WO2017047406A1 - Plaque polarisante composite et panneau à cristaux liquides qui l'utilise - Google Patents

Plaque polarisante composite et panneau à cristaux liquides qui l'utilise Download PDF

Info

Publication number
WO2017047406A1
WO2017047406A1 PCT/JP2016/075807 JP2016075807W WO2017047406A1 WO 2017047406 A1 WO2017047406 A1 WO 2017047406A1 JP 2016075807 W JP2016075807 W JP 2016075807W WO 2017047406 A1 WO2017047406 A1 WO 2017047406A1
Authority
WO
WIPO (PCT)
Prior art keywords
polarizing plate
film
polarizing
protective film
resin
Prior art date
Application number
PCT/JP2016/075807
Other languages
English (en)
Japanese (ja)
Inventor
寿和 松本
Original Assignee
住友化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友化学株式会社 filed Critical 住友化学株式会社
Priority to JP2017539830A priority Critical patent/JPWO2017047406A1/ja
Publication of WO2017047406A1 publication Critical patent/WO2017047406A1/fr

Abstract

L'invention concerne une plaque polarisante composite qui ne subit qu'une faible diminution du degré de polarisation dans des environnements à température élevée, ou à température élevée et humidité élevée. L'invention concerne également un panneau à cristaux liquides qui présente une résistance à la chaleur élevée et une résistance à la chaleur humide élevée. Elle concerne une plaque de polarisation composite dans laquelle sont superposées, dans cet ordre, une couche à faible perméabilité à l'humidité qui a une perméabilité à l'humidité de 200 g/m2 sur 24 h ou moins, un premier film polarisant qui a une épaisseur de 15 µm ou moins et un deuxième film polarisant qui a une épaisseur de 15 µm ou moins. L'axe d'absorption du premier film polarisant et l'axe d'absorption du deuxième film polarisant sont approximativement parallèles.
PCT/JP2016/075807 2015-09-18 2016-09-02 Plaque polarisante composite et panneau à cristaux liquides qui l'utilise WO2017047406A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2017539830A JPWO2017047406A1 (ja) 2015-09-18 2016-09-02 複合偏光板及びそれを用いた液晶パネル

Applications Claiming Priority (8)

Application Number Priority Date Filing Date Title
JP2015-184781 2015-09-18
JP2015184782 2015-09-18
JP2015-184782 2015-09-18
JP2015184781 2015-09-18
JP2015-240881 2015-12-10
JP2015240882 2015-12-10
JP2015-240882 2015-12-10
JP2015240881 2015-12-10

Publications (1)

Publication Number Publication Date
WO2017047406A1 true WO2017047406A1 (fr) 2017-03-23

Family

ID=58289252

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/075807 WO2017047406A1 (fr) 2015-09-18 2016-09-02 Plaque polarisante composite et panneau à cristaux liquides qui l'utilise

Country Status (3)

Country Link
JP (1) JPWO2017047406A1 (fr)
TW (1) TWI822651B (fr)
WO (1) WO2017047406A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2018205464A (ja) * 2017-06-01 2018-12-27 株式会社サンリッツ 偏光板および画像表示装置

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20200142256A1 (en) * 2017-07-14 2020-05-07 Lg Chem, Ltd. Liquid crystal panel and manufacturing method thereof
KR102281482B1 (ko) * 2018-11-12 2021-07-26 닛토덴코 가부시키가이샤 화상 표시 장치

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10133196A (ja) * 1996-10-28 1998-05-22 Sony Corp 液晶表示装置および液晶表示装置用偏光板
JP2003084271A (ja) * 2001-09-14 2003-03-19 Fujitsu Ltd 液晶表示装置
JP2005345958A (ja) * 2004-06-07 2005-12-15 Nitto Denko Corp 液晶パネル、偏光板および液晶表示装置
JP2006201401A (ja) * 2005-01-19 2006-08-03 Sharp Corp 液晶表示装置
JP2007233362A (ja) * 2006-02-02 2007-09-13 Semiconductor Energy Lab Co Ltd 表示装置
JP2009009100A (ja) * 2007-05-31 2009-01-15 Sumitomo Chemical Co Ltd 偏光板
JP2010039420A (ja) * 2008-08-08 2010-02-18 Nitto Denko Corp 液晶パネルおよび液晶表示装置
JP2011059266A (ja) * 2009-09-08 2011-03-24 Hitachi Displays Ltd 液晶表示装置
WO2012111703A1 (fr) * 2011-02-15 2012-08-23 富士フイルム株式会社 Élément formant barrière et dispositif d'affichage tridimensionnel

