WO2020075577A1 - ポリオレフィン系接着剤組成物 - Google Patents

ポリオレフィン系接着剤組成物 Download PDF

Info

Publication number
WO2020075577A1
WO2020075577A1 PCT/JP2019/038749 JP2019038749W WO2020075577A1 WO 2020075577 A1 WO2020075577 A1 WO 2020075577A1 JP 2019038749 W JP2019038749 W JP 2019038749W WO 2020075577 A1 WO2020075577 A1 WO 2020075577A1
Authority
WO
WIPO (PCT)
Prior art keywords
mass
parts
adhesive composition
acid
polyolefin
Prior art date
Application number
PCT/JP2019/038749
Other languages
English (en)
French (fr)
Inventor
知佳 高田
Original Assignee
東洋紡株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 東洋紡株式会社 filed Critical 東洋紡株式会社
Priority to JP2020521622A priority Critical patent/JPWO2020075577A1/ja
Publication of WO2020075577A1 publication Critical patent/WO2020075577A1/ja

Abstract

【課題】　硬化剤不使用でもポリオレフィン樹脂基材とその他の異種材との良好な接着性を示し、低温での貼り合わせが可能であり、貯蔵安定性に優れる接着剤組成物を提供する。 【解決手段】　酸変性ポリオレフィン（Ａ）、応力緩和剤（Ｂ）および粘着付与剤（Ｃ）を（A）１００重量部に対して1～４５重量部含有する接着剤組成物。

Description

ポリオレフィン系接着剤組成物
　本発明は、接着剤組成物、積層体に関する。
ポリプロピレン、ポリエチレン等のポリオレフィン系樹脂は、安価で成形性、耐薬品性、耐水性、電気特性など多くの優れた性質を有するため、シート、フィルム、成形物等として、近年広く採用されている。 
しかし、これらポリオレフィン系樹脂からなる基材（以下、ポリオレフィン系基材）は、ポリウレタン系樹脂、ポリアミド樹脂、アクリル系樹脂、ポリエステル樹脂等の極性基材とは異なり、非極性かつ結晶性であるため、塗装や接着が困難であるという欠点を有する。
最近は、ポリオレフィン系基材同士のみならず、例えば塩化ビニル（PVC）、ポリエステルといった極性プラスチック基材や、金属など異種材料とポリオレフィン系基材との優れた付着性への要求が大きくなっている。
異種材接着剤の主成分としては、エチレン－酢酸ビニル共重合体のケトン化物、ポリアミド樹脂、無水ポリカルボン酸、エチレンとアクリル酸エステル類との共重合体からなるもの（特許文献１）や、スチレン－ エチレン－ プロピレン－ スチレンブロック共重合ゴムあるいはスチレン－ ブタジエン－ スチレンブロック共重合ゴムに、粘着付与樹脂成分およびプロセスオイルなどの液状可塑剤を添加してなるものなどが知られている（特許文献２）が、いずれも接着剤組成物とポリオレフィン系基材との極性の差が大きく親和性に乏しいため、ポリオレフィン系基材との間での剥離が生じやすく、接着性は不充分である。
そこで、ポリオレフィン系基材との親和性が高い、変性ポリオレフィン樹脂等の有機溶剤溶解物（ ワニス） を接着剤としてポリオレフィン系基材に塗布することにより、接着性の向上をはかる手法（特許文献３）等が用いられている。しかし、極性基材への接着性のみであり、ポリプロピレンなどの非極性基材に対する接着性は低い。
このような状況のもと、異種材料用接着剤が種々提案されている（例えば、特許文献４～６参照）。
特開平１１－９２７３３号公報 特開平８－６０１２１号公報 特開２００２－１７３５１４号公報 特許第６００６３８７号 特開２００４－２９２７１６号公報 特許第５３２０６６２号
　しかしながら、前記提案されている接着剤組成物は硬化剤を使用しない場合の接着性が不十分であり、硬化剤が必須であった。そのため、エージングが必要である点、ポットライフが短いという点でいまだ不十分であった。本発明は、硬化剤不使用でもポリオレフィン樹脂基材とその他の異種材との良好な接着性を示し、低温での貼り合わせが可能である接着剤組成物を提供するものである。
　上記課題を達成するため、本発明者らは鋭意検討し、特定の応力緩和剤、粘着付与剤および酸変性ポリオレフィンの組み合わせが有効であることを見出し、以下の発明を提案するに至った。すなわち本発明は、以下の構成からなる。
