CN107419858A - A kind of inner wall render smears construction method - Google Patents
A kind of inner wall render smears construction method Download PDFInfo
- Publication number
- CN107419858A CN107419858A CN201710536017.2A CN201710536017A CN107419858A CN 107419858 A CN107419858 A CN 107419858A CN 201710536017 A CN201710536017 A CN 201710536017A CN 107419858 A CN107419858 A CN 107419858A
- Authority
- CN
- China
- Prior art keywords
- bottoming
- putty
- layer
- wall
- construction method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of inner wall render to smear construction method, comprises the following steps：Step 1：Clear up metope；Step 2：Base treatment, continue watering moistening interior wall basal plane, swabbing mud 1 ~ 3, then with the part by weight of cement and yellow ground be 1:2 ~ 3 cement mortar is painted, and is divided two layers and is painted, is then struck off with floating rule, is finally rubbed with the hands with wooden float flat；Step 3：Putty bottoming;When the mortar strength in step 2 reaches 70 ~ 75%, bottoming is carried out with powder of lacquer putty for use on, point two layers of progress bottoming, the bottoming of first layer putty and second layer putty bottoming interval are after 8 ~ 24 hours, beat behind bottom after carrying out natural curing, and polished with Plane surface grinding machine, rubber paper two procedures；Step 4：Surface layer roller coating.The present invention provides a kind of inner wall render smearing method, the inner wall putty powder using desulfurated plaster as base-material, not only with excellent application property and grinability, is easy to improve efficiency of construction, has very high environmental benefit and social benefit.
Description
Technical field
The invention belongs to furnishing fields, and in particular to a kind of inner wall render smears construction method.
Background technology
The coating of Discussion on architecture metope paints technique and determines that whether smooth metope is attractive in appearance, and irrational construction method can be led
Cause numerous quality problems, as putty dry after it is cracked, cause emulsion paint to be cracked, its reason once apply Puttying it is too thick or
It is uneven, base treatment is not clean, hole recess dust, debris are not cleaned out, and putty can not take root；And for example surface layer hollowing,
Crack, its main cause are structural substrates injustice, scratch coat gage distortion, are not layered bottoming by code and lattice is constructed, by
The not lattice, not stratified after large area cement mortar is smeared, dries contraction and differs, can form hollowing and cracks；In addition, doing surface layer
When, because base cleaning is not net, basic unit is relatively dry, also equally can be by surface layer drawing crack.
The content of the invention
In view of the above-mentioned problems, the technical problem to be solved in the present invention is to provide a kind of inner wall render to smear construction method, put down
It is whole uniform, without crack.
To achieve the above object, the technical scheme is that：A kind of inner wall render smears construction method, including following step
Suddenly：
Step 1：Clear up metope
First the foreign matter of metope is removed with broom in the inner wall surface that will paint smearing, then is sprinkled with 10~20kg/m3Water,
Wait water to be completely immersed in inner wall surface and stop watering, 20~30min of naturally dry；
Step 2：Base treatment
Continue watering moistening interior wall basal plane, swabbing mud 1~3, then with the part by weight of cement and yellow ground be 1:2~3
Cement mortar painted, painted point two layers, then struck off, finally rubbed with the hands with wooden float flat with floating rule；
Step 3：Putty bottoming
When the mortar strength in step 2 reaches 70~75%, bottoming is carried out with powder of lacquer putty for use on, point two layers of progress bottoming, the
One layer of putty bottoming and second layer putty bottoming interval be after 8~24 hours, has beaten behind bottom after carrying out natural curing, and with polishing
Machine, rubber paper two procedures are polished；
Step 4：Surface layer roller coating
Beat in step 3 on the metope of powder of lacquer putty for use on and brush a bed boundary agent, and rolled one time again after 3~6 hours, then
Maintained.
Preferably, the foreign matter in the step 1 is powder ash, greasy dirt, coating or weaker zone.
Preferably, painted in the step 2, it is 0.08~0.1cm that first layer, which paints thickness, second layer powder point two layers
Brush thickness is 0.05~0.09cm.
