WO2019065542A1 - 熱間鍛造材の製造方法 - Google Patents

熱間鍛造材の製造方法 Download PDF

Info

Publication number
WO2019065542A1
WO2019065542A1 PCT/JP2018/035214 JP2018035214W WO2019065542A1 WO 2019065542 A1 WO2019065542 A1 WO 2019065542A1 JP 2018035214 W JP2018035214 W JP 2018035214W WO 2019065542 A1 WO2019065542 A1 WO 2019065542A1
Authority
WO
WIPO (PCT)
Prior art keywords
hot forging
heating
mold
forging
temperature
Prior art date
Application number
PCT/JP2018/035214
Other languages
English (en)
French (fr)
Inventor
翔悟 鈴木
友典 上野
信一 小林
▲高▼橋　正一
孝憲 松井
Original Assignee
日立金属株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日立金属株式会社 filed Critical 日立金属株式会社
Priority to CN201880063368.9A priority Critical patent/CN111163876B/zh
Priority to EP18860729.5A priority patent/EP3689492B1/en
Priority to US16/650,270 priority patent/US11278953B2/en
Priority to JP2019538705A priority patent/JP6635326B2/ja
Publication of WO2019065542A1 publication Critical patent/WO2019065542A1/ja

Abstract

ダブルバレリング状の鍛造欠陥の発生を防止可能な熱間鍛造材の製造方法を提供する。　上型と下型の両方がＮｉ基超耐熱合金製であり、熱間鍛造用素材を前記下型と前記上型とにより大気中で押圧することにより熱間鍛造材とする熱間鍛造材の製造方法において、前記熱間鍛造用素材を加熱炉内で１０００～１１５０℃の範囲内の加熱温度に加熱する素材加熱工程と、前記熱間鍛造用素材を把持する把持治具を前記熱間鍛造用素材加熱温度マイナス５０℃～プラス１００℃の温度範囲内に加熱する治具加熱工程と、前記上型と前記下型を９５０～１１００℃の範囲内の加熱温度に加熱する金型加熱工程と、マニピュレータに取り付けた前記把持治具を用いて前記熱間鍛造用素材を前記下型上まで搬送する搬送工程とを含む熱間鍛造材の製造方法。

Description

熱間鍛造材の製造方法
　本発明は、加熱した金型を用いて行われる熱間鍛造材の製造方法に関する。
　耐熱合金の鍛造において、鍛造用素材は変形抵抗を低くするため所定の温度に加熱される。耐熱合金は高温でも高い強度を有するため、その鍛造に用いる熱間鍛造用金型には高温での高い機械的強度が必要とされる。また、熱間鍛造において熱間鍛造用金型の温度が室温と同程度である場合、抜熱により鍛造用素材の加工性が低下するため、例えばＡｌｌｏｙ７１８やＴｉ合金等の難加工性材の鍛造は、素材とともに熱間鍛造用金型を加熱して行われる。従って、熱間鍛造用金型は、鍛造用素材が加熱される温度と同じかもしくはそれに近い高温で、高い機械的強度を有したものでなければならない。この要求を満たす熱間鍛造用金型として、大気中での金型温度１０００℃以上の熱間鍛造に使用できるＮｉ基超耐熱合金が提案されている（例えば、特許文献１～３参照）。
　難加工性材の熱間鍛造には、鍛造用素材と近い温度に加熱した金型を用いて、例えば０．０１～０．１／ｓｅｃ程度のひずみ速度で鍛造するホットダイ鍛造や、鍛造用素材と等温に加熱した金型を用いることでホットダイ鍛造より遅い、例えば、０．００１／ｓｅｃ以下のひずみ速度での鍛造が可能な恒温鍛造が適用される。特許文献１乃至３で提案された前記Ｎｉ基超耐熱合金製の金型を用いて大気中で行う熱間鍛造として、恒温鍛造の実施例が非特許文献１に、ホットダイ鍛造の実施例が特許文献４に示されている。熱間鍛造材を最終形状に近い形状とすることで歩留り向上と加工費低減が可能となるため、鍛造用素材費の点では、熱間鍛造材に金型による抜熱に伴う不均一変形部が存在しない恒温鍛造が有利である。一方、金型の温度が低い程金型の高温強度が高くなり型寿命が向上するため、金型費の点では、金型温度が比較的低いホットダイ鍛造が有利である。熱間鍛造材の組織に影響を及ぼすひずみ速度等の鍛造条件が許容範囲であるならば、ホットダイ鍛造と恒温鍛造との選択では、これらの費用に設備費や鍛造工程数等に依存する作業費などを加えた製造費が低い方が選ばれる。
特開昭６２－５０４２９号公報 特公昭６３－２１７３７号公報 米国特許第４７４０３５４号明細書 特開平０３－１７４９３８号公報
Transactions　of　the　Iron　and　Steel　Institute　of　Japan　Vol.28(1988)　No.11　P.958-964
