WO2017201864A1 - Anti-condensation coating adhesive - Google Patents
Anti-condensation coating adhesive Download PDFInfo
- Publication number
- WO2017201864A1 WO2017201864A1 PCT/CN2016/092247 CN2016092247W WO2017201864A1 WO 2017201864 A1 WO2017201864 A1 WO 2017201864A1 CN 2016092247 W CN2016092247 W CN 2016092247W WO 2017201864 A1 WO2017201864 A1 WO 2017201864A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- parts
- condensation
- condensation coating
- acrylate
- coating adhesive
- Prior art date
Abstract
An anti-condensation coating adhesive, comprising the following components in parts by weight: 12-30 parts of zinc oxide, 8-16 parts of benzoyl peroxide, 10-20 parts of dibutyl phthalate, 10-20 parts of triphenyl phosphate, 2-10 parts of isopropyl acrylate, 20-80 parts of styrene, 120-200 parts of butyl acrylate, 40-120 parts of acrylic acid, 80-100 parts of methyl methacrylate, 10-20 parts of zinc ammonia carbonate, 20-40 parts of titanium dioxide, 10-20 parts of ethylene glycol monopropyl ether, and 6-12 parts of ethyl acrylate. The anti-condensation coating adhesive features easy preparation, non-toxic raw materials for production, and good effects, is environmentally friendly, can form a firm layer, and has long-lasting anti-condensation and waterproof properties.
Description
本发明涉及一种化学用品的技术领域,具体涉及一种防结露涂胶。The invention relates to the technical field of chemical products, in particular to an anti-condensation coating.
涂胶在生产和生活中的作用非常大,广泛应用与各个领域,涂胶形成的涂膜可对物体起到装饰、保护和标致作用,目前市面上的大部分涂胶虽然制作简单、售价便宜但同时功能比较单一,只能简单的作为装饰之用,而在一些特殊的作业环境中,简单的涂胶的并不能满足人们的所需。Gluing has a very large role in production and life. It is widely used in various fields. The coating film formed by gluing can play a role in decoration, protection and labeling. Most of the coatings on the market are simple to make and sell. Cheap but at the same time the function is relatively simple, can only be used as a decoration, and in some special working environments, simple glue can not meet people's needs.
发明内容Summary of the invention
本发明的目的提供一种防结露涂胶,解决上述现有技术问题中的一个或者多个。It is an object of the present invention to provide an anti-condensation coating that addresses one or more of the above prior art problems.
根据本发明的一个方面,一种防结露涂胶,包括如下重量份的组分,氧化锌12~30份,过氧化苯甲酰8~16份,邻苯二甲酸二丁酯10~20份,磷酸三苯酯10~20份,丙烯酸异丙酯2~10份,苯乙烯20~80份,丙烯酸丁酯120~200份,丙烯酸40~120份,甲基丙烯酸甲酯80~100份,碳酸锌氨10~20份,二氧化钛20~40份,乙二醇单丙醚10~20份,丙烯酸乙酯6~12份。According to one aspect of the invention, an anti-condensation coating comprises the following components by weight, 12 to 30 parts of zinc oxide, 8 to 16 parts of benzoyl peroxide, and 10 to 20 parts of dibutyl phthalate. Parts, 10 to 20 parts of triphenyl phosphate, 2 to 10 parts of isopropyl acrylate, 20 to 80 parts of styrene, 120 to 200 parts of butyl acrylate, 40 to 120 parts of acrylic acid, and 80 to 100 parts of methyl methacrylate 10 to 20 parts of zinc carbonate ammonia, 20 to 40 parts of titanium dioxide, 10 to 20 parts of ethylene glycol monopropyl ether, and 6 to 12 parts of ethyl acrylate.
本发明提供的一种防结露涂胶,制作简单,采用的生产原料选择无毒性的,涂胶的使用效果好,环保,可形成坚韧涂层,具有持久的防结露性和防水性。The anti-condensation coating provided by the invention has the advantages of simple preparation, non-toxicity of the raw materials used for the selection, good use effect of the glue coating, environmental protection, formation of a tough coating layer, long-lasting anti-condensation property and waterproof property.
