CN106366713A - Delicate-fragrant-type environment-friendly wall surface coating - Google Patents
Delicate-fragrant-type environment-friendly wall surface coating Download PDFInfo
- Publication number
- CN106366713A CN106366713A CN201610724903.3A CN201610724903A CN106366713A CN 106366713 A CN106366713 A CN 106366713A CN 201610724903 A CN201610724903 A CN 201610724903A CN 106366713 A CN106366713 A CN 106366713A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- nano
- coating
- attapulgite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a delicate-fragrant-type environment-friendly wall surface coating which includes, by weight, 2-3 parts of polypropylene oxide glycol, 1-2 parts of propyl gallate, 0.8-1 part of Chinese tallow oil, 0.7-1 part of n-salicylaniline, 1-2 parts of calcium lactate, 2-3 parts of palm wax, 3-4 parts of poly(1,2-propylene glycol adipate), 0.7-2 parts of polybenzimidazole, 5-7 parts of attapulgite, 10-13 parts of potassium feldspar powder, 100-140 parts of butyl acrylate, 160-200 parts of vinyl acetate, 5-7 parts of walnut shell powder, 8-10 parts of triethanolamine, 6-8 parts of nano silicon dioxide powder, 6-8 parts of powder of aralia echinocaulis, 0.1-0.2 parts of agalloch powder, 4-6 parts of 3-hydroxybenzoic acid, 1-2 parts of lauryl sulfate, 4-6 parts of plant saponin, 0.1-0.2 parts of terpilenol and 1-3 parts of nano diatomite. The coating contains a composite component of modified plastic, which can improve adhesion force of the coating when being added to the coating, so that a problem of stripping off of the coating is solved. The coating can release a delicate fragrance continuously and also has the anti-corrosion, anti-mildewing and anti-aging properties, and has the effect of adsorption and indoor air purification.
Description
Technical field
The invention belongs to plastic-wood material paint field, specifically a kind of metope delicate fragrance type environmental protection coating material.
Background technology
Construction material refers to the general name of the various materials for building and field of civil engineering, referred to as " building materials ".In the narrow sense
The building materials material that refers to for civil engineering, such as steel, timber, glass, cement, coating etc., generally by cement, steel and timber
It is referred to as three big materials of common buildings engineering.Sensu lato building materials also include the material for Architectural Equipment, such as electric wire, water pipe
Deng." construction material " of discipline of architecture refers to the subject that physics and the chemical characteristic of different construction materials are studied.
House decoration refers to carry out in room, and including walking, the institute such as Hydroelectric Project Construction, body of wall, floor, ceiling, landscape is real
Existing a whole set of construction according to certain design concept and rule formation attractive in appearance and solution.The little court putting door to furniture
To the big customized treatment arriving room accessories and light fixture, is all the embodiment of finishing.Finishing is different with decoration, and decoration is that opposite is applied flexibly
Product or living environment carry out the maneuver that art is processed.Strengthen aesthetic effect, and improve its function, economic worth and social benefit,
And with environmental protection as design concept.Perfect decoration should be combined closely with the function of object, adapts to processing technology, plays material
Performance, and there is good artistic effect.
The existing additive for interior wall coating, Performance comparision is single, in the combination property needing to improve coating, needs
Multiple additives to be added, the waste causing resource improves the cost of use simultaneously, and environment protecting is undesirable.
Content of the invention
It is an object of the invention to overcoming prior art defect, provide a kind of metope delicate fragrance type environmental protection coating material.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of metope delicate fragrance type environmental protection coating material, includes following component: polyoxypropyleneglycol 2-3 part, no food by weight
Sub- propyl propionate 1-2 part, Chinese tallow 0.8-1 part, n- N-phenylsalicylamide 0.7-1 part, calcium lactate 1-2 part, palm wax 2-3 part, oneself two
Acid propylene glycol polyester 3-4 part, polybenzimidazoles 0.7-2 part, attapulgite 5-7 part, feldspar in powder 10-13 part, butyl acrylate
100-140 part, vinylacetate 160-200 part, walnut shell powder 5-7 part, triethanolamine 8-10 part, nano-silica powder 6-8
Part, spine stem wood powder 6-8 part, eaglewood powder 0.1-0.2 part, 3- hydroxy benzoic acid 4-6 part, sulfated lauryl alcohol 1-2 part, plant
Saponin 4-6 part, terpineol 0.1-0.2 part, nano silicone diatomaceous earth 1-3 part.
