CN105086848A - Mould-proof glue - Google Patents

Abstract

The invention discloses mould-proof glue. The mould-proof glue comprises, by weight, 10-28 parts of styrene, 10-24 parts of ethyl alcohol, 20-30 parts of poly-isobutyl ester, 10-30 parts of aluminum hydroxide, 8-12 parts of asbestos fibers, 20-30 parts of graphite nodules, 20-40 parts of methoxyphenol, 10-12 parts of acetone, 4-12 parts of acrylamide, 24-48 parts of phosphotriester, 12-18 parts of antimonous oxide, 12-16 parts of styrene, 150-200 parts of butyl methacrylate, 20-40 parts of methacrylic acid, 8-16 parts of dehydroacetic acid and 20-40 parts of butanol. The mould-proof glue is easy to manufacture, adopted and selected production raw materials are free of toxicity, the glue is good in use effect and environmentally friendly, a tough coating can be formed, and permanent waterproofness and antistatic performance are achieved.

Description

A kind of mildew-resistant glue

Technical field

The present invention relates to a kind of technical field of chemical article, be specifically related to a kind of mildew-resistant glue.

Background technology

The effect of glue in production and life is very large; widespread use and every field; the film that glue is formed can play decoration, protection and beautiful effect to object; although current most of glue on the market makes simply, price is cheap but function ratio is more single simultaneously; can only simply as the use of decoration; and in the operating environment that some are special, can not meeting needed for people of simple glue.

Summary of the invention

Object of the present invention provides a kind of mildew-resistant glue, solves one or more in above-mentioned prior art problem.

According to an aspect of the present invention, a kind of mildew-resistant glue, comprises the component of following weight part,

Vinylbenzene 10 ~ 28 parts, ethanol 10 ~ 24 parts, poly-isobutyl ester 20-30 part, 10 ~ 30 parts, aluminium hydroxide, fibrous magnesium silicate 8 ~ 12 parts, graphite pebbles 20 ~ 30 parts, methoxyphenol 20 ~ 40 parts, 10 ~ 12 parts, acetone, acrylamide 4 ~ 12 parts, phosphotriester 24 ~ 48 parts, antimonous oxide 12 ~ 18 parts, vinylbenzene 12 ~ 16 parts, butyl methacrylate 150 ~ 200 parts, methacrylic acid 20 ~ 40 parts, dehydroacetic acid (DHA) 8 ~ 16 parts, 20 ~ 40 parts, butanols.

A kind of mildew-resistant glue provided by the invention, makes simple, and the raw materials for production of employing are selected avirulent, and the result of use of glue is good, environmental protection, and bonding effect is good, has good anti-mildew performance.

Embodiment

Embodiment 1

A kind of mildew-resistant glue, comprises the component of following weight part, vinylbenzene 10 parts, ethanol 10 parts, poly-isobutyl ester 20 parts, 10 parts, aluminium hydroxide, fibrous magnesium silicate 8 parts, graphite pebbles 20 parts, methoxyphenol 20 parts, 10 parts, acetone, acrylamide 4 parts, phosphotriester 24 parts, antimonous oxide 12 parts, vinylbenzene 12 parts, butyl methacrylate 150 parts, methacrylic acid 20 parts, dehydroacetic acid (DHA) 8 parts, 20 parts, butanols, namely mix and blend obtains product.

Embodiment 2

A kind of mildew-resistant glue, comprises the component of following weight part, vinylbenzene 17 parts, ethanol 17 parts, poly-isobutyl ester 25 parts, 20 parts, aluminium hydroxide, fibrous magnesium silicate 10 parts, graphite pebbles 25 parts, methoxyphenol 30 parts, 11 parts, acetone, acrylamide 8 parts, phosphotriester 36 parts, antimonous oxide 15 parts, vinylbenzene 14 parts, butyl methacrylate 175 parts, methacrylic acid 30 parts, dehydroacetic acid (DHA) 12 parts, 30 parts, butanols, namely mix and blend obtains product.

Embodiment 3

A kind of mildew-resistant glue, comprises the component of following weight part, vinylbenzene 28 parts, ethanol 24 parts, poly-isobutyl ester 30 parts, 30 parts, aluminium hydroxide, fibrous magnesium silicate 12 parts, graphite pebbles 30 parts, methoxyphenol 40 parts, 12 parts, acetone, acrylamide 12 parts, phosphotriester 48 parts, antimonous oxide 18 parts, vinylbenzene 16 parts, butyl methacrylate 200 parts, methacrylic acid 40 parts, dehydroacetic acid (DHA) 16 parts, 40 parts, butanols, namely mix and blend obtains product.

The above is only optimal way of the present invention; it should be pointed out that to those skilled in the art, without departing from the concept of the premise of the invention; can also make some similar distortion and improvement, these also should be considered as within protection scope of the present invention.

Claims (1)

1. a mildew-resistant glue, is characterized in that: the component comprising following weight part,

Vinylbenzene 10 ~ 28 parts, ethanol 10 ~ 24 parts, poly-isobutyl ester 20-30 part, 10 ~ 30 parts, aluminium hydroxide, fibrous magnesium silicate 8 ~ 12 parts, graphite pebbles 20 ~ 30 parts, methoxyphenol 20 ~ 40 parts, 10 ~ 12 parts, acetone, acrylamide 4 ~ 12 parts, phosphotriester 24 ~ 48 parts, antimonous oxide 12 ~ 18 parts, vinylbenzene 12 ~ 16 parts, butyl methacrylate 150 ~ 200 parts, methacrylic acid 20 ~ 40 parts, dehydroacetic acid (DHA) 8 ~ 16 parts, 20 ~ 40 parts, butanols.