　特許文献２の実施例において従来合金として示されているＭａｒ－Ｍ２００等のＮｉ基合金を金型に用いた場合の、実機での難加工性材のホットダイ鍛造における一般的な金型の上限温度は、金型寿命の点から、９００℃程度である。難加工性材の一般的な加熱温度は１０００～１１５０℃であるため、金型温度は熱間鍛造用素材より１００～２５０℃低い。熱間鍛造材を最終形状に近い形状とするためには金型温度と熱間鍛造用素材の温度差は小さい方が有利であり、特許文献１乃至３で提案されているような、高温強度に優れ、金型耐用寿命の点で有利なＮｉ基超耐熱合金をホットダイ鍛造の金型に適用することで、熱間鍛造用素材との温度差を小さくすることができる。金型温度を向上させることによる効果を十分に得るために、この場合の金型温度は９５０℃以上である必要がある。　加熱炉内で加熱した熱間鍛造用素材の表面付近の温度は搬送中に低下する。熱間鍛造用素材と金型加熱温度の差が小さい場合、搬送中に表面付近が温度低下した熱間鍛造用素材を下型に載置すると、熱間鍛造用素材の表面付近の温度は金型の加熱温度以下となる。この状態で鍛造すると、熱間鍛造中に上型と下型（一対の上型と下型のことを「金型」と記す）と接触する熱間鍛造用素材の上下底面付近では金型によって加熱されることで温度が複熱する一方、金型と接触していない熱間鍛造用素材の側面は温度が低下したままとなる。このような温度むらのある状態で熱間鍛造を行うと変形抵抗の比較的低い上下底面付近が優先的に変形することによる、熱間鍛造材の側面におけるダブルバレリング状の鍛造欠陥の生じる可能性が高くなる。なお、本発明で言う上下底面とは、熱間鍛造用素材の上型と接する面、及び下型と接する面のことを言う。また、本発明で言うダブルバレリング状の鍛造欠陥とは、円柱状の鍛造用素材に対する一般的な据込み鍛造後の鍛造材の側面において、熱間鍛造用素材が外周方向に曲面状に膨出することで生じるバレリング部が上下底面付近に生じることでできる、鍛造材の側面における楕円状の凹みのことを言う。図１に、熱間鍛造工程も含め、本発明で言うダブルバレリング状の鍛造欠陥を図示する。一般的には、この鍛造欠陥が生じると、熱間鍛造材における最終形状以外の切り捨て部分の体積が増加するため歩留まりが低下する。
　先述した課題は特に大型の鍛造材を得る場合に顕著になる傾向がある。そのため、高温強度に優れた、金型耐用寿命で有利なＮｉ基超耐熱合金を金型に適用したホットダイ鍛造では、金型材の変更とともに、ダブルバレリング状の鍛造欠陥の生じない製造方法を適用する必要が有る。
　そのための第１の方法として、熱間鍛造用素材の表面温度の搬送中の低下は搬送時間の短縮により抑制可能である。しかしながら、金型温度９００℃以下の一般的なホットダイ鍛造でも搬送時間の短縮は図られている。そのため、搬送時間の短縮以外の方法を検討する方が効果的である。
　特許文献４には、鍛造用素材を鍛造温度以上の融点を有する金属材で被覆して鍛造するホットダイ鍛造が示されている。この方法を用いれば金型温度９５０℃以上でもダブルバレリング状の鍛造欠陥が生じないホットダイ鍛造を実施できる可能性がある。しかし、この特許文献４の方法では鍛造前の熱間鍛造用素材への被覆と鍛造後の被覆除去工程が必要となり、生産性が低下する。
　金型温度が９５０℃以上のホットダイ鍛造において、生産性の低下を招かずにダブルバレリング状の鍛造欠陥の発生を防止する熱間鍛造材の製造方法の提案は見当たらないのが現実である。
　本発明の目的は、ダブルバレリング状の鍛造欠陥の発生を防止可能な熱間鍛造材の製造方法を提供することである。
　本発明者は、金型温度が９５０℃以上であるホットダイ鍛造におけるダブルバレリング状の鍛造欠陥の発生を検討し、加熱した把持治具を用いた搬送工程の適用による搬送中の温度低下の抑制により、生産性を維持しつつ、ダブルバレリング状の鍛造欠陥の発生を防止することができることを見出し本発明に到達した。
　すなわち本発明は、上型と下型の両方がＮｉ基超耐熱合金製であり、熱間鍛造用素材を前記下型と前記上型とにより大気中で押圧することにより熱間鍛造材とする熱間鍛造材の製造方法において、前記熱間鍛造用素材を加熱炉内で１０００～１１５０℃の範囲内の加熱温度に加熱する素材加熱工程と、前記熱間鍛造用素材を把持する把持治具を前記熱間鍛造用素材加熱温度マイナス５０℃～プラス１００℃の温度範囲内に加熱する治具加熱工程と、前記上型と前記下型とを９５０～１１００℃の範囲内の加熱温度に加熱する金型加熱工程と、前記素材加熱工程と前記治具加熱工程と前記金型加熱工程とが終了した後に、マニピュレータに取り付けた前記把持治具を用いて前記熱間鍛造用素材を前記下型上まで搬送する搬送工程とを含む熱間鍛造材の製造方法である。
　また、前記熱間鍛造用素材の加熱温度から前記上型と前記下型の加熱温度を引いた値が５０℃以上であることが好ましい。
　また、前記Ｎｉ基超耐熱合金の組成は、質量％で、Ｗ：７．０～１５．０％、Ｍｏ：２．５～１１．０％、Ａｌ：５．０～７．５％、選択元素として、Ｃｒ：７．５％以下、Ｔａ：７．０％以下、Ｔｉ：７．０％以下、Ｎｂ：７．０％以下、Ｃｏ：１５．０％以下、Ｃ：０．２５％以下、Ｂ：０．０５％以下、Ｚｒ：０．５％以下、Ｈｆ：０．５％以下、希土類元素：０．２％以下、Ｙ：０．２％以下、Ｍｇ：０．０３％以下、残部はＮｉ及び不可避的不純物であることが好ましい。なお、前述した選択元素の含有量の下限は０％を含むものである。
　また、前記把持治具は、前記熱間鍛造用素材を把持する部分に突起部を有するとともに、前記熱間鍛造用素材の周囲を囲むカバー部を有することが好ましい。
　また、前記熱間鍛造用素材が前記素材加熱工程において加熱される前に、前記熱間鍛造用素材の表面に液体潤滑剤を塗布することによって潤滑被覆を形成することが好ましい。
　また本発明は、熱間鍛造用素材を鍛造温度に加熱する素材加熱工程と、前記熱間鍛造用素材を把持するための把持治具を加熱する治具加熱工程と、Ｎｉ基超耐熱合金製の上型および下型からなる金型を加熱する金型加熱工程と、前記治具加熱工程によって加熱された前記把持治具をマニピュレータに取り付け、前記マニピュレータに取り付けられた前記把持治具を用いて前記素材加熱工程によって加熱された前記熱間鍛造用素材を搬送し、前記金型加熱工程によって加熱された前記下型上に、前記熱間鍛造用素材の表面温度が前記金型の表面温度以上の状態で載置する搬送工程と、前記下型上に搬送された前記熱間鍛造用素材を、前記金型加熱工程によって加熱された前記金型により大気中で押圧することにより熱間鍛造材を得る熱間鍛造工程とを有する熱間鍛造材の製造方法である。
