光子層 1 0 3と背面板 1 0 5との間に配置される。 位 相差層は、 第 1粘着剤層 1 0 2、 第 2粘着剤層 1 0 4、 又はこれらの層以外 の粘着剤若しくは接着剤から構成される層 （以下、 貼合層ともいう） を介し て他の層 （他の位相差層を含む。 ） 上に積層させることができる。
[01 14] [貼合層]
貼合層は、 第 1粘着剤層 1 〇 2と第 2粘着剤層 1 0 4との間に配置される 層であり、 粘着剤又は接着剤から構成される層である。 貼合層を構成する粘 着剤は、 第 1粘着剤層 1 〇 2や第 2粘着剤層を構成する粘着剤組成物にっい て例示したものと同じ剤であってもよいし、 他の粘着剤、 例えば （メタ） ア クリル系粘着剤、 スチレン系粘着剤、 シリコーン系粘着剤、 ゴム系粘着剤、 ウレタン系粘着剤、 ポリエステル系粘着剤、 エポキシ系共重合体粘着剤等で あってもよい。
[01 15] 貼合層を構成する接着剤としては、 例えば、 水系接着剤、 活性エネルギー 線硬化型接着剤、 粘着剤等のうち 1 または 2種以上を組み合せて形成するこ とができる。 水系接着剤としては、 例えばポリビニルアルコール系樹脂水溶 液、 水系二液型ウレタン系エマルジョン接着剤等を挙げることができる。 活 性エネルギー線硬化型接着剤としては、 紫外線等の活性エネルギー線を照射 することによって硬化する接着剤であり、 例えば重合性化合物および光重合 性開始剤を含むもの、 光反応性樹脂を含むもの、 バインダー樹脂および光反 応性架橋剤を含むもの等を挙げることができる。 上記重合性化合物としては 、 光硬化性エポキシ系モノマー、 光硬化性アクリル系モノマー、 光硬化性ウ レタン系モノマー等の光重合性モノマーや、 これらモノマーに由来するオリ ゴマー等を挙げることができる。 上記光重合開始剤としては、 紫外線等の活 性エネルギー線を照射して中性ラジカル、 アニオンラジカル、 カチオンラジ 〇 2020/175092 29 卩（：170? 2020 /004755
カルといった活性種を発生する物質を含むものを挙げることができる。
[01 16] 貼合層の厚みは、 例えば 1 以上であってよく、 好ましくは 1 以上
2 5 以下、 より好ましくは 2 以上 1 5 以下、 さらに好ましくは 2 . 5 以上 5 以下である。
[01 17] 図 2に示す積層体 2 0 0は、 前面板 1 0 1、 第 1粘着剤層 1 0 2、 偏光子 層 1 0 3、 貼合層 1 0 8および背面板 1 0 5を備え、 第 1位相差層 1 0 6、 貼合層 1 0 9、 第 2位相差層 1 0 7および第 2粘着剤層 1 0 4をさらに備え る。
[01 18] 位相差層の例としては、 ス / 4板やス / 2板等のポジティブ八プレート、 およびポジティブ〇プレート等が挙げられる。
位相差層は、 例えば上述の熱可塑性樹脂フィルムから形成することができ る位相差フィルムであってもよいし、 重合性液晶化合物を硬化してなる層、 すなわち、 重合性液晶化合物の硬化物を含む層であってもよいが、 好ましく は後者である。
位相差フィルムの厚みは、 上述の熱可塑性樹脂フィルムの厚みと同様であ ってよい。 重合性液晶化合物を硬化してなる位相差層の厚みは、 例えば、 〇 . 1 〇1以上 1 〇 以下であり、 好ましくは〇. 5 〇!以上 8 〇!以下で あり、 より好ましくは 1 以上 6 〇!以下である。
[01 19] 重合性液晶化合物を硬化してなる位相差層は、 重合性液晶化合物を含む組 成物を基材フィルムに塗布し硬化させることによって形成することができる 。 基材フィルムと塗布層との間に配向層が形成されていてもよい。 基材フィ ルムの材料および厚みは、 上述した熱可塑性樹脂フィルムの材料および厚み と同様であってよい。
重合性液晶化合物を硬化してなる位相差層は、 配向層および/または基材 フィルムを有する形態で積層体 1 0 0に組み込まれてもよい。 背面板 1 0 5 が、 上記組成物が塗布される基材フィルムであってもよい。
[0120] 上述のように、 貼合層 1 0 8は、 粘着剤を用いてもよいし、 接着剤を用い てもよい。 この粘着剤は上述の粘着剤組成物 であってよい。 \¥0 2020/175092 30 卩（：17 2020 /004755
接着剤としては、 水系接着剤または活性エネルギー線硬化性接着剤を用い ることができる。 水系接着剤としては、 ポリビニルアルコール系樹脂水溶液 からなる接着剤、 水系二液型ウレタン系エマルジョン接着剤等が挙げられる
