CN104559788A - Base paint of litchi surface stone-like paint and preparation method of base paint - Google Patents

Base paint of litchi surface stone-like paint and preparation method of base paint Download PDF

Info

Publication number
CN104559788A
CN104559788A CN201510032769.6A CN201510032769A CN104559788A CN 104559788 A CN104559788 A CN 104559788A CN 201510032769 A CN201510032769 A CN 201510032769A CN 104559788 A CN104559788 A CN 104559788A
Authority
CN
China
Prior art keywords
thickening
paint
emulsion
base paint
defoamer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510032769.6A
Other languages
Chinese (zh)
Inventor
王宝群
王丽萍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANDONG HORIZON BUILDING ENERGY-EFFICIENCV TECHNOLOGY Co Ltd
Original Assignee
SHANDONG HORIZON BUILDING ENERGY-EFFICIENCV TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANDONG HORIZON BUILDING ENERGY-EFFICIENCV TECHNOLOGY Co Ltd filed Critical SHANDONG HORIZON BUILDING ENERGY-EFFICIENCV TECHNOLOGY Co Ltd
Priority to CN201510032769.6A priority Critical patent/CN104559788A/en
Publication of CN104559788A publication Critical patent/CN104559788A/en
Pending legal-status Critical Current

Abstract

The invention relates to a base paint of a litchi surface stone-like paint and a preparation method of the base paint, and provides a litchi surface stone-like paint which has the advantages of natural stone-like effect, high hardness of a coating, strong water resistance, strong adhesion and weather resistance and a manufacturing method of the litchi surface stone-like paint. By improving the formula of the base paint and the manufacturing method of the base paint, the water resistance of the coating is greatly improved. The base paint provided by the invention has the beneficial effects of reasonable and unique formula, natural stone-like effect, high hardness of the coating, strong water resistance, strong adhesive force, good weather resistance, good anti-aging effect and the like. The preparation method provided by the invention has simple construction process flow and one-time spray molding and is easy to realize, the manpower is saved, the construction period can be greatly shortened, and the production efficiency is improved; and furthermore, the prepared stone-like paint has good quality and relatively good decorative effect.

Description

Base paint of bush-hammered face stone similar paint and preparation method thereof
Technical field
Invention belongs to stone similar paint technical field, is specifically related to a kind of bush-hammered face stone similar paint and preparation method thereof.
Background technology
Stone similar paint is that a kind of decorative effect exactly likes marble, granitic thick matter exterior wall decorating coating.The particle of main employing shades of colour is formulated.Buildings after stone similar paint finishing, has natural real natural colour, gives elegance, harmony, serious aesthetic feeling.It is suitable for the indoor and outdoor decoration of all kinds of buildings, particularly decorates on curved-surface building thing, can receive vivid, effect of back to nature.Stone similar paint has fire prevention, waterproof, acid and alkali-resistance, anti-pollution, nontoxic, tasteless, bonding force is strong, the feature such as will never fade, extraneous severe environment can be effectively stoped to corrode buildings, extend the life-span of buildings, because stone similar paint possesses good sticking power and freeze-thaw resistance property, be therefore particularly suitable for using in cold district.
Generally there is the problem that coating is too soft or water resisting property is poor in traditional stone similar paint, if some stone similar paint coating is after each raining, all can turn white, coating becomes loose, and after rain stops, shines through the sun one, and coating recovers again original color.In fact, this is because the water tolerance of coating is bad, absorb caused by moisture, and formula reason is that the ACRYLIC EMULSION selected need add tensio-active agent when synthesizing, some producer in order to increase emulsion intercalation method, tensio-active agent used excess greatly; Some producer adds the material such as carboxymethyl cellulose, Natvosol as thickening material when preparing stone similar paint, and adds Sodium Benzoate as sanitas.These materials are all water miscible or hydrophilic, stay in the coating after coating film forming, just greatly reduce the water resistance of coating.
Along with people are to the raising of coating for internal and external wall cosmetic requirement, natural stone similar paint is more and more subject to everybody liking with the outward appearance of its uniqueness and performance, many high-end residentials, garden even high buildings and large mansions all propose to cover with paint, lacquer, colour wash, etc. the stone similar paint very close with the natural stone appearance such as natural granite, marble, have stronger hardness, waterproof, ageing-resistant etc. in aspect of performance requirement.But traditional stone similar paint is substantially all ganoid, and do not reach the feature of natural marble surface irregularity, the sense of reality is poor.Stone similar paint is sprayed again, polishing after dry, last spray plane oil twice after need spraying end oil twice during traditional stone similar paint construction.Its construction process is complicated, and decorative effect is not good, inefficiency.And polishing can destroy paint film, cause bottom to loosen, sticking power can be caused time serious bad, and stone similar paint comes off.