　本発明によれば、ダブルバレリング状の鍛造欠陥の発生を防止することができる。
熱間鍛造工程により生じるダブルバレリング状の鍛造欠陥を示した図である。 把持治具の概念図を示した模式図である。 本発明に係る熱間鍛造材の製造方法の各工程と各工程間の流れを例示した模式図である。 本発明に係る熱間鍛造材の製造方法の適用によるダブルバレリング状の鍛造欠陥の防止効果を示した模式図である。
　以下に、本発明を詳しく説明する。
　＜熱間鍛造用素材＞
　最初に、本発明の熱間鍛造材の製造方法で用いる熱間鍛造用素材について説明する。
　本発明は難加工性材からなる熱間鍛造用素材の熱間鍛造材の製造に好適である。難加工性材としてはＮｉを主成分とするＮｉ基超耐熱合金やＴｉを主成分とするＴｉ合金等が代表的である。なお、本発明で言う主成分とは、質量％で最も含有量の高い元素のことを指す。熱間鍛造用素材の形状と内部組織は特に限定しないが、一般的に熱間鍛造用素材用として好適な形状や内部組織であればよい。なお、本発明で言う「Ｎｉ基超耐熱合金」とは、超合金、耐熱超合金、superalloyとも称される６００℃以上の高温領域で使用されるＮｉ基の合金であって、γ’などの析出相によって強化される合金を言う。
　本発明における熱間鍛造用素材の形状は、ダブルバレリング状の鍛造欠陥の発生を防止する点から、熱間鍛造用素材を金型に載置した時の素材の高さを素材の最大幅（直径）で割った値が３．０以下であることが好ましく、２．８以下であることがより好ましい。この値が３．０を超えると、ダブルバレリング状の鍛造欠陥の他に、座屈などの別の鍛造欠陥の生じる可能性が高くなるからである。
　また、熱間鍛造用素材の表面は、スケールが形成された表面状態でもよいが、潤滑剤を均一に塗布するため、機械加工後に脱脂洗浄した金属面であることが好ましい。
　また、熱間鍛造時においては、熱間鍛造用素材表面と金型が高温且つ高い応力負荷状態で接触するため、成形荷重の低減、金型と鍛造用素材間の拡散結合による焼き付き防止、金型の摩耗の抑制等のため潤滑剤ないしは離型剤が用いられる。本発明のような、大気中での金型温度９５０℃以上での熱間鍛造では、潤滑剤ないしは離型剤として、グラファイト系の潤滑剤、窒化硼素系の離型剤、ガラス系の潤滑剤兼離型剤等が使用される。
　本発明では、成形荷重低減の点と塗布作業性の点から、水などの分散剤にガラスフリットを分散させたガラス系液体潤滑剤を使用することが好ましい。ガラスフリットは、成形荷重低減の点で有利な粘度を有するホウケイ酸ガラスであることが好ましい。また、熱間鍛造用素材と金型における酸化腐食を助長する化学反応を抑制する点から、この液体潤滑剤のガラスのアルカリ成分含有量は低い方が好ましい。
　前述したガラス系液体潤滑剤は、例えば、熱間鍛造用素材全面へのスプレー、刷毛塗り、浸漬による塗布や、金型表面へのスプレー、刷毛塗りなどにより、熱間鍛造用素材の表面に付与され、熱間鍛造用素材と金型の間に供給される。このうち、潤滑被膜の厚さの制御の点からスプレーによる塗布が塗布方法として最も好ましい。潤滑剤を塗布する前の熱間鍛造用素材は、液体潤滑剤に含まれる水等の分散剤の揮発を促進するため、塗布作業の前に室温以上の温度に加熱されていても良い。
　塗布によるガラス系潤滑被膜の厚さは、鍛造中における連続的な潤滑膜の形成のため１００μｍ以上が好ましい。１００μｍ未満では潤滑膜が部分的に破損し、熱間鍛造用素材と金型の直接接触による潤滑性の悪化に加え、金型の摩耗や焼き付きが生じやすくなるおそれがある。また、熱間鍛造用素材の搬送中の温度低下を抑制する点では、潤滑被膜の厚さは厚い方が好ましい。しかし、潤滑被膜の厚さが厚すぎると、複雑な形状の型彫り面を有する金型を用いた鍛造の場合、ガラスの型彫り面への堆積による鍛造品の寸法公差外れが生じるおそれがある。そのため、潤滑被膜の厚さは５００μｍ以下であることが好ましい。
　＜金型＞
　次に本発明で用いる金型について説明する。
　本発明で用いる金型の材質は、高温強度に優れ金型耐用寿命の点で有利なＮｉ基超耐熱合金とする。高温強度に優れた金型の材質として、Ｎｉ基超耐熱合金の他にもファインセラミックスとＭｏ基合金をあげることができる。しかし、ファインセラミックス製の金型は、そのコストが高額である。また、Ｍｏ基合金製の金型であると、不活性雰囲気で使用しなければならないため専用の大規模かつ特殊な設備が必要となる。そのため、これらはＮｉ基超耐熱合金に比べ製造コストの点で不利である。前記の理由から本発明で用いる金型の材質をＮｉ基超耐熱合金とする。
　前記高温強度に優れたＮｉ基超耐熱合金の中でも、下記で説明する合金組成を有するＮｉ基超耐熱合金は高温圧縮強度が優れているだけなく、高温の大気雰囲気中においても熱間鍛造用の金型として十分に使用できるだけの強度を有する合金である。
　以下に、好ましい熱間鍛造用金型用のＮｉ基超耐熱合金の組成について説明する。なお、化学組成の単位は質量％である。好ましいＮｉ基超耐熱合金の組成は、質量％で、Ｗ：７．０～１５．０％、Ｍｏ：２．５～１１．０％、Ａｌ：５．０～７．５％、選択元素として、Ｃｒ：７．５％以下、Ｔａ：７．０％以下、Ｔｉ：７．０％以下、Ｎｂ：７．０％以下、Ｃｏ：１５．０％以下、Ｃ：０．２５％以下、Ｂ：０．０５％以下、Ｚｒ：０．５％以下、Ｈｆ：０．５％以下、希土類元素：０．２％以下、Ｙ：０．２％以下、Ｍｇ：０．０３％以下、残部はＮｉ及び不可避的不純物である。
　＜Ｗ：７．０～１５．０％＞