[0121 ] 活性エネルギー線硬化性接着剤とは、 紫外線等の活性エネルギー線を照射 することで硬化する接着剤をいい、 例えば、 重合性化合物および光重合開始 剤を含むもの、 光反応性樹脂を含むもの、 バインダー樹脂および光反応性架 橋剤を含むもの等が挙げられる。
重合性化合物としては、 光硬化性エポキシ系モノマー、 光硬化性 （メタ） アクリル系モノマー、 光硬化性ウレタン系モノマー等の光重合性モノマーや 、 光重合性モノマーに由来するオリゴマー等が挙げられる。
光重合開始剤としては、 紫外線等の活性エネルギー線の照射により中性ラ ジカル、 アニオンラジカル、 カチオンラジカルのような活性種を発生する物 質を含むものが挙げられる。 重合性化合物および光重合開始剤を含む活性エ ネルギー線硬化性接着剤として、 光硬化性エポキシ系モノマーおよび光カチ オン重合開始剤を含むものを好ましく用いることができる。
[0122] [積層体の製造方法]
積層体 1 0 0は、 粘着剤層、 あるいはさらに接着剤層を介して積層体 1 0 0を構成する層同士を貼合する工程を含む方法によつて製造することができ る。 粘着剤層や接着剤層を介して層同士を貼合する場合には、 密着性を高め るために、 貼合面の一方または両方に対して、 例えばコロナ処理等の表面活 性化処理を施すことが好ましい。
偏光子層 1 〇 3は、 熱可塑性樹脂フイルムまたは基材フイルム上に直接形 成することが可能であり、 この熱可塑性樹脂フイルムまたは基材フイルムは 積層体 1 0 0に組み込まれてもよいし、 あるいは、 偏光子層 1 0 3から剥離 されて積層体の構成要素とはならなくてもよい。
[0123] <表示装置 >
本発明に係る表示装置は、 上記本発明に係る積層体 1 〇〇を含む。 表示装 〇 2020/175092 31 卩（：170? 2020 /004755
置は特に限定されず、 例えば有機巳 1_表示装置、 無機巳 1_表示装置、 液晶表 示装置、 電界発光表示装置等の画像表示装置が挙げられる。 表示装置はタッ チパネル機能を有していてもよい。 光学積層体は、 屈曲または折り曲げ等が 可能な可撓性を有する表示装置に好適である。
[0124] 表示装置において、 光学積層体は、 前面板を外側 （表示素子側とは反対側 、 すなわち視認側） に向けて表示装置が有する表示素子の視認側に配置され る。
[0125] 本発明に係る表示装置は、 スマートフォン、 タブレッ ト等のモバイル機器 、 テレビ、 デジタルフォトフレーム、 電子看板、 測定器や計器類、 事務用機 器、 医療機器、 電算機器等として用いることができる。
[0126] <粘着剤組成物 >
本発明に係る粘着剤組成物は、 好ましくは上述の粘着剤組成物 である。 本発明に係る粘着剤組成物は、 公知の方法により、 例えば各成分をミキサー 等を用いて一括混合することにより製造することができる。
[0127] <粘着シ _卜>
本発明に係る粘着シートは、 （メタ） アクリル系ポリマーと、 窒素原子及 び （メタ） アクリロイル基を有する化合物とを含む粘着剤組成物から形成さ れた粘着剤層を含み、 好ましくは粘着剤組成物 から形成された粘着剤層を 含む。 粘着剤層は、 粘着剤組成物を基材上に塗布することにより形成するこ とができる。 粘着剤組成物として活性エネルギー線硬化型粘着剤組成物を用 いた場合は、 形成された粘着剤層に、 活性エネルギー線を照射することによ り所望の硬化度を有する硬化物とすることができる。 粘着剤組成物として熱 硬化型粘着剤組成物を用いた場合には、 形成された粘着剤層に、 加熱処理 （ 及び養生） を施すことにより所望の硬化度を有する硬化物とすることができ る。
[0128] 基材は離型処理が施された剥離フィルムであってよい。 粘着シートは、 離 型フィルム上に粘着剤からなる層をシート状に形成しておき、 その粘着剤層 上にさらに別の剥離フィルムを貼合することにより作製することができる。 〇 2020/175092 32 卩（：170? 2020 /004755
[0129] 本発明に係る粘着シートの粘着層は、 優れた耐熱性を有する。 粘着剤層の 形成に用いられる粘着剤組成物により形成される、 熱分解質量減少率を 8 [ %] とすると、 好ましくは下記の関係式 （4） :
Figure imgf000034_0001
を満たし、 より好ましくは下記の関係式 （4 3） :
1 1 £ 1 9 （4 3）
を満たす。
[0130] 以下、 実施例により本発明をさらに詳細に説明するが、 本発明はこれらの 例によって限定されるものではない。
実施例
[0131 ] [熱硬化型粘着剤組成物を用いた粘着シート]
[ 1 ] 粘着シート 1 1 の製造
（1） （メタ） アクリル系ポリマーの調製