Summary of the invention
The object of the invention is to provide a kind of effect had as imitation natural stone, and coating hardness is large, water resisting property is strong, strong adhesion, weather-proof bush-hammered face stone similar paint and preparation method thereof.
For achieving the above object, technical scheme provided by the present invention is:
A base paint for bush-hammered face stone similar paint, is characterized in that: base paint respectively forms and is in mass:
Water 20.0 ~ 35 ﹪,
Sanitas 0.2 ~ 0.3 ﹪,
Dispersion agent 0.1 ~ 0.2 ﹪,
Kaolin 5.0 ~ 10.0 ﹪,
Titanium dioxide 0.5 ~ 1.0%,
Defoamer 0.4 ~ 0.6 ﹪,
Propylene glycol 0.7 ~ 0.9%,
Mierocrystalline cellulose 0.45 ~ 0.6%,
Multifunctional assistant 0.04 ~ 0.07%,
Film coalescence aid 0.5 ~ 0.8%
Emulsion 15 ~ 25%,
Thickening material 0.05 ~ 0.3%,
Wetting agent 0.2 ~ 0.4%,
Protecting glue solution 3 ~ 6%,
Snowflake white sand 25 ~ 40%.
Described base paint respectively forms; water: 27.0 ﹪; sanitas: 0.2 ﹪; dispersion agent: 0.15 ﹪, kaolin: 7.0 ﹪, titanium dioxide: 0.7%; defoamer: 0.5 ﹪; propylene glycol: 0.8 ﹪, Mierocrystalline cellulose: 0.6%, multifunctional assistant: 0.05%; film coalescence aid: 0.7 ﹪; described emulsion comprises elastic emulsion RS-6733 and organosilicon crylic acid latex 996AD, emulsion 996AD:4 ﹪, emulsion RS-6733:18%; thickening material: 0.14 ﹪; protecting glue solution: 3.77 ﹪, wetting agent: 0.39%, snowflake white sand: 36 ﹪.
The electric conductivity of described water is 40 μ S/CM, described sanitas model is F203, and the model of defoamer is Nuo Pu section NXZ, and multifunctional assistant is AMP-95, snowflake white sand is 80-120 orders, the model of dispersion agent is TM 731A, and kaolin is 1200-1300 order, and cellulosic model is HS30000, the model of titanium dioxide is rutile titanium white powder, thickening material comprises thickening material Y996 and thickening material SN612, and wherein thickening material Y996 accounts for 0.07% of total mass, and thickening material SN612 accounts for 0.07% of total mass.
Described base paint respectively forms; water: 25.0 ﹪; sanitas: 0.22 ﹪; dispersion agent: 0.17 ﹪, kaolin: 8.0 ﹪, titanium dioxide: 0.9%; defoamer: 0.6 ﹪; propylene glycol: 0.9 ﹪, Mierocrystalline cellulose: 0.5%, multifunctional assistant: 0.06%; film coalescence aid: 0.6 ﹪; described emulsion comprises elastic emulsion RS-6733 and organosilicon crylic acid latex 996AD, emulsion 996AD:3.4 ﹪, emulsion RS-6733:20%; thickening material: 0.2 ﹪; protecting glue solution: 4.13 ﹪, wetting agent: 0.32%, snowflake white sand: 35 ﹪.
The electric conductivity of described water is 40 μ S/CM, described sanitas model is F203, the model of defoamer is Nuo Pu section NXZ, and multifunctional assistant is AMP-95, and snowflake white sand is 80-120 orders, the model of described dispersion agent is TM 731A, described kaolin is 1250 order kaolin, and described cellulosic model is HS30000, and described thickening material comprises thickening material Y996 and thickening material SN612, wherein thickening material Y996 accounts for 0.1% of total mass, and thickening material SN612 accounts for 0.1% of total mass.
