WO2019216109A1 - Composition de caoutchouc vulcanisé, bande de roulement et pneumatique - Google Patents

Composition de caoutchouc vulcanisé, bande de roulement et pneumatique Download PDF

Info

Publication number
WO2019216109A1
WO2019216109A1 PCT/JP2019/015827 JP2019015827W WO2019216109A1 WO 2019216109 A1 WO2019216109 A1 WO 2019216109A1 JP 2019015827 W JP2019015827 W JP 2019015827W WO 2019216109 A1 WO2019216109 A1 WO 2019216109A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
rubber composition
vulcanized rubber
component
unit
Prior art date
Application number
PCT/JP2019/015827
Other languages
English (en)
Japanese (ja)
Inventor
靖宏 庄田
茂樹 大石
Original Assignee
株式会社ブリヂストン
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社ブリヂストン filed Critical 株式会社ブリヂストン
Priority to JP2020518209A priority Critical patent/JPWO2019216109A1/ja
Publication of WO2019216109A1 publication Critical patent/WO2019216109A1/fr

Abstract

L'invention a pour objectif de fournir une composition de caoutchouc excellente en termes de résistance à l'usure inégale et d'aptitude au façonnage.　Afin d'atteindre cet objectif, la composition de caoutchouc vulcanisée selon l'invention se caractérise en ce que le composant caoutchouc comprend un copolymère à multiples composants contenant une unité diène conjugué, une unité oléfine non conjuguée, et une unité vinylaromatique et en ce que la rugosité superficielle de cette composition de caoutchouc vulcanisé est comprise entre 5 et 100μm.
PCT/JP2019/015827 2018-05-08 2019-04-11 Composition de caoutchouc vulcanisé, bande de roulement et pneumatique WO2019216109A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2020518209A JPWO2019216109A1 (ja) 2018-05-08 2019-04-11 加硫ゴム組成物、タイヤトレッド及びタイヤ

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2018089774 2018-05-08
JP2018-089774 2018-05-08

Publications (1)

Publication Number Publication Date
WO2019216109A1 true WO2019216109A1 (fr) 2019-11-14

Family

ID=68466964

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2019/015827 WO2019216109A1 (fr) 2018-05-08 2019-04-11 Composition de caoutchouc vulcanisé, bande de roulement et pneumatique

Country Status (2)

Country Link
JP (1) JPWO2019216109A1 (fr)
WO (1) WO2019216109A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2021106413A1 (fr) * 2019-11-28 2021-06-03 株式会社ブリヂストン Complexe caoutchouc-métal, pneu et article en caoutchouc
WO2022050175A1 (fr) * 2020-09-01 2022-03-10 株式会社ブリヂストン Composition de résine et corps moulé
WO2022254751A1 (fr) * 2021-05-31 2022-12-08 株式会社ブリヂストン Composition de caoutchouc, et pneumatique
WO2022254749A1 (fr) * 2021-05-31 2022-12-08 株式会社ブリヂストン Composition de caoutchouc vulcanisée et pneumatique
WO2022254750A1 (fr) * 2021-05-31 2022-12-08 株式会社ブリヂストン Composition de caoutchouc, et pneumatique

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH09291121A (ja) * 1996-04-26 1997-11-11 Asahi Chem Ind Co Ltd ブテン・ブタジエン共重合体、その製造方法及び加硫ゴム
JPH1180269A (ja) * 1997-07-18 1999-03-26 Mitsui Chem Inc 不飽和性共重合体、その製造方法および該共重合体系組成物
JP2001514275A (ja) * 1997-08-27 2001-09-11 ザ ダウ ケミカル カンパニー 熱硬化インターポリマー類および発泡体
JP2010515614A (ja) * 2007-01-12 2010-05-13 チャン、ハイロン 耐パンク、防弾、及び漏れ防止安全タイヤ及びその調製方法、並びにその方法で利用される漏れ防止かつ密閉架橋高分子材料
WO2017002966A1 (fr) * 2015-07-02 2017-01-05 横浜ゴム株式会社 Composition de caoutchouc pour bande de roulement
JP2017101181A (ja) * 2015-12-03 2017-06-08 株式会社ブリヂストン 多元共重合体の製造方法及び多元共重合体
JP2017128649A (ja) * 2016-01-19 2017-07-27 株式会社ブリヂストン ゴム組成物の製造方法、ゴム組成物及びタイヤ
JP2018053177A (ja) * 2016-09-30 2018-04-05 住友ゴム工業株式会社 スタッドレスタイヤ用キャップトレッドゴム組成物

