WO2019150445A1 - フィルム状接着剤及びその製造方法、並びに半導体装置及びその製造方法 - Google Patents

フィルム状接着剤及びその製造方法、並びに半導体装置及びその製造方法 Download PDF

Info

Publication number
WO2019150445A1
WO2019150445A1 PCT/JP2018/003022 JP2018003022W WO2019150445A1 WO 2019150445 A1 WO2019150445 A1 WO 2019150445A1 JP 2018003022 W JP2018003022 W JP 2018003022W WO 2019150445 A1 WO2019150445 A1 WO 2019150445A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
adhesive
semiconductor element
wire
mass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2018/003022
Other languages
English (en)
French (fr)
Inventor
大輔 舛野
祐樹 中村
慎太郎 橋本
健太 菊地
智陽 山崎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Resonac Corp
Original Assignee
Hitachi Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hitachi Chemical Co Ltd filed Critical Hitachi Chemical Co Ltd
Priority to PCT/JP2018/003022 priority Critical patent/WO2019150445A1/ja
Priority to KR1020207022892A priority patent/KR102491831B1/ko
Priority to SG11202007034UA priority patent/SG11202007034UA/en
Priority to JP2019568438A priority patent/JP7028264B2/ja
Priority to CN201880087615.9A priority patent/CN111656499A/zh
Priority to TW108101899A priority patent/TW201936828A/zh
Publication of WO2019150445A1 publication Critical patent/WO2019150445A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

基板上に第１のワイヤを介して第１の半導体素子がワイヤボンディング接続されると共に、第１の半導体素子上に、第２の半導体素子が圧着されてなる半導体装置において、第２の半導体素子を圧着すると共に、少なくとも第１のワイヤの少なくとも一部を埋め込むために用いられるフィルム状接着剤であって、第１の接着フィルムと、第１の接着フィルム上に積層された第２の接着フィルムと、を備え、フィルム状接着剤の溶剤含有率がフィルム状接着剤全量を基準として１．５質量％以下であり、フィルム状接着剤の８０℃におけるずり粘度が５０００Ｐａ・ｓ以下である、フィルム状接着剤が開示される。

Description

フィルム状接着剤及びその製造方法、並びに半導体装置及びその製造方法
　本発明は、フィルム状接着剤及びその製造方法、並びに半導体装置及びその製造方法に関する。
　従来、半導体チップと半導体チップ搭載用の支持部材との接合には、主に銀ペーストが使用されている。しかし、近年の半導体チップの小型化及び集積化に伴い、使用される支持部材にも小型化及び細密化が要求されるようになってきている。その一方で、銀ペーストを用いる場合では、ペーストのはみ出し又は半導体チップの傾きに起因するワイヤボンディング時における不具合の発生、膜厚制御の困難性、ボイド発生等の問題が生じる場合がある。
　そのため、近年、半導体チップと支持部材とを接合するためのフィルム状接着剤が使用されている（例えば、特許文献１参照）。ダイシングテープとダイシングテープ上に積層されたフィルム状接着剤とを備える接着シートを用いる場合、半導体ウェハの裏面にフィルム状接着剤を貼り付け、ダイシングによって半導体ウェハを個片化することによって、フィルム状接着剤付き半導体チップを得ることができる。得られたフィルム状接着剤付き半導体チップは、フィルム状接着剤を介して支持部材に貼り付け、熱圧着により接合することができる。
特開２００７－０５３２４０号公報
　しかしながら、半導体チップのサイズが小さくなるにつれて、熱圧着時に単位面積当たりにかかる力が大きくなり、フィルム状接着剤が半導体チップからはみ出す、ブリードという現象が発生する場合がある。
　また、フィルム状接着剤をワイヤ埋め込み型フィルム状接着剤であるＦＯＷ（Ｆｉｌｍ　Ｏｖｅｒ　Ｗｉｒｅ）又は半導体チップ埋め込み型フィルム状接着剤であるＦＯＤ（Ｆｉｌｍ　Ｏｖｅｒ　Ｄｉｅ）として用いる場合は、埋め込み性を向上させる観点から、熱圧着時に高い流動性が求められる。そのため、ブリードの発生頻度及び量がさらに増大する傾向にある。場合によっては、ブリードが半導体チップ上面にまで生じることがあり、これによって、電気不良又はワイヤボンディング不良につながるおそれがある。
　本発明は、このような実情に鑑みてなされたものであり、熱圧着時に良好な埋め込み性を有しつつ、ブリードを抑制することが可能なフィルム状接着剤を提供することを主な目的とする。
　本発明者らが鋭意検討したところ、接着フィルムを積層したフィルム状接着剤を用い、さらにフィルム状接着剤の溶剤含有率及びずり粘度を調整することによって、上記課題が解決されることを見出し、本発明を完成するに至った。