The base paint preparation method of described bush-hammered face stone similar paint comprises the following steps:
(1) first water, sanitas, dispersion agent, kaolin, titanium dioxide, defoamer, propylene glycol is added to mixing equipment in order, add rear 600-800r/min to disperse slowly to add Mierocrystalline cellulose after 4-6 minute, add rear water jar for irrigating liquid limit, 850r/min disperses 9 minutes;
(2) then add multifunctional assistant, 650-850r/min disperses 15-25 minute, and film coalescence aid is added mixing equipment, stirs 2-4 minute;
(3) again dispersing apparatus speed is down to 600-800r/min and slowly adds emulsion, defoamer, add rear dispersion 4 minutes, add thickening material respectively, disperse 4 minutes;
(4) again dispersing apparatus speed is promoted to 750-900r/min; disperse 3-5 minute after slowly adding wetting agent, then ready-made protecting glue solution, 80 ~ 120 order snowflake white sands are added mixing equipment, add rear dispersion 6-9 minute; finally add thickening material, disperse to shut down for subsequent use in 3-5 minute.
In described step (1), defoamer is the half of amount used, and in step (3), defoamer is second half of amount used.
Described step (3) adds thickening material SN612, half thickening material Y996; step (4) adds second half thickening material Y996; the thickening material Y996 added in described step (3) (4) is the mixture of thickening material and water; its weight percent is 1:2, and the concentration of the protecting glue solution added in described step (4) is 6 ﹪.
The invention has the beneficial effects as follows, fill a prescription reasonable, unique, there is the effect as imitation natural stone, coating hardness is large, water tolerance is strong, strong adhesion, weather-proof, ageing-resistant effective etc.The construction process of preparation method provided by the invention is simple, a spray mo(u)lding, is easy to realize, and saves artificial, can reduction of erection time greatly, improve production efficiency, and obtained stone similar paint quality is good, excellent decoration effect.
Embodiment
Embodiment 1
The present embodiment provides a kind of effect had as imitation natural stone, and coating hardness is large, water tolerance is strong, the bush-hammered face stone similar paint base paint of strong adhesion, good weatherability, and its raw material comprises the component of following weight percent.
Base paint
Water: 27.0 ﹪, sanitas: 0.2 ﹪, dispersion agent: 0.15 ﹪; kaolin: 7.0 ﹪, titanium dioxide: 0.7%, defoamer: 0.5 ﹪; propylene glycol: 0.8 ﹪, Mierocrystalline cellulose: 0.6%, multifunctional assistant: 0.05%; film coalescence aid: 0.7 ﹪, emulsion 996AD:4 ﹪, emulsion RS-6733:18%; thickening material: 0.14 ﹪; protecting glue solution: 3.77 ﹪, wetting agent: 0.39%, snowflake white sand: 36 ﹪.
The electric conductivity of above-mentioned water is 40 μ S/CM.Described sanitas model is F203, and the model of defoamer is Nuo Pu section NXZ.Multifunctional assistant is AMP-95, and snowflake white sand is 80-120 orders, to improve the texture of paint film, increases its decorative effect.The model of described dispersion agent is TM 731A, this kind of dispersant efficiency is high, water tolerance is high, there is good glossiness, very effective for inorganic color stuffing, good glossiness and opacifying power can be provided under both economical consumption, simultaneously, when with high-performance emulsions and other high performance adjuvant with the use of time, can give coating better corrosion resistance nature.
Described kaolin is 1200-1300 order kaolin, have that whiteness is high, matter is soft, easy dispersion suspension in water, good plasticity-and high cohesiveness, excellent electrical insulation capability; Have good antiacid dissolubility, very low cation exchange capacity, preferably resistivity against fire, oil absorbency is good.
Described cellulosic model is HS30000, can shorten jitter time, improves gloss, improves tinting strength and opacifying power, improves color developing and toning property, prevents floating, prevent flocculation, prevent sedimentation.The model of described titanium dioxide is rutile titanium white powder, has the characteristics such as high, the easy dispersion of whiteness, opacifying power be good.
As a modification of the present invention, described emulsion comprises elastic emulsion RS-6733 and organosilicon crylic acid latex 996AD, and wherein elastic emulsion RS-6733 accounts for total mass 18%, and organosilicon crylic acid latex 996AD accounts for total mass 4%, Main Function can make paint film have certain elasticity, can have certain rigidity again.
As another improvement of the present invention, described thickening material comprises thickening material Y996 and thickening material SN612, and wherein thickening material Y996 accounts for 0.07% of total mass, thickening material SN612 accounts for 0.07% of total mass, and Main Function changes the rheological property of dispersion, anti-settling, anti-splashing, improves the flow agent of film.The stone similar paint prepared through the present invention has the effect as imitation natural stone, and coating hardness is large, water resisting property is strong, strong adhesion, weather-proof, ageing-resistant etc.
