WO2019163640A1 - ゲルベアルコールを製造する方法 - Google Patents
ゲルベアルコールを製造する方法 Download PDFInfo
- Publication number
- WO2019163640A1 WO2019163640A1 PCT/JP2019/005363 JP2019005363W WO2019163640A1 WO 2019163640 A1 WO2019163640 A1 WO 2019163640A1 JP 2019005363 W JP2019005363 W JP 2019005363W WO 2019163640 A1 WO2019163640 A1 WO 2019163640A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- alcohol
- transition metal
- reaction
- solvent
- nanoparticles
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C29/00—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring
- C07C29/32—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring increasing the number of carbon atoms by reactions without formation of -OH groups
- C07C29/34—Preparation of compounds having hydroxy or O-metal groups bound to a carbon atom not belonging to a six-membered aromatic ring increasing the number of carbon atoms by reactions without formation of -OH groups by condensation involving hydroxy groups or the mineral ester groups derived therefrom, e.g. Guerbet reaction
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C31/00—Saturated compounds having hydroxy or O-metal groups bound to acyclic carbon atoms
- C07C31/02—Monohydroxylic acyclic alcohols
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07B—GENERAL METHODS OF ORGANIC CHEMISTRY; APPARATUS THEREFOR
- C07B61/00—Other general methods
Definitions
- the present invention relates to a method for producing Gerve alcohol.
- Gelbe alcohol is a ⁇ -branched alcohol produced by a Gelbe reaction that dimerizes an alcohol having a primary hydroxyl group or a secondary hydroxyl group, and is used industrially, for example, as a raw material for industrial and cosmetic purposes.
- Patent Document 1 discloses a reaction in which a metal catalyst supported on a carrier such as carbon is used as a heterogeneous hydrogenation catalyst as a gel reaction for obtaining a gel alcohol.
- Heterogeneous metal catalysts are economically advantageous over homogeneous metal catalysts in that they can be recovered after the reaction is complete and easily reused.
- an object of one aspect of the present invention is to provide a method that makes it possible to obtain Gerve alcohol by a reaction at a lower temperature while using a metal catalyst that can be easily recovered after the reaction.
- one or two or more alcohols having 4 to 16 carbon atoms having a primary or secondary hydroxyl group are dimerized in the presence of transition metal nanoparticles and a base to obtain a gel gel.
- a method for producing Gerve alcohol comprising the step of producing alcohol is provided.
- the transition metal nanoparticles are particles generated by heating a transition metal compound in a solvent containing a coordinating organic solvent.
- the transition metal nanoparticles used in this method can be easily recovered after completion of the reaction by ordinary methods such as distillation of the product and filtration. Further, according to this method, the dimerization of alcohol at a lower temperature can proceed to obtain Gerve alcohol.
- gel alcohol can be obtained by reaction at a lower temperature while using a catalyst that can be easily recovered after the reaction.
- one or more alcohols having a primary or secondary hydroxyl group are dimerized by a Gerve reaction in the presence of transition metal nanoparticles and a base, Including the step of producing Gerve alcohol. Dimerization here means that the same kind of alcohol molecules or two different kinds of alcohol molecules react to produce Gerve alcohol. This may be dimerized using only one alcohol as starting material.
- the starting alcohol may be any compound that has a primary or secondary hydroxyl group and can be dimerized to produce Gerve alcohol, and may be a linear alkyl alcohol.
- the carbon number of the starting alcohol is usually 4 to 16, but may be 8 or more. It may be.
- the starting alcohol can be, for example, a compound represented by the following formula (1).
- R 1 , R 2 and R 3 each independently represent a linear, branched or cyclic saturated or unsaturated aliphatic group, and the number of carbon atoms of R 1 , R 2 and R 3 Is 2 to 14 in total.
- R 1 may be a linear, branched or cyclic saturated or unsaturated aliphatic group having 2 to 12 carbon atoms
- R 2 and R 3 may be a hydrogen atom.
