WO2019012763A1 - レンズ製造方法 - Google Patents

レンズ製造方法 Download PDF

Info

Publication number
WO2019012763A1
WO2019012763A1 PCT/JP2018/015075 JP2018015075W WO2019012763A1 WO 2019012763 A1 WO2019012763 A1 WO 2019012763A1 JP 2018015075 W JP2018015075 W JP 2018015075W WO 2019012763 A1 WO2019012763 A1 WO 2019012763A1
Authority
WO
WIPO (PCT)
Prior art keywords
lens
processed
polishing
manufacturing
polishing step
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2018/015075
Other languages
English (en)
French (fr)
Inventor
隆敏 土手内
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nidec Corp
Original Assignee
Nidec Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nidec Corp filed Critical Nidec Corp
Publication of WO2019012763A1 publication Critical patent/WO2019012763A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

本発明の一態様に係るレンズ製造方法は、Ａｌ２Ｏ３からなる被加工レンズを研磨する研磨工程を備える。研磨工程は、ダイヤモンド粒子を含むダイヤモンドペーストを用いて、Ａｌ２Ｏ３からなる被加工レンズを研磨する第１研磨工程を有する。

Description

レンズ製造方法
本発明は、レンズ製造方法に関する。
従来、車体の外部に取り付けられ、外部の様子を撮影する車載用の撮像装置が知られている（例えば、特許文献１参照）。
特開２０１５－２０５６１８号公報
上述したような車体の外部に取り付けられる撮像装置の場合、飛来物が撮像装置に当たることがある。飛来物としては、例えば、車両走行中にタイヤで跳ね飛ばした小石が挙げられる。このような飛来物が撮像装置のレンズに当たった場合、レンズが傷付き、撮像画像に深刻な影響を与えることがある。そのため、傷付きにくいレンズが求められていた。　
さらに、このような傷付きにくいレンズに対する要求は、車載用の撮像装置に限らない。無人飛行体（ドローン）が備えるカメラが備えるレンズ、またはアクションカメラと呼ばれる、主として屋外で用いるために最適化された小型カメラが備えるレンズにおいても、傷付きにくいレンズが求められていた。　
発明者らは、上記課題の解決のため、レンズの材料としてサファイアガラスを研磨してレンズを製造することに思い至った。サファイアガラスは、モース硬度９と非常に硬いため、サファイアガラスから削り出したレンズは、飛来物が当たっても傷がつきにくいと考えた。　
しかし、通常のガラスレンズを作製する方法でサファイアガラスを研磨すると、研磨にムラが生じ、精度良く加工ができなかった。検討したところ、通常のガラスレンズを作製する条件と比べ研磨時間を長く設定すると、研磨時間が長くなるにつれて徐々に研磨ムラが解消する傾向があった。しかし、研磨時間を延長すると生産効率の低下につながる。　
本発明はこのような事情に鑑みてなされたものであって、高い生産効率で形状精度よくＡｌ２Ｏ３からなるレンズを製造することが可能なレンズ製造方法を提供することを目的とする。
上記の課題を解決するため、本発明の一態様によれば、Ａｌ２Ｏ３からなる被加工レンズを研磨する研磨工程を備え、前記研磨工程は、ダイヤモンド粒子を含むダイヤモンドペーストを用いて、Ａｌ２Ｏ３からなる被加工レンズを研磨する第１研磨工程を有するレンズ製造方法が提供される。
本発明によれば、高い生産効率で形状精度よくＡｌ２Ｏ３からなるレンズを製造することが可能なレンズ製造方法を提供することができる。
図１は、実施形態のレンズ製造方法で製造されるレンズの一例を示す模式図である。 図２は、実施形態のレンズ製造方法を示すフローチャートである。
以下、図１～図２を参照しながら、本発明の実施形態に係るレンズ製造方法について説明する。なお、以下の全ての図面においては、図面を見やすくするため、各構成要素の寸法、比率などは適宜異ならせてある。　
［レンズ］

　図１は、本実施形態のレンズ製造方法で製造されるレンズの一例を示す模式図である。図に示すように、本実施形態のレンズ製造方法で製造されるレンズ１は、レンズ本体１０と、コーティング膜２０と、を有している。　
（レンズ本体）