酸変性ポリオレフィン（Ａ）、応力緩和剤（Ｂ）および粘着付与剤（Ｃ）を含有し、酸変性ポリオレフィン（A）１００重量部に対して、粘着付与剤を1質量部以上５０重量部未満含有する接着剤組成物。
前記応力緩和剤（Ｂ）が、スチレン成分を１０質量％以上含有したスチレン系エラストマーであることが好ましい。
前記応力緩和剤（Ｂ）は、デュロメータＡ硬さが３０以上のスチレン系エラストマーであることが好ましい。
前記酸変性ポリオレフィン（Ａ）の酸価は、２～５０ｍｇＫＯＨ／ｇであることが好ましい。
前記酸変性ポリオレフィン（Ａ）１００質量部に対して、応力緩和剤（Ｂ）の質量比が、５質量部以上３００質量部以下であることが好ましい。
さらに溶剤（D）を含む、前記いずれかに記載の接着剤組成物。
前記溶剤（D）が、脂環式炭化水素溶剤（D１）およびエステル系溶剤またはケトン系溶剤（D２）含むことが好ましい。
脂環式炭化水素溶剤（D１）とエステル系溶剤またはケトン系溶剤（D２）の質量比が、（D１）／（D２）＝９５／５～５０／５０である、前記に記載の接着剤組成物。
　ポリオレフィン樹脂基材とポリエステル基材との接着に用いられる前記いずれかに記載の接着剤組成物。
　ポリオレフィン樹脂基材と異種基材との接着に用いられる前記いずれかに記載の接着剤組成物。
　前記いずれかに記載の接着剤組成物によって接着されたポリオレフィン樹脂基材とポリエステルまたは異種基材の積層体。
　　本発明の接着剤組成物は、酸変性ポリオレフィン、応力緩和剤および粘着付与剤を含み、硬化剤を使用しない場合でもポリオレフィンのような非極性基材とポリエステルのような極性基材、金属などのその他異種基材の接着性に優れる。また、ドライラミネートにより塗工可能なため、設備費を削減でき、膜厚も薄くすることができる。さらに、ポリオレフィン基材の熱収縮影響が小さい９０℃以下のような低温で加熱接着した場合でも優れた接着性を発現する。
本発明の接着剤組成物は、ポリオレフィン基材のみならず、ポリエチレンテレフタレート（ＰＥＴ）、アクリロニトリル－ブタジエン－スチレン共重合体（ＡＢＳ）、ポリ塩化ビニル（ＰＶＣ）、アクリル樹脂、アルミニウム等の基材とも良好な密着性を示すため、マルチ基材用接着剤として有用である。
　また、本発明の接着剤組成物は硬化剤を使用しないため、接着後でも熱処理を行うことで基材から簡単に剥離することができる。
　以下、本発明の実施の形態について詳細に説明する。
＜酸変性ポリオレフィン（Ａ）＞
　本発明で用いる酸変性ポリオレフィン（Ａ）は限定的ではないが、ポリプロピレンにα，β－不飽和カルボン酸及びその酸無水物の少なくとも１種をグラフトすることにより得られるものが好ましい。　
　ポリプロピレンとしては、ホモポリプロピレンが特に好ましく使用できるが、プロピレン・α－オレフィン共重合体も使用できる。プロピレン・α－オレフィン共重合体は、プロピレンを主体としてこれにα－オレフィンを共重合したものである。α－オレフィンとしては、例えば、エチレン、１－ブテン、１－ヘプテン、１－オクテン、４－メチル－１－ペンテン、酢酸ビニルなどを１種又は数種用いることができる。これらのα－オレフィンの中では、エチレン、１－ブテンが好ましく、１－ブテンが最も好ましい。
　酸変性ポリオレフィン（Ａ）はオレフィン成分としてプロピレンを６０モル％以上含有することが好ましい。より好ましくは７０モル％以上であり、さらに好ましくは８０モル％以上である。まして好ましいのは９０モル％以上である。プロピレン含有量が多いほど、プロピレン基材との接着性および応力緩和剤との相溶性が向上する。
　プロピレンと１－ブテンのモル比の好ましい範囲としてはプロピレン／１－ブテン＝１００～６０／０～４０であり、より好ましくは９８～６５／２～３５、さらに好ましくは９０～７０／１０～３０である。プロピレンのモル比が６０％以上であることで、ポリオレフィン基材との優れた接着性を発現できる。また、１－ブテンのモル比が２％以上であれば有機溶剤への溶解性が増し、接着剤としての塗工性が向上する。
　オレフィン成分として、プロピレンと１－ブテン成分の合計量は６２モル％以上であることが好ましい。より好ましくは８０モル％以上であり、さらに好ましくは９０モル％以上であり、特に好ましくは９５モル％以上であり、１００モル％であっても差し支えない。プロピレンと１－ブテン成分の合計量が６２モル％以上であると、接着性および耐薬品性が特に良好である。
　α，β－不飽和カルボン酸及びその酸無水物の少なくとも１種としては、例えば、マレイン酸、イタコン酸、シトラコン酸及びこれらの酸無水物が挙げられる。これらの中でも酸無水物が好ましく、無水マレイン酸がより好ましい。具体的には、無水マレイン酸変性ポリプロピレン、無水マレイン酸変性プロピレン・エチレン共重合体、無水マレイン酸変性プロピレン・１－ブテン共重合体、無水マレイン酸変性プロピレン・エチレン・１－ブテン共重合体等が挙げられ、これら酸変性ポリオレフィンを１種類又は２種類以上を組み合わせて使用することができる。なかでも無水マレイン酸変性プロピレンが好ましい。