A kind of described metope delicate fragrance type environmental protection coating material, includes following component by weight: 2 parts of polyoxypropyleneglycol, does not have
1 part of propyl galate, 1 part of Chinese tallow, 0.8 part of n- N-phenylsalicylamide, 1 part of calcium lactate, 2 parts of palm wax, adipic acid propylene glycol gather
3 parts of ester, 1 part of polybenzimidazoles, 6 parts of attapulgite, 12 parts of feldspar in powder, 130 parts of butyl acrylate, 180 parts of vinylacetate,
6 parts of walnut shell powder, 9 parts of triethanolamine, 7 parts of nano-silica powder, 7 parts of spine stem wood powder, 0.2 part of eaglewood powder, 3- hydroxyl
4 parts of benzoic acid, 1 part of sulfated lauryl alcohol, 6 parts of plant saponin, 0.1 part of terpineol, 1 part of nano silicone diatomaceous earth.
A kind of described metope delicate fragrance type environmental protection coating material, its preparation method comprises the following steps:
(1) successively by polyoxypropyleneglycol, propylgallate, Chinese tallow, n- N-phenylsalicylamide, calcium lactate, Petiolus Trachycarpi
Wax, adipic acid propanediol polyester, polybenzimidazoles, attapulgite, feldspar in powder, butyl acrylate, vinylacetate, walnut shell
Powder, triethanolamine, nano-silica powder, spine stem wood powder, eaglewood powder, 3- hydroxy benzoic acid, sulfated lauryl alcohol, plant
Saponin, terpineol, nano silicone diatomaceous earth add high-speed mixer to be sufficiently mixed uniformly；
(2) extrusion molding, compound material grain is stirred mixing, is subsequently adding the thread composite of extruder extrusion, squeezes
The machine barrel going out machine includes five warm areas, from feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C, 260 DEG C,
200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05mpa；
(3), after thread composite cooling shaping, through broken, grind to form composite powder material, composite powder material
Particle diameter is 0.3 μm -1.2 μm.
Described Muscovitum Powder Particle Size is 100-260 mesh.
Beneficial effects of the present invention: contain the compound composition of modified plastics in the coating of the present invention, be added in coating, permissible
Increase the adhesive force of coating, prevent the situation of disengaging, can persistently give out delicate fragrance；And have anticorrosive, anti-mildew become, resistance to
Aging performance, the effect that there is absorption and purify the interior space.
Specific embodiment
For the ease of it will be appreciated by those skilled in the art that the present invention is further illustrated with reference to specific embodiment.
Embodiment 1
A kind of metope delicate fragrance type environmental protection coating material, includes following component: polyoxypropyleneglycol 2, gallic acid by weight
Propyl ester 1, Chinese tallow 0.8, n- N-phenylsalicylamide 0.7, calcium lactate 1, palm wax 2, adipic acid propanediol polyester 3
, polybenzimidazoles 0.7, attapulgite 5, feldspar in powder 10, butyl acrylate 100, vinylacetate 160,
Walnut shell powder 5, triethanolamine 8, nano-silica powder 6, spine stem wood powder 6, eaglewood powder 0.1,3- hydroxyl
Benzoic acid 4, sulfated lauryl alcohol 1, plant saponin 4, terpineol 0.1, nano silicone diatomaceous earth 1.
