CN109054647A - A kind of stone coating and preparation method thereof - Google Patents
A kind of stone coating and preparation method thereof Download PDFInfo
- Publication number
- CN109054647A CN109054647A CN201810937104.3A CN201810937104A CN109054647A CN 109054647 A CN109054647 A CN 109054647A CN 201810937104 A CN201810937104 A CN 201810937104A CN 109054647 A CN109054647 A CN 109054647A
- Authority
- CN
- China
- Prior art keywords
- parts
- turns
- mesh
- revolving speed
- snowflake white
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of stone coatings and preparation method thereof.The stone coating includes thick prime paint and fine flour layer paint；The thick prime paint includes the raw material of following parts by weight: 35-45 parts of water, 2-5 parts of cellulose, 2-5 parts of coalescing agent, 2-6 parts of ethylene glycol, 1-3 parts of neutralizer, 1-2 parts of preservative, 100-130 parts of lotion, 60 105-135 parts of mesh snowflake white sands, 80 600-750 parts of mesh snowflake white sands；The fine flour layer enamel-cover includes the raw material of following parts by weight: 40-50 parts of water, 2-6 parts of cellulose, 3-5 parts of coalescing agent, 1-4 parts of ethylene glycol, 1-2 parts of neutralizer, 1-2 parts of preservative, 100-140 parts of lotion, 90 600-750 parts of mesh snowflake white sands, 100 100-140 parts of mesh snowflake white sands.Flexibility is good after stone coating construction molding of the invention, resistance to scrub, good water-proof effect, and adhesive force is good；Do not occur the accumulation of salt in the surface soil, whiting June not dropping alkali and not doing to construct on the wall that alkali resistant bottom closing paint is handled.
Description
Technical field
The present invention relates to building coating technical field, specifically a kind of stone coating and preparation method thereof.
Background technique
Existing inner-outer wall has the disadvantage in that 1 with coating, at present generally using powder of lacquer putty for use on, batch ash, mortar to inner-outer wall
Carry out bottoming, there are hardness it is low, flexible cracking resistance is poor, poor adhesive force the disadvantages of, be easy to appear mouldy shedding cracking or monolith and shell
Fall phenomenon；2, bottoming is carried out to inner-outer wall using powder of lacquer putty for use on, batch ash, mortar, that there is also service times is long, labor intensive is big etc. lacks
Point.3, coating for internal and external wall construction is easy to appear whiting, accumulation of salt in the surface soil phenomenon, influences dope layer quality when on the stronger ground of alkalinity；
4, coating for internal and external wall construction, due to poor adhesive force, is easy to appear peeling decortication phenomenon when in powder of lacquer putty for use on, batch plastered wall.
Summary of the invention
The purpose of the present invention is to provide a kind of stone coatings and preparation method thereof, mentioned above in the background art to solve
Problem.
To achieve the above object, the invention provides the following technical scheme:
A kind of stone coating, including thick prime paint and fine flour layer paint；The thick prime paint includes the raw material of following parts by weight:
35-45 parts of water, 2-5 parts of cellulose, 2-5 parts of coalescing agent, 2-6 parts of ethylene glycol, 1-3 parts of neutralizer, 1-2 parts of preservative, lotion
100-130 parts, 60 105-135 parts of mesh snowflake white sands, 80 600-750 parts of mesh snowflake white sands；The fine flour layer enamel-cover includes following heavy
Measure the raw material of number: 40-50 parts of water, 2-6 parts of cellulose, 3-5 parts of coalescing agent, 1-4 parts of ethylene glycol, 1-2 parts of neutralizer, anti-corrosion
1-2 parts of agent, 100-140 parts of lotion, 90 600-750 parts of mesh snowflake white sands, 100 100-140 parts of mesh snowflake white sands.
As a further solution of the present invention: the thick prime paint includes the raw material of following parts by weight: 42.5 parts of water, fibre
Tie up plain 3 parts, 4 parts of coalescing agent, 3 parts of ethylene glycol, 1 part of neutralizer, 1.5 parts of preservative, 120 parts of lotion, 60 mesh snowflake white sands 125
Part, 80 700 parts of mesh snowflake white sands.
As a further solution of the present invention: the fine flour layer enamel-cover includes the raw material of following parts by weight: 42.5 parts of water, fibre
Tie up plain 3 parts, 4 parts of coalescing agent, 3 parts of ethylene glycol, 1 part of neutralizer, 1.5 parts of preservative, 120 parts of lotion, 90 mesh snowflake white sands 700
Part, 100 125 parts of mesh snowflake white sands.
