WO2020162468A1 - Procédé de formage de plaque de verre - Google Patents

Procédé de formage de plaque de verre Download PDF

Info

Publication number
WO2020162468A1
WO2020162468A1 PCT/JP2020/004192 JP2020004192W WO2020162468A1 WO 2020162468 A1 WO2020162468 A1 WO 2020162468A1 JP 2020004192 W JP2020004192 W JP 2020004192W WO 2020162468 A1 WO2020162468 A1 WO 2020162468A1
Authority
WO
WIPO (PCT)
Prior art keywords
glass plate
molding
glass
forming
mold
Prior art date
Application number
PCT/JP2020/004192
Other languages
English (en)
Japanese (ja)
Inventor
諭 金杉
祐司 井本
純一 宮下
達也 山下
Original Assignee
Ａｇｃ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ａｇｃ株式会社 filed Critical Ａｇｃ株式会社
Priority to JP2020571222A priority Critical patent/JP7476805B2/ja
Priority to CN202080010214.0A priority patent/CN113329978A/zh
Publication of WO2020162468A1 publication Critical patent/WO2020162468A1/fr

Abstract

L'invention concerne un procédé de formage à la presse de plaque de verre qui consiste à enserrer une plaque de verre avec deux moules de formage, à former la partie centrale en verre de la plaque de verre par l'application d'une première force de compression inférieure ou égale à 0,1 MPa dans la direction de serrage de moule ou sans application de la force de compression et à former la partie périphérie externe en verre en introduisant une seconde force de compression de 0,1 à 10 MPa. En variante, le procédé consiste à appliquer la première force de compression inférieure ou égale à 0,1 MPa dans la direction de serrage de moule à partir de l'un de la paire de moules de formage sur la plaque de verre, à enserrer la partie périphérique externe en verre de la plaque de verre entre la paire de moules de formage, à délimiter, sur le côté de périphérie interne de la partie de périphérie externe en verre, un espace entre la plaque de verre et le premier moule de formage disposé au niveau de l'extrémité avant dans la direction de serrage de moule et à fournir une pression négative au niveau de cet espace pour amener la plaque de verre à être aspirée sur le premier moule de formage.
PCT/JP2020/004192 2019-02-08 2020-02-04 Procédé de formage de plaque de verre WO2020162468A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP2020571222A JP7476805B2 (ja) 2019-02-08 2020-02-04 ガラス板の成形方法
CN202080010214.0A CN113329978A (zh) 2019-02-08 2020-02-04 玻璃板的成形方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2019021562 2019-02-08
JP2019-021562 2019-02-08

Publications (1)

Publication Number Publication Date
WO2020162468A1 true WO2020162468A1 (fr) 2020-08-13

Family

ID=71948025

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/004192 WO2020162468A1 (fr) 2019-02-08 2020-02-04 Procédé de formage de plaque de verre

Country Status (4)

Country Link
JP (1) JP7476805B2 (fr)
CN (1) CN113329978A (fr)
TW (1) TWI830868B (fr)
WO (1) WO2020162468A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20230068048A (ko) * 2021-11-10 2023-05-17 주식회사 도우인시스 Cid용 멀티 곡률 윈도우 글라스 제조 방법

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130081428A1 (en) * 2011-09-30 2013-04-04 Hon Hai Precision Industry Co., Ltd. Method and equipment for manufacturing curved glass sheet
WO2018097068A1 (fr) * 2016-11-22 2018-05-31 旭硝子株式会社 Feuille d'article moulé, pièce d'article moulé, et procédé de production destiné à une feuille d'article moulé
JP2018525306A (ja) * 2015-06-26 2018-09-06 コーニング インコーポレイテッド シート材を再形成するための装置および方法

