CN107868555A - A kind of hydrophobicity texture coating - Google Patents
A kind of hydrophobicity texture coating Download PDFInfo
- Publication number
- CN107868555A CN107868555A CN201711317035.8A CN201711317035A CN107868555A CN 107868555 A CN107868555 A CN 107868555A CN 201711317035 A CN201711317035 A CN 201711317035A CN 107868555 A CN107868555 A CN 107868555A
- Authority
- CN
- China
- Prior art keywords
- parts
- good
- hydrophobicity
- texture coating
- coating according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of hydrophobicity texture coating, is related to technical field of coatings, and the present invention is made up of following composition by weight：25 32 parts of deionized water, 13 17 parts of silicone acrylic emulsion, 13 17 parts of pure-acrylic emulsion, 10 14 parts of fluorine carbon emulsion, 8 12 parts of compounded mix, 8 12 parts of rutile type titanium white, water-fast 58 parts of silica, special 46 parts of silicones, 200 46 parts of mesh dicalcium powders, 600 5 10 parts of mesh dicalcium powders, 8 12 parts of titanium dioxide, 35 parts of organobentonite, 12 parts of superfine alumina silicate, 0.1 0.2 parts of defoamer, 0.4 0.6 parts of thickener, 0.06 0.09 parts of pH adjusting agent, 0.1 0.2 parts of preservative, 0.5 1 parts of wetting dispersing agent, 0.1 0.15 parts of antifreezing agent；Coating flexibility produced by the present invention is good, and workability is good, and texture is good, in bright gay color true lasting, intensity is high, not easy to crack, good weatherability, fire resistance is good, and wearability is high, water-tolerant, adhesive force is good, strong covering power, and anti-corrosive properties are good, resistance to soiling is good, thus painting brushing effects are good, and aesthetics is high, and durability is good, use cost is low, has preferable application value.
Description
Technical field
The present invention relates to technical field of coatings, more particularly to a kind of hydrophobicity texture coating.
Background technology
Texture coating is exactly that the coating material sense of reality applied after spreading wall is referred to as texture.Texture coating is varied with its
The individual character collocation of three-dimensional texture, more options, shows the spatial view of uniqueness, abundant and lively, makes us fresh and new.And
Integral decoration style is met with individual character creation so that texture coating shows the individual style of oneself in decoration.It is this new
Type art coatings, brought into the new era of natural environmental-protective type bumps coating the smooth type epoch of wall body coating.It can substitute
Wallpaper, and it is more environmentally-friendly, it is economical, it is personalized.Texture coating is radiationless, and from heavy and light, effect is true to nature, passes through different constructions
Technique, gimmick and skill, create infinite special decorative effect.Here it is the novel decorative new material that in the market is popular --
Texture coating.
The main flexible texture coating of texture coating, dry powder texture, wet pulp texture etc., different series, the effect reached
It is different.Texture coating is exactly mainly to mould different moulding and pattern on the wall with special instrument, makes space more
It is three-dimensional and true elegant in appearance.
In the prior art, the overall performance of texture coating is not excellent enough, lack pliability, application property, texture, wearability,
The texture coating of the excellent combination properties such as weatherability, fire resistance, water-resistant type, resistance to soiling, and cause the cost using texture coating
It is higher, it is unfavorable for the large-scale promotion application of texture coating.
The content of the invention
It is an object of the invention to：In order to solve the deficiencies in the prior art, the present invention provides a kind of hydrophobicity texture coating.
The present invention specifically uses following technical scheme to achieve these goals：
A kind of hydrophobicity texture coating, by weight, it is made up of following component：Deionized water 25-32 parts, silicone acrylic emulsion
13-17 parts, pure-acrylic emulsion 13-17 parts, fluorine carbon emulsion 10-14 parts, compounded mix 8-12 parts, rutile type titanium white 8-12 parts,
Water-fast silica 5-8 parts, special silicones 4-6 parts, 200 mesh dicalcium powder 4-6 parts, 600 mesh dicalcium powder 5-10 parts, titanium dioxide
8-12 parts, organobentonite 3-5 parts, superfine alumina silicate 1-2 parts, defoamer 0.1-0.2 parts, thickener 0.4-0.6 parts, pH are adjusted
Save agent 0.06-0.09 parts, preservative 0.1-0.2 parts, wetting dispersing agent 0.5-1 parts, antifreezing agent 0.1-0.15 parts.
