WO2019122478A1 - Composición que comprende cenizas de cremación - Google Patents

Composición que comprende cenizas de cremación Download PDF

Info

Publication number
WO2019122478A1
WO2019122478A1 PCT/ES2018/070807 ES2018070807W WO2019122478A1 WO 2019122478 A1 WO2019122478 A1 WO 2019122478A1 ES 2018070807 W ES2018070807 W ES 2018070807W WO 2019122478 A1 WO2019122478 A1 WO 2019122478A1
Authority
WO
WIPO (PCT)
Prior art keywords
composition
composition according
clay
ashes
cremation
Prior art date
Application number
PCT/ES2018/070807
Other languages
English (en)
French (fr)
Inventor
Gabriel Narbón Prieto
Francisco Ramón SÁNCHEZ-GUITARD LÓPEZ-VALERA
Antonio Teruel Saiz
Original Assignee
Narbon, S.L.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Narbon, S.L. filed Critical Narbon, S.L.
Priority to JP2020566328A priority Critical patent/JP2021517528A/ja
Priority to CN201880089825.1A priority patent/CN112074496A/zh
Priority to US16/975,621 priority patent/US20210114935A1/en
Priority to KR1020207021058A priority patent/KR20200112848A/ko
Priority to EP18855173.3A priority patent/EP3730469A1/en
Publication of WO2019122478A1 publication Critical patent/WO2019122478A1/es
Priority to CONC2020/0008921A priority patent/CO2020008921A2/es

Abstract

La presente invención se refiere a una composición que comprende arcilla y cenizas procedentes de la cremación de personas, animales o vegetales fallecidas y tiene por finalidad la creación de un vínculo emocional entre la pieza creada con dicha composición y el usuario que lo quiera adquirir.

