WO2016123181A1 - Alliage de magnésium et de terres rares - Google Patents

Alliage de magnésium et de terres rares Download PDF

Info

Publication number
WO2016123181A1
WO2016123181A1 PCT/US2016/015057 US2016015057W WO2016123181A1 WO 2016123181 A1 WO2016123181 A1 WO 2016123181A1 US 2016015057 W US2016015057 W US 2016015057W WO 2016123181 A1 WO2016123181 A1 WO 2016123181A1
Authority
WO
WIPO (PCT)
Prior art keywords
alloy
rare earth
earth element
amount
yttrium
Prior art date
Application number
PCT/US2016/015057
Other languages
English (en)
Inventor
Syamala Rani Pulugurtha
Jeff Allen
Ya Guo
Original Assignee
Medtronic Vascular Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Medtronic Vascular Inc. filed Critical Medtronic Vascular Inc.
Priority to EP16715132.3A priority Critical patent/EP3250723A1/fr
Priority to CN201680007557.5A priority patent/CN107208200A/zh
Publication of WO2016123181A1 publication Critical patent/WO2016123181A1/fr

Abstract

La présente invention concerne un alliage de magnésium comprenant un composant d'alliage des terres rares comprenant l'yttrium, une terre rare autre que l'yttrium, le complément étant constitué de magnésium. La terre rare autre que l'yttrium peut comprendre deux ou plusieurs terres rares autres que l'yttrium. La terre rare autre que l'yttrium peut comprendre une terre rare lourde et une terre rare légère. L'alliage peut comprendre d'environ 4 à 10 % en poids d'yttrium, de 0 à 9 % en poids de terre rare lourde, de 0 à 7 % en poids de terre rare légère, de 0 à 7 % en poids de zinc, de 0 à 0,7 % en poids de zirconium, le complément étant constitué de magnésium. Le complément de magnésium peut représenter une quantité allant jusqu'à 90 % en poids
PCT/US2016/015057 2015-01-28 2016-01-27 Alliage de magnésium et de terres rares WO2016123181A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
EP16715132.3A EP3250723A1 (fr) 2015-01-28 2016-01-27 Alliage de magnésium et de terres rares
CN201680007557.5A CN107208200A (zh) 2015-01-28 2016-01-27 镁及稀土元素合金

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201562108923P 2015-01-28 2015-01-28
US62/108,923 2015-01-28

Publications (1)

Publication Number Publication Date
WO2016123181A1 true WO2016123181A1 (fr) 2016-08-04

Family

ID=55697440

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2016/015057 WO2016123181A1 (fr) 2015-01-28 2016-01-27 Alliage de magnésium et de terres rares

Country Status (4)

Country Link
US (1) US20160215372A1 (fr)
EP (1) EP3250723A1 (fr)
CN (1) CN107208200A (fr)
WO (1) WO2016123181A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107400815A (zh) * 2017-08-04 2017-11-28 山东省科学院新材料研究所 一种高性能Mg‑Y‑Mn‑Gd变形镁合金及其制备方法
CN110964961A (zh) * 2019-12-31 2020-04-07 龙南龙钇重稀土科技股份有限公司 一种高强高耐腐蚀性镁合金及其制备工艺

Families Citing this family (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN109576544B (zh) * 2018-12-11 2021-06-15 上海航天精密机械研究所 一种稀土镁合金熔焊焊丝及其制造方法和使用方法
CN109609825B (zh) * 2018-12-28 2021-01-08 北京工业大学 一种采用预拉伸复合双级时效工艺制备超高强镁合金的方法
CN109943757B (zh) * 2019-03-29 2021-07-20 上海交通大学 适于低压铸造的高强韧耐热Mg-Y-Er合金及其制备方法
CN110284035B (zh) * 2019-08-07 2020-12-08 中国科学院长春应用化学研究所 一种耐热镁合金及其制备方法
CN111057924B (zh) * 2020-01-05 2021-07-02 北京工业大学 一种高塑性低稀土镁合金及其制备方法
CN111304510B (zh) * 2020-03-19 2021-05-25 上海交通大学 一种高强高耐腐蚀三元镁合金及其制备方法
CN112251657B (zh) * 2020-09-13 2022-04-19 北京工业大学 一种改善稀土镁合金塑性成形的制备方法
CN113667873A (zh) * 2021-09-03 2021-11-19 中北大学 一种高强韧含钪耐热镁钆合金锭的制备方法
CN116356171B (zh) * 2023-05-31 2023-09-12 北京爱康宜诚医疗器材有限公司 医用镁合金及其制备方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101078080A (zh) * 2007-07-04 2007-11-28 北京有色金属研究总院 抗蠕变镁合金及其制备方法
WO2010038016A1 (fr) * 2008-09-30 2010-04-08 Magnesium Elektron Limited Alliages de magnésium contenant des terres rares
US20130060326A1 (en) * 2004-09-07 2013-03-07 Biotronik Vi Patent Ag Implant made of a biodegradable magnesium alloy
CN104278185A (zh) * 2014-11-03 2015-01-14 北京汽车股份有限公司 一种汽车用含SiC颗粒的高强高模量稀土镁基复合材料