A kind of preparation method of stone coating, comprising the following steps:
(1) it prepares thick prime paint: water and cellulose is mixed, disperse 3-8 minutes under 800-1200 turns/min revolving speed；So
Coalescing agent, ethylene glycol, neutralizer and lotion are added afterwards, is stirred evenly under 100-300 turns/min revolving speed；Then anti-corrosion is added
Agent, and 60 mesh snowflake white sands and 80 mesh snowflake white sands are slowly added to, it is stirred evenly under 50-150 turns/min revolving speed；
(2) it prepares fine flour layer paint: water and cellulose is mixed, disperse 2-10 minutes under 900-1400 turns/min revolving speed；
Then coalescing agent, ethylene glycol, neutralizer and lotion is added, is stirred evenly under 100-300 turns/min revolving speed；Then it is added anti-
Rotten agent, and 90 mesh snowflake white sands, 100 mesh snowflake white sands are slowly added to, it is stirred evenly under 80-150 turns/min revolving speed.
As a further solution of the present invention: step (1) prepares thick prime paint: water and cellulose are mixed, 1000 turns/
Disperse 5 minutes under min revolving speed；Then coalescing agent, ethylene glycol, neutralizer and lotion is added, is stirred under 200 turns/min revolving speed
Uniformly；Then preservative is added, and is slowly added to 60 mesh snowflake white sands and 80 mesh snowflake white sands, is stirred under 100 turns/min revolving speed
It mixes uniformly.
As a further solution of the present invention: step (2) prepares fine flour layer paint: water and cellulose are mixed, 1000 turns/
Disperse 5 minutes under min revolving speed；Then coalescing agent, ethylene glycol, neutralizer and lotion is added, is stirred under 200 turns/min revolving speed
Uniformly；Then preservative is added, and is slowly added to 90 mesh snowflake white sands, 100 mesh snowflake white sands, is stirred under 100 turns/min revolving speed
It mixes uniformly.
Compared with prior art, the beneficial effects of the present invention are:
Flexibility is good, it can be achieved that 45 degree of bendings are not cracked after stone coating construction molding of the invention；Resistance to brush is carried out after parching
Test is washed, does not fall off drop 2000 times；Carry out closure dress water experiment, 48 hours water-tight, good water-proof effects；Alkali is not dropping not
It does construction on the wall of alkali resistant bottom closing paint processing and does not occur the accumulation of salt in the surface soil, whiting June；Adhesive force test is carried out, perpendicular to the ground
Smooth glass face on construction to parch back edge impermeable, natural conditions lower 6 months without the absciss layer phenomenon that falls off.The present invention solves
Conventionally employed powder of lacquer putty for use on, batch ash, mortar carry out low, poor, poor adhesive force of flexible cracking resistance of hardness existing for bottoming etc. to inner-outer wall and lack
Point；And stone coating of the present invention is not required to maintain, and parches the next procedure that can construct, shortens the construction period, labor intensive is few；Stone of the present invention
Paint does not contain strong acid alkaloid substance, will not corrode top coat paint layer, guarantees that top coat paint layer is not destroyed by bottom；Top coat paint layer is applied
Work can penetrate into stone coating on stone coating bottom, increase adhesive force, will not film-like removing bottom.
Specific embodiment
The technical solution of the patent is explained in further detail With reference to embodiment.
Embodiment 1
A kind of stone coating, including thick prime paint and fine flour layer paint；The thick prime paint includes the raw material of following parts by weight:
35 parts of water, 2 parts of cellulose, 2 parts of coalescing agent, 2 parts of ethylene glycol, 1 part of neutralizer, 1 part of preservative, 100 parts of lotion, 60 mesh snowflakes
105 parts of white sand, 80 600 parts of mesh snowflake white sands；The fine flour layer enamel-cover includes the raw material of following parts by weight: 40 parts of water, cellulose 2
Part, 3 parts of coalescing agent, 1 part of ethylene glycol, 1 part of neutralizer, 1 part of preservative, 100 parts of lotion, 90 600 parts of mesh snowflake white sands, 100
100 parts of mesh snowflake white sand.
A kind of preparation method of stone coating, comprising the following steps: (1) prepare thick prime paint: water and cellulose are mixed,
Disperse 3 minutes under 800 turns/min revolving speed；Then coalescing agent, ethylene glycol, neutralizer and lotion is added, in 100 turns/min revolving speed
Under stir evenly；Then preservative is added, and is slowly added to 60 mesh snowflake white sands and 80 mesh snowflake white sands, in 50 turns/min revolving speed
Under stir evenly；(2) it prepares fine flour layer paint: water and cellulose being mixed, dispersed 2 minutes under 900 turns/min revolving speed；Then plus
Enter coalescing agent, ethylene glycol, neutralizer and lotion, is stirred evenly under 100 turns/min revolving speed；Then preservative is added, and delays
It is slow that 90 mesh snowflake white sands, 100 mesh snowflake white sands are added, it is stirred evenly under 80 turns/min revolving speed.