Description

COMPOSICIÓN QUE COMPRENDE CENIZAS DE CREMACIÓN
La presente invención se refiere a una composición que comprende arcilla y cenizas procedentes de la cremación de personas, animales o vegetales fallecidas y tiene por finalidad la creación de un vínculo emocional entre la pieza creada con dicha composición y el usuario que lo quiera adquirir.
ANTECEDENTES DE LA INVENCIÓN
En la actualidad existen diferentes productos relativos al homenaje y al recuerdo de las personas fallecidas personas, incluso también de las mascotas. Estos son, en la manera tradicional, creados mediante pelo, dientes y otras partes o tejidos pertenecientes al ser querido fallecido.
Actualmente, la cremación o incineración es una de las prácticas más habituales como destino final del cadáver, que consiste en quemar al fallecido, lo que frecuentemente tiene lugar en un lugar denominado crematorio u horno de cremación. Un horno de cremación es un horno industrial capaz de alcanzar altas temperaturas (de aproximadamente 870 a 980 °C), con modificaciones especiales para asegurar la eficiente desintegración del cuerpo, procedimiento del cual resultan las cenizas. Poco a poco la cremación están ganando espacio a la práctica de la inhumación y además el destino final de las cenizas suele ser su esparcimiento, lo que imposibilita posteriormente tener un vínculo emocional de contacto directo entre el recuerdo del fallecido y sus dolientes.
DESCRIPCIÓN DE LA INVENCIÓN
La presente invención proporciona una composición caracterizada por que comprende una mezcla de al menos una arcilla y cenizas procedentes de la cremación de un sujeto fallecido (persona, animal o planta). Dicha composición tiene como fin la fabricación de un objeto emocional o de recuerdo permanente.
Por tanto, un primer aspecto de la presente invención se refiere a una composición emocional caracterizada por que comprende:
(a) arcilla; y
(b) cenizas procedentes de la cremación de un sujeto fallecido. La ventaja obtenida mediante la utilización de la composición de la presente invención frente al resto descrito en el estado de la técnica es la capacidad de personalización y el aspecto homogéneo tanto de la composición como del objeto formado con la composición, incluso por compresión. Así como la generación de un vínculo emocional con la persona que lleve o posea dicho objeto.
En otra realización preferida, la composición está caracterizada por que la arcilla se selecciona de la lista que comprende: arcilla blanca, pasta de loza calcárea, dolomita, feldespato, caolinita, halloisita, ¡Hita, clorita, vermiculita, montmorillonita, sepiolita- paligorskita y cualquier combinación de las anteriores.
En una realización más preferida, la composición emocional está caracterizada por que la arcilla es arcilla blanca.
En otra realización preferida, la composición emocional está caracterizada por que la arcilla tiene un porcentaje de entre 90% y 95% en peso con respecto a la composición final.
En otra realización preferida, la composición emocional está caracterizada por que las cenizas tiene un porcentaje de entre 5% y 10% en peso con respecto a la composición final.
En otra realización preferida, la composición emocional está caracterizada por que esta composición está cocida, se encuentra en forma sólida y además comprende una capa externa (c) de esmalte, donde dicha capa externa de esmalte es adecuada para el caso de que la composición se utilice como un elemento o figura cerámica o figura o elemento tridimensional obtenido de impresión 3D. Este esmalte se añade para que los poros generados durante dicho proceso de cocción sean ocluidos con dicho esmalte dando uniformidad y rigidez al elemento o figura cerámica final o figura o elemento tridimensional obtenido de impresión 3D. Este esmalte se añade tras cocción en horno convencional de la composición emocional a una temperatura de entre 800 °C y 900 °C y previa a una segunda cocción en horno convencional a una temperatura de entre 1000 °C y 1060 °C. Una realización más preferida de la composición, donde la capa de esmalte es un resina seleccionada de la siguiente lista resina epoxi, resina fotosensible o cualquier combinación de las anteriores.
En otra realización preferida, la composición emocional está caracterizada por que la arcilla tiene un tamaño de partícula en relación con el tamaño de las cenizas tal que se eviten la generación de poros masivos en la estructura, ya que de esta manera la fragilidad del cerámico será minimizada, así como la compactación adecuada del cerámico con las cenizas en su interior, que evitara su laminado o rotura.
Otro aspecto de la presente invención se refiere a un elemento o figura que comprende una composición según se ha descrito en la present invención.
Otro aspecto de la presente invención se refiere a un elemento o figura que comprende una composición que comprende una capa externa de esmalte, que preferiblemente es un resina seleccionada de la siguiente lista resina epoxi, resina fotosensible o cualquier combinación de las anteriores, y que se encuentra engarzada en un soporte.
Una realización preferida de la presente invención es el elemento o figura donde dicho elemento o figura es tridimensional.
Otro aspecto de la presente invención se refiere al uso de la composición descrita como tinta de una impresora 3D para obtener un elemento o figura tridimensional, para así dar lugar a un objeto con finalidad de recordatorio de una persona, mascota o ser vivo fallecido. Preferiblemente, el elemento o figura tridimensional es un relicario.
Otro aspecto de la presente invención se refiere al uso de la composción descrita como elemento o figura cerámica. Preferiblemente este elemento o figura es un relicario.
Una realización más preferida es el uso del elemento o figura tridimensional, o figura cerámica, ya esmaltada se engarza en los soportes correspondientes.
En la presente invención se entiende por“composición emocional” a toda aquella composición que comprende al menos un tanto por ciento de ceniza procedente de la cremación de un cadáver.
En la presente invención se entiende por“sujeto” un humano, animal o vegetal.
En la presente invención se entiende por“cenizas” a aquellas procedentes de un procedimiento de cremación bien de una persona fallecida, o bien de una animal fallecido, tal como un animal de compañía o mascota, o incluso de un vegetal.
En una realización preferida, las cenizas se recuperan a la finalización del proceso de cremación y posteriormente se filtran y tamizan hasta un tamaño inferior a 0,25 milímetros de diámetro, para aseguramos una homogeneidad en la posterior mezcla de la composición final. Esta realización está adecuada para la obtención de la composición de la invención con el tamaño de partículas óptimas para su utilización como tinta de impresora 3D, debido a que con este tamaño de partículas de la composición se encuentra así optimizada para su extrusión a presiones de 4 bares desde la cámara presurizada de una impresora 3D.
En la presente invención se entiende por“arcilla” a cualquier partícula o fragmento ya sea un filosilicato o cualquier otro mineral aglomerante, que tengan un tamaño de partícula inferior a 0,002 milímetros.
En la presente invención se entiende por“filosilicato” a una subclase de los silicatos que incluye minerales comunes en ambientes muy diversos y que presentan, como rasgo común, un hábito hojoso (phyllon = hoja) o escamoso derivado de la existencia de una exfoliación basal perfecta. Esto es consecuencia de la presencia en su estructura de capas de tetraedros de dimensionalidad infinita en dos direcciones del espacio. La fórmula química de estos compuestos siempre tiene el anión (Si205 2 )n.
A lo largo de la descripción y las reivindicaciones la palabra "comprende" y sus variantes no pretenden excluir otras características técnicas, aditivos, componentes o pasos. Para los expertos en la materia, otros objetos, ventajas y características de la invención se desprenderán en parte de la descripción y en parte de la práctica de la invención. Los siguientes ejemplos y figuras se proporcionan a modo de ilustración, y no se pretende que sean limitativos de la presente invención. REALIZACIÓN PREFERENTE DE LA INVENCIÓN
Seguidamente se proporciona una explicación detallada de un ejemplo de realización preferente del objeto de la presente invención.
Preparación de una figura de arcilla y cenizas obtenida mediante impresión 3D y posterior esmaltado.
Para la preparación se recuperan las cenizas procedentes de la cremación de restos de un ser vivo fallecido, las cuales son posteriormente filtradas y tamizadas para descartar aquellas partículas con un diámetro superior a 0,25 milímetros.
Las partículas seleccionadas son mezcladas con arcillas, con un tamaño de partícula inferior a 0,002 milímetros, hasta obtener una mezcla homogénea, la cual es posteriormente introducida en el interior de un contenedor dotado de un sistema de presión, que ejerce una sobrepresión de 4 bares sobre los materiales contenidos en su interior.
El contenedor comprende una salida a través de la cual la mezcla de materiales es desalojada de su interior, con la sobrepresión introducida, para alimentar con dicha mezcla de materiales a una impresora 3D dotada de al menos una boquilla extrusora.
La boquilla de la impresora deposita, sobre un sustrato externo, una pluralidad de capas compuestas por la mezcla de materiales, hasta conformar el objeto deseado, cuyo diseño ha sido previamente introducido mediante un fichero informático. En la realización preferente aquí descrita, cada una de las sucesivas capas tiene un grosor aproximado de 1 milímetro, y se obtiene finalmente un objeto rígido con el diseño seleccionado.
Una vez finalizada la impresión, la pieza se deja secar aproximadamente 8-12 h.
Cuando la pieza esta totalmente seca se realiza la primera cocción que dura alrededor de 15h, donde la temperatura máxima que alcanza esta primera cocción es de 850 °C. Posteriormente se esmalta la pieza con ayuda de un pincel recubriendo toda su superficie, y se realiza una segunda cocción, donde el esmalte se funde en la superficie del objeto. Este proceso dura 12h y alcanza una temperatura máxima de 1030°C.
Por último se engarza la pieza ya esmaltada en los soportes correspondientes.