酸変性ポリオレフィン（Ａ）の酸価は、２～５０ｍｇＫＯＨ／ｇの範囲であることが好ましい。より好ましくは３～４０ｍｇＫＯＨ／ｇ、さらに好ましくは５～３０ｍｇＫＯＨ／ｇ、特に好ましくは５～１６ｍｇＫＯＨ／ｇの範囲である。酸価が２ｍｇＫＯＨ／ｇ以上では、接着力が良好に発揮される。一方、酸価が５０ｍｇＫＯＨ／ｇ以下では、応力緩和剤（Ｂ）との相溶性が良好な傾向を示す。
酸変性ポリオレフィン（Ａ）の融点（Ｔｍ）は、５０℃以上１００℃以下であることが好ましい。より好ましくは５５℃以上であり、さらに好ましくは６０℃以上である。また、より好ましくは9０℃以下であり、さらに好ましくは90℃未満であり、それ以上に好ましいのは８７℃以下、最も好ましくは8５℃以下である。５０℃以上では、結晶由来の凝集力が強くなり、接着性が良好である。一方、前記の値以下では、溶液安定性、流動性が良好で接着する際の操作性に優れる。
酸変性ポリオレフィン（Ａ）の結晶化度は、１２～４０％の範囲であることが好ましい。より好ましくは１５～３５の範囲であり、最も好ましくは２０～２８％の範囲である。前記の値以上であると、結晶由来の凝集力が強くなり、基材との接着性が優れる。一方、前記の値以下では、ゲル化しにくく、溶液安定性が良好である。
　変性ポリオレフィン（Ａ）の融解熱量は、２５～４０Ｊ/ｇの範囲であることが好ましい。より好ましくは２８～３８Ｊ/ｇの範囲であり、最も好ましくは３０～３６Ｊ/ｇの範囲である。前記の値以上であると、結晶由来の凝集力が強くなり、接着性が優れる。一方、前記の値未満では、ゲル化しにくく、溶液安定性が良好である。
酸変性ポリオレフィン（Ａ）の重量平均分子量（Ｍｗ）は、１０，０００～２００，０００の範囲であることが好ましい。より好ましくは２０，０００～１８０，０００の範囲であり、さらに好ましくは３０，０００～１６０，０００の範囲であり、特に好ましくは４０，０００～１４０，０００の範囲であり、最も好ましくは、５０，０００～１００，０００の範囲である。前記の値以上であると、凝集力が発揮され接着性が良好となる。一方、前記の値以下では、流動性が高くなり接着する際の操作性が容易である。
　酸変性ポリオレフィン（Ａ）の製造方法としては、特に限定されず、例えばラジカルグラフト反応（すなわち主鎖となるポリマーに対してラジカル種を生成し、そのラジカル種を重合開始点として不飽和カルボン酸および酸無水物をグラフト重合させる反応）、などが挙げられる。
　ラジカル発生剤としては、特に限定されないが、有機過酸化物を使用することが好ましい。有機過酸化物としては、特に限定されないが、ジ－ｔｅｒｔ－ブチルパーオキシフタレート、ｔｅｒｔ－ブチルヒドロパーオキサイド、ジクミルパーオキサイド、ベンゾイルパーオキサイド、ｔｅｒｔ－ブチルパーオキシベンゾエート、ｔｅｒｔ－ブチルパーオキシ－２－エチルヘキサノエート、ｔｅｒｔ－ブチルパーオキシピバレート、メチルエチルケトンパーオキサイド、ジ－ｔｅｒｔ－ブチルパーオキサイド、ラウロイルパーオキサイド等の過酸化物；アゾビスイソブチロニトリル、アゾビスイソプロピオニトリル等のアゾニトリル類等が挙げられる。
　これらの酸変性ポリオレフィン（Ａ）は、単独で用いてもよく、また２種類以上を組み合わせて用いてもよい。
＜応力緩和剤（Ｂ）＞
　本発明の接着剤組成物は応力緩和剤（Ｂ）を含有する。応力緩和剤を含有させることにより、接着剤を成膜した後の内部応力を軽減させ、基材との接着性を向上させることができる。
　本発明に用いる応力緩和剤（Ｂ）は、限定的ではないが、単量体としてスチレン成分を１０質量％以上含有することが好ましい。より好ましくは１２質量％以上６５質量%以下であり、さらに好ましくは１５質量％以上５０質量％以下、特に好ましくは１８質量％以上４５質量％以下、それ以上に好ましくは２０質量％以上３５質量％以下、最も好ましくは２０質量％以上３０質量％以下である。１０質量％以上であると酸変性ポリオレフィン（Ａ）との相溶性がほどよく、応力緩和効果が発現され、接着性が良好となる傾向がある。また、６５質量％以下では、酸変性ポリオレフィン（Ａ）との相溶性が著しく向上する。応力緩和剤（Ｂ）は、スチレン系エラストマーが好ましく、スチレン系熱可塑性エラストマーがより好ましい。
スチレン系熱可塑性エラストマーは特に限定されないが、スチレン-エチレン-ブチレン-スチレン樹脂、スチレン-エチレン-プロピレン樹脂が好ましい。他にも、スチレンエラストマー、スチレンブタジエン樹脂、スチレンエチレンプロピレンスチレン樹脂、スチレンイソプレンブタジエンスチレンブ樹脂、スチレンイソプレンスチレン樹脂などが挙げられる。スチレン系熱可塑性エラストマーは酸変性物であってもよい。
　本発明の応力緩和剤（Ｂ）としてはスチレン系エラストマーの他に、スチレン成分を含有するオレフィン系エラストマー、アルケン系エラストマー、塩化ビニル系エラストマー、ウレタン系エラストマー、アミド系エラストマーなども用いることができる。