　Ｗは、オーステナイトマトリックスに固溶するとともに、析出強化相であるＮｉ３Ａｌを基本型とするガンマプライム相（γ’相）にも固溶して合金の高温強度を高める。一方、Ｗは、耐酸化性を低下させる作用や、ＴＣＰ(Topologically　Close　Packed)相等の有害相を析出しやすくする作用を有する。高温強度を高め、且つ、耐酸化性の低下と有害相の析出をより抑制する観点から、本発明におけるＮｉ基超耐熱合金中のＷの含有量は７．０～１５．０％とする。Ｗの効果をより確実に得るための好ましい下限は１０．０％であり、好ましい上限は１２．０％であり、更に好ましい上限は１１．０％である。
　＜Ｍｏ：２．５～１１．０％＞
　Ｍｏは、オーステナイトマトリックスに固溶するとともに、析出強化相であるＮｉ３Ａｌを基本型とするガンマプライム相にも固溶して合金の高温強度を高める。一方、Ｍｏは、耐酸化性を低下させる作用を有する。高温強度を高め、且つ、耐酸化性の低下をより抑制する観点から、本発明におけるＮｉ基超耐熱合金中のＭｏの含有量は２．５～１１．０％とする。なお、Ｗと後述するＴａ、Ｔｉ、Ｎｂの添加に伴うＴＣＰ相等の有害相の析出を抑制するため、Ｗと後述するＴａ、Ｔｉ、Ｎｂ含有量との兼ね合いで好ましいＭｏの下限を設定するのが好ましく、Ｔａを含有する場合のＭｏの効果をより確実に得るための好ましい下限は４．０％であり、更に好ましい下限は４．５％である。一方、Ｔａ、Ｔｉ、Ｎｂを添加しない場合のＭｏの好ましい下限は７．０％とすると良く、更に好ましい下限は９．５％である。また、好ましいＭｏの上限は１０．５であり、更に好ましい上限は、１０．２％である。
＜Ａｌ：５．０～７．５％＞
　Ａｌは、Ｎｉと結合してＮｉ３Ａｌからなるガンマプライム相を析出し、合金の高温強度を高め、合金の表面にアルミナの被膜を生成し、合金に耐酸化性を付与する作用を有する。一方、Ａｌの含有量が多過ぎると、共晶ガンマプライム相を過度に生成し、合金の高温強度を低める作用もある。耐酸化性及び高温強度を高める観点から、本発明におけるＮｉ基超耐熱合金中のＡｌの含有量は５．０～７．５％とする。Ａｌの効果をより確実に得るための好ましい下限は５．５％であり、更に好ましい下限は６．１％である。また、好ましいＡｌの上限は６．７％であり、更に好ましい上限は６．５％である。
　＜Ｃｒ：７．５％以下＞
　本発明におけるＮｉ基超耐熱合金は、Ｃｒを含有することができる。Ｃｒは、合金表面もしくは内部におけるアルミナの連続層の形成を促進し、合金の耐酸化性を向上させる作用を有する。恒温鍛造に比べて熱間鍛造材の寸法公差が大きく、また、金型加熱温度の低いホットダイ鍛造の場合は、耐酸化性の重要性が比較的低くＣｒの添加は必須でないため、本発明におけるＮｉ基超耐熱合金ではＣｒは必要に応じて添加される。また、Ｃｒの添加が必要な場合は、７．５％を超える範囲のＣｒの添加は１０００℃以上における合金の圧縮強度を低下させるため避けなければならない。Ｃｒの効果を確実に得るための好ましい下限は０．５％であり、更に好ましい下限は１．３％であり、好ましいＣｒの上限は３．０％である。
　＜Ｔａ：７．０％以下＞
　本発明におけるＮｉ基超耐熱合金は、Ｔａを含有することができる。Ｔａは、Ｎｉ３Ａｌからなるガンマプライム相にＡｌサイトを置換する形で固溶して合金の高温強度を高めるとともに、合金表面に形成された酸化物皮膜の密着性と耐酸化性を高め、合金の耐酸化性を向上させる作用を有する。恒温鍛造に比べて熱間鍛造材の寸法公差が大きく、また、金型加熱温度の低いホットダイ鍛造の場合は、耐酸化性と高温強度の重要性が比較的低いためＴａの添加は必須でない。加えて、Ｔａは高価であり多量に添加すると金型費が高額となる。そのため、本発明におけるＮｉ基超耐熱合金では、Ｔａは必要に応じて添加される。また、Ｔａの添加が必要な場合は、Ｔａの含有量が多すぎると、ＴＣＰ相等の有害相を析出しやすくする作用や、共晶ガンマプライム相を過度に生成し、合金の高温強度を低める作用もあるため、７．０％を超える範囲の添加は避けなければならない。Ｔａの効果を確実に得るための好ましい下限は０．５％であり、更に好ましい下限は２．５％である。好ましいＴａの上限は６．５％である。なお、後述するＴｉ乃至はＮｂとともにＴａを含有する場合は、これらの元素の含有量の総和が大きいと有害相の析出や共晶ガンマプライム相の過度な生成に伴い高温強度が低下するため、これらの元素の含有量の総和は７．０％以下であることが好ましい。
　＜Ｔｉ：７．０％以下＞
　本発明におけるＮｉ基超耐熱合金は、Ｔｉを含有することができる。Ｔｉは、Ｔａと同様にＮｉ３Ａｌからなるガンマプライム相にＡｌサイトを置換する形で固溶して、合金の高温強度を高める。また、Ｔａに比べて安価な元素であるため金型コストの点で有利である。恒温鍛造に比べて熱間鍛造材の寸法公差が大きく、また、金型加熱温度の低いホットダイ鍛造の場合は、高温強度の重要性が比較的低いためＴｉの添加は必須でない。そのため、本発明におけるＮｉ基超耐熱合金では、Ｔｉは必要に応じて添加される。また、Ｔｉの添加が必要な場合は、Ｔｉの含有量が多すぎると、ＴＣＰ相等の有害相を析出しやすくする作用や、共晶ガンマプライム相を過度に生成し、合金の高温強度を低める作用もあるため、７．０％を超える範囲の添加は避けなければならない。Ｔｉの効果を確実に得るための好ましい下限は０．５％であり、更に好ましい下限は２．５％である。好ましいＴｉの上限は６．５％である。なお、先述したＴａ乃至は後述するＮｂとともにＴｉを含有する場合は、これらの元素の含有量の総和が大きいと有害相の析出や共晶ガンマプライム相の過度な生成に伴い高温強度が低下するため、これらの元素の含有量の総和は７．０％以下であることが好ましい。
　＜Ｎｂ：７．０％以下＞