实施例1Example 1
一种防结露涂胶,包括如下重量份的组分,氧化锌12份,过氧化苯甲酰8份,邻苯二甲酸二丁酯10份,磷酸三苯酯10份,丙烯酸异丙酯2份,苯乙烯20份,丙烯酸丁酯120份,丙烯酸40份,甲基丙烯酸甲酯80份,
碳酸锌氨10份,二氧化钛20份,乙二醇单丙醚10份,丙烯酸乙酯6份,混合搅拌即得产品。An anti-condensation coating comprising the following components by weight, 12 parts of zinc oxide, 8 parts of benzoyl peroxide, 10 parts of dibutyl phthalate, 10 parts of triphenyl phosphate, isopropyl acrylate 2 parts, 20 parts of styrene, 120 parts of butyl acrylate, 40 parts of acrylic acid, 80 parts of methyl methacrylate,
10 parts of zinc carbonate ammonia, 20 parts of titanium dioxide, 10 parts of ethylene glycol monopropyl ether, and 6 parts of ethyl acrylate were mixed and stirred to obtain a product.
实施例2Example 2
一种防结露涂胶,包括如下重量份的组分,氧化锌21份,过氧化苯甲酰12份,邻苯二甲酸二丁酯15份,磷酸三苯酯15份,丙烯酸异丙酯6份,苯乙烯51份,丙烯酸丁酯160份,丙烯酸80份,甲基丙烯酸甲酯90份,碳酸锌氨15份,二氧化钛30份,乙二醇单丙醚15份,丙烯酸乙酯9份,混合搅拌即得产品。An anti-condensation coating comprising the following components by weight, 21 parts of zinc oxide, 12 parts of benzoyl peroxide, 15 parts of dibutyl phthalate, 15 parts of triphenyl phosphate, isopropyl acrylate 6 parts, 51 parts of styrene, 160 parts of butyl acrylate, 80 parts of acrylic acid, 90 parts of methyl methacrylate, 15 parts of zinc carbonate ammonia, 30 parts of titanium dioxide, 15 parts of ethylene glycol monopropyl ether, 9 parts of ethyl acrylate Mix and stir to get the product.
实施例3Example 3
一种防结露涂胶,包括如下重量份的组分,氧化锌30份,过氧化苯甲酰16份,邻苯二甲酸二丁酯20份,磷酸三苯酯20份,丙烯酸异丙酯10份,苯乙烯80份,丙烯酸丁酯200份,丙烯酸120份,甲基丙烯酸甲酯100份,碳酸锌氨20份,二氧化钛40份,乙二醇单丙醚20份,丙烯酸乙酯12份,混合搅拌即得产品。An anti-condensation coating comprising the following components by weight, 30 parts of zinc oxide, 16 parts of benzoyl peroxide, 20 parts of dibutyl phthalate, 20 parts of triphenyl phosphate, isopropyl acrylate 10 parts, 80 parts of styrene, 200 parts of butyl acrylate, 120 parts of acrylic acid, 100 parts of methyl methacrylate, 20 parts of zinc carbonate ammonia, 40 parts of titanium dioxide, 20 parts of ethylene glycol monopropyl ether, 12 parts of ethyl acrylate Mix and stir to get the product.
以上所述仅是本发明的优选方式,应当指出,对于本领域普通技术人员来说,在不脱离本发明创造构思的前提下,还可以做出若干相似的变形和改进,这些也应视为本发明的保护范围之内。
The above is only a preferred mode of the present invention, and it should be noted that various similar modifications and improvements can be made by those skilled in the art without departing from the inventive concept. Within the scope of protection of the present invention.
Claims (1)
- 一种防结露涂胶,其特征在于:包括如下重量份的组分,An anti-condensation coating characterized by comprising the following components by weight,氧化锌12~30份,过氧化苯甲酰8~16份,邻苯二甲酸二丁酯10~20份,磷酸三苯酯10~20份,丙烯酸异丙酯2~10份,苯乙烯20~80份,丙烯酸丁酯120~200份,丙烯酸40~120份,甲基丙烯酸甲酯80~100份,碳酸锌氨10~20份,二氧化钛20~40份,乙二醇单丙醚10~20份,丙烯酸乙酯6~12份。 12 to 30 parts of zinc oxide, 8 to 16 parts of benzoyl peroxide, 10 to 20 parts of dibutyl phthalate, 10 to 20 parts of triphenyl phosphate, 2 to 10 parts of isopropyl acrylate, and styrene 20 ~80 parts, 120-200 parts of butyl acrylate, 40-120 parts of acrylic acid, 80-100 parts of methyl methacrylate, 10-20 parts of zinc carbonate ammonia, 20-40 parts of titanium dioxide, 10~ ethylene glycol monopropyl ether 20 parts, ethyl acrylate 6 to 12 parts.