Preferably, the powder of lacquer putty for use in the step 3 is made up of the raw material of following parts by weight：Desulfurated plaster 10~15
Part, 5~12 parts of slag powders, 3~9 parts of aluminate cement, 5~12 parts of talcum powder, 2~5 parts of lime, hydroxypropyl starch ether and fluorine silicon
Sour 0.5~3.5 part of sodium.
Preferably, the first layer putty bottoming thickness in the step 3 is 0.3~0.5cm, second layer putty bottoming thickness
For 0.2~0.3cm.
Preferably, the husky mulberry paper in the step 3 is 500~600 mesh sand mulberry paper.
Preferably, the preparation method of the interfacial agents in the step 4 is from portland cement and sand, the silicate
Cement is 42.5R portland cement, and the clay content of the sand is 3%~7%, and the granularity of sand is 2.0~2.5mm, will
Portland cement and sand uniform stirring, water is added during stirring and obtains the interfacial agents.
Preferably, resulting interfacial agents were finished in 2~3 hours.
The beneficial effects of the present invention are：The present invention provides a kind of inner wall render smearing method, using desulfurated plaster as base-material
Inner wall putty powder, not only with excellent application property and grinability, be easy to improve efficiency of construction, there is very high environmental benefit
And social benefit.
The rendering of the present invention smears construction with easily smearing, easily striking off, easily repairing, and labor intensity is low, and material consumption is few, winter
The features such as construction influences when not being bullied temperature drop as little as close to 0 DEG C；Last in the construction brushes one on the metope for beat powder of lacquer putty for use on
Bed boundary agent, painted wall crazing can be prevented, and there is the characteristics of moistureproof.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is described in further detail.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, and it is unlimited
The fixed present invention.
Embodiment 1
A kind of inner wall render smears construction method, comprises the following steps：
Step 1：Clear up metope
First the foreign matter of metope is removed with broom in the inner wall surface that will paint smearing, then is sprinkled with 10kg/m3Water, wait
Water is completely immersed in inner wall surface and stops watering, naturally dry 20min；
Step 2：Base treatment
Continue watering moistening interior wall basal plane, swabbing mud 1, then with the part by weight of cement and yellow ground be 1:2 cement
Mortar is painted, and is divided two layers and is painted, is then struck off with floating rule, is finally rubbed with the hands with wooden float flat；
Step 3：Putty bottoming
When the mortar strength in step 2 reaches 70%, bottoming is carried out with powder of lacquer putty for use on, point two layers of progress bottoming, first layer
Putty bottoming and second layer putty bottoming interval be after 8 hours, has beaten behind bottom after carrying out natural curing, and with Plane surface grinding machine, rubber
Paper two procedures are polished；
Step 4：Surface layer roller coating
Beat in step 3 on the metope of powder of lacquer putty for use on and brush a bed boundary agent, rolled again after 3 hours one time, Ran Houjin
Row maintenance.
Foreign matter in the step 1 is powder ash, greasy dirt, coating or weaker zone.
Divide two layers in the step 2 and painted, it is 0.08cm that first layer, which paints thickness, and the second layer paints thickness and is
0.05cm。
The powder of lacquer putty for use in the step 3 is made up of the raw material of following parts by weight：10 parts of desulfurated plaster, 5 parts of slag powders,
0.5 part of 3 parts of aluminate cement, 5 parts of talcum powder, 2 parts of lime, hydroxypropyl starch ether and prodan.
First layer putty bottoming thickness in the step 3 is 0.3m, and second layer putty bottoming thickness is 0.2cm.
Husky mulberry paper in the step 3 is 500 mesh sand mulberry paper.
The preparation method of interfacial agents in the step 4 is to be from portland cement and sand, the portland cement
42.5R portland cement, the clay content of the sand is 3%, and the granularity of sand is 2.0mm, by portland cement and sand
Uniform stirring, water is added during stirring and obtains the interfacial agents.
Resulting interfacial agents were finished in 2 hours.
