CN103993714B - A kind of in mixed earth metope brushing alkyd resin coating method - Google Patents
A kind of in mixed earth metope brushing alkyd resin coating method Download PDFInfo
- Publication number
- CN103993714B CN103993714B CN201410228129.8A CN201410228129A CN103993714B CN 103993714 B CN103993714 B CN 103993714B CN 201410228129 A CN201410228129 A CN 201410228129A CN 103993714 B CN103993714 B CN 103993714B
- Authority
- CN
- China
- Prior art keywords
- alkyd resin
- resin coating
- brushing
- putty
- metope
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention has opened one in mixed earth metope brushing alkyd resin coating method, comprises the following steps: S1: the impurity on cleaning metope, S2: the impurity such as residue and mottling is polished, polished with sand paper; S3: choose coupling priming paint, S4: the putty of the following component of proportioning and mass fraction: laterally scrape first pass putty: vertically completely scrape with rubber scraper plate again, S5: brushing first pass alkyd resin coating, S7: brush second time alkyd resin coating, S8: after alkyd resin coating drying, S9: brush the 3rd time alkyd resin coating, S10: after alkyd resin coating drying, individual defects or leakage are smeared putty and will be repaired, and polish, polish after drying with dry sanding paper.The method makes metope avoid occurring several salient points or concave point, more smooth.
Description
Technical field
The present invention relates to a kind of in mixed earth metope brushing alkyd resin coating method.
Background technology
Alkyd resin production technical maturity, raw material sources are easy, obtained film combination property is good, there is the advantages such as dryness, gloss, pliability, adhesive power is good, alkyd resins can painting separately, also (some performance of film can be improved by introducing other resin with other classification resin miscible, wherein important with the amino-stoving varnish coordinated with amino resins) painting afterwards, varnish can be made, also can be made into colored paint, these products can be constructed by methods such as spraying, brushing, dip-coating, roller coat.Therefore with a very important position in current coating industry of alkyd resins and alkyd resin coating, can not be substituted.
But alkyd resin coating is directly brushed on mixed earth metope by there be limited evidence currently of, because mixed earth metope is comparatively coarse, after alkyd resin coating brushing, directly causes metope to have several salient points or concave point, cannot construction requirement be reached.And when brushing, also can only adopt and repeatedly spraying, causing the lacquer painting of metope that consistency of thickness cannot be ensured like this, and finally still can there is several salient points or concave point on metope.
Summary of the invention
The technical problem to be solved in the present invention is, provides a kind of metope that makes to avoid occurring several salient points or concave point, more smooth in mixed earth metope brushing alkyd resin coating method.
Technical scheme of the present invention is, provides a kind of preparation method at mixed earth metope brushing alkyd resin coating with following structure, comprises the following steps: comprise the following steps:
S1: the impurity on cleaning metope, the filling of basic crack use putty is repaired, and collides with, pitted skin, gap place gypsum putty repair;
S2: after the basic unit's drying after process, polishes with sand paper residue and mottling impurity, polishes;
S3: choose coupling priming paint, and by paint: the dilution paint of priming paint=1:3 adopts roller coating, brushing and spraying to carry out, and makes priming paint permeate basic unit, forms firmly basal plane;
S4: the putty of the following component of proportioning and mass fraction:
French chalk 4.5 ~ 5.5 parts
Emulsion 0.8 ~ 1.2 part
2% cmc soln 3 ~ 5 parts;
Laterally scrape first pass putty: with rubber scraper plate transverse direction completely scrape, and then a plate, joint are end to end for a plate, wait air-dry after, with sand papering, floating putty, mottling, brush line are all polished, polish;
Vertically completely scrape with rubber scraper plate, an a plate and then plate, joint does not interspace again, wait air-dry after, with sand papering, floating putty, mottling, brush line are all polished, polish;
S5: brushing first pass alkyd resin coating, adopts spread pen brushing, and brushing order is sent top to bottm, from left to right;
S6: after alkyd resin coating drying, will repair if putty is smeared in defectiveness or leakage, polishes, polishes after drying with dry sanding paper;
S7: brush second time alkyd resin coating, adopts roll coating process, alkyd resin coating is first roughly coated in basic unit by W mode by the hair roller dipping in paint, and metope is upper and lower, roll back and forth in left and right, coating is evenly launched in basic unit then to use the hair roller not dipping in paint to be close to;
S8: after alkyd resin coating drying, individual defects or leakage are smeared putty and will be repaired, and polish, polish after drying with dry sanding paper;
S9: brush the 3rd time alkyd resin coating, brushing order is sent top to bottm, and from left to right, adopt spraying brushing, the distance of nozzle and metope is about 400MM ~ 600MM, and during spraying, route wants straight, and nozzle will perpendicular to metope.
S10: after alkyd resin coating drying, individual defects or leakage are smeared putty and will be repaired, and polish, polish after drying with dry sanding paper.
In described step S1, old paint film paint stripper is removed, then clean with family expenses Eusol, retain to rinse well with clear water after 48 hours and dry again.
Have color separation for metope, before brushing, bullet divides colo(u)r streak, first to brush after light alkyd resin coating degradation look alkyd resin coating again during brushing.
After adopting above step, method of the present invention compared with prior art has the following advantages: tied by base treatment, dry sanding paper and primed early stage and do pretreatment, mixed earth body of wall is made to become flat smooth like this, for the brushing alkyd resin coating in later stage is prepared, and then by primary spread pen brushing, again by secondary roll coating process brushing after dry process, last spraying brushing for the third time after again dry, thus metope can be made to avoid occurring several salient points or concave point, more smooth.
