Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C44/00—Shaping by internal pressure generated in the material, e.g. swelling or foaming ; Producing porous or cellular expanded plastics articles
  • B29C44/20—Shaping by internal pressure generated in the material, e.g. swelling or foaming ; Producing porous or cellular expanded plastics articles for articles of indefinite length
  • B29C44/28—Expanding the moulding material on continuous moving surfaces without restricting the upwards growth of the foam
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C43/00—Compression moulding, i.e. applying external pressure to flow the moulding material; Apparatus therefor
  • B29C43/32—Component parts, details or accessories; Auxiliary operations
  • B29C43/44—Compression means for making articles of indefinite length
  • B29C43/46—Rollers
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C44/00—Shaping by internal pressure generated in the material, e.g. swelling or foaming ; Producing porous or cellular expanded plastics articles
  • B29C44/34—Auxiliary operations
  • B29C44/36—Feeding the material to be shaped
  • B29C44/38—Feeding the material to be shaped into a closed space, i.e. to make articles of definite length
  • B29C44/44—Feeding the material to be shaped into a closed space, i.e. to make articles of definite length in solid form
  • B29C44/445—Feeding the material to be shaped into a closed space, i.e. to make articles of definite length in solid form in the form of expandable granules, particles or beads
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
  • B29C48/001—Combinations of extrusion moulding with other shaping operations
  • B29C48/0012—Combinations of extrusion moulding with other shaping operations combined with shaping by internal pressure generated in the material, e.g. foaming
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
  • B29C48/25—Component parts, details or accessories; Auxiliary operations
  • B29C48/94—Lubricating
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C59/00—Surface shaping of articles, e.g. embossing; Apparatus therefor
  • B29C59/02—Surface shaping of articles, e.g. embossing; Apparatus therefor by mechanical means, e.g. pressing
  • B29C59/04—Surface shaping of articles, e.g. embossing; Apparatus therefor by mechanical means, e.g. pressing using rollers or endless belts
  • B29C59/046—Surface shaping of articles, e.g. embossing; Apparatus therefor by mechanical means, e.g. pressing using rollers or endless belts for layered or coated substantially flat surfaces
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
  • C08J9/04—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof using blowing gases generated by a previously added blowing agent
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C44/00—Shaping by internal pressure generated in the material, e.g. swelling or foaming ; Producing porous or cellular expanded plastics articles
  • B29C44/34—Auxiliary operations
  • B29C44/3442—Mixing, kneading or conveying the foamable material
  • B29C44/3446—Feeding the blowing agent
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C44/00—Shaping by internal pressure generated in the material, e.g. swelling or foaming ; Producing porous or cellular expanded plastics articles
  • B29C44/34—Auxiliary operations
  • B29C44/36—Feeding the material to be shaped
  • B29C44/46—Feeding the material to be shaped into an open space or onto moving surfaces, i.e. to make articles of indefinite length
  • B29C44/50—Feeding the material to be shaped into an open space or onto moving surfaces, i.e. to make articles of indefinite length using pressure difference, e.g. by extrusion or by spraying
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
  • B29K2009/00—Use of rubber derived from conjugated dienes, as moulding material
  • B29K2009/06—SB polymers, i.e. butadiene-styrene polymers
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
  • B29K2025/00—Use of polymers of vinyl-aromatic compounds or derivatives thereof as moulding material
  • B29K2025/04—Polymers of styrene
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
  • B29K2025/00—Use of polymers of vinyl-aromatic compounds or derivatives thereof as moulding material
  • B29K2025/04—Polymers of styrene
  • B29K2025/06—PS, i.e. polystyrene
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
  • B29K2025/00—Use of polymers of vinyl-aromatic compounds or derivatives thereof as moulding material
  • B29K2025/04—Polymers of styrene
  • B29K2025/08—Copolymers of styrene, e.g. AS or SAN, i.e. acrylonitrile styrene
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
  • B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
  • B29K2105/04—Condition, form or state of moulded material or of the material to be shaped cellular or porous
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J2300/00—Characterised by the use of unspecified polymers
  • C08J2300/20—Polymers characterized by their physical structure
  • C08J2300/206—Star polymers
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J2353/00—Characterised by the use of block copolymers containing at least one sequence of a polymer obtained by reactions only involving carbon-to-carbon unsaturated bonds; Derivatives of such polymers
  • C08J2353/02—Characterised by the use of block copolymers containing at least one sequence of a polymer obtained by reactions only involving carbon-to-carbon unsaturated bonds; Derivatives of such polymers of vinyl aromatic monomers and conjugated dienes
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
  • C08J9/36—After-treatment

