WO2018123356A1 - Tôle d'acier à haute résistance et tôle d'acier électrozinguée à haute résistance - Google Patents

Tôle d'acier à haute résistance et tôle d'acier électrozinguée à haute résistance Download PDF

Info

Publication number
WO2018123356A1
WO2018123356A1 PCT/JP2017/041809 JP2017041809W WO2018123356A1 WO 2018123356 A1 WO2018123356 A1 WO 2018123356A1 JP 2017041809 W JP2017041809 W JP 2017041809W WO 2018123356 A1 WO2018123356 A1 WO 2018123356A1
Authority
WO
WIPO (PCT)
Prior art keywords
mass
less
steel sheet
strength
test
Prior art date
Application number
PCT/JP2017/041809
Other languages
English (en)
Japanese (ja)
Inventor
潤一郎 衣笠
幸博 内海
航佑 柴田
Original Assignee
株式会社神戸製鋼所
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2017183608A external-priority patent/JP2018109222A/ja
Application filed by 株式会社神戸製鋼所 filed Critical 株式会社神戸製鋼所
Publication of WO2018123356A1 publication Critical patent/WO2018123356A1/fr

Abstract

La présente invention concerne une tôle d'acier à haute résistance qui contient C : 0,10 à 0,35 % en masse, Si : 0 à 0,6 % en masse, Mn : plus de 0 % en masse et pas plus de 1,5 % en masse, Al : plus de 0 % en masse et pas plus de 0,15 % en masse, N : plus de 0 % en masse et pas plus de 0,01 % en masse, P : plus de 0 % en masse et pas plus de 0,02 %, et S : plus de 0 % en masse et pas plus de 0,01 % en masse, le reste étant du fer et des impuretés inévitables ; le pourcentage de surface de martensite dans la structure globale est d'au moins 95 % ; la quantité de solution solide C dans la martensite n'est pas supérieure à 0,05 % en masse ; la densité numérique de carbure ayant un diamètre principal d'au moins 200 nm n'est pas supérieure à 50 par µm3 ; et la résistance à la traction est d'au moins 1270 MPa.
PCT/JP2017/041809 2016-12-28 2017-11-21 Tôle d'acier à haute résistance et tôle d'acier électrozinguée à haute résistance WO2018123356A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2016-255466 2016-12-28
JP2016255466 2016-12-28
JP2017183608A JP2018109222A (ja) 2016-12-28 2017-09-25 高強度鋼板および高強度電気亜鉛めっき鋼板
JP2017-183608 2017-09-25

Publications (1)

Publication Number Publication Date
WO2018123356A1 true WO2018123356A1 (fr) 2018-07-05

Family

ID=62707369

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/041809 WO2018123356A1 (fr) 2016-12-28 2017-11-21 Tôle d'acier à haute résistance et tôle d'acier électrozinguée à haute résistance

Country Status (1)

Country Link
WO (1) WO2018123356A1 (fr)

Cited By (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020002285A1 (fr) * 2018-06-26 2020-01-02 Tata Steel Nederland Technology B.V. Acier martensitique laminé à froid à haute résistance et haute aptitude au cintrage et son procédé de production
WO2020026838A1 (fr) * 2018-07-31 2020-02-06 Ｊｆｅスチール株式会社 Tôle fine d'acier et son procédé de production
WO2020079925A1 (fr) * 2018-10-18 2020-04-23 Ｊｆｅスチール株式会社 Tôle en acier électrozingué hautement résistante et à haut rendement, et procédé de fabrication de celle-ci
WO2021039776A1 (fr) * 2019-08-30 2021-03-04 Ｊｆｅスチール株式会社 Tôle d'acier, élément et leurs procédés de production
EP3702477A4 (fr) * 2017-10-26 2021-03-31 University Of Science And Technology Beijing Procédé de production d'une tôle d'acier martensitique laminée à froid d'ultra haute résistance à l'aide d'un procédé de chauffage ultra rapide
WO2021153393A1 (fr) * 2020-01-31 2021-08-05 Ｊｆｅスチール株式会社 Tole en acier, element et procede de fabrication de ceux-ci
JPWO2021153392A1 (fr) * 2020-01-31 2021-08-05
WO2022138895A1 (fr) * 2020-12-25 2022-06-30 Ｊｆｅスチール株式会社 Tôle d'acier, élément, et procédés de fabrication de ceux-ci
WO2022138894A1 (fr) * 2020-12-25 2022-06-30 Ｊｆｅスチール株式会社 Tôle d'acier, élément, et procédés de fabrication de ceux-ci
JP7311070B1 (ja) * 2022-03-30 2023-07-19 Ｊｆｅスチール株式会社 鋼板および部材、ならびに、それらの製造方法
JP7311067B1 (ja) * 2022-03-30 2023-07-19 Ｊｆｅスチール株式会社 鋼板および部材、ならびに、それらの製造方法
WO2023188505A1 (fr) * 2022-03-30 2023-10-05 Ｊｆｅスチール株式会社 Tôle d'acier et élément, et leurs procédés de production
WO2023188504A1 (fr) * 2022-03-30 2023-10-05 Ｊｆｅスチール株式会社 Tôle d'acier, élément, procédé de production de ladite tôle d'acier et procédé de production dudit élément
EP4071260A4 (fr) * 2020-01-21 2024-05-01 Kobe Steel Ltd Tôle d'acier haute résistance dotée d'une excellente résistance à la rupture différée