Embodiment 2
A kind of stone coating, including thick prime paint and fine flour layer paint；The thick prime paint includes the raw material of following parts by weight:
45 parts of water, 5 parts of cellulose, 5 parts of coalescing agent, 6 parts of ethylene glycol, 3 parts of neutralizer, 2 parts of preservative, 130 parts of lotion, 60 mesh snowflakes
135 parts of white sand, 80 750 parts of mesh snowflake white sands；The fine flour layer enamel-cover includes the raw material of following parts by weight: 50 parts of water, cellulose 6
Part, 5 parts of coalescing agent, 4 parts of ethylene glycol, 2 parts of neutralizer, 2 parts of preservative, 140 parts of lotion, 90 750 parts of mesh snowflake white sands, 100
140 parts of mesh snowflake white sand.
A kind of preparation method of stone coating, comprising the following steps: (1) prepare thick prime paint: water and cellulose are mixed,
Disperse 8 minutes under 1200 turns/min revolving speed；Then coalescing agent, ethylene glycol, neutralizer and lotion is added, turns in 300 turns/min
It is stirred evenly under speed；Then preservative is added, and is slowly added to 60 mesh snowflake white sands and 80 mesh snowflake white sands, in 150 turns/min
It is stirred evenly under revolving speed；(2) it prepares fine flour layer paint: water and cellulose being mixed, dispersed 10 minutes under 1400 turns/min revolving speed；
Then coalescing agent, ethylene glycol, neutralizer and lotion is added, is stirred evenly under 300 turns/min revolving speed；Then anti-corrosion is added
Agent, and 90 mesh snowflake white sands, 100 mesh snowflake white sands are slowly added to, it is stirred evenly under 150 turns/min revolving speed.
Embodiment 3
A kind of stone coating, including thick prime paint and fine flour layer paint；The thick prime paint includes the raw material of following parts by weight:
42.5 parts of water, 3 parts of cellulose, 4 parts of coalescing agent, 3 parts of ethylene glycol, 1 part of neutralizer, 1.5 parts of preservative, 120 parts of lotion, 60 mesh
125 parts of snowflake white sand, 80 700 parts of mesh snowflake white sands.The fine flour layer enamel-cover includes the raw material of following parts by weight: 42.5 parts of water,
3 parts of cellulose, 4 parts of coalescing agent, 3 parts of ethylene glycol, 1 part of neutralizer, 1.5 parts of preservative, 120 parts of lotion, 90 mesh snowflake white sands
700 parts, 100 125 parts of mesh snowflake white sands.
A kind of preparation method of stone coating, comprising the following steps: (1) prepare thick prime paint: water and cellulose are mixed,
Disperse 5 minutes under 1000 turns/min revolving speed；Then coalescing agent, ethylene glycol, neutralizer and lotion is added, turns in 200 turns/min
It is stirred evenly under speed；Then preservative is added, and is slowly added to 60 mesh snowflake white sands and 80 mesh snowflake white sands, in 100 turns/min
It is stirred evenly under revolving speed.(2) it prepares fine flour layer paint: water and cellulose being mixed, dispersed 5 minutes under 1000 turns/min revolving speed；
Then coalescing agent, ethylene glycol, neutralizer and lotion is added, is stirred evenly under 200 turns/min revolving speed；Then anti-corrosion is added
Agent, and 90 mesh snowflake white sands, 100 mesh snowflake white sands are slowly added to, it is stirred evenly under 100 turns/min revolving speed.
The working principle of the invention is: thick prime paint is levelling for bottom metope and does point checkers lines with (such as needing
Black lines are wanted just to add pigment that thick prime paint is tuned into black).Stainless steel batch knife must be used to construct.Fine flour layer paint is coated in
The upper layer of thick prime paint, can make metope smooth, the dope layer effect on surface of constructing is more preferable, and the color of fine flour layer paint can also be according to top
The color of coating is tuned into similar color, increase coating coverage rate (such as top coat paint be Chinese red artificial granite, fine flour layer
Paint can then add pigment to be tuned into red).Stainless steel batch knife must be used to construct.When construction, thick prime paint must be criticized and be struck off
Whole, pressing, which is returned sword, to be avoided tool marks occur when construction fine flour layer paint in place, influence the aesthetic effect of dope layer.Construction fine flour layer
Criticizing to scrape when paint avoids founding situation from occurring, and can carry out sanding and polishing with 80 mesh and the above sand paper after dry.Execution conditions temperature is low
It cannot construct when 5 degrees Celsius, humidity, which is greater than 80%, to construct, it is ensured that not by rain drop erosion, thick bottom in 2 hours after construction is good
Fine flour layer paint (cannot construct in 4 hours) could be constructed after drying must be waited after the completion of layer paint.Usage amount: thick prime paint 2.5 is public
Jin/square；1.25 kilogram/square of fine flour layer paint.
