WO2017213453A1 - Vlt와 irr 조절이 가능한 태양광 차단필름 - Google Patents

Vlt와 irr 조절이 가능한 태양광 차단필름 Download PDF

Info

Publication number
WO2017213453A1
WO2017213453A1 PCT/KR2017/006005 KR2017006005W WO2017213453A1 WO 2017213453 A1 WO2017213453 A1 WO 2017213453A1 KR 2017006005 W KR2017006005 W KR 2017006005W WO 2017213453 A1 WO2017213453 A1 WO 2017213453A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
vlt
irr
functional
base film
Prior art date
Application number
PCT/KR2017/006005
Other languages
English (en)
French (fr)
Inventor
이기선
Original Assignee
이기선
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이기선 filed Critical 이기선
Publication of WO2017213453A1 publication Critical patent/WO2017213453A1/ko

Abstract

본 발명은 VLT와 IRR 조절이 가능한 태양광 차단필름에 관한 것으로, 필름의 표면에 기능성 패턴라인을 소정의 폭으로 형성하여 가시광선투과율(VLT)과 자외선차단율(IRR)을 조절할 수 있는 태양광 차단필름에 관한 것이다. 본 발명의 제1실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 합성수지 필름 등의 판형상의 제작된 기저필름(10)과, 기저필름(10)의 일표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어진 것을 특징으로 한다.