　本発明に用いる応力緩和剤（Ｂ）のデュロメータＡ硬さは、３０以上であることが好ましい。より好ましくは３５以上９５以下であり、さらに好ましくは４０以上８５以下、特に好ましくは５０以上７５以下、最も好ましくは５６以上６９未満である。３０以上であると、応力緩和効果が大きくなりすぎることはなく良好に効果が発揮され、接着層が凝集破壊せず良好に接着される。デュロメータＡ硬さは、JIS K6253-3:2012に従って測定することができる。
　応力緩和剤（Ｂ）の密度は、０．８８～０．９９ｇ／ｃｍ３の範囲であることが好ましい。より好ましくは、０．８９～０．９１ｇ／ｃｍ３の範囲である。０．８８ｇ／ｃｍ３以上であると、酸変性ポリオレフィン（Ａ）との比重差が大きくなりすぎず、溶液安定性が良好な傾向である。また、０．９９ｇ／ｃｍ３以下では、酸変性ポリオレフィン（A）との比重差が大きくなりすぎず、溶液安定性が良好となる。
　応力緩和剤（Ｂ）の引張強さは、１～１７ＭＰaの範囲であることが好ましい。より好ましくは、３～１２ＭＰaの範囲である。前記の範囲内であることで、良好な接着性が発現する。
これらの応力緩和剤は、単独で用いてもよく、また２種類以上を組み合わせて用いてもよい。 
　本発明の接着剤組成物中の応力緩和剤（Ｂ）の含有量は、酸変性ポリオレフィン（Ａ）を１００質量部としたとき、（Ｂ）が５質量部以上であることが好ましい。より好ましくは１０質量部以上であり、さらに好ましくは２０質量部以上、特に好ましくは３０質量部以上、それ以上に好ましくは４５質量部以上であり，最も好ましくは６０質量部以上である。５質量部以上であると、ポリオレフィン基材との接着性が良好に発揮される。また、酸変性ポリオレフィン（Ａ）１００質量部としたとき、応力緩和剤（Ｂ）は３００質量部以下が好ましい。より好ましくは２００質量部以下、さらに好ましくは１００質量部以下、増して好ましくは８５質量部以下、それ以上に好ましくは８０質量部以下、最も好ましくは７０質量部以下である。また、３００質量部以下では、ポリオレフィン基材との接着性が特に良好である。
＜粘着付与剤（C）＞
　本発明の接着剤組成物は粘着付与剤（C）を含有する。粘着付与剤を含有させることにより、接着剤を成膜した後、表面の粘着性が維持でき、基材との接着性を向上させることができる。
本発明に用いる粘着付与剤（C）の含有量としては、酸変性ポリオレフィン（Ａ）１００重量部に対して1質量部以上５０質量部未満である。より好ましくは、２質量部以上４５質量部以下、さらに好ましくは３質量部以上４０質量部以下、特に好ましくは４以上３０質量部以下、それ以上に好ましくは５質量部以上２５質量部以下、最も好ましくは６質量部以上２０質量部以下である。また、１質量部以上であると、表面の接着性が優れ、接着性が良好に発揮される。一方、５０質量部未満であると、溶液粘度がほどよく、溶液安定性が良好となる。
　本発明に用いる粘着付与剤（C）の軟化点としては、８０℃以上であることが好ましい。より好ましくは８５℃以上であり、さらに好ましくは９０℃以上である。また、好ましくは１６０℃以下であり、さらに好ましくは１５０℃以下、特に好ましくは１４０℃以下、それ以上に好ましくは１３０℃以下であり，最も好ましくは１２０℃以下である。軟化点が８０℃以上であると常温での粘着付与剤が表面にブリードアウトしにくく滑らかな表面となり、接着性が良好である。また、１６０℃以下であると常温でのタック性が生じ、接着性が良好である。
本発明に用いる粘着付与剤（C）のとしては、種々のものがあるが、例えば、石油樹脂（脂肪族系、脂環族系、芳香族系等）、テルペン樹脂（α－ピネン、β-ピネン、リモネンなどの重合体）、芳香族炭化水素変性テルペン樹脂、ロジン系樹脂（ガムロジン、トール油ロジン、ウッドロジン、水添ロジン、不均化ロジン、重合ロジン、マレイン化ロジン、ロジンエステル等）、テルペンフェノール樹脂などが挙げられ、これらは単独あるいは２種以上をあわせて用いても良い。
＜溶剤（D）＞
　本発明の接着剤組成物は、溶剤（D）を含むことができる。溶剤（D）は酸変性ポリオレフィン（Ａ）、応力緩和剤（Ｂ）および粘着付与剤（C）を溶解または分散できるものであれば特に限定されないが、脂環式炭化水素溶剤（D1）、エステル系溶剤またはケトン系溶剤（D2）が好ましい。
　例えば、脂環式炭化水素溶剤（D1）としてはシクロヘキサン、メチルシクロヘキサン、エチルシクロヘキサン等が挙げられる。エステル系溶剤またはケトン系溶剤（D２）としては、酢酸エチル、酢酸プロピル、酢酸ブチル、メチルエチルケトン等が挙げられる。これらの中ではメチルシクロヘキサン、酢酸プロピルが好ましい。これらを単独で使用しても良いし、２種以上を任意に組み合わせて使用しても良い。
　本発明で使用される溶剤（D）は、脂環式炭化水素溶剤（D１）とエステル系溶剤またはケトン系溶剤（D２）を含む混合溶剤を用いることができる。脂環式炭化水素溶剤とエステル系溶剤またはケトン系溶剤の混合溶剤とすることで、接着剤組成物の溶解性を向上させることができる。 