Definitions

• Foam products are commonly made by injection molding or by forming a large block of foam and then cutting the block into sheets. Converting processes such as convoluted cutting, hot wire, machining and contour cutting is commonly used to provide shapes on surfaces of the sheets. Such shaped surfaces typically exhibit open cells.
• Another common approach to making shaped foam is to cast a foamed film onto a casting roll to create a smooth surface foamed film.
• the film can be embossed, thereby compressing sections of the film. The cells in the compressed areas are crushed, permanently damaging the cell structure.
• a third approach to making shaped foam is by profile extrusion, wherein foamed polymer is extruded through a profile die having the desired contour shape cut in the die.
• the resulting contoured foam shape is continuous in the down web direction.
• Uses of such shaped foams include gasket seals.
• the present disclosure describes a polymeric foam layer comprising a star polymer, wherein the polymeric foam layer has a thickness up to 25,700 micrometers (in some embodiments, in a range from 100 micrometers to 1000 micrometers, 1000 micrometers to 6000 micrometers, 6000 micrometers to 12,700 micrometers or even 12,700 micrometers to 25,400 micrometers).
• the present disclosure describes a first method of making a polymeric foam layer described herein, the method comprising:
• a rotating tool roll having a major circumferential surface and an extrusion die with a die lip spaced in proximity of the tool roll to form a gap between the tool roll and the extrusion die; and introducing a star polymer comprising a foaming agent onto a portion of the major circumferential surface of the tool roll, wherein of the portion of the major circumferential surface is in proximity of the die lip to provide the star polymeric foam layer.
• the present disclosure describes a second method of making a polymeric foam layer described herein, the method comprising:
• a rotating tool roll having a major circumferential surface and an extrusion die with a die lip spaced in proximity of the tool roll to form a gap between the tool roll and the extrusion die; and introducing a star polymer comprising a gas onto a portion of the major circumferential surface of the tool roll, wherein of the portion of the major circumferential surface is in proximity of the die lip, wherein a gas is injected into the star polymer at least one of prior to or during contact of the star polymer with the portion of the major circumferential surface of the tool roll and, wherein the star polymer foams to provide the polymeric foam layer.
• the present disclosure describes a third method of making a polymeric foam layer described herein, the method comprising:
• a rotating tool roll having a major circumferential surface and an extrusion die with a die lip spaced in proximity of the tool roll to form a gap between the tool roll and the extrusion die; and introducing a star polymer comprising polymeric microspheres onto a portion of the major circumferential surface of the tool roll, wherein the portion of the major circumferential surface is in proximity of the die lip and wherein the star polymer foams to provide the polymeric foam layer.
• the present disclosure describes a fourth method of making a polymeric foam layer described herein, the method comprising:
• Exemplary uses of polymeric foam layers described herein including vibration damping and polishing applications (e.g., polishing pads useful in chemical mechanical planarization (CMP)).
• CMP chemical mechanical planarization
• FIG. 1 is an exemplary apparatus for the first method of making a polymeric foam layer described herein.
• FIG. 2 is an exemplary apparatus for the second method of making a polymeric foam layer described herein.
• FIG. 3 is an exemplary apparatus for the third method of making a polymeric foam layer described herein.
• FIG. 4 is an exemplary apparatus for the fourth method of making a polymeric foam layer described herein.
• Exemplary star polymers include styrene isoprene styrene (SIS), styrene ethylene propylene styrene (SEPS), styrene ethylene butadiene styrene (SEBS), or styrene butadiene styrene (SBS) (including mixtures thereof).
• SIS styrene isoprene styrene
• SEPS styrene ethylene propylene styrene
• SEBS styrene ethylene butadiene styrene
• SBS styrene butadiene styrene
• polymeric foam layers described herein have a glass transition temperature, T g , in a range from -125°C to 150°C (in some embodiments, in a range from -125°C to - 10°C, -10°C to 80°C, 50°C to 150°C or even 50°C to 80°C).
• T g glass transition temperature
• the glass transition temperature is determined as follows, using a differential scanning calorimeter (DSC) available under the trade designation "Q2000 DSC" from TA Instruments, New Castle, DE.
• the DSC procedure is as follows: cool sample to -180°C, temperature ramp at 10°C/min. to 300°C.
• the glass transition temperature is recorded as the inflection point in the heat flow versus temperature curve.