Family Cites Families (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4116731A (en) * 1976-08-30 1978-09-26 Nina Mikhailovna Tikhova Heat treated and aged magnesium-base alloy
SU1360223A1 (ru) * 1985-09-24 1994-10-15 В.А. Блохина Сплав на основе магния
KR100701028B1 (ko) * 2004-06-14 2007-03-29 연세대학교 산학협력단 비정질 형성능이 우수한 마그네슘계 비정질 합금
CN100383271C (zh) * 2006-01-23 2008-04-23 中南大学 高强耐热稀土镁合金
EP2021522A2 (fr) * 2006-04-28 2009-02-11 Biomagnesium Systems Ltd. Alliages de magnésium biodégradables et utilisations de ceux-ci
CN100545286C (zh) * 2006-09-29 2009-09-30 上海交通大学 高强度抗蠕变镁合金及其制备方法
CN100436624C (zh) * 2007-06-22 2008-11-26 西安工业大学 高强耐热变形镁合金
CN101353747B (zh) * 2008-09-11 2010-06-02 上海交通大学 压铸耐热镁合金及其制备方法
CN102392166B (zh) * 2011-10-27 2013-04-10 哈尔滨工业大学 一种Mg-Gd-Y-Zn-Zr系合金大型铸锭及其制备方法
CN104195396A (zh) * 2014-08-04 2014-12-10 上海交通大学 含硅、锌和Gd(-Y)的耐热稀土镁合金及其制备方法

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130060326A1 (en) * 2004-09-07 2013-03-07 Biotronik Vi Patent Ag Implant made of a biodegradable magnesium alloy
CN101078080A (zh) * 2007-07-04 2007-11-28 北京有色金属研究总院 抗蠕变镁合金及其制备方法
WO2010038016A1 (fr) * 2008-09-30 2010-04-08 Magnesium Elektron Limited Alliages de magnésium contenant des terres rares
CN104278185A (zh) * 2014-11-03 2015-01-14 北京汽车股份有限公司 一种汽车用含SiC颗粒的高强高模量稀土镁基复合材料

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107400815A (zh) * 2017-08-04 2017-11-28 山东省科学院新材料研究所 一种高性能Mg‑Y‑Mn‑Gd变形镁合金及其制备方法
CN107400815B (zh) * 2017-08-04 2019-01-11 山东省科学院新材料研究所 一种高性能Mg-Y-Mn-Gd变形镁合金及其制备方法
CN110964961A (zh) * 2019-12-31 2020-04-07 龙南龙钇重稀土科技股份有限公司 一种高强高耐腐蚀性镁合金及其制备工艺

Also Published As

Publication number Publication date
CN107208200A (zh) 2017-09-26
US20160215372A1 (en) 2016-07-28
EP3250723A1 (fr) 2017-12-06

Similar Documents

Publication Publication Date Title
US20160215372A1 (en) Biodegradable magnesium alloy
JP5913459B2 (ja) 吸収性マグネシウム合金
MX2011003293A (es) Aleaciones de magnesio que contienen tierras raras.
EP2971206A1 (fr) Alliage de magnésium à taux de dégradation ajustable
AU2017393044B2 (en) Magnesium alloy
JP5703881B2 (ja) 高強度マグネシウム合金およびその製造方法
WO2013115490A1 (fr) Alliage de magnésium d'une grande ductilité et d'une grande ténacité et son procédé de préparation
Rzychoń et al. Microstructure, castability, microstructural stability and mechanical properties of ZRE1 magnesium alloy
EP1813689A1 (fr) Alliage de magnesium
Mingbo et al. Comparison of effects of cerium, yttrium and gadolinium additions on as-cast microstructure and mechanical properties of Mg-3Sn-1Mn magnesium alloy
Xiao et al. Microstructural characterization of high pressure die cast Mg-Zn-Al-RE alloys
KR20200078343A (ko) 컴프레서 미끄럼 이동 부품용 알루미늄 합금, 컴프레서 미끄럼 이동 부품 단조품 및 그 제조 방법
Kubásek et al. Structural and mechanical study on Mg–xLM (x= 0–5 wt.%, LM= Sn, Ga) alloys
Kabirian et al. Effects of Zirconium Additions on the Microstructure of As‐Cast and Aged AZ91 Magnesium Alloy
Huang et al. Influence of aluminum content on microstructure and performance of Mg-Zn-Ca-Al-Mn magnesium alloys
US11608546B2 (en) Aluminum-cerium-manganese alloy embodiments for metal additive manufacturing
Kubasek et al. Structural and corrosion characterization of biodegradable Mg-Zn alloy castings
KR101561147B1 (ko) Ｍｇ기 합금
JP2005213535A (ja) 高性能マグネシウム合金及びその製造方法
MAGNEZIJEVE Effect of heat pre-treatment and extrusion on the structure and mechanical properties of WZ21 magnesium alloy
Liu et al. Microstructure evolution and age-hardening response in Mg-Sn-Sm alloys under a wide range of Sm/Sn ratio
Ahmad et al. Effect of yttrium addition on microstructure and hardness of cast EV31A magnesium alloy
WO2023080056A1 (fr) Matériau d'extension d'alliage à base de magnésium
Heinl Influence of alloying elements (Cu, Mg, Ag) and hot rolling on the solidification microstructure, precipitation microstructure and hardness of an Al-Cu-Mg-Ag alloy
Liu et al. Influence of re on microstructure and mechanical properties of Mg-Li-Al alloys

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16715132

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

REEP Request for entry into the european phase

Ref document number: 2016715132

Country of ref document: EP