A preparation method for above-mentioned bush-hammered face stone similar paint base paint, it comprises the following steps:
Base paint raw material comprises the component of following weight percent: water: 27.0 ﹪, sanitas: 0.2 ﹪, dispersion agent: 0.15 ﹪; kaolin: 7.0 ﹪, titanium dioxide: 0.7%, defoamer: 0.5 ﹪; propylene glycol: 0.8 ﹪, Mierocrystalline cellulose: 0.6%, multifunctional assistant: 0.05%; film coalescence aid: 0.7 ﹪, emulsion 996AD:4 ﹪, emulsion RS-6733:18%; thickening material: 0.14 ﹪; protecting glue solution: 3.77 ﹪, wetting agent: 0.39%, snowflake white sand: 36 ﹪.
(1) first add water, sanitas, dispersion agent, kaolin, titanium dioxide, defoamer, propylene glycol to mixing equipment in order, add after rear 600r/min disperses 4 minutes and slowly add Mierocrystalline cellulose, add rear water jar for irrigating liquid limit, 850r/min disperses 9 minutes;
(2) then add multifunctional assistant, 850r/min disperses 20 minutes, and film coalescence aid is added mixing equipment, stirs 3 minutes;
(3) again dispersing apparatus speed is down to 600r/min and slowly adds emulsion, defoamer, add rear dispersion 4 minutes, add thickening material SN612, half thickening material Y996 respectively, disperse 4 minutes;
(4) again dispersing apparatus speed is promoted to 850r/min; disperse 4 minutes after slowly adding wetting agent, then ready-made protecting glue solution, 80 ~ 120 order snowflake white sands are added mixing equipment, add rear dispersion 8 minutes; finally add second half thickening material Y996, disperse to shut down for subsequent use in 4 minutes.
As a modification of the present invention, in described step (1), defoamer is the half of amount used, now puts into reach and presses down bubble effect.In step (3), defoamer is second half of amount used, reaches the effect of froth breaking.
The thickening material Y996 added in described step (3) (4) is the mixture of thickening material and water, and its weight percent is 1:2; The concentration of the G988 solution added in described step (4) is 6 ﹪.
The construction process of preparation method provided by the invention is simple, a spray mo(u)lding, is easy to realize, and saves artificial, can reduction of erection time greatly, improve production efficiency, and obtained stone similar paint quality is good, excellent decoration effect.
Embodiment 2
The present embodiment provides a kind of effect had as imitation natural stone, and coating hardness is large, water tolerance is strong, the bush-hammered face stone similar paint of strong adhesion, good weatherability, and its raw material comprises the component of following weight percent.
Base paint
Water: 25.0 ﹪, sanitas: 0.22 ﹪, dispersion agent: 0.17 ﹪; kaolin: 8.0 ﹪, titanium dioxide: 0.9%, defoamer: 0.6 ﹪; propylene glycol: 0.9 ﹪, Mierocrystalline cellulose: 0.5%, multifunctional assistant: 0.06%; film coalescence aid: 0.6 ﹪, emulsion 996AD:3.4 ﹪, emulsion RS-6733:20%; thickening material: 0.2 ﹪; protecting glue solution: 4.13 ﹪, wetting agent: 0.32%, snowflake white sand: 35 ﹪.
The electric conductivity of described water is 40 μ S/CM.Described sanitas model is F203, and the model of defoamer is Nuo Pu section NXZ.Multifunctional assistant is AMP-95, and snowflake white sand is 80-120 orders, to improve the texture of paint film, increases its decorative effect.
The model of described dispersion agent is TM 731A, this kind of dispersant efficiency is high, water tolerance is high, there is good glossiness, very effective for inorganic color stuffing, good glossiness and opacifying power can be provided under both economical consumption, simultaneously, when with high-performance emulsions and other high performance adjuvant with the use of time, can give coating better corrosion resistance nature.
Described kaolin is 1250 order kaolin, have that whiteness is high, matter is soft, easy dispersion suspension in water, good plasticity-and high cohesiveness, excellent electrical insulation capability; Have good antiacid dissolubility, very low cation exchange capacity, preferably resistivity against fire, oil absorbency is good.
Described cellulosic model is HS30000, can shorten jitter time, improves gloss, improves tinting strength and opacifying power, improves color developing and toning property, prevents floating, prevent flocculation, prevent sedimentation.The model of described titanium dioxide is rutile titanium white powder, has the characteristics such as high, the easy dispersion of whiteness, opacifying power be good.