- the aliphatic group herein may be a linear alkyl group.
- the starting alcohol is oxidized to form a carbonyl compound, and the dimer having a carbonyl group and a carbon-carbon double bond by aldol condensation of two molecules of the carbonyl compound. It is presumed to include the production of a body and the addition of hydrogen to the dimer to produce Gerve alcohol. Transition metal nanoparticles are thought to be primarily responsible for the oxidation of alcohols and the addition of hydrogen to dimers. The base is believed to be primarily involved in aldol condensation.
- the starting alcohol may be a linear alkyl alcohol, and specific examples thereof include 1-butanol, 1-hexanol, 1-octanol, 1-decanol, 1-dodecanol, 1-tetradecanol, 1- Hexadecanol and two combinations selected from these are mentioned.
- the transition metal nanoparticles used as the metal catalyst are particles having a nano-size particle size and are considered to be metal cluster particles.
- the average particle diameter of the transition metal nanoparticles is, for example, 0.5 to 4 nm, and may be 2 nm or less.
- the particle diameter of the transition metal nanoparticles means the maximum width of the transition metal nanoparticles observed in, for example, a transmission electron microscope (TEM) image.
- the transition metal nanoparticles can be particles generated by heating the transition metal compound in a solvent containing a coordinating organic solvent. It is considered that a coordinating organic solvent is disposed on the surface of the transition metal nanoparticle generated by this method, thereby protecting the transition metal nanoparticle.
- the transition metal nanoparticles can be synthesized with reference to, for example, a method described in JP2011-12097A.
- the transition metal compound used to obtain the transition metal nanoparticles can be, for example, a transition metal halide, sulfate, or nitrate.
- the transition metal may be at least one selected from the group consisting of ruthenium, iridium, palladium, rhodium, and copper, and may be ruthenium or iridium in particular.
- Transition metal nanoparticles containing ruthenium or iridium can be obtained by heating the ruthenium compound or iridium compound in a solvent containing a coordinating organic solvent.
- the valence of the transition metal contained in the transition metal compound is not particularly limited.
- the ruthenium compound used to obtain ruthenium nanoparticles may contain trivalent ruthenium (Ru (III)), tetravalent ruthenium (Ru (IV)), or both.
- the coordinating organic solvent used for obtaining the transition metal nanoparticles is an organic solvent capable of coordinating with the transition metal.
- the coordinating organic solvent is selected from, for example, an amide solvent, an amine solvent, an alcohol solvent, an ether solvent, a ketone solvent, an ester solvent, a nitrile solvent, a nitro solvent, a sulfoxide solvent, or these. It can be a combination of two or more.
- amide solvents include N, N-dimethylformamide (DMF), N, N-dimethylacetamide (DMA), 1,3-dimethyl-2-imidazolidinone (DMI), and N-methyl-2- Examples thereof include carboxylic acid amides such as pyrrolidone (NMP) and phosphoric acid amides such as hexamethylphosphoric triamide (HMPA).
- carboxylic acid amides such as pyrrolidone (NMP) and phosphoric acid amides such as hexamethylphosphoric triamide (HMPA).
- the amine solvent include triethylamine, pyridine and ethanolamine.
- alcohol solvents include isopropanol and propylene glycol.
- ether solvents include diethyl ether, diisopropyl ether, dioxane, and tetrahydrofuran (THF).
- Examples of the ketone solvent include acetone and 2-butanone.
- Examples of the ester solvent include ethyl acetate and methyl acetate.
- An example of a nitrile solvent is acetonitrile.
- An example of a nitro solvent is nitromethane.
- An example of the sulfoxide solvent is dimethyl sulfoxide.
- the coordinating organic solvent may be an amide solvent, particularly N, N-dimethylformamide.
- transition metal nanoparticles are formed in a solvent containing a coordinating organic solvent
- the transition metal nanoparticles protected with the coordinating organic solvent are taken out from the obtained dispersion, and this is used as a catalyst for the Guerbe reaction.