• polymeric foam layers described herein can be wrapped around a 1 m (in some embodiments, 75 cm, 50 cm, 25 cm, 10 cm, 5 cm, 1 cm, 5 mm, or even 1 mm) diameter rod without breaking.
• polymeric foam layers described herein have first and second opposed major surfaces, and comprising foam features extending from or into the first major surface by at least 100 (in some embodiments, in a range from 100 to 1000, 1000 to 6000, 6000 to 12,700 or even 12,700 to 25,400) micrometers.
• the features comprise at least one of the following shapes: a cone, a cube, a pyramid, a continuous rail, continuous multi-directional rails, a hemisphere, a cylinder, or a multi-lobed cylinder.
• the features have a cross-section in at least one of the following shapes: a circle, a square, a rectangle, a triangle, a pentagon, other polygon, a sinusoidal, a herringbone, or a multi-lobe.
• polymeric foam layers described herein have porosity therein having an average cell size (i.e., pore size) in a range from 10 to 3000 (in some embodiments, 10 to 2000, 10 to 1000, 10 to 500, or even 10 to 100) micrometers.
• polymeric foam layers described herein have a total porosity of at least 5 (in some embodiments, at least 10, 20, 25, 30, 40, 50, 60, or even at least 70; in some embodiments, in a range from 10 to 70, 10 to 60, or even 10 to 50) percent, based on the total volume of the polymeric foam layer.
• polymeric foam layers described herein comprise a reinforcement material (e.g., a woven, nonwoven, fibers, a mesh, or a film).
• a reinforcement material e.g., a woven, nonwoven, fibers, a mesh, or a film.
• polymeric foam layers described herein comprise at least one of glass beads, glass bubbles, glass fibers, abrasive grain, carbon black, carbon fibers, diamond particles, composite particles, nanoparticles, mineral oil, tackifier, wax nanoparticles, rubber particles or flame retardant.
• polymeric foam layers described herein comprise a thermal conductive material (e.g., BN).
• a thermal conductive material e.g., BN
• the first method of making a polymeric foam layer described herein comprises:
• a rotating tool roll having a major circumferential surface and an extrusion die with a die lip spaced in proximity of the tool roll to form a gap between the tool roll and the extrusion die; and introducing a star polymer comprising a foaming agent onto a portion of the major
• the major circumferential surface of the compression roll comprises an array of cavities.
• the major circumferential surface of the tool roll comprises an array of protrusions.
• the size and shape of the cavities or protrusions can be as desired.
• Exemplary shapes may include a cone, a cube, a pyramid, a continuous rail, continuous multi-directional rails, a hemisphere, a cylinder, and a multi-lobed cylinder.
• Exemplary cross-sections may include a circle, a square, a rectangle, a triangle, a pentagon, other polygon, a sinusoidal, a herringbone, or a multi-lobe.
• Exemplary sizes may be heights in a range from 100 micrometers to 25,400 micrometers and widths in a range from 100 micrometers to 25,400 micrometers.
• the foaming agent comprises at least one of an acid (e.g., citric acid), a bicarbonate, an
• azodicarbonamide a modified azodicarbonamide, a hydrazide, a sodium bicarbonate and citric acid blend, a dinitrosopentamethylenetetramine, p-toluenesulfonyl hydrazide, 4-4'-oxybis hydrazide, azodicarbonamide, p-toluenesulfonyl semicarbazide, 5-phenyltetrazole, a 5-phenyltetrazole analogue, diisopropylhydrazodicarboxylate, 5-phenyl-3,6-dihydro-l,3,4-oxadiazin-2-one, or sodium borohydride.
• apparatus 99 has rotating tool roll 110 having major circumferential surface 111 and extrusion die 112 with die lip 113 spaced in proximity of tool roll 110 to form gap 115 between tool roll 110 and extrusion die 112.
• Star polymer 117 comprising a foaming agent is injected onto portion 120 of major circumferential surface 111 of tool roll 110.
• Portion 120 of major circumferential surface 111 is in proximity of die lip 113 to provide star polymeric foam layer 100.
• the second method of making a polymeric foam layer described herein comprising: providing a rotating tool roll having a major circumferential surface and an extrusion die with a die lip spaced in proximity of the tool roll to form a gap between the tool roll and the extrusion die; and introducing a star polymer comprising a gas onto a portion of the major circumferential surface of the tool roll, wherein of the portion of the major circumferential surface is in proximity of the die lip, wherein a gas is injected into the star polymer at least one of prior to or during contact of the star polymer with the portion of the major circumferential surface of the tool roll and, wherein the star polymer foams to provide the polymeric foam layer.
• the major circumferential surface of the tool roll comprises an array of cavities. In some embodiments of the second method, the major circumferential surface of the tool roll comprises an array of protrusions.
• the size and shape of the cavities or protrusions can be as desired.