　前記混合溶剤を用いる場合、脂環式炭化水素溶剤（D１）とエステル系溶剤またはケトン系溶剤（D２）の質量比は（D１）／（D２）＝９５／５～５０／５０であることが好ましい。より好ましくは９０／１０～６０／４０であり、特に好ましくは８０／２０～７０／３０の範囲である。前記の範囲より脂環式炭化水素（D１）が多いと、粘度が高く塗工ムラが発生し、接着性が低下する場合がある。前記の範囲の脂環式炭化水素（D１）であると、樹脂の溶解性が良好である。
　溶剤（D）は、酸変性ポリオレフィン（Ａ）１００質量部に対して、１０～２０００質量部の範囲で含むことができる。好ましくは２５質量部以上１５００質量部以下であり、より好ましくは５０質量部以上１０００質量部以下、さらに好ましくは１００質量部以上９００質量部以下、それ以上に好ましくは１００質量部以上８００質量部以下である。前記範囲内であると製造コスト、輸送コストの面から有利である。
　本発明にかかる接着剤組成物は、本発明の性能を損なわない範囲で、酸変性ポリオレフィン（Ａ）、応力緩和剤（Ｂ）および粘着付与剤（C）の他に、各種の可塑剤、硬化促進剤、難燃剤、顔料、ブロッキング防止剤等の添加剤を配合して使用することができる。
＜接着剤組成物＞
　本発明の接着剤組成物は、酸変性ポリオレフィン（Ａ）、応力緩和剤（Ｂ）および粘着付与剤（C）を含み、必要に応じて溶剤（D）を含有する。接着剤組成物の固形分１００質量部中、スチレンを０．１質量部以上含むことが好ましい。より好ましくは０．５質量部以上であり、さらに好ましくは１．５質量部以上、特に好ましくは３質量部以上、それ以上に好ましくは４．５質量部以上、最も好ましくは６質量部以上である。また、上限としては６５質量部以下が好ましく、より好ましくは５０質量部以下、さらに好ましくは３０質量部以下、特に好ましくは２５質量部以下、最も好ましくは２０質量部以下である。前記範囲内では酸変性ポリオレフィンとの相溶性および接着強度が良好な傾向にある。
　本発明の接着剤組成物は、接着剤組成物中における酸変性ポリオレフィン（Ａ）、応力緩和剤（Ｂ）および粘着付与剤（C）を合計５質量％以上含むことが好ましい。より好ましくは７質量％以上、さらに好ましくは１０質量％以上、特に好ましくは１３質量％以上である。また、４０質量％以下が好ましく、３５質量％以下がより好ましい。さらに好ましくは３０質量％以下であり、特に好ましくは２５質量％以下である。前記範囲内では、貯蔵安定性および接着性が良好であり、また、塗工性が良好な傾向にある。
　本発明の接着剤組成物は、硬化剤を実質的に含まなくてもよい。実質的に含まないとは、例えば酸変性ポリオレフィン１００質量部に対して１質量部以下であり、より好ましくは０．５質量部以下、さらに好ましくは０．３質量部以下、それ以上に好ましくは０．１質量部以下であり、０質量部でも差支えがないということである。硬化剤を実質的に含有しないことで、一度作製した基材／接着剤／基材の積層体であっても加熱等の処理により容易に剥がすことが可能となる。
　上記硬化剤は特に限定されず、一般的に公知のものを指す。例えば、エポキシ硬化剤や、イソシアネート硬化剤、オキサゾリン基またはカルボジイミド基を含有する化合物、シランカップリング剤などである。
＜積層体＞
　本発明の積層体は、ポリオレフィン樹脂基材と異種基材を本発明にかかる接着剤組成物で積層したものである。前記異種基材とは、ポリオレフィン基材１とは異なる基材のことである。例えば、ポリオレフィン基材１がポリプロピレンであれば、異種基材はポリプロピレン以外のポリエステルやアルミニウム箔、ポリ塩化ビニル基材などである。
上述した本発明の積層体は、例えば、バンパー、インストルメントパネル、トリム、ガーニッシュなどの自動車部品や新幹線の内装材等の乗り物用部品、テレビ、洗濯機槽、冷蔵庫部品、エアコン部品、掃除機部品などの家電機器部品、などの各種工業部品、携帯電話端末やノートパソコンなどのモバイル機器や通信機器、各種機器のタッチパネル、日用品に有用である。
　積層する方法としては、従来公知のラミネート製造技術を利用することができる。例えば、特に限定されないが、基材の表面に接着剤組成物をアプリケータやバーコータ等の適当な塗布手段を用いて塗布し、乾燥させる。乾燥後、基材表面に形成された接着剤組成物の層（接着剤層）が溶融状態にある間に、その塗布面にもう片方の基材を積層接着（ラミネート接着、ヒートシール接着）して積層体を得ることができる。ラミネート接着やヒートシール接着いずれの積層体作製方法であっても、十分な接着性を確保できる。
　前記接着剤組成物により形成される接着剤層の厚みは、特に限定されないが、異種基材がフィルムの場合、０．５～１５μｍにすることが好ましく、１～１２μｍにすることがより好ましく、２～１０μｍにすることがさらに好ましい。異種基材が成型品である場合、5～８0μmにすることが好ましく、10～６0μmにすることがさらに好ましい。
＜ポリオレフィン樹脂基材（フィルム）＞