Preferably, the model that the part material of the thick prime paint of the present invention can be used but be not limited in table 1.
Table 1
| Raw material | Model |
| Cellulose | Klein 10W |
| Coalescing agent | Yi Shiman |
| Ethylene glycol | Y200 |
| Neutralizer | AMP95 |
| Preservative | CHS5 |
| Lotion | 959 |
Preferably, the model that the part material of fine flour layer paint of the present invention can be used but be not limited in table 2.
Table 2
| Raw material | Model |
| Cellulose | Klein 10W |
| Coalescing agent | Yi Shiman |
| Ethylene glycol | Y200 |
| Neutralizer | AMP95 |
| Preservative | CHS5 |
| Lotion | 959 |
The preferred embodiment of the patent is described in detail above, but this patent is not limited to above-mentioned embodiment party
Formula within the knowledge of one of ordinary skill in the art can also be under the premise of not departing from this patent objective
Various changes can be made.
Claims (6)
1. a kind of stone coating, which is characterized in that including thick prime paint and fine flour layer paint；The thick prime paint includes following parts by weight
Several raw material: 35-45 parts of water, 2-5 parts of cellulose, 2-5 parts of coalescing agent, 2-6 parts of ethylene glycol, 1-3 parts of neutralizer, preservative 1-
2 parts, 100-130 parts of lotion, 60 105-135 parts of mesh snowflake white sands, 80 600-750 parts of mesh snowflake white sands；The fine flour layer enamel-cover
Include the raw material of following parts by weight: 40-50 parts of water, 2-6 parts of cellulose, 3-5 parts of coalescing agent, 1-4 parts of ethylene glycol, neutralizer 1-
2 parts, 1-2 parts of preservative, 100-140 parts of lotion, 90 600-750 parts of mesh snowflake white sands, 100 100-140 parts of mesh snowflake white sands.
2. stone coating according to claim 1, which is characterized in that the thick prime paint includes the original of following parts by weight
Material: 42.5 parts of water, 3 parts of cellulose, 4 parts of coalescing agent, 3 parts of ethylene glycol, 1 part of neutralizer, 1.5 parts of preservative, 120 parts of lotion,
60 125 parts of mesh snowflake white sands, 80 700 parts of mesh snowflake white sands.
3. stone coating according to claim 1, which is characterized in that the fine flour layer enamel-cover includes the original of following parts by weight
Material: 42.5 parts of water, 3 parts of cellulose, 4 parts of coalescing agent, 3 parts of ethylene glycol, 1 part of neutralizer, 1.5 parts of preservative, 120 parts of lotion,
90 700 parts of mesh snowflake white sands, 100 125 parts of mesh snowflake white sands.
4. a kind of preparation method of stone coating according to claim 1 to 3, which comprises the following steps:
(1) it prepares thick prime paint: water and cellulose is mixed, disperse 3-8 minutes under 800-1200 turns/min revolving speed；Then plus
Enter coalescing agent, ethylene glycol, neutralizer and lotion, is stirred evenly under 100-300 turns/min revolving speed；Then preservative is added,
And 60 mesh snowflake white sands and 80 mesh snowflake white sands are slowly added to, it is stirred evenly under 50-150 turns/min revolving speed；
(2) it prepares fine flour layer paint: water and cellulose is mixed, disperse 2-10 minutes under 900-1400 turns/min revolving speed；Then
Coalescing agent, ethylene glycol, neutralizer and lotion is added, is stirred evenly under 100-300 turns/min revolving speed；Then anti-corrosion is added
Agent, and 90 mesh snowflake white sands, 100 mesh snowflake white sands are slowly added to, it is stirred evenly under 80-150 turns/min revolving speed.
5. the preparation method of stone coating according to claim 4, which is characterized in that step (1) prepares thick prime paint: by water
It mixes with cellulose, disperses 5 minutes under 1000 turns/min revolving speed；Then coalescing agent, ethylene glycol, neutralizer and cream is added
Liquid stirs evenly under 200 turns/min revolving speed；Then preservative is added, and is slowly added to 60 mesh snowflake white sands and 80 mesh snowflakes
White sand stirs evenly under 100 turns/min revolving speed.
6. the preparation method of stone coating according to claim 4, which is characterized in that step (2) prepares fine flour layer paint: by water
It mixes with cellulose, disperses 5 minutes under 1000 turns/min revolving speed；Then coalescing agent, ethylene glycol, neutralizer and cream is added
Liquid stirs evenly under 200 turns/min revolving speed；Then preservative is added, and is slowly added to 90 mesh snowflake white sands, 100 mesh snowflakes
White sand stirs evenly under 100 turns/min revolving speed.