Preferably, by weight, it is made up of following component：Deionized water 27-30 parts, silicone acrylic emulsion 14-16 parts,
Pure-acrylic emulsion 14-16 parts, fluorine carbon emulsion 11-13 parts, compounded mix 9-11 parts, rutile type titanium white 9-11 parts, water-fast dioxy
SiClx 6-7 parts, special silicones 4.5-5.5 parts, 200 mesh dicalcium powder 4.5-5.5 parts, 600 mesh dicalcium powder 6-9 parts, titanium dioxide 9-
11 parts, organobentonite 3.5-4.5 parts, superfine alumina silicate 1.2-1.8 parts, defoamer 0.12-0.18 parts, thickener 0.45-
0.55 part, pH conditioning agent 0.07-0.09 parts, preservative 0.12-0.18 parts, wetting dispersing agent 0.6-0.9 parts, antifreezing agent 0.11-
0.14 part.
Preferably, the compounded mix is colorful quartz sands, Dali stone sand, the one or more of glass flake.
Preferably, the defoamer is organosilicon.
Preferably, the thickener is aqueous polyurethane.
Preferably, the pH adjusting agent is organic acid.
Preferably, the preservative is isothiazolinone.
Preferably, the wetting dispersing agent is APES.
Preferably, the antifreezing agent is ethylene glycol or propane diols.
Beneficial effects of the present invention are as follows：
Well-designed, preferably each raw material and proportioning of the invention, it is soft using the mutually coordinated effect between raw material, obtained coating
Good toughness, workability is good, and texture is good, and in bright gay color true lasting, intensity is high, and not easy to crack, good weatherability, fire resistance is good,
Wearability is high, and water-tolerant, adhesive force is good, strong covering power, and anti-corrosive properties are good, and resistance to soiling is good, thus painting brushing effects are good, aesthetics
Height, and durability is good, use cost is low, has preferable application value.
Embodiment
All features disclosed in this specification, can be with any in addition to mutually exclusive feature and/or step
Mode combines.
Embodiment 1
A kind of hydrophobicity texture coating, by weight, it is made up of following component：25 parts of deionized water, silicone acrylic emulsion 13
Part, 13 parts of pure-acrylic emulsion, 10 parts of fluorine carbon emulsion, 8 parts of compounded mix, 8 parts of rutile type titanium white, water-fast 5 parts of silica,
Special 4 parts of silicones, 200 4 parts of mesh dicalcium powders, 600 5 parts of mesh dicalcium powders, 8 parts of titanium dioxide, 3 parts of organobentonite, ultra-fine silicic acid
1 part of aluminium, 0.1 part of defoamer, 0.4 part of thickener, 0.06 part of pH adjusting agent, 0.1 part of preservative, 0.5 part of wetting dispersing agent, prevent
Freeze 0.1 part of agent.
The compounded mix is the mixture of colorful quartz sands and Dali stone sand.
The defoamer is organosilicon.
The thickener is aqueous polyurethane.
The pH adjusting agent is organic acid.
The preservative is isothiazolinone.
The wetting dispersing agent is APES.
The antifreezing agent is ethylene glycol.
Coating flexibility made from the present embodiment is good, and workability is good, and texture is good, and in bright gay color true lasting, intensity is high,
Not easy to crack, good weatherability, fire resistance is good, and wearability is high, and water-tolerant, adhesive force is good, strong covering power, and anti-corrosive properties are good, resistant
Property it is good, thus apply that brushing effects are good, and aesthetics is high, and durability is good, use cost is low.
Embodiment 2
A kind of hydrophobicity texture coating, by weight, it is made up of following component：32 parts of deionized water, silicone acrylic emulsion 17
Part, 17 parts of pure-acrylic emulsion, 14 parts of fluorine carbon emulsion, 12 parts of compounded mix, 12 parts of rutile type titanium white, water-fast silica 8
Part, special 6 parts of silicones, 200 6 parts of mesh dicalcium powders, 600 10 parts of mesh dicalcium powders, 12 parts of titanium dioxide, 5 parts of organobentonite, surpass
Thin 2 parts of alumina silicate, 0.2 part of defoamer, 0.6 part of thickener, 0.09 part of pH adjusting agent, 0.2 part of preservative, wetting dispersing agent 1
Part, 0.15 part of antifreezing agent.
The compounded mix is colorful quartz sands, Dali stone sand, the mixture of glass flake.
The defoamer is organosilicon.
The thickener is aqueous polyurethane.
The pH adjusting agent is organic acid.
The preservative is isothiazolinone.
The wetting dispersing agent is APES.
The antifreezing agent is propane diols.
Coating flexibility made from the present embodiment is good, and workability is good, and texture is good, and in bright gay color true lasting, intensity is high,
Not easy to crack, good weatherability, fire resistance is good, and wearability is high, and water-tolerant, adhesive force is good, strong covering power, and anti-corrosive properties are good, resistant
Property it is good, thus apply that brushing effects are good, and aesthetics is high, and durability is good, use cost is low.