• Exemplary shapes may include a cone, a cube, a pyramid, a continuous rail, continuous multi-directional rails, a hemisphere, a cylinder, and multi-lobed cylinders.
• Exemplary cross-sections may include a circle, a square, a rectangle, a triangle, a pentagon, other polygon, a sinusoidal, a herringbone, or a multi-lobe.
• Exemplary sizes may be heights in a range from 100 micrometers to 25,400 micrometers and widths in a range from 100 micrometers to 25,400 micrometers.
• the gas comprises at least one of argon, carbon dioxide, nitrogen, a butane (e.g., n-butane and isobutane), a heptane (e.g., n-heptane, isoheptane, and cycloheptane), a hexane (e.g., n-hexane, neohexane, isohexane, and cyclohexane), an octane (e.g., n-octane and cyclooctane), or a pentane (e.g., n-pentane, cyclopentane, neopentane, and isopentane).
• a butane e.g., n-butane and isobutane
• a heptane e.g., n-heptane, isoheptane, and
• apparatus 199 has rotating tool roll 210 having major circumferential surface 211 and extrusion die 212 with die lip 213 spaced in proximity of tool roll 210 to form gap 215 between tool roll 210 and extrusion die 212.
• Star polymer 217 comprising a gas is injected onto portion 220 of major circumferential surface 211 of tool roll 210. Portion 220 of major circumferential surface 211 is in proximity of die lip 213. Gas 223 is injected into star polymer 217a at least one of prior to or during contact of star polymer 217 with portion 220 of major circumferential surface 211 of tool roll 210.
• Star polymer 217 foams to provide polymeric foam layer 200.
• the present disclosure describes a third method of making a polymeric foam layer described herein, the method comprising: providing a rotating tool roll having a major circumferential surface and an extrusion die with a die lip spaced in proximity of the tool roll to form a gap between the tool roll and the extrusion die; and introducing a star polymer comprising polymeric microspheres onto a portion of the major circumferential surface of the tool roll, wherein the portion of the major circumferential surface is in proximity of the die lip and wherein the star polymer foams to provide the polymeric foam layer.
• the major circumferential surface of the tool roll comprises an array of cavities.
• the major circumferential surface of the tool roll comprises an array of protrusions.
• the size and shape of the cavities or protrusions can be as desired. Exemplary shapes may include a cone, a cube, a pyramid, a continuous rail, continuous multi-directional rails, a hemisphere, a cylinder, and multi-lobed cylinders.
• Exemplary cross-sections may include a circle, a square, a rectangle, a triangle, a pentagon, other polygon, a sinusoidal, a herringbone, or a multi-lobe. Exemplary sizes may be heights in a range from 100 micrometers to 25,400 micrometers and widths in a range from 100 micrometers to 25,400 micrometers.
• the polymeric microspheres comprise expanding bubbles.
• Exemplary expanding bubbles are available, for example, under the trade designation "EXPANCEL” from AkzoNobel, Amsterdam, Netherlands or “DUALITE” from Chase Corporation, Westwood, MA.
• apparatus 299 has rotating tool roll 310 having major circumferential surface 311 and extrusion die 312 with die lip 313 spaced in proximity of tool roll 310 to form gap 315 between tool roll and extrusion die 312.
• Star polymer 317 comprising polymeric microspheres onto portion 320 of major circumferential surface 311 of tool roll 310.
• Portion 320 of major circumferential surface 311 is in proximity of die lip 312.
• Star polymer 317 foams to provide polymeric foam layer 300.
• the fourth method of making a polymeric foam layer described herein comprising: providing a rotating tool roll having a major circumferential surface and compression roll in proximity of the tool roll to form a gap between the tool roll and the compression roll;
• the major circumferential surface of the tool roll comprises an array of cavities.
• the major circumferential surface of the tool roll comprises an array of protrusions.
• the size and shape of the cavities or protrusions can be as desired. Exemplary shapes may include a cone, a cube, a pyramid, a continuous rail, continuous multi-directional rails, a hemisphere, a cylinder, and multi-lobed cylinders.
• Exemplary cross-sections may include a circle, a square, a rectangle, a triangle, a pentagon, other polygon, a sinusoidal, a herringbone, or a multi-lobe. Exemplary sizes may be heights in a range from 100 micrometers to 25,400 micrometers and widths in a range from 100 micrometers to 25,400 micrometers.
• the oil comprises at least one of a lanolin, a liquid polyacrylate, a liquid polybutene, a mineral oil, or a phthalate.
• the foaming agent comprises at least one of an acid, bicarbonate, an azodicarbonamide, a modified azodicarbonamide, a hydrazide, a sodium bicarbonate and citric acid blend,
• azodicarbonamide p-toluenesulfonyl semicarbazide
• 5 ⁇ phenyltetrazole a 5-phenyltetrazole analogue
• diisopropylhydrazodicarboxylate 5-phenyl-3 ,6-dihydro- 1 ,3 ,4-oxadiazin-2-one, or sodium borohydride.