アクリル酸门ーブチル 5 4質量部、 アクリル酸 2 -エチルヘキシル 4 5質 量部およびアクリル酸 4 -ヒドロキシブチル 1質量部を共重合させて、 （メ 夕） アクリル系ポリマーを調製した。 この （メタ） アクリル系ポリマーの分 子量を後述する方法で測定したところ、 重量平均分子量 （!\/! %） は 8 0万で あった。
[0132] （2） 粘着剤組成物の調製
上記工程で得られた （メタ） アクリル系ポリマー 1 0 0質量部 （固形分換 算値；以下同じ） と、 熱架橋剤としてのトリメチロールプロパン変性キシリ レンジイソシアネート （綜研化学社製、 製品名 「丁0 - 7 5」 ） 〇. 2 5質 量部、 およびシランカツプリング剤としての 3—グリシドキシプロピルトリ メ トキシシラン （信越化学工業社製、 製品名 「＜巳!\/1 4 0 3」 ） 〇. 2質量 部とを混合し、 十分に撹拌して、 メチルエチルケトンで希釈することにより 、 粘着剤組成物の塗布溶液を得た。 （メタ） アクリル系ポリマーを 1 〇〇質 量部 （固形分換算値） とした場合の粘着剤組成物の各配合 （固形分換算値） を表 1 に示す。 なお、 表 1 に記載の略号等は以下を表す。 〇 2020/175092 33 卩（：170? 2020 /004755
巳八 ： アクリル酸 -ブチル
2巳 1~1八 ： アクリル酸 2 -エチルヘキシル
41~1巳八 ： アクリル酸 4 -ヒドロキシブチル
[0133] （3） 粘着シート八 1 1の製造
得られた粘着剤組成物の塗布溶液を、 軽セパレータ （リンテック社製， 製 品名 「3 一 巳丁 752 1 50」 ） の剥離処理面に、 ナイフコーターで塗 布した。 そして、 塗布層に対し、 90°〇で 1分間加熱処理して塗布層を形成 した。 次いで、 上記で得られた軽セパレータ上の塗布層と、 重セパレータ （ リンテック社製、 製品名 「3 一 巳丁 382 1 20」 ） とを、 当該セパレ —夕の剥離処理面が塗布層に接触するように貼合し、 23°〇、 50%[¾1~1の 条件下で 7日間養生することにより、 厚さ 25 の粘着剤層を有する粘着 シート八 1 1、 すなわち、 軽セパレータ/粘着剤層 （厚さ ： 25 ） /重 セパレータの構成からなる粘着シート八 1 1 を作製した。 粘着シート八 1 1 の粘着剤層を粘着剤層八 1 1 とする。 粘着シート八 1 1 について、 測定され た熱分解質量減少率を表 1 に示す。 なお、 粘着剤層 1 1の厚さ、 及び熱分 解質量減少率は、 後述する方法で測定した値である。
[0134] [2] 粘着シート八 1 2〜八 1 6の製造
（1） （メタ） アクリル系ポリマーの調製
（メタ） アクリル系ポリマーを構成する各モノマーの割合を表 1 に示すよ うに調製し、 粘着シート 1 1の製造工程と同様にして、 表 1 に示す重量平 均分子量
Figure imgf000035_0001
の （メタ） アクリル系ポリマーを調製した。
[0135] （2） 粘着剤組成物の調製
上記工程で得られた （メタ） アクリル系ポリマー 1 〇〇質量部と、 熱架橋 剤としてのトリメチロールプロパン変性キシリレンジイソシアネート （綜研 化学社製、 製品名 「丁0-75」 ） と、 シランカップリング剤としての 3- グリシドキシプロピルトリメ トキシシラン （信越化学工業社製、 製品名 「＜ 巳1\/1403」 ） とを表 1 に示す配合割合で混合し、 十分に撹拌して、 メチル エチルケトンで希釈することにより、 粘着剤組成物の塗布溶液を得た。 〇 2020/175092 34 卩(：170? 2020 /004755
[0136] （3） 粘着シート八 1 2〜八 1 6の製造
得られた粘着剤組成物の塗布溶液を用いて、 粘着シート 1 1の製造工程 と同様にして、 粘着シート八 1 2 ~八 1 6を作製した。 粘着シート八 1 2〜 八 1 6の粘着剤層を粘着剤層八 1 2 ~八 1 6とする。 粘着シート八 1 2 ~八 1 6について、 後述する方法で測定した粘着剤層八 1 2 ~八 1 6の厚さ、 及 び熱分解質量減少率を表 1 に示す。
[0137] [表 1 ]
Figure imgf000036_0001
[0138] [活性エネルギー線硬化型粘着剤組成物を用いた粘着シート]
[ 1 ] 粘着シート 2 1の製造
（1） （メタ） アクリル系ポリマー八2 1の調製
[0139] 窒素ガスが還流して温度調節が容易になるよう、 冷却装置を設置した 1 !_ の反応器に 2—エチルヘキシルアクリレート （2—巳 1~1八） モノマー 8 4 .