Its preparation method comprises the following steps:
(1) successively by polyoxypropyleneglycol 2, propylgallate 1, Chinese tallow 0.8, n- N-phenylsalicylamide
0.7th, calcium lactate 1, palm wax 2, adipic acid propanediol polyester 3, polybenzimidazoles 0.7, attapulgite 5, potassium
Feldspar powder 10, butyl acrylate 100, vinylacetate 160, walnut shell powder 5, triethanolamine 8, nanometer titanium dioxide
Silica flour 6, spine stem wood powder 6, eaglewood powder 0.1,3- hydroxy benzoic acid 4, sulfated lauryl alcohol 1, plant Fructus Gleditsia
Glycosides 4, terpineol 0.1, nano silicone diatomaceous earth 1 add high-speed mixer to be sufficiently mixed uniformly；
(2) extrusion molding, compound material grain is stirred mixing, is subsequently adding the thread composite of extruder extrusion, squeezes
The machine barrel going out machine includes five warm areas, from feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C, 260 DEG C,
200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05mpa；
(3), after thread composite cooling shaping, through broken, grind to form composite powder material, composite powder material
Particle diameter is 0.3 μm -1.2 μm.
Embodiment 2
A kind of metope delicate fragrance type environmental protection coating material, includes following component: polyoxypropyleneglycol 3, gallic acid by weight
Propyl ester 2, Chinese tallow 1, n- N-phenylsalicylamide 1, calcium lactate 2, palm wax 3, adipic acid propanediol polyester 4, poly-
Benzimidazole 2, attapulgite 7, feldspar in powder 13, butyl acrylate 140, vinylacetate 200, walnut shell powder
7th, triethanolamine 10, nano-silica powder 8, spine stem wood powder 8, eaglewood powder 0.2,3- hydroxy benzoic acid 6
, sulfated lauryl alcohol 2, plant saponin 6, terpineol 0.2, nano silicone diatomaceous earth 3.
Its preparation method comprises the following steps:
(1) successively by polyoxypropyleneglycol 3, propylgallate 2, Chinese tallow 1, n- N-phenylsalicylamide 1,
Calcium lactate 2, palm wax 3, adipic acid propanediol polyester 4, polybenzimidazoles 2, attapulgite 7, feldspar in powder 13
, butyl acrylate 140, vinylacetate 200, walnut shell powder 7, triethanolamine 10, nano-silica powder 8
, spine stem wood powder 8, eaglewood powder 0.2,3- hydroxy benzoic acid 6, sulfated lauryl alcohol 2, plant saponin 6,
Terpineol 0.2, nano silicone diatomaceous earth 3 add high-speed mixer to be sufficiently mixed uniformly；
(2) extrusion molding, compound material grain is stirred mixing, is subsequently adding the thread composite of extruder extrusion, squeezes
The machine barrel going out machine includes five warm areas, from feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C, 260 DEG C,
200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05mpa；
(3), after thread composite cooling shaping, through broken, grind to form composite powder material, composite powder material
Particle diameter is 0.3 μm -1.2 μm.
Embodiment 3
A kind of metope delicate fragrance type environmental protection coating material, includes following component: polyoxypropyleneglycol 2, gallic acid by weight
Propyl ester 1, Chinese tallow 1, n- N-phenylsalicylamide 0.8, calcium lactate 1, palm wax 2, adipic acid propanediol polyester 3,
Polybenzimidazoles 1, attapulgite 6, feldspar in powder 12, butyl acrylate 130, vinylacetate 180, walnut shell
Powder 6, triethanolamine 9, nano-silica powder 7, spine stem wood powder 7, eaglewood powder 0.2,3- hydroxy benzoic acid 4
, sulfated lauryl alcohol 1, plant saponin 6, terpineol 0.1, nano silicone diatomaceous earth 1.