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010248565A (ja) * 2009-04-15 2010-11-04 Jfe Steel Corp 伸びフランジ性に優れた超高強度冷延鋼板およびその製造方法
JP5662920B2 (ja) * 2011-11-11 2015-02-04 株式会社神戸製鋼所 耐遅れ破壊性に優れた高強度鋼板およびその製造方法
JP2015168841A (ja) * 2014-03-06 2015-09-28 株式会社神戸製鋼所 焼付け硬化性と曲げ性に優れた高強度合金化溶融亜鉛めっき鋼板

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010248565A (ja) * 2009-04-15 2010-11-04 Jfe Steel Corp 伸びフランジ性に優れた超高強度冷延鋼板およびその製造方法
JP5662920B2 (ja) * 2011-11-11 2015-02-04 株式会社神戸製鋼所 耐遅れ破壊性に優れた高強度鋼板およびその製造方法
JP2015168841A (ja) * 2014-03-06 2015-09-28 株式会社神戸製鋼所 焼付け硬化性と曲げ性に優れた高強度合金化溶融亜鉛めっき鋼板

Cited By (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3702477A4 (fr) * 2017-10-26 2021-03-31 University Of Science And Technology Beijing Procédé de production d'une tôle d'acier martensitique laminée à froid d'ultra haute résistance à l'aide d'un procédé de chauffage ultra rapide
WO2020002285A1 (fr) * 2018-06-26 2020-01-02 Tata Steel Nederland Technology B.V. Acier martensitique laminé à froid à haute résistance et haute aptitude au cintrage et son procédé de production
WO2020026838A1 (fr) * 2018-07-31 2020-02-06 Ｊｆｅスチール株式会社 Tôle fine d'acier et son procédé de production
JPWO2020026838A1 (ja) * 2018-07-31 2020-08-06 Ｊｆｅスチール株式会社 薄鋼板
CN112513311A (zh) * 2018-07-31 2021-03-16 杰富意钢铁株式会社 薄钢板及其制造方法
US11965223B2 (en) 2018-07-31 2024-04-23 Jfe Steel Corporation Thin steel sheet and method for manufacturing the same
WO2020079925A1 (fr) * 2018-10-18 2020-04-23 Ｊｆｅスチール株式会社 Tôle en acier électrozingué hautement résistante et à haut rendement, et procédé de fabrication de celle-ci
JP6760520B1 (ja) * 2018-10-18 2020-09-23 Ｊｆｅスチール株式会社 高降伏比高強度電気亜鉛系めっき鋼板及びその製造方法
WO2021039776A1 (fr) * 2019-08-30 2021-03-04 Ｊｆｅスチール株式会社 Tôle d'acier, élément et leurs procédés de production
JPWO2021039776A1 (fr) * 2019-08-30 2021-03-04
JP6958752B2 (ja) * 2019-08-30 2021-11-02 Ｊｆｅスチール株式会社 鋼板、部材及びそれらの製造方法
EP4071260A4 (fr) * 2020-01-21 2024-05-01 Kobe Steel Ltd Tôle d'acier haute résistance dotée d'une excellente résistance à la rupture différée
JPWO2021153393A1 (fr) * 2020-01-31 2021-08-05
WO2021153392A1 (fr) * 2020-01-31 2021-08-05 Ｊｆｅスチール株式会社 Tole en acier, element et procede de fabrication de ceux-ci
JP7001197B2 (ja) 2020-01-31 2022-01-19 Ｊｆｅスチール株式会社 鋼板、部材及びそれらの製造方法
JP7001198B2 (ja) 2020-01-31 2022-01-19 Ｊｆｅスチール株式会社 鋼板、部材及びそれらの製造方法
WO2021153393A1 (fr) * 2020-01-31 2021-08-05 Ｊｆｅスチール株式会社 Tole en acier, element et procede de fabrication de ceux-ci
JPWO2021153392A1 (fr) * 2020-01-31 2021-08-05
JP7140301B1 (ja) * 2020-12-25 2022-09-21 Ｊｆｅスチール株式会社 鋼板、部材およびそれらの製造方法
JP7140302B1 (ja) * 2020-12-25 2022-09-21 Ｊｆｅスチール株式会社 鋼板、部材およびそれらの製造方法
WO2022138894A1 (fr) * 2020-12-25 2022-06-30 Ｊｆｅスチール株式会社 Tôle d'acier, élément, et procédés de fabrication de ceux-ci
WO2022138895A1 (fr) * 2020-12-25 2022-06-30 Ｊｆｅスチール株式会社 Tôle d'acier, élément, et procédés de fabrication de ceux-ci
JP7311070B1 (ja) * 2022-03-30 2023-07-19 Ｊｆｅスチール株式会社 鋼板および部材、ならびに、それらの製造方法
JP7311067B1 (ja) * 2022-03-30 2023-07-19 Ｊｆｅスチール株式会社 鋼板および部材、ならびに、それらの製造方法
WO2023188505A1 (fr) * 2022-03-30 2023-10-05 Ｊｆｅスチール株式会社 Tôle d'acier et élément, et leurs procédés de production
WO2023188504A1 (fr) * 2022-03-30 2023-10-05 Ｊｆｅスチール株式会社 Tôle d'acier, élément, procédé de production de ladite tôle d'acier et procédé de production dudit élément