- the dispersion may be added as it is, or if necessary, after being concentrated into the system for the Gerve reaction.
- the base used for the Gerbe reaction may contain an alkali metal or alkaline earth metal hydroxide, alkoxide or hydride.
- bases include potassium tert-butoxide, sodium ethoxide, sodium methoxide, potassium hydroxide, and sodium hydroxide.
- the gel reaction for dimerizing alcohol can be performed in a solvent-free reaction mixture containing alcohol, transition metal nanoparticles and base, or in a reaction solution containing a solvent.
- the Gerve reaction in a solvent-free reaction mixture tends to produce the desired Gerve alcohol with higher yield and selectivity.
- the solventless reaction mixture may contain a trace amount of solvent.
- the content of the solvent based on the mass of the reaction mixture may be 3% by mass or less, or 1% by mass or less.
- the solvent can be, for example, an alcohol solvent that does not dimerize such as t-butanol or isopropanol, or an ether solvent such as tetrahydrofuran.
- the content of the solvent in the reaction solution may be 0 to 200% by volume with respect to the volume of the starting alcohol.
- the amount of transition metal nanoparticles used in the Gerbe reaction may be such that the ratio of ruthenium atoms to the total amount of starting alcohol is 0.01 to 1 mol%.
- the amount of the base may be 0.1 to 50 mol% with respect to the total amount of the starting alcohol.
- the reaction temperature (the temperature of the reaction mixture or reaction solution) of the Gelbe reaction for dimerizing alcohol is low, a relatively inexpensive heat source such as steam can be used, which is economically advantageous. In addition, there is a tendency that by-products are not easily generated. Therefore, the reaction temperature may be 190 ° C. or lower, 160 ° C. or lower, 150 ° C. or lower, or 140 ° C. or lower. According to the method according to the present embodiment, the Gerve reaction can be efficiently advanced even at such a low temperature. When the reaction temperature is 190 ° C. or lower, the reaction can efficiently proceed while suppressing thermal decomposition of the transition metal nanoparticles. The reaction temperature may be 40 ° C. or higher. In the gel reaction process, the reaction temperature may be changed.
- the gel reaction process may include a relatively low temperature first stage and a relatively high temperature second stage. This tends to further improve the yield of gel alcohol.
- the reaction temperature in the first stage may be higher than the temperature at which the starting alcohol melts or dissolves.
- the reaction temperature of the first stage may be 40 ° C. or more and less than 100 ° C.
- the reaction temperature of the second stage may be 100 ° C. or more and 190 ° C. or less.
- the total amount of starting alcohol may be mixed with the transition metal nanoparticles and the base at a time, or the alcohol may be mixed with the transition metal nanoparticles and the base a plurality of times (for example, twice).
- the upper limit of the number of times alcohol is introduced is not particularly limited, but may be, for example, 5 times or less, 4 times or less, or 3 times or less.
- the yield of gel alcohol tends to be further improved.
- the second and subsequent alcohols may be introduced into the reaction mixture or reaction solution.
- the reaction mixture or reaction solution into which the first alcohol is introduced is stirred at a low temperature (for example, 40 ° C. or more and less than 100 ° C.), and the reaction mixture or reaction solution into which the second or later alcohol is introduced is heated to a higher temperature (for example, you may stir at 100 degreeC or more and 190 degrees C or less.
- the amount of alcohol introduced at the first time may be smaller than the amount of alcohol introduced after the second time.
- the gel reaction for dimerizing alcohol may be performed in an atmospheric pressure atmosphere. According to the method according to the present embodiment, the gel reaction can be efficiently advanced without requiring pressurization.
- the reaction time of the Gerbe reaction may be adjusted within a range in which the reaction sufficiently proceeds, and may be, for example, 16 hours or longer, or 30 hours or longer, or 72 hours or shorter, or 48 hours or shorter. As described above, when the gel reaction process includes the first stage having a relatively low temperature and the second stage having a relatively high temperature, the reaction time of the second stage may be within these ranges.