4質量％、 プチルアクリレート （巳八） モノマー 1 5質量％、 2—ヒドロキ シエチルアクリレート （2— 1~1巳八） モノマー〇. 5質童％からなるモノマ —混合物を投入した後、 酸素を除去するため、 窒素ガスを 1時間還流した後 、 8 0 °〇に維持した。 上記モノマー混合物を均一に混合した後、 光重合開始 剤ベンジルジメチルケタール （丨 _ 6 5 1） 〇. 0 5質量％と 1 —ヒドロキ シシクロヘキシルフエニルケトン （丨 一 1 8 4） 〇. 0 5質量％とを投入し た。 次いで攪拌しながら、 II Vランプ （ 1 0 ） を照射して重量平均分子 量 （1\/1 ） 3 7万の （メタ） アクリル系ポリマー八 2 1 を製造した。
[0140] アクリル系ポリマー八 2 1の各モノマー及び各成分の割合を表 2に示す。
なお、 表 2に記載の略号等は以下を表す。
[0141 ] 2—巳 ! ! ： 2—エチルヘキシルアクリレート（東京化成工業株式会社， 日 本）、
BA:プチルアクリ レート（東京化成工業株式会社， 日本）、
2 _H E A: 2—ヒ ドロキシエチルアクリ レート（東京化成工業株式会社， 日本）、
2 -H EMA : 2—エチルヘキシルメタアクリ レート（東京化成工業株式会 社， 日本）、 L A :ラウリルアクリ レート（東京化成工業株式会社， 日本） 、
I - 65 1 :ベンジルジメチルケタール（光重合開始剤， BASF, ドイツ）、
I — 1 84 : 1 —ヒ ドロキシシクロヘキシルフエニルケトン （光重合開始剤 , BASF, ドイツ）。
[0142] （2） 粘着剤組成物の調製
上記工程で得られた （メタ） アクリル系ポリマー 95質量％ （固形分換算 値；以下同じ） と、 添加剤として、 イソデシルアクリ レート（ 丨 DA, Mi won specialty chemical, 韓国） 1質量％及び N—ブトキシメチルアクリルアミ ド （N BMA, 東京化成工業株式会社， 日本） 3質量％と、 光重合開始剤とし て、 ジフエニル （2, 4, 6— トリメチルべンゾイル） ホスフィンオキシド
（T P O, 東京化成工業株式会社， 日本） 0. 5質量％及び 1 _ヒ ドロキシ シクロヘキシルフエニルケトン （ I — 1 84, BASF, ドイツ） 0. 5質量％と を混合し、 十分に攪拌して、 メチルエチルケトンで希釈することにより、 粘 着剤組成物の塗布溶液を得た。 粘着剤組成物の各配合 （固形分換算値） を表 3に示す。 なお、 表 3に記載の略号等は以下を表す。
[0143] I D A :イソデシルアクリ レート（Miwon specialty chemical, 韓国）
N BMA : N—ブトキシメチルアクリルアミ ド （N BMA, 東京化成工業 株式会社， 日本）
T P〇 ： ジフエニル （2, 4, 6— トリメチルべンゾイル） ホスフィンオ キシド （東京化成工業株式会社， 日本）
1 - 1 84 : 1 —ヒ ドロキシシクロヘキシルフエニルケトン （BASF, ドイ ツ）
[0144] （3） 粘着シート八 2 1 の製造 〇 2020/175092 36 卩（：170? 2020 /004755
得られた粘着剤組成物の塗布溶液を、 軽セパレータ （ポリエチレンテレフ タレートフイルム、 厚み 38 ） の離型処理面に、 ナイフコータで塗布し た。 次いで、 上記で得られた系セパレータ上の塗布層と、 重セパレータ （ポ リエチレンテレフタレートフイルム、 厚み 38 〇1） とを、 当該セパレータ の離型処理面が塗布層に接触するように貼合し、
Figure imgf000038_0001
照射 （光源： 1^_八 、 照射強度
Figure imgf000038_0002
積算光量〇. 4」/〇 2） を行い、 厚さ 2 5 の粘着剤層を有する粘着シート 2 1、 すなわち軽セパレータ/粘着 剤層 （厚さ ： 25 ） /重セパレータの構成からなる粘着シート八 2 1 を 作製した。 粘着シート 2 1の粘着剤層を粘着剤層 2 1 とする。 粘着シー 卜八2 1 について、 測定された熱分解質量減少率を表 3に示す。 なお、 粘着 剤層 2 1の厚さ、 及び熱分解質量減少率は、 後述する方法で測定した値で ある。
[0145] [2] 粘着シート八22, 八 23の製造
（1） （メタ） アクリル系ポリマー八 22， 八 23の調製
（メタ） アクリル系ポリマーを構成する各モノマーの割合を表 2に示すよ うに調製し、 粘着シート 2 1の製造工程と同様にして、 表 2に示す重量平 均分子量 （1\/1 ） の （メタ） アクリル系ポリマー八 22, 八 23を調製した
[0146] （2） 粘着剤組成物の調製
上記工程で得られた （メタ） アクリル系ポリマーと、 添加剤とを表 3に示 す配合割合で混合し、 十分に攪拌して、 メチルエチルケトンで希釈すること により、 粘着剤組成物の塗布溶液を得た。
[0147] （3） 粘着剤シート八 22, 八23の製造
得られた粘着剤組成物の塗布溶液を用いて、 粘着シート 2 1の製造工程 と同様にして、 粘着シート八22, 八 23を作製した。 粘着シート八22, 八 23の粘着剤層を粘着剤層八 22, 八23とする。 粘着シート八22, 八 23について、 後述する方法で測定した粘着剤層 22, 23の厚さ、 及 び熱分解質量減少率を表 3に示す。 〇 2020/175092 37 卩（：170? 2020 /004755
[0148] [表 2]
Figure imgf000039_0006
[0149] [表 3]
Figure imgf000039_0007
[0150] ＜重量平均分子量 （IV! \«） の測定＞
（メタ） アクリル系ポリマーの重量平均分子量
Figure imgf000039_0001
は、 ポリスチレン 換算の数平均分子量 （Mn） として、 移動相にテトラヒドロフランを用い、 下記のサイズエクスクルージョンクロマトグラフィー （3巳〇） により求め た。