　ポリオレフィン樹脂基材としては、従来から公知のポリオレフィン樹脂の中から適宜選択すればよい。例えば、特に限定されないが、ポリエチレン、ポリプロピレン、エチレン－プロピレン共重合体などを用いることができる。中でも、ポリプロピレンの無延伸フィルム（以下、ＣＰＰともいう。）の使用が好ましい。その厚さは、特に限定されないが、２０～１００μｍであることが好ましく、２５～９５μｍであることがより好ましく、３０～９０μｍであることがさらに好ましい。なお、ポリオレフィン樹脂基材には必要に応じて顔料や種々の添加物を配合してもよいし、表面処理を施してもよい。
＜ポリエステル樹脂基材（フィルム）＞
　ポリエステル樹脂基材としては、特に限定されない。ポリエステル樹脂基材としては、例えばポリエチレンテレフタレート（PET）、ポリブチレンテレフタレート（PBT）等が挙げられる。また、使用目的によっても異なるが、一般的には０．０１～１０ｍｍ、好ましくは０．０２～５ｍｍの厚みのシートの形で使用される。
　また、これらポリエステル樹脂基材の表面を予め表面処理を施しておいてもよいし、未処理のままでもよい。いずれも場合であっても同等の効果を発揮することができる。
＜その他異種基材＞
　異種基材としては、ABS樹脂、ポリ塩化ビニル、アクリル樹脂、Al箔等を用いることができる。特に限定されないが、市販の試験板を用いることができる。その厚さも特に限定されないが、１００μm～３mmであることが好ましく、さらに１～２．５ｍｍであることがより好ましい。また、これら異種基材の表面を予め表面処理を施しておいてもよいし、未処理のままでもよい。いずれも場合であっても同等の効果を発揮することができる。
　以下、実施例を挙げて本発明を更に詳細に説明する。但し、本発明は実施例に限定されない。
＜酸変性ポリオレフィン（Ａ）の製造例＞
製造例１
　１Ｌオートクレーブに、ポリプロピレン（Ｔｍ：８０℃、結晶化度＝2３％）１００質量部、トルエン１５０質量部及び無水マレイン酸８．５質量部、ジ－ｔｅｒｔ－ブチルパーオキサイド４質量部を加え、１４０℃まで昇温した後、更に１時間撹拌した（ここで、1時間「反応」したという）。その後、得られた反応液を１２５℃まで冷却後、予め４０℃に加温したメチルエチルケトン２１９質量部が入った容器に攪拌しながら注ぎ、４０℃まで冷却し、更に３０分間攪拌し、更に２５℃まで冷却することで樹脂を析出させた（ここで、反応液をメチルエチルケトンなどの溶剤に攪拌しながら注ぎ込み、冷却することで樹脂を析出させる操作を「再沈」という）。その後、当該樹脂を含有するスラリー液を遠心分離することで無水マレイン酸がグラフト重合した酸変性ポリプロピレンと（ポリ）無水マレイン酸および低分子量物とを分離した。
　更に、遠心分離して取り出した酸変性ポリプロピレンを、予め２５℃に保温した新たな２０００質量部のメチルエチルケトンが入った容器に攪拌しながら投入し、１時間攪拌を続けた。その後、スラリー液を遠心分離することで、更に酸変性ポリプロピレンと（ポリ）無水マレイン酸および低分子量物とを分離した。当該操作を２回繰り返すことで、精製した（ここで、遠心分離して取り出した酸変性ポリプロピレンをメチルエチルケトンに攪拌しながら投入し、再度遠心分離することで、精製を強化する操作を「リスラリー」とする）。
精製後、減圧下５０℃で５時間乾燥させることにより、酸変性ポリオレフィンである無水マレイン酸変性ポリプロピレン（Ａ－１、酸価１２ｍｇＫＯＨ／ｇ-resin、重量平均分子量６０，０００、Ｔｍ８０℃、結晶化度＝２５％）を得た。
製造例２
　製造例１で用いた無水マレイン酸の量を３．５質量部に変更した以外は製造例１と同様にすることにより、酸変性ポリオレフィンである無水マレイン酸変性ポリプロピレン（Ａ－２、酸価６ｍｇＫＯＨ／ｇ-resin、重量平均分子量７７，０００、Ｔｍ８０℃、結晶化度＝２５％）を得た。
製造例３
　製造例１で用いたポリプロピレン（Ｔｍ：８０℃）をプロピレン－ブテン共重合体（Ｔｍ：８３℃、プロピレン８０質量％、ブテン２０質量％）に変更した以外は製造例１と同様にすることにより、酸変性ポリオレフィンである無水マレイン酸変性プロピレン－ブテン共重合体（Ａ－３、酸価１２ｍｇＫＯＨ／ｇ-resin、重量平均分子量９０，０００、Ｔｍ８０℃、結晶化度＝36％）を得た。
製造例４
　製造例１で用いたポリプロピレン（Ｔｍ：８０℃）をプロピレン－ブテン共重合体（Ｔｍ：９８℃、プロピレン８５質量％、ブテン１５質量％）に変更した以外は製造例１と同様にすることにより、酸変性ポリオレフィンである無水マレイン酸変性プロピレン－ブテン共重合体（Ａ－４、酸価１７ｍｇＫＯＨ／ｇ-resin、重量平均分子量７５，０００、Ｔｍ９５℃、結晶化度＝４０％）を得た。
実施例１
　水冷還流凝縮器と撹拌機を備えた５００ｍｌの四つ口フラスコに、製造例１で得られた無水マレイン酸変性ポリプロピレン（Ａ－１）を５４質量部、応力緩和剤（Ｂ－１）を３６質量部、粘着付与剤（C-1）を１０質量部、シクロヘキサンを２８０質量部および酢酸n-プロピルを１２０質量部仕込み、撹拌しながら７０℃まで昇温し、撹拌を１時間続けた後、冷却することで接着剤組成物１を得た。この接着剤組成物１を用いて、下記の方法で積層体を作成した。