- Gerve alcohol can be purified by a usual method if necessary.
- the transition metal nanoparticles can be taken out of the reaction mixture containing the reaction mixture or the solvent after the reaction is completed, and used again for the Gerube reaction.
- the alcohol of the starting material may be further added to the reaction mixture or reaction solution, and the Gerve reaction may be performed again.
- a dispersion containing iridium nanoparticles was obtained by the same procedure as above except that iridium (III) chloride hydrate was used instead of ruthenium (III) chloride hydrate.
- the reaction solution was diluted with diethyl ether, and dodecane as an internal standard was added to prepare a sample solution.
- This sample solution was analyzed by gas chromatography. Based on the peak area ratio in the obtained chromatogram, the consumption rate of the starting material 1-dodecanol and the resulting gelve alcohol (2) with respect to 1-dodecanol (1) Yield was calculated. Further, the ratio (selectivity) of 1-dodecanol to the entire product including by-products was determined based on the ratio of the peak area of the chromatogram.
- Table 1 shows the analysis results. It was confirmed that by the reaction in the presence of the transition metal nanoparticles and the base, the gel reaction proceeds sufficiently even at a relatively low temperature of 130 ° C. or 150 ° C., and gel alcohol is obtained. In the table, “nd” indicates that no peak was detected.
- Table 2 shows the analysis results. Even when any base was used, it was confirmed that the Gelbe reaction proceeded sufficiently at 130 ° C. In particular, potassium compounds tended to provide high yield and selectivity.
- ⁇ Examination 3 Diluting solvent> 1 mL of a dispersion containing ruthenium nanoparticles was placed in a Schlenk tube, and DMF was distilled off by an evaporator. 0.2 mmol of potassium tert-butoxide (tBuOK) was placed in a Schlenk tube in which ruthenium nanoparticles protected by DMF remained, and the atmosphere in the Schlenk tube was replaced with argon. A Schlenk tube was charged with 2 mmol of 1-dodecanol and t-butanol (0.5 mL) or toluene (0.2 mL) as a solvent. While stirring the reaction solution, the Schlenk tube was heated at 130 ° C. for 24 hours with an oil bath. After cooling, dodecane as an internal standard was added to the reaction solution to prepare a sample solution. The sample solution was analyzed by gas chromatography to determine the starting material consumption rate, product yield and selectivity.
- tBuOK potassium tert-butoxide
- Table 3 shows the analysis results together with the results of the solvent-free reaction in Study 1. Even in the reaction in the reaction solution to which the solvent was added, it was confirmed that the Gelbe reaction proceeded at a low temperature of 130 ° C., although the yield was slightly lower than the reaction without solvent.
- Synthesis test 4-2 The reaction was carried out in the same manner as in Synthesis Test 4-1, except that the amount of the dispersion containing ruthenium nanoparticles was changed to 75 mL, and the yield of the produced gerbealcohol relative to 1-dodecanol was calculated.
- Synthesis test 4-3 75 mL of the same dispersion containing ruthenium nanoparticles and DMF as in Synthesis Test 4-1 was placed in a four-necked flask, and DMF was distilled off under reduced pressure while heating to 120 ° C. To a four-necked flask in which ruthenium nanoparticles protected by DMF remain, 27.1 g of the first 1-dodecanol and 4.13 g of potassium hydroxide (flakes, purity 95%) were placed. The atmosphere was replaced with nitrogen. The reaction mixture in the flask was stirred for 3 hours while heating to 70-80 ° C.
- Test Examples 4-4 to 4-8 In the same manner as in Test Example 4-3, except that the type of alcohol and the amount of alcohol added in the second time were changed as shown in Table 4, gel alcohol was produced by adding alcohol in two portions. I let you. The yield of the resulting Gerbe alcohol relative to the starting alcohol was determined by GC analysis.