As improvement, in described step S1, remove for old paint film paint stripper, then clean with family expenses Eusol, retain to rinse well with clear water after 48 hours and dry, such treatment effect is better.
As improvement, have color separation for metope, before brushing, bullet divides colo(u)r streak, first to brush after light alkyd resin coating degradation look alkyd resin coating again, ensure the final effect of color separation during brushing.
Detailed description of the invention
According to specific embodiment, the invention will be further described below.
One of the present invention, in mixed earth metope brushing alkyd resin coating method, comprises the following steps: comprise the following steps:
S1: the impurity on cleaning metope, the filling of basic crack use putty is repaired, and collides with, pitted skin, gap place gypsum putty repair;
S2: after the basic unit's drying after process, polishes with sand paper residue and mottling impurity, polishes;
S3: choose coupling priming paint, and by paint: the dilution paint of priming paint=1:3 adopts roller coating, brushing and spraying to carry out, and makes priming paint permeate basic unit, forms firmly basal plane;
S4: the putty of the following component of proportioning and mass fraction:
French chalk 5 parts
Emulsion 1 part
2% cmc soln 3.5 parts;
Laterally scrape first pass putty: with rubber scraper plate transverse direction completely scrape, a plate and then a plate, joint do not interspace, wait air-dry after, with sand papering, floating putty, mottling, brush line are all polished, polish;
Vertically completely scrape with rubber scraper plate, an a plate and then plate, joint is end to end again, wait air-dry after, with sand papering, floating putty, mottling, brush line are all polished, polish;
S5: brushing first pass alkyd resin coating, adopts spread pen brushing, and brushing order is sent top to bottm, from left to right;
S6: after alkyd resin coating drying, will repair if putty is smeared in defectiveness or leakage, polishes, polishes after drying with dry sanding paper;
S7: brush second time alkyd resin coating, adopts roll coating process, alkyd resin coating is first roughly coated in basic unit by W mode by the hair roller dipping in paint, and metope is upper and lower, roll back and forth in left and right, coating is evenly launched in basic unit then to use the hair roller not dipping in paint to be close to;
S8: after alkyd resin coating drying, individual defects or leakage are smeared putty and will be repaired, and polish, polish after drying with dry sanding paper;
S9: brush the 3rd time alkyd resin coating, brushing order is sent top to bottm, and from left to right, adopt spraying brushing, the distance of nozzle and metope is about 400MM ~ 600MM, and during spraying, route wants straight, and nozzle will perpendicular to metope.
S10: after alkyd resin coating drying, individual defects or leakage are smeared putty and will be repaired, and polish, polish after drying with dry sanding paper.
In described step S1, old paint film paint stripper is removed, then clean with family expenses Eusol, retain to rinse well with clear water after 48 hours and dry again.
Have color separation for metope, before brushing, bullet divides colo(u)r streak, first to brush after light alkyd resin coating degradation look alkyd resin coating again during brushing.
Claims (3)
1., in a mixed earth metope brushing alkyd resin coating method, it is characterized in that: comprise the following steps:
S1: the impurity on cleaning metope, the filling of basic crack use putty is repaired, and collides with, pitted skin, gap place gypsum putty repair;
S2: after the basic unit's drying after process, polishes with sand paper residue and mottling impurity, polishes;
S3: choose coupling priming paint, and by paint: the dilution paint of priming paint=1:3 adopts roller coating, brushing and spraying to carry out, and makes priming paint permeate basic unit, forms firmly basal plane;
S4: the putty of the following component of proportioning and mass fraction:
French chalk 4.5 ~ 5.5 parts
Emulsion 0.8 ~ 1.2 part
2% cmc soln 3 ~ 5 parts;
Laterally scrape first pass putty: with rubber scraper plate transverse direction completely scrape, and then a plate, joint are end to end for a plate, wait air-dry after, with sand papering, floating putty, mottling, brush line are all polished, polish;
Vertically completely scrape with rubber scraper plate, an a plate and then plate, joint does not interspace again, wait air-dry after, with sand papering, floating putty, mottling, brush line are all polished, polish;
S5: brushing first pass alkyd resin coating, adopts spread pen brushing, and brushing order is sent top to bottm, from left to right;
S6: after alkyd resin coating drying, will repair if putty is smeared in defectiveness or leakage, polishes, polishes after drying with dry sanding paper;
S7: brush second time alkyd resin coating, adopts roll coating process, alkyd resin coating is first roughly coated in basic unit by W mode by the hair roller dipping in paint, and metope is upper and lower, roll back and forth in left and right, coating is evenly launched in basic unit then to use the hair roller not dipping in paint to be close to;
S8: after alkyd resin coating drying, individual defects or leakage are smeared putty and will be repaired, and polish, polish after drying with dry sanding paper;
S9: brush the 3rd time alkyd resin coating, brushing order is sent top to bottm, and from left to right, adopt spraying brushing, the distance of nozzle and metope is about 400MM ~ 600MM, and during spraying, route wants straight, and nozzle will perpendicular to metope.
S10: after alkyd resin coating drying, individual defects or leakage are smeared putty and will be repaired, and polish, polish after drying with dry sanding paper.
2. one according to claim 1 is in mixed earth metope brushing alkyd resin coating method: it is characterized in that: in described step S1, old paint film paint stripper is removed, clean with family expenses Eusols again, retain to rinse well with clear water after 48 hours and dry again.
3. one according to claim 1 is in mixed earth metope brushing alkyd resin coating method: it is characterized in that: have color separation for metope, and before brushing, bullet divides colo(u)r streak, first to brush after light alkyd resin coating degradation look alkyd resin coating again during brushing.