WO2017003875A1 - Composition adhésive durcissable à l'humidité à base de polylactide polyols - Google Patents

Composition adhésive durcissable à l'humidité à base de polylactide polyols Download PDF

Info

Publication number
WO2017003875A1
WO2017003875A1 PCT/US2016/039323 US2016039323W WO2017003875A1 WO 2017003875 A1 WO2017003875 A1 WO 2017003875A1 US 2016039323 W US2016039323 W US 2016039323W WO 2017003875 A1 WO2017003875 A1 WO 2017003875A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyol
adhesive
adhesive composition
substrate
polylactide
Prior art date
Application number
PCT/US2016/039323
Other languages
English (en)
Inventor
Anthony J. OSTLUND
Dorian P. NELSON
Original Assignee
H.B. Fuller Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by H.B. Fuller Company filed Critical H.B. Fuller Company
Publication of WO2017003875A1 publication Critical patent/WO2017003875A1/fr

Abstract

La présente invention concerne une composition adhésive durcissable à l'humidité comprenant un prépolymère polyuréthane à terminaison isocyanate qui est un produit de la réaction d'un constituant polyol et d'un constituant isocyanate. Le constituant polyol comprend un polylactide polyol qui est un produit de la réaction d'un lactide et d'un initiateur à fonctionnalité hydroxyle choisi dans le groupe constitué par un glycérol, un monoglycéride d'acide gras, un diglycéride d'acide gras, et des combinaisons de ceux-ci.
PCT/US2016/039323 2015-07-01 2016-06-24 Composition adhésive durcissable à l'humidité à base de polylactide polyols WO2017003875A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201562187453P 2015-07-01 2015-07-01
US62/187,453 2015-07-01

Publications (1)

Publication Number Publication Date
WO2017003875A1 true WO2017003875A1 (fr) 2017-01-05

Family

ID=56373145

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2016/039323 WO2017003875A1 (fr) 2015-07-01 2016-06-24 Composition adhésive durcissable à l'humidité à base de polylactide polyols

Country Status (2)

Country Link
US (1) US20170002241A1 (fr)
WO (1) WO2017003875A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110564355A (zh) * 2019-09-23 2019-12-13 皇冠（太仓）胶粘制品有限公司 生物基聚氨酯压敏胶及其制备方法

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7261218B2 (ja) 2017-07-07 2023-04-19 ステパン カンパニー ポリウレタン用途のための低粘度ポリオール
CN109400844A (zh) * 2018-09-19 2019-03-01 江苏三木化工股份有限公司 一种生物基可光固化预聚物及其制备方法
TW202128933A (zh) 2019-11-15 2021-08-01 德商巴斯夫歐洲公司 具有高初始強度之濕氣固化聚氨酯熱熔膠

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4804691A (en) * 1987-08-28 1989-02-14 Richards Medical Company Method for making a biodegradable adhesive for soft living tissue
US5399353A (en) * 1986-06-20 1995-03-21 Henkel Kommanditgesellschaft Auf Aktien Preparations for covering undamaged and/or damaged areas of human or animal skin
WO2000035982A1 (fr) * 1998-12-17 2000-06-22 Henkel Kommanditgesellschaft Auf Aktien Adhesif polyester-polyurethanne et son utilisation

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100100124A1 (en) * 2005-05-05 2010-04-22 Tyco Healthcare Group Lp Bioabsorbable surgical composition
KR101260590B1 (ko) * 2008-07-10 2013-05-06 닛본 덴끼 가부시끼가이샤 폴리락트산 수지 조성물 및 폴리락트산 수지 성형체
US8653155B2 (en) * 2009-08-13 2014-02-18 Boston Scientific Scimed, Inc. Polymers having lipophilic hydrocarbon and biodegradable polymeric segments
US20170002240A1 (en) * 2015-07-01 2017-01-05 H.B. Fuller Company Adhesive composition based on polylactide polyols

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5399353A (en) * 1986-06-20 1995-03-21 Henkel Kommanditgesellschaft Auf Aktien Preparations for covering undamaged and/or damaged areas of human or animal skin
US4804691A (en) * 1987-08-28 1989-02-14 Richards Medical Company Method for making a biodegradable adhesive for soft living tissue
WO2000035982A1 (fr) * 1998-12-17 2000-06-22 Henkel Kommanditgesellschaft Auf Aktien Adhesif polyester-polyurethanne et son utilisation

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110564355A (zh) * 2019-09-23 2019-12-13 皇冠（太仓）胶粘制品有限公司 生物基聚氨酯压敏胶及其制备方法

Also Published As

Publication number Publication date
US20170002241A1 (en) 2017-01-05

Similar Documents

Publication Publication Date Title
US9181460B2 (en) Gas transmitting polyurethane adhesive
WO2017003872A1 (fr) Composition adhésive à base de polyols de polylactide
US10836939B2 (en) One-part polyurethane adhesive composition, method of making a laminate, and laminate
TWI425086B (zh) 生物系多元醇
JP4948507B2 (ja) ラミネート接着剤
WO2017003875A1 (fr) Composition adhésive durcissable à l'humidité à base de polylactide polyols
CN107523253A (zh) 生物可降解的压敏胶粘剂
JP6163766B2 (ja) ポリエステル樹脂、ポリエステル樹脂水分散体、及びポリエステル樹脂水分散体の製造方法
JP5466095B2 (ja) 共重合ポリエステル樹脂およびそれを用いた接着剤
JP2012214558A (ja) 共重合ポリエステル樹脂およびそれを用いた接着剤
JP6881647B1 (ja) 粘着剤組成物および粘着シート
US8546494B2 (en) Isocyanate-terminated prepolymer
JP7443763B2 (ja) 接着剤組成物、及び積層体
JP6996291B2 (ja) 接着用組成物、および積層体の製造方法
JP7317197B1 (ja) 無溶剤型反応性接着剤、及び積層体
JP2009007419A (ja) 感圧式接着剤組成物及びその利用
WO2022220223A1 (fr) Composition adhésive et feuille adhésive
JP2023070009A (ja) 粘着剤および粘着シート
WO2023228601A1 (fr) Stratifié absorbant l'oxygène
WO2022189282A1 (fr) Dispersion aqueuse de polyuréthane
JP2023024399A (ja) ポリエステル系樹脂（ａ）およびそれを用いたポリエステル系樹脂組成物、インキ用組成物、接着剤用組成物、並びに上記ポリエステル系樹脂（ａ）の製法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16736685

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16736685

Country of ref document: EP

Kind code of ref document: A1