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH09291121A (ja) * 1996-04-26 1997-11-11 Asahi Chem Ind Co Ltd ブテン・ブタジエン共重合体、その製造方法及び加硫ゴム
JPH1180269A (ja) * 1997-07-18 1999-03-26 Mitsui Chem Inc 不飽和性共重合体、その製造方法および該共重合体系組成物
JP2001514275A (ja) * 1997-08-27 2001-09-11 ザ ダウ ケミカル カンパニー 熱硬化インターポリマー類および発泡体
JP2010515614A (ja) * 2007-01-12 2010-05-13 チャン、ハイロン 耐パンク、防弾、及び漏れ防止安全タイヤ及びその調製方法、並びにその方法で利用される漏れ防止かつ密閉架橋高分子材料
WO2017002966A1 (fr) * 2015-07-02 2017-01-05 横浜ゴム株式会社 Composition de caoutchouc pour bande de roulement
JP2017101181A (ja) * 2015-12-03 2017-06-08 株式会社ブリヂストン 多元共重合体の製造方法及び多元共重合体
JP2017128649A (ja) * 2016-01-19 2017-07-27 株式会社ブリヂストン ゴム組成物の製造方法、ゴム組成物及びタイヤ
JP2018053177A (ja) * 2016-09-30 2018-04-05 住友ゴム工業株式会社 スタッドレスタイヤ用キャップトレッドゴム組成物

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2021106413A1 (fr) * 2019-11-28 2021-06-03 株式会社ブリヂストン Complexe caoutchouc-métal, pneu et article en caoutchouc
JP7386258B2 (ja) 2019-11-28 2023-11-24 株式会社ブリヂストン ゴム－金属複合体、タイヤ、及びゴム物品
WO2022050175A1 (fr) * 2020-09-01 2022-03-10 株式会社ブリヂストン Composition de résine et corps moulé
WO2022254751A1 (fr) * 2021-05-31 2022-12-08 株式会社ブリヂストン Composition de caoutchouc, et pneumatique
WO2022254749A1 (fr) * 2021-05-31 2022-12-08 株式会社ブリヂストン Composition de caoutchouc vulcanisée et pneumatique
WO2022254750A1 (fr) * 2021-05-31 2022-12-08 株式会社ブリヂストン Composition de caoutchouc, et pneumatique

Also Published As

Publication number Publication date
JPWO2019216109A1 (ja) 2021-05-13

Similar Documents

Publication Publication Date Title
WO2019216109A1 (fr) Composition de caoutchouc vulcanisé, bande de roulement et pneumatique
JP7217744B2 (ja) 加硫ゴム組成物、タイヤトレッド及びタイヤ
JP6637716B2 (ja) 多元共重合体、ゴム組成物、架橋ゴム組成物及びゴム物品
JP5769577B2 (ja) クローラ用ゴム組成物及びそれを用いたゴムクローラ
JP2017075286A (ja) 多元共重合体、ゴム組成物、架橋ゴム組成物、及びゴム物品
JP5973735B2 (ja) タイヤ用ゴム組成物及び該タイヤ用ゴム組成物を具えたタイヤ
JP5735886B2 (ja) ゴム支承被覆用ゴム組成物及びそれを用いたゴム支承被覆用ゴム
WO2019216100A1 (fr) Composition de caoutchouc, caoutchouc mousse, bande de roulement de pneu et pneu
WO2017064860A1 (fr) Copolymère à composants multiples, composition de caoutchouc, composition de caoutchouc réticulé, et article en caoutchouc
JP5840481B2 (ja) 空気入りタイヤ
WO2020235285A1 (fr) Copolymère à plusieurs constituants, composition de caoutchouc, composition de résine, pneu et produit en résine
JP2019214680A (ja) ゴム組成物、タイヤ及びゴム物品
JP5973737B2 (ja) タイヤ用ゴム組成物、タイヤ用架橋ゴム組成物、及びタイヤ
JP2012179807A (ja) ゴム積層体
JP5856494B2 (ja) 空気入りタイヤ
JP2016128552A (ja) ゴム組成物及びそれを用いたタイヤ
JP2013159631A (ja) ゴム組成物、タイヤトレッド用ゴム組成物、架橋ゴム、及びタイヤ
JP5973736B2 (ja) タイヤ用ゴム組成物、タイヤ用架橋ゴム組成物、及びタイヤ
WO2018230410A1 (fr) Composition de caoutchouc, et pneumatique
WO2017064858A1 (fr) Copolymère à composants multiples, composition de caoutchouc, composition de caoutchouc réticulé, et article en caoutchouc
JP2012197420A (ja) ゴム組成物の製造方法
JP2019214679A (ja) ゴム組成物、タイヤ用ゴム組成物、タイヤ及びゴム物品
JP5798941B2 (ja) ゴム組成物及び空気入りタイヤ
JP2020114918A (ja) 多元共重合体、ゴム組成物、架橋ゴム組成物及びゴム物品
JP2012197422A (ja) ゴム組成物及びタイヤ

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19799102

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2020518209

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase