CN104119790B - A kind of external application building coating - Google Patents
A kind of external application building coating Download PDFInfo
- Publication number
- CN104119790B CN104119790B CN201410381489.1A CN201410381489A CN104119790B CN 104119790 B CN104119790 B CN 104119790B CN 201410381489 A CN201410381489 A CN 201410381489A CN 104119790 B CN104119790 B CN 104119790B
- Authority
- CN
- China
- Prior art keywords
- parts
- external application
- building coating
- oxide
- application building
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of external application building coating, its raw materials by weight portion proportioning is as follows: trimellitic acid 1,2-anhydride 100 parts; Di(2-ethylhexyl)phosphate cresols ester 40-50 part; Epoxy soybean oil 70-80 part; Rosin 5-10 part; Tetramethylolmethane 45-55 part; Plumbous oxide 20-30 part; Deionized water 60-80 part; Magnesium oxide 30-40 part; Promotor 20-30 part; Zinc oxide 25-35 part; Sulphur 5-15 part; Paraffin 5-15 part; Softening agent 5-10 part; Zinc chloride 10-20 part; Titanium dioxide 25-35 part; Manganese naphthenate 1-10 part; Product viscosity 50-60s, opacifying power 280-320g/cm2; Package stability 6-8 month; Without exception soak 5-15d in water after; The film 2600-2800 of resistance to wiping time, the widespread production not division of history into periods can replace current material.
Description
Technical field
The application belongs to paint field, particularly relates to a kind of external application building coating.
Background technology
Coating, is called paint in Chinese tradition name.So-called coating is coated in protected or decorated body surface; and the continuous film of firm attachment can be formed with coated article; normally based on resin or oily or emulsion; add or do not add promotor, filler; add corresponding additive, with organic solvent or the formulated thick liquid of tetramethylolmethane.Paint finishing can bond very well with body material in body surface and form the material of complete and tough and tensile protective membrane, is called coating.Coating and paint are identical concepts.Paint is people's custom titles used for a long time, after introducing China, just utilizes in building trade always.The effect of coating may be summarized to be three aspects: provide protection, decoration function, specific function effect.The general composition of coating: comprise filmogen, color stuffing, solvent, auxiliary agent.
Coating refers to and is applied to body surface and the general name forming the material of tough and tensile protective membrane, and building coating is an important class in coating, in China, generally will be used for inner wall of building, exterior wall, ceiling, ground, and the coating of toilet is called building coating.Building coating has decoration functions, defencive function and livability and improves function.Proportion shared by various function is not quite similar because application target is different.Decoration functions is the function of beautifying the appearance value improving it by buildings.Mainly comprise the design design of plane color, pattern and gloss aspect and the design design of three-dimensional pattern.But to match with the size and shape of the moulding of buildings itself and base material itself, just can fully play out.Defencive function refers to architecture protection thing not by the impact of environment and the function of destruction.The content that different types of protected body requires defencive function is also different.As just very large in the indoor index difference with reaching required by outdoor application.Building coating is mainly used in the coating products of house decoration as a class, and its market development and real estate industry develop closely related.
Some buildingss to mildew-resistant, fire prevention, heat insulating, corrosion-resistant etc. have particular requirement.Livability improves function mainly for indoor application, contributes to the function improving living environment exactly, as sound-proofing, sound absorbing, antisweat etc.And universal along with humanity concept, and the formation of novel harmonious society, designs that a kind of viscosity is high, opacifying power is high, the external application building coating of water tolerance and resistance to wiping excellence is very important.
Summary of the invention
The technical problem solved:
The application, for above-mentioned technical problem, provides a kind of external application building coating, solves that existing external application building coating viscosity is low, opacifying power is low, the technical problem such as water tolerance and resistance to wiping difference.
Technical scheme:
A kind of external application building coating, the raw materials by weight portion proportioning of described external application building coating is as follows: trimellitic acid 1,2-anhydride 100 parts; Di(2-ethylhexyl)phosphate cresols ester 40-50 part; Epoxy soybean oil 70-80 part; Rosin 5-10 part; Tetramethylolmethane 45-55 part; Plumbous oxide 20-30 part; Deionized water 60-80 part; Magnesium oxide 30-40 part; Promotor 20-30 part; Zinc oxide 25-35 part; Sulphur 5-15 part; Paraffin 5-15 part; Softening agent 5-10 part; Zinc chloride 10-20 part; Titanium dioxide 25-35 part; Manganese naphthenate 1-10 part.
As a preferred technical solution of the present invention: the raw materials by weight portion proportioning of described external application building coating is as follows: trimellitic acid 1,2-anhydride 100 parts; Di(2-ethylhexyl)phosphate cresols ester 45 parts; Epoxy soybean oil 75 parts; Rosin 8 parts; Tetramethylolmethane 50 parts; 25 parts, plumbous oxide; Deionized water 70 parts; 35 parts, magnesium oxide; Promotor 25 parts; 30 parts, zinc oxide; 10 parts, sulphur; 10 parts, paraffin; 7 parts, softening agent; Zinc chloride 15 parts; Titanium dioxide 30 parts; Manganese naphthenate 5 parts.
As a preferred technical solution of the present invention: described promotor adopts benzothiazole.
As a preferred technical solution of the present invention: described softening agent adopts dibutyl phthalate.
Beneficial effect:
A kind of external application building coating of the present invention adopts above technical scheme compared with prior art, has following technique effect: 1, product viscosity 50-60s, opacifying power 280-320g/cm
2; 2, package stability 6-8 month; Without exception soak 5-15d in water after; 3, the film 2600-2800 of resistance to wiping time, the widespread production not division of history into periods current material can be replaced.