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5546766B2 (ja) * 2009-01-07 2014-07-09 日東電工株式会社 液晶パネルおよび液晶表示装置
JP5930636B2 (ja) * 2011-09-27 2016-06-08 住友化学株式会社 偏光板
JP6116880B2 (ja) * 2012-12-07 2017-04-19 住友化学株式会社 偏光性積層フィルムおよび偏光板の製造方法
JP5602823B2 (ja) * 2012-12-07 2014-10-08 住友化学株式会社 偏光性積層フィルムおよび偏光板の製造方法、偏光性積層フィルム

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10133196A (ja) * 1996-10-28 1998-05-22 Sony Corp 液晶表示装置および液晶表示装置用偏光板
JP2003084271A (ja) * 2001-09-14 2003-03-19 Fujitsu Ltd 液晶表示装置
JP2005345958A (ja) * 2004-06-07 2005-12-15 Nitto Denko Corp 液晶パネル、偏光板および液晶表示装置
JP2006201401A (ja) * 2005-01-19 2006-08-03 Sharp Corp 液晶表示装置
JP2007233362A (ja) * 2006-02-02 2007-09-13 Semiconductor Energy Lab Co Ltd 表示装置
JP2009009100A (ja) * 2007-05-31 2009-01-15 Sumitomo Chemical Co Ltd 偏光板
JP2010039420A (ja) * 2008-08-08 2010-02-18 Nitto Denko Corp 液晶パネルおよび液晶表示装置
JP2011059266A (ja) * 2009-09-08 2011-03-24 Hitachi Displays Ltd 液晶表示装置
WO2012111703A1 (fr) * 2011-02-15 2012-08-23 富士フイルム株式会社 Élément formant barrière et dispositif d'affichage tridimensionnel

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2018205464A (ja) * 2017-06-01 2018-12-27 株式会社サンリッツ 偏光板および画像表示装置

Also Published As

Publication number Publication date
TWI822651B (zh) 2023-11-21
TW201721193A (zh) 2017-06-16
JPWO2017047406A1 (ja) 2018-07-05

Similar Documents

Publication Publication Date Title
JP5251827B2 (ja) 液晶表示装置
JP5903794B2 (ja) 偏光板のセット、液晶パネル及び液晶表示装置
WO2018193729A1 (fr) Plaque de polarisation et écran d'affichage à cristaux liquides
WO2017047408A1 (fr) Plaque de polarisation composite et panneau à cristaux liquides utilisant celle-ci
JP2011203571A (ja) 偏光板及びその製造方法
JP2011170234A (ja) 液晶表示装置
JP6323477B2 (ja) 偏光板のセットおよび液晶パネル
WO2017047406A1 (fr) Plaque polarisante composite et panneau à cristaux liquides qui l'utilise
WO2017047405A1 (fr) Plaque polarisante composite et panneau à cristaux liquides l'utilisant
JP2017083820A (ja) 偏光板および液晶パネル並びに偏光板の製造方法
JP2017156399A (ja) 偏光板のセットおよび液晶パネル
JP2021036328A (ja) 偏光板のセットおよび液晶パネル
WO2017130656A1 (fr) Procédé de production de plaques polarisantes
CN106990471B (zh) 偏振板和液晶面板
JP2017138582A (ja) 偏光板の製造方法
JP2017097087A (ja) 偏光板及び画像表示装置
JP6112249B2 (ja) 偏光板のセット及び液晶パネル
WO2017047407A1 (fr) Plaque de polarisation composite et panneau à cristaux liquides l'utilisant
JP2017102425A (ja) 偏光板および液晶パネル
JP2018067020A (ja) 偏光板のセットおよび液晶パネル

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16846277

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2017539830

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16846277

Country of ref document: EP

Kind code of ref document: A1