Claims

REIVINDICACIONES
1. Composición caracterizada por que comprende:
(a) arcilla; y
(b) cenizas procedentes de la cremación de un sujeto fallecido.
2. Composición según la reivindicación 1 , donde la arcilla se selecciona de la lista que comprende: arcilla blanca, pasta de loza calcárea, dolomita, feldespato, caolinita, halloisita, ¡Hita, clorita, vermiculita, montmorillonita, sepiolita-paligorskita y cualquier combinación de las anteriores.
3. Composición según cualquiera de las reivindicaciones 1 ó 2, donde la arcilla es arcilla blanca.
4. Composición según cualquiera de las reivindicaciones 1 a 3, donde las cenizas tienen un tamaño inferior a 0,25 mm de diámetro.
5. Composición según cualquiera de las reivindicaciones 1 a 4, donde la arcilla está en un porcentaje de entre 90% y 95% en peso con respecto a la composición final.
6. Composición según cualquiera de las reivindicaciones 1 a 5, donde ceniza está en un porcentaje de entre 5% y 10% en peso con respecto a la composición final.
7. Composición según cualquiera de las composiciones 1 a 6, donde las cenizas proceden de persona o animal.
8. Composición según cualquiera de las reivindicaciones 1 a 7, donde dicha composición está cocida, se encuentra en forma sólida y además comprende una capa externa de esmalte.
9. Composición según la reivindicación 8, donde la capa de esmalte es un resina seleccionada de la siguiente lista resina epoxi, resina fotosensible o cualquier combinación de las anteriores.
10. Elemento o figura que comprende una composición según cualquiera de las reivindicaciones 1 a 9.
11. Elemento o figura que comprende una composición según cualquiera de las reivindicaciones 8 o 9 y que se encuentra engarzada en un soporte.
12. Elemento o figura según cualquiera de las reivindicaciones 10 o 11 , donde el elemento o figura es tridimensional.
13. Uso de la composición descrita según cualquiera de las reivindicaciones 1 a 7, como tinta de una impresora 3D para obtener un elemento o figura tridimensional.
14. Uso de la composición descrita según cualquiera de las reivindicaciones 1 a 9 como elemento o figura cerámica.
15. Uso de la composición descrita según cualquiera de las reivindicaciones 13 o 14 donde el elemento o figura tridimensional, o figura cerámica, ya esmaltada se engarza en los soportes correspondientes.
PCT/ES2018/070807 2017-12-19 2018-12-17 Composición que comprende cenizas de cremación WO2019122478A1 (es)