Description

VLT와 IRR 조절이 가능한 태양광 차단필름
본 발명은 VLT와 IRR 조절이 가능한 태양광 차단필름에 관한 것으로, 필름의 표면에 기능성 패턴라인을 소정의 폭으로 형성하여 가시광선투과율(Visible Light Transimittance;VLT)과 자외선차단율(Infrared Rejection:IRR)을 조절할 수 있는 태양광 차단필름에 관한 것이다.
태양 광선은 가시광 성분 뿐만 아니라 자외선과 같이 인체에 유해한 성분 및 적외선과 같이 밀폐된 공간을 승온시키는 열성분을 포함하고 있다. 태양 광선 중 이와 같은 불필요한 성분을 차단할 목적으로 건물의 외벽 유리나 차창 등에 태양광을 차단하는 필름이 사용된다.
예컨대, 적외선의 특정 영역의 빛을 흡수하는 물질을 사용하여 필름을 제조하고, 이를 유리면에 부착시켜 열에너지를 차단하는 방안이 제시되고 있다. 그러나, 이런 방식의 필름의 경우, 가시광선투과율(VLT) 투과율이 높으면 자외선차단율(IRR)이 낮아지고, 자외선차단율(IRR)이 높으면 가시광선 영역의 빛도 같이 차단되어 시안성의 문제가 발생하고, 대부분의 적외선 영역의 빛이 흡수되기 때문에 필름이나 유리의 온도가 증가하여 열차단 효율이 저하되는 등의 문제점이 있다.
이에 따라 태양광 차단필름은 가시광에 대한 투과 특성이 우수하고 적외선에 대한 차단 특성이 우수할 것이 요구된다.
본 발명의 목적은 필름의 표면에 기능성 패턴라인을 소정의 폭으로 형성하여 가시광선투과율(VLT)과 자외선차단율(IRR)을 조절할 수 있는 태양광 차단필름을 제공하는 데 있다.
본 발명의 다른 목적은 필름의 표면에 가시광선투과율(VLT)이 조절된 재료와 자외선차단율(IRR)을 조절하는 재료를 이웃하게 형성하여 필름의 표면을 미끈하게 형성할 수 있는 VLT와 IRR 조절이 가능한 태양광 차단필름을 제공하는 데 있다.
본 발명의 제1실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 합성수지 필름 등의 판형상의 제작된 기저필름(10)과, 기저필름(10)의 일표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어진 것을 특징으로 한다.
본 발명의 제2실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 합성수지 필름 등의 판형상의 제작된 기저필름(10)과, 기저필름(10)의 일표면에 형성되며 가시광선투과율(VLT)이 조절되는 투과성 재료의 투과성 코팅층(30)과, 투과성 코팅층(30)의 외측표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어지는 것을 특징으로 한다.
본 발명의 제3실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 판형상의 제작된 기저필름(10)과; 기저필름(10)의 일표면에 형성되며 자외선차단율(IRR)이 조절되는 기능성 재료의 투과성 코팅층(20-1)과; 투과성 코팅층(30)의 외측표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어지는 것을 특징으로 한다.
바람직하게, 기저필름(10)의 타표면에 접착재료의 접착층(40)이 형성되고, 접착층(40)의 외면에는 접착부재의 접착력을 보호하기 위한 보호필름(50)이 위치하는 것을 특징으로 한다.
바람직하게, 기능성 패턴라인(20)의 외면에 접착층(40-1)이 형성되고, 접착층(40-1)의 외면에 접착부재의 접착력을 보호하기 위한 보호필름(50)이 위치하는 것을 특징으로 한다.
바람직하게, 기능성 패턴라인(20) 부분은 30~50%의 가시광선투과율(VLT)을 갖고, 80% 이상의 적외선차단율(IRR)을 갖도록 형성되는 것을 특징으로 한다.
바람직하게, 기능성 패턴라인(20)을 형성하는 기능성 재료는 자외선흡수 재료, 도전성 재료, 방열 재료, 절연성 재료, 전자파 흡수재료 또는 이들을 혼합한 것 중의 어느 하나인 것을 특징으로 한다.
본 발명의 제5실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 합성수지 필름 등의 판형상의 제작된 기저필름(10)과, 기저필름(10)의 일표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)과, 기능성 패턴라인(20) 사이의 기저필름(10)의 표면에 기능성 패턴라인(20)과 동일한 높이로 형성되는 가시광선투과율(VLT)이 조절되는 투과성 재료의 투과성 코팅층(30)으로 이루어지는 것을 특징으로 한다.
바람직하게, 제5실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름의 제조방법은 합성수지 필름 등의 판형상의 제작된 기저필름(10)을 준비하는 공정과, 기저필름(10)의 일표면에 소정의 폭으로 기능성 재료를 도포하여 기능성 코팅라인을 형성하는 공정과, 기능성 코팅라인의 상부면에 계면장력이 낮은 접착물질을 도포하여 결로형 박막을 형성하는 공정과, 기능성 패턴라인(20) 사이의 기저필름(10)의 표면에 투과성 재료를 기능성 코팅라인과 동일한 높이로 도포하여 투과성 코팅층(30)을 형성하는 공정으로 이루어진 것을 특징으로 한다.