　本発明の一側面は、基板上に第１のワイヤを介して第１の半導体素子がワイヤボンディング接続されると共に、第１の半導体素子上に、第２の半導体素子が圧着されてなる半導体装置において、第２の半導体素子を圧着すると共に第１のワイヤの少なくとも一部を埋め込むために用いられるフィルム状接着剤であって、第１の接着フィルムと、第１の接着フィルム上に積層された第２の接着フィルムと、を備え、フィルム状接着剤の溶剤含有率がフィルム状接着剤全量を基準として１．５質量％以下であり、フィルム状接着剤の８０℃におけるずり粘度が５０００Ｐａ・ｓ以下である、フィルム状接着剤を提供する。このようなフィルム状接着剤によれば、熱圧着時に良好な埋め込み性を有しつつ、ブリードを抑制することが可能となる。
　フィルム状接着剤の厚さは、３～１５０μｍであってよい。フィルム状接着剤の８０℃における貯蔵弾性率は、１０ＭＰａ以下であってよい。
　別の側面において、本発明は、上述のフィルム状接着剤の製造方法であって、溶剤を含有する第１の接着剤組成物のワニスを基材上に塗布し、塗布された第１の接着剤組成物のワニスを５０～１５０℃で加熱乾燥し、溶剤含有率が第１の接着フィルム全量を基準として１．５質量％以下である第１の接着フィルムを作製する工程と、溶剤を含有する第２の接着剤組成物のワニスを基材上に塗布し、塗布された第２の接着剤組成物のワニスを５０～１５０℃で加熱乾燥し、溶剤含有率が第２の接着フィルム全量を基準として１．５質量％以下である第２の接着フィルムを作製する工程と、第１の接着フィルムと第２の接着フィルムとを貼り合わせる工程と、を備える、フィルム状接着剤の製造方法を提供する。
　別の側面において、本発明は、基板上に第１のワイヤを介して第１の半導体素子がワイヤボンディング接続されると共に、第１の半導体素子上に、第２の半導体素子が上述のフィルム状接着剤を介して圧着されることで、第１のワイヤの少なくとも一部がフィルム状接着剤に埋め込まれてなる、半導体装置を提供する。なお、半導体装置は、第１のワイヤの少なくとも一部がフィルム状接着剤に埋め込まれてなるワイヤ埋込型の半導体装置であっても、第１のワイヤ及び第１の半導体チップが接着フィルムに埋め込まれてなるチップ埋込型の半導体装置であってもよい。
　別の側面において、本発明は、基板上に第１のワイヤを介して第１の半導体素子を電気的に接続するワイヤボンディング工程と、第２の半導体素子の片面に、上述のフィルム状接着剤を貼付するラミネート工程と、フィルム状接着剤が貼付された第２の半導体素子を、フィルム状接着剤を介して圧着することで、第１のワイヤの少なくとも一部をフィルム状接着剤に埋め込むダイボンド工程と、を備える半導体装置の製造方法を提供する。
　本発明によれば、熱圧着時に良好な埋め込み性を有しつつ、ブリードを抑制することが可能なフィルム状接着剤が提供される。また、本発明によれば、このようなフィルム状接着剤の製造方法、並びにこのようなフィルム状接着剤を用いた半導体装置及びその製造方法が提供される。
一実施形態に係るフィルム状接着剤を示す模式断面図である。 一実施形態に係る接着シートを示す模式断面図である。 他の実施形態に係る接着シートを示す模式断面図である。 一実施形態に係る半導体装置を示す模式断面図である。 一実施形態に係る半導体装置の製造方法の一連の工程を示す模式断面図である。 一実施形態に係る半導体装置の製造方法の一連の工程を示す模式断面図である。 一実施形態に係る半導体装置の製造方法の一連の工程を示す模式断面図である。 一実施形態に係る半導体装置の製造方法の一連の工程を示す模式断面図である。 一実施形態に係る半導体装置の製造方法の一連の工程を示す模式断面図である。
　以下、図面を適宜参照しながら、本発明の実施形態について説明する。ただし、本発明は以下の実施形態に限定されるものではない。
　本明細書において、（メタ）アクリル酸はアクリル酸又はそれに対応するメタクリル酸を意味する。（メタ）アクリロイル基等の他の類似表現についても同様である。
［フィルム状接着剤］
　図１は、一実施形態に係るフィルム状接着剤を示す模式断面図である。フィルム状接着剤１０は、第１の接着フィルム２と第１の接着フィルム２上に積層された第２の接着フィルム４とを備える。第１の接着フィルム２及び第２の接着フィルム４は、いずれも熱硬化性であり、半硬化（Ｂステージ）状態を経て、硬化処理後に完全硬化物（Ｃステージ）状態となり得る第１の接着剤組成物及び第２の接着剤組成物をフィルム状に成形して作製することができる。フィルム状接着剤１０は、得られた第１の接着フィルム２と第２の接着フィルム４とをラミネートすることによって作製することができる。
　フィルム状接着剤１０を構成する第１の接着フィルム２及び第２の接着フィルム４は、熱硬化性樹脂（以下、単に「（ａ）成分」という場合がある。）と、高分子量成分（以下、単に「（ｂ）成分」という場合がある。）と、無機フィラー（以下、単に「（ｃ）成分」という場合がある。）と、を含有することが好ましい。第１の接着フィルム２及び第２の接着フィルム４は、カップリング剤（以下、単に「（ｄ）成分」という場合がある。）と、硬化促進剤（以下、単に「（ｅ）成分」という場合がある。）と、をさらに含有していてもよい。第１の接着フィルム２及び第２の接着フィルム４は、第１の接着フィルム２及び第２の接着フィルム４を形成する際に用いられる溶剤が残存していてもよい。フィルム状接着剤１０（第１の接着フィルム２及び第２の接着フィルム４）の溶剤含有率は、フィルム状接着剤全量を基準として１．５質量％以下である。第１の接着フィルム２及び第２の接着フィルム４は互いに同一のフィルムであっても異なるフィルムであってもよいが、互いに同一のフィルムであることが好ましい。
＜（ａ）熱硬化性樹脂＞
　（ａ）成分は、接着性の観点から、エポキシ樹脂（以下、単に「（ａ１）成分」という場合がある。）及びエポキシ樹脂の硬化剤となり得るフェノール樹脂（以下、単に「（ａ２）成分」という場合がある。）を含むことが好ましい。
　（ａ１）成分は、分子内にエポキシ基を有するものであれば、特に制限なく用いることができる。（ａ１）成分としては、例えば、ビスフェノールＡ型エポキシ樹脂、ビスフェノールＦ型エポキシ樹脂、ビスフェノールＳ型エポキシ樹脂、フェノールノボラック型エポキシ樹脂、クレゾールノボラック型エポキシ樹脂、ビスフェノールＡノボラック型エポキシ樹脂、ビスフェノールＦノボラック型エポキシ樹脂、ジシクロペンタジエン骨格含有エポキシ樹脂、スチルベン型エポキシ樹脂、トリアジン骨格含有エポキシ樹脂、フルオレン骨格含有エポキシ樹脂、トリフェノールフェノールメタン型エポキシ樹脂、ビフェニル型エポキシ樹脂、キシリレン型エポキシ樹脂、ビフェニルアラルキル型エポキシ樹脂、ナフタレン型エポキシ樹脂、多官能フェノール類、アントラセン等の多環芳香族類のジグリシジルエーテル化合物などが挙げられる。これらは、１種を単独で又は２種以上を組み合わせて用いてもよい。これらの中でも、（ａ１）成分は、耐熱性の観点から、クレゾールノボラック型エポキシ樹脂、ビスフェノールＦ型エポキシ樹脂、又はビスフェノールＡ型エポキシ樹脂であってもよい。
　（ａ１）成分のエポキシ当量は、９０～３００ｇ／ｅｑ、１１０～２９０ｇ／ｅｑ、又は１３０～２８０ｇ／ｅｑであってよい。（ａ１）成分のエポキシ当量がこのような範囲にあると、フィルム状接着剤のバルク強度を維持しつつ、流動性を確保することができる傾向にある。
　（ａ１）成分の含有量は、（ａ）成分、（ｂ）成分、及び（ｃ）成分の総質量１００質量部に対して、５～５０質量部、１０～４０質量部、又は２０～３０質量部であってよい。（ａ１）成分の含有量が５質量部以上であると、フィルム状接着剤の埋め込み性がより良好となる傾向にある。（ａ１）成分の含有量が５０質量部以下であると、ブリードの発生をより抑制できる傾向にある。
　（ａ２）成分は、分子内にフェノール性水酸基を有するものであれば特に制限なく用いることができる。（ａ２）成分としては、例えば、フェノール、クレゾール、レゾルシン、カテコール、ビスフェノールＡ、ビスフェノールＦ、フェニルフェノール、アミノフェノール等のフェノール類及び／又はα－ナフトール、β－ナフトール、ジヒドロキシナフタレン等のナフトール類とホルムアルデヒド等のアルデヒド基を有する化合物とを酸性触媒下で縮合又は共縮合させて得られるノボラック型フェノール樹脂、アリル化ビスフェノールＡ、アリル化ビスフェノールＦ、アリル化ナフタレンジオール、フェノールノボラック、フェノール等のフェノール類及び／又はナフトール類とジメトキシパラキシレン又はビス（メトキシメチル）ビフェニルから合成されるフェノールアラルキル樹脂、ナフトールアラルキル樹脂などが挙げられる。これらは、１種を単独で又は２種以上を組み合わせて用いてもよい。これらの中でも、（ａ２）成分は、吸湿性及び耐熱性の観点から、フェノールアラルキル樹脂、ナフトールアラルキル樹脂、又はノボラック型フェノール樹脂であってもよい。
　（ａ２）成分の水酸基当量は、８０～２５０ｇ／ｅｑ、９０～２００ｇ／ｅｑ、又は１００～１８０ｇ／ｅｑであってよい。（ａ２）成分の水酸基当量がこのような範囲にあると、フィルム状接着剤の流動性を保ちつつ、接着力をより高く維持することができる傾向にある。
　（ａ２）成分の軟化点は、５０～１４０℃、５５～１２０℃、又は６０～１００℃であってよい。
　（ａ２）成分の含有量は、（ａ）成分、（ｂ）成分、及び（ｃ）成分の総質量１００質量部に対して、５～５０質量部、１０～４０質量部、又は２０～３０質量部であってよい。（ａ２）成分の含有量が５質量部以上であると、より良好な硬化性が得られる傾向にある。（ａ２）成分の含有量が５０質量部以下であると、フィルム状接着剤の埋め込み性がより良好になる傾向にある。
　（ａ１）成分のエポキシ当量と（ａ２）成分の水酸基当量との比（（ａ１）成分のエポキシ当量／（ａ２）成分の水酸基当量）は、硬化性の観点から、０．３０／０．７０～０．７０／０．３０、０．３５／０．６５～０．６５／０．３５、０．４０／０．６０～０．６０／０．４０、又は０．４５／０．５５～０．５５／０．４５であってよい。当該当量比が０．３０／０．７０以上であると、より充分な硬化性が得られる傾向にある。当該当量比が０．７０／０．３０以下であると、粘度が高くなり過ぎることを防ぐことができ、より充分な流動性を得ることができる。
＜（ｂ）高分子量成分＞
　（ｂ）成分は、ガラス転移温度（Ｔｇ）が５０℃以下であるものが好ましい。
　（ｂ）成分としては、例えば、アクリル樹脂、ポリエステル樹脂、ポリアミド樹脂、ポリイミド樹脂、シリコーン樹脂、ブタジエン樹脂、アクリロニトリル樹脂及びこれらの変性体等が挙げられる。
　（ｂ）成分は、流動性の観点から、アクリル樹脂を含んでいてもよい。ここで、アクリル樹脂とは、（メタ）アクリル酸エステルに由来する構成単位を含むポリマーを意味する。アクリル樹脂は、構成単位として、エポキシ基、アルコール性又はフェノール性水酸基、カルボキシル基等の架橋性官能基を有する（メタ）アクリル酸エステルに由来する構成単位を含むポリマーであることが好ましい。また、アクリル樹脂は、（メタ）アクリル酸エステルとアクリルニトリルとの共重合体等のアクリルゴムであってもよい。
　アクリル樹脂のガラス転移温度（Ｔｇ）は、－５０～５０℃又は－３０～３０℃であってよい。アクリル樹脂のＴｇが－５０℃以上であると、接着剤組成物の柔軟性が高くなり過ぎることを防ぐことができる傾向にある。これにより、ウェハダイシング時にフィルム状接着剤を切断し易くなり、バリの発生を防ぐことが可能となる。アクリル樹脂のＴｇが５０℃以下であると、接着剤組成物の柔軟性の低下を抑えることができる傾向にある。これにより、フィルム状接着剤をウェハに貼り付ける際に、ボイドを充分に埋め込み易くなる傾向にある。また、ウェハの密着性の低下によるダイシング時のチッピングを防ぐことが可能となる。ここで、ガラス転移温度（Ｔｇ）は、ＤＳＣ（熱示差走査熱量計）（例えば、株式会社リガク製「Ｔｈｅｒｍｏ　Ｐｌｕｓ　２」）を用いて測定した値を意味する。
　アクリル樹脂の重量平均分子量（Ｍｗ）は、１０万～３００万又は５０万～２００万であってよい。アクリル樹脂のＭｗがこのような範囲にあると、フィルム形成性、フィルム状における強度、可撓性、タック性等を適切に制御することができると共に、リフロー性に優れ、埋め込み性を向上することができる。ここで、Ｍｗは、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）で測定し、標準ポリスチレンによる検量線を用いて換算した値を意味する。
　アクリル樹脂の市販品としては、例えば、ＳＧ－７０Ｌ、ＳＧ－７０８－６、ＷＳ－０２３　ＥＫ３０、ＳＧ－２８０　ＥＫ２３、ＨＴＲ－８６０Ｐ－３ＣＳＰ、ＨＴＲ－８６０Ｐ－３ＣＳＰ－３ＤＢ（いずれもナガセケムテックス株式会社製）が挙げられる。
　（ｂ）成分の含有量は、（ａ）成分、（ｂ）成分、及び（ｃ）成分の総質量１００質量部に対して、５～７０質量部、１０～５０質量部、又は１５～３０質量部であってよい。（ｂ）成分の含有量が５質量部以上であると、成形時の流動性の制御及び高温での取り扱い性をより一層良好にすることができる。（ｂ）成分の含有量が７０質量部以下であると、埋め込み性をより一層良好にすることができる。
＜（ｃ）無機フィラー＞
　（ｃ）成分としては、例えば、例えば、水酸化アルミニウム、水酸化マグネシウム、炭酸カルシウム、炭酸マグネシウム、ケイ酸カルシウム、ケイ酸マグネシウム、酸化カルシウム、酸化マグネシウム、酸化アルミニウム、窒化アルミニウム、ホウ酸アルミウィスカ、窒化ホウ素、シリカ等が挙げられる。これらは、１種を単独で又は２種以上を組み合わせて用いてもよい。これらの中でも、（ｃ）成分は、樹脂との相溶性の観点から、シリカであってもよい。
　（ｃ）成分の平均粒径は、接着性の向上の観点から、０．００５～１μｍ又は０．０５～０．５μｍであってよい。ここで、平均粒径は、ＢＥＴ比表面積から換算することによって求められる値を意味する。
　（ｃ）成分の含有量は、（ａ）成分、（ｂ）成分、及び（ｃ）成分の総質量１００質量部に対して、５～５０質量部、１５～４５質量部、又は２５～４０質量部であってよい。（ｃ）成分の含有量が５質量部以上であると、フィルム状接着剤の流動性がより向上する傾向にある。（ｃ）成分の含有量が５０質量部以下であると、フィルム状接着剤のダイシング性がより良好となる傾向にある。
＜（ｄ）カップリング剤＞
　（ｄ）成分は、シランカップリング剤であってよい。シランカップリング剤としては、例えば、γ－ウレイドプロピルトリエトキシシラン、γ－メルカプトプロピルトリメトキシシラン、３－フェニルアミノプロピルトリメトキシシラン、３－（２－アミノエチル）アミノプロピルトリメトキシシラン等が挙げられる。これらは、１種を単独で又は２種以上を組み合わせて用いてもよい。
　（ｄ）成分の含有量は、（ａ）成分、（ｂ）成分、及び（ｃ）成分の総質量１００質量部に対して、０．０１～５質量部であってよい。
＜（ｅ）硬化促進剤＞
　（ｅ）成分は、特に限定されず、一般に使用されるものを用いることができる。（ｅ）成分としては、例えば、イミダゾール類及びその誘導体、有機リン系化合物、第二級アミン類、第三級アミン類、第四級アンモニウム塩等が挙げられる。これらは、１種を単独で又は２種以上を組み合わせて用いてもよい。これらの中でも、反応性の観点から（ｅ）成分はイミダゾール類及びその誘導体であってもよい。
　イミダゾール類としては、例えば、２－メチルイミダゾール、１－ベンジル－２－メチルイミダゾール、１－シアノエチル－２－フェニルイミダゾール、１－シアノエチル－２－メチルイミダゾール等が挙げられる。これらは、１種を単独で又は２種以上を組み合わせて用いてもよい。
　（ｅ）成分の含有量は、（ａ）成分、（ｂ）成分、及び（ｃ）成分の総質量１００質量部に対して、０．０１～１質量部であってよい。
＜溶剤＞
　第１の接着フィルム２及び第２の接着フィルム４は、後述の第１の接着フィルム２及び第２の接着フィルム４を形成する際に用いられる溶剤が残存していてもよい。溶剤は、各成分を均一に溶解、混練または分散できるものであれば制限はなく、従来公知のものを使用することができる。このような溶剤としては、例えば、アセトン、メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン等のケトン系溶媒、ジメチルホルムアミド、ジメチルアセトアミド、Ｎメチルピロリドン、トルエン、キシレン等が挙げられる。乾燥速度が速く、価格が安い点でメチルエチルケトン、シクロヘキサノン等を使用することが好ましい。
　フィルム状接着剤１０（第１の接着フィルム２及び第２の接着フィルム４）の溶剤含有率は、フィルム状接着剤全量を基準として１．５質量％以下である。溶剤含有率は、１．２質量％以下、０．９質量％以下、又は０．６量％以下であってもよい。溶剤含有率は１．５質量％以下であると、ブリードを抑制できる傾向にある。溶剤含有率の下限値は、特に制限されないが、例えば、０．０１質量％以上であってよい。
　接着フィルムは、その厚さを薄くすることによって、溶剤を加熱乾燥し易くなり、溶剤含有率が低減される傾向にある。そのため、フィルム状接着剤１０のように、第１の接着フィルム２及び第２の接着フィルム４を備えるものは、単層で構成される同じ厚さのものに比べて、加熱乾燥条件を高くすることなく、溶剤含有率を低減し易くなる。また、フィルム状接着剤１０の溶剤含有率は、例えば、接着剤組成物のワニスの加熱乾燥の条件を変化させることによって、調整することができる。
　第１の接着フィルム２及び第２の接着フィルム４は、その他の成分をさらに含有していてもよい。その他の成分としては、例えば、イオントラップ剤、レオロジーコントロール剤等が挙げられる。その他の成分の含有量は、（ａ）成分、（ｂ）成分、及び（ｃ）成分の総質量１００質量部に対して、０．０１～２０質量部であってよい。
　フィルム状接着剤１０（第１の接着フィルム２及び第２の接着フィルム４）の８０℃におけるずり粘度は５０００Ｐａ・ｓ以下である。８０℃におけるずり粘度は、３５００Ｐａ・ｓ以下、２５００Ｐａ・ｓ以下、又は１５００Ｐａ・ｓ以下であってよい。８０℃におけるずり粘度は５０００Ｐａ・ｓ以下であると、流動性が高まり、埋め込み性が向上する傾向にある。８０℃におけるずり粘度の下限値は、特に制限されないが、例えば、１０Ｐａ・ｓ以上であってよい。なお、８０℃におけるずり粘度は、例えば、実施例に記載の方法によって測定することができる。
　フィルム状接着剤１０の８０℃におけるずり粘度は、例えば、上述の（ｂ）成分及び（ｃ）成分の含有量に依存する傾向にあり、これらを変化させることによって、調整することができる。
　フィルム状接着剤１０（第１の接着フィルム２及び第２の接着フィルム４）の８０℃における貯蔵弾性率は１０ＭＰａ以下であってよい。８０℃における貯蔵弾性率は、５ＭＰａ以下、１ＭＰａ以下、又は０．５ＭＰａ以下であってもよい。８０℃における貯蔵弾性率は１０ＭＰａ以下であると、埋め込み性により優れる傾向にある。８０℃における貯蔵弾性率の下限値は、特に制限されないが、例えば、０．０２ＭＰａ以上であってよい。
　フィルム状接着剤１０の８０℃における貯蔵弾性率は、例えば、（ａ）成分の官能基当量を変化させることによって調整することができる。
　第１の接着フィルム２の厚さ及び第２の接着フィルム４の厚さは、互いに同一であっても異なっていてもよいが、互いに同一であることが好ましい。第１の接着フィルム２の厚さ及び第２の接着フィルム４の厚さは、それぞれ２～１４０μｍであってよい。第１の接着フィルム２の厚さ及び第２の接着フィルム４の厚さは、それぞれ５～１１０μｍ、１０～９０μｍ、又は２０～６０μｍであってよい。これらの厚さがそれぞれ２μｍ以上であると、埋め込み性がより良好となる傾向にある。これらの厚さがそれぞれ１４０μｍ以下であると、溶剤含有率をより低くすることができる傾向にある。
　フィルム状接着剤１０の厚さ（第１の接着フィルム２と第２の接着フィルム４との合計の厚さ）は、第１のワイヤ及び第１の半導体素子、並びに基板の配線回路等の凹凸を十分に充填可能とするため、３～１５０μｍであってよい。フィルム状接着剤１０の厚さは、２０～１４０ｍ又は４０～１３０μｍであってもよい。フィルム状接着剤１０の厚さが３μｍ以上であると、埋め込み性により優れる傾向にある。フィルム状接着剤１０の厚さが１５０μｍ以下であると、ブリードをより抑制できる傾向にある。
　フィルム状接着剤１０は、第１の接着フィルム２及び第２の接着フィルム４に、さらに接着フィルムが積層されていてもよい。すなわち、フィルム状接着剤１０は、３層以上の接着フィルムを備えていてもよい。第１の接着フィルム２及び第２の接着フィルム４以外の接着フィルムは、第１の接着フィルム２及び第２の接着フィルム４と同一のものであってよい。
［フィルム状接着剤の製造方法］
　フィルム状接着剤の製造方法は、溶剤を含有する第１の接着剤組成物のワニスを基材上に塗布し、塗布された第１の接着剤組成物のワニスを５０～１５０℃で加熱乾燥し、溶剤含有率が第１の接着フィルム全量を基準として１．５質量％以下である第１の接着フィルムを作製する工程と、溶剤を含有する第２の接着剤組成物のワニスを基材上に塗布し、塗布された第２の接着剤組成物のワニスを５０～１５０℃で加熱乾燥し、溶剤含有率が第２の接着フィルム全量を基準として１．５質量％以下である第２の接着フィルムを作製する工程と、第１の接着フィルムと第２の接着フィルムとを貼り合わせる工程と、を備える。
　第１の接着剤組成物のワニス及び第２の接着剤組成物のワニスは、例えば、（ａ）～（ｅ）成分、必要に応じて（ｄ）成分及び（ｅ）成分を、溶剤中で混合、混練することによって調製することができる。
　混合、混練は、通常の撹拌機、らいかい機、三本ロール、ボールミル等の分散機を用い、これらを適宜組み合わせて行うことができる。
　第１の接着剤組成物のワニス及び第２の接着剤組成物のワニスを作製するための溶剤は、上記各成分を均一に溶解、混練または分散できるものであれば制限はなく、従来公知のものを使用することができる。このような溶剤としては、例えば、アセトン、メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン等のケトン系溶媒、ジメチルホルムアミド、ジメチルアセトアミド、Ｎメチルピロリドン、トルエン、キシレン等が挙げられる。乾燥速度が速く、価格が安い点でメチルエチルケトン、シクロヘキサノン等を使用することが好ましい。
　基材フィルムとしては、特に制限はなく、例えば、ポリエステルフィルム、ポリプロピレンフィルム（ＯＰＰフィルム等）、ポリエチレンテレフタレートフィルム、ポリイミドフィルム、ポリエーテルイミドフィルム、ポリエーテルナフタレートフィルム、メチルペンテンフィルム等が挙げられる。
　第１の接着剤組成物のワニス及び第２の接着剤組成物のワニスを基材フィルムに塗布する方法としては、公知の方法を用いることができ、例えば、ナイフコート法、ロールコート法、スプレーコート法、グラビアコート法、バーコート法、カーテンコート法等が挙げられる。加熱乾燥の条件は、使用した溶剤が充分に揮散する条件であれば特に制限はないが、例えば、５０～１５０℃で、１～３０分間加熱して行うことができる。加熱乾燥は、５０～１５０℃の範囲内の温度で段階的に昇温させて行ってもよい。加熱温度を５０℃以上とすることによって、第１の接着フィルム２及び第２の接着フィルム４（フィルム状接着剤１０）の溶剤含有率をフィルム状接着剤全量基準で１．５質量％以下とし易くなる傾向にある。一方、加熱温度を１５０℃以下とすることによって、接着剤組成物の硬化が進むことを抑制できる傾向にある。
　フィルム状接着剤１０は、第１の接着フィルム２と第２の接着フィルム４とをロールラミネーター、真空ラミネーター等を用いて所定条件（例えば、室温（２０℃）、又は加熱状態）で貼り合わせることによって作製することができる。
　フィルム状接着剤１０は、まず、第１の接着剤組成物のワニスを基材フィルムに塗布し、溶剤を加熱乾燥して除去して第１の接着フィルム２を作製し、次いで、第１の接着フィルム２上に、第２の接着剤組成物のワニスを塗布し、溶剤を加熱乾燥して除去して第２の接着フィルムを形成することによっても作製することができる。
［接着シート］
　図２は、一実施形態に係る接着シートを示す模式断面図である。接着シート１００は、基材フィルム２０と基材フィルム２０上に設けられた第１の接着フィルム２及び第２の接着フィルム４からなるフィルム状接着剤１０とを備える。
　基材フィルム２０は、ダイシングテープであってもよい。このような接着シートは、ダイシングダイボンディング一体型接着シートとして使用することができる。この場合、半導体ウェハへのラミネート工程が１回となることから、作業の効率化が可能である。
　ダイシングテープとしては、例えば、ポリテトラフルオロエチレンフィルム、ポリエチレンテレフタレートフィルム、ポリエチレンフィルム、ポリプロピレンフィルム、ポリメチルペンテンフィルム、ポリイミドフィルム等のプラスチックフィルム等が挙げられる。また、ダイシングテープは、必要に応じて、プライマー塗布、ＵＶ処理、コロナ放電処理、研磨処理、エッチング処理等の表面処理が行われていてもよい。ダイシングテープは、粘着性を有するものであることが好ましい。このようなダイシングテープは、上述のプラスチックフィルムに粘着性を付与したものであってもよく、上述のプラスチックフィルムの片面に粘着剤層を設けたものであってもよい。
　接着シート１００は、まず、第１の接着剤組成物のワニスを調製し、これを基材フィルムに塗布し、溶剤を加熱乾燥して除去することによって第１の接着フィルム２を作製する。次いで、別途、第２の接着剤組成物のワニスから第２の接着フィルム４を作製し、これを第１の接着フィルム２にラミネートすることによって作製することができる。
　図３は、他の実施形態に係る接着シートを示す模式断面図である。接着シート１１０は、フィルム状接着剤１０の基材フィルム２０とは反対側の面（第２の接着フィルム４側の面）に積層された保護フィルム３０をさらに備える。保護フィルム３０は、上述の基材フィルム２０と同様のものであってよい。保護フィルムの厚さは、例えば、６０～２００μｍ又は７０～１７０μｍであってよい。
［半導体装置］
　図４は、一実施形態に係る半導体装置を示す模式断面図である。半導体装置２００は、基板１４に、第１のワイヤ８８を介して１段目の第１の半導体素子Ｗａがワイヤボンディング接続されると共に、第１の半導体素子Ｗａ上に、第２の半導体素子Ｗａａがフィルム状接着剤１０を介して圧着されることで、第１のワイヤ８８の少なくとも一部がフィルム状接着剤１０に埋め込まれてなる半導体装置である。半導体装置は、第１のワイヤ８８の少なくとも一部が埋め込まれてなるワイヤ埋め込み型の半導体装置であっても、第１のワイヤ８８及び第１の半導体素子Ｗａが埋め込まれてなる半導体装置であってもよい。また、半導体装置２００では、基板１４と第２の半導体素子Ｗａａとがさらに第２のワイヤ９８を介して電気的に接続されると共に、第２の半導体素子Ｗａａが封止材４２により封止されている。
　第１の半導体素子Ｗａの厚さは、１０～１７０μｍであってよく、第２の半導体素子Ｗａａの厚さは、２０～４００μｍであってよい。フィルム状接着剤１０内部に埋め込まれている第１の半導体素子Ｗａは、半導体装置２００を駆動するためのコントローラチップである。
　基板１４は、表面に回路パターン８４、９４がそれぞれ二箇所ずつ形成された有機基板９０からなる。第１の半導体素子Ｗａは、回路パターン９４上に接着剤４１を介して圧着されている。第２の半導体素子Ｗａａは、第１の半導体素子Ｗａが圧着されていない回路パターン９４、第１の半導体素子Ｗａ、及び回路パターン８４の一部が覆われるようにフィルム状接着剤１０を介して基板１４に圧着されている。基板１４上の回路パターン８４、９４に起因する凹凸の段差には、フィルム状接着剤１０が埋め込まれている。そして、樹脂製の封止材４２により、第２の半導体素子Ｗａａ、回路パターン８４及び第２のワイヤ９８が封止されている。
［半導体装置の製造方法］
　本実施形態に係る半導体装置の製造方法は、基板上に第１のワイヤを介して第１の半導体素子を電気的に接続する第１のワイヤボンディング工程と、第２の半導体素子の片面に、上述のフィルム状接着剤を貼付するラミネート工程と、フィルム状接着剤が貼付された第２の半導体素子を、フィルム状接着剤を介して圧着することで、第１のワイヤの少なくとも一部をフィルム状接着剤に埋め込むダイボンド工程と、を備える。
　図５～９は、一実施形態に係る半導体装置の製造方法の一連の工程を示す模式断面図である。本実施形態に係る半導体装置２００は、第１のワイヤ８８及び第１の半導体素子Ｗａが埋め込まれてなる半導体装置であり、以下の手順により製造される。まず、図５に示すとおり、基板１４上の回路パターン９４上に、接着剤４１を有する第１の半導体素子Ｗａを圧着し、第１のワイヤ８８を介して基板１４上の回路パターン８４と第１の半導体素子Ｗａとを電気的にボンディング接続する（第１のワイヤボンディング工程）。
　次に、半導体ウェハ（例えば、厚さ：５０μｍ、サイズ：８インチ）の片面に、接着シート１００をラミネートし、基材フィルム２０を剥がすことによって、半導体ウェハの片面にフィルム状接着剤１０（例えば、厚さ：１３５μｍ）を貼り付ける。そして、フィルム状接着剤１０にダイシングテープを貼り合わせた後、所定の大きさ（例えば、７．５ｍｍ角）にダイシングすることにより、図６に示すとおり、フィルム状接着剤１０が貼付した第２の半導体素子Ｗａａを得る（ラミネート工程）。
　ラミネート工程の温度条件は、５０～１００℃又は６０～８０℃であってよい。ラミネート工程の温度が５０℃以上であると、半導体ウェハと良好な密着性を得ることができる。ラミネート工程の温度が１００℃以下であると、ラミネート工程中にフィルム状接着剤１０が過度に流動することが抑えられるため、厚さの変化等を引き起こすことを防止できる。
　ダイシング方法としては、例えば、回転刃を用いるブレードダイシング、レーザーによってフィルム状接着剤又はウェハとフィルム状接着剤の両方を切断する方法等が挙げられる。
　そして、フィルム状接着剤１０が貼付した第２の半導体素子Ｗａａを、第１の半導体素子Ｗａが第１のワイヤ８８を介してボンディング接続された基板１４に圧着する。具体的には、図７に示すとおり、フィルム状接着剤１０が貼付された第２の半導体素子Ｗａａを、フィルム状接着剤１０によって第１のワイヤ８８及び第１の半導体素子Ｗａが覆われるように載置し、次いで、図８に示すとおり、第２の半導体素子Ｗａａを基板１４に圧着させることで基板１４に第２の半導体素子Ｗａａを固定する（ダイボンド工程）。ダイボンド工程は、フィルム状接着剤１０を８０～１８０℃、０．０１～０．５０ＭＰａの条件で０．５～３．０秒間圧着することが好ましい。ダイボンド工程の後、フィルム状接着剤１０を６０～１７５℃、０．３～０．７ＭＰａの条件で、５分間以上加圧及び加熱する。
　次いで、図９に示すとおり、基板１４と第２の半導体素子Ｗａａとを第２のワイヤ９８を介して電気的に接続した後（第２のワイヤボンディング工程）、回路パターン８４、第２のワイヤ９８及び第２の半導体素子Ｗａａを封止材４２で封止する。このような工程を経ることで半導体装置２００を製造することができる。
　他の実施形態として、半導体装置は、第１のワイヤ８８の少なくとも一部が埋め込まれてなるワイヤ埋め込み型の半導体装置であってもよい。
　以下、本発明について実施例を挙げてより具体的に説明する。ただし、本発明はこれら実施例に限定されるものではない。
＜接着剤組成物のワニスの調製＞
（合成例１～３）