• the gas comprises at least one of argon, carbon dioxide, nitrogen, a butane (e.g., n-butane and isobutane), a heptane (e.g., n-heptane, isoheptane, and cycloheptane), a hexane (e.g., n-hexane, neohexane, isohexane, and cyclohexane), an octane (e.g., n-octane and cyclooctane), or a pentane (e.g., n-pentane, cyclopentane, neopentane, and isopentane).
• a butane e.g., n-butane and isobutane
• a heptane e.g., n-heptane, isoheptane, and
• the polymeric microspheres comprise expanding bubbles.
• Exemplary expanding bubbles are available, for example, under the trade designations "EXPANEL” from AkzoNobel, or "DUALITE” from Chase Corporation.
• the oil is at a temperature greater than 80°C (in some embodiments, at least 90°C, 100°C, 125°C, 150°C, 175°C, or even, at least 200°C; in some embodiments, in a range from 80°C to 250°C, 100°C to 250°C, or even 100°C to 200°C).
• apparatus 399 has rotating tool roll 410 having major circumferential surface 411, extrusion die 412 with die lip 413 spaced in proximity of tool roll 410 to form gap 415 between tool roll 410 and extrusion die 412.
• Compression roll 414 in proximity of tool roll 410 to form gap 416 between tool roll 410 and compression roll 414.
• Oil 424 is injected into star polymer 417a comprising at least one of a foaming agent, a gas, or polymeric microspheres in extrusion chamber 430.
• Polymer 417 is extruded into gap 415.
• Polymer 417 foams to provide polymeric foam layer described herein 400.
• the present disclosure also described a method of providing an article, the method comprising; providing a polymeric foam layer of any A Exemplary Embodiment;
• the apparatus can be made of conventional materials and techniques known in the art for apparatuses of these general types.
• Exemplary uses of polymeric foam layers described herein including vibration damping and polishing applications (e.g., polishing pads useful in chemical mechanical planarization (CMP)).
• CMP chemical mechanical planarization
• a polymeric foam layer comprising a star polymer, wherein the polymeric foam layer has a thickness up to 25,700 (in some embodiments, in a range from 100 to 1000, 1000 to 6000 micrometers, 6000 to 12,700 or even 12,700 to 25,400) micrometers.
• SIS styrene isoprene styrene
• SEPS styrene ethylene propylene styrene
• SEBS styrene ethylene butadiene styrene
• SBS styrene butadiene styrene
• the polymeric foam layer of any of preceding A Exemplary Embodiment that can be wrapped around a 1 m (in some embodiments, 75 cm, 50 cm, 25 cm, 10 cm, 5 cm, 1 cm, 5 mm, or even 1 mm) diameter rod without breaking.
• the polymeric foam layer of any preceding A Exemplary Embodiment having first and second opposed major surfaces, and comprising foam features extending from or into the first major surface by at least 100 (in some embodiments, in a range from 100 to 1000, 1000 to 6000, 6000 to 12,700 or even 12,700 to 25,400) micrometers.
• 6A The polymeric foam layer of Exemplary Embodiment 5A, wherein the features comprise at least one of the following shapes: a cone, a cube, a pyramid, a continuous rail, continuous multi -directional rails, a hemisphere, a cylinder, or a multi-lobed cylinder.
• the polymeric foam layer of Exemplary Embodiment 5A wherein the features have a cross- section in at least one of the following shapes: a circle, a square, a rectangle, a triangle, a pentagon, other polygon, a sinusoidal, a herringbone, or a multi-lobe.
• the polymeric foam layer of any preceding A Exemplary Embodiment having porosity therein having an average cell size (i.e., pore size) in a range from 10 to 3000 (in some embodiments, 10 to 200, 10 to 1000, 10 to 5000, or even 10 to 1000) micrometers.
• reinforcement material e.g., a woven, nonwoven, fibers, a mesh, or a film.
• the polymeric foam layer of any preceding A Exemplary Embodiment comprising at least one of glass beads, glass bubbles, glass fibers, abrasive grain, carbon black, carbon fibers, diamond particles, composite particles, nanoparticles, mineral oil, tackifier, wax nanoparticles, rubber particles or flame retardant.
• the polymeric foam layer of any preceding A Exemplary Embodiment comprising a thermal conductive material (e.g., BN).
• a thermal conductive material e.g., BN
• a method of making a polymeric foam layer comprising:
• a rotating tool roll having a major circumferential surface and an extrusion die with a die lip spaced in proximity of the tool roll to form a gap between the tool roll and the extrusion die; and introducing a star polymer comprising a foaming agent onto a portion of the major
• the foaming agent comprises at least one of an acid, a bicarbonate, an azodicarbonamide, a modified azodicarbonamide, a hydrazide, a sodium bicarbonate and citric acid blend, a diiiitrosopentamethylenetetramine, p-toluenesulfonyl hydrazide, 4-4'-oxybis hydrazide, azodicarbonamide, p-toluenesulfonyl semicarbazide, 5- phenyltetrazole, a 5-phenyltetrazole analogue, diisopropylhydrazodicarboxylate, 5-phenyl-3,6-dihydro- l,3,4-oxadiazin-2-one, or sodium borohydride.
