CN104559505A - Waterproof paint - Google Patents

Waterproof paint Download PDF

Info

Publication number
CN104559505A
CN104559505A CN 201410809306 CN201410809306A CN104559505A CN 104559505 A CN104559505 A CN 104559505A CN 201410809306 CN201410809306 CN 201410809306 CN 201410809306 A CN201410809306 A CN 201410809306A CN 104559505 A CN104559505 A CN 104559505A
Authority
CN
Grant status
Application
Patent type
Prior art keywords
parts
methacrylate
styrene
waterproof paint
methyl
Prior art date
Application number
CN 201410809306
Other languages
Chinese (zh)
Inventor
刘骏
Original Assignee
刘骏
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

The invention discloses a waterproof paint. The waterproof paint comprises the following components in parts by weight: 75-125 parts of methyl acrylic acid-2-hydroxy ethyl acrylate, 20-40 parts of methyl acrylic acid, 100-150 parts of methyl methacrylate, 80-100 parts of dodecyl methacrylate, 200-300 parts of styrene, 150-200 parts of butyl methacrylate and 20-40 parts of styrene. The waterproof paint disclosed by the invention is simple to prepare, is prepared from nontoxic production raw materials, is good in using effect, is environment-friendly, is capable of forming a firm and tenacious coating, and has long-lasting waterproofness and antistatic property.

Description

一种耐水性涂料 One kind of water-resistant coating

技术领域 FIELD

[0001] 本发明涉及一种化学用品的技术领域,具体涉及一种耐水性涂料。 [0001] The present invention relates to the technical field of chemicals, in particular, to a water-resistant coating.

背景技术 Background technique

[0002] 涂料在生产和生活中的作用非常大,广泛应用与各个领域,涂料形成的涂膜可对物体起到装饰、保护和标致作用,目前市面上的大部分涂料虽然制作简单、售价便宜但同时功能比较单一,只能简单的作为装饰之用,而在一些特殊的作业环境中,简单的涂料的并不能满足人们的所需。 [0002] role in the production of paint and life is very large, widely used in various fields, film coatings may play a decorative form of the object, protection and Peugeot effect, although currently most of the paint market making simple, price cheap but relatively simple function only as a simple decorative purposes, and in some special operating environment, a simple paint does not meet people's needs.

发明内容 SUMMARY

[0003] 本发明的目的提供一种耐水性涂料,解决上述现有技术问题中的一个或者多个。 [0003] The object of the present invention to provide a water-resistant coating, address one or more of the above-described prior art problems.

[0004] 根据本发明的一个方面,一种耐水性涂料,包括如下重量份的组分, [0004] In accordance with one aspect of the present invention, a water-resistant coating, comprising parts by weight of component,

[0005] 甲基丙烯酸-2-羟乙酯75〜125份,甲基丙烯酸20〜40份,甲基丙烯酸甲酯100〜150份,甲基丙烯酸月桂酯80〜100份,苯乙烯200〜300份,甲基丙烯酸丁酯150〜200份,苯乙烯20〜40份。 [0005] methyl 75~125 parts of 2-hydroxyethyl methacrylate, methacrylic acid parts of 20~40, 100~150 parts of methyl methacrylate, 80 ~ 100 parts of lauryl methacrylate, styrene 200-300 parts, 150~200 parts of butyl methacrylate, styrene 20~40 parts.

[0006] 本发明提供的一种耐水性涂料,制作简单,采用的生产原料选择无毒性的,涂料的使用效果好,环保,可形成坚韧涂层,具有持久的防水性和抗静电性。 [0006] The present invention provides a water-resistant coating, making simple, selection of raw materials used in the production of non-toxic, the use of effective coatings, environmental protection, can form a tough coating having durable water repellency and antistatic properties.

具体实施方式 detailed description

[0007] 实施例1 [0007] Example 1

[0008] 一种耐水性涂料,包括如下重量份的组分,甲基丙烯酸-2-羟乙酯75份,甲基丙烯酸20份,甲基丙烯酸甲酯100份,甲基丙烯酸月桂酯80份,苯乙烯200份,甲基丙烯酸丁酯150份,苯乙烯20份;甲基丙烯酸-2-羟乙酯75份,甲基丙烯酸20份,甲基丙烯酸甲酯100份,甲基丙烯酸月桂酯80份,苯乙烯200份,甲基丙烯酸丁酯150份,苯乙烯20份,混合搅拌即得产品。 [0008] A water-resistant coating, comprising parts by weight of component methacrylate, 75 parts of 2-hydroxyethyl methacrylate, 20 parts of methacrylic acid, 100 parts of methyl methacrylate, 80 parts of lauryl methacrylate , 200 parts of styrene, 150 parts of butyl methacrylate, 20 parts of styrene; methacrylate, 75 parts of 2-hydroxyethyl methacrylate, 20 parts of methacrylic acid, 100 parts of methyl methacrylate, lauryl methacrylate 80 parts of 200 parts of styrene, 150 parts of butyl methacrylate, 20 parts of styrene, mixed and stirred to obtain product.