Embodiment 2
A kind of inner wall render smears construction method, comprises the following steps：
Step 1：Clear up metope
First the foreign matter of metope is removed with broom in the inner wall surface that will paint smearing, then is sprinkled with 15kg/m3Water, wait
Water is completely immersed in inner wall surface and stops watering, naturally dry 25min；
Step 2：Base treatment
Continue watering moistening interior wall basal plane, swabbing mud 2, then with the part by weight of cement and yellow ground be 1:2.5 water
Cement mortar is painted, and is divided two layers and is painted, is then struck off with floating rule, is finally rubbed with the hands with wooden float flat；
Step 3：Putty bottoming
When the mortar strength in step 2 reaches 73%, bottoming is carried out with powder of lacquer putty for use on, point two layers of progress bottoming, first layer
Putty bottoming and second layer putty bottoming interval be after 16 hours, has beaten behind bottom after carrying out natural curing, and with Plane surface grinding machine, rubber
Paper two procedures are polished；
Step 4：Surface layer roller coating
Beat in step 3 on the metope of powder of lacquer putty for use on and brush a bed boundary agent, rolled again after 4 hours one time, Ran Houjin
Row maintenance.
Foreign matter in the step 1 is powder ash, greasy dirt, coating or weaker zone.
Divide two layers in the step 2 and painted, it is 0.09cm that first layer, which paints thickness, and the second layer paints thickness and is
0.07cm。
The powder of lacquer putty for use in the step 3 is made up of the raw material of following parts by weight：12 parts of desulfurated plaster, 9 parts of slag powders,
2 parts of 6 parts of aluminate cement, 8 parts of talcum powder, 3 parts of lime, hydroxypropyl starch ether and prodan.
First layer putty bottoming thickness in the step 3 is 0.4cm, and second layer putty bottoming thickness is 0.25cm.
Husky mulberry paper in the step 3 is 550 mesh sand mulberry paper.
The preparation method of interfacial agents in the step 4 is to be from portland cement and sand, the portland cement
42.5R portland cement, the clay content of the sand is 5%, and the granularity of sand is 2.3mm, by portland cement and sand
Uniform stirring, water is added during stirring and obtains the interfacial agents.
Resulting interfacial agents were finished in 2.5 hours.
Embodiment 3
A kind of inner wall render smears construction method, comprises the following steps：
Step 1：Clear up metope
First the foreign matter of metope is removed with broom in the inner wall surface that will paint smearing, then is sprinkled with 20kg/m3Water, wait
Water is completely immersed in inner wall surface and stops watering, naturally dry 30min；
Step 2：Base treatment
Continue watering moistening interior wall basal plane, swabbing mud 3, then with the part by weight of cement and yellow ground be 1:3 cement
Mortar is painted, and is divided two layers and is painted, is then struck off with floating rule, is finally rubbed with the hands with wooden float flat；
Step 3：Putty bottoming
When the mortar strength in step 2 reaches 75%, bottoming is carried out with powder of lacquer putty for use on, point two layers of progress bottoming, first layer
Putty bottoming and second layer putty bottoming interval be after 24 hours, has beaten behind bottom after carrying out natural curing, and with Plane surface grinding machine, rubber
Paper two procedures are polished；
Step 4：Surface layer roller coating
Beat in step 3 on the metope of powder of lacquer putty for use on and brush a bed boundary agent, rolled again after 6 hours one time, Ran Houjin
Row maintenance.
Foreign matter in the step 1 is powder ash, greasy dirt, coating or weaker zone.
Divide two layers in the step 2 and painted, it is 0.1cm that first layer, which paints thickness, and the second layer paints thickness and is
0.09cm。
The powder of lacquer putty for use in the step 3 is made up of the raw material of following parts by weight：15 parts of desulfurated plaster, slag powders 12
Part, 9 parts of aluminate cement, 12 parts of talcum powder, 5 parts of lime, hydroxypropyl starch ether and 3.5 parts of prodan.
First layer putty bottoming thickness in the step 3 is 0.5cm, and second layer putty bottoming thickness is 0.3cm.