　表１に示す品名及び組成比（単位：質量部）で、（ａ）熱硬化性樹脂としてのエポキシ樹脂及びフェノール樹脂、並びに（ｃ）無機フィラーからなる組成物にシクロヘキサノンを加え、撹拌混合した。これに、表１に示す（ｂ）高分子量成分としてのアクリルゴムを加えて撹拌し、さらに表１に示す（ｄ）カップリング剤及び（ｅ）硬化促進剤を加えて各成分が均一になるまで撹拌して合成例１～３の接着剤組成物のワニスを調製した。
　なお、表１中の各成分の記号は下記のものを意味する。
（エポキシ樹脂）
　ＹＤＣＮ－７００－１０（商品名、新日鉄住金化学株式会社製、ｏ－クレゾールノボラック型エポキシ樹脂、エポキシ当量：２０９ｇ／ｅｑ）
　ＥＸＡ－８３０ＣＲＰ（商品名、ＤＩＣ株式会社製、ビスフェノールＦ型エポキシ樹脂、エポキシ当量：１５９ｇ／ｅｑ）
　ＪＥＲ　ＹＬ－９８０（商品名、三菱ケミカル株式会社製、ビスフェノールＡ型エポキシ樹脂、エポキシ当量：１８５ｇ／ｅｑ）
（フェノール樹脂）
　ＨＥ－１００Ｃ－３０（商品名、エア・ウォーター株式会社製、フェノールアラルキル樹脂、水酸基当量：１７５ｇ／ｅｑ、軟化点７７℃）
　ＭＥＨ－７８００Ｈ（商品名、明和化成株式会社製、フェノールアラルキル樹脂、水酸基当量１７８ｇ／ｅｑ、軟化点８７℃）
（高分子量成分）
　ＨＴＲ－８６０Ｐ－３ＣＳＰ（商品名、ナガセケムテックス株式会社製、アクリルゴム、重量平均分子量：８０万、Ｔｇ：１２℃）
　ＳＧ－７０Ｌ（商品名、ナガセケムテックス株式会社製、アクリルゴム、重量平均分子量：９０万、Ｔｇ：－１３℃）
（無機フィラー）
　ＳＣ２０５０－ＨＬＧ（商品名、株式会社アドマテックス製、シリカフィラー分散液、平均粒径：０．５０μｍ）
　ＳＥ２０５０－ＭＣ（商品名、株式会社アドマテックス製、シリカフィラー分散液、平均粒径０．５０μｍ）
（カップリング剤）
　Ａ－１１６０（商品名、モメンティブ・パフォーマンス・マテリアルズ・ジャパン合同会社製、γ－ウレイドプロピルトリエトキシシラン）
　Ａ－１８９（商品名、モメンティブ・パフォーマンス・マテリアルズ・ジャパン合同会社製、γ－メルカプトプロピルトリメトキシシラン）
（硬化促進剤）
　２ＰＺ－ＣＮ（商品名、四国化成工業株式会社製、１－シアノエチル－２－フェニルイミダゾール）
　ＴＰＰ－Ｋ（商品名、北興化学工業株式会社製、テトラフェニルホスホニウムテトラフェニルボレート）
Figure JPOXMLDOC01-appb-T000001
＜接着シートの作製＞
（実施例１）
　合成例１の接着剤組成物のワニスを１００メッシュのフィルターでろ過し、真空脱泡した。基材フィルムとして、厚さ３８μｍの離型処理を施したポリエチレンテレフタレート（ＰＥＴ）フィルムを用意し、真空脱泡後の接着剤組成物のワニスをＰＥＴフィルム上に塗布した。塗布したワニスを、９０℃で５分間、続いて１４０℃で５分間の２段階で加熱乾燥した。こうして、ＰＥＴフィルム上に、Ｂステージ状態にある厚さ６０μｍの接着フィルムを備える接着シートを得た。次いで、２枚の接着シートを用意し、接着フィルム同士が接するように配置して、７０℃のホットプレート上でラミネートして、２層の接着フィルムからなる厚さを１２０μｍのフィルム状接着剤を備える接着シートを作製した。
（実施例２）
　合成例１の接着剤組成物のワニスを合成例２の接着剤組成物のワニスに変更した以外は、実施例１と同様にして、２層の接着フィルムからなる厚さを１２０μｍのフィルム状接着剤を備える接着シートを作製した。
（実施例３）
　合成例１の接着剤組成物のワニスを合成例３の接着剤組成物のワニスに変更した以外は、実施例１と同様にして、２層の接着フィルムからなる厚さを１２０μｍのフィルム状接着剤を備える接着シートを作製した。
（比較例１）
　合成例１の接着剤組成物のワニスを１００メッシュのフィルターでろ過し、真空脱泡した。基材フィルムとして、厚さ３８μｍの離型処理を施したポリエチレンテレフタレート（ＰＥＴ）フィルムを用意し、真空脱泡後の接着剤組成物のワニスをＰＥＴフィルム上に塗布した。塗布したワニスを、９０℃で１０分間、続いて１５０℃で１０分間の２段階で加熱乾燥した。こうして、ＰＥＴフィルム上に、Ｂステージ状態にある単層の厚さ１２０μｍのフィルム状接着剤を備える接着シートを作製した。
（比較例２）
　９０℃で１０分間、１５０℃で１０分間の２段階の加熱乾燥を、１２０℃で２０分間、１６０℃で２０分間の２段階の加熱乾燥に変更した以外は、比較例１と同様にして、ＰＥＴフィルム上に、Ｂステージ状態にある単層の厚さ１２０μｍのフィルム状接着剤を備える接着シートを作製した。
（比較例３）
　合成例１の接着剤組成物のワニスを合成例２の接着剤組成物のワニスに変更した以外は、比較例２と同様にして、ＰＥＴフィルム上に、Ｂステージ状態にある単層の厚さ１２０μｍのフィルム状接着剤を備える接着シートを作製した。
（比較例４）
　合成例１の接着剤組成物のワニスを合成例３の接着剤組成物のワニスに変更した以外は、比較例２と同様にして、ＰＥＴフィルム上に、Ｂステージ状態にある単層の厚さ１２０μｍのフィルム状接着剤を備える接着シートを作製した。
＜各種物性の評価＞
　実施例１～３及び比較例１～４の接着シートのフィルム状接着剤について、溶剤含有率、８０℃におけるずり粘度、８０℃における貯蔵弾性率、１７５℃加圧オーブン硬化後の埋め込み性、及びブリード量の測定を行った。
（溶剤含有率）
　上記接着シートから、基材フィルムを剥離除去し、フィルム状接着剤１ｇを、１質量％の２－（２－エトキシエトキシ）エタノールを含む１，４－ジオキサン溶液３０ｇに加え、振とう機で６時間撹拌した。撹拌後の溶液をガスクロマトグラフィー（キャリアガス：ヘリウム、カラム温度：１４０℃）で測定し、各溶剤と２－（２－エトキシエトキシ）エタノールとのピーク面積からフィルム状接着剤の溶剤含有率（質量％）を見積もった。結果を表２に示す。
（８０℃におけるずり粘度）
　上記接着シートから、基材フィルムを剥離除去し、厚さ方向に１０ｍｍ角に打ち抜くことで、１０ｍｍ角の四角形の積層体を得た。動的粘弾性装置ＡＲＥＳ（レオメトリック・サイエンティフィック社製）に直径８ｍｍの円形アルミプレート治具をセットし、さらにここに打ち抜いたフィルム状接着剤の四角形の積層体をセットした。その後、３５℃で５％の歪みを与えながら５℃／分の昇温速度で８０℃まで昇温させ、８０℃におけるずり粘度（Ｐａ・ｓ）を測定した。結果を表２に示す。
（８０℃における貯蔵弾性率）