　本発明におけるＮｉ基超耐熱合金は、Ｎｂを含有することができる。Ｎｂは、Ｔａ、Ｔｉと同様にＮｉ３Ａｌからなるガンマプライム相にＡｌサイトを置換する形で固溶して、合金の高温強度を高める。また、Ｔａに比べて安価な元素であるため金型コストの点で有利である。恒温鍛造に比べて熱間鍛造材の寸法公差が大きく、また、金型加熱温度の低いホットダイ鍛造の場合は、高温強度の重要性が比較的低いためＮｂの添加は必須でない。そのため、本発明におけるＮｉ基超耐熱合金では、Ｎｂは必要に応じて添加される。また、Ｎｂの添加が必要な場合は、Ｎｂの含有量が多すぎると、ＴＣＰ相等の有害相を析出しやすくする作用や、共晶ガンマプライム相を過度に生成し、合金の高温強度を低める作用もあるため、７．０％を超える範囲の添加は避けなければならない。Ｎｂの効果を確実に得るための好ましい下限は０．５％であり、更に好ましい下限は２．５％である。好ましいＴｉの上限は６．５％である。なお、先述したＴａ乃至はＴｉとともにＮｂを含有する場合は、これらの元素の含有量の総和が大きいと有害相の析出や共晶ガンマプライム相の過度な生成に伴い高温強度が低下するため、これらの元素の含有量の総和は７．０％以下であることが好ましい。
　＜Ｃｏ：１５．０％以下＞
　本発明におけるＮｉ基超耐熱合金は、Ｃｏを含有することができる。Ｃｏは、オーステナイトマトリックスに固溶し、合金の高温強度を高める。恒温鍛造に比べて熱間鍛造材の寸法公差が大きく、また、金型加熱温度の低いホットダイ鍛造の場合は、高温強度の重要性が比較的低いためＣｏの添加は必須でない。そのため、本発明におけるＮｉ基超耐熱合金では、Ｃｏは必要に応じて添加される。また、Ｃｏの含有量が多すぎると、ＣｏはＮｉに比べて高価な元素であるため金型コストを高め、また、ＴＣＰ相等の有害相を析出しやすくする作用もある。そのため、１５．０％を超える範囲の添加は避けなければならない。Ｃｏの効果を確実に得るための好ましい下限は０．５％であり、更に好ましい下限は２．５％である。好ましい上限は１３．０％である。
　＜Ｃ及びＢ＞
　本発明におけるＮｉ基超耐熱合金は、Ｃ、Ｂから選択される１種または２種の元素を含有することができる。Ｃ、Ｂは、合金の結晶粒界の強度を向上させ、高温強度や延性を高める。そのため、本発明におけるＮｉ基超耐熱合金では、Ｃ、Ｂから選択される１種または２種の元素も必要に応じて添加される。また、Ｃ、Ｂの含有量が多すぎると、粗大な炭化物やホウ化物が形成され、合金の強度を低下させる作用もある。合金の結晶粒界の強度を高め、粗大な炭化物やホウ化物の形成を抑制する観点から、本発明におけるＣの含有量の上限は０．２５％、Ｂの含有量の上限は０．０５％である。Ｃの効果を確実に得るための好ましい下限は０．００５％であり、更に好ましい下限は０．０１％である。また、好ましい上限は０．１５％である。Ｂの効果を確実に得るための好ましい下限は０．００５％であり、更に好ましい下限は０．０１％である。また、好ましい上限は０．０３％である。
　経済性や高温強度が特に必要とされる場合はＣのみを添加することが好ましく、延性が特に必要とされる場合はＢのみを添加することが好ましい。高温強度と延性の両者が特に必要とされる場合は、ＣとＢを同時に添加することが好ましい。
　＜その他の任意の添加元素＞
　本発明におけるＮｉ基超耐熱合金は、Ｚｒ、Ｈｆ、希土類元素、Ｙ及びＭｇから選択される１種または２種以上の元素を含有することができる。Ｚｒ、Ｈｆ、希土類元素、Ｙは、合金表面に形成される酸化物被膜の結晶粒界への偏析によりその粒界での金属イオンと酸素の拡散を抑制する。この粒界拡散の抑制は、酸化物被膜の成長速度を低下させ、また、酸化物被膜の剥離を促進するような成長機構を変化させることで酸化物被膜と合金との密着性を向上させる。すなわち、これらの元素は、前述した酸化物被膜の成長速度の低下と酸化物被膜の密着性の向上によって合金の耐酸化性を向上させる作用を有する。
　また、合金中にはＳ（硫黄）が不純物として少なからず含有される。このＳは、合金表面に形成される酸化物被膜と合金との界面への偏析とそれらの化学結合の阻害により酸化物被膜の密着性を低下させる。Ｍｇは、Ｓと硫化物を形成し、Ｓの偏析を防止することで酸化物被膜の密着性を向上させ、合金の耐酸化性を向上させる作用を有する。
　なお、前記希土類元素のなかでもＬａを用いるのが好ましい。Ｌａは耐酸化性の向上の効果が大きいためである。Ｌａは前述した拡散の抑制に加えてＳの偏析を防止する作用も有し、且つ、それらの作用が優れているため、希土類元素のなかではＬａを選択するのが良い。また、ＹにおいてもＬａと同じ作用効果を奏するためＹの添加も好ましく、ＬａとＹを含む２種以上を用いるのが特に好ましい。
　耐酸化性に加えて優れた機械的特性も必要な場合は、ＨｆまたはＺｒを用いるのが好ましく、Ｈｆを用いるのが特に好ましい。また、Ｈｆを添加する場合は、ＨｆはＳの偏析を防止する作用が小さいため、Ｈｆに加えてＭｇを同時に添加すると耐酸化性がより向上する。そのため、耐酸化性とともに機械的特性がもとめられる場合は、ＨｆとＭｇを含む２種以上の元素を用いるのが更に好ましい。
　前述したＺｒ、Ｈｆ、希土類元素、Ｙ及びＭｇの元素の添加量が多すぎると、Ｎｉ等との金属間化合物を過度に生成して合金の靱性を低下させるため、これらの任意の添加元素は好適な含有量とすることが好ましい。
　耐酸化性を高め、且つ、靱性の低下を抑制する観点から、本発明におけるＺｒ、Ｈｆのそれぞれの含有量の上限は０．５％である。Ｚｒ、Ｈｆのそれぞれの含有量の好ましい上限は０．２％であり、さらに好ましくは０．１５％であり、より好ましくは０．１％である。希土類元素、ＹはＺｒ、Ｈｆよりも靱性を低める作用が高いため、本発明におけるこれらの元素のそれぞれの含有量の上限は０．２％であり、好ましい上限は０．１％であり、さらに好ましくは０．０５％であり、より好ましくは０．０２％である。Ｚｒ、Ｈｆ、希土類元素、Ｙを含有させる場合の好ましい下限は０．００１％である。Ｚｒ、Ｈｆ、希土類元素、Ｙの含有の効果を十分に発揮する好ましい下限は０．００５％であり、更に好ましくは０．０１％以上含有するのがよい。