[0009] 实施例2 [0009] Example 2

[0010] 一种耐水性涂料,包括如下重量份的组分,甲基丙烯酸-2-羟乙酯100份,甲基丙烯酸30份,甲基丙烯酸甲酯125份,甲基丙烯酸月桂酯90份,苯乙烯250份,甲基丙烯酸丁酯175份,苯乙烯30份;甲基丙烯酸-2-羟乙酯100份,甲基丙烯酸30份,甲基丙烯酸甲酯125份,甲基丙烯酸月桂酯90份,苯乙烯250份,甲基丙烯酸丁酯175份,苯乙烯30份,混合搅拌即得产品。 [0010] A water-resistant coating, comprising parts by weight of component methacrylate, 100 parts of 2-hydroxyethyl methacrylate, 30 parts of methacrylic acid, 125 parts of methyl methacrylate, 90 parts of lauryl methacrylate , 250 parts of styrene, 175 parts of butyl methacrylate, 30 parts of styrene; methacrylate, 2-hydroxyethyl methacrylate 100 parts, 30 parts of methacrylic acid, 125 parts of methyl methacrylate, lauryl methacrylate 90 parts of 250 parts of styrene, 175 parts of butyl methacrylate, 30 parts of styrene, mixed and stirred to obtain product.

[0011] 实施例3 [0011] Example 3

[0012] —种耐水性涂料,包括如下重量份的组分,甲基丙烯酸-2-羟乙酯125份,甲基丙烯酸40份,甲基丙烯酸甲酯150份,甲基丙烯酸月桂酯100份,苯乙烯300份,甲基丙烯酸丁酯200份,苯乙烯40份;甲基丙烯酸-2-羟乙酯125份,甲基丙烯酸40份,甲基丙烯酸甲酯150份,甲基丙烯酸月桂酯100份,苯乙烯300份,甲基丙烯酸丁酯200份,苯乙烯40份,混合搅拌即得产品。 [0012] - seed coating water resistance, comprising the following parts by weight of component methacrylate, 125 parts of 2-hydroxyethyl methacrylate, 40 parts of methacrylic acid, 150 parts of methyl methacrylate, 100 parts of lauryl methacrylate , 300 parts of styrene, 200 parts of butyl methacrylate, 40 parts of styrene; methacrylate, 125 parts of 2-hydroxyethyl methacrylate, 40 parts of methacrylic acid, 150 parts of methyl methacrylate, lauryl methacrylate 100 parts, 300 parts of styrene, 200 parts of butyl methacrylate, 40 parts of styrene, mixed and stirred to obtain product.

[0013] 以上所述仅是本发明的优选方式,应当指出,对于本领域普通技术人员来说,在不脱离本发明创造构思的前提下,还可以做出若干相似的变形和改进,这些也应视为本发明的保护范围之内。 [0013] The above are only preferred embodiment of the present invention, it should be noted that those of ordinary skill in the art, without departing from the concept of the present invention to create a premise, can make various modifications and similar improvements, which are also It should be considered within the scope of the present invention.

Claims (1)

  1. 1.一种耐水性涂料,其特征在于:包括如下重量份的组分, 甲基丙烯酸-2-羟乙酯75〜125份,甲基丙烯酸20〜40份,甲基丙烯酸甲酯100〜150份,甲基丙烯酸月桂酯80〜100份,苯乙烯200〜300份,甲基丙烯酸丁酯150〜200份,苯乙烯20〜40份。 A water-resistant coating, characterized by: comprising the following parts by weight of component, methacrylate, 2-hydroxyethyl methacrylate 75~125 parts of 20~40 parts of methacrylic acid, methyl methacrylate 100~150 parts, 80 ~ 100 parts of lauryl methacrylate, 200 to 300 parts of styrene, butyl methacrylate 150~200 parts of 20~40 parts of styrene.
CN 201410809306 2014-12-23 2014-12-23 Waterproof paint CN104559505A (en)