測定する （メタ） アクリル系ポリマーを約〇. 05質量％の濃度でテトラ ヒドロフランに溶解させ、 3巳（3に 1 〇 し注入した。 移動相は、 1. 〇 1-/分の流量で流した。 カラムとして、 1_ 96 丨 IV! 丨 X巳 0 _巳 （ポリ マーラボラトリーズ製） を用いた。 検出器には
Figure imgf000039_0002
I 3検出器 （商品名
Figure imgf000039_0003
を用いた。
[0151] ＜層の厚み＞
接触式膜厚測定装置 （株式会社ニコン製 「!\/!3_5（3」 ） を用いて測定し た。
ただし、 偏光子層および配向膜については、 レーザー顕微鏡 （オリンパス 株式会社製 「〇!_33000」 ） を用いて測定した。
[0152] ＜熱分解質量減少率＞
粘着シートを幅 25〇1〇1 長さ 1
Figure imgf000039_0004
に裁断した。 粘着シートから離 型フィルムを除去した後、 粘着剤層をパンに入れ、 熱重量分析装置 （製品名 :丁〇八550、
Figure imgf000039_0005
社製） にて、 昇温速度 1 0°〇/分で室温から 200 °〇までこの粘着剤層を加熱した。 室温での粘着剤層の質量 [9] 及び 20 〇 2020/175092 38 卩（：170? 2020 /004755
〇°〇まで加熱した後の粘着剤層の質量 \^/2 0 0 [ 9 ] に基づいて、 下記の式 （5 ） により熱分解質量減少率 8を算出した。
[¾ = { （\^ - \^/2 0 0） / 「} X 1 0 0 [%] （5）
[0153] [前面板（ウインドウフイルム）]
前面板として、 片面にハードコート層 （厚み 1 〇 ） を有するポリイミ ドフイルム （厚み 5 0 〇〇 を用意した。
[0154] [偏光子層]
1 . 以下の材料を準備した。
1） 厚み 2 5 〇1の丁八〇フイルム。
[0155] 2） 配向膜形成用組成物。
＜ポリマー 1＞
以下の構造単位からなる光反応性基を有するポリマー 1 を準備した。
Figure imgf000040_0001
[0157] ポリマー 1 を濃度 5質量％でシクロペンタノンに溶解した溶液を配向膜形 成用組成物 [以下、 組成物 （〇_ 1） ともいう] として用いた。
[0158] 3） 偏光子層形成用組成物
＜重合性液晶化合物＞
重合性液晶化合物は、 式 （1 _ 1） で表される重合性液晶化合物 [以下、 化合物 （1 _ 1） ともいう] と式 （1 _ 2） で表される重合性液晶化合物 [ 以下、 化合物 （1 —2） ともいう] とを用いた。
Figure imgf000040_0002
Figure imgf000041_0001
［0161］ 化合物 （ 1 - 1） および化合物 （1 -2） は、 L u b e t a l . R e c I . T r a v . C h i m . P a y s— B a s、 1 1 5、 32 1 —328 （ 1 996） 記載の方法により合成した。
［0162］ ＜二色性色素＞
二色性色素には、 下記式 （2 _ 1 a） 、 （2— 1 b） 、 （2— 3 a） で示 される特開 201 3- 1 01 328号公報の実施例に記載のアゾ色素を用い た。
Figure imgf000041_0002
［0165］ 偏光子層形成用組成物 ［以下、 組成物 （八_ 1） ともいう］ は、 化合物 （
1 - 1） 75質量部、 化合物 （1 _2） 25質量部、 二色性染料としての上 記式 （2— 1 3） 、 （2— 1 13） 、 （2— 33） で示されるアゾ色素各 2.
5質量部、 重合開始剤としての 2—ジメチルアミノー 2—ベンジルー 1 — （ 4 -モルホリノフエニル） ブタンー 1 -オン （ I 「 93〇リ 「 6369、 巳 八 3 ジャパン社製） 6質量部、 およびレべリング剤としてのポリアクリレ -卜化合物 （巳丫［＜-36 1 1\1、 巳丫［＜-〇 6〇1 丨 6社製） 1. 2質量部 を、 溶剤のトルエン 400質量部に混合し、 得られた混合物を 80°〇で 1時 間攪拌することにより調製した。
［0166］ 4） 保護層 （0◦層） 形成用組成物
保護層 （〇◦層） 形成用組成物 ［以下、 組成物 （巳_ 1） ともいう］ は、 水： 1 〇〇質量部、 ポリビニルアルコール樹脂粉末 （ （株） クラレ製、 平均 重合度 1 8000、 商品名 ： KL— 3 1 8） : 3質量部、 ポリアミ ドエポキ シ樹脂 （架橋剤、 住化ケムテックス （株） 製、 商品名 ： S R 650 （30） ） : 1. 5質量部を混合することにより調製した。
[0167] 2. 作製方法
1） 以下のようにして TACフィルム側に配向膜形成用組成物をコーティ ングした。
まず T ACフィルム側にコロナ処理を 1回施した。 コロナ処理の条件は、 出力 0. 3 kW、 処理速度 3 m/分とした。 その後、 該 TAC上に、 上述の 通り得られた組成物 （D— 1） をバーコート法により塗布し、 80°Cの乾燥 オーブン中で 1分間加熱乾燥した。 得られた乾燥被膜に偏光 UV照射処理を 施して第 1配向膜 （AL 1） を形成した。 偏光 UV処理は、 UV照射装置 （ S POT CU R E S P- 7 ; ウシオ電機株式会社製） から照射される光 を、 ワイヤーグリッ ド （U 丨 S-27 1 32 ##、 ゥシオ電機株式会社製） を透過させて、 波長 365 n mで測定した積算光量が 1 00mJ/c m2であ る条件で行った。 第 1配向膜 （A L 1） の厚みは 1 00 n mであった。
[0168] 2） 以下のようにして配向膜側に偏光子層形成用組成物をコーティングし た。
まず形成した第 1配向膜 （AL 1） 上に、 組成物 （A- 1） をパーコート 法により塗布し、 1 20°Cの乾燥オーブンにて 1分間加熱乾燥した後、 室温 まで冷却した。 上記 UV照射装置を用いて、 積算光量 1 200 mJ/c m2 （ 365 n m基準） で紫外線を、 乾燥被膜に照射することにより、 偏光子層 （
P〇 I） を形成した。 得られた偏光子層 （p〇 丨） の厚みをレーザー顕微鏡 （オリンパス株式会社社製 OLS 3000） により測定したところ、 1.