Embodiment 3
A kind of hydrophobicity texture coating, by weight, it is made up of following component：29 parts of deionized water, silicone acrylic emulsion 15
Part, 15 parts of pure-acrylic emulsion, 12 parts of fluorine carbon emulsion, 10 parts of compounded mix, 10 parts of rutile type titanium white, water-fast silica 7
Part, special 5 parts of silicones, 200 5 parts of mesh dicalcium powders, 600 7 parts of mesh dicalcium powders, 10 parts of titanium dioxide, 4 parts of organobentonite are ultra-fine
1.5 parts of alumina silicate, 0.15 part of defoamer, 0.5 part of thickener, 0.08 part of pH adjusting agent, 0.15 part of preservative, wetting dispersing agent
0.7 part, 0.13 part of antifreezing agent.
The compounded mix is colorful quartz sands, Dali stone sand, the mixture of glass flake.
The defoamer is organosilicon.
The thickener is aqueous polyurethane.
The pH adjusting agent is organic acid.
The preservative is isothiazolinone.
The wetting dispersing agent is APES.
The antifreezing agent is propane diols.
Coating flexibility made from the present embodiment is good, and workability is good, and texture is good, and in bright gay color true lasting, intensity is high,
Not easy to crack, good weatherability, fire resistance is good, and wearability is high, and water-tolerant, adhesive force is good, strong covering power, and anti-corrosive properties are good, resistant
Property it is good, thus apply that brushing effects are good, and aesthetics is high, and durability is good, use cost is low.
Described above, only presently preferred embodiments of the present invention is not intended to limit the invention, patent protection model of the invention
Enclose and be defined by claims, the equivalent structure change that every description with the present invention is made, all should similarly be included
Within the scope of the present invention.
Claims (9)
- A kind of 1. hydrophobicity texture coating, it is characterised in that：By weight, it is made up of following component：Deionized water 25-32 Part, silicone acrylic emulsion 13-17 parts, pure-acrylic emulsion 13-17 parts, fluorine carbon emulsion 10-14 parts, compounded mix 8-12 parts, rutile type titanium White powder 8-12 parts, water-fast silica 5-8 parts, special silicones 4-6 parts, 200 mesh dicalcium powder 4-6 parts, 600 mesh dicalcium powder 5-10 Part, titanium dioxide 8-12 parts, organobentonite 3-5 parts, superfine alumina silicate 1-2 parts, defoamer 0.1-0.2 parts, thickener 0.4-0.6 Part, pH adjusting agent 0.06-0.09 parts, preservative 0.1-0.2 parts, wetting dispersing agent 0.5-1 parts, antifreezing agent 0.1-0.15 parts.
- 2. hydrophobicity texture coating according to claim 1, it is characterised in that：By weight, it is made up of following component： Deionized water 27-30 parts, silicone acrylic emulsion 14-16 parts, pure-acrylic emulsion 14-16 parts, fluorine carbon emulsion 11-13 parts, compounded mix 9-11 Part, rutile type titanium white 9-11 parts, water-fast silica 6-7 parts, special silicones 4.5-5.5 parts, 200 mesh dicalcium powder 4.5- 5.5 parts, 600 mesh dicalcium powder 6-9 parts, titanium dioxide 9-11 parts, organobentonite 3.5-4.5 parts, superfine alumina silicate 1.2-1.8 parts, Defoamer 0.12-0.18 parts, thickener 0.45-0.55 parts, pH adjusting agent 0.07-0.09 parts, preservative 0.12-0.18 parts, profit Hygroscopic water powder 0.6-0.9 parts, antifreezing agent 0.11-0.14 parts.
- 3. hydrophobicity texture coating according to claim 1, it is characterised in that：The compounded mix be colorful quartz sands, The one or more of Dali stone sand, glass flake.
- 4. hydrophobicity texture coating according to claim 1, it is characterised in that：The defoamer is organosilicon.
- 5. hydrophobicity texture coating according to claim 1, it is characterised in that：The thickener is aqueous polyurethane.
- 6. hydrophobicity texture coating according to claim 1, it is characterised in that：The pH adjusting agent is organic acid.
- 7. hydrophobicity texture coating according to claim 1, it is characterised in that：The preservative is isothiazolinone.
- 8. hydrophobicity texture coating according to claim 1, it is characterised in that：The wetting dispersing agent is alkyl phenol polyoxy Vinethene.
- 9. hydrophobicity texture coating according to claim 1, it is characterised in that：The antifreezing agent is ethylene glycol or the third two Alcohol.