• a method of making a polymeric foam layer comprising:
• a rotating tool roll having a major circumferential surface and an extrusion die with a die lip spaced in proximity of the tool roll to form a gap between the tool roll and the extrusion die; and introducing a star polymer comprising a gas onto a portion of the major circumferential surface of the tool roll, wherein the portion of the major circumferential surface is in proximity of the die lip, wherein a gas is injected into the star polymer at least one of prior to or during contact of the star polymer with the portion of the major circumferential surface of the tool roll and, wherein the star polymer foams to provide the polymeric foam layer of any preceding A Exemplary Embodiment.
• the gas comprises at least one of argon, carbon dioxide, nitrogen, a butane (e.g., n-butane and isobutane), a heptane (e.g., n-heptane, isoheptane, and cycloheptane), a hexane (e.g., n-hexane, neohexane, isohexane, and cyclohexane), an octane (e.g., n-octane and cyclooctane), or a pentane (e.g., n-pentane, cyclopentane, neopentane, and isopentane).
• a butane e.g., n-butane and isobutane
• a heptane e.g., n-heptane, isoheptane, and
• a method of making a polymeric foam layer comprising:
• a rotating tool roll having a major circumferential surface and an extrusion die with a die lip spaced in proximity of the tool roll to form a gap between the tool roll and the extrusion die; and introducing a star polymer comprising polymeric microspheres onto a portion of the major circumferential surface of the tool roll, wherein of the portion of the major circumferential surface is in proximity of the die lip and wherein the star polymer foams to provide the polymeric foam layer of any preceding A Exemplary Embodiment.
• a method of making a polymeric foam layer comprising:
• the foaming agent comprises at least one of an acid, bicarbonate, an azodicarbonamide, a modified azodicarbonamide, a hydrazide, a sodium bicarbonate and citric acid blend, dinitrosopentamethylenetetramine, p-toluenesulfonyl hydrazide, 4-4'-oxybis hydrazide, azodicarbonamide, p-toluenesulfonyl semicarbazide, 5- phenyltetrazole, a 5-phenyltetrazole analogue, diisopropylhydrazodicarboxylate, 5-phenyl-3,6-dihydro- l,3,4-oxadiazin-2-one, or sodium borohydride.
• the gas comprises at least one of argon, carbon dioxide, nitrogen, a butane (e.g., n-butane and isobutane), a heptane (e.g., n-heptane, isoheptane, and cycloheptane), a hexane (e.g., n-hexane, neohexane, isohexane, and cyclohexane), an octane (e.g., n-octane and cyclooctane), or a pentane (e.g., n-pentane, cyclopentane, neopentane, and isopentane).
• a butane e.g., n-butane and isobutane
• a heptane e.g., n-heptane, isoheptane, and
• a method of providing an article comprising;
• Example 1 was made using an apparatus as generally shown in FIG. 1.
• the extrusion die was 20.3 cm (8 inches) wide (obtained under the trade designation "MASTERFLEX” (Model LD-40) from Cloeren, Orange, TX) configured with the die positioned on the top of the tool roll at top dead center.
• the die was orientated such that the bottom of the die was on the trailing edge of the tooling roll.
• the bottom die lip had a 3.18 mm (0.125 inch) land.
• the extruder was a 6.35 cm (2.5 inch) single screw extruder (obtained from Davis-Standard, Pawcatuck, CT).
• the die temperature set points used are shown in the Table, below.
• a single tooling roll station was used with the die mounted at the top dead center of the roll.
• the die was mounted on linear slides to move in the up and down direction.
• the roll was nominally 30.5 cm (12 inch) in diameter with a 40.6 cm (16 inch) face width.
• the tooling roll has internal water cooling with spiral wound internal channels.
• a 33.6 cm (13.25 inch) outside diameter silicone tooling shell was mounted onto the outer surface of the roll.
• the linear motion of the die was controlled by linear actuators to move the die and to control the gap between the die lip and tooling roll.
• the tooling roll had through holes drilled through the silicone shell. The straight holes were 3 mm (0.118 inch) in diameter at the surface. The holes were spaced 5 mm (0.2 inch) apart on center in both directions.
• the tooling roll was set with a cooling temperature set point of 15.6°C (60°F).
• the gap between the die lip and the tool roll surface was set at 508 micrometers (0.020 inch).
• the line speed was 0.53 meter (1.75 feet) per minute.
• a polymer was manually premixed prior to being fed into the extruder.
• the polymer was a resin blend of 68 percent by weight block co-polymer elastomer (obtained under the trade designation "KRATON 1161” from Kraton, Houston, TX), 27 percent by weight block co-polymer elastomer (obtained under the trade designation “KRATON DL12340” from Kraton) and 5 percent by weight blowing agent (obtained under the trade designation "ECOCELL H” from Polyfil Corporation, Rockaway, NJ).
• a polymeric foam layer was produced with protrusions extending from the surface with the protrusion spacing and height matching the tooling roll pattern.