8仰 であった。 このようにして 「TAC/AL 1 /p o 丨」 からなる積層 体を得た。
[0169] 3） 以下のようにして偏光子層側に保護層 （OC層） 形成用組成物をコー テイングした。 〇 2020/175092 41 卩（：170? 2020 /004755
形成した偏光子層 （ 〇 丨） 上に、 組成物 （巳_ 1） をバーコート法によ り塗布し、 乾燥後の厚みが 1. 〇 となるように塗工し、 温度 80 °〇で 3 分間乾燥した。 このようにして 「丁八〇フイルム/〇 !_ （八1_ 1 + 〇 1 十保護層） 」 からなる積層体を得た。
[0170] [位相差層]
1. 材料準備
以下の材料を準備した。
1） 厚み 1 00 〇1の 巳丁フイルム。
[0171] 2） 配向膜形成用組成物。
<ポリマー 1 >
以下の構造単位からなる光反応性基を有するポリマー 1 を準備した。
Figure imgf000043_0001
[0172] ポリマー 1 を濃度 5質量％で、 シクロペンタノンに溶解した溶液を配向膜 形成用組成物 [以下、 組成物 （〇_ 1） ともいう] として用いた。
[0173] 3） 位相差層形成用組成物
下記に示す各成分を混合し、 得られた混合物を 80°◦で 1時間攪拌するこ とにより、 組成物 （巳_ 1） を得た。
下記式で示される化合物匕 _ 1 : 80質量部
Figure imgf000043_0002
〇 2020/175092 42 卩（：170? 2020 /004755
[0174] 下記式で示される化合物 1^— 2 : 20質量部
Figure imgf000044_0001
[0175] 重合開始剤 （丨 「 9 3〇リ 「 6369、 2—ジメチルアミノー 2—ベンジ ルー ·！ 一 （4—モルホリノフエニル） ブタンー 1 —オン、 巳八3 ジャパン 社製） ： 6質量部
レべリング剤 （巳丫[<-36 1 1\1、 ポリアクリレート化合物、 巳丫 ー〇 ㊀社製） ： 0. 1質量部
溶剤 （シクロペンタノン） ： 400質量部
[0176] 2. 作製方法
1） 以下のようにして 巳丁フィルムに配向膜形成用組成物をコーティン グした。
基材として厚み 1 0 0 〇1のポリエチレンテレフタレートフイルム （ 巳 丁） を準備し、 該フィルム上に組成物 （0_ 1） をバーコート法により塗布 し、 80°〇の乾燥オーブン中で 1分間加熱乾燥した。 得られた乾燥被膜に偏 光 II V照射処理を施して第 2配向膜 （ !_ 2） を形成した。 偏光 II V処理は 、 上記リ V照射装置を用いて、 波長 365 n mで測定した積算光量が 1 00
Figure imgf000044_0002
2である条件で行った。 また、 偏光 II Vの偏光方向は偏光子層の吸 収軸に対して 45° となるように行った。 このようにして 「基材 （ 巳丁）
/第 2配向膜 （八1_ 2） 」 からなる積層体を得た。
[0177] 2） 以下のようにして 巳丁フィルムの配向膜側に位相差層形成用組成物 をコーティングした。
こうして得られた第 1基材の第 2配向膜 （八!_ 2） 上に、 組成物 （巳_ 1 ） をバーコート法により塗布し、 1 20°〇の乾燥オーブンで 1分間加熱乾燥 した後、 室温まで冷却した。 得られた乾燥被膜に、 上記 II V照射装置を用い て、 積算光量
Figure imgf000044_0003
（365 n 基準） の紫外線を照射するこ 〇 2020/175092 43 卩（：170? 2020 /004755
とにより、 位相差層を形成した。 得られた位相差層の厚みをレーザー顕微鏡 （オリンパス株式会社製 01-33000） により測定したところ、 2. 〇 であった。 位相差層は、 面内方向にス /4の位相差値を示すス /4板 （〇 ） であった。 このようにして 「基材 （ 巳丁） /八1_ 2/〇\^/ 」 から なる積層体を得た。
[0178] [共通粘着シート]
1） アクリル樹脂の重合
下記成分を、 窒素雰囲気下で撹拌しながら 55 °〇で反応させることにより アクリル樹脂を得た。
アクリル酸プチル： 70質量部
アクリル酸メチル： 20質量部
アクリル酸： 2. 0質量部
ラジカル重合開始剤 （2, 2’ ーアゾビスイソプチロニトリル） ： 0. 2 質量部
[0179] 2） 粘着剤組成物の調液
下記成分を混合し、 粘着剤組成物を得た。
アクリル樹脂： 1 〇〇質量部
架橋剤 （東ソー株式会社製 「コロネート！-」 ） ： 1. 0質量部 シランカップリング剤 （信越シリコン株式会社製 「乂_ 1 2-981」 ）
: 〇. 5質量部
全体固形分濃度が 1 〇質量％になるように酢酸エチルを添加して、 粘着剤 組成物を得た。
