WO2016099656A1 - Procédés de formation de revêtements réfléchissants et systèmes d'éclairage les comprenant - Google Patents

Procédés de formation de revêtements réfléchissants et systèmes d'éclairage les comprenant Download PDF

Info

Publication number
WO2016099656A1
WO2016099656A1 PCT/US2015/057073 US2015057073W WO2016099656A1 WO 2016099656 A1 WO2016099656 A1 WO 2016099656A1 US 2015057073 W US2015057073 W US 2015057073W WO 2016099656 A1 WO2016099656 A1 WO 2016099656A1
Authority
WO
WIPO (PCT)
Prior art keywords
binder resin
cross
cure
reflective coating
hard
Prior art date
Application number
PCT/US2015/057073
Other languages
English (en)
Inventor
Dengke Cai
Gary Robert Allen
Matthew A. BUGENSKE
Martin Norman Hassink
Cherian Jacob
Christopher Henry Wilson
Original Assignee
GE Lighting Solutions, LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US14/572,922 external-priority patent/US20150103529A1/en
Application filed by GE Lighting Solutions, LLC filed Critical GE Lighting Solutions, LLC
Publication of WO2016099656A1 publication Critical patent/WO2016099656A1/fr

Abstract

L'invention concerne des procédés et des matériaux permettant de réguler le type et les quantités relatives du pouvoir de réflexion (par exemple, la réflexion spéculaire par rapport à la réflexion par diffusion) dans des revêtements réfléchissants, et destinés notamment à être inclus dans un luminaire ou une autre source d'éclairage. Un procédé de formation d'un revêtement réfléchissant sur un substrat consiste à appliquer sur le substrat un matériau précurseur qui comprend une résine de liant réticulable, un agent de réticulation et des particules de pigment de diffusion. Les particules de pigment sont principalement au niveau ou à proximité d'une surface externe du matériau précurseur appliqué. Ensuite, le matériau précurseur appliqué est soumis à un durcissement à une ou plusieurs étapes pour former le revêtement réfléchissant par réticulation de la résine de liant. Le niveau d'énergie et la durée du durcissement empêchent la migration des particules de pigment et/ou de la résine de liant dans le matériau précurseur appliqué, de sorte que les particules de pigment restent principalement au niveau ou à proximité d'une surface externe du revêtement réfléchissant.
PCT/US2015/057073 2014-12-17 2015-10-23 Procédés de formation de revêtements réfléchissants et systèmes d'éclairage les comprenant WO2016099656A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US14/572,922 2014-12-17
US14/572,922 US20150103529A1 (en) 2012-04-19 2014-12-17 Methods of forming reflective coatings and lighting systems provided therewith

Publications (1)

Publication Number Publication Date
WO2016099656A1 true WO2016099656A1 (fr) 2016-06-23

Family

ID=54704065

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2015/057073 WO2016099656A1 (fr) 2014-12-17 2015-10-23 Procédés de formation de revêtements réfléchissants et systèmes d'éclairage les comprenant

Country Status (2)

Country Link
TW (1) TW201631059A (fr)
WO (1) WO2016099656A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115537104A (zh) * 2022-11-04 2022-12-30 浙江绿环新材料科技有限公司 一种环保型高反射率粉末涂料及其制备工艺
CN117820936A (zh) * 2024-03-06 2024-04-05 广东睿智环保科技股份有限公司 一种漫反射粉末涂料的制备方法及应用
CN117820936B (zh) * 2024-03-06 2024-05-31 广东睿智环保科技股份有限公司 一种漫反射粉末涂料的制备方法及应用