- Test Examples 4-9 and 4-10 Gelbacoal was produced in the same manner as in Test Example 4-7 or 4-8, except that the temperature of the reaction mixture after the second alcohol addition was changed from 150 ° C. to 160 ° C. The yield of the resulting gerbealcohol relative to 1-tetradecanol or 1-hexadecanol was determined by GC analysis.
- Table 4 shows the results. From a comparison between the synthesis test 4-1 and the results of the above-described Study 2, it was observed that the reaction mixture was stirred at a relatively low temperature and then heated to a high temperature to improve the yield of gel alcohol. . In addition, it was also confirmed that by introducing alcohol into the reaction mixture in two portions, gel alcohol was produced in a higher yield even when the amount of ruthenium nanoparticles was small.
- Synthesis test 5-1 75 mL of the same dispersion containing ruthenium nanoparticles and DMF as in Synthesis Test 4-1 was placed in a four-necked flask, and DMF was distilled off under reduced pressure while heating to 120 ° C. To a four-necked flask in which ruthenium nanoparticles protected by DMF remain, 27.1 g of the first 1-decanol and 8.26 g of potassium hydroxide (flakes, purity of 95%) were placed. The atmosphere was replaced with nitrogen. The reaction mixture in the flask was stirred for 3 hours while heating to 70-80 ° C.
- the gel reaction similar to 1 was performed, and the yield of gel alcohol was determined by GC analysis.
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
- Low-Molecular Organic Synthesis Reactions Using Catalysts (AREA)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2019538707A JP6632049B1 (ja) | 2018-02-20 | 2019-02-14 | ゲルベアルコールを製造する方法 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2018028012 | 2018-02-20 | ||
JP2018-028012 | 2018-02-20 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2019163640A1 true WO2019163640A1 (ja) | 2019-08-29 |
Family
ID=67687196
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2019/005363 WO2019163640A1 (ja) | 2018-02-20 | 2019-02-14 | ゲルベアルコールを製造する方法 |
Country Status (3)
Country | Link |
---|---|
JP (1) | JP6632049B1 (zh) |
TW (1) | TW201936556A (zh) |
WO (1) | WO2019163640A1 (zh) |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH09227424A (ja) * | 1996-02-28 | 1997-09-02 | Kao Corp | 分枝二量化アルコールの製造方法 |
JP2009233845A (ja) * | 2008-03-03 | 2009-10-15 | Tohoku Univ | ソルボサーマル法を用いたナノ粒子合成法 |
JP2013510105A (ja) * | 2009-11-06 | 2013-03-21 | コグニス・アイピー・マネージメント・ゲゼルシャフト・ミット・ベシュレンクテル・ハフツング | ゲルベアルコールの製造方法 |
JP2018021011A (ja) * | 2016-07-21 | 2018-02-08 | 花王株式会社 | ゲルベアルコールの製造方法 |
-
2019
- 2019-02-14 JP JP2019538707A patent/JP6632049B1/ja active Active
- 2019-02-14 WO PCT/JP2019/005363 patent/WO2019163640A1/ja active Application Filing
- 2019-02-19 TW TW108105371A patent/TW201936556A/zh unknown
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH09227424A (ja) * | 1996-02-28 | 1997-09-02 | Kao Corp | 分枝二量化アルコールの製造方法 |
JP2009233845A (ja) * | 2008-03-03 | 2009-10-15 | Tohoku Univ | ソルボサーマル法を用いたナノ粒子合成法 |
JP2013510105A (ja) * | 2009-11-06 | 2013-03-21 | コグニス・アイピー・マネージメント・ゲゼルシャフト・ミット・ベシュレンクテル・ハフツング | ゲルベアルコールの製造方法 |
