CN104277616A - Anti-freezing interior wall coating - Google Patents
Anti-freezing interior wall coating Download PDFInfo
- Publication number
- CN104277616A CN104277616A CN201410607081.1A CN201410607081A CN104277616A CN 104277616 A CN104277616 A CN 104277616A CN 201410607081 A CN201410607081 A CN 201410607081A CN 104277616 A CN104277616 A CN 104277616A
- Authority
- CN
- China
- Prior art keywords
- parts
- interior wall
- wall coating
- coating
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-freezing interior wall coating comprising the following raw materials in parts by weight: 100 parts of polyvinyl alcohol resin, 40-50 parts of carboxymethylcellulose, 15-20 parts of polyvinyl acetate, 30-40 parts of methyl ethyl ketone, 80-100 parts of water, 10-20 parts of triethylamine, 20-40 parts of a coloring pigment, 5-10 parts of butyl alcohol, 40-50 parts of zeolite, 5-15 parts of cresol, 60-80 parts of an extender pigment, 20-30 parts of silicon dioxide powder, 40-60 parts of talcum powder and 15-25 parts of ammonia water. According to the anti-freezing interior wall coating disclosed by the invention, the viscosity of a product is 30-60s, the fineness is 70-90 microns, the surface drying time is 0.5-0.8h, blistering and powder falling phenomena cannot be generated after the coating is soaked in water for 2-3 days, the whiteness is 90-100, and a freezing phenomenon cannot be caused at -10 DEG C; and the anti-freezing interior wall coating is flat and smooth in film coating, ensures that the scrub resistance and adhesive force can reach 100%, and can be widely produced for continuously replacing existing materials.
Description
Technical field
The application belongs to paint field, particularly relates to a kind of freeze proof interior wall coating.
Background technology
Coating refers to and is applied to body surface and the general name forming the material of tough and tensile protective membrane, and building coating is an important class in coating, in China, generally will be used for inner wall of building, exterior wall, ceiling, ground, and the coating of toilet is called building coating.China's coating circle more authoritative " coating process " book is definition like this: " coating is a kind of material, and this material can be coated in article surface by different construction technologies, forms adhere well, has some strength, continuous print solid film.The film common name film of such formation, also known as paint film or coating." paint finishing can bond very well with body material in body surface and form the material of complete and tough and tensile protective membrane, is called coating.Coating and paint are identical concepts.Paint is people's custom titles used for a long time, after introducing China, just utilizes in building trade always.The effect of coating may be summarized to be three aspects: provide protection, decoration function, specific function effect.The general composition of coating: comprise filmogen, color stuffing, solvent, auxiliary agent.
Building coating has decoration functions, defencive function and livability and improves function.Proportion shared by various function is not quite similar because application target is different.Decoration functions is the function of beautifying the appearance value improving it by buildings.Mainly comprise the design design of plane color, pattern and gloss aspect and the design design of three-dimensional pattern.But to match with the size and shape of the moulding of buildings itself and base material itself, just can fully play out.Defencive function refers to architecture protection thing not by the impact of environment and the function of destruction.The content that different types of protected body requires defencive function is also different.As just very large in the indoor index difference with reaching required by outdoor application.Some buildingss to mildew-resistant, fire prevention, heat insulating, corrosion-resistant etc. have particular requirement.Livability improves function mainly for indoor application, contributes to the function improving living environment exactly, as sound-proofing, sound absorbing, antisweat etc.China's paint industry grows stronger day by day under the promotion of downstream industry, and as the building coating of one of them branch, have also been obtained significant progress.Statistic data shows, and within 2011, Chinese architecture coating amounts to output about 351.82 ten thousand tons, increases by more than 30% on a year-on-year basis.As can be seen here, although Chinese architecture paint industry experienced by the impact of global financial crisis in 2008, the prices of raw and semifnished materials go up and Central Bank the increases the interest pressure brought, its growth momentum does not still subtract, and also maintains higher rate of increase.