　また、Ｍｇについては合金に含有される不純物Ｓと硫化物を形成させるために必要な量のみ含有すればよいため、Ｍｇの含有量は０．０３％以下とする。好ましいＭｇの上限は０．０２％であり、さらに好ましくは０．０１％である。である。一方、Ｍｇ添加による効果をより確実に発揮させるには０．００５％を下限とするのがよい。
　以上説明する添加元素以外はＮｉ及び不可避的不純物である。本発明におけるＮｉ基超耐熱合金においてＮｉはガンマ相を構成する主要元素であるとともに、Ａｌ、Ｔａ、Ｔｉ、Ｎｂ、Ｍｏ、Ｗとともにガンマプライム相を構成する。また、不可避的不純物としては、Ｐ、Ｎ、Ｏ、Ｓ、Ｓｉ、Ｍｎ、Ｆｅ等が想定され、Ｐ、Ｎ、Ｏ、Ｓはそれぞれ０．００３％以下であれば含有されていてもかまわなく、また、Ｓｉ、Ｍｎ、Ｆｅはそれぞれ０．０３％以下であれば含有されていてもかまわない。また、本発明のＮｉ基合金は、Ｎｉ基耐熱合金と呼ぶこともできる。なお、前記不可避的不純物元素のうち、特にＳについては０．００１％以下とするのが好ましい。なお、前述の不純物元素の他に、特に制限すべき元素としてＣａが挙げられる。本発明で規定する組成にＣａが添加されるとシャルピー衝撃値を著しく低下させるため、Ｃａの添加は避けるべきである。
　本発明では金型の形状は制限されず、熱間鍛造用素材乃至は熱間鍛造材の形状に応じた形状を選択してよい。本発明では、作業性の向上等の点から、必要に応じて上記の合金組成を有する金型の成形面または側面の少なくとも一方の面を、酸化防止剤の塗布層を有する面とすることができる。これにより、高温での大気中の酸素と金型の母材の接触による金型表面の酸化とそれに伴うスケール飛散を防止し、作業環境の劣化及び形状劣化を防止できる。前述した酸化防止剤は、窒化物、酸化物、炭化物の何れか１種類以上でなる無機材料であることが好ましい。これは、窒化物や酸化物や炭化物の塗布層により緻密な酸素遮断膜を形成し、金型母材の酸化を防ぐためである。なお、塗布層は窒化物、酸化物、炭化物の何れかの単層でもよいし、窒化物、酸化物、炭化物の何れか２種以上の組合わせの積層構造であってもよい。更に、塗布層は窒化物、酸化物、炭化物の何れか２種以上からなる混合物であってもよい。
　次に、「素材加熱工程」、「金型加熱工程」及び「治具加熱工程」について説明する。上述したダブルバレリング状の鍛造欠陥を防止するには、（１）熱間鍛造用素材の加熱温度、（２）金型の加熱温度、（３）把持治具の加熱温度が非常に重要となる。
　本発明者は、金型温度が９５０℃以上であるホットダイ鍛造におけるダブルバレリング状の鍛造欠陥の発生を検討し、発生の主因が、搬送中の熱間鍛造用素材表面付近における温度低下と金型による素材底面付近の復熱とによる鍛造中の素材底面付近の優先的な変形であることを知見した。従って、前述の（１）～（３）を適切に管理することが重要となる。
＜素材加熱工程＞
　上述した熱間鍛造用素材を用いて、その熱間鍛造用素材を所定の温度に加熱する。以降の工程は図３にその一例を例示する。金型加熱工程と素材加熱工程と治具加熱工程とはそれぞれ同時進行で行ってもよい。しかし、搬送工程はこれらの工程が全て完了した後に行われ、鍛造工程はこの搬送工程が完了した後に行われる。
　熱間鍛造用素材は、加熱炉を用いて目的とする素材温度まで加熱される。本発明では、熱間鍛造用素材を加熱炉内で１０００～１１５０℃の範囲内の加熱温度に加熱する。この加熱によって、熱間鍛造用素材の温度は加熱温度となる。加熱時間は、熱間鍛造用素材全体が均一な温度となる時間以上であればよい。加熱温度が１０００℃未満であるとダブルバレリング状の鍛造欠陥が生じやすくなる。一方、１１５０℃を超える温度となると、熱間鍛造用素材の金属組織が粗大化する問題が生じる。なお、実際の加熱温度は、熱間鍛造用素材の材質に応じて１０００～１１５０℃の範囲内で決定すると良い。
　＜治具加熱工程＞
　後述する搬送工程に、加熱した把持治具を適用して搬送中の熱間鍛造用素材の表面付近の温度低下を抑制することで、金型温度が９５０℃以上であるホットダイ鍛造におけるダブルバレリング状の鍛造欠陥を防止することができる。これは、適当な温度に加熱した把持治具によりマニピュレータの挟持指との接触による熱間鍛造用素材の温度低下が抑制できるためである。
　熱間鍛造用素材を搬送するときに過度な温度低下を防止するには、把持治具の加熱温度の下限を熱間鍛造用素材加熱温度マイナス５０℃とする。なお、ここで熱間鍛造用素材加熱温度とは、加熱された素材温度のことであり、把持冶具の加熱温度とは、加熱された把持冶具の温度である。把持冶具の加熱温度が、熱間鍛造用素材加熱温度マイナス５０℃より低い温度域となると熱間鍛造用素材の温度低下抑制効果が損なわれる。また、熱間鍛造用素材を搬送するときにマニピュレータの挟持指との接触による熱間鍛造用素材の抜熱を防止するには、熱間鍛造用素材加熱温度以上に把持治具を加熱しておくのが好ましく、より確実にダブルバレリング状の鍛造欠陥を防止することができる。なお、把持治具の加熱温度の上限は熱間鍛造用素材加熱温度プラス１００℃とする。これを超えて把持治具を加熱しても、より一層のダブルバレリング状の鍛造欠陥を防止する効果は見込めないだけでなく、把持治具の素材の強度が低下することで把持治具の寿命が低下する。
　なお、把持治具は熱間鍛造用素材の加熱温度と同程度の温度に加熱されるため、耐熱合金からなるものが好ましい。本発明では把持治具の素材の制限はないが、耐熱性に優れたＮｉ基合金であることが好ましい。また、把持治具の加熱は通常の加熱炉を用いれば良く、例えば、熱間鍛造用素材の加熱温度と同じ温度に加熱する場合は同じ加熱炉で把持治具も加熱してもよい。