　ポリオレフィン樹脂基材とポリエステル樹脂基材との積層体の作製（ラミネート接着）ポリエステル樹脂基材にはＰＥＴフィルム（東洋紡社製、Ｅ５１０１、厚さ５０μｍ）を使用し、ポリオレフィン樹脂基材には無延伸ポリプロピレンフィルム（東洋紡社製パイレン（登録商標）フィルムＣＴ、厚さ４０μｍ）（以下、ＣＰＰともいう。）を使用した。
　得られた接着剤組成物をポリエステル樹脂基材にアプリケータを用いて乾燥後の接着剤層の膜厚が８μｍ程度になるように調整して塗布した。温風乾燥機を用いて塗布面を１００℃雰囲気で１分間乾燥させ、膜厚８μｍ程度の接着剤層が積層されたポリエステル樹脂基材を得た。前記接着剤層表面にポリオレフィン樹脂基材を重ね合わせ、テスター産業社製の小型卓上テストラミネーター（ＳＡ－１０１０－Ｓ）を用いて、ラミネート温度８０℃で、０．３ＭＰａ、１ｍ／分にて貼り合わせ、室温で、１日間養生することで積層体を得た。得られた積層体に対して、接着性を評価した。結果を表１に示す。
（実施例２～１２、比較例１～４）
　酸変性ポリオレフィン、応力緩和剤および粘着付与剤を表１に示すとおりに変更し、実施例１と同様な方法で接着剤組成物２～１６を作製した。得られた接着剤組成物２～１６を用いて実施例１と同様な方法で積層体を作製し、接着性評価を実施した。評価結果を表１に示す。
表１で用いた応力緩和剤（Ｂ）は以下のものである。
Ｂ－１：　旭化成社製　タフテック（登録商標）P１０８３（スチレン含量２０質量％、デュロメータＡ硬さ５６、スチレン-ブタジエン-ブチレン-スチレン共重合体、密度０．８９g/cm3、引張強さ９MPa）
Ｂ－２：　旭化成社製　タフテック（登録商標）H１０５２　（スチレン含量２０質量％、デュロメータＡ硬さ６７、スチレン-エチレン-ブチレン-スチレン共重合体、密度０．８９g/cm3、引張強さ１２MPa）
Ｂ－３：　旭化成社製　タフテック（登録商標）Ｐ１５００（スチレン含量３０質量％、デュロメータＡ硬さ６９、スチレン-ブタジエン-ブチレン-スチレン共重合体、密度０．９１g/cm3、引張強さ３MPa）
B－４：　旭化成社製　タフテック（登録商標）H１２２１（スチレン含量１２質量％、デュロメータＡ硬さ４２、スチレン-エチレン-ブチレン-スチレン共重合体、密度０．８９g/cm3、引張強さ１０MPa）
表１で用いた粘着付与剤（C）は以下のものである。
C－１：　荒川化学工業社製　アルコン（登録商標）P９０（軟化点９０℃）
C－２：　ヤスハラケミカル社製　YSレジン（登録商標）TO１２５　（軟化点１２５℃）
C－３：　ヤスハラケミカル社製　YSレジン（登録商標）PX１２５０　（軟化点１２５℃）
実施例１３
実施例１と同様の方法で接着剤組成物１を得た。この接着剤組成物１を用いて、下記の方法で積層体を作成した。
　ポリオレフィン樹脂基材とその他異種基材との積層体の作製（ヒートシール接着）
　ポリオレフィン樹脂基材には上記と同様の無延伸ポリプロピレンフィルムを使用した。得られた接着剤組成物をポリオレフィン樹脂基材にアプリケータを用いて乾燥後の接着剤層の膜厚が３0μｍ程度になるように調整して塗布した。温風乾燥機を用いて塗布面を１００℃雰囲気で５分間乾燥させ、膜厚３０μｍ程度の接着剤層が積層されたポリオレフィン樹脂基材を得た。前記接着剤層表面にポリプロピレン（PP）試験板（日本テストパネル社製、厚さ2mm）、ABS試験板（日本テストパネル社製、厚さ2mm）、ポリ塩化ビニル（PVC）試験板（日本テストパネル社製、厚さ2mm）、アクリル（PMMA）試験板（日本テストパネル社製、厚さ2mm）、ＰＥＴ試験板（日本テストパネル社製、厚さ2mm）、Al箔（住軽アルミ箔社製、８０７９－０、厚さ４０μｍ）を重ね合わせ、テスター産業社製のヒートシールテスター（TP－７０１－B）を用いて、ヒートシール温度９０℃（試験板側は５５℃）で、０．３ＭＰａ、１５ｓにて貼り合わせ、室温で、１日間養生することで積層体を得た。得られた積層体に対して、接着性を評価した。結果を表２に示す。
　上記のようにして得られた各酸変性ポリオレフィン、応力緩和剤、粘着付与剤、接着剤組成物および積層体に対して下記方法に基づいて分析測定および評価を行った。
＜スチレン成分の含有量の測定＞　
　応力緩和剤を重水素化クロロホルムに溶解し、その試料溶液のＨ－ＮＭＲスペクトルを観測幅１５ｐｐｍで測定した。またあらかじめ、３種の濃度のポリスチレン／重水素化クロロホルム溶液のＨ－ＮＭＲスペクトルのスチレンのピーク面積と濃度から検量線を求め、この検量線を用いて、試料溶液のスチレンのピーク面積からスチレンの含有量を算出した。 
＜酸価の測定＞
　本発明における酸価（ｍｇＫＯＨ／ｇ-ｒｅｓｉｎ）は、１ｇの酸変性ポリオレフィン（Ａ）を中和するのに必要とするＫＯＨ量のことであり、ＪＩＳ　Ｋ００７０（１９９２）の試験方法に準じて、測定した。具体的には、１００℃に温度調整したキシレン１００ｇに、酸変性ポリオレフィン１ｇを溶解させた後、同温度でフェノールフタレインを指示薬として、０．１ｍｏｌ／Ｌ水酸化カリウムエタノール溶液［商品名「０．１ｍｏｌ／Ｌエタノール性水酸化カリウム溶液」、和光純薬（株）製］で滴定を行った。この際、滴定に要した水酸化カリウム量をｍｇに換算して酸価（ｍｇＫＯＨ／ｇ）を算出した。