　上記接着シートから、基材フィルムを剥離除去し、長さ４ｃｍ、幅４ｍｍに切り出した。動的粘弾性装置（製品名：Ｒｈｅｏｇｅｌ－Ｅ４０００、株式会社ユービーエム製）にセットし、引張り荷重をかけて、周波数１０Ｈｚ、３℃／分の昇温速度で８０℃まで昇温させ、８０℃における貯蔵弾性率を測定した。結果を表２に示す。
（１７５℃加圧オーブン硬化後の埋め込み性）
　上記接着シートのフィルム状接着剤を、厚さ５０μｍの半導体ウェハ（８インチ）に７０℃で貼り付けた。次に、それらを７．５ｍｍ角にダイシングして半導体素子を得た。また、フィルム状接着剤ＨＲ－９００４Ｔ－１０（日立化成株式会社製、厚さ２０μｍ）を厚さ５０μｍの半導体ウェハ（８インチ）に７０℃で貼り付けた。次に、それらを３．０ｍｍ角にダイシングしてチップを得た。個片化したＨＲ－９００４Ｔ－１０付きのチップを、表面凹凸が最大６μｍである評価用基板に１３０℃、０．２０ＭＰａ、２秒間の条件で圧着し、１２０℃／２時間加熱し、半硬化させた。次に、このようにして得られたサンプルに、フィルム状接着剤付きの７．５ｍｍ半導体素子を１２０℃、０．２０ＭＰａ、２秒間の条件で圧着した。この際、先に圧着しているＨＲ－９００４Ｔ－１０付きのチップが中央となるように位置合わせを行った。得られたサンプルを加圧オーブンに投入し、３５℃から３℃／分の昇温速度で１７５℃まで昇温させ、１７５℃で３０分加熱した。このようにして得られたサンプルを超音波映像装置ＳＡＴ（日立建機製、品番ＦＳ２００ＩＩ、プローブ：２５ＭＨｚ）にてボイドの有無を観測し、ボイドが観測された場合は、単位面積あたりのボイドの面積を算出し、これらの分析結果を埋め込み性として評価した。評価基準は、以下のとおりである。結果を表２に示す。
　Ａ：ボイドが観測されなかった。
　Ｂ：ボイドが観測されたが、その割合が５面積％未満であった。
　Ｃ：ボイドが観測され、その割合が５面積％以上であった。
（ブリード量の測定）
　上記１７５℃加圧オーブン硬化後の埋め込み性の評価において、「Ａ」及び「Ｂ」であったものについて、ブリード量を測定した。サンプルは、上記１７５℃加圧オーブン硬化後の埋め込み性で作製したサンプルと同様の手順で作製した。得られたサンプルの４辺の中心から、フィルム状接着剤のはみ出し量をそれぞれ測長し、その平均値をブリード量とした。結果を表２に示す。
Figure JPOXMLDOC01-appb-T000002
　表１より、実施例１～３の２層の接着フィルムからなる接着シートは、埋め込み性が良好であり、ブリードが抑制されていることが分かった。一方、比較例１の溶剤含有率が１．５質量％を超える単層の接着フィルムを用いた接着シートは、埋め込み性は良好であるものの、ブリードを抑制することができなかった。また、８０℃におけるずり粘度が５０００Ｐａ・ｓを超える単層の接着フィルムを用いた接着シートは、埋め込み性が充分ではなかった。これらの結果より、本発明のフィルム状接着剤が、熱圧着時に良好な埋め込み性を有しつつ、ブリードを抑制することが可能であることが確認された。
　２…第１の接着フィルム、４…第２の接着フィルム、１０…フィルム状接着剤、１４…基板、２０…基材フィルム、３０…保護フィルム、４１…接着剤、４２…封止材、８４、９４…回路パターン、８８…第１のワイヤ、９０…有機基板、９８…第２のワイヤ、１００、１１０…接着シート、２００…半導体装置、Ｗａ…第１の半導体素子、Ｗａａ…第２の半導体素子。

Claims (6)

  1. 　基板上に第１のワイヤを介して第１の半導体素子がワイヤボンディング接続されると共に、前記第１の半導体素子上に、第２の半導体素子が圧着されてなる半導体装置において、前記第２の半導体素子を圧着すると共に、前記第１のワイヤの少なくとも一部を埋め込むために用いられるフィルム状接着剤であって、
    　第１の接着フィルムと、前記第１の接着フィルム上に積層された第２の接着フィルムと、を備え、
    　前記フィルム状接着剤の溶剤含有率がフィルム状接着剤全量を基準として１．５質量％以下であり、
    　前記フィルム状接着剤の８０℃におけるずり粘度が５０００Ｐａ・ｓ以下である、フィルム状接着剤。
  2. 　前記フィルム状接着剤の厚さが３～１５０μｍである、請求項１に記載のフィルム状接着剤。
  3. 　前記フィルム状接着剤の８０℃における貯蔵弾性率が１０ＭＰａ以下である、請求項１又は２に記載のフィルム状接着剤。
  4. 　請求項１～３のいずれか一項に記載のフィルム状接着剤の製造方法であって、
    　溶剤を含有する第１の接着剤組成物のワニスを基材上に塗布し、塗布された前記第１の接着剤組成物のワニスを５０～１５０℃で加熱乾燥し、溶剤含有率が第１の接着フィルム全量を基準として１．５質量％以下である第１の接着フィルムを作製する工程と、
    　溶剤を含有する第２の接着剤組成物のワニスを基材上に塗布し、塗布された前記第２の接着剤組成物のワニスを５０～１５０℃で加熱乾燥し、溶剤含有率が第２の接着フィルム全量を基準として１．５質量％以下である第２の接着フィルムを作製する工程と、
    　前記第１の接着フィルムと前記第２の接着フィルムとを貼り合わせる工程と、
    を備える、フィルム状接着剤の製造方法。
  5. 　基板上に第１のワイヤを介して第１の半導体素子がワイヤボンディング接続されると共に、前記第１の半導体素子上に、第２の半導体素子が請求項１～３のいずれか一項に記載のフィルム状接着剤を介して圧着されることで、前記第１のワイヤの少なくとも一部が前記フィルム状接着剤に埋め込まれてなる、半導体装置。
  6. 　基板上に第１のワイヤを介して第１の半導体素子を電気的に接続するワイヤボンディング工程と、
    　第２の半導体素子の片面に、請求項１～３のいずれか一項に記載のフィルム状接着剤を貼付するラミネート工程と、
    　前記フィルム状接着剤が貼付された第２の半導体素子を、前記フィルム状接着剤を介して圧着することで、前記第１のワイヤの少なくとも一部を前記フィルム状接着剤に埋め込むダイボンド工程と、
    を備える、半導体装置の製造方法。
PCT/JP2018/003022 2018-01-30 2018-01-30 フィルム状接着剤及びその製造方法、並びに半導体装置及びその製造方法 Ceased WO2019150445A1 (ja)