JP2018021011A (ja) * | 2016-07-21 | 2018-02-08 | 花王株式会社 | ゲルベアルコールの製造方法 |
Non-Patent Citations (2)
Title |
---|
HERNANDEZ, WILLINTON Y: "One-pot preparation of Ni-Cu nanoparticles supported on y -A1203 as selective and stable catalyst for the Guerbet reaction of 1-octanol", CATALYSIS COMMUNICATIONS, vol. 98, 2017, pages 94 - 97, XP085045041, doi:10.1016/j.catcom.2017.05.005 * |
PANCHENKO, VALENTINA N. ET AL.: "Solid Base Assisted n-Pentanol Coupling over VIII Group Metals: Elucidation of the Guerbet Reaction Mechanism by DRIFTS", INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH, vol. 56, 2017, pages 13310 - 13321, XP055632745 * |
Also Published As
Publication number | Publication date |
---|---|
JP6632049B1 (ja) | 2020-01-15 |
TW201936556A (zh) | 2019-09-16 |
JPWO2019163640A1 (ja) | 2020-04-09 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
Wu et al. | AlCl3-catalyzed oxidation of alcohol | |
Liu et al. | Synthesis of dimethylformamide from CO 2, H 2 and dimethylamine over Cu/ZnO | |
JP6101636B2 (ja) | バナジウム錯体を用いたファルネサールの製造方法 | |
Jiang et al. | Iron‐Catalyzed Aerobic Oxidation of Aldehydes: Single Component Catalyst and Mechanistic Studies | |
CN109134172B (zh) | 一种配体调控的醇供氢铱催化选择性合成z-和e-烯烃方法 | |
Ke et al. | Alcohol promoted N-methylation of anilines with CO 2/H 2 over a cobalt catalyst under mild conditions | |
Kharat et al. | Green and chemoselective oxidation of alcohols with hydrogen peroxide: A comparative study on Co (II) and Co (III) activity toward oxidation of alcohols | |
JP6632049B1 (ja) | ゲルベアルコールを製造する方法 | |
EP3546441B1 (en) | Method for preparing acrylic acid and methyl acrylate | |
US9315435B2 (en) | Method for producing hydroxyphenylcyclohexanol compound | |
Kanomata et al. | Biomimetic Oxidation of Aldehyde with NAD+ Models: Glycolysis‐Type Hydrogen Transfer in an NAD+/NADH Model System | |
JP2007520510A (ja) | メチルヘプテノンの製造方法 | |
CN114890867B (zh) | 一种制备1,3-丁二醇的方法 | |
JP2016537420A (ja) | エステルの合成方法および該合成のための触媒 | |
JP2004300131A (ja) | エステル類の水素化によりアルコール類を製造する方法 | |
Reyes-Rios et al. | Alkylation of amines with alcohols catalyzed by palladium nanoparticles | |
US6790976B2 (en) | Process for producing aliphatic tricarbonitriles | |
JP4426633B2 (ja) | 2−アルキル−2−シクロアルケン−1−オンの製造方法 | |
Liu et al. | Selective hydrogenation of trans-4-phenyl-3-butene-2-one to unsaturated alcohol over Ru/γ-Al2O3 modified by PPh3 and diamines | |
TW201130785A (en) | Process for preparing 2,2-difluoroethylamine by hydrogenating 1,1-difluoro-2-nitroethane | |
CN107029759B (zh) | 三氯化钌在催化硝基苯类化合物与醇类化合物反应制备亚胺中的应用 | |
JP6002572B2 (ja) | ビス(アセチルアセトナト)ジオキソモリブデン(vi)を用いたファルネサールの製造方法 | |
JP6014486B2 (ja) | ビス(アセチルアセトナト)オキソバナジウム(iv)を用いたファルネサールの製造方法 | |
JP4849547B2 (ja) | モンモリロナイト層間固定化サブナノオーダーパラジウム触媒 | |
KR101874740B1 (ko) | 산소 함유 탄소 화합물의 제조 방법 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
ENP | Entry into the national phase |
Ref document number: 2019538707 Country of ref document: JP Kind code of ref document: A |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 19758094 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 19758094 Country of ref document: EP Kind code of ref document: A1 |