　レンズ本体１０は、平面視円形に形成されており、Ａｌ２Ｏ３の単結晶からなる。Ａｌ２Ｏ３の単結晶は、コランダム、鋼玉とも称する。Ａｌ２Ｏ３の単結晶は、モース硬さが９である。そのため、Ａｌ２Ｏ３の単結晶からなるレンズ本体１０は、硬く、表面に傷がつきにくい。　
レンズ本体１０は、後述する方法で、Ａｌ２Ｏ３単結晶の板材から削り出して作製することができる。Ａｌ２Ｏ３単結晶の板材は、サファイアガラスと称する。　
レンズ本体１０は、レンズ本体１０の光軸Ｌに沿って視た一方の面Ｓ１と、一方の面Ｓ１に対向する他方の面Ｓ２と、レンズ本体１０の周方向に延在し一方の面Ｓ１および他方の面Ｓ２と交差して交わる周面Ｓ３とを有する。　
一方の面Ｓ１は、光軸Ｌに沿って視て光軸Ｌと重なる凹面Ｓａと、凹面Ｓａの周囲に配置され凹面Ｓａと連続する平坦面Ｓｂと、を含む。凹面Ｓａは、光透過面である。レンズ本体１０の光軸Ｌに沿って一方の面Ｓ１を視たときに、凹面Ｓａは光軸Ｌの位置を中心とする円形に形成されている。　
また、レンズ本体１０においては、他方の面Ｓ２は、凸面となっている。他方の面Ｓ２は、光透過面である。　
レンズ本体１０は、いわゆるメニスカスレンズである。また、レンズ本体１０は、他方の面Ｓ２の曲率よりも凹面Ｓａの曲率の方が大きく設計されており、負のパワーを有する。　
（コーティング膜）

　コーティング膜２０は、レンズ本体１０の一方の面Ｓ１に設けられている。図に示すレンズ１において、コーティング膜２０としては、反射防止膜として機能する誘電体多層膜、またはレンズ本体１０の傷付きを防止する膜として機能するハードコート膜が挙げられる。コーティング膜２０は、レンズ本体１０の凹面Ｓａの全面を覆っている。また、コーティング膜２０は、レンズ本体の他方の面Ｓ２には設けられていない。　
コーティング膜２０が誘電体多層膜である場合、コーティング膜２０は、屈折率の異なる２種の無機材料を、マスクを介して交互に蒸着して成膜することにより得られる。得られたコーティング膜２０は、レンズ１に反射防止機能を付与する。　
［レンズ製造方法］