Its preparation method comprises the following steps:
(1) successively by polyoxypropyleneglycol 2, propylgallate 1, Chinese tallow 1, n- N-phenylsalicylamide 0.8
, calcium lactate 1, palm wax 2, adipic acid propanediol polyester 3, polybenzimidazoles 1, attapulgite 6, feldspar in powder
12nd, butyl acrylate 130, vinylacetate 180, walnut shell powder 6, triethanolamine 9, nano-silica powder 7
, spine stem wood powder 7, eaglewood powder 0.2,3- hydroxy benzoic acid 4, sulfated lauryl alcohol 1, plant saponin 6,
Terpineol 0.1, nano silicone diatomaceous earth 1 add high-speed mixer to be sufficiently mixed uniformly；
(2) extrusion molding, compound material grain is stirred mixing, is subsequently adding the thread composite of extruder extrusion, squeezes
The machine barrel going out machine includes five warm areas, from feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C, 260 DEG C,
200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05mpa；
(3), after thread composite cooling shaping, through broken, grind to form composite powder material, composite powder material
Particle diameter is 0.3 μm -1.2 μm.
Embodiment 4
A kind of metope delicate fragrance type environmental protection coating material, includes following component: polyoxypropyleneglycol 2, gallic acid by weight
Propyl ester 2, Chinese tallow 0.8, n- N-phenylsalicylamide 1, calcium lactate 1, palm wax 2, adipic acid propanediol polyester 4,
Polybenzimidazoles 1, attapulgite 6, feldspar in powder 12, butyl acrylate 130, vinylacetate 175, walnut shell
Powder 6, triethanolamine 9, nano-silica powder 7, spine stem wood powder 6, eaglewood powder 0.2,3- hydroxy benzoic acid 4
, sulfated lauryl alcohol 1, plant saponin 6, terpineol 0.1, nano silicone diatomaceous earth 3.
Its preparation method comprises the following steps:
(1) successively by polyoxypropyleneglycol 2, propylgallate 2, Chinese tallow 0.8, n- N-phenylsalicylamide 1
, calcium lactate 1, palm wax 2, adipic acid propanediol polyester 4, polybenzimidazoles 1, attapulgite 6, feldspar in powder
12nd, butyl acrylate 130, vinylacetate 175, walnut shell powder 6, triethanolamine 9, nano-silica powder 7
, spine stem wood powder 6, eaglewood powder 0.2,3- hydroxy benzoic acid 4, sulfated lauryl alcohol 1, plant saponin 6,
Terpineol 0.1, nano silicone diatomaceous earth 3 add high-speed mixer to be sufficiently mixed uniformly；
(2) extrusion molding, compound material grain is stirred mixing, is subsequently adding the thread composite of extruder extrusion, squeezes
The machine barrel going out machine includes five warm areas, from feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C, 260 DEG C,
200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05mpa；
(3), after thread composite cooling shaping, through broken, grind to form composite powder material, composite powder material
Particle diameter is 0.3 μm -1.2 μm.
Embodiment 5
A kind of metope delicate fragrance type environmental protection coating material, includes following component: polyoxypropyleneglycol 3, gallic acid by weight
Propyl ester 1, Chinese tallow 0.8, n- N-phenylsalicylamide 1, calcium lactate 1, palm wax 2, adipic acid propanediol polyester 4,
Polybenzimidazoles 1, attapulgite 6, feldspar in powder 12, butyl acrylate 135, vinylacetate 175, walnut shell
Powder 6, triethanolamine 9, nano-silica powder 7, spine stem wood powder 7, eaglewood powder 0.1,3- hydroxy benzoic acid 6
, sulfated lauryl alcohol 1, plant saponin 4, terpineol 0.2, nano silicone diatomaceous earth 3.
Its preparation method comprises the following steps:
(1) successively by polyoxypropyleneglycol 3, propylgallate 1, Chinese tallow 0.8, n- N-phenylsalicylamide 1
, calcium lactate 1, palm wax 2, adipic acid propanediol polyester 4, polybenzimidazoles 1, attapulgite 6, feldspar in powder
12nd, butyl acrylate 135, vinylacetate 175, walnut shell powder 6, triethanolamine 9, nano-silica powder 7
, spine stem wood powder 7, eaglewood powder 0.1,3- hydroxy benzoic acid 6, sulfated lauryl alcohol 1, plant saponin 4,
Terpineol 0.2, nano silicone diatomaceous earth 3 add high-speed mixer to be sufficiently mixed uniformly；
(2) extrusion molding, compound material grain is stirred mixing, is subsequently adding the thread composite of extruder extrusion, squeezes
The machine barrel going out machine includes five warm areas, from feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C, 260 DEG C,
200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05mpa；
(3), after thread composite cooling shaping, through broken, grind to form composite powder material, composite powder material
Particle diameter is 0.3 μm -1.2 μm.