Husky mulberry paper in the step 3 is 600 mesh sand mulberry paper.
The preparation method of interfacial agents in the step 4 is to be from portland cement and sand, the portland cement
42.5R portland cement, the clay content of the sand is 7%, and the granularity of sand is 2.5mm, by portland cement and sand
Uniform stirring, water is added during stirring and obtains the interfacial agents.
Resulting interfacial agents were finished in 3 hours.
Performance test
To the present embodiment 1, embodiment 2, crack resistance is dried in embodiment 3, surface answers pressure to test, and with existing
There is technology to be compared as a control group, the following form of test result：
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, although with reference to foregoing reality
Apply example the present invention is described in detail, for those skilled in the art, it still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic.All essences in the present invention
God any modification, equivalent substitution and improvements made etc., should be included in the scope of the protection with principle.
Claims (8)
1. a kind of inner wall render smears construction method, it is characterised in that comprises the following steps：
Step 1：Clear up metope
First the foreign matter of metope is removed with broom in the inner wall surface that will paint smearing, then is sprinkled with 10 ~ 20kg/m3Water, wait water
It is completely immersed in inner wall surface and stops watering, 20 ~ 30min of naturally dry；
Step 2：Base treatment
Continue watering moistening interior wall basal plane, swabbing mud 1 ~ 3, then with the part by weight of cement and yellow ground be 1:2 ~ 3 cement
Mortar is painted, and is divided two layers and is painted, is then struck off with floating rule, is finally rubbed with the hands with wooden float flat；
Step 3：Putty bottoming
When the mortar strength in step 2 reaches 70 ~ 75%, bottoming is carried out with powder of lacquer putty for use on, divides two layers and carries out bottoming, first layer is greasy
Sub- bottoming and second layer putty bottoming interval be after 8 ~ 24 hours, has beaten behind bottom after carrying out natural curing, and with Plane surface grinding machine, rubber
Paper two procedures are polished；
Step 4：Surface layer roller coating
Beat in step 3 on the metope of powder of lacquer putty for use on and brush a bed boundary agent, and rolled after 3 ~ 6 hours one time, then carry out again
Maintenance.
2. a kind of inner wall render according to claim 1 smears construction method, it is characterised in that different in the step 1
Thing is powder ash, greasy dirt, coating or weaker zone.
3. a kind of inner wall render according to claim 1 smears construction method, it is characterised in that is divided to two in the step 2
Layer is painted, and it is 0.08 ~ 0.1cm that first layer, which paints thickness, and it is 0.05 ~ 0.09cm that the second layer, which paints thickness,.
4. a kind of inner wall render according to claim 1 smears construction method, it is characterised in that the institute in the step 3
Powder of lacquer putty for use on is stated to be made up of the raw material of following parts by weight：10 ~ 15 parts of desulfurated plaster, 5 ~ 12 parts of slag powders, 3 ~ 9 parts of aluminate cement,
0.5 ~ 3.5 part of 5 ~ 12 parts of talcum powder, 2 ~ 5 parts of lime, hydroxypropyl starch ether and prodan.
5. a kind of inner wall render according to claim 1 smears construction method, it is characterised in that the in the step 3
One layer of putty bottoming thickness is 0.3 ~ 0.5cm, and second layer putty bottoming thickness is 0.2 ~ 0.3cm.
6. a kind of inner wall render according to claim 1 smears construction method, it is characterised in that the sand in the step 3
Mulberry paper is 500 ~ 600 mesh sand mulberry paper.
7. a kind of inner wall render according to claim 1 smears construction method, it is characterised in that the boundary in the step 4
The preparation method of face agent is from portland cement and sand, and the portland cement is 42.5R portland cement, the sand
The clay content of son is 3% ~ 7%, and the granularity of sand is 2.0 ~ 2.5mm, by portland cement and sand uniform stirring, the process of stirring
Middle addition water obtains the interfacial agents.
8. a kind of inner wall render according to claim 7 smears construction method, it is characterised in that resulting interfacial agents exist
It is finished in 2 ~ 3 hours.