Embodiment
Embodiment 1:
A kind of external application building coating, its raw materials by weight portion proportioning is as follows: trimellitic acid 1,2-anhydride 100 parts; Di(2-ethylhexyl)phosphate cresols ester 40 parts; Epoxy soybean oil 70 parts; Rosin 5 parts; Tetramethylolmethane 45 parts; 20 parts, plumbous oxide; Deionized water 60 parts; 30 parts, magnesium oxide; Benzothiazole 20 parts; 25 parts, zinc oxide; 5 parts, sulphur; 5 parts, paraffin; Dibutyl phthalate 5 parts; Zinc chloride 10 parts; Titanium dioxide 25 parts; Manganese naphthenate 1 part.
Di(2-ethylhexyl)phosphate cresols ester is added after dissolving in deionized water, add trimellitic acid 1,2-anhydride, epoxy soybean oil, tetramethylolmethane, benzothiazole, dibutyl phthalate, plumbous oxide, zinc oxide, with ball mill ball milling 30min, then add rosin and surplus stock, ball milling 30min both obtained finished product.
Product viscosity 50s, opacifying power 280g/cm
2; Package stability 6 months; Without exception soak 5d in water after; The resistance to wiping of film 2600 times.
Embodiment 2:
A kind of external application building coating, its raw materials by weight portion proportioning is as follows: trimellitic acid 1,2-anhydride 100 parts; Di(2-ethylhexyl)phosphate cresols ester 50 parts; Epoxy soybean oil 80 parts; Rosin 10 parts; Tetramethylolmethane 55 parts; 30 parts, plumbous oxide; Deionized water 80 parts; 40 parts, magnesium oxide; Benzothiazole 30 parts; 35 parts, zinc oxide; 15 parts, sulphur; 15 parts, paraffin; Dibutyl phthalate 10 parts; Zinc chloride 20 parts; Titanium dioxide 35 parts; Manganese naphthenate 10 parts.
Di(2-ethylhexyl)phosphate cresols ester is added after dissolving in deionized water, add trimellitic acid 1,2-anhydride, epoxy soybean oil, tetramethylolmethane, benzothiazole, dibutyl phthalate, plumbous oxide, zinc oxide, with ball mill ball milling 30min, then add rosin and surplus stock, ball milling 30min both obtained finished product.
Product viscosity 55s, opacifying power 300g/cm
2; Package stability 7 months; Without exception soak 10d in water after; The resistance to wiping of film 2700 times.
Embodiment 3:
A kind of external application building coating, its raw materials by weight portion proportioning is as follows: trimellitic acid 1,2-anhydride 100 parts; Di(2-ethylhexyl)phosphate cresols ester 45 parts; Epoxy soybean oil 75 parts; Rosin 8 parts; Tetramethylolmethane 50 parts; 25 parts, plumbous oxide; Deionized water 70 parts; 35 parts, magnesium oxide; Benzothiazole 25 parts; 30 parts, zinc oxide; 10 parts, sulphur; 10 parts, paraffin; Dibutyl phthalate 7 parts; Zinc chloride 15 parts; Titanium dioxide 30 parts; Manganese naphthenate 5 parts.
Di(2-ethylhexyl)phosphate cresols ester is added after dissolving in deionized water, add trimellitic acid 1,2-anhydride, epoxy soybean oil, tetramethylolmethane, benzothiazole, dibutyl phthalate, plumbous oxide, zinc oxide, with ball mill ball milling 30min, then add rosin and surplus stock, ball milling 30min both obtained finished product.
Product viscosity 60s, opacifying power 320g/cm
2; Package stability 8 months; Without exception soak 15d in water after; The resistance to wiping of film 2800 times.
Composition all components in above embodiment all can business be bought.
Above-described embodiment is just for setting forth content of the present invention, instead of restriction, and any change therefore in the implication suitable with claims of the present invention and scope, all should think to be included in the scope of claims.
Claims (2)
1. an external application building coating, is characterized in that the raw materials by weight portion proportioning of described external application building coating is as follows: trimellitic acid 1,2-anhydride 100 parts; Di(2-ethylhexyl)phosphate cresols ester 40-50 part; Epoxy soybean oil 70-80 part; Rosin 5-10 part; Tetramethylolmethane 45-55 part; Plumbous oxide 20-30 part; Deionized water 60-80 part; Magnesium oxide 30-40 part; Promotor 20-30 part; Zinc oxide 25-35 part; Sulphur 5-15 part; Paraffin 5-15 part; Softening agent 5-10 part; Zinc chloride 10-20 part; Titanium dioxide 25-35 part; Manganese naphthenate 1-10 part;
Described promotor adopts benzothiazole;
Described softening agent adopts dibutyl phthalate.
2. a kind of external application building coating according to claim 1, is characterized in that the raw materials by weight portion proportioning of described external application building coating is as follows: trimellitic acid 1,2-anhydride 100 parts; Di(2-ethylhexyl)phosphate cresols ester 45 parts; Epoxy soybean oil 75 parts; Rosin 8 parts; Tetramethylolmethane 50 parts; 25 parts, plumbous oxide; Deionized water 70 parts; 35 parts, magnesium oxide; Promotor 25 parts; 30 parts, zinc oxide; 10 parts, sulphur; 10 parts, paraffin; 7 parts, softening agent; Zinc chloride 15 parts; Titanium dioxide 30 parts; Manganese naphthenate 5 parts.