본 발명의 VLT와 IRR 조절이 가능한 태양광 차단필름은 기능성 패턴라인의 개수 또는 폭을 조절하면 필름 전체의 적외선차단율을 간단하게 조절할 수 있기 때문에 간단하게 필름의 가시광선투과율도 함께 조절할 수 있는 장점이 있다.
또한, 기능성 패턴라인을 줄무늬 모양, 벌집모양, 사각형 모양 등의 다양한 형상 및 색상으로 형성할 수 있기 때문에 사용자가 원하는 미관을 갖도록 제작할 수 있는 장점이 있다.
또한, 외부에서 충격이 가해지는 경우에 충격이 패턴라인을 따라 이동하면서 흡수 및 분산되기 때문에 안전필름으로도 사용할 수 있는 장점이 있다.
도 1은 본 발명의 제1실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름의 단면도.
도 2a 내지 도 2c는 본 발명에 따른 기능성 패턴라인의 예시도.
도 3은 본 발명의 제2실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름의 단면도.
도 4는 본 발명의 제3실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름의 단면도.
도 5는 본 발명의 제4실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름의 단면도.
도 6a 및 도 6b는 본 발명의 제5실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름의 단면도.
도 7은 도 6의 태양광 차단필름을 제작하기 위한 공정도.
이하, 첨부된 도면을 참조하여 본 발명의 실시예에 대하여 자세히 설명한다. 이때, 각각의 실시예에서 동일한 구성은 동일한 도면부호를 부여하기로 한다.
이하, 본 발명에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름의 개별 구성에 대하여 자세히 살펴본다.
도 1에 도시된 바와 같이, 본 발명의 제1실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 합성수지 필름 등의 판형상의 제작된 기저필름(10)과, 기저필름(10)의 일표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20), 기저필름(10)의 타표면에 접착재료의 접착층(40)이 형성되고, 접착층(40)의 외면에는 접착부재의 접착력을 보호하기 위한 보호필름(50)이 위치하는 것이 바람직하다.
이때, 기저필름(10)은 에스터계 고분자 필름, 스티렌계 고분자 필름, 카보네이트류 고분자 필름, 이미드류 고분자 필름, 설폰계 고분자 필름, 셀루로오스계 고분자 필름 등의 다양한 재료가 사용가능하다.
그리고, 기능성 패턴라인(20) 부분은 5%~70%의 가시광선투과율(VLT)을 갖고, 30%~95% 이상의 적외선차단율(IRR)을 갖도록 형성되는 것이 바람직하지만, 기능성 패턴라인(20)의 폭은 필름 전체의 가시광선투과율과 자외선차단율에 따라 조절하게 된다. 기능성 패턴라인(20)을 형성하는 기능성 재료는 나노입자를 분산한 잉크로, MgO, TiO2, CeO, 벤조페논계 등의 자외선흡수 재료, 나노크기의 카본, 금속산화물, ATO(Antimony Tin Oxide), ITO(Indium Tin Oxide), Ag-소수성 실리카 에어로겔 등의 적외선흡수 재료, 열차단재료, BaO2, PMMA(Poly Methyl Methacrylate), TiO2, ZnO2 등의 확산재료, 나노크기의 그래핀, 그라파이트, 철, 카본변성, 알루미늄, 산화마그네슘 등의 도전성 재료, 방열 재료, 절연성 재료, 전자파 흡수재료에서 선택한 하나 이상의 재료인 것이 바람직하다. 특히, 전도성 물질을 사용하면 상변환 필름으로 사용할 수도 있고, 확산재료를 사용하면 영상 필름으로 사용할 수도 있다.
이러한 제1실시예에 따른 태양광 차단필름은 기저필름(10)의 일표면에 형성되는 기능성 패턴라인(20)의 개수 또는 폭을 조절하면 필름 전체의 적외선차단율을 간단하게 조절할 수 있기 때문에 간단하게 필름의 가시광선투과율도 함께 조절할 수 있게 된다. 또한, 도 2a 내지 도 2c에 도시된 바와 같이, 패턴라인을 줄무늬 모양, 벌집모양, 사각형 모양 등의 다양한 형상 및 색상으로 형성할 수 있기 때문에 사용자가 원하는 미관을 갖도록 제작할 수 있다. 그리고, 외부에서 충격이 가해지는 경우에 충격이 패턴라인을 따라 이동하면서 흡수 및 분산되기 때문에 안전필름을 제작할 수 있게 된다.
도 3에 도시된 바와 같이, 본 발명의 제2실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 합성수지 필름 등의 판형상의 제작된 기저필름(10)과, 기저필름(10)의 일표면에 형성되며 가시광선투과율(VLT)이 조절되는 투과성 재료의 투과성 코팅층(30)과, 투과성 코팅층(30)의 외측표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어지며, 기저필름(10)의 타표면에 접착층(40)이 형성되고, 접착층(40)의 외면에는 접착부재의 접착력을 보호하기 위한 보호필름(50)이 위치하는 것이 바람직하다. 이때, 투과성 코팅층(30)은 60~90%의 가시광선투과율을 갖도록 형성되는 것이 바람직하고, 기능성 패턴라인(20)의 30~50%의 가시광선투과율을 갖고, 80% 이상의 적외선차단율(IRR)을 갖도록 형성되는 것이 바람직하다.