[0180] 3） 粘着シートの製造
得られた粘着剤組成物を離型処理されたポリエチレンテレフタレートフィ ルム （重セパレータ、 厚み 38 ） の離型処理面に、 アプリケーターを利 用して乾燥後の厚みが 5 になるように塗布した。 塗布層を 1 00°〇で1 分間乾燥して、 粘着剤層を備えるフィルムを得た。 その後、 粘着剤層の露出 面上に、 離型処理された別のポリエチレンテレフタレートフイルム （軽セパ 〇 2020/175092 44 卩（：170? 2020 /004755
レータ、 厚み 38 ） を貼合した。 その後、 温度 23°（：、 相対湿度 50%
Figure imgf000046_0001
軽セパレータ/共通粘着剤層/重セパレータ を得た。
［0181］ ［実施例 1］
図 4 （3） 〜 （6） に示す手順で積層体を製造した。 まず、 上述の偏光子 層を含む積層体 4 1 0 ［丁八〇フィルム 301 /〇 1_ （ （八1_ 1 + 〇 1 ） 302/〇〇層303） ］ と上述の共通粘着シート 420 （軽セパレータ
304/共通粘着剤層 305/重セパレータ 306） とを準備した （図 4 （ 3） ） 。 偏光子層を含む積層体 4 1 0の〇〇層303側と、 共通粘着シート
420の軽セパレータ 304を剥離した面とにコロナ処理 （出力〇. 3 <\^/ 、 速度
Figure imgf000046_0002
を施した後、 貼合し、 積層体 3430を得た。 上述の位相 差層 440 ［基材 （ 巳丁） 308/ !_ 2/〇\^/ 307］ を準備した。
（図 4 （匕） ） 。
［0182］ 次に位相差層 44〇の〇 307側と、 積層体 3430の重セパレータ
306とを剥離した面にコロナ処理 （出力〇.
Figure imgf000046_0003
を施 した後、 貼合し、 積層体匕 450を得た。 その後、 粘着シート 460 （軽セ パレータ 309/粘着剤層 3 1 0/重セパレータ 3 1 1） として上述で作製 した粘着シート 1 2を準備した （図 4 （〇） ） 。 粘着シート 460の粘着 剤層 3 1 0は第 2粘着剤層に相当する。
［0183］ 積層体匕 450の基材 （ 巳丁） 308を剥離した面と、 粘着シート 46
0の軽セパレータ 309を剥離した面とにコロナ処理 （出力〇. 3 <\^/、 速 度 3 /分） を施した後、 貼合し、 積層体〇 470を得た。 さらに、 粘着シ —卜 490 （軽セパレータ 3 1 4/粘着剤層 3 1 5/重セパレータ 3 1 6） として上述で作製した粘着シート八 1 1 を準備し、 軽セパレータ 3 1 4を剥 離した面と、 上述の前面板 480 （ポリイミ ドフィルム 3 1 3/ハードコー 卜層 3 1 2） のポリイミ ドフィルム 3 1 3側とにコロナ処理 （出力 0. 3 < 、
Figure imgf000046_0004
を施した後、 貼合し、 積層体 500を得た （図 4 （ ） ） 。 粘着シート 490の粘着剤層 3 1 5は第 1粘着剤層に相当する。 〇 2020/175092 45 卩（：170? 2020 /004755
[0184] 積層体 500の重セパレータ 3 1 6を剥離した面と、 積層体〇 470の 丁八0301側にコロナ処理 （出力〇.
Figure imgf000047_0001
を施した後
、 貼合し、 実施例 1の積層体 300を得た （図 4 （6） ） 。 実施例 1の積層 体について、 後述の方法により常温屈曲性及び常温粘着耐久性の評価を行っ た。 結果を表 4に示す。
[0185] [実施例 2〜 5, 比較例 1 , 2]
実施例 1 において、 粘着シート八 1 1 , 八 1 2を用いたことに代えて、 表 4に示す粘着剤層を有する粘着シートを用いたこと以外は実施例 1 と同様に して、 実施例 2〜 5, 比較例 1 , 2の積層体を作製した。 実施例 2〜 5, 比 較例 1 , 2の積層体について、 後述の方法により常温屈曲性及び常温粘着耐 久性の評価を行った。 結果を表 4に示す。
[0186] ＜常温屈曲性＞
各実施例及び各比較例で得られた積層体について、 屈曲装置
Figure imgf000047_0002
丨 e n 〇 6 T ow n社製、 3丁3 - [¾丁一500） を用いて、 常温屈曲性を確 認する評価試験を行った。
重セパレータ 3 1 1 を剥離して、 厚み 1 00 〇1の 巳丁フイルムに貼合し 、 積層体を得た。 巳丁フィルムは背面板に相当する。 図 3は、 本評価試験 の方法を模式的に示す図である。 図 3に示すように、 個別に移動可能な二つ の載置台 501 , 502を、 間隙〇が 6.