Similar Documents

Publication Publication Date Title
WO2018123356A1 (fr) Tôle d'acier à haute résistance et tôle d'acier électrozinguée à haute résistance
KR102173601B1 (ko) 고강도 박강판 및 그 제조 방법
KR101615463B1 (ko) 용융 아연 도금 강판 및 그 제조 방법
TWI399442B (zh) 加工性優異之高強度熔融鍍鋅鋼板及其製造方法
TWI412609B (zh) 高強度鋼板及其製造方法
US8840834B2 (en) High-strength steel sheet and method for manufacturing the same
KR101335069B1 (ko) 성형성이 우수한 고강도 냉연 강판, 고강도 용융 아연 도금 강판 및 그들의 제조 방법
TWI488976B (zh) A high-strength steel sheet excellent in shape freezing property, a high-strength galvanized steel sheet and a manufacturing method thereof
KR101528080B1 (ko) 성형성이 우수한 고강도 용융 아연 도금 강판 및 그 제조 방법
KR101831020B1 (ko) 가공성이 우수한 고항복비 고강도 강판
JP3889768B2 (ja) 塗膜密着性と延性に優れた高強度冷延鋼板および自動車用鋼部品
WO2017179372A1 (fr) Feuille d'acier à haute résistance et son procédé de fabrication
WO2017026125A1 (fr) Matériau pour tôle d'acier à haute résistance, matériau laminé à chaud pour tôle d'acier à haute résistance, matériau recuit après laminage à chaud et pour tôle d'acier à haute résistance, tôle d'acier à haute résistance, tôle d'acier galvanisé à chaud à haute résistance, tôle d'acier galvanisé à haute résistance et leur procédé de fabrication
JP6223905B2 (ja) 降伏強度と加工性に優れた高強度合金化溶融亜鉛めっき鋼板
KR20110110367A (ko) 성형성이 우수한 고강도 용융 아연 도금 강판 및 그 제조 방법
JP2008156680A (ja) 高降伏比を有する高強度冷延鋼板及びその製造方法
JP2011001579A (ja) 加工性および耐疲労特性に優れた高強度合金化溶融亜鉛めっき鋼板およびその製造方法
KR101740843B1 (ko) 고강도 강판 및 그 제조 방법
JP6965956B2 (ja) 高強度鋼板およびその製造方法
WO2011125738A1 (fr) Tôle d'acier galvanisée à chaud par trempage et tôle d'acier allié galvanisée à chaud par trempage, chacune ayant une excellente aptitude au traitement, un rapport d'élasticité élevé et une résistance élevée
JPWO2018088421A1 (ja) 高強度冷延薄鋼板および高強度冷延薄鋼板の製造方法
KR102119017B1 (ko) 고강도 냉연 박강판 및 그의 제조 방법
CN108713066B (zh) 高强度钢板及其制造方法
JP2018109222A (ja) 高強度鋼板および高強度電気亜鉛めっき鋼板
WO2017009938A1 (fr) Tôle d'acier, tôle d'acier galvanisée par immersion à chaud, tôle d'acier galvanisée par immersion à chaud alliée et procédés de production associés

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17888009

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17888009

Country of ref document: EP

Kind code of ref document: A1