이러한 제2실시예에 따른 태양광 차단필름은 기능성 패턴라인(20)의 개수 또는 폭을 조절하면 필름 전체의 가시광선 투과율과 적외선 차단율을 간단하게 조절할 수 있기 때문에 필름이 사용되는 장소에 따른 용도에 적합한 필름을 간단하게 제작할 수 있다. 또한, 패턴라인을 줄무늬 모양, 벌집모양, 사각형 모양 등의 다양한 형상으로 형성할 수 있기 때문에 사용자이 원하는 미관도 제작할 수 있다.
도 4에 도시된 실시와 같이, 본 발명의 제3실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 합성수지 필름 등의 판형상의 제작된 기저필름(10)과, 기저필름(10)의 일표면에 형성되며 자외선차단율(IRR)이 조절되는 기능성 재료의 기능성 코팅층(20-1)과, 기능성 코팅층(30)의 외측표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어지며, 기저필름(10)의 타표면에 접착층(40)이 형성되고, 접착층(40)의 외면에는 접착부재의 접착력을 보호하기 위한 보호필름(50)이 위치하는 것이 바람직하다. 이때, 기능성 코팅층(20-1)과, 기능성 패턴라인(20)은 40~50%의 가시광선투과율을 갖고, 80% 이상의 적외선차단율(IRR)을 갖도록 형성되는 것이 바람직하다.
이러한 제3실시예에 따른 태양광 차단필름은 기본적인 기능성 코팅층으로 1차적으로 필름에 기능성을 부여하고, 추가적으로 기능성 패턴라인을 형성하기 때문에 필름이 사용되는 장소에 따라서 추가적인 기능성을 부여한 필름을 간단하게 제작할 수 있다.
도 5에 도시된 바와 같이, 본 발명의 제4실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 합성수지 필름 등의 판형상의 제작된 기저필름(10)과, 기저필름(10)의 일표면에 형성되며 가시광선투과율(VLT)이 조절되는 투과성 재료의 투과성 코팅층(30)과, 투과성 코팅층(30)의 외측표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어지며, 기능성 패턴라인(20)의 외면에 접착층(40-1)이 형성되고, 접착층(40-1)의 외면에 접착부재의 접착력을 보호하기 위한 보호필름(50)이 위치하는 것이 바람직하다.
이러한 제4실시예에 의한 태양광 차단필름은 기능성 패턴라인(20) 사이에 공간이 형성되어 있어 있기 때문에 기능성 패턴라인(20)의 외면에 형성된 접착층(40-1)이 유리 등의 표면에 부착되면 표면과 투과성 코팅층(30) 사이에 진공층이 형성되어 단열효과를 높일 수 있게 된다.
또한, 기능성 패턴라인(20)으로 방열물질을 사용하면 필름에서 흡수된 열이 패턴라인을 따라 외측으로 이동시키면서 외부로 배출시킬 수 있기 때문에 플름에서 흡수한 열이 유리 등의 표면을 통해서 실내 등으로 유입되는 것을 차단할 수 있게 된다.
도 6에 도시된 바와 같이, 본 발명의 제5실시예에 따른 VLT와 IRR 조절이 가능한 태양광 차단필름은 합성수지 필름 등의 판형상의 제작된 기저필름(10)과, 기저필름(10)의 일표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)과, 기능성 패턴라인(20) 사이의 기저필름(10)의 표면에 기능성 패턴라인(20)과 동일한 높이로 형성되는 가시광선투과율(VLT)이 조절되는 투과성 재료의 투과성 코팅층(30)으로 이루어지며, 기저필름(10)의 내측표면에 접착층(40)이 형성되거나(도 6a 참조), 또는 기능성 패턴라인(20)과 투과성 코팅층(30)의 외면에 접착층(40)이 형성되고(도 6b 참조), 접착층(40)의 외면에 접착부재의 접착력을 보호하기 위한 보호필름(50)이 위치하는 것이 바람직하다.
이러한, 도 7에 도시된 바와 같이, 제5실시예에 따른 태양광 차단필름의 제조방법은 합성수지 필름 등의 판형상의 제작된 기저필름(10)을 준비하는 공정과, 기저필름(10)의 일표면에 소정의 폭으로 기능성 재료를 도포하여 기능성 코팅라인을 형성하는 공정과, 기능성 코팅라인의 상부면에 계면장력이 낮은 접착물질을 도포하여 결로형 박막을 형성하는 공정과, 기능성 패턴라인(20) 사이의 기저필름(10)의 표면에 투과성 재료를 기능성 코팅라인과 동일한 높이로 도포하여 투과성 코팅층(30)을 형성하는 공정으로 이루어진다. 이때, 계면장력이 낮은 접착물질은 실리콘계 또는 불소계의 접착물질인 것이 바람직하다.
이와 같이 기능성 코팅라인을 형성한 후에 투과성 코팅층(30)을 도포하면 계면장력에 의하여 계면장력이 높은 투과성 코팅층(30)이 계면장력이 낮은 결로형 박막의 표면에 쌓이지 않으면서 기능성 패턴라인의 사이에만 채워지면서 기능성 코팅라인과 투과성 코팅층(30)이 동일한 높이로 형성할 수 있게 된다.
본 발명이 속하는 기술분야의 통상의 지식을 가진 자는 본 발명이 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시 예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구의 범위에 의하여 나타내어지며, 특허청구의 범위의 의미 및 범위 그리고 그 균등 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.