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4711653A (en) * 1986-12-29 1987-12-08 Ppg Industries, Inc. Innovative press bending of thermoplastic sheets
US4767437A (en) * 1987-03-25 1988-08-30 Ppg Industries, Inc. Horizontal press bending using a splitting vacuum/pressure pickup
JPH0297432A (ja) * 1988-10-04 1990-04-10 Nippon Sheet Glass Co Ltd 板ガラスの成形方法
GB9407594D0 (en) * 1994-04-15 1994-06-08 Pilkington Glass Ltd Bending glass sheets
CN101883739B (zh) * 2007-12-04 2013-06-05 旭硝子株式会社 玻璃板的弯曲成形方法及玻璃板的弯曲成形装置
CN102173568B (zh) * 2011-02-18 2012-11-07 福耀玻璃工业集团股份有限公司 一种弯曲玻璃板的方法和装置
US10479052B2 (en) * 2014-08-20 2019-11-19 Corning Incorporated Methods of forming shaped glass articles from glass sheets

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130081428A1 (en) * 2011-09-30 2013-04-04 Hon Hai Precision Industry Co., Ltd. Method and equipment for manufacturing curved glass sheet
JP2018525306A (ja) * 2015-06-26 2018-09-06 コーニング インコーポレイテッド シート材を再形成するための装置および方法
WO2018097068A1 (fr) * 2016-11-22 2018-05-31 旭硝子株式会社 Feuille d'article moulé, pièce d'article moulé, et procédé de production destiné à une feuille d'article moulé

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20230068048A (ko) * 2021-11-10 2023-05-17 주식회사 도우인시스 Cid용 멀티 곡률 윈도우 글라스 제조 방법
KR102557819B1 (ko) 2021-11-10 2023-07-20 주식회사 도우인시스 Cid용 멀티 곡률 윈도우 글라스 제조 방법

Also Published As

Publication number Publication date
TW202039380A (zh) 2020-11-01
CN113329978A (zh) 2021-08-31
JPWO2020162468A1 (ja) 2021-12-09
TWI830868B (zh) 2024-02-01
JP7476805B2 (ja) 2024-05-01

Similar Documents

Publication Publication Date Title
WO2020162467A1 (fr) Dispositif de moulage de plaque de verre
TWI551554B (zh) The forming device and forming method of glass frame body
CN104843976B (zh) 一种3d曲面超薄玻璃弯曲成型装置和制造方法
WO2020162468A1 (fr) Procédé de formage de plaque de verre
JP2012116705A (ja) 光学素子の成形装置及び成形方法
KR20210069099A (ko) 시트를 벤딩하는 방법 및 장치
JP3608768B2 (ja) ガラス光学素子用プレス成形装置及びガラス光学素子の成形方法
WO2013011853A1 (fr) Dispositif de moulage et procédé de moulage pour revêtements en verre
JPH0463817B2 (fr)
JP2621956B2 (ja) 光学素子の成形方法
JP3216100B2 (ja) 精密ガラス製品の製造方法
JP2011136882A (ja) 光学素子の成形装置
JP5953906B2 (ja) 光学素子の成形装置及び成形方法
US20020116950A1 (en) Heated ceramic female mold
JP2598475B2 (ja) 板ガラスの曲げ成形装置
JP2011184248A (ja) 光学素子の成形装置
JP4327974B2 (ja) 光学ガラス素子の成形方法
JP2013112592A (ja) 光学素子の成形装置及び成形方法
JP2013252986A (ja) 光学素子の成形装置、成形型及び光学素子の成形方法
TW201341321A (zh) 離型片材及玻璃成形品之成形方法
JPS6168331A (ja) ガラスレンズのプレス成形方法
JP2014139117A (ja) 光学素子の成形方法
JPH02275722A (ja) 光学素子の成形方法及び成形装置
JP2003054968A (ja) 光学素子の成形方法
JP2001335329A (ja) ガラスプリフォームの浮上搬送装置

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20752185

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2020571222

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20752185

Country of ref document: EP

Kind code of ref document: A1