　なお、把持治具の形状は、図２（ａ）の正面図と図２（ｂ）の平面図に示すように、熱間鍛造用素材の側面を左右一対のカバーで覆う構造を備えることが好ましい。この構造とすることで、把持治具のカバーが保温層として機能し、カバーに覆われた部分の熱間鍛造用素材側面の搬送中の温度低下を抑制することが可能となる。これにより、素材底面付近の優先的な変形を抑制する効果が向上する。また、底面付近の優先的な変形をより確実に抑制する点から素材底面付近の側面、すなわち、側面のうち上下方向の一端と他端は覆われていない方が好ましい。また、このカバー部は、熱間鍛造用素材の側面の周囲を覆う構造としているが、覆う範囲や覆う形状は適宜変更が可能である。
　また、熱間鍛造用素材を把持するため、把持治具は、図２（ｃ）に示すようにカバーと熱間鍛造用素材との間に熱間鍛造用素材を把持する部分を有する必要がある。把持する部分（熱間鍛造用素材と把持治具部とが接触する部分）は、接触圧を高め、且つ、マニピュレータによる抜熱を抑制する点から、素材と接触する面に突起部を有することが好ましい。突起部により、熱間鍛造用素材とカバーとの間に空間が生じ、これがマニピュレータによる抜熱を抑制する空気層（保温層）として機能する。本発明では突起部の形状に制限は無く、例えば、線状や点状であってもよい。
　把持治具はマニピュレータの挟持部に取り付けるため、把持治具は、図２（ｄ）に示すような挟持部挿入部を有する必要がある。挿入部の形状は、マニピュレータの挟持部の形状に応じて決定される。
　＜金型加熱工程＞
　本発明においては熱間鍛造に用いる金型についても９５０～１１００℃の範囲内の加熱温度に加熱する。この加熱によって、金型の温度は加熱温度となる。このとき、上記の好ましい組成を有するＮｉ基超耐熱合金製の金型であると大気中で目的の温度まで加熱することができる。金型の加熱温度を９５０～１１００℃としたのはホットダイ鍛造を行うのに必要な温度であることと、ダブルバレリング状の鍛造欠陥を防止するためである。この９５０～１１００℃の範囲外ではダブルバレリング状の鍛造欠陥が生じるおそれがある。金型の加熱においては、少なくとも金型の押圧面の表面温度が目的の温度となっていれば良い。
　なお、金型の加熱については、加熱炉、誘導加熱及び抵抗加熱等で所定の温度に加熱した金型を熱間鍛造装置へ搬送する方法、熱間鍛造装置に備えた加熱炉、誘導加熱装置及び抵抗加熱装置等で所定の温度に加熱する方法、または、これらを組み合わせる方法により、所定の温度とすれば良い。
　また、本発明においては、熱間鍛造用素材の加熱温度から上型と下型の加熱温度を引いた値が５０℃以上とするのが好ましい。熱間鍛造用素材の加熱温度から金型の加熱温度を差し引いた温度差が５０℃未満の場合、加熱した把持治具を用いていたとしても熱間鍛造用素材を下型に載置した時、搬送中の温度低下により熱間鍛造用素材の表面付近の温度が金型表面の温度以下となってしまう恐れがある。この状態で鍛造を行うと、鍛造中に熱間鍛造用素材の上下底面付近では金型の熱によって復熱する一方、復熱されない熱間鍛造用素材の側面の表面付近では温度が底面付近に比べて低くなり、温度むらとそれに伴う変形抵抗の差が生じ、変形抵抗の比較的低い上下底面付近が優先的に変形することによって、ダブルバレリング状の鍛造欠陥が生じうる。熱間鍛造用素材を下型に載置した時に熱間鍛造用素材の表面付近の温度が金型表面の温度以上となるように、熱間鍛造用素材の加熱温度から金型の加熱温度を差し引いた温度差を５０℃以上として、意図的に両者に温度差を設けると、より確実にダブルバレリング状の鍛造欠陥を抑制することができる。
　＜搬送工程＞
　熱間鍛造用素材は、目的とする温度に加熱された後、先述した加熱された把持治具を取り付けたマニピュレータによって加熱された下型上まで搬送される。一般的に、熱間鍛造用素材の搬送に使用されるマニピュレータとして、熱間鍛造用素材を左右から挟んで把持するための一対の挟持指を有し、且つ、所定の重量の把持と搬送が可能であるものが使用され、本発明でも同様の機能を有するマニピュレータを使用することが好ましい。
　前記治具加熱工程によって加熱された前記把持治具をマニピュレータに取り付け、前記マニピュレータに取り付けられた前記把持治具を用いて前記素材加熱工程によって加熱された前記熱間鍛造用素材を搬送し、前記金型加熱工程によって加熱された前記下型上に、熱間鍛造用素材を載置する。
　なお、マニピュレータでの搬送については、ダブルバレリング状の鍛造欠陥の発生を抑制する点から、熱間鍛造用素材の表面付近の温度が金型表面の温度未満とならないような時間で搬送を終えることが好ましい。換言すると、熱間鍛造用素材の表面温度が金型の表面温度以上の状態で載置するのが良い。
　＜熱間鍛造工程＞
　前述した所定の温度に加熱した熱間鍛造用素材及び金型（下型と上型）を用いて熱間鍛造する。熱間鍛造は、熱間鍛造用素材を下型上に載置し、その熱間鍛造用素材を下型と上型とにより大気中で押圧することにより行われる。これにより、ダブルバレリング状の鍛造欠陥の発生を防止した熱間鍛造材を得ることができる。
　以下の実施例で本発明をさらに詳しく説明する。
　まず、本発明で使用される金型材として好ましいＮｉ基超耐熱合金についての実施例を示す。真空溶解にて表１に示すＮｉ基超耐熱合金のインゴットを製造した。表１に示す組成を有するＮｉ基超耐熱合金は表２に示すような優れた高温圧縮強度の特性を有するものである。なお、表１に示すインゴットに含有されているＰ、Ｎ、Ｏはそれぞれ０．００３％以下であった。また、Ｓｉ、Ｍｎ、Ｆｅはそれぞれ０．０３％以下である。　表２に示す高温圧縮強度（圧縮耐力）は１１００℃での歪速度１０－３／ｓｅｃの条件で行ったものである。この条件で３００ＭＰａ以上あれば熱間鍛造用の金型として十分な強度を有すると言える。表２に示す表１に示した組成のＮｉ基超耐熱合金の圧縮耐力は、最も高い値で４８９ＭＰａ、最も低い値で３３２ＭＰａである。そのため、これら全てが熱間鍛造用の金型として十分な強度を有することがわかる。なお、Ｎｏ．１については歪速度１０－2／ｓｅｃと歪速度１０－1／ｓｅｃの試験条件でも試験を行い、前者での値は５７０ＭＰａ、後者での値は５８０ＭＰａであり、歪速度の比較的大きな条件でも優れた圧縮耐力を有することを確認した。また、表１に示した組成の１１００℃以下の高温圧縮強度は、表２に示した値以上となる。