　上述のようなレンズ１を製造するにあたり、特にレンズ本体１０は、次のような方法で製造する。　
図２は、本実施形態のレンズ製造方法を示すフローチャートである。以下、上述した図１のレンズを製造することとして説明する。そのため以下の説明では、必要に応じ、図１で示した符号を適宜用いる。　
本実施形態のレンズ製造方法においては、まず、硝材を削りＡｌ２Ｏ３からなる被加工レンズを製造する（ステップＳ１１）。硝材としては、Ａｌ２Ｏ３の単結晶、またはサファイアガラスを用いることができる。　
なお、以下の説明においては、本実施形態のレンズ製造方法における目的物を「レンズ」とし、目的物を得るまでの加工途中のレンズ状成形体のことを全て「被加工レンズ」と称する。　
ステップＳ１１においては、まず硝材を研削し、硝材からレンズ形状を削り出す。硝材の研削は、ガラスレンズの加工において通常用いられる装置により行うことができる。　
次いで、研磨材であるアルミナ粒子を用い、得られた被加工レンズを荒削りする。この際、用いるアルミナ粒子の粒度を徐々に細かくしながら複数回研磨を行い、被加工レンズの形状精度を高めるとよい。　
これらの工程により、目的とするレンズの曲率に合わせて荒削りされた被加工レンズが得られる。　
次いで、ダイヤモンドペーストを用い、得られた被加工レンズを研磨する（ステップＳ１２）。本ステップは、本発明における「第１研磨工程」に該当する。　
通常のガラスレンズの製造方法においては、研磨材としてコロイダルシリカを用いる方法が知られている。この方法では、例えば、荒削りして得られた被加工レンズにコロイダルシリカを流しかけながら、被加工レンズの研磨面に研磨皿を押し当てて研磨する。　
しかし、発明者がＡｌ２Ｏ３製のレンズの製造を検討するにあたって、Ａｌ２Ｏ３製の被加工レンズの研磨において上記方法を適用したところ、生産効率を低下させることなく所望の形状精度で加工することが困難であることが分かった。　
詳しくは、コロイダルシリカを研磨材として用いＡｌ２Ｏ３製の被加工レンズを研磨する場合、通常のガラスレンズの製造と同様の条件で研磨しても、所望の形状精度が得られないことが分かった。通常のガラスレンズの製造と同様とする条件とは、例えば研磨皿の回転速度、研磨時間等が挙げられる。このような方法では、加工後の面のＰＶ値が所望の値よりも大きくなりやすい。　
ここで、「ＰＶ（Peak to Valley）値」は、被加工レンズを研磨した際の「形状精度」を示す指標である。ＰＶ値とは、加工した面の設計値を基準としたときの、加工後の面の最も高い点と最も低い点との差である。ＰＶ値が大きいほど、加工後の被加工レンズの表面に大きなうねりが存在することを意味する。　
一方、コロイダルシリカを研磨材として用いてＡｌ２Ｏ３製の被加工レンズを研磨する場合であっても、例えば、長時間かけて徐々に被加工レンズの表面を研磨することにより、所望の形状精度で被加工レンズを加工することは可能である。しかしこの場合、被加工レンズの生産効率が低下することは明らかである。　
これらは、Ａｌ２Ｏ３からなる被加工レンズの硬度がモース硬度９であり、加工しにくいことが理由であると考えられる。　
上記課題に対し、発明者が種々検討した結果、ダイヤモンドペーストを用いて被加工レンズを研磨することで、生産効率を低下させることなく、所望の形状精度で加工することが可能であることが分かった。　
ダイヤモンドペーストは、通常、金属部材の微細研磨、または鏡面研磨に用いられるペースト状の研磨材である。ダイヤモンドペーストは、ダイヤモンド微粒子と、ダイヤモンド微粒子が分散する分散媒とを含む。分散媒は、例えば高分子量の炭化水素である。このようなダイヤモンドペーストは、代表的には、樹脂加工で用いられる金型の表面研磨または仕上げ磨きに用いられるものであり、通常、レンズ加工には用いられない。　
本実施形態のレンズ製造方法において、Ａｌ２Ｏ３からなる被加工レンズの研磨では、被加工レンズの表面に少量のダイヤモンドペーストを塗り、被加工レンズに研磨皿でダイヤモンドペーストをこすり付けることで被加工レンズを研磨する。また、通常のガラスレンズ加工のように、アルミナスラリーのような液体を加工中に流しかけることなく、研磨を行う。　
ダイヤモンドペーストに含まれるダイヤモンド微粒子は、モース硬度１０であり、被加工レンズを構成するＡｌ２Ｏ３よりも高硬度である。また、研磨中にアルミナスラリーのような液体を流しかけることが無いため、研磨中にダイヤモンドペーストが被加工レンズの表面に残留しやすい。そのため、上述のようにダイヤモンドペーストを用いると、被加工レンズ上にダイヤモンドペーストが留まり、容易に被加工レンズの研磨が可能である。　
本実施形態のレンズ製造方法においては、被加工レンズの研磨にダイヤモンドペーストを用いることで、短時間のうちに所望の形状精度で被加工レンズを研磨することが可能となる。　
次いで、被加工レンズの表面を洗浄し、ダイヤモンドペーストを除去する（ステップＳ１３）。本ステップは、本発明における「洗浄工程」に該当する。　
被加工レンズの表面にダイヤモンドペーストが残存すると、次のステップＳ１４において被加工レンズの表面を研磨する際に、ダイヤモンドペーストでさらに研磨することになり、所望の形状精度が得られない。そのため、ステップＳ１４の前に、被加工レンズの表面のダイヤモンドペーストを除去し、ダイヤモンドペーストの影響が後の工程へ及ばないようにすると好ましい。　
なお、研磨に用いる研磨皿も交換する。ダイヤモンドペーストを用いて研磨する際の研磨皿は、ステップＳ１２においてのみ用いる専用品とするとよい。　
次いで、被加工レンズを研磨する（ステップＳ１４）。本ステップは、本発明における「第２研磨工程」に該当する。　
ステップＳ１４においては、研磨材として、ステップＳ１２で用いたダイヤモンドペーストに含まれるダイヤモンド粒子よりも硬度が低い材料を形成材料とする研磨粒子と、研磨粒子が分散する水と、を含むスラリーを用いる。このような研磨材としては、例えば、研磨粒子がシリカ粒子であるコロイダルシリカを用いることができる。また、コロイダルシリカの他に、ダイヤモンド粒子よりも硬度が低い材料からなる研磨粒子であれば、本ステップにおいて研磨材として用いることができる。　
これにより、被加工レンズの表面に付いた微細な傷、荒れ等が除かれ、透明な被加工レンズが得られる。　
なお、被加工レンズの加工においては、被加工レンズの一方の面に対して上述のステップＳ１２からステップＳ１４を行い、その後、被加工レンズの他方の面に対して上述のステップＳ１２からステップＳ１４を行うこととしてもよい。　
また、被加工レンズの両面にステップＳ１２を行った後に、ステップＳ１３の洗浄を行い、その後、レンズの両面にステップＳ１４を行うこととしてもよい。被加工レンズの両面とは、被加工レンズの一方の面および他方の面のことである。　
図１のレンズを製造する場合、上述したステップＳ１１からステップＳ１４の加工を経ることで、被加工レンズがメニスカスレンズに加工される。　
次いで、被加工レンズの一面にコーティング処理を行う（ステップＳ１５）。本ステップは、本発明における「コーティング工程」に該当する。　
コーティング処理は、例えば、レンズ表面に行う反射防止膜、または表面の傷付き防止のために行うハードコート膜が挙げられる。反射防止膜としては、通常知られた誘電体多層膜が挙げられる。例えば、被加工レンズの一方の面に形成された凹面内に誘電体多層膜を形成する。　
次いで、被加工レンズの外周を研削し、被加工レンズの中心軸と被加工レンズの光軸とを一致させる「芯取り」を行う（ステップＳ１６）。本ステップは、本発明における「芯取り工程」に該当する。被加工レンズが、図１に示すレンズ本体１０となる。　
次いで、必要に応じて、図１に示す被加工レンズであるレンズ本体１０の平坦面Ｓｂ、および周面Ｓ３に遮光処理を行う（ステップＳ１７）。本ステップは、本発明における「遮光工程」に該当する。　
遮光処理は、メニスカスレンズの凸面と凹面とを除く面、すなわち平坦面Ｓｂおよび周面Ｓ３に施す。遮光処理としては、平坦面Ｓｂおよび周面Ｓ３を磨り面に加工すること、平坦面Ｓｂおよび周面Ｓ３に墨塗りを施すことが挙げられる。これらの加工により、得られるレンズにおいて迷光を抑制し、高品質のレンズが得られる。　
以上のようにして、本実施形態のレンズ製造方法が行われ、図１に示すレンズ１が得られる。　
以上のような構成のレンズ製造方法によれば、高い生産効率で形状精度よくＡｌ２Ｏ３からなるレンズを製造することが可能となる。　
なお、本実施形態においては、メニスカスレンズを製造することとして説明したが、これに限らない。本発明のレンズ製造方法によれば、他の形状のレンズを製造することもできる。　
また、本実施形態においては、図１のレンズ１を製造することとして説明したが、レンズの設計に応じて、適宜製造工程を変更することができる。例えば、製造するレンズがコーティング膜２０を有していない場合には、ステップＳ１５を省略することができる。　また、製造するレンズが、墨塗り面または磨り面を有していない場合には、ステップＳ１７を省略することができる。　
以上、添付図面を参照しながら本発明に係る好適な実施の形態例について説明したが、本発明は係る例に限定されないことは言うまでもない。上述した例において示した各構成部材の諸形状、組み合わせ等は一例であって、本発明の主旨から逸脱しない範囲において設計要求等に基づき種々変更可能である。
１…レンズ、１０…レンズ本体、２０…コーティング膜、Ｌ…光軸、ｍｐ…被加工レンズ、Ｓ１…一方の面、Ｓ２…他方の面、Ｓａ…凹面、Ｓｂ…平坦面