Landscapes

• Engineering & Computer Science (AREA)
• Mechanical Engineering (AREA)
• Chemical & Material Sciences (AREA)
• Polymers & Plastics (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Health & Medical Sciences (AREA)
• Organic Chemistry (AREA)
• Materials Engineering (AREA)
• Extrusion Moulding Of Plastics Or The Like (AREA)
• Manufacture Of Porous Articles, And Recovery And Treatment Of Waste Products (AREA)
• Molding Of Porous Articles (AREA)
• Laminated Bodies (AREA)

Priority Applications (4)

Applications Claiming Priority (2)

Publications (1)

Family

ID=63787983

Family Applications (1)

Country Status (6)

Cited By (2)

Citations (8)

Family Cites Families (7)

• 2018
  • 2018-09-17 US US16/650,131 patent/US20200223117A1/en not_active Abandoned
  • 2018-09-17 WO PCT/IB2018/057120 patent/WO2019064120A1/en not_active Ceased
  • 2018-09-17 EP EP18782802.5A patent/EP3687756A1/en active Pending
  • 2018-09-17 CN CN201880063160.7A patent/CN111163913B/zh active Active
  • 2018-09-17 JP JP2020517900A patent/JP7273809B2/ja active Active
  • 2018-09-17 TW TW107132569A patent/TWI779097B/zh active

Patent Citations (8)

Also Published As

Similar Documents

Legal Events