　この表１に示したＮｉ基超耐熱合金から、代表例としてＮｏ．１の組成の上型と下型とを作製した。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
　表１のＮｏ．１に示したＮｉ基超耐熱合金製の金型（下型と上型）を用いて、金型加熱温度約１０４０℃、熱間鍛造用素材加熱温度約１１００℃のホットダイ鍛造を大気中で行った。把持治具の加熱温度は熱間鍛造用素材の加熱温度と同じとした。
　熱間鍛造用素材はＮｉ基超耐熱合金からなり、熱間鍛造用素材の高温圧縮強度は表２に示したＮｉ基超耐熱合金以下である。また、その形状は直径約３００ｍｍ、高さ約６００ｍｍの円柱であり、熱間鍛造用素材の表面を機械加工し、その機械加工面を、ホウケイ酸ガラスのフリットを含有した液体ガラス系潤滑剤を刷毛塗りにより塗布し、４００μｍ程度の厚みで潤滑剤を被覆した。その後、熱間鍛造用素材を所定の温度に加熱した。熱間鍛造用素材の加熱温度は１１００℃である。
　なお、用いた把持治具の形状は、図２（ａ）と図２（ｂ）に示すように、熱間鍛造用素材の側面に沿うようにカバーを設け、且つ、左右一対のカバーが熱間鍛造用素材を覆う（取り囲む）構造である。把持する部分は、接触圧を高め、且つ、マニピュレータによる抜熱を抑制する点から、素材と接触する面に突起部を有するものである。
　熱間鍛造用素材と金型の温度が所定の温度に到達した後、加熱した熱間鍛造用素材をその加熱温度と同じ温度に加熱した先述した把持治具を取り付けたマニピュレータによって加熱炉から取り出して下型上に載置した。その後、下型と上型とにより熱間鍛造用素材を押圧するホットダイ鍛造を行った。圧縮率は約７０％程度、ひずみ速度は過度な加工発熱が抑制され、また、比較的変形抵抗の低い約０．０１／ｓｅｃであり、最大荷重は約４０００トンであった。なお、熱間鍛造用素材を下型に載置した時に熱間鍛造用素材の表面付近の温度は金型表面の温度以上であった。
　また、比較のため、把持治具を用いないで、マニピュレータで直接熱間鍛造用素材を把持して搬送した以外は同条件としてホットダイ鍛造を行った。比較例の熱間鍛造用素材を下型に載置した時に熱間鍛造用素材の表面付近の温度は金型表面の温度未満であった。
　図４（ａ）に本発明のホットダイ鍛造により製造した熱間鍛造材の外観の概念図を、図４（ｂ）に比較例の熱間鍛造材の外観の概念図を示す。図４（ａ）と（ｂ）から明らかなように、本発明の把持治具を用いたホットダイ鍛造により、鍛造欠陥の生じない熱間鍛造材を得ることができる。

 

Claims (6)

  1. 　上型と下型の両方がＮｉ基超耐熱合金製であり、熱間鍛造用素材を前記下型と前記上型とにより大気中で押圧することにより熱間鍛造材とする熱間鍛造材の製造方法において、
    　前記熱間鍛造用素材を加熱炉内で１０００～１１５０℃の範囲内の加熱温度に加熱する素材加熱工程と、
    　前記熱間鍛造用素材を把持する把持治具を前記熱間鍛造用素材加熱温度マイナス５０℃～プラス１００℃の温度範囲内に加熱する治具加熱工程と、
    　前記上型と前記下型を９５０～１１００℃の範囲内の加熱温度に加熱する金型加熱工程と、
    　前記素材加熱工程と前記治具加熱工程と前記金型加熱工程とが終了した後に、マニピュレータに取り付けた前記把持治具を用いて前記熱間鍛造用素材を前記下型上まで搬送する搬送工程と、
    　を含むことを特徴とする熱間鍛造材の製造方法。
  2. 　前記熱間鍛造用素材の加熱温度から前記上型と前記下型の加熱温度を引いた値が５０℃以上であることを特徴とする請求項１に記載の熱間鍛造材の製造方法。
  3. 　前記Ｎｉ基超耐熱合金が、質量％で、Ｗ：７．０～１５．０％、Ｍｏ：２．５～１１．０％、Ａｌ：５．０～７．５％、選択元素として、Ｃｒ：７．５％以下、Ｔａ：７．０％以下、Ｔｉ：７．０％以下、Ｎｂ：７．０％以下、Ｃｏ：１５．０％以下、Ｃ：０．２５％以下、Ｂ：０．０５％以下、Ｚｒ：０．５％以下、Ｈｆ：０．５％以下、希土類元素：０．２％以下、Ｙ：０．２％以下、Ｍｇ：０．０３％以下、残部はＮｉ及び不可避的不純物の組成を有することを特徴とする請求項１または２に記載の熱間鍛造材の製造方法。
  4. 　前記把持治具が、前記熱間鍛造用素材を把持する部分に突起部を有するとともに、前記熱間鍛造用素材の周囲を囲むカバー部を有することを特徴とする請求項１乃至３のいずれか一項に記載の熱間鍛造材の製造方法。
  5. 　前記熱間鍛造用素材が前記素材加熱工程において加熱される前に、前記熱間鍛造用素材の表面に液体潤滑剤を塗布することによって潤滑被覆を形成することを特徴とする請求項１乃至４のいずれか一項に記載の熱間鍛造材の製造方法。
  6. 　熱間鍛造用素材を鍛造温度に加熱する素材加熱工程と、
    　前記熱間鍛造用素材を把持するための把持治具を加熱する治具加熱工程と、
    　Ｎｉ基超耐熱合金製の上型および下型からなる金型を加熱する金型加熱工程と、
    　前記治具加熱工程によって加熱された前記把持治具をマニピュレータに取り付け、前記マニピュレータに取り付けられた前記把持治具を用いて前記素材加熱工程によって加熱された前記熱間鍛造用素材を搬送し、前記金型加熱工程によって加熱された前記下型上に、前記熱間鍛造用素材の表面温度が前記金型の表面温度以上の状態で載置する搬送工程と、
    　前記下型上に搬送された前記熱間鍛造用素材を、前記金型加熱工程によって加熱された前記金型により大気中で押圧することにより熱間鍛造材を得る熱間鍛造工程と
    　を有する熱間鍛造材の製造方法。

     
     
PCT/JP2018/035214 2017-09-29 2018-09-21 熱間鍛造材の製造方法 WO2019065542A1 (ja)