As a modification of the present invention, described emulsion comprises elastic emulsion RS-6733 and organosilicon crylic acid latex 996AD, and wherein elastic emulsion RS-6733 accounts for total mass 20%, and organosilicon crylic acid latex 996AD accounts for total mass 3.4%, Main Function can make paint film have certain elasticity, can have certain rigidity again.
As of the present invention another improve, described thickening material comprises thickening material Y996 and thickening material SN612, and wherein thickening material Y996 accounts for 0.1% of total mass, and thickening material SN612 accounts for 0.1% of total mass, and the change rheological of dispersion of Main Function is held; Anti-settling; Anti-splashing, improves the flow agent of film.
The stone similar paint prepared through the present invention has the effect as imitation natural stone, and coating hardness is large, water resisting property is strong, strong adhesion, weather-proof, ageing-resistant etc.
A preparation method for above-mentioned bush-hammered face stone similar paint base paint, it comprises the following steps:
Base paint
Raw material comprises the component of following weight percent: water: 25.0 ﹪, sanitas: 0.22 ﹪, dispersion agent: 0.17 ﹪; kaolin: 8.0 ﹪, titanium dioxide: 0.9%, defoamer: 0.6 ﹪; propylene glycol: 0.9 ﹪, Mierocrystalline cellulose: 0.5%, multifunctional assistant: 0.06%; film coalescence aid: 0.6 ﹪, emulsion 996AD:3.4 ﹪, emulsion RS-6733:20%; thickening material: 0.2 ﹪; protecting glue solution: 4.13 ﹪, wetting agent: 0.32%, snowflake white sand: 35 ﹪.
(1) first add water, sanitas, dispersion agent, kaolin, titanium dioxide, defoamer, propylene glycol to mixing equipment in order, add after rear 600r/min disperses 4 minutes and slowly add Mierocrystalline cellulose, add rear water jar for irrigating liquid limit, 850r/min disperses 9 minutes;
(2) then add multifunctional assistant, 850r/min disperses 20 minutes; Film coalescence aid is added mixing equipment, stirs 3 minutes;
(3) again dispersing apparatus speed is down to 600r/min and slowly adds emulsion, defoamer, add rear dispersion 4 minutes; Add thickening material SN612 respectively, half thickening material Y996, disperse 4 minutes;
(4) again dispersing apparatus speed is promoted to after 850r/min slowly adds wetting agent and disperses 4 minutes; then ready-made protecting glue solution, 80 ~ 120 order snowflake white sands are added mixing equipment; add rear dispersion 8 minutes, finally add second half thickening material Y996, disperse to shut down for subsequent use in 4 minutes.
As a modification of the present invention, in described step (1), defoamer is the half of amount used, now puts into reach and presses down bubble effect.(3) in, defoamer is second half of amount used, reaches the effect of froth breaking.
The thickening material Y996 added in described step (3) (4) is the mixture of thickening material and water, and its weight percent is 1:2; The concentration of the G988 solution added in described step (4) is 6 ﹪.
The construction process of preparation method provided by the invention is simple, a spray mo(u)lding, is easy to realize, and saves artificial, can reduction of erection time greatly, improve production efficiency, and obtained stone similar paint quality is good, excellent decoration effect.

Claims (8)

1. a base paint for bush-hammered face stone similar paint, is characterized in that: base paint respectively forms and is in mass:
Water 20.0 ~ 35 ﹪,
Sanitas 0.2 ~ 0.3 ﹪,
Dispersion agent 0.1 ~ 0.2 ﹪,
Kaolin 5.0 ~ 10.0 ﹪,
Titanium dioxide 0.5 ~ 1.0%,
Defoamer 0.4 ~ 0.6 ﹪,
Propylene glycol 0.7 ~ 0.9%,
Mierocrystalline cellulose 0.45 ~ 0.6%,
Multifunctional assistant 0.04 ~ 0.07%,
Film coalescence aid 0.5 ~ 0.8%
Emulsion 15 ~ 25%,
Thickening material 0.05 ~ 0.3%,
Wetting agent 0.2 ~ 0.4%,
Protecting glue solution 3 ~ 6%,
Snowflake white sand 25 ~ 40%.