＜デュロメータＡ硬さの測定＞
　デュロメータＡ硬さは、JIS K6253-3:2012に従って測定した。具体的には平たんで堅固な面に試験片を置き、デュロメータの加圧板が試験片の表面に平行になるより，かつ，押針がゴムの表面に対して直角になるようにデュロメータを保持し，加圧板を試験片に接触させる。押針先端は，試験片の端から12.0 mm以上離れた位置で測定した。
＜重量平均分子量（Ｍｗ）の測定＞
　本発明における重量平均分子量は、日本ウォーターズ社製ゲルパーミエーションクロマトグラフＡｌｌｉａｎｃｅ ｅ２６９５（以下、ＧＰＣ、標準物質：ポリスチレン樹脂、移動相：テトラヒドロフラン、カラム：Shodex KF-806 + KF-803、カラム温度：40℃、流速：１．０ｍｌ/分、検出器：フォトダイオードアレイ検出器（波長254nm = 紫外線））によって測定した。
＜融点、融解熱量の測定＞
　本発明における融点、融解熱量は示差走査熱量計（以下、ＤＳＣ、ティー・エー・インスツルメント・ジャパン製、Ｑ－２０００）を用いて、－５０℃で５分間保持後、１０℃／分の速度で昇温融解し、２００℃で融解したら２００℃で２分間保持し、１０℃／分の速度で冷却樹脂化して、冷却樹脂化すると再度１０℃／分の速度で昇温融解した際の融解ピークのトップ温度および面積から測定した。
＜結晶化度の測定＞
テフロン（登録商標）シートの表面に接着剤組成物をアプリケータを用いて塗布し、乾燥させた後、剥離させ、フィルム状の接着組成物を得た。その後、以下の条件でXRD測定を行った。測定機器：理学電機製X線回折装置RINT2500 
ターゲット：Ｃｕ
管電圧：４０ｋＶ
管電流：２００ｍＡ
コリメータ：1mmφ
スリット：縦2°、横1/2°
受光部：Niフィルター、シンチレーションカウンター
走査範囲：2θ/θ
得られたXRD回折ピークから結晶化度を算出した。
＜接着性の評価＞
　積層体を１５ｍｍの短冊状に切断し、１８０°剥離試験により接着性を以下の基準により評価した。Ｔ型剥離試験はＡＳＴＭ－Ｄ１８７６－６１の試験法に準拠し、オリエンテックコーポレーション社製のテンシロンＲＴＭ－１００を用いて、２５℃環境下で、引張速度５０ｍｍ／分における剥離強度を測定した。異種基材／ポリオレフィン樹脂基材間の剥離強度（Ｎ／１５ｍｍ）は３回の試験値の平均値とした。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
　本発明の接着剤組成物は、酸変性ポリオレフィン、応力緩和剤および粘着付与剤を含み、硬化剤不使用の場合でもポリオレフィンのような非極性基材と極性基材、金属などのその他異種基材の接着性に優れる。また、ドライラミネートにより塗工可能なため、設備費を削減でき、膜厚も薄くすることができる。さらに、ポリオレフィン基材の熱収縮影響が小さい９０℃以下のような低温での加熱接着でも優れた接着性を発現する。そのため、本発明の接着剤組成物は、様々な種類の基材同士を貼り合わせる接着剤として幅広く利用し得るものである。 

Claims (11)

  1. 酸変性ポリオレフィン（Ａ）、応力緩和剤（Ｂ）および粘着付与剤（Ｃ）を含有し、酸変性ポリオレフィン（A）１００重量部に対して、粘着付与剤（C）を1質量部以上５０質量部未満含有する接着剤組成物。
  2. 前記応力緩和剤（Ｂ）が、スチレン成分を1０質量％以上含有したスチレン系エラストマーである、請求項１に記載の接着剤組成物。
  3. 前記応力緩和剤（Ｂ）のデュロメータA硬さが３０以上のスチレン系エラストマーである、請求項１または２に記載の接着剤組成物。
  4. 前記酸変性ポリオレフィン（Ａ）の酸価が２～５０ｍｇＫＯＨ／ｇである、請求項１～3いずれかに記載の接着剤組成物。
  5. 前記酸変性ポリオレフィン（Ａ）１００質量部に対して、前記応力緩和剤（Ｂ）の質量比が、５質量部以上３００質量部以下である、請求項１～４いずれかに記載の接着剤組成物。
  6. さらに溶剤（D）を含む、請求項１～５いずれかに記載の接着剤組成物。
  7. 前記溶剤（D）が、脂環式炭化水素溶剤（D１）およびエステル系溶剤またはケトン系溶剤（D２）を含む、請求項６に記載の接着剤組成物。
  8. 脂環式炭化水素溶剤（D１）とエステル系溶剤またはケトン系溶剤（D２）の質量比が、（D１）／（D２）＝９５／５～５０／５０である、請求項７に記載の接着剤組成物。
  9. 　ポリオレフィン樹脂基材１と基材１とは異なる基材２との接着に用いられる請求項１～８いずれかに記載の接着剤組成物。
  10. 　基材２がポリエステル基材である請求項９に記載の接着剤組成物。
  11. 　請求項１～８のいずれかに記載の接着剤組成物によって接着されたポリオレフィン樹脂基材１と基材１とは異なる基材２の積層体。
PCT/JP2019/038749 2018-10-10 2019-10-01 ポリオレフィン系接着剤組成物 WO2020075577A1 (ja)