Claims (8)

  1. Ａｌ２Ｏ３からなる被加工レンズを研磨する研磨工程を備え、

    　前記研磨工程は、ダイヤモンド粒子を含むダイヤモンドペーストを用いて、Ａｌ２Ｏ３からなる被加工レンズを研磨する第１研磨工程を有するレンズ製造方法。
  2. 前記第１研磨工程の後に、前記被加工レンズを研磨する第２研磨工程を有し、

    　前記第２研磨工程で用いる研磨材は、前記ダイヤモンド粒子よりも硬度が低い材料を形成材料とする研磨粒子と、前記研磨粒子が分散する水と、を含むスラリーである請求項１に記載のレンズ製造方法。
  3. 前記研磨粒子は、シリカ粒子である請求項２に記載のレンズ製造方法。
  4. 前記第１研磨工程と前記第２研磨工程との間に、前記被加工レンズを洗浄する洗浄工程を有する請求項２または３に記載のレンズ製造方法。
  5. 前記被加工レンズは、メニスカスレンズである請求項１から４のいずれか１項に記載のレンズ製造方法。
  6. 前記研磨工程の後に、前記被加工レンズの凹面の表面にコーティング処理を行うコーティング工程を有する請求項５に記載のレンズ製造方法。
  7. 前記コーティング工程の後に、前記被加工レンズの外周を研削し、前記被加工レンズの中心軸と前記被加工レンズの光軸とを一致させる芯取り工程を有する請求項６に記載のレンズ製造方法。
  8. 前記コーティング工程の後に、前記メニスカスレンズの凸面と前記凹面とを除く面に遮光処理を行う遮光工程を有する請求項７に記載のレンズ製造方法。
PCT/JP2018/015075 2017-07-12 2018-04-10 レンズ製造方法 Ceased WO2019012763A1 (ja)