Interior wall coating is exactly the emulsion paint generally fitted up.Namely emulsion paint is emulsion coating, according to the difference of base material, is divided into polyvinyl acetate emulsion and the large class of ACRYLIC EMULSION two.Emulsion paint is thinner with water, be a kind of easy construction, safe, water-fastness, good permeability coating, it can mix different color and lusters according to different scheme of colo(u)r.Kind: water-based inner wall paint, oiliness interior wall paint, dry powder type interior wall paint, belongs to water-borne coatings, and primarily of water, emulsion, pigment, filler, additive five kinds of compositions are formed.And popularizing along with humanity concept, and the formation of novel harmonious society, the freeze proof interior wall coating designing a kind of moisture resistance and frost resistance excellence is very important.
Summary of the invention
The technical problem solved:
The application, for above-mentioned technical problem, provides a kind of freeze proof interior wall coating, solve existing freeze proof interior wall coating easy to foaming, come off, the technical problems such as whiteness is low, cryoprotective effects is not obvious.
Technical scheme:
A kind of freeze proof interior wall coating, the raw materials by weight portion proportioning of described freeze proof interior wall coating is as follows: polyvinyl alcohol resin 100 parts; Carboxymethyl cellulose 40-50 part; Polyvinyl acetate (PVA) 15-20 part; Methylethylketone 30-40 part; Water 80-100 part; Triethylamine 10-20 part; Tinting pigment 20-40 part; Butanols 5-10 part; Zeolite 40-50 part; Cresols 5-15 part; Pigment extender 60-80 part; Silicon dioxide powder 20-30 part; Talcum powder 40-60 part; Ammoniacal liquor 15-25 part.
As a preferred technical solution of the present invention: the raw materials by weight portion proportioning of described freeze proof interior wall coating is as follows: polyvinyl alcohol resin 100 parts; Carboxymethyl cellulose 45 parts; Polyvinyl acetate (PVA) 18 parts; Methylethylketone 35 parts; 90 parts, water; Triethylamine 15 parts; Tinting pigment 30 parts; 7 parts, butanols; 45 parts, zeolite; 10 parts, cresols; Pigment extender 70 parts; Silicon dioxide powder 25 parts; Talcum powder 50 parts; Ammoniacal liquor 20 parts.
As a preferred technical solution of the present invention: described tinting pigment adopts titanium dioxide.
As a preferred technical solution of the present invention: described pigment extender adopts light calcium carbonate.
Beneficial effect:
The freeze proof interior wall coating of one of the present invention adopts above technical scheme compared with prior art, has following technique effect: 1, product viscosity 30-60s, fineness 70-90 μm; 2, surface drying 0.5-0.8h, to soak after 2-3d without bubbling, shedding phenomenon in water; 3, whiteness 90-100 ,-10 DEG C are not freezed; 4, smooth coating is smooth, abrasion resistance, sticking power 100%, the widespread production not division of history into periods can replace current material.
Embodiment
Embodiment 1:
A kind of freeze proof interior wall coating, its raw materials by weight portion proportioning is as follows: polyvinyl alcohol resin 100 parts; Carboxymethyl cellulose 40 parts; Polyvinyl acetate (PVA) 15 parts; Methylethylketone 30 parts; 80 parts, water; Triethylamine 10 parts; Titanium dioxide 20 parts; 5 parts, butanols; 40 parts, zeolite; 5 parts, cresols; Light calcium carbonate 60 parts; Silicon dioxide powder 20 parts; Talcum powder 40 parts; Ammoniacal liquor 15 parts.
Polyvinyl alcohol resin and water are loaded in reactor, heat while stirring to 90 DEG C, carboxymethyl cellulose, methylethylketone, triethylamine, silicon dioxide powder and ammoniacal liquor is added after polyvinyl alcohol resin dissolves completely, be cooled to 30 DEG C, add polyvinyl acetate (PVA) reaction 0.8h, add titanium dioxide, light calcium carbonate and surplus stock, after mixing, both obtain finished product.
Product viscosity 30s, fineness 70 μm; Surface drying 0.8h, to soak after 2d without bubbling, shedding phenomenon in water; Whiteness 90 ,-5 DEG C are not freezed, sticking power 100%.