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2002013978A2 (fr) * 2000-08-16 2002-02-21 Daniel Mushett Procede de formation de surface reflechissante
WO2007056096A2 (fr) * 2005-11-03 2007-05-18 E. I. Du Pont De Nemours And Company Revêtement en poudre faiblement émissif
US20110064939A1 (en) * 2009-03-20 2011-03-17 Eric Teather Diffusively light reflective paint composition, method for making paint composition, and diffusively light reflective articles
US20130279174A1 (en) * 2012-04-19 2013-10-24 GE Lighting Solutions, LLC Methods for tailoring the properties of a reflective coating

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2002013978A2 (fr) * 2000-08-16 2002-02-21 Daniel Mushett Procede de formation de surface reflechissante
WO2007056096A2 (fr) * 2005-11-03 2007-05-18 E. I. Du Pont De Nemours And Company Revêtement en poudre faiblement émissif
US20110064939A1 (en) * 2009-03-20 2011-03-17 Eric Teather Diffusively light reflective paint composition, method for making paint composition, and diffusively light reflective articles
US20130279174A1 (en) * 2012-04-19 2013-10-24 GE Lighting Solutions, LLC Methods for tailoring the properties of a reflective coating

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115537104A (zh) * 2022-11-04 2022-12-30 浙江绿环新材料科技有限公司 一种环保型高反射率粉末涂料及其制备工艺
CN115537104B (zh) * 2022-11-04 2023-11-24 浙江绿环新材料科技有限公司 一种环保型高反射率粉末涂料及其制备工艺
CN117820936A (zh) * 2024-03-06 2024-04-05 广东睿智环保科技股份有限公司 一种漫反射粉末涂料的制备方法及应用
CN117820936B (zh) * 2024-03-06 2024-05-31 广东睿智环保科技股份有限公司 一种漫反射粉末涂料的制备方法及应用

Also Published As

Publication number Publication date
TW201631059A (zh) 2016-09-01

Similar Documents

Publication Publication Date Title
US9676000B2 (en) Lighting system with reflective coating having cross-linked polymeric powder and a pigment
US20150103529A1 (en) Methods of forming reflective coatings and lighting systems provided therewith
JP2009164275A (ja) シリコーン樹脂基材
CN105911623A (zh) 光学膜和包括光学膜的发光器件
JP7013736B2 (ja) プライマー層形成用組成物、バリアフィルム、波長変換シート、及び、波長変換シートの製造方法
DE60332561D1 (de) Hochreflexionspolyesterbeschichtung
JP2016126023A (ja) 光拡散シート
WO2016099656A1 (fr) Procédés de formation de revêtements réfléchissants et systèmes d'éclairage les comprenant
JP2012177880A (ja) 光拡散材料及び照明器具並びに照明器具の製造方法
CN112859221B (zh) 一种真空镀膜反光产品及其制备工艺
US9236545B2 (en) Hybrid metallization on plastic for a light emitting diode (LED) lighting system
KR101209331B1 (ko) 빛을 투과하는 금속 재질의 코팅면을 구비하는 발광체 및 그 코팅면의 제조방법
JP4762916B2 (ja) 再帰性反射シートとその製造方法及び使用方法
JP7036509B2 (ja) 光方向転換フィルム構造体及びその製造方法
JP2009151143A (ja) 光反射板用塗料組成物、光反射板用プレコート金属板及び液晶表示装置用光反射板
KR102208205B1 (ko) 2액형 광확산 코팅제 조성물
WO2012099966A2 (fr) Réflecteur à changement de couleur
JPH10305510A (ja) 反射フィルム
US20170038030A1 (en) Reflective matte coating for lighting fixture
KR20090044754A (ko) 램프의 효율을 증대시키는 반사층 형성기술
KR100692930B1 (ko) 조명기구용 고조도 백색 반사강판
JP2000133027A (ja) 反射鏡
CN212102659U (zh) 高原气候专用耐候性好的复合防水涂层
US20170043374A1 (en) Double layer coating for lighting fixture
KR20230101142A (ko) 항공장애표시등용 리플렉터 및 그 제조방법

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15801003

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15801003

Country of ref document: EP

Kind code of ref document: A1