Claims (12)

  1. 판형상의 제작된 기저필름(10)과;
    기저필름(10)의 일표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어진 것을 특징으로 하는 VLT와 IRR 조절이 가능한 태양광 차단필름.
  2. 판형상의 제작된 기저필름(10)과;
    기저필름(10)의 일표면에 형성되며 가시광선투과율(VLT)이 조절되는 투과성 재료의 투과성 코팅층(30)과;
    투과성 코팅층(30)의 외측표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어지는 것을 특징으로 하는 VLT와 IRR 조절이 가능한 태양광 차단필름.
  3. 판형상의 제작된 기저필름(10)과;
    기저필름(10)의 일표면에 형성되며 자외선차단율(IRR)이 조절되는 기능성 재료의 투과성 코팅층(20-1)과;
    투과성 코팅층(30)의 외측표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)으로 이루어지는 것을 특징으로 하는 VLT와 IRR 조절이 가능한 태양광 차단필름.
  4. 청구항 1 내지 청구항 3 중의 어느 한 항에 있어서, 기저필름(10)의 타표면에 접착재료의 접착층(40)이 형성되고, 접착층(40)의 외면에는 접착부재의 접착력을 보호하기 위한 보호필름(50)이 위치하는 것을 특징으로 하는 VLT와 IRR 조절이 가능한 태양광 차단필름.
  5. 청구항 1 내지 청구항 3 중의 어느 한 항에 있어서, 기능성 패턴라인(20)의 외면에 접착층(40-1)이 형성되고, 접착층(40-1)의 외면에 접착부재의 접착력을 보호하기 위한 보호필름(50)이 위치하는 것을 특징으로 하는 VLT와 IRR 조절이 가능한 태양광 차단필름.
  6. 청구항 1 내지 청구항 3 중의 어느 한 항에 있어서, 기저필름(10)은 에스터계 고분자 필름, 스티렌계 고분자 필름, 카보네이트류 고분자 필름, 이미드류 고분자 필름, 설폰계 고분자 필름, 셀루로오스계 고분자 필름 중의 어느 하나가 사용되는 것을 특징으로 하는 VLT와 IRR 조절이 가능한 태양광 차단필름.
  7. 청구항 1 내지 청구항 3 중의 어느 한 항에 있어서, 기능성 패턴라인(20) 부분은 30~50%의 가시광선투과율(VLT)을 갖고, 80% 이상의 적외선차단율(IRR)을 갖도록 형성되는 것을 특징으로 하는 VLT와 IRR 조절이 가능한 태양광 차단필름.
  8. 청구항 1 내지 청구항 3 중의 어느 한 항에 있어서, 기능성 패턴라인(20)을 형성하는 기능성 재료는 자외선흡수 재료, 적외선흡수 재료, 확산재료, 도전성 재료, 방열 재료, 절연성 재료, 전자파 흡수재료 또는 이들을 혼합한 것 중의 어느 하나인 것을 특징으로 하는 VLT와 IRR 조절이 가능한 태양광 차단필름.
  9. 판형상의 제작된 기저필름(10)과;
    기저필름(10)의 일표면에 소정의 폭으로 형성되는 기능성 재료의 기능성 패턴라인(20)과;
    기능성 패턴라인(20) 사이의 기저필름(10)의 표면에 기능성 패턴라인(20)과 동일한 높이로 형성되는 가시광선투과율(VLT)이 조절되는 투과성 재료의 투과성 코팅층(30)으로 이루어지는 것을 특징으로 하는 VLT와 IRR 조절이 가능한 태양광 차단필름.
  10. 청구항 9에 있어서, 기능성 패턴라인(20)과 투과성 코팅층(30)의 외면에 접착층(40)이 형성되고, 접착층(40)의 외면에 접착부재의 접착력을 보호하기 위한 보호필름(50)이 위치하는 것을 특징으로 하는 VLT와 IRR 조절이 가능한 태양광 차단필름.
  11. 판형상의 제작된 기저필름(10)을 준비하는 공정과;
    기저필름(10)의 일표면에 소정의 폭으로 기능성 재료를 도포하여 기능성 코팅라인을 형성하는 공정과;
    기능성 코팅라인의 상부면에 계면장력이 낮은 접착물질을 도포하여 결로형 박막을 형성하는 공정과;
    기능성 패턴라인(20) 사이의 기저필름(10)의 표면에 투과성 재료를 기능성 코팅라인과 동일한 높이로 도포하여 투과성 코팅층(30)을 형성하는 공정으로 이루어진 것을 특징으로 하는 VLT와 IRR 조절이 가능한 태양광 차단필름의 제조방법.
  12. 청구항 11에 있어서, 계면장력이 낮은 접착물질은 실리콘계 또는 불소계의 접착물질인 것을 특징으로 하는 VLT와 IRR 조절이 가능한 태양광 차단필름의 제조방법.
PCT/KR2017/006005 2016-06-10 2017-06-09 Vlt와 irr 조절이 가능한 태양광 차단필름 WO2017213453A1 (ko)