Figure imgf000047_0003
（38） となるように配置 し、 間隙〇の中心に幅方向の中心が位置するようにし、 かつ、 ハードコート 層 3 1 2が上側に位置するようにして積層体を固定して配置した （図 3 （3 ） ） 。 そして、 二つの載置台 501 , 502を位置 1および位置 2を回 転軸の中心として上方に 90度回転させて、 載置台の間隙＜3に対応する積層 体の領域に曲げの力 （前面板 480を内側にした曲げの力） を付加した （図 3 （匕） ） 。 その後、 二つの載置台 501 , 502を元の位置に戻した （図 3 （3） ） 。 以上の一連の操作を完了して、 曲げの力の付加回数を 1回と力 ウントした。 これを、 温度 25°〇において繰返し行った後、 積層体の載置台 501 , 502の間隙（3に対応する領域における粘着剤層中の気泡の発生の 〇 2020/175092 46 卩（：170? 2020 /004755
有無を確認した。 載置台 5 0 1 , 5 0 2の移動速度、 曲げの力の付加のベー スは、 いずれの積層体に対する評価試験においても同一の条件とした。 「粘 着剤抜け」 とは、 粘着剤層が積層体の端部からはみ出すことを意味する。 八 ：曲げの力の付加回数が 2 0万に達しても気泡が発生しなかった。 巳 ：曲げの力の付加回数が 1 5万以上 2 0万未満で気泡が発生した。
0 :曲げの力の付加回数が 1 0万以上 1 5万未満で気泡が発生した。
〇 :曲げの力の付加回数が 5万以上 1 0万未満で気泡が発生した。
巳 ：曲げの力の付加回数が 5万未満で気泡/粘着剤抜けが発生した。
[0187] <高温粘着耐久性 >
各実施例及び各比較例で得られた積層体を幅 1 〇〇 長さ 1 〇〇 にカッテイングした。 重セパレータ 3 1 1 を剥がして、 無アルカリガラスに 貼合した。 オートクレープ （5 0 °〇、 5気圧） 中で約 2 0分圧着処理し、 恒 温恒湿条件 （ 2 3 °〇、 5 0 % [¾ 1~1） で 4時間保持した。 8 5 °〇のオーブンに サンプルを入れて、 2 5 0時間後、 浮き、 剥がれ、 気泡の有無を判断した。 なお、 貼合された積層体において、 無アルカリガラスが背面板に相当する。
〇： 浮き、 剥れ、 発泡等の外観変化がほとんどみられない。
△: 浮き、 剥れ、 発泡等の外観変化がやや目立つ。
X： 浮き、 剥れ、 発泡等の外観変化が顕著に認められる。
[0188] [表 4]
Figure imgf000048_0002
[0189] 実施例 1〜 5は 「[¾ 1 > [¾ 2」 の関係を満たし、 かつ、
Figure imgf000048_0001
に 1 0質量％以上 2 0質量％以下の範囲に含まれる。
符号の説明
[0190] 1 0 0 , 2 0 0 積層体、 1 0 1 前面板、 1 0 2 第 1粘着剤層、 1 0 20/175092 47 卩（：170? 2020 /004755
3 偏光子層、 1 04 第 2粘着剤層、 1 05 背面板、 1 06 第 1位相 差層、 1 07 第 2位相差層、 1 08, 1 09 貼合層、 301 丁八〇フ ィルム、 302 〇 丨、 303 〇〇層、 305 共通粘着剤層、 306
, 3 1 1 , 3 1 6 重セパレータ、 307 〇 、 308 基材、 304 , 309, 3 1 4 軽セパレータ、 3 1 0, 3 1 5 粘着剤層、 3 1 2 ハ —ドコート層、 3 1 3 ポリイミ ドフィルム、 4 1 0 偏光子層を含む積層 体、 420 共通粘着シート、 430 積層体 3、 440 位相差層、 45 0 積層体 460, 490 粘着シート、 470 積層体〇、 500 積層体 、 501 , 502 ステージ。

Claims

〇 2020/175092 48 卩（：170? 2020 /004755 請求の範囲
[請求項 1 ] 前面板と、 第 1粘着剤組成物を用いて形成された第 1粘着剤層と、 偏光子層と、 第 2粘着剤組成物を用いて形成された第 2粘着剤層と、 背面板と、 をこの順に含み、
前記第 1粘着剤層の熱分解質量減少率を 8 1 [%] 、 前記第 2粘着 剤層の熱分解質量減少率を 8 2 [%] とすると、 下記の関係式 （ 1 ）
Figure imgf000050_0001
を満たし、
前記第 1粘着剤層と前記第 2粘着剤層は、 熱分解質量減少率が 1 0 質量％以上 2 0質量％以下である、 積層体。
[請求項 2] 前記第 1粘着剤組成物及び前記第 2粘着剤組成物は、 いずれも （メ 夕） アクリル系ポリマーを含み、
前記 （メタ） アクリル系ポリマーは、 反応性官能基を有するモノマ _に由来する構成単位が全質量を基準に 5質量％未満である、 請求項 1 に記載の積層体。
[請求項 3] 前記第 1粘着剤層及び前記第 2粘着剤層は、 いずれも （メタ） アク リル系ポリマーを含み、
前記 （メタ） アクリル系ポリマーは、 重量平均分子量
Figure imgf000050_0002
が 2 0万以上 1 5 0万以下である、 請求項 1又は 2に記載の積層体。
[請求項 4] 前記背面板は、 タッチセンサパネルである、 請求項 1 〜 3のいずれ か 1項に記載の積層体。
[請求項 5] 請求項 1 〜 4のいずれか 1項に記載の積層体を含む表示装置。
[請求項 6] 前記前面板側を内側にして屈曲可能である、 請求項 5に記載の表示 装置。
PCT/JP2020/004755 2019-02-27 2020-02-07 積層体 WO2020175092A1 (ja)