CN104513511A - Optical photosensitive coating - Google Patents

Abstract

The invention discloses an optical photosensitive coating. The optical photosensitive coating comprises the following components in parts by weight: 12 to 36 parts of epoxy resin, 20 to 30 parts of graphite pebbles, 16 to 18 parts of vanadium trioxide, 10 to 20 parts of azo-dicarbonamide, 4 to 12 parts of benzoyl peroxide, 12 to 24 parts of isopropyl alcohol, 12 to 18 parts of dibutyl phthalate, 10 to 20 parts of triphenyl phosphate, 4 to 8 parts of isopropyl acrylate, 8 to 12 parts of butyl acetate, and 4 to 12 parts of ethylene glycol. The optical photosensitive coating provided by the invention has the advantages that the preparation is simple; the adopted raw materials are non-toxic, so that the coating is good in use effect and environment-friendly; the coating can be photo-cured, so as to achieve high optical transparency, as well as good anti-ultraviolet and wear-resistant performance.

Description

A kind of optical light coating

Technical field

The present invention relates to a kind of technical field of chemical article, be specifically related to a kind of optical light coating.

Background technology

The effect of coating in production and life is very large; widespread use and every field; the film that coating is formed can play decoration, protection and beautiful effect to object; although current most of coating on the market makes simply, price is cheap but function ratio is more single simultaneously; can only simply as the use of decoration; and in the operating environment that some are special, can not meeting needed for people of simple coating.

Summary of the invention

Object of the present invention provides a kind of optical light coating, solves one or more in above-mentioned prior art problem.

According to an aspect of the present invention, a kind of optical light coating, comprises the component of following weight part,

Epoxy resin 12 ~ 36 parts, graphite pebbles 20 ~ 30 parts, vanadous oxide 16 ~ 18 parts, azodicarbonamide 10 ~ 20 parts, benzoyl peroxide 4 ~ 12 parts, Virahol 12 ~ 24 parts, dibutyl phthalate 12 ~ 18 parts, triphenylphosphate 10 ~ 20 parts, isopropyl acrylate 4 ~ 8 parts, butylacetate 8 ~ 12 parts, ethylene glycol 4 ~ 12 parts.

A kind of optical light coating provided by the invention, makes simple, and the raw materials for production of employing are selected avirulent, and the result of use of coating is good, environmental protection, and this coating can photo-curing, forms optics high-clarity, has ultraviolet resistance, wear resisting property.

Embodiment

Embodiment 1

By epoxy resin 12 parts, graphite pebbles 20 parts, vanadous oxide 16 parts, azodicarbonamide 10 parts, benzoyl peroxide 4 parts, Virahol 12 parts, dibutyl phthalate 12 parts, triphenylphosphate 10 parts, isopropyl acrylate 4 parts, butylacetate 8 parts, reactor put into by ethylene glycol 4 parts, continuous stirring, mixes complete post-heating to 65 DEG C, namely obtains product after uniform stirring.

Embodiment 2

By epoxy resin 24 parts, graphite pebbles 25 parts, vanadous oxide 17 parts, azodicarbonamide 15 parts, benzoyl peroxide 8 parts, Virahol 18 parts, dibutyl phthalate 15 parts, triphenylphosphate 15 parts, isopropyl acrylate 6 parts, butylacetate 10 parts, reactor put into by ethylene glycol 8 parts, continuous stirring, mixes complete post-heating to 65 DEG C, namely obtains product after uniform stirring.

Embodiment 3

By epoxy resin 36 parts, graphite pebbles 30 parts, vanadous oxide 18 parts, azodicarbonamide 20 parts, benzoyl peroxide 12 parts, Virahol 24 parts, dibutyl phthalate 18 parts, triphenylphosphate 20 parts, isopropyl acrylate 8 parts, butylacetate 12 parts, reactor put into by ethylene glycol 12 parts, continuous stirring, mixes complete post-heating to 65 DEG C, namely obtains product after uniform stirring.

The above is only optimal way of the present invention; it should be pointed out that to those skilled in the art, without departing from the concept of the premise of the invention; can also make some similar distortion and improvement, these also should be considered as within protection scope of the present invention.

Claims (1)

1. an optical light coating, is characterized in that: the component comprising following weight part,

Epoxy resin 12 ~ 36 parts, graphite pebbles 20 ~ 30 parts, vanadous oxide 16 ~ 18 parts, azodicarbonamide 10 ~ 20 parts, benzoyl peroxide 4 ~ 12 parts, Virahol 12 ~ 24 parts, dibutyl phthalate 12 ~ 18 parts, triphenylphosphate 10 ~ 20 parts, isopropyl acrylate 4 ~ 8 parts, butylacetate 8 ~ 12 parts, ethylene glycol 4 ~ 12 parts.