Embodiment 2:
A kind of freeze proof interior wall coating, its raw materials by weight portion proportioning is as follows: polyvinyl alcohol resin 100 parts; Carboxymethyl cellulose 50 parts; Polyvinyl acetate (PVA) 20 parts; Methylethylketone 40 parts; 100 parts, water; Triethylamine 20 parts; Titanium dioxide 40 parts; 10 parts, butanols; 50 parts, zeolite; 15 parts, cresols; Light calcium carbonate 80 parts; Silicon dioxide powder 30 parts; Talcum powder-60 parts; Ammoniacal liquor 25 parts.
Polyvinyl alcohol resin and water are loaded in reactor, heat while stirring to 100 DEG C, carboxymethyl cellulose, methylethylketone, triethylamine, silicon dioxide powder and ammoniacal liquor is added after polyvinyl alcohol resin dissolves completely, be cooled to 40 DEG C, add polyvinyl acetate (PVA) reaction 1.2h, add titanium dioxide, light calcium carbonate and surplus stock, after mixing, both obtain finished product.
Product viscosity 60s, fineness 90 μm; Surface drying 0.6h, to soak after 2.5d without bubbling, shedding phenomenon in water; Whiteness 95 ,-8 DEG C are not freezed, sticking power 100%.
Embodiment 3:
A kind of freeze proof interior wall coating, its raw materials by weight portion proportioning is as follows: polyvinyl alcohol resin 100 parts; Carboxymethyl cellulose 45 parts; Polyvinyl acetate (PVA) 18 parts; Methylethylketone 35 parts; 90 parts, water; Triethylamine 15 parts; Titanium dioxide 30 parts; 7 parts, butanols; 45 parts, zeolite; 10 parts, cresols; Light calcium carbonate 70 parts; Silicon dioxide powder 25 parts; Talcum powder 50 parts; Ammoniacal liquor 20 parts.
Polyvinyl alcohol resin and water are loaded in reactor, heat while stirring to 95 DEG C, carboxymethyl cellulose, methylethylketone, triethylamine, silicon dioxide powder and ammoniacal liquor is added after polyvinyl alcohol resin dissolves completely, be cooled to 35 DEG C, add polyvinyl acetate (PVA) reaction 1h, add titanium dioxide, light calcium carbonate and surplus stock, after mixing, both obtain finished product.
Product viscosity 45s, fineness 80 μm; Surface drying 0.5h, to soak after 3d without bubbling, shedding phenomenon in water; Whiteness 100 ,-10 DEG C are not freezed, sticking power 100%.
Composition all components in above embodiment all can business be bought.
Above-described embodiment is just for setting forth content of the present invention, instead of restriction, and any change therefore in the implication suitable with claims of the present invention and scope, all should think to be included in the scope of claims.
Claims (4)
1. a freeze proof interior wall coating, is characterized in that the raw materials by weight portion proportioning of described freeze proof interior wall coating is as follows: polyvinyl alcohol resin 100 parts; Carboxymethyl cellulose 40-50 part; Polyvinyl acetate (PVA) 15-20 part; Methylethylketone 30-40 part; Water 80-100 part; Triethylamine 10-20 part; Tinting pigment 20-40 part; Butanols 5-10 part; Zeolite 40-50 part; Cresols 5-15 part; Pigment extender 60-80 part; Silicon dioxide powder 20-30 part; Talcum powder 40-60 part; Ammoniacal liquor 15-25 part.
2. the freeze proof interior wall coating of one according to claim 1, is characterized in that the raw materials by weight portion proportioning of described freeze proof interior wall coating is as follows: polyvinyl alcohol resin 100 parts; Carboxymethyl cellulose 45 parts; Polyvinyl acetate (PVA) 18 parts; Methylethylketone 35 parts; 90 parts, water; Triethylamine 15 parts; Tinting pigment 30 parts; 7 parts, butanols; 45 parts, zeolite; 10 parts, cresols; Pigment extender 70 parts; Silicon dioxide powder 25 parts; Talcum powder 50 parts; Ammoniacal liquor 20 parts.
3. the freeze proof interior wall coating of one according to claim 1, is characterized in that: described tinting pigment adopts titanium dioxide.
4. the freeze proof interior wall coating of one according to claim 1, is characterized in that: described pigment extender adopts light calcium carbonate.