Above content is only citing made for the present invention and illustrates, affiliated those skilled in the art are to being retouched
The specific embodiment stated is made various modifications or supplements or substituted using similar mode, without departing from invention or super
More scope defined in the claims, all should belong to protection scope of the present invention.
Claims (4)
1. a kind of metope delicate fragrance type environmental protection coating material is it is characterised in that include following component by weight: polyoxypropyleneglycol 2-
3 parts, propylgallate 1-2 part, Chinese tallow 0.8-1 part, n- N-phenylsalicylamide 0.7-1 part, calcium lactate 1-2 part, palm wax 2-3
Part, adipic acid propanediol polyester 3-4 part, polybenzimidazoles 0.7-2 part, attapulgite 5-7 part, feldspar in powder 10-13 part, propylene
Acid butyl ester 100-140 part, vinylacetate 160-200 part, walnut shell powder 5-7 part, triethanolamine 8-10 part, nano silicon
Powder 6-8 part, spine stem wood powder 6-8 part, eaglewood powder 0.1-0.2 part, 3- hydroxy benzoic acid 4-6 part, sulfated lauryl alcohol 1-2
Part, plant saponin 4-6 part, terpineol 0.1-0.2 part, nano silicone diatomaceous earth 1-3 part.
2. as claimed in claim 1 a kind of metope delicate fragrance type environmental protection coating material it is characterised in that including following component by weight:
2 parts of polyoxypropyleneglycol, 1 part of propylgallate, 1 part of Chinese tallow, 0.8 part of n- N-phenylsalicylamide, 1 part of calcium lactate, Petiolus Trachycarpi
2 parts of wax, 3 parts of adipic acid propanediol polyester, 1 part of polybenzimidazoles, 6 parts of attapulgite, 12 parts of feldspar in powder, butyl acrylate
130 parts, 180 parts of vinylacetate, 6 parts of walnut shell powder, 9 parts of triethanolamine, 7 parts of nano-silica powder, spine stem wood powder 7
Part, 0.2 part of eaglewood powder, 4 parts of 3- hydroxy benzoic acid, 1 part of sulfated lauryl alcohol, 6 parts of plant saponin, 0.1 part of terpineol, receive
1 part of meter level kieselguhr.
3. as claimed in claim 1 a kind of metope delicate fragrance type environmental protection coating material it is characterised in that its preparation method includes following step
Rapid:
(1) successively by polyoxypropyleneglycol, propylgallate, Chinese tallow, n- N-phenylsalicylamide, calcium lactate, palm wax, oneself
Diacid propanediol polyester, polybenzimidazoles, attapulgite, feldspar in powder, butyl acrylate, vinylacetate, walnut shell powder, three
Ethanolamine, nano-silica powder, spine stem wood powder, eaglewood powder, 3- hydroxy benzoic acid, sulfated lauryl alcohol, plant Fructus Gleditsia
Glycosides, terpineol, nano silicone diatomaceous earth add high-speed mixer to be sufficiently mixed uniformly；
(2) extrusion molding, compound material grain is stirred mixing, is subsequently adding the thread composite of extruder extrusion, extruder
Machine barrel include five warm areas, from feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C, 260 DEG C, 200
DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05mpa；
(3), after thread composite cooling shaping, through broken, composite powder material, the particle diameter of composite powder material are ground to form
For 0.3 μm -1.2 μm.
4. a kind of metope delicate fragrance type environmental protection coating material according to claim 1 is it is characterised in that described Muscovitum Powder Particle Size is
100-260 mesh.