2. the base paint of bush-hammered face stone similar paint according to claim 1, it is characterized in that: base paint respectively forms and is in mass, water: 27.0 ﹪, sanitas: 0.2 ﹪, dispersion agent: 0.15 ﹪, kaolin: 7.0 ﹪, titanium dioxide: 0.7%, defoamer: 0.5 ﹪, propylene glycol: 0.8 ﹪, Mierocrystalline cellulose: 0.6%, multifunctional assistant: 0.05%, film coalescence aid: 0.7 ﹪, described emulsion comprises elastic emulsion RS-6733 and organosilicon crylic acid latex 996AD, emulsion 996AD:4 ﹪, emulsion RS-6733:18%, thickening material: 0.14 ﹪, protecting glue solution: 3.77 ﹪, wetting agent: 0.39%, snowflake white sand: 36 ﹪.
3. the base paint of bush-hammered face stone similar paint according to claim 2, it is characterized in that: the electric conductivity of described water is 40 μ S/CM, described sanitas model is F203, the model of defoamer is Nuo Pu section NXZ, multifunctional assistant is AMP-95, snowflake white sand is 80-120 orders, the model of dispersion agent is TM 731A, kaolin is 1200-1300 order, cellulosic model is HS30000, the model of titanium dioxide is rutile titanium white powder, thickening material comprises thickening material Y996 and thickening material SN612, wherein thickening material Y996 accounts for 0.07% of total mass, thickening material SN612 accounts for 0.07% of total mass.
4. the base paint of bush-hammered face stone similar paint according to claim 1, it is characterized in that: base paint respectively forms and is in mass, water: 25.0 ﹪, sanitas: 0.22 ﹪, dispersion agent: 0.17 ﹪, kaolin: 8.0 ﹪, titanium dioxide: 0.9%, defoamer: 0.6 ﹪, propylene glycol: 0.9 ﹪, Mierocrystalline cellulose: 0.5%, multifunctional assistant: 0.06%, film coalescence aid: 0.6 ﹪, described emulsion comprises elastic emulsion RS-6733 and organosilicon crylic acid latex 996AD, emulsion 996AD:3.4 ﹪, emulsion RS-6733:20%, thickening material: 0.2 ﹪, protecting glue solution: 4.13 ﹪, wetting agent: 0.32%, snowflake white sand: 35 ﹪.
5. the base paint of bush-hammered face stone similar paint according to claim 4, it is characterized in that: the electric conductivity of described water is 40 μ S/CM, described sanitas model is F203, the model of defoamer is Nuo Pu section NXZ, multifunctional assistant is AMP-95, snowflake white sand is 80-120 orders, the model of described dispersion agent is TM 731A, described kaolin is 1250 order kaolin, described cellulosic model is HS30000, described thickening material comprises thickening material Y996 and thickening material SN612, and wherein thickening material Y996 accounts for 0.1% of total mass, and thickening material SN612 accounts for 0.1% of total mass.
6. prepare a base paint preparation method for bush-hammered face stone similar paint described in any one of claim 1-5, it is characterized in that: it comprises the following steps:
(1) first water, sanitas, dispersion agent, kaolin, titanium dioxide, defoamer, propylene glycol is added to mixing equipment in order, add rear 600-800r/min to disperse slowly to add Mierocrystalline cellulose after 4-6 minute, add rear water jar for irrigating liquid limit, 850r/min disperses 8-10 minute;
(2) then add multifunctional assistant, 650-850r/min disperses 15-25 minute, and film coalescence aid is added mixing equipment, stirs 2-4 minute;
(3) again dispersing apparatus speed is down to 600-800r/min and slowly adds emulsion, defoamer, add rear dispersion 3-5 minute, add thickening material respectively, dispersion 3-5 minute;
(4) again dispersing apparatus speed is promoted to 750-900r/min; disperse 3-5 minute after slowly adding wetting agent, then ready-made protecting glue solution, 80 ~ 120 order snowflake white sands are added mixing equipment, add rear dispersion 6-9 minute; finally add thickening material, disperse to shut down for subsequent use in 3-5 minute.
7. the base paint preparation method of bush-hammered face stone similar paint according to claim 6, is characterized in that: in described step (1), defoamer is the half of amount used, and in step (3), defoamer is second half of amount used.
8. the base paint preparation method of bush-hammered face stone similar paint according to claim 6; it is characterized in that: described step (3) adds thickening material SN612, half thickening material Y996; step (4) adds second half thickening material Y996; the thickening material Y996 added in described step (3) (4) is the mixture of thickening material and water; its weight percent is 1:2, and the concentration of the protecting glue solution added in described step (4) is 6 ﹪.
CN201510032769.6A 2015-01-23 2015-01-23 Base paint of litchi surface stone-like paint and preparation method of base paint Pending CN104559788A (en)