CN105086850A - Anti-corrosion glue - Google Patents

Abstract

The invention discloses anti-corrosion glue. The anti-corrosion glue comprises, by weight, 80-120 parts of 2-hydroxyethyl methacrylate, 80-160 parts of methyl methacrylate, 40-80 parts of lauryl methacrylate, 10-30 parts of styrene, 20-30 parts of graphite nodules, 20-40 parts of methoxyphenol, 10-18 parts of acetone, 6-12 parts of acrylamide, 24-48 parts of phosphotriester, 12-18 parts of antimonous oxide, 12-16 parts of styrene, 15-20 parts of butyl methacrylate, 20-40 parts of methacrylic acid, 8-16 parts of dehydroacetic acid and 20-40 parts of butanol. The anti-corrosion glue is easy to manufacture, adopted and selected production raw materials are free of toxicity, the glue is good in use effect and environmentally friendly, a tough coating can be formed, and permanent waterproofness and anti-static performance are achieved.

Description

A kind of anticorrosion glue

Technical field

The present invention relates to a kind of technical field of chemical article, be specifically related to a kind of anticorrosion glue.

Background technology

The effect of glue in production and life is very large; widespread use and every field; the film that glue is formed can play decoration, protection and beautiful effect to object; although current most of glue on the market makes simply, price is cheap but function ratio is more single simultaneously; can only simply as the use of decoration; and in the operating environment that some are special, can not meeting needed for people of simple glue.

Summary of the invention

Object of the present invention provides a kind of anticorrosion glue, solves one or more in above-mentioned prior art problem.

According to an aspect of the present invention, a kind of anticorrosion glue, comprises the component of following weight part,

2-hydroxyethyl methacrylate 80 ~ 120 parts, methyl methacrylate 80 ~ 160 parts, lauryl methacrylate(LMA) 40 ~ 80 parts, vinylbenzene 10 ~ 30 parts, graphite pebbles 20 ~ 30 parts, methoxyphenol 20 ~ 40 parts, 10 ~ 18 parts, acetone, acrylamide 6 ~ 12 parts, phosphotriester 24 ~ 48 parts, antimonous oxide 12 ~ 18 parts, vinylbenzene 12 ~ 16 parts, butyl methacrylate 15 ~ 20 parts, methacrylic acid 20 ~ 40 parts, dehydroacetic acid (DHA) 8 ~ 16 parts, 20 ~ 40 parts, butanols.

The anticorrosion glue of one provided by the invention, makes simple, and the raw materials for production of employing are selected avirulent, and the result of use of glue is good, environmental protection, and bonding effect is good, has good anti-mildew performance.

Embodiment

Embodiment 1

A kind of anticorrosion glue, comprises the component of following weight part, 2-hydroxyethyl methacrylate 80 parts, methyl methacrylate 80 parts, lauryl methacrylate(LMA) 40 parts, vinylbenzene 10 parts, graphite pebbles 20 parts, methoxyphenol 20 parts, 10 parts, acetone, acrylamide 6 parts, phosphotriester 24 parts, antimonous oxide 12 parts, vinylbenzene 12 parts, butyl methacrylate 15 parts, methacrylic acid 20 parts, dehydroacetic acid (DHA) 8 parts, 20 parts, butanols, namely mix and blend obtains product.

Embodiment 2

A kind of anticorrosion glue, comprises the component of following weight part, 2-hydroxyethyl methacrylate 100 parts, methyl methacrylate 120 parts, lauryl methacrylate(LMA) 60 parts, vinylbenzene 20 parts, graphite pebbles 25 parts, methoxyphenol 30 parts, 14 parts, acetone, acrylamide 9 parts, phosphotriester 36 parts, antimonous oxide 15 parts, vinylbenzene 14 parts, butyl methacrylate 18 parts, methacrylic acid 30 parts, dehydroacetic acid (DHA) 12 parts, 30 parts, butanols, namely mix and blend obtains product.

Embodiment 3

A kind of anticorrosion glue, comprises the component of following weight part, 2-hydroxyethyl methacrylate 120 parts, methyl methacrylate 160 parts, lauryl methacrylate(LMA) 80 parts, vinylbenzene 30 parts, graphite pebbles 30 parts, methoxyphenol 40 parts, 18 parts, acetone, acrylamide 12 parts, phosphotriester 48 parts, antimonous oxide 18 parts, vinylbenzene 16 parts, butyl methacrylate 20 parts, methacrylic acid 20 ~ 40 parts, dehydroacetic acid (DHA) 16 parts, 40 parts, butanols, namely mix and blend obtains product.

The above is only optimal way of the present invention; it should be pointed out that to those skilled in the art, without departing from the concept of the premise of the invention; can also make some similar distortion and improvement, these also should be considered as within protection scope of the present invention.

Claims (1)

1. an anticorrosion glue, is characterized in that: the component comprising following weight part,

2-hydroxyethyl methacrylate 80 ~ 120 parts, methyl methacrylate 80 ~ 160 parts, lauryl methacrylate(LMA) 40 ~ 80 parts, vinylbenzene 10 ~ 30 parts, graphite pebbles 20 ~ 30 parts, methoxyphenol 20 ~ 40 parts, 10 ~ 18 parts, acetone, acrylamide 6 ~ 12 parts, phosphotriester 24 ~ 48 parts, antimonous oxide 12 ~ 18 parts, vinylbenzene 12 ~ 16 parts, butyl methacrylate 15 ~ 20 parts, methacrylic acid 20 ~ 40 parts, dehydroacetic acid (DHA) 8 ~ 16 parts, 20 ~ 40 parts, butanols.