CN105802300A - Water-based glue - Google Patents

Abstract

The invention discloses water-based glue, which is prepared from the following components in parts by weight: 100-160 parts of polyester, 20-40 parts of butanediol acrylate, 40-60 parts of trimethylolpropane, 20-60 parts of polyimide, 40-60 parts of polyisobutyl ester, 20-40 parts of vanadium trioxide, 10-20 parts of azodicarbonamide, 8-12 parts of zinc oxide, 2-8 parts of benzoyl peroxide, 40-80 parts of phenol-formaldehyde resin, 20-30 parts of acetone, 10-18 parts of dibutyl phthalate and 8-20 parts of triphenyl phosphate. The water-based glue disclosed by the invention is simple in preparation; the adopted production raw materials are nontoxic; the glue is good in using effect and environmentally friendly; and a glue coating has good anti-static fire resistance.

Description

A kind of water-based glue

Technical field

The present invention relates to the technical field of a kind of chemical article, be specifically related to a kind of water-based glue.

Background technology

Glue effect in producing and living is very big; extensive use and every field; object can be played decoration, protection and beautiful effect by the film that glue is formed; although most of glue on the market makes simply at present, price is cheap but function is more single simultaneously; can only simply as the use of decoration; and in the working environment that some are special, simple glue can not meet people needed for.

Summary of the invention

It is an object of the invention to provide a kind of water-based glue, solve one or more in above-mentioned prior art problem.

According to an aspect of the present invention, a kind of water-based glue, including the component of following weight portion,

Polyester 100～160 parts, butylene glycol aerylate 20～40 parts, trimethylolpropane 40～60 parts, polyimides 20～60 parts, poly-isobutyl ester 40～60 parts, Vanadium sesquioxide 20～40 parts, azo dicarbonamide 10～20 parts, zinc oxide 8～12 parts, benzoyl peroxide 2～8 parts, 40～80 parts of phenolic resin, 20～30 parts of acetone, dibutyl phthalate 10～18 parts, triphenyl phosphate 8～20 parts.

A kind of water-based glue provided by the invention, makes simple, and the raw materials for production of employing select avirulent, and the result of use of glue is good, environmental protection, acts on leather surface covering with paint and can form firm bright film.

Detailed description of the invention

Embodiment 1

By polyester 100 parts, butylene glycol aerylate 20 parts, trimethylolpropane 40 parts, polyimides 20 parts, poly-isobutyl ester 40 parts, Vanadium sesquioxide 20 parts, azo dicarbonamide 10 parts, zinc oxide 8 parts, benzoyl peroxide 2 parts, 40 parts of phenolic resin, 20 parts of acetone, dibutyl phthalate 10 parts, triphenyl phosphate 8 parts is put in reactor, it is stirred continuously, mixes complete post-heating to 50 DEG C, after uniform stirring, namely obtain product.

Embodiment 2

By polyester 100～160 parts, butylene glycol aerylate 20～40 parts, trimethylolpropane 40～60 parts, polyimides 20～60 parts, poly-isobutyl ester 40～60 parts, Vanadium sesquioxide 20～40 parts, azo dicarbonamide 10～20 parts, zinc oxide 8～12 parts, benzoyl peroxide 2～8 parts, 40～80 parts of phenolic resin, 20～30 parts of acetone, dibutyl phthalate 10～18 parts, triphenyl phosphate 8～20 parts is put in reactor, it is stirred continuously, mixes complete post-heating to 50 DEG C, after uniform stirring, namely obtain product.

Embodiment 3

By polyester 160 parts, butylene glycol aerylate 40 parts, trimethylolpropane 60 parts, polyimides 60 parts, poly-isobutyl ester 60 parts, Vanadium sesquioxide 40 parts, azo dicarbonamide 20 parts, zinc oxide 12 parts, benzoyl peroxide 8 parts, 80 parts of phenolic resin, 30 parts of acetone, dibutyl phthalate 18 parts, triphenyl phosphate 20 parts is put in reactor, it is stirred continuously, mixes complete post-heating to 50 DEG C, after uniform stirring, namely obtain product.

The above is only the optimal way of the present invention, it is noted that to those skilled in the art, without departing from the concept of the premise of the invention, it is also possible to making some similar deformation and improvement, these also should be regarded as within protection scope of the present invention.

Claims (1)

1. a water-based glue, it is characterised in that: include the component of following weight portion,

Polyester 100～160 parts, butylene glycol aerylate 20～40 parts, trimethylolpropane 40～60 parts, polyimides 20～60 parts, poly-isobutyl ester 40～60 parts, Vanadium sesquioxide 20～40 parts, azo dicarbonamide 10～20 parts, zinc oxide 8～12 parts, benzoyl peroxide 2～8 parts, 40～80 parts of phenolic resin, 20～30 parts of acetone, dibutyl phthalate 10～18 parts, triphenyl phosphate 8～20 parts.