WO2019179917A1 - Composition - Google Patents

Composition Download PDF

Info

Publication number
WO2019179917A1
WO2019179917A1 PCT/EP2019/056663 EP2019056663W WO2019179917A1 WO 2019179917 A1 WO2019179917 A1 WO 2019179917A1 EP 2019056663 W EP2019056663 W EP 2019056663W WO 2019179917 A1 WO2019179917 A1 WO 2019179917A1
Authority
WO
WIPO (PCT)
Prior art keywords
composition
monocarboxylic acid
acid
zinc
alkyl
Prior art date
Application number
PCT/EP2019/056663
Other languages
English (en)
Inventor
Marit Dahling
Original Assignee
Jotun A/S
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jotun A/S filed Critical Jotun A/S
Priority to JP2020550814A priority Critical patent/JP7372933B2/ja
Priority to CN201980013991.8A priority patent/CN111770970A/zh
Priority to KR1020207027418A priority patent/KR20200130701A/ko
Publication of WO2019179917A1 publication Critical patent/WO2019179917A1/fr

Abstract

La présente invention concerne une composition de revêtement antisalissure comprenant : (i) un copolymère d'ester d'acétal acrylique; et l'un ou l'autre (ii) un sel de zinc d'un acide monocarboxylique ou (ii) un acide monocarboxylique; et (iii) un composé de zinc qui réagit avec l'acide monocarboxylique pour former un sel de zinc d'un acide monocarboxylique.
PCT/EP2019/056663 2018-03-20 2019-03-18 Composition WO2019179917A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
JP2020550814A JP7372933B2 (ja) 2018-03-20 2019-03-18 組成物
CN201980013991.8A CN111770970A (zh) 2018-03-20 2019-03-18 组合物
KR1020207027418A KR20200130701A (ko) 2018-03-20 2019-03-18 조성물

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GB1804434.7 2018-03-20
GBGB1804434.7A GB201804434D0 (en) 2018-03-20 2018-03-20 Composition

Publications (1)

Publication Number Publication Date
WO2019179917A1 true WO2019179917A1 (fr) 2019-09-26

Family

ID=62017968

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2019/056663 WO2019179917A1 (fr) 2018-03-20 2019-03-18 Composition

Country Status (5)

Country Link
JP (1) JP7372933B2 (fr)
KR (1) KR20200130701A (fr)
CN (1) CN111770970A (fr)
GB (1) GB201804434D0 (fr)
WO (1) WO2019179917A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB202107159D0 (en) 2021-03-23 2021-06-30 Jotun As Monitoring a vessel
WO2021180588A2 (fr) 2020-03-09 2021-09-16 Jotun A/S Robot de nettoyage de coque
WO2021191388A1 (fr) 2020-03-27 2021-09-30 Jotun A/S Composition de revêtement antisalissure
WO2022200430A1 (fr) 2021-03-23 2022-09-29 Jotun A/S Surveillance de la propreté d'une surface immergée d'un objet stationnaire

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102014001222A1 (de) * 2014-01-29 2015-07-30 Clariant lnternational Ltd Halogenfreie feste Flammschutzmittelmischung und ihre Verwendung

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3885146T2 (de) * 1987-04-28 1994-03-24 Fina Research Selbstpolierende Anwuchsverhindernde Anstrichfarben.
US5008146A (en) * 1988-11-04 1991-04-16 Cape Cod Research, Inc. Zinc-carbon antifouling coating
JPH11116858A (ja) * 1997-10-17 1999-04-27 Nof Corp 塗料組成物
JP2001302989A (ja) * 2000-02-15 2001-10-31 Dainippon Toryo Co Ltd 防汚塗料組成物
JP4361239B2 (ja) * 2002-03-06 2009-11-11 中国塗料株式会社 防汚塗料組成物、該組成物からなる塗膜、該塗膜で被覆された基材、および防汚方法
JP2011026357A (ja) * 2007-11-21 2011-02-10 Nitto Kasei Co Ltd 防汚塗料組成物、該組成物の製造方法、該組成物を用いて形成される防汚塗膜、該塗膜を表面に有する塗装物、及び該塗膜を形成する防汚処理方法
CN103881576A (zh) * 2013-10-29 2014-06-25 东南大学 一种防污油漆
JP6488159B2 (ja) 2015-03-09 2019-03-20 Fdk株式会社 組電池の直列接続用部品および組電池
US20180051179A1 (en) * 2015-04-16 2018-02-22 Mitsubishi Chemical Corporation Antifouling coating composition

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102014001222A1 (de) * 2014-01-29 2015-07-30 Clariant lnternational Ltd Halogenfreie feste Flammschutzmittelmischung und ihre Verwendung

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2021180588A2 (fr) 2020-03-09 2021-09-16 Jotun A/S Robot de nettoyage de coque
WO2021191388A1 (fr) 2020-03-27 2021-09-30 Jotun A/S Composition de revêtement antisalissure
GB202107159D0 (en) 2021-03-23 2021-06-30 Jotun As Monitoring a vessel
WO2022200427A1 (fr) 2021-03-23 2022-09-29 Jotun A/S Surveillance d'un navire
WO2022200430A1 (fr) 2021-03-23 2022-09-29 Jotun A/S Surveillance de la propreté d'une surface immergée d'un objet stationnaire

Also Published As

Publication number Publication date
CN111770970A (zh) 2020-10-13
JP2021518475A (ja) 2021-08-02
KR20200130701A (ko) 2020-11-19
JP7372933B2 (ja) 2023-11-01
GB201804434D0 (en) 2018-05-02

Similar Documents

Publication Publication Date Title
CN111655799B (zh) 防污组合物
JP7332593B2 (ja) 防汚組成物
JP7145175B2 (ja) 組成物
JP7372933B2 (ja) 組成物
JP7427391B2 (ja) 防汚組成物
EP2935288B1 (fr) Copolymère d'ester de silyl
JP7386603B2 (ja) 防汚組成物
GB2560158A (en) Composition
EP3710539B1 (fr) Composition antisalissures
JP7085573B2 (ja) 組成物
WO2021191388A1 (fr) Composition de revêtement antisalissure

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19711596

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2020550814

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 20207027418

Country of ref document: KR

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 19